Nitrogen‐Doped Hollow Amorphous Carbon Spheres@Graphitic Shells Derived from Pitch: New Structure Leads to Robust Lithium Storage

Nitrogen‐doped mesoporous hollow carbon spheres (NHCS) consisting of hybridized amorphous and graphitic carbon were synthesized by chemical vapor deposition with pitch as raw material. Treatment with HNO₃ vapor was performed to incorporate oxygen‐containing groups on NHCS, and the resulting NHCS‐O showed excellent rate capacity, high reversible capacity, and excellent cycling stability when tested as the anode material in lithium‐ion batteries. The NHCS‐O electrode maintained a reversible specific capacity of 616 mAh g^?1 after 250 cycles at a current rate of 500 mA g^?1, which is an increase of 113 % compared to the pristine hollow carbon spheres. In addition, the NHCS‐O electrode exhibited a reversible capacity of 503 mAh g^?1 at a high current density of 1.5 A g^?1. The superior electrochemical performance of NHCS‐O can be attributed to the hybrid structure, high N and O contents, and rich surface defects.     

Formation of Triple‐Shelled Molybdenum–Polydopamine Hollow Spheres and Their Conversion into MoO2/Carbon Composite Hollow Spheres for Lithium‐Ion Batteries

Unique triple‐shelled Mo‐polydopamine (Mo‐PDA) hollow spheres are synthesized through a facile solvothermal process. A sequential self‐templating mechanism for the multi‐shell formation is proposed, and the number of shells can be adjusted by tuning the size of the Mo‐glycerate templates. These triple‐shelled Mo‐PDA hollow spheres can be converted to triple‐shelled MoO₂/carbon composite hollow spheres by thermal treatment. Owing to the unique multi‐shells and hollow interior, the as‐prepared MoO₂/carbon composite hollow spheres exhibit appealing performance as an anode material for lithium‐ion batteries, delivering a high capacity of ca. 580 mAh g^?1 at 0.5 A g^?1 with good rate capability and long cycle life.     

Template‐Free Synthesis of Nanorod‐Assembled Hierarchical Zn1−xMnxS Hollow Nanostructures with Enhanced Pseudocapacitive Properties

Mixed‐metal sulfide Zn_1?xMn_xS nanorod‐assembled hierarchical hollow spheres were synthesized by a template‐free solvothermal process based on Ostwald ripening. In the reaction system, glycerol plays a key role in the formation of Zn_xMn_1?xS hierarchical hollow structures by a quasi‐microemulsion‐template mechanism. When applied as capacitor electrode material, the hierarchical Zn_1?xMn_xS hollow spheres show excellent electrochemical performance. Specifically, Zn_0.25Mn_0.75S hollow spheres can deliver a high specific capacitance of 664 F g^?1 at a current rate of 1 A g^?1, which is almost five times of that of MnS under the same conditions and higher than those of previously reported single Mn‐based compounds.     

MnO2 Nanosheets Grown on Nitrogen‐Doped Hollow Carbon Shells as a High‐Performance Electrode for Asymmetric Supercapacitors

A hierarchical hollow hybrid composite, namely, MnO₂ nanosheets grown on nitrogen‐doped hollow carbon shells (NHCSs@MnO₂), was synthesized by a facile in situ growth process followed by calcination. The composite has a high surface area (251 m²g^?1) and mesopores (4.5 nm in diameter), which can efficiently facilitate transport during electrochemical cycling. Owing to the synergistic effect of NHCSs and MnO₂, the composite shows a high specific capacitance of 306 F g^?1, good rate capability, and an excellent cycling stability of 95.2 % after 5000 cycles at a high current density of 8 A g^?1. More importantly, an asymmetric supercapacitor (ASC) assembled by using NHCSs@MnO₂ and activated carbon as the positive and negative electrodes exhibits high specific capacitance (105.5 F g^?1 at 0.5 A g^?1 and 78.5 F g^?1 at 10 A g^?1) with excellent rate capability, achieves a maximum energy density of 43.9 Wh kg^?1 at a power density of 408 W kg^?1, and has high stability, whereby the ASC retains 81.4 % of its initial capacitance at a current density of 5 A g^?1 after 4000 cycles. Therefore, the NHCSs@MnO₂ electrode material is a promising candidate for future energy‐storage systems.     

Synthesis of Highly Uniform Molybdenum–Glycerate Spheres and Their Conversion into Hierarchical MoS2 Hollow Nanospheres for Lithium‐Ion Batteries

Highly uniform Mo–glycerate solid spheres are synthesized for the first time through a solvothermal process. The size of these Mo–glycerate spheres can be easily controlled in the range of 400–1000 nm by varying the water content in the mixed solvent. As a precursor, these Mo–glycerate solid spheres can be converted into hierarchical MoS₂ hollow nanospheres through a subsequent sulfidation reaction. Owing to the unique ultrathin subunits and hollow interior, the as‐prepared MoS₂ hollow nanospheres exhibit appealing performance as the anode material for lithium‐ion batteries. Impressively, these hierarchical structures deliver a high capacity of about 1100 mAh g^?1 at 0.5 A g^?1 with good rate retention and long cycle life.     

One‐Pot Fabrication of Hierarchical Nanosheet‐Based TiO2–Carbon Hollow Microspheres for Anode Materials of High‐Rate Lithium‐Ion Batteries

Hierarchical and hollow nanostructures have recently attracted considerable attention because of their fantastic architectures and tunable property for facile lithium ion insertion and good cycling stability. In this study, a one‐pot and unusual carving protocol is demonstrated for engineering hollow structures with a porous shell. Hierarchical TiO₂ hollow spheres with nanosheet‐assembled shells (TiO₂ NHS) were synthesized by the sequestration between the titanium source and 2,2′‐bipyridine‐5,5′‐dicarboxylic acid, and kinetically controlled etching in trifluoroacetic acid medium. In addition, annealing such porous nanostructures presents the advantage of imparting carbon‐doped functional performance to its counterpart under different atmospheres. Such highly porous structures endow very large specifics surface area of 404 m² g^?1 and 336 m² g^?1 for the as‐prepared and calcination under nitrogen gas. C/TiO₂ NHS has high capacity of 204 mA h g^?1 at 1 C and a reversible capacity of 105 mA h g^?1 at a high rate of 20 C, and exhibits good cycling stability and superior rate capability as an anode material for lithium‐ion batteries.     

Development of an Amperometric Biosensor for β‐N‐Oxalyl‐L‐α,β‐Diaminopropionic Acid (β‐ODAP)

An amperometric method for the determination of the neurotoxic amino acid β‐N‐oxalyl‐L ‐α,β‐diaminopropionic acid (β‐ODAP) using a screen printed carbon electrode (SPCE) is reported. The electrode material was bulk‐modified with manganese dioxide and used as a detector in flow injection analysis (FIA). The enzyme glutamate oxidase (GlOx) was immobilized in a Nafion‐film on the electrode surface. The performance of the biosensor was optimized using glutamate as an analyte. Optimum parameters were found as: operational potential 440 mV (vs. Ag/AgCl), flow rate 0.2 mL min^?1, and carrier composition 0.1 mol L^?1 phosphate buffer (pH 7.75). The same conditions were used for the determination of β‐ODAP. The signal was linear within the concentration range 53–855 μmol L^?1 glutamate and 195–1950 μmol L^?1 β‐ODAP. Detection limits (as 3σ value) for both analytes were 9.12 and 111.0 μmol L^?1, respectively, with corresponding relative standard deviations of 3.3 and 4.5%. The biosensor retained more than 73% of its activity after 40 days of on‐line use.     

A Multi‐Wall Sn/SnO2@Carbon Hollow Nanofiber Anode Material for High‐Rate and Long‐Life Lithium‐Ion Batteries

Multi‐wall Sn/SnO₂@carbon hollow nanofibers evolved from SnO₂ nanofibers are designed and programable synthesized by electrospinning, polypyrrole coating, and annealing reduction. The synthesized hollow nanofibers have a special wire‐in‐double‐wall‐tube structure with larger specific surface area and abundant inner spaces, which can provide effective contacting area of electrolyte with electrode materials and more active sites for redox reaction. It shows excellent cycling stability by virtue of effectively alleviating pulverization of tin‐based electrode materials caused by volume expansion. Even after 2000 cycles, the wire‐in‐double‐wall‐tube Sn/SnO₂@carbon nanofibers exhibit a high specific capacity of 986.3 mAh g^?1 (1 A g^?1) and still maintains 508.2 mAh g^?1 at high current density of 5 A g^?1. This outstanding electrochemical performance suggests the multi‐wall Sn/SnO₂@ carbon hollow nanofibers are great promising for high performance energy storage systems.     

Construction of CoO/Co‐Cu‐S Hierarchical Tubular Heterostructures for Hybrid Supercapacitors

Hierarchical hollow structures for electrode materials of supercapacitors could enlarge the surface area, accelerate the transport of ions and electrons, and accommodate volume expansion during cycling. Besides, construction of heterostructures would enhance the internal electric fields to regulate the electronic structures. All these features of hierarchical hollow heterostructures are beneficial for promoting the electrochemical properties and stability of electrode materials for high‐performance supercapacitors. Herein, CoO/Co‐Cu‐S hierarchical tubular heterostructures (HTHSs) composed of nanoneedles are prepared by an efficient multi‐step approach. The optimized sample exhibits a high specific capacity of 320 mAh g^?1 (2300 F g^?1) at 2.0 A g^?1 and outstanding cycling stability with 96.5 % of the initial capacity retained after 5000 cycles at 10 A g^?1. Moreover, an all‐solid‐state hybrid supercapacitor (HSC) constructed with the CoO/Co‐Cu‐S and actived carbon shows a stable and high energy density of 90.7 Wh kg^?1 at a power density of 800 W kg^?1.     

High‐Performance Lithium‐Ion Anodes with Hierarchically Assembled Single‐Crystal SnO2 Nanoflake Spheres

A large‐scale hierarchical assembly route is reported for the formation of SnO₂ on the nanoscale that contains rigid and robust spheres with irregular channels for rapid access of Li ions into the hierarchically structured interiors. Large volume changes during the process of Li insertion and extraction are accommodated by the SnO₂ nanoflake spheres’ internal porosity. The hierarchical SnO₂ nanoflake spheres exhibit good lithium storage properties with high capacity and long‐lasting performance when used as lithium‐ion anodes. A reversible capacity of 517 mA h g^?1, still greater than the theoretical capacity of graphite (372 mA h g^?1), after 50 charge–discharge cycles is attained. Meanwhile, the synthesis process is simple, inexpensive, safe, and broadly applicable, providing new avenues for the rational engineering of electrode materials with enhanced conductivity and power.     

Template‐Free Synthesis of Hierarchical Vanadium‐Glycolate Hollow Microspheres and Their Conversion to V2O5 with Improved Lithium Storage Capability

Nanosheet‐assembled hierarchical V₂O₅ hollow microspheres are successfully obtained from V‐glycolate precursor hollow microspheres, which in turn are synthesized by a simple template‐free solvothermal method. The structural evolution of the V‐glycolate hollow microspheres has been studied and explained by the inside‐out Ostwald‐ripening mechanism. The surface morphologies of the hollow microspheres can be controlled by varying the mixture solution and the solvothermal reaction time. After calcination in air, hierarchical V₂O₅ hollow microspheres with a high surface area of 70 m² g^?1 can be obtained and the structure is well preserved. When evaluated as cathode materials for lithium‐ion batteries, the as‐prepared hierarchical V₂O₅ hollow spheres deliver a specific discharge capacity of 144 mA h g^?1 at a current density of 100 mA g^?1, which is very close to the theoretical capacity (147 mA h g^?1) for one Li⁺ insertion per V₂O₅. In addition, excellent rate capability and cycling stability are observed, suggesting their promising use in lithium‐ion batteries.     

Hierarchical Metal Sulfide/Carbon Spheres: A Generalized Synthesis and High Sodium‐Storage Performance

The development of suitable anode materials is far from satisfactory and is a major scientific challenge for a competitive sodium‐ion battery technology. Metal sulfides have demonstrated encouraging results, but still suffer from sluggish kinetics and severe capacity decay associated with the phase change. Herein we show that rational electrode design, that is, building efficient electron/ion mixed‐conducting networks, can overcome the problems resulting from conversion reactions. A general strategy for the preparation of hierarchical carbon‐coated metal sulfide (MS?C) spheres through thermal sulfurization of metal glycerate has been developed. We demonstrate the concept by synthesizing highly uniform hierarchical carbon coated vanadium sulfide (V₂S₃?C) spheres, which exhibit a highly reversibly sodium storage capacity of 777 mAh g^?1 at 100 mA g^?1, excellent rate capability (410 mAh g^?1 at 4000 mA g^?1), and impressive cycling ability.     

Ultrahigh Energy Density Realized by a Single‐Layer β‐Co(OH)2 All‐Solid‐State Asymmetric Supercapacitor

A conceptually new all‐solid‐state asymmetric supercapacitor based on atomically thin sheets is presented which offers the opportunity to optimize supercapacitor properties on an atomic level. As a prototype, β‐Co(OH)₂ single layers with five‐atoms layer thickness were synthesized through an oriented‐attachment strategy. The increased density‐of‐states and 100 % exposed hydrogen atoms endow the β‐Co(OH)₂ single‐layers‐based electrode with a large capacitance of 2028 F g^?1. The corresponding all‐solid‐state asymmetric supercapacitor achieves a high cell voltage of 1.8 V and an exceptional energy density of 98.9 Wh kg^?1 at an ultrahigh power density of 17 981 W kg^?1. Also, this integrated nanodevice exhibits excellent cyclability with 93.2 % capacitance retention after 10 000 cycles, holding great promise for constructing high‐energy storage nanodevices.     

One‐Step Pyro‐Synthesis of a Nanostructured Mn3O4/C Electrode with Long Cycle Stability for Rechargeable Lithium‐Ion Batteries

A nanostructured Mn₃O₄/C electrode was prepared by a one‐step polyol‐assisted pyro‐synthesis without any post‐heat treatments. The as‐prepared Mn₃O₄/C revealed nanostructured morphology comprised of secondary aggregates formed from carbon‐coated primary particles of average diameters ranging between 20 and 40 nm, as evidenced from the electron microscopy studies. The N₂ adsorption studies reveal a hierarchical porous feature in the nanostructured electrode. The nanostructured morphology appears to be related to the present rapid combustion strategy. The nanostructured porous Mn₃O₄/C electrode demonstrated impressive electrode properties with reversible capacities of 666 mAh g^?1 at a current density of 33 mA g^?1, good capacity retentions (1141 mAh g^?1 with 100 % Coulombic efficiencies at the 100^th cycle), and rate capabilities (307 and 202 mAh g^?1 at 528 and 1056 mA g^?1, respectively) when tested as an anode for lithium‐ion battery applications.     

Highly Stereoselective β‐Mannopyranosylation via the 1‐α‐Glycosyloxy‐isochromenylium‐4‐gold(I) Intermediates

While the gold(I)‐catalyzed glycosylation reaction with 4,6‐O‐benzylidene tethered mannosyl ortho‐alkynylbenzoates as donors falls squarely into the category of the Crich‐type β‐selective mannosylation when Ph₃PAuOTf is used as the catalyst, in that the mannosyl α‐triflates are invoked, replacement of the ^?OTf in the gold(I) complex with less nucleophilic counter anions (i.e., ^?NTf₂, ^?SbF₆, ^?BF₄, and ^?BAr₄^F) leads to complete loss of β‐selectivity with the mannosyl ortho‐alkynylbenzoate β‐donors. Nevertheless, with the α‐donors, the mannosylation reactions under the catalysis of Ph₃PAuBAr₄^F (BAr₄^F=tetrakis[3,5‐bis(trifluoromethyl)phenyl]borate) are especially highly β‐selective and accommodate a broad scope of substrates; these include glycosylation with mannosyl donors installed with a bulky TBS group at O3, donors bearing 4,6‐di‐O‐benzoyl groups, and acceptors known as sterically unmatched or hindered. For the ortho‐alkynylbenzoate β‐donors, an anomerization and glycosylation sequence can also ensure the highly β‐selective mannosylation. The 1‐α‐mannosyloxy‐isochromenylium‐4‐gold(I) complex ( Cα ), readily generated upon activation of the α‐mannosyl ortho‐alkynylbenzoate ( 1 α ) with Ph₃PAuBAr₄^F at ?35 °C, was well characterized by NMR spectroscopy; the occurrence of this species accounts for the high β‐selectivity in the present mannosylation.     

Self‐Template Synthesis of Hybrid Porous Co3O4–CeO2 Hollow Polyhedrons for High‐Performance Supercapacitors

In this work, hybrid porous Co₃O₄–CeO₂ hollow polyhedrons have been successfully obtained via a simple cation‐exchange route followed by heat treatment. In the synthesis process, ZIF‐67 polyhedron frameworks are firstly prepared, which not only serve as a host for the exchanged Ce3⁺ ions but also act as the template for the synthesis of hybrid porous Co₃O₄–CeO₂ hollow polyhedrons. When utilized as electrode materials for supercapacitors, the hybrid porous Co₃O₄–CeO₂ hollow polyhedrons delivered a large specific capacitance of 1288.3 F g^?1 at 2.5 A g^?1 and a remarkable long lifespan cycling stability (<3.3 % loss after 6000 cycles). Furthermore, an asymmetric supercapacitor (ASC) device based on hybrid porous Co₃O₄–CeO₂ hollow polyhedrons was assembled. The ASC device possesses an energy density of 54.9 W h kg^?1, which can be retained to 44.2 W h kg^?1 even at a power density of 5100 W kg^?1, indicating its promising application in electrochemical energy storage. More importantly, we believe that the present route is a simple and versatile strategy for the preparation of other hybrid metal oxides with desired structures, chemical compositions and applications.     

Measurements of the kinetics of the OH + α‐pinene and OH + β‐pinene reactions at low pressure

The rate constants for the OH + α‐pinene and OH + β‐pinene reactions have been measured in 5 Torr of He using discharge‐flow systems coupled with resonance fluorescence and laser‐induced fluorescence detection of the OH radical. At room temperature, the measured effective bimolecular rate constant for the OH + α‐pinene reaction was (6.08 ± 0.24) × 10^?11 cm³ molecule^?1 s^?1. These results are in excellent agreement with previous absolute measurements of this rate constant, but are approximately 13% greater than the value currently recommended for atmospheric modeling. The measured effective bimolecular rate constant for the OH + β‐pinene reaction at room temperature was (7.72 ± 0.44) × 10^?11 cm³ molecule^?1 s^?1, in excellent agreement with previous measurements and current recommendations. Above 300 K, the effective bimolecular rate constants for these reactions display a negative temperature dependence suggesting that OH addition dominates the reaction mechanisms under these conditions. This negative temperature dependence is larger than that observed at higher pressures. The measured rate constants for the OH + α‐pinene and OH + β‐pinene reactions are in good agreement with established reactivity trends relating the rate constant for OH + alkene reactions with the ionization potential of the alkene when ab initio calculated energies for the highest occupied molecular orbital are used as surrogates for the ionization potentials for α‐ and β‐pinene. © 2002 Wiley Periodicals, Inc. Int J Chem Kinet 34: 300–308, 2002     

High Performance Non‐enzymatic Glucose Sensor Based on One‐Step Electrodeposited Nickel Sulfide

Nanostructured NiS thin film was prepared by a one‐step electrodeposition method and the structural, morphological characteristics of the as‐prepared films were analyzed by X‐ray diffractometry (XRD), field emission scanning electron microscopy (FESEM) and energy dispersive X‐ray analysis (EDAX). The electrocatalytic activity of NiS thin film towards glucose oxidation was investigated by fabricating a non‐enzymatic glucose sensor and the sensor performance was studied by cyclic voltammetry (CV) and amperometry. The fabricated sensor showed excellent sensitivity and low detection limit with values of 7.43 μA μM ^?1 cm^?2 and 0.32 μM , respectively, and a response time of <8 s.     

Hydrothermal Synthesis of Nickel Oxide Nanosheets for Lithium‐Ion Batteries and Supercapacitors with Excellent Performance

Nickel oxide nanosheets have been successfully synthesized by a facile ethylene glycol mediated hydrothermal method. The morphology and crystal structure of the nickel oxide nanosheets were characterized by X‐ray diffraction, field‐emission SEM, and TEM. When applied as electrode materials for lithium‐ion batteries and supercapacitors, nickel oxide nanosheets exhibited a high, reversible lithium storage capacity of 1193 mA h g^?1 at a current density of 500 mA g^?1, an enhanced rate capability, and good cycling stability. Nickel oxide nanosheets also demonstrated a superior specific capacitance of 999 F g^?1 at a current density of 20 A g^?1 in supercapacitors.     

Dual‐Confined Sulfur Nanoparticles Encapsulated in Hollow TiO2 Spheres Wrapped with Graphene for Lithium–Sulfur Batteries

Lithium–sulfur (Li?S) batteries are attractive owing to their higher energy density and lower cost compared with the universally used lithium‐ion batteries (LIBs), but there are some problems that stop their practical use, such as low utilization and rapid capacity‐fading of the sulfur cathode, which is mainly caused by the shuttle effect, and the uncontrollable deposition of lithium sulfide species. Herein, we report the design and fabrication of dual‐confined sulfur nanoparticles that were encapsulated inside hollow TiO₂ spheres; the encapsulated nanoparticles were prepared by a facile hydrolysis process combined with acid etching, followed by “wrapping” with graphene (G?TiO₂@S). In this unique composite architecture, the hollow TiO₂ spheres acted as effective sulfur carriers by confining the polysulfides and buffering volume changes during the charge‐discharge processes by means of physical force from the hollow spheres and chemical binding between TiO₂ and the polysulfides. Moreover, the graphene‐wrapped skin provided an effective 3D conductive network to improve the electronic conductivity of the sulfur cathode and, at the same time, to further suppress the dissolution of the polysulfides. As results, the G?TiO₂@S hybrids exhibited a high and stable discharge capacity of up to 853.4 mA h g^?1 over 200 cycles at 0.5 C (1 C=1675 mA g^?1) and an excellent rate capability of 675 mA h g^?1 at a current rate of 2 C; thus, G?TiO₂@S holds great promise as a cathode material for Li?S batteries.