Thermodynamics of solutions of cyclic polymethylene ester oligomers in p‐dioxane and chloroform

Differential vapor pressures were measured for mixtures of two cyclic polymethylene ester oligomers in p‐dioxane and chloroform at 25, 30, 35, and 40 °C at five different concentrations ranging from 1 to 20 wt %. The Flory–Huggins interaction parameter (χ) as well as Leonard's interaction parameter (χ′) for flexible and semiflexible rings were calculated and compared to one another. A new method for the estimation of the number of segments of a cyclic polymer is proposed that allows Leonard's equations to be applied correctly to a particular cyclic compound. Consistent differences between χ and χ′ were observed for all studied mixtures, and the differences became smaller if the cyclic oligomers were considered semiflexible. Interestingly, the enthalpic parameter (κ) deduced from values of χ and χ′ did not differ within their uncertainties. This supports the prediction that mixing cyclic polymer compared to its linear counterpart is mainly due to a molecular configurational entropy difference and that this difference should become less pronounced as the cyclic compound becomes larger. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 443–455, 2000     

Ring‐opening polymerization of the cyclic dimer of poly(trimethylene terephthalate)

Poly(trimethylene terephthalate) (PTT) was prepared by the ring‐opening polymerization of its cyclic dimer. Antimony(III) oxide, titanium(IV) butoxide, dibutyltin oxide, and titanium(IV) isopropoxide were used as catalysts. Among the catalysts, titanium(IV) butoxide was the most effective for the same reaction conditions. A weight‐average molecular weight of 63,500 g/mol was obtained from ring‐opening poly merization at 265 °C for 2 h in the presence of 0.5 mol % titanium(IV) butoxide. The PTTs obtained from the polymerization catalyzed with increasing amounts of antimony(III) oxide showed increasing weight‐average molecular weights and reaction conversions. When 1 mol % antimony(III) oxide was used, the weight‐average molecular weight was 32,000 g/mol and the conversion was 82% after 1 h of polymerization at 265 °C. In the case of the polymer catalyzed by titanium(IV) butoxide under the same conditions, the weight‐average molecular weight and conversion were 40,000 g/mol and 77% when 0.25 mol % was used, whereas 0.5 mol % catalyst produced a weight‐average molecular weight of 27,000 g/mol and a conversion of 95%. To get an acceptable molecular weight and relatively high reaction conversion, a catalyst concentration of at least 0.5 mol % was found to be necessary, in contrast to conventional condensation polymerizations, which require only about one‐tenth of this amount of the catalyst. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 6801–6809, 2006     

Effect of chain architecture on the phase transition of star and cyclic poly(N‐isopropylacrylamide) in water

The heat‐induced phase transition of aqueous solutions of Poly(N‐isopropylacrylamide) (PNIPAM) in water is examined for a four‐arm PNIPAM star (s‐PNIPAM), a cyclic PNIPAM (c‐PNIPAM), and their linear counterparts (l‐PNIPAM) in the case of polymers (1.0 g L^?1) of 12,700 g mol^?1 < M_n < 14,700 g mol^?1. Investigations by turbidity, high‐sensitivity differential scanning calorimetry (HS‐DSC), and light scattering (LS) indicate that the polymer architecture has a strong effect on the cloud point (T_c: decrease for s‐PNIPAM; increase for c‐PNIPAM), the phase transition enthalpy change (ΔH decrease for s‐PNIPAM and c‐PNIPAM), and the hydrodynamic radius of the aggregates formed above T_c (R_H: c‐PNIPAM < s‐PNIPAM < l‐PNIPAM). The properties of s‐PNIPAM are compared with those of previously reported PNIPAM star polymers (3 to 52 arms). The overall observations are described in terms of the arm molecular weight and the local chain density in the vicinity of the core of the star, by analogy with the model developed for PNIPAM brushes on nanoparticles or planar surfaces. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 2059–2068.     

Synthesis and ring‐opening polymerization of co‐cyclic(aromatic aliphatic disulfide) oligomers

An effective approach was presented for the synthesis of co‐cyclic(aromatic aliphatic disulfide) oligomers by catalytic oxidation of aromatic and aliphatic dithiols with oxygen in the presence of a copper‐amine catalyst. The aromatic dithiols can be 4,4′‐oxybis(benzenethiol), 4,4′‐diphenyl dithiol, 4,4′‐diphenylsulfone dithiol. The aliphatic dithiols can be 1,2‐ethanedithiol, 2,3‐butanedithiol, 1,6‐hexane dithiol. The co‐cyclic(aromatic aliphatic disulfide) oligomers were characterized by gradient HPLC, MALDI‐TOF‐MS, GPC, ¹H‐NMR, TGA, and DSC techniques. The glass transition temperatures of these co‐cyclics ranged from ?11.3 to 56.6°C. In general, these co‐cyclic(aromatic aliphatic disulfide) oligomers are soluble in common organic solvents, such as CHCl₃, THF, DMF, DMAc. These co‐cyclic oligomers readily underwent free radical ring‐opening polymerization in the melt at 180°C, producing linear, tough and high molecular weight poly(aromatic aliphatic disulfide)s. The glass transition temperatures of these polymers ranged from ?3.7 to 107.8°C that are higher than those of corresponding co‐cyclics. Copyright © 2003 John Wiley & Sons, Ltd.     

Molecular modeling of poly(p‐phenylenevinylene): Synthesis and photophysical properties of oligomers

A series of oligo(phenylenevinylene)s (OPVs) of different lengths containing aldehyde and dialdehyde groups on the ends were synthesized and characterized. Their photophysical properties were also investigated via ultraviolet–visible, steady‐state, and time‐resolved fluorescence spectra. The results indicated that the absorption maximum, radiative rate constant, and excitation maximum of an OPVnCHO oligomer series (where n represents the oligomeric length) showed linear relationships with the reciprocal number of conjugated units. Similarly, the absorption maximum and emission lifetime of the oligomers of an OPVn–2CHO series showed linear relationships with the reciprocal number of conjugated units. The dependence of the fluorescence intensities of the OPVs on the concentration of the quencher C₆₀ was evaluated. Apparently, upon photoexcitation, the OPVs underwent significant fluorescence quenching. The results for different OPV derivatives and a quenching mechanistic discussion showed that the static quenching contribution was indeed responsible for the significant upward curvature. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 911–924, 2007     

Branched versus linear oligo(dimethylsiloxane): Differences in their thermodynamic interaction with solvents

The thermodynamic behavior of linear and of branched oligo(dimethylsiloxane) (O‐DMS) solutions was studied by means of vapor pressure measurements and vapor pressure osmometry at different temperatures for the thermodynamically favorable solvent THF. The branched material required for that purpose was synthesized and afterwards fractionated by means of the single solvent acetone to eliminate components of low degrees of branching. The Flory‐Huggins interaction parameters, χ, for the systems THF/O‐DMS as a function of composition pass a minimum at all temperatures (25, 40, and 60 °C) in the case of the branched material. For the unbranched oligomer such a minimum is only observed at 60 °C. At 40 °C the results are ambigous whereas the dependence is definitely linear at 25 °C. This exceptional behavior of the linear product at the latter temperature is tentatively attributed to the formation of favorable orientational order in the pure state under these conditions. At high oligomer concentrations THF interacts more favorably with the branched material, however, this preference is reversed upon dilution. All measured composition dependencies of χ can be modeled quantitatively by an approach accounting for chain connectivity and for the ability of the oligomers to change their conformation upon dilution. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1309–1318, 2010     

Melt‐processable blends of ionic poly(p‐phenylene terephthalamide) and poly(4‐vinylpyridine): Relaxation behavior

Melt‐processable blends were prepared from rigid molecules of an ionically modified poly(p‐phenylene terephthalamide) (PPTA) and flexible‐coil molecules of poly(4‐vinylpyridine) (PVP). Dynamic mechanical analyses of blends with 50% or more of the ionic PPTA component revealed the presence of two distinct phases. The glass‐transition temperature of the more stable, ionic PPTA‐rich phase increased linearly with the ionic PPTA content. The second phase present in these blends was an ionic PPTA‐poor, or a PVP‐rich, phase. For this phase, a reasonably good fit of the data, showing the glass‐transition temperature as a function of the ionic PPTA content, was achieved between the results of this study and the reported results of previous investigation of molecular composites of the same two components with ionic PPTA contents of 15 wt % or less. The possible influence of annealing on the blend structure of a 90/10 blend of ionic PPTA and PVP was examined. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1468–1475, 2003     

Evaluation of the interaction parameter for poly(ε‐caprolactone)/poly(styrene‐co‐acrylonitrile) blends

In this article, the miscibility of poly(ε‐caprolactone) (PCL) with poly(styrene‐co‐acrylonitrile) (SAN) containing 25 wt % of acrylonitrile is studied from both a qualitative and a quantitative point of view. The evidences coming from thermal analysis (differential scanning calorimetry) demonstrate that PCL and SAN are miscible in the whole range of composition. The Flory interaction parameter χ_1,2 was calculated by the Patterson approximation and the melting point depression of the crystalline phase in the blends; in both cases, negative values of χ_1,2 were found, confirming that the system is miscible. The interaction parameter evaluated within the framework of the mean field theory demonstrates that the miscibility of PCL/SAN blends is due to the repulsive interaction between the styrene and acrylonitrile segments in SAN. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Synthesis,characterization, and ring opening polymerization of poly(1,4‐cyclohexylenedimethylene terephthalate) cyclic oligomers

Cyclic oligomers of poly(1,4‐cyclohexylenedimethylene terephthalate) (PCT) were prepared by reaction of 1,4‐cyclohexanedimethanol (CHDM) with terephthaloyl chloride under diluted conditions and separated from the linear products by silica gel column at a yield of 23.7 wt %. Cyclic dimer, trimer, tetramer, pentamer, and hexamer were further separated by high performance liquid chromatography, and found to constitute 98% of the cyclics mixtures. The structures of PCT cyclics were confirmed by means of mass spectrometry, Fourier transform infrared, and ¹H NMR analysis. A series of experiments were carried out to study the effects of catalysts and cis/trans configuration of isomers of CHDM on the yield of cyclic oligomers. Ring opening polymerization of the cyclic oligomers was carried out by heating the sample mixtures at 310 °C for 30 min in the presence of antimony oxide. Polymerization was confirmed by inherent viscosity changes and infrared spectra of the resulting polyesters. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 1828–1833, 2000     

Prediction of miscibility regions in ternary blends of poly(styrene-stat-acrylonitrile), poly(acrylonitrile-stat-methyl methacrylate), and poly(styrene-stat-methyl methacrylate)

The miscibilities of ternary copolymer blends prepared from poly(styrene-stat-acrylonitrile), poly(styrene-stat-methyl methacrylate), and poly(methyl methacrylate-stat-acrylonitrile) were predicted by calculating the interaction parameter, χ_blend, for various blend combinations, from the corresponding binary segmental interaction parameters estimated from previous work. Binodal and spinodal curves were calculated using the Flory-Huggins theory and it was observed that the most accurate estimate of the boundary between miscible and immiscible blends was given by the spinodal. It has also been demonstrated that in some of the ternary blends with fixed copolymer compositions the miscibility of the blend can be altered by changing the ratio of the three components in the mixture. Conditions for miscibility in this ternary system, and possibly a general feature of all such systems, are (a) that at least two of the binary interaction parameters χ_ij are less than the critical value χ_crit, while the third should not be too much larger, that is, one of the copolymers may act as a compatibilizer for the other two copolymers, (b) that the difference Δχ = /χ₁₂ ? χ₁₃/ is small. © 1992 John Wiley & Sons, Inc.     

Isolation and identification of cyclic oligomers of the poly(ethylene terephthalate)–poly(ethylene isophthalate) copolymer

New cyclic oligomers of the copolymer of poly(ethylene terephthalate) (PET) and poly(ethylene isophthalate) (PEI) were isolated and identified. A condensation polymerization was carried out at a high temperature, and the solid‐state polymerization that followed yielded the high molecular weight polymer. The oligomers were extracted from the high molecular weight PET–PEI copolymer and separated with preparative high performance liquid chromatography techniques. Their chemical structures and properties were analyzed and determined by ¹H NMR, differential scanning calorimetry, and mass spectroscopy. The oligomers observed at early retention times were a cyclic dimer and cyclic trimers and consisted of [GT]₃, [GI]₂, [GI]₃, [GT]₂[GI]₁, and [GT]₁[GI]₂. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 881–889, 2003     

Morphology of poly(p‐oxybenzoyl) prepared in perfluoropolyether

Solvent effect on the morphology of poly(p‐oxybenzoyl) (POB) prepared by the reaction‐induced phase separation of oligomers was examined by the polymerization of p‐acetoxybenzoic acid in perfluoropolyether Aflunox^TM (AFL2507 and AFL606). Polymerization was carried out at 320°C for 6 hr. POB microspheres were formed in AFL2507 by the liquid–liquid phase separation of oligomers due to the low miscibility of oligomers in AFL2507. The molecular weight of the solvent influenced the morphology, and the polymerization in AFL606 of which the molecular weight was lower than AFL2507 yielded whiskers formed by crystallization of oligomers induced by the increase in miscibility compared with that in AFL2507. The solvent structure and its molecular weight influenced the miscibility of oligomers and ultimately controlled the morphology from whisker to microsphere. Copyright © 2004 John Wiley & Sons, Ltd.     

Synthesis and ring‐opening polymerization of macrocyclic (arylene thioether ketone) oligomers

Macrocyclic (arylene thioether ketone) oligomers together with a linear poly(phenylene sulfide ketone) oligomer were synthesized by a one‐step reaction. The macrocycles and linear oligomer were fully characterized by ¹³C‐NMR, H‐NMR, matrix assisted laser desorption/ionization time‐of‐flight mass spectrometry (MALDI‐TOF‐MS), differential scanning calorimetry (DSC) and FT‐IR. Uncatalyzed, simultaneously ring‐opening polymerization (ROP) of the macrocycles and the mixture of macrocycles and linear oligomer were carried out under dynamic heating conditions. The ROP temperature of the macrocycles decreased upon mixing it with the linear oligomer. The ROP conditions and mechanism were investigated and discussed. The macrocycles and their mixture show potential applications in high temperature adhesives and sealants. Copyright © 2006 John Wiley & Sons, Ltd.     

Self‐assembled complexes of poly(acrylic acid) and poly(styrene)‐block‐poly(4‐vinyl pyridine)

Polymer complexes were prepared from high molecular weight poly(acrylic acid) (PAA) and poly(styrene)‐block‐poly(4‐vinyl pyridine) (PS‐b‐P4VP) in dimethyl formamide (DMF). The hydrogen bonding interactions, phase behavior, and morphology of the complexes were investigated using Fourier transform infrared (FTIR) spectroscopy, differential scanning calorimetry (DSC), dynamic light scattering (DLS), atomic force microscopy (AFM), and transmission electron microscopy (TEM). In this A‐b‐B/C type block copolymer/homopolymer system, P4VP block of the block copolymer has strong intermolecular interaction with PAA which led to the formation of nanostructured micelles at various PAA concentrations. The pure PS‐b‐P4VP block copolymer showed a cylindrical rodlike morphology. Spherical micelles were observed in the complexes and the size of the micelles increased with increasing PAA concentration. The micelles are composed of hydrogen‐bonded PAA/P4VP core and non‐bonded PS corona. Finally, a model was proposed to explain the microphase morphology of complex based on the experimental results obtained. The selective swelling of the PS‐b‐P4VP block copolymer by PAA resulted in the formation of different micelles. © 2009 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 47: 1192–1202, 2009     

Miscibility and interactions in blends of two proton‐donating polymers: Poly(acrylic acid)/poly(p‐vinylphenol) blends

Blends of poly(acrylic acid) (PAA) and poly(p‐vinylphenol) (PVPh) were prepared from N,N‐dimethylformamide (DMF) and ethanol solutions. The DMF‐cast blends exhibited single T_g's, as shown by modulated differential scanning calorimetry, whereas the ethanol‐cast blends had double T_g's. Fourier transform infrared spectroscopy showed that there was a specific interaction between PAA and PVPh in the DMF‐cast blends. The single‐T_g blends cast from DMF showed single‐exponential decay behavior for the proton spin–lattice relaxation in both the laboratory frame and the rotating frame, indicating that the two polymers mixed intimately on a scale of 2–3 nm. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 789–796, 2003     

Synthesis and characterization of main‐chain NLO oligomers and polymer that contain 4‐dialkylamino‐ 4′‐(alkylsulfonyl)azobenzene chromophores

An ω‐amino carboxylic acid monomer that contained a nonlinear optical (NLO) chromophore was prepared by a convergent synthesis. Strategies for selective protection/deprotection of the amino and carboxylic acid functionalities were developed. The protected monomer, 4‐[N‐(4‐benzyloxycarbonyl)butyl‐N‐methylamino]‐4′‐[2″,5″‐bis(decyloxy)‐4″‐(phthalimidomethyl)benzylsulfonyl]azobenzene, could be deprotected selectively or sequentially to give HOOC‐monomer‐N‐phthaloyl, benzyl‐OOC‐monomer‐NH₂, or HOOC‐monomer‐NH₂. Sequential synthesis was performed to yield main‐chain NLO dimers and tetramers. This was accomplished by selective deprotection and dicyclohexylcarbodiimide coupling. The HOOC‐monomer‐NH₂ was polymerized by treatment with diphenylphosphoryl azide to give a main‐chain NLO polyamide. The monomer, dimer, tetramer, and polymer NLO materials were characterized by ¹H, ¹³C, IR, and UV–visible spectroscopy as well as by gel permeation chromatography, differential scanning calorimetry, and elemental analysis. The NLO properties of these materials were measured. Thin films of the oligomers and polymer were prepared by spin casting on indium‐tin oxide coated glass. The second‐order NLO properties of the oligomers and polymer thin films were studied by in situ corona poling/second‐harmonic generation and attenuated total reflection methods. The optimal poling temperatures were significantly lower than the melting temperatures or glass‐transition temperatures of the oligomers and polymer. The poling efficiency increased in the following order: monomer, oligomers, and polymer. An electro‐optic coefficient of 4 pm/V at 1.06 μm was obtained for the polymer. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 38: 546–559, 2000     

Miscibility of poly(styrene‐co‐butyl acrylate) with poly(ethyl methacrylate): Existence of both UCST and LCST

A miscible homopolymer–copolymer pair viz., poly(ethyl methacrylate) (PEMA)–poly(styrene‐co‐butyl acrylate) (SBA) is reported. The miscibility has been studied using differential scanning calorimetry. While 1 : 1 (w/w) blends with SBA containing 23 and 34 wt % styrene (ST) become miscible only above 225 and 185 °C respectively indicating existence of UCST, those with SBA containing 63 wt % ST is miscible at the lowest mixing temperature (i.e., T_g's) but become immiscible when heated at ca 250 °C indicating the existence of LCST. Miscibility for blends with SBA of still higher ST content could not be determined by this method because of the closeness of the T_g's of the components. The miscibility window at 230 °C refers to the two copolymer compositions of which one with the lower ST content is near the UCST, while the other with the higher ST content is near the LCST. Using these compositions and the mean field theory binary interaction parameters between the monomer residues have been calculated. The values are χ_ST‐BA = 0.087 and χ_EMA‐BA = 0.013 at 230 °C. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 369–375, 2000     

Miscibility and crystallization behavior in blends of poly(methyl methacrylate) and poly(vinylidene fluoride): Effect of star‐like topology of poly(methyl methacrylate) chain

A tetraarmed star‐shaped poly(methyl methacrylate) (s‐PMMA) was synthesized via atom transfer radical polymerization with 2‐bromoisobutyryl pentaerythritol as the initiator. For comparison, a linear PMMA with the identical molecular weight (l‐PMMA) was also prepared. The blends of the two PMMA samples with poly (vinylidene fluoride) (PVDF) were prepared to investigate the effect of macromolecular topological structure on miscibility and crystallization behavior of the binary blends. The behavior of single and composition‐dependent glass transition temperatures was found for the blends of s‐PMMA with PVDF, indicating that the s‐PMMA is miscible with PVDF in the amorphous state just like l‐PMMA. The miscibility was further evidenced by the depression of equilibrium melting points. It is found that the blends of s‐PMMA and PVDF displayed the larger k value of Gordon–Taylor equation than the blends of l‐PMMA and PVDF blends. According to the depression of equilibrium melting points, the intermolecular parameters for the two blends were estimated. It is noted that the s‐PMMA/PVDF blends displayed the lower interaction parameter than l‐PMMA/PVDF blends. The isothermal crystallization kinetics shows that the crystallization of PVDF in the blends containing s‐PMMA is faster than that in the blends containing the linear PMMA. The surface‐folding free energy of PVDF chains in the blends containing s‐PMMA is significantly lower than those in the blends containing l‐PMMA. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 2580–2593, 2007     

Crystallization and morphology of poly(vinylidene fluoride)/poly(3‐hydroxybutyrate) blends. III. Crystallization and phase diagram by differential scanning calorimetry

The crystallization of poly(vinylidene fluoride) (PVDF)/poly(3‐hydroxybutyrate) (PHB) blends was studied with differential scanning calorimetry, from which the phase diagram was derived. Strong miscibility was underlined by the large negative Flory–Huggins interaction parameter (?0.25). The crystallization of the blend components differed remarkably. Whereas PVDF always crystallized in the surroundings of a homogeneous melt, PHB crystallized in a volume that was confined by the already existing PVDF spherulites, partly in their surroundings and partly inside. Under isothermal conditions, PVDF usually crystallized regularly in three dimensions with predominant quench‐induced athermal nucleation. The Avrami exponent for PVDF dendritic spherulitic growth was, however, distinctly smaller than that for compact growth, and this revealed the two‐dimensional lamellar growth inside. This deviation from ideal Avrami behavior was caused by the development of compositional inhomogeneities as PVDF crystallization proceeded, and this decelerated the kinetics. PHB crystallized three‐dimensionally with mixed thermal and athermal nucleation outside the PVDF spherulites. Inside the PVDF spherulites, PHB crystallization proceeded in a fibrillar fashion with thermal nucleation; the growth front followed the amorphous paths inside the dendritic PVDF spherulites. The crystallization was faster than that in the melt of uncrystallized PVDF. Solid PVDF acts possibly heterogeneously nucleating, accelerating PHB crystallization. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 287–295, 2005