磁性Fe3O4 /壳聚糖的化学修饰及包覆机理研究

Nano-sized Fe₃O₄ powder was prepared through an Oxygenation-Hydrothermal method. The chitosan magnetic complex was prepared by coating chitosan on the surface of Fe₃O₄ powders through Microlatex-Crosslinking Method. The product was characterized by IR， XRD， TEM， Vibrating Sample Magnetometer (VSM)， TG methods. Results show that the as-prepared powder is 25 nm in size and shows supermagnetism. The content of magnetite in microspheres is 37.8%. The mechanism for the coating reaction of chitosan to Fe₃O₄ nanoparticles is also suggested.     

MgFe2O4-Fe2O3纳米粉体的软化学合成及电磁学特性

Nano-MgFe₂O₄-Fe₂O₃ magnetic powders were synthesized by citrate gel under microwave irradiation. The structure，particle size distribution，electromagnetic characteristics of nano-MgFe₂O₄-Fe₂O₃ were characterized by using TG-DTA, X-ray, electronic microscope, nano-size measurement and electromagnetism measurement apparatus。The results show that the product is a mixture of MgFe₂O₄ and Fe₂O₃ with average size of 44 nm, tanδ for the product is 0.265 and 0.610 at frequency of 1.0 GHz and 1.8 GHz respectively.     

碳纳米管负载的Fe2O3催化剂制备

Carbon nanotubes were modified by FeSO₄-H₂O₂ system, iron hydroxides were adsorbed on the wall of carbon nanotubes simultaneously. These precursors were treated at 723K for 2 h under hydrogen, nitrogen and air atmosphere to prepare carbon nanotubes supported γ-Fe₂O₃catalyst, γ-Fe₂O₃and α-Fe₂O₃compound catalyst and amorphous Fe₂O₃catalyst, respectively. This is green method to prepare high Fe₂O₃loading (≥50 %) catalyst without adding other cation. The different structures Fe₂O₃catalysts can be synthesized by controlling the condition of thermal treatment to content active phase requirements for different catalytic reactions. The paper presents a new method to prepare carbon nanotubes supported catalysts.     

锂离子电池正极材料LiMn2O4的合成与晶体结构（英）

Spinel LiMn₂O₄ powders were prepared using two-step synthesis method consisting of solid-state reaction method and citrate modified sol-gel method. The effects of the calcination temperature and the Li/Mn ratio of raw materials were studied on the physicochemical and electrochemical properties of the spinel LiMn₂O₄ powders, such as crystallinity, lattice constant and density. The title compound was characterized by powder X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). Polycrystalline LiMn₂O₄ powers calcined at 750 ℃ were found to be composed of very uniformly-sized microcrystal with an average particle size of 300 nm. The improvement in electrochemical properties was mainly attributed to the process of re-grinding by absolute alcohol.     

电镀烧结法制备Ti/SnO2-Sb2O4电极的研究

The Ti/SnO₂-Sb₂O₄ electrode has been prepared by the electroplate-sinter method. The effect of SbCl₃ adding amount and sintering temperature on its electrode lifetime and oxygen evolution potential were investigated by means of EDX, SEM and XRD analysis. The results indicated that the electrode appeared the best performance when the SbCl₃ adding amounts was 0.2g and the sintering temperature was 550℃. In optimized conditions Ti substrate was entirely covered by SnO₂-Sb₂O₄ and the combinations among them were tight. Due to the use of electroplate method, the electrical conductivity, the oxygen evolution potential and the electrode lifetime were increased, so the elec-tro-catalytic activity and the electrochemical stability of the prepared electrode were found to be superior.     

硬脂酸法制备超细K2La2Ti3O10及其酸交换性质研究

A new stearic acid method(SAM) has been used to prepare ultrafine K₂La₂Ti₃O₁₀ nanocrystalline. Each state of synthesis process was followed by the use of FT-IR analysis. The resulting materials have been characterized by means of XRD， TEM， BET surface area analysis. The acid-exchanging property of the obtained product was also studied. The experimental results showed that comparing with the product of traditional solid-state reaction， the particle size of the K₂La₂Ti₃O₁₀ synthesized by SAM is greatly reduced， BET surface area is high(more than 11.83m²·g^-1) and has different acid-exchanging properties. It can be easily exfoliated in 2mol·L^-1 HNO₃ so-lution.     

草酸盐共沉淀法制备Y1.84La0.16O3纳米粉体

Nanopowder of Y_1.84La_0.16O₃ was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re₂(NO₃)₂(C₂O₄)₂·2H₂O (Re=Y, La), and the Y_1.84La_0.16O₃ nanopowders produced by calcining the precursor at 1 000 ℃ for 4 h are 20～40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1 450～1 550 ℃ in H₂ atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.     

Bi2Fe4O9纳米粉体:水热法制备及表征

Bi₂Fe₄O₉ nanoparticles were prepared at low temperature via a facile, one-step hydrothermal synthesis process using iron(Ⅲ) nitrate nonahydrate(Fe(NO₃)₃·9H₂O) and bismuth nitrate pentahydrate (Bi(NO₃)₃·5H₂O) as starting materials and sodium hydroxide (NaOH) as the precipitant and mineralizer. XRD results indicate that the as-prepared nanoparticles are pure Bi₂Fe₄O₉. SEM images reveal that the as-prepared Bi₂Fe₄O₉ nanoparticles have a sheet-like morphology. The Bi₂Fe₄O₉ nanoparticles thus obtained are paramagnetic at room temperature as shown by magnetic measurements.     

纳米Mn-Zn铁氧体的制备和研究

Nanosize manganese zinc ferrites were fabricated by hydrothermal precipitation route using Fe₂(SO₄)₃, ZnSO₄·7H₂O, MnSO₄·H₂O as material, then some calcinated at 500 ℃ and studied by XRD, TEM, IR and VSM. The results showed that the products were spinel crystal structure and uniformly sized nanoparticles (15～25 nm) with little aggregation. The analysis of IR showed that the superficial water can be eliminated, but that was embedded in crystal lattice can not be removed by calcinating. The effect Zn content x on the lattice (a) of nanosize Mn_1-xZn_xFe₂O₄ was also discussed. The lattice of nanosize Mn_1-xZn_xFe₂O₄ decreases with x increasing; and its value deviated the standard lattice (a₀) of normal size manganese zinc ferrites. A lot of water was absorbed during the hydrothermal process owing to the large surface of nanosize particles. The change of magnetic properties of Mn_xZn_1-xFe₂O₄ with x increasing was studied: nanosize Mn_xZn_1-xFe₂O₄ particles synthesized by us exhibited peculiar magnetic properties curve with Zn content (x) increasing, Superparamagnetic behaviors of the synthesized ZnFe₂O₄ samples were confirmed by magnetic characterization, which can be explained by the difference between the distribution of the metal ions (Mn²⁺, Zn²⁺ and Fe³⁺) among the tetrahedral (A) and the octahedral (B) sites of nanosize ferrite and that of bulk ferrite.     

不同形态的α-Fe2O3纳米粉体的水热合成、表征及其磁性研究

Four different hematite (α-Fe₂O₃) nanopowders with various morphologies have been synthesized in the presence of surfactant (HPC) via hydrothermal route at 180 ℃, using four kinds of iron salts, Fe₂(SO₄)₃, FeC₂O₄, FeSO₄ and (NH₄)₃Fe(C₂O₄)₃, as precursor materials. The products were characterized by means of X-ray diffraction (XRD), transmission electron micrograph (TEM), Fourier transform infrared spectroscopy (FTIR) and magnetization measurements. The hysteresis measurements show that the products exhibit weak ferromagnetic property at room temperature. It is concluded that the different precursor materials and the presence of the surfactant are important factors that exert significant effects on the morphologies and magnetic properties of the products.     

Sol-gel synthesis of K3InF6 and structural characterization of K2InC10O10H6F9, K3InC12O14H4F18 and K3InC12O12F18

K₃InF₆ is synthesized by a sol-gel route starting from indium and potassium acetates dissolved in isopropanol in the stoichiometry 1:3, with trifluoroacetic acid as fluorinating agent. The crystal structures of the organic precursors were solved by X-ray diffraction methods on single crystals. Three organic compounds were isolated and identified: K₂InC₁₀O₁₀H₆F₉, K₃InC₁₂O₁₄H₄F₁₈ and K₃InC₁₂O₁₂F₁₈. The first one, deficient in potassium in comparison with the initial stoichiometry, is unstable. In its crystal structure, acetate as well as trifluoroacetate anions are coordinated to the indium atom. The two other precursors are obtained, respectively, by quick and slow evaporation of the solution. They correspond to the final organic compounds, which give K₃InF₆ by decomposition at high temperature. The crystal structure of K₃InC₁₂O₁₄H₄F₁₈ is characterized by complex anions [In(CF₃COO)₄(OH_x)₂]^(5−2x)− and isolated [CF₃COOH_2−x]^(x−1)− molecules with x=2 or 1, surrounded by K⁺ cations. The crystal structure of K₃InC₁₂O₁₂F₁₈ is only constituted by complex anions [In(CF₃COO)₆]³⁻ and K⁺ cations. For all these compounds, potassium cations ensure only the electroneutrality of the structure. IR spectra of K₂InC₁₀O₁₀H₆F₉ and K₃InC₁₂O₁₂F₁₈ were also performed at room temperature on pulverized crystals.     

Li2O-TiO2-SiO2-P2O5和Li2O-TiO2-Al2O3-P2O5体系锂离子固体电解质的制备及性能研究

一些具有NASICON型网格结构的固体电解质具有高的电导率和好的稳定性,NASICON的意思是Na Super Ionic Conductor[1]。当NaZr2(PO4)3中P5 被Si4 部分取代时便可以得到具有NASICON结构的Na1 xZr2SixP3-xO12体系,其具有高的钠离子电导率。然而有相同结构的Li1 xZr2SixP3-xO12体系的离子电导率却很低,这是因为Li 半径太小,而NASICON三维网格结构的离子通道太大,两者不匹配而使电导率下降[2]。但当LiZr2(PO4)3中Zr4 被离子半径小些的Ti4 取代,所得LiTi2(PO4)3的通道就与Li 半径相匹配,适合于锂离子的迁移,从而使其电导率…     

Non-centrosymmetric Ba3Ti3O6(BO3)2

The compound previously reported as Ba₂Ti₂B₂O₉ has been reformulated as Ba₃Ti₃B₂O₁₂, or Ba₃Ti₃O₆(BO₃)₂, a new barium titanium oxoborate. Small single crystals have been recovered from a melt with a composition of BaTiO₃:BaTiB₂O₆ (molar ratio) cooled between 1100°C and 850°C. The crystal structure has been determined by X-ray diffraction: hexagonal system, non-centrosymmetric space group, a=8.7377(11) Å, c=3.9147(8) Å, Z=1, wR(F²)=0.039 for 504 unique reflections. Ba₃Ti₃O₆(BO₃)₂ is isostructural with K₃Ta₃O₆(BO₃)₂. Preliminary measurements of nonlinear optical properties on microcrystalline samples show that the second harmonic generation efficiency of Ba₃Ti₃O₆(BO₃)₂ is equal to 95% of that of LiNbO₃.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

Synthesis, crystal structure, infrared and Raman spectra of Sr4Cu3(AsO4)2(AsO3OH)4·3H2O and Ba2Cu4(AsO4)2(AsO3OH)3

The two new compounds, Sr₄Cu₃(AsO₄)₂(AsO₃OH)₄·3H₂O (1) and Ba₂Cu₄(AsO₄)₂(AsO₃OH)₃(2), were synthesized under hydrothermal conditions. They represent previously unknown structure types and are the first compounds synthesized in the systems SrO/BaO-CuO-As₂O₅-H₂O. Their crystal structures were determined by single-crystal X-ray diffraction [space group C2/c, a=18.536(4) Å, b=5.179(1) Å, c=24.898(5) Å, β=93.67(3)°, V=2344.0(8) Å³, Z=4 for 1; space group P4₂/n, a=7.775(1) Å, c=13.698(3) Å, V=828.1(2) Å³, Z=2 for 2]. The crystal structure of 1 is related to a group of compounds formed by Cu²⁺-(XO₄)³⁻ layers (X=P⁵⁺, As⁵⁺) linked by M cations (M=alkali, alkaline earth, Pb²⁺, or Ag⁺) and partly by hydrogen bonds. In 1, worth mentioning is the very short hydrogen bond length, D···A=2.477(3) Å. It is one of the examples of extremely short hydrogen bonds, where the donor and acceptor are crystallographically different. Compound 2 represents a layered structure consisting of Cu₂O₈ centrosymmetric dimers crosslinked by As1φ₄ tetrahedra, where φ is O or OH, which are interconnected by Ba, As2 and hydrogen bonds to form a three-dimensional network. The layers are formed by Cu₂O₈ centrosymmetric dimers of CuO₅ edge-sharing polyhedra, crosslinked by As1O₄ tetrahedra. Vibrational spectra (FTIR and Raman) of both compounds are described. The spectroscopic manifestation of the very short hydrogen bond in 1, and ABC-like spectra in 2 were discussed.     

Raman scattering investigations on lanthanum-doped Bi4Ti3O12-SrBi4Ti4O15 intergrowth ferroelectrics

The ferroelectric ceramics of Bi₄Ti₃O₁₂, SrBi₄Ti₄O₁₅, and lanthanum-doped Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅ were synthesized, and their Raman spectra were investigated. La-doping resulted in the enlargement of remnant polarization of Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The structure of the Bi₂O₂ layers and TiO₆ octahedra of the intergrowth was found to be different from those of Bi₄Ti₃O₁₂ and SrBi₄Ti₄O₁₅. La³⁺ ions exhibit pronounced selectivity for the occupation of A site as La content is lower than 0.50, and tend to be incorporated into Bi₂O₂ layers when the La content is higher than 0.50. Lanthanum substitution brings about the structural phase transition in Bi₄Ti₃O₁₂-SrBi₄Ti₄O₁₅. The variation of ferroelectric property may be attributed to combined contribution from the decreasing of the oxygen vacancies, the relaxation of the lattice distortion, the destroying of the insulation and the space charge compensation effects of the Bi₂O₂ slabs.     

Ion-beam irradiation of lanthanum compounds in the systems La2O3-Al2O3 and La2O3-TiO2

Thin crystals of La₂O₃, LaAlO₃, La_2/3TiO₃, La₂TiO₅, and La₂Ti₂O₇ have been irradiated in situ using 1 MeV Kr²⁺ ions at the Intermediate Voltage Electron Microscope-Tandem User Facility (IVEM-Tandem), Argonne National Laboratory (ANL). We observed that La₂O₃ remained crystalline to a fluence greater than 3.1×10¹⁶ ions cm⁻² at a temperature of 50 K. The four binary oxide compounds in the two systems were observed through the crystalline-amorphous transition as a function of ion fluence and temperature. Results from the ion irradiations give critical temperatures for amorphisation (T_c) of 647 K for LaAlO₃, 840 K for La₂Ti₂O₇, 865 K for La_2/3TiO₃, and 1027 K for La₂TiO₅. The T_c values observed in this study, together with previous data for Al₂O₃ and TiO₂, are discussed with reference to the melting points for the La₂O₃-Al₂O₃ and La₂O₃-TiO₂ systems and the different local environments within the four crystal structures. Results suggest that there is an observable inverse correlation between T_c and melting temperature (T_m) in the two systems. More complex relationships exist between T_c and crystal structure, with the stoichiometric perovskite LaAlO₃ being the most resistant to amorphisation.     

g-C_3N_4/CaTi_2O_5复合材料制备及其光催化性能

利用类石墨氮化碳(g-C_3N_4)和亚稳相钙钛氧化物(CaTi_2O_5)固相法制备C_3N_4/CaTi_2O_5复合材料。利用X射线衍射(XRD)、金相显微镜、扫描电子显微镜(SEM)及附带能谱分析仪(EDS)和N2吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计(UV-Vis)测试了样品的光吸收性能,研究C_3N_4与CaTi_2O_5物质的量之比(nC_3N_4/nCaTi_2O_5)对C_3N_4/CaTi_2O_5复合样品的物相结构和微观形貌的影响,同时考察C_3N_4/CaTi_2O_5复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明:相比纯C_3N_4和CaTi_2O_5样品,C_3N_4/CaTi_2O_5复合样品在可见光下具有较高的光催化性能,随着nC_3N_4/nCaTi_2O_5增加,样品的光催化降解率随之增加而后降低,当nC_3N_4/nCaTi_2O_5=1∶1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

g-C3N4/CaTi2O5复合材料制备及其光催化性能

利用类石墨氮化碳（g-C₃N₄）和亚稳相钙钛氧化物（CaTi₂O₅）固相法制备C₃N₄/CaTi₂O₅复合材料。利用X射线衍射（XRD）、金相显微镜、扫描电子显微镜（SEM）及附带能谱分析仪（EDS）和N₂吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计（UV-Vis）测试了样品的光吸收性能,研究C₃N₄与CaTi₂O₅物质的量之比（n_C3N4/nCaTi₂O₅）对C₃N₄/CaTi₂O₅复合样品的物相结构和微观形貌的影响,同时考察C₃N₄/CaTi₂O₅复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明：相比纯C₃N₄和CaTi₂O₅样品,C₃N₄/CaTi₂O₅复合样品在可见光下具有较高的光催化性能,随着n_C3N4/nCaTi₂O₅增加,样品的光催化降解率随之增加而后降低,当n_C3N4/nCaTi₂O₅=1：1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

Magnetic diphase nanostructure of ZnFe2O4/γ-Fe2O3

Magnetic diphase nanostructures of ZnFe₂O₄/γ-Fe₂O₃ were synthesized by a solvothermal method. The formation reactions were optimized by tuning the initial molar ratios of Fe/Zn. All samples were characterized by X-ray diffraction, thermogravimetric analysis, infrared spectroscopy, and Raman spectra. It is found that when the initial molar ratio of Fe/Zn is larger than 2, a diphase magnetic nanostructure of ZnFe₂O₄/γ-Fe₂O₃ was formed, in which the presence of ZnFe₂O₄ enhanced the thermal stability of γ-Fe₂O₃. Further increasing the initial molar ratio of Fe/Zn larger than 6 destabilized the diphase nanostructure and yielded traces of secondary phase α-Fe₂O₃. The grain surfaces of diphase nanostructure exhibited a spin-glass-like structure. At room temperature, all diphase nanostructures are superparamagnetic with saturation magnetization being increased with γ-Fe₂O₃ content.