Evidence and understanding of ALD HfO/sub 2/-Al/sub 2/O/sub 3/ laminate MIM capacitors outperforming sandwich counterparts

Metal-insulator-metal capacitors with atomic-layer-deposited HfO/sub 2/-Al/sub 2/O/sub 3/ laminated and sandwiched dielectrics have been compared, for the first time, for analog circuit applications. The experimental results indicate that significant improvements can be obtained using the laminated dielectrics, including an extremely low leakage current of 1/spl times/10/sup -9/ A/cm/sup 2/ at 3.3V and 125/spl deg/C, a high breakdown electric field of /spl sim/3.3MV/cm at 125/spl deg/C, good polarity-independent electrical characteristics, while retaining relatively high capacitance density of 3.13 fF//spl mu/m/sup 2/ as well as voltage coefficients of capacitance as low as -80 ppm/V and 100 ppm/V/sup 2/ at 100 kHz. The underlying mechanism is likely due to alternate insertions of Al/sub 2/O/sub 3/ layers that reduce the thickness of each HfO/sub 2/ layer, hereby efficiently inhibiting HfO/sub 2/ crystallization, and blocking extensions of grain boundary channels from top to bottom as well as to achieve good interfacial quality.     

High-performance MIM capacitor using ALD high-k HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectrics

For the first time, we successfully fabricated and demonstrated high performance metal-insulator-metal (MIM) capacitors with HfO/sub 2/-Al/sub 2/O/sub 3/ laminate dielectric using atomic layer deposition (ALD) technique. Our data indicates that the laminate MIM capacitor can provide high capacitance density of 12.8 fF//spl mu/m/sup 2/ from 10 kHz up to 20 GHz, very low leakage current of 3.2 /spl times/ 10/sup -8/ A/cm/sup 2/ at 3.3 V, small linear voltage coefficient of capacitance of 240 ppm/V together with quadratic one of 1830 ppm/V/sup 2/, temperature coefficient of capacitance of 182 ppm//spl deg/C, and high breakdown field of /spl sim/6 MV/cm as well as promising reliability. As a result, the HfO/sub 2/-Al/sub 2/O/sub 3/ laminate is a very promising candidate for next generation MIM capacitor for radio frequency and mixed signal integrated circuit applications.     

Electrical characteristics and reliability of UV transparent Si/sub 3/N/sub 4/ metal-insulator-metal (MIM) capacitors

In this paper, we discuss the electrical characteristics and reliability of UV transparent Si/sub 3/N/sub 4/ metal-insulator-metal (MIM) capacitors. We examine film thicknesses in the range of 55 to 25 nm with capacitance densities from 1.2 ff//spl mu/m/sup 2/ to 2.8 ff//spl mu/m/sup 2/, respectively, for single MIM capacitors. A new approach for projecting the dielectric reliability of these films extends the limits of maximum operating voltage. Accounting for temperature acceleration and area scaling, the projected lifetimes can be met for a wide range of operating conditions.     

PVD HfO/sub 2/ for high-precision MIM capacitor applications

Metal-insulator-metal (MIM) capacitors are fabricated using sputtered HfO/sub 2/ with Ta and TaN for top and bottom electrodes, respectively. High-capacitance densities from 4.7 to 8.1 fF//spl mu/m/sup 2/ have been achieved while maintaining the leakage current densities around 1 /spl times/ 10/sup -8/ A/cm/sup 2/ within the normal circuit bias conditions. A guideline for the insulator thickness and its dielectric constant has been obtained by analyzing the tradeoff between the linearity coefficient and the capacitance density.     

Lanthanide (Tb)-doped HfO/sub 2/ for high-density MIM capacitors

A high-density metal-insulator-metal (MIM) capacitor with a lanthanide-doped HfO/sub 2/ dielectric prepared by physical vapor deposition (PVD) is presented for the first time. A significant improvement was shown in both the voltage coefficient of capacitance (VCC) and the leakage current density of MIM capacitor, yet the high capacitance density of HfO/sub 2/ dielectrics was maintained by achieving the doping of Tb with an optimum concentration in HfO/sub 2/. This technique allows utilizing thinner dielectric film in MIM capacitors and achieving a capacitance density as high as 13.3 fF//spl mu/m/sup 2/ with leakage current and VCC values that fully meet requirements from year 2005 for radio frequency (RF) bypass capacitors applications.     

MIM capacitors using atomic-layer-deposited high-/spl kappa/ (HfO/sub 2/)/sub 1-x/(Al/sub 2/O/sub 3/)/sub x/ dielectrics

Metal-insulator-metal (MIM) capacitors with (HfO/sub 2/)/sub 1-x/(Al/sub 2/O/sub 3/)/sub x/ high-/spl kappa/ dielectric films were investigated for the first time. The results show that both the capacitance density and voltage/temperature coefficients of capacitance (VCC/TCC) values decrease with increasing Al/sub 2/O/sub 3/ mole fraction. It was demonstrated that the (HfO/sub 2/)/sub 1-x/(Al/sub 2/O/sub 3/)/sub x/ MIM capacitor with an Al/sub 2/O/sub 3/ mole fraction of 0.14 is optimized. It provides a high capacitance density (3.5 fF//spl mu/m/sup 2/) and low VCC values (/spl sim/140 ppm/V/sup 2/) at the same time. In addition, small frequency dependence, low loss tangent, and low leakage current are obtained. Also, no electrical degradation was observed for (HfO/sub 2/)/sub 1-x/(Al/sub 2/O/sub 3/)/sub x/ MIM capacitors after N/sub 2/ annealing at 400/spl deg/C. These results show that the (HfO/sub 2/)/sub 0.86/(Al/sub 2/O/sub 3/)/sub 0.14/ MIM capacitor is very suitable for capacitor applications within the thermal budget of the back end of line process.     

Improvement of voltage linearity in high-/spl kappa/ MIM capacitors using HfO/sub 2/-SiO/sub 2/ stacked dielectric

It is demonstrated that the voltage coefficients of capacitance (VCC) in high-/spl kappa/ metal-insulator-metal (MIM) capacitors can be actively engineered and voltage linearity can be significantly improved maintaining high capacitance density, by using a stacked insulator structure of high-/spl kappa/ and SiO/sub 2/ dielectrics. A MIM capacitor with capacitance density of 6 fF/spl mu/m/sup 2/ and quadratic VCC of only 14 ppm/V/sup 2/ has been demonstrated together with excellent frequency and temperature dependence (temperature coefficients of capacitance of 54 ppm /spl deg/C) as well as low leakage current of less than 10 nA/cm/sup 2/ up to 4 V at 125 /spl deg/C.     

Metal-insulator-metal RF bypass capacitor using niobium oxide (Nb/sub 2/O/sub 5/) with HfO/sub 2//Al/sub 2/O/sub 3/ barriers

A high capacitance density (C/sub density/) metal-insulator-metal (MIM) capacitor with niobium pentoxide (Nb/sub 2/O/sub 5/) whose k value is higher than 40, is developed for integrated RF bypass or decoupling capacitor application. Nb/sub 2/O/sub 5/ MIM with HfO/sub 2//Al/sub 2/O/sub 3/ barriers delivers a high C/sub density/ of >17 fF//spl mu/m/sup 2/ with excellent RF properties, while maintaining comparable leakage current and reliability properties with other high-k dielectrics. The capacitance from the dielectric is shown to be stable up to 20 GHz, and resonant frequency of 4.2 GHz and Q of 50 (at 1 GHz) is demonstrated when the capacitor is integrated using Cu-BEOL process.     

Interfacial defect states in HfO/sub 2/ and ZrO/sub 2/ nMOS capacitors

A comprehensive analysis of the bump/kink observed in the experimental capacitance-voltage (C-V) curves of HfO/sub 2/ and ZrO/sub 2/ capacitors was performed using self-consistent numerical simulations. Both HfO/sub 2/ samples grown by sputter deposition and grown by metal-organic chemical vapor deposition (MOCVD) were examined. The bumps in the C-V curves were found to be consistent with an interface state centered 0.25 eV above the valence bandedge for the sputter deposited devices, and 0.30 eV above the bandedge for the MOCVD devices. Annealing of the HfO/sub 2/ devices reduced the densities of these traps, but also increased the effective oxide thickness. Similar defect states were detected for the ZrO/sub 2/ devices centered 0.25 eV above the valence bandedge.     

Charge trapping and dielectric reliability of SiO/sub 2/-Al/sub 2/O/sub 3/ gate stacks with TiN electrodes

A detailed study on charge trapping and dielectric reliability of SiO/sub 2/-Al/sub 2/O/sub 3/ gate stacks with TiN electrodes has been carried out. Due to the inherent asymmetry of the dual layer stack all electrical properties studied were found to be strongly polarity dependent. The gate current is strongly reduced for injection from the TiN (gate) electrode compared to injection from the n-type Si substrate. For substrate injection, electron trapping occurs in the bulk of the Al/sub 2/O/sub 3/ film, whereas for gate injection mainly hole trapping near the Si substrate is observed. Furthermore, no significant interface state generation is evident for substrate injection. In case of gate injection a rapid build up of interface states occurs already at small charge fluence (q/sub inj/ /spl sim/ 1 mC/cm/sup 2/). Dielectric reliability is consistent with polarity-dependent defect generation. For gate injection the interfacial layer limits the dielectric reliability and results in low Weibull slopes independent of the Al/sub 2/O/sub 3/ thickness. In the case of substrate injection, reliability is limited by the bulk of the Al/sub 2/O/sub 3/ layer leading to a strong thickness dependence of the Weibull slope as expected by the percolation model.     

Very high density RF MIM capacitors (17 fF//spl mu/m/sup 2/) using high-/spl kappa/ Al/sub 2/O/sub 3/ doped Ta/sub 2/O/sub 5/ dielectrics

Using high-/spl kappa/ Al/sub 2/O/sub 3/ doped Ta/sub 2/O/sub 5/ dielectric, we have obtained record high MIM capacitance density of 17 fF//spl mu/m/sup 2/ at 100 kHz, small 5% capacitance reduction to RF frequency range, and low leakage current density of 8.9/spl times/10/sup -7/ A/cm/sup 2/. In combination of both high capacitor density and low leakage current density, a very low leakage current of 5.2/spl times/10/sup -12/ A is calculated for a typical large 10 pF capacitor used in RF IC that is even smaller than that of a deep sub-/spl mu/m MOSFET. This very high capacitance density with good MIM capacitor characteristics can significantly reduce the chip size of RF ICs.     

A high-density MIM capacitor (13 fF//spl mu/m/sup 2/) using ALD HfO/sub 2/ dielectrics

Metal-insulator-metal (MIM) capacitors with different HfO/sub 2/ thickness have been investigated. The results show that both the capacitance density and voltage coefficients of capacitance (VCCs) increase with decreasing HfO/sub 2/ thickness. In addition, it is found that the VCCs decrease logarithmically with increasing thickness. Furthermore, the MIM capacitor with 10-nm HfO/sub 2/ shows a record high capacitance density of 13 fF//spl mu/m/sup 2/ and a VCC of 607 ppm/V, which can meet the requirement of the International Technology Roadmap for Semiconductors. It can also provide a low leakage current of 5.95 /spl times/ 10/sup -8/A/cm/sup 2/ at room temperature at 1 V, low tangent values below 0.05, and a small frequency dependence. These results indicate that the devices are suitable for use in silicon integrated circuit applications.     

High-performance Pt/SrBi/sub 2/Ta/sub 2/O/sub 9//HfO/sub 2//Si structure for nondestructive readout memory

Metal-ferroelectric-insulator-semiconductor (MFIS) capacitors with 390-nm-thick SrBi/sub 2/Ta/sub 2/O/sub 9/ (SBT) ferroelectric film and 8-nm-thick hafnium oxide (HfO/sub 2/) layer on silicon substrate have been fabricated and characterized. It is demonstrated for the first time that the MFIS stack exhibits a large memory window of around 1.08 V at an operation voltage of 3.5 V. Moreover, the MFIS memory structure suffers only 18% degradation in the memory window after 10/sup 9/ switching cycles. The excellent performance is attributed to the formation of well-crystallized SBT perovskite thin film on top of the HfO/sub 2/ buffer layer, as evidenced by the distinctive sharp peaks in X-ray diffraction (XRD) spectra. In addition to its relatively high /spl kappa/ value, HfO/sub 2/ also serves as a good seed layer for SBT crystallization, making the proposed Pt/SrBi/sub 2/Ta/sub 2/O/sub 9//HfO/sub 2//Si structure ideally suitable for low-voltage and high-performance ferroelectric memories.     

Low-frequency noise in submicrometer MOSFETs with HfO/sub 2/, HfO/sub 2//Al/sub 2/O/sub 3/ and HfAlO/sub x/ gate stacks

Low-frequency noise measurements were performed on p- and n-channel MOSFETs with HfO/sub 2/, HfAlO/sub x/ and HfO/sub 2//Al/sub 2/O/sub 3/ as the gate dielectric materials. The gate length varied from 0.135 to 0.36 /spl mu/m with 10.02 /spl mu/m gate width. The equivalent oxide thicknesses were: HfO/sub 2/ 23 /spl Aring/, HfAlO/sub x/ 28.5 /spl Aring/ and HfO/sub 2//Al/sub 2/O/sub 3/ 33 /spl Aring/. In addition to the core structures with only about 10 /spl Aring/ of oxide between the high-K dielectric and silicon substrate, there were "double-gate oxide" structures where an interfacial oxide layer of 40 /spl Aring/ was grown between the high-K dielectric and Si. DC analysis showed low gate leakage currents in the order of 10/sup -12/ A(2-5 /spl times/ 10/sup -5/ A/cm/sup 2/) for the devices and, in general, yielded higher threshold voltages and lower mobility values when compared to the corresponding SiO/sub 2/ devices. The unified number-mobility fluctuation model was used to account for the observed 1/f noise and to extract the oxide trap density, which ranged from 1.8 /spl times/ 10/sup 17/ cm/sup -3/ eV/sup -1/ to 1, 3 /spl times/ 10/sup 19/ cm/sup -3/ eV/sup -1/ somewhat higher compared to conventional SiO/sub 2/ MOSFETs with the similar device dimensions. There was no evidence of single electron switching events or random telegraph signals. The aim of this paper is to present a general discussion on low-frequency noise characteristics of the three different high-K/gate stacks, relative comparison among them and to the Si-SiO/sub 2/ system.     

Modeling of tunneling currents through HfO/sub 2/ and (HfO/sub 2/)/sub x/(Al/sub 2/O/sub 3/)/sub 1-x/ gate stacks

We present a physical modeling of tunneling currents through ultrathin high-/spl kappa/ gate stacks, which includes an ultrathin interface layer, both electron and hole quantization in the substrate and gate electrode, and energy band offsets between high-/spl kappa/ dielectrics and Si determined from high-resolution XPS. Excellent agreements between simulated and experimentally measured tunneling currents have been obtained for chemical vapor deposited and physical vapor deposited HfO/sub 2/ with and without NH/sub 3/-based interface layers, and ALD Al/sub 2/O/sub 3/ gate stacks with different EOT and bias polarities. This model is applied to more thermally stable (HfO/sub 2/)/sub x/(Al/sub 2/O/sub 3/)/sub 1-x/ gate stacks in order to project their scalability for future CMOS applications.     

Channel hot-electron degradation on 60-nm HfO/sub 2/-gated nMOSFET DC and RF performances

Channel hot-carrier-induced dc and RF performance degradations in 60-nm high-k nMOSFETs are examined experimentally. RF performances such as the cutoff frequency, noise figure, linearity, and flicker noise of high-k MOSFETs show significant vulnerability to the hot-electron effect. Analytical equations for normalized RF degradations relating to the device dc and ac parameters are derived. Good agreement between the analytical predictions and experimental data is obtained. The accuracy of the model equations suggests fast and effective evaluation of noise figure and linearity degradations using simple dc and ac parameters directly.     

Low-frequency noise in submicrometer MOSFETs with HfO/sub 2/, HfO/sub 2//Al/sub 2/O/sub 3/ and HfAlO/sub x/ gate stacks

Low-frequency noise measurements were performed on p- and n-channel MOSFETs with HfO/sub 2/, HfAlO/sub x/ and HfO/sub 2//Al/sub 2/O/sub 3/ as the gate dielectric materials. The gate length varied from 0.135 to 0.36 /spl mu/m with 10.02 /spl mu/m gate width. The equivalent oxide thicknesses were: HfO/sub 2/ 23 /spl Aring/, HfAlO/sub x/ 28.5 /spl Aring/ and HfO/sub 2//Al/sub 2/O/sub 3/ 33 /spl Aring/. In addition to the core structures with only about 10 /spl Aring/ of oxide between the high-/spl kappa/ dielectric and silicon substrate, there were "double-gate oxide" structures where an interfacial oxide layer of 40 /spl Aring/ was grown between the high-/spl kappa/ dielectric and Si. DC analysis showed low gate leakage currents in the order of 10/sup -12/A(2-5/spl times/10/sup -5/ A/cm/sup 2/) for the devices and, in general, yielded higher threshold voltages and lower mobility values when compared to the corresponding SiO/sub 2/ devices. The unified number-mobility fluctuation model was used to account for the observed 1/f noise and to extract the oxide trap density, which ranged from 1.8/spl times/10/sup 17/ cm/sup -3/eV/sup -1/ to 1.3/spl times/10/sup 19/ cm/sup -3/eV/sup -1/, somewhat higher compared to conventional SiO/sub 2/ MOSFETs with the similar device dimensions. There was no evidence of single electron switching events or random telegraph signals. The aim of this paper is to present a general discussion on low-frequency noise characteristics of the three different high-/spl kappa//gate stacks, relative comparison among them and to the Si--SiO/sub 2/ system.     

Ultrathin Al/sub 2/O/sub 3/ and HfO/sub 2/ gate dielectrics on surface-nitrided Ge

We have studied ultrathin Al/sub 2/O/sub 3/ and HfO/sub 2/ gate dielectrics on Ge grown by ultrahigh vacuum-reactive atomic-beam deposition and ultraviolet ozone oxidation. Al/sub 2/O/sub 3/-Ge gate stack had a t/sub eq//spl sim/23 /spl Aring/, and three orders of magnitude lower leakage current compared to SiO/sub 2/. HfO/sub 2/-Ge allowed even greater scaling, achieving t/sub eq//spl sim/11 /spl Aring/ and six orders of magnitude lower leakage current compared to SiO/sub 2/. We have carried out a detailed study of cleaning conditions for the Ge wafer, dielectric deposition condition, and anneal conditions and their effect on the electrical properties of metal-gated dielectric-Ge capacitors. We show that surface nitridation is important in reducing hysteresis, interfacial layer formation and leakage current. However, surface nitridation also introduces positive trapped charges and/or dipoles at the interface, resulting in significant flatband voltage shifts, which are mitigated by post-deposition anneals.     

A novel strained Si/sub 0.7/Ge/sub 0.3/ surface-channel pMOSFET with an ALD TiN/Al/sub 2/O/sub 3//HfAlO/sub x//Al/sub 2/O/sub 3/ gate stack

Proof-of-concept pMOSFETs with a strained-Si/sub 0.7/Ge/sub 0.3/ surface-channel deposited by selective epitaxy and a TiN/Al/sub 2/O/sub 3//HfAlO/sub x//Al/sub 2/O/sub 3/ gate stack grown by atomic layer chemical vapor deposition (ALD) techniques were fabricated. The Si/sub 0.7/Ge/sub 0.3/ pMOSFETs exhibited more than 30% higher current drive and peak transconductance than reference Si pMOSFETs with the same gate stack. The effective mobility for the Si reference coincided with the universal hole mobility curve for Si. The presence of a relatively low density of interface states, determined as 3.3 /spl times/ 10/sup 11/ cm/sup -2/ eV/sup -1/, yielded a subthreshold slope of 75 mV/dec. for the Si reference. For the Si/sub 0.7/Ge/sub 0.3/ pMOSFETs, these values were 1.6 /spl times/ 10/sup 12/ cm/sup -2/ eV/sup -1/ and 110 mV/dec., respectively.     

A novel high-/spl kappa/ SONOS memory using TaN/Al/sub 2/O/sub 3//Ta/sub 2/O/sub 5//HfO/sub 2//Si structure for fast speed and long retention operation

A novel high-/spl kappa/ silicon-oxide-nitride-oxide-silicon (SONOS)-type memory using TaN/Al/sub 2/O/sub 3//Ta/sub 2/O/sub 5//HfO/sub 2//Si (MATHS) structure is reported for the first time. Such MATHS devices can keep the advantages of our previously reported TaN/HfO/sub 2//Ta/sub 2/O/sub 5//HfO/sub 2//Si device structure to obtain a better tradeoff between long retention and fast programming as compared to traditional SONOS devices. While at the same time by replacing hafnium oxide (HfO/sub 2/) with aluminum oxide (Al/sub 2/O/sub 3/) for the top blocking layer, better blocking efficiency can be achieved due to Al/sub 2/O/sub 3/'s much larger barrier height, resulting in greatly improved memory window and faster programming. The fabricated devices exhibit a fast program and erase speed, excellent ten-year retention and superior endurance up to 10/sup 5/ stress cycles at a tunnel oxide of only 9.5 /spl Aring/ equivalent oxide thickness.