白光LED用新型红色荧光粉KCaY(MoO4)3:Eu3+的制备及发光性能

采用高温固相法制备了新型KCaY1-x(Mo04)3:Eux红色荧光粉.利用X射线衍射(XRD)、扫描电镜(SEM)和荧光光谱技术对粉体进行了结构、表面形貌和发光性能表征.结果表明:该系列荧光粉均为四方晶系的白钨矿结构,能够被近紫外光(394 nm)和蓝光(465 nm)有效激发,产生Eu3的5 D0→7 F2特征跃迁红光发射(613 nm).对这种荧光粉作后处理,可改善其表面形貌,并提高其发光强度.该系列荧光粉在394,465 nm的吸收与目前广泛应用的近紫外和蓝光LED芯片的输出波长相匹配.因此这种荧光粉是一种可能应用在白光LED上的红色荧光粉材料.     

KLa(MoO_4)_2∶Eu~(3+)红色荧光粉的合成和发光性能

采用高温固相法制备了KLa(MoO4)2∶Eu3+红色荧光粉,对其物相结构、光谱性质进行了分析,研究了Eu3+的不同掺杂浓度对荧光粉的发光性能的影响,同时对其色坐标进行了分析.结果表明,KLa(MoO4)2为体心对称的单斜相;KLa(MoO4)2∶Eu3+荧光粉中Eu3+的最佳掺杂浓度为9%,当掺杂浓度大于9%出现浓度猝灭现象,出现这一现象的主要原因是由于交换作用导致Eu3+之间能量的转移.     

红色荧光粉KYyEu1-y(WO4)x(MoO4)2-x的制备及其发光性能研究

采用高温固相法结合超声波技术合成了红色荧光粉KYyEu1-y(WO4)x(MoO4)2-x系列,探讨了其合成工艺条件,确定了最佳烧结温度为750℃,烧结时间为5 h;并确定了当x=0.5,y=0.1时样品的相对发光亮度达到最大值为118.2,发射峰的位置处在615nm附近(Eu3+离子的5Do→7F2跃迁),色纯度高,显色性能好.经过研究发现,随着钨酸盐的浓度增加,以466 nm波长激发时,Eu3+的5Do→7F2跃迁发射强度也相应增加,当Mo/W=3时亮度达到最大值.     

Sr2+含量对红色荧光粉Ca0.85-xSrxMoO4:Eu3+0.075,Li+0.075发光性能的影响

采用溶胶-凝胶法制备了Ca0.85-xSrxMoO4:Eu3+0.075,Li+0.075(x=0,0.05,0.1,0.15,0.2,0.3,0.4)系列红色荧光粉.对样品前驱体的热重分析表明:温度升高到540℃后样品质量基本上保持稳定,不再发生失重现象;此外,还对样品的结构和发光性能进行表征,实验结果表明:适量Sr2+取代部分的Ca2+不但没有改变Ca0.85MoO4:Eu3+,Li+的物相结构,而且明显提高了荧光粉Ca0.85MoO4:Eu3+,Li+的相对发光强度,其主要是由于加入少量的Sr2+使晶体发生了畸变,从而导致发光强度的增加.实验结果表明,Sr2+的最佳掺杂量为15%(原子分数).     

超细红色荧光粉LaMgAl_(11)O_(19):Eu~(3+)的制备与发光性能

采用凝胶-燃烧法制备了稀土Eu3+掺杂的LaMgAl11O19红色荧光粉的前驱粉末,在低于700℃退火处理时,得到非晶态样品,而高于850℃退火处理后为单一六方相结构LaMgAl11O19:Eu3+样品.SEM结果表明,该法制备的样品为颗粒分布均匀,粒径在200～400nm之间的超细粉末.通过激发光谱和发射光谱研究了Eu3+在LaMgAl11O19基质中的发光性能,结果显示,非晶态和晶态La1-xMgAl11O19:xEu3+样品都可发光,在613nm波长光的监测下所得荧光粉的激发光谱为一宽带和系列锐峰,其最强激发峰出现在蓝光465nm处,次强峰为394nm,表明该荧光粉与广泛使用的紫外和蓝光LED芯片的输出波长相匹配.在465nm波长光的激发下观察到超细LaMgAl11O19粉末中Eu3+的613nm(5D0→7F2)强的特征发射,且随着粉末逐渐成相5D0→7F2跃迁明显增强,说明LaMgAl11O19:Eu3+超细粉末可作为白光LED的红色补偿荧光粉.     

钨钼酸盐荧光粉基质组成及其退火过程对荧光性能的影响

采用高温固相法合成了一系列Eu3+掺杂的钨钼酸盐红色荧光粉CaxSr0.88-x(WO4)y(MoO4)1-y:0.08Eu3+。对其晶体结构和荧光性能进行了X射线衍射(XRD)、荧光光谱(PL)的表征,研究了不同Sr/Ca和WO4/MoO4比例对荧光粉光谱性能的影响,初步研究了不同退火过程对其发光性能的影响。所合成的Ca0.70Sr0.18(MoO4)0.5(WO4)0.5:0.08Eu3+荧光粉发光强度较好,可以被近紫外光(395 nm)和蓝光(465nm)有效激发,发射峰位于616 nm(Eu3+的5 D0→7 F2跃迁)。     

Eu3+掺杂双钙钛矿Sr2CaMoO6橙红色荧光粉的结构特征及其发光性能

采用EDTA-柠檬酸联合配位法制备一系列组成的(Sr1-xEux)2CaMoO6橙红色荧光粉。通过X射线衍射、拉曼光谱、扫描电镜及荧光光谱研究不同Eu3+离子掺杂浓度下Sr2CaMoO6∶Eu3+荧光粉的晶体结构、掺杂位置、形貌及其光致发光性能。Rietveld全谱拟合结果表明:掺杂后样品为(Ca/Mo)O6八面体少量倾斜的空间群为P21/n的正交双钙钛矿结构,随着Eu3+离子共掺杂浓度的增加,样品的晶胞体积减小;Eu3+离子取代八面体间隙的Sr2+位置致使双钙钛矿的T2g(1)拉曼振动模发生蓝移;在近紫外区宽而强电荷迁移带和蓝光激发下,该荧光粉分别发射以Eu3+离子5D0-7F1磁偶极跃迁为主的橙光和以5D0-7F2电偶极跃迁为主的红光,组成为(Sr0.98Eu0.02)2CaMoO6的荧光粉具有最强的橙红光发射强度,是一种潜在的适用于近紫外LED芯片的光转换红光材料。     

稀土双掺发光材料的制备与发光性能

采用溶胶-凝胶法合成了系列Li_2Eu_(4-x)(MoO_4)_7:xYb~(3+)红色荧光粉。研究结果表明Li_2Eu_(3.76)Yb_(0.24)(MoO_4)7在615 nm处发出的红光明显强于未掺杂第二稀土的Li_2Eu_4(MoO_4)_7荧光粉。Yb~(3+)离子掺杂能够将吸收的能量很好地传递给激活离子Eu~(3+),从而起到能量传递的作用。该系列荧光粉可被395 nm的近紫外光和465 nm的可见光有效激发,在615 nm处发射亮红光,对应于Eu~(3+)的~5D_0→~7F_2跃迁,其色度优于商用红粉Y_2O_2S:Eu~(2+),能够用于紫外光和蓝光芯片激发的白光LED用红色荧光粉。     

白光LED用荧光粉的研究进展

综述了国内外白光LED用荧光粉的研究进展.根据目前LED实现白光的两种主流方式:蓝光LED芯片+黄色荧光粉(或+绿色/红色荧光粉)和近紫光LED芯片+红/绿/蓝三基色荧光粉,重点介绍了蓝光芯片激发的黄色,绿色和红色荧光粉以及紫光芯片激发的红色,绿色和蓝色荧光粉.文中并给出了部分具有代表性的荧光粉的激发和发射光谱图.归纳了各种基质材料用于荧光粉的优缺点,对该领域存在的问题及其发展趋势作出了分析和展望.     

低温制备Mn4+掺杂Gd2ZnTiO6红色荧光粉及其发光性能研究

Mn4+掺杂A2BB'O6型双钙钛矿红色荧光粉可应用于植物生长照明领域而受到广泛研究,但该类荧光粉的合成温度普遍较高.通过添加一种新的助熔剂LiCl,成功将Gd2ZnTiO6:Mn4+ (GZTO:Mn4+)的合成温度从1300℃降低至950℃.通过X射线衍射(XRD)、扫描电子显微镜(SEM)、能谱仪(EDS)、激发...     

白光LED用红色荧光粉CaWO_4:Eu~(3+),Li~+,Bi~(3+)的制备与表征

采用预先球磨、再二次热处理的高温固相合成法,制备了一系列白光LED用红色荧光粉CaWO4:Eu3+,L i+,B i3+,利用XRD,SEM和荧光光谱测试对其进行表征。XRD分析表明,所合成的样品为单一的四方晶系CaWO4,Eu3+,L i+,B i3+离子的先后掺杂使基质的部分衍射峰峰位向小角度移动;SEM照片显示,经过预先球磨制备的样品颗粒比较均一,尺寸约为0.5~3μm范围,结晶性好;荧光光谱测试发现这一系列荧光粉不仅可以被紫外光(254 nm)激发,还能被近紫外光(393 nm)和蓝光(465 nm)有效激发,其主发射峰值位于616 nm(Eu3+离子的5D0→7F2跃迁)的红光;另外详细研究了预先球磨的效果、加入H3BO3做助熔剂的质量分数以及Eu3+,L i+,B i3+离子单掺或多掺时的浓度对该体系荧光粉发光特性的影响。     

A Novel White Light Emitting Long-lasting Phosphor

A novel white light emitting long-lasting phosphor Cd1-xDyxSiO3 is reported in this letterThe Dy^3 doped CdSiO3 phosphor emits white light. The phosphorescence can be seen with the naked eye in the dark clearly even after the 254nm UV irradiation have been removed for about 30min. In the emission spectrum of 5% Dy^3 doped CdSiO3 phosphor, there are two emission peaks of Dy^3 , 580nm (^4F9/2→^6H13/2) and 486nm (^4F9/2→^6H15/2), as well as a broad band emission located at about 410nm. All the three emissions form a white light with CIE chromaticity coordinates x=0.3874, y=0.3760 and the color temperature is 4000 K under 254 nm excitation. It indicated that this phosphor is a promising new luminescent material for practice application.     

New Phosphors for White LEDs

White light-emitting diodes (WLEDs) have matched the emission efficiency of florescent lights and will rapidly spread as light source for homes and offices in the next 5 to 10 years. WLEDs provide a light element having a semiconductor light emitting layer (blue or UV LEDs) and photoluminescence phosphors. GaN-based highly efficient blue InGaN LEDs combined with phosphors can produce white light. These solid-state LED lamps have a number of advantages over conventional incandescent bulbs and halogen lamps, such as high efficiency to convert electrical energy into light, reliability, and long operating lifetime (about 100,000 hours). For the purpose of development of high energy-efficient white light sources, we need to produce highly efficient new phosphors, which can absorb excitation energy from blue or UV LEDs and generate emissions.In this paper, we investigate the development of blue or UV LEDs by the appropriate combination of new phosphors which can lead us to obtain high brightness white light. The criteria of choosing the best phosphors, for blue (380-450 nm) and UV (360-400 nm) LEDs, strongly depends on the absorption and emission of the phosphors. Moreover, the balance light between the light emission from blue LEDs and the yellow YAG:Ce,Gd phosphor is important to obtain white light with high color temperature. The phosphors with high efficiency which can be excited by UV LEDs are important to obtain the white light with high color rendering index.     

白光发光二极管用钇铝石榴石萤光粉配方与机制研究

研究了钇铝石榴石萤光粉的合成及其发光特性，目的在于探讨掺入稀土元素离子的钇铝石榴石萤光粉晶体结构和发光光谱研究，并研究以不同元素及不同量取代的活化剂借以了解对萤光体各种相关特性的效应。     

磷酸钡钙:铈、锰红色荧光粉的研制

采用高温固相反应合成了磷酸钡钙：铈、锰红色荧光粉. 借助TG, XRD, 荧光粉相对亮度仪、荧光分光光度仪等手段系统研究了合成过程中原料化学组成及配比、合成条件对磷酸钡钙：铈、锰发光性能的影响. 结果表明, 荧光粉基质 （BaxCa1-x）3（PO4）2具有畸变的Ca3（PO4）2结构. 该荧光粉中Ce^3＋是助激活剂, Mn^2＋是激活剂, 由Ce3＋→Mn^2＋ 的能量传递使Mn^2＋激发产生650 nm左右的发射, 当Ce^3＋和Mn^2＋浓度相等且都为0.15时, 荧光粉有最高的红色发射亮度.     

(CaO)20.68(MgO)1.32(SiO2)4S2∶Eu2+,Dy3+红光材料的制备与发光特性

研究了峰值波长651nm的红色发光材料(CaO)20.68(MgO)1.32(SiO2)4S2∶Eu2 ,Dy3 的制备及发光特性。通过XRD分析表明硫气氛中合成的材料为具有硫成分的硅酸盐相。红光发射带为硫元素进入晶格后在发光中心周围形成了类似长余辉材料CaS∶Eu2 ,Cl-的局域结构。这也使材料具有了硫化物长余辉材料的发射光谱特征和硅酸盐材料高化学稳定性和高亮度的优点。热释光测量揭示它可能是一种潜在的红色长余辉材料。     

紫外光发光二极管用铋与铕离子掺杂的氧化钇红光荧光体研究

将铋离子（Bi^3＋）加入铕离子掺杂的氧化钇红色荧光体中, 探讨了其结构与光学性质. 发现加入铋离子能促进红色荧光体于300～380 nm的紫外线能量吸收, 此乃由于铋离子吸收紫外线能量再以能量转移的方式传给铕离子.     

稀土铝酸盐蓝色荧光粉前驱体的制备及其应用

以硫酸铝铵和碳酸氢铵为原料，制备了结晶碳酸铝铵，用IR，XRD，DTA－TG等手段研究了结晶碳酸铝铵在煅烧过程中的相变和热分解机理，并考察了煅烧过程中的粒度和比表面变化以及煅烧产物的外观形貌，结果表明：在煅烧过程中结晶碳酸铝铵首先分解为无定型氧化铝，并依次从无定型Al2O3-γ-Al2O3-κ-Al2O3,δ-Al2O3,τ-Al2O3-α-Al2O3,τ-Al2O3-α-Al2O3转变，比表面在600℃之前是随温度升高而增大，600摄氏度之后则下降，而粒度变化在900摄氏度之前随温度升高而降低，900摄氏度之后则增大，煅烧产物为粒度在2-3um的片状结晶氧化铝，用该氧化铝所合成的稀土铝酸盐蓝粉，晶相纯，发光强度高，且粒度小，可以满足不球磨蓝色荧光粉的基本要求。