Synthesis and magnetic properties of single-crystalline BaFe12O19 nanoparticles

Rod-like and platelet-like nanoparticles of simple-crystalline barium hexaferrite (BaFe₁₂O₁₉) have been synthesized by the molten salt method. Both particle size and morphology change with the reaction temperature and time. The easy magnetization direction (0 0 l) of the BaFe₁₂O₁₉ nanoparticles has been observed directly by performing X-ray diffraction on powders aligned at 0.5 T magnetic field. The magnetic properties of the BaFe₁₂O₁₉ magnet were investigated with various sintering temperatures. The maximum values of saturation magnetization (σ_s=65.8 emu/g), remanent magnetization (σ_r=56 emu/g) and coercivity field (H_ic=5251 Oe) of the aligned samples occurred at the sintering temperatures of 1100 °C. These results indicate that BaFe₁₂O₁₉ nanoparticles synthesized by the molten salt method should enable detailed investigation of the size-dependent evolution of magnetism, microwave absorption, and realization of a nanodevice of magnetic media.     

Magnetic properties of c-axis oriented Sr0.8La0.2Fe11.8Co0.2O19 ferrite film prepared by chemical solution deposition

A Sr_0.8La_0.2Fe_11.8Co_0.2O₁₉ ferrite film has been prepared on a (0 0 1) sapphire substrate by chemical solution deposition. Structural characteristics indicate that the film is c-axis oriented and single-phase with space group P6₃/mmc. The grains are regular columnar with diameter between 50 and 100 nm as determined by atomic force microscopy. The sample possesses high saturation magnetization (130 emu/cm³), high coercivity (6.9 kOe), and large squareness ratio (0.9) at room temperature, which makes it a promising recording material.     

(Ni0.8Zn0.2Fe2O4)epoxy-PZT双层膜中的磁电效应

讨论了Ni_0.8Zn_0.2Fe₂O₄ (NZFO)与锆钛酸铅(PZT)的双层膜结构样品的磁电(ME)效应.NZFO粉料由溶胶-凝胶法制成，再经900℃热压，并高温烧结.在该双层膜中测量到了很强的磁电相互作用.发现横向的磁电效应比纵向效应大一个数量级，并且随NZFO烧结温度的提高而增加.当烧结温度从950℃上升到1380℃时，横向ME电压系数(α_E)的最大值变化范围为25.6 mV Am^-2≤α_E≤199.6 mV Am^-2.理论分析显示NZFO-PZT双层膜样品中ME效应源于NZFO与PZT之间相对良好的磁电耦合. 关键词： 镍铁氧体 PZT 热压法 ME效应     

针状纳米MnxNi0.5-xZn0.5Fe2O4的共沉淀法制备及表征

通过在碱液中共沉淀Mn²⁺、Ni²⁺和Fe²⁺后制备了棒状的前躯体,前躯体于不同温度煅烧后制得了Mn_xNi_0:5-xZn_0:5Fe₂O₄棒状体. 利用X射线衍射仪和透射电镜对棒状体的物相、形貌及粒径进行了表征,并利用振动样品磁强计对磁性能进行研究. 结果表明长径比大于15的棒状,随着x值的增加,Mn_xNi_0:5-xZn_0:5Fe₂O₄样品的直径增加,长度下降,长径比变小,当x=0.5时其直径在50 nm左右而长径比减小到7～8. 随着x值的增加,样品的矫顽力先增加后减少,x值达到0.4时样品的矫顽力再次增加,当煅烧温度为600 oC,x=0.5时样品的矫顽力最大为134.3 Oe. 饱和磁化强度随着x值的增加先增加后减少,当煅烧温度为800 oC和x=0.2时达到最大为68.5 Oe.     

Synthesis and magnetic properties of hard/soft SrFe12O19/Ni0.7Zn0.3Fe2O4 nanocomposite magnets

Magnetic nanocomposite SrFe₁₂O₁₉/Ni_0.7Zn_0.3Fe₂O₄ powders with different weight fractions of the Ni_0.7Zn_0.3Fe₂O₄ soft ferrite were synthesized by a combination of the sol–gel self-propagation and glyoxilate precursor methods. The results of magnetic measurements revealed the higher Mr/Ms ratio for the nanocomposites than that for the single phase SrFe₁₂O₁₉ which proves the existence of the intergrain exchange coupling between hard and soft magnetic phases with the exchange spring behavior. The highest Mr/Ms ratio of 0.63 was obtained in the composite consisting of 80 wt% of SrFe₁₂O₁₉ and 20 wt% Ni_0.7Zn_0.3Fe₂O₄. The microstructural studies of this sample exhibited the average dimensions of hard and soft phases about 20 nm and 15 nm, respectively which are small enough for strong exchange coupling according to the theoretical studies. The variations of the reduced remanence (Mr/Ms) with increasing the weight fraction of the soft phase could be also explained by the role of the exchange and dipolar interactions in tuning the magnetic properties of the nanocomposites.     

Study on dielectric and magnetic properties of Ho3Fe5O12 ceramics

Ho₃Fe₅O₁₂ ceramics with garnet structure were prepared by the solid-state reaction method. The results revealed the existence of Fe²⁺ ions have intensive influence on dielectric and magnetic properties of Ho₃Fe₅O₁₂ ceramics, which could be further confirmed by oxygen treatment. With a magnetic field lower than 10 kOe, the ME coefficient reaches 33 ps m⁻¹ at room temperature. And the ME coupling was further verified by dielectric anomaly near Néel temperature.     

Synthesis and magnetic properties of hard magnetic (CoFe2O4)-soft magnetic (Fe3O4) nano-composite ceramics by SPS technology

CoFe₂O₄/Fe₃O₄ nano-composite ceramics were synthesized by Spark Plasma Sintering. The X-ray diffraction patterns show that all samples are composed of CoFe₂O₄ and Fe₃O₄ phases when the sintering temperature is below 900 °C. It is found that the magnetic properties strongly depend on the sintering temperature. The two-step hysteresis loops for samples sintered below 500 °C are observed, but when sintering temperature reaches 500 °C, the step disappears, which indicates that the CoFe₂O₄ and Fe₃O₄ are well exchange coupled. As the sintering temperature increases from 500 to 800 °C, the results of X-ray diffractometer indicate the constriction of crystalline regions due to the ion diffusion at the interfaces of CoFe₂O₄/Fe₃O₄ phases, which have great impact on the magnetic properties.     

A study of the properties and microstructure of Ni81Fe19 ultrathin films with MgO

The anisotropic magnetoresistance (AMR) of a Ta (5 nm)/MgO (3 nm)/Ni₈₁Fe₁₉ (10 nm)/MgO (2 nm)/Ta (3 nm) film with MgO-Nano Oxide Layer (NOL) increases dramatically from 1.05% to 3.24% compared with a Ta (5 nm)/Ni₈₁Fe₁₉ (10 nm)/Ta (3 nm) film without the MgO-NOL layer after annealing at 380 °C for 2 h. Although the MgO destroys the NiFe (1 1 1) texture, it enhances the specular electron scattering of the conduction electrons at the NOL interface and suppresses the interface reactions and diffusion at the Ta/NiFe and NiFe/Ta interfaces. The NiFe (1 1 1) texture was formed after the annealing, resulting in a higher AMR ratio. X-ray photoelectron spectroscope results show that Mg and Mg²⁺ were present in the MgO_x films.     

Origin of the intriguing physical properties in A-site-ordered LaCu3Fe4O12 double perovskite

Our density functional theory calculations show that the origin of the stability of the Cu³⁺ oxide, LaCu₃Fe₄O₁₂, is the strong hybridization interaction between La-O-Cu, which also suppresses structural symmetry change with changing temperature. From low-temperature antiferromagnetism to high-temperature paramagnetism, each Fe ion loses 0.34 electron and each Cu ion gets 0.45 electron, while the charges of La and O ions do not change. Additionally, each type of ion has the same total charge. The Coulomb attractive force between Fe-O-Fe at high temperature is stronger than that at low temperature, driving a large negative thermal expansion.     

Biosynthesis and magnetic properties of mesoporous Fe3O4 composites

Magnetic Fe₃O₄ materials with mesoporous structure are synthesized by co-precipitation method using yeast cells as a template. The X-ray diffraction (XRD) pattern indicates that the as-synthesized mesoporous hybrid Fe₃O₄ is well crystallized. The Barrett-Joyner-Halenda (BJH) models reveal the existence of mesostructure in the dried sample which has a specific surface area of 96.31 m²/g and a pore size distribution of 8-14 nm. Transmission electron microscopy (TEM) measurements confirm the wormhole-like structure of the resulting samples. The composition and chemical bonds of the Fe₃O₄/cells composites are studied by Fourier transform infrared (FT-IR) spectroscopy. Preliminary magnetic properties of the mesoporous hybrid Fe₃O₄ are characterized by a vibrating sample magnetometer (VSM). The magnetic Fe₃O₄/cells composites with mesoporous structure have potential applications in biomedical areas, such as drug delivery.     

Effect of grain size on the magnetic properties of superparamagnetic Ni0.5Zn0.5Fe2O4 nanoparticles by co-precipitation process

Ni_0.5Zn_0.5Fe₂O₄ (NZFO) spinel-type nanoparticles were directly fabricated by the chemical co-precipitation process using metal nitrate and acetate as precursors since nitrogen and carbon would be taken away in the forms of oxynitride and oxycarbide, respectively, after the precursors were annealed and then investigated in detail by employing X-ray diffraction (XRD), magnetic measurement and Raman spectroscopy. XRD analysis indicates that the as-prepared nanocrystals are all of a pure cubic spinel structure with their sizes ranging from 20.8 to 53.3 nm, as well as peaks of some samples shifting to lower angles due to lattice expansion. Calculations from the derived XRD data indicate that the activation energy is 30.83 kJ/mol. The magnetic measurements show that these samples are superparamagnetic. The saturation magnetization increases with annealing temperature, which may be explained by super-exchange interactions of Fe ions occurring at A- and B-sites. The variation of coercivity with particle size is interpreted on the basis of domain structure and crystal anisotropy. Furthermore, these nanoparticles exhibit a redshift phenomenon at lower temperatures seen in the Raman spectra, which could be related to ionic substitution.     

Effect of calcination temperature on the structure and hydroxylation activity of Ni0.5Cu0.5Fe2O4 nanoparticles

Nanocrystalline Ni_0.5Cu_0.5Fe₂O₄ was synthesized by sol-gel method with varying calcination temperature over the range of 500-1000. The powders obtained were characterized by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and X-ray photoelectron spectroscopy (XPS). In addition, thermal analysis (TG-DTG-DTA) of the precursor was carried out. The study reveals the simultaneous decomposition and ferritization process at rather low temperature (280-350). For the crystalline structure investigated, single cubic spinel is gained when the precursor was decomposed at 800-1000, whereas separated crystal CuO formed when calcination temperature is below 800. The increase of calcination temperature favors the appearance of Fe_B³⁺, Cu_A²⁺ and O on the spinel surface. The hydroxylation activity is relative to the amount of Cu_B²⁺ species on the spinel surface. The lattice oxygen species on the spinel surface are favorable for the deep oxidation of phenol.     

Comparison of magnetic properties in LixCoO2 and its decomposition products LiCo2O4 and Co3O4

Thermal stability of cathode material in the charged state is an important aspect for the safety of rechargeable batteries. It is well known that layered Li_xCoO₂ decomposes to a mixture of LiCoO₂ and Co₃O₄ at elevated temperatures. However, not many experimental evidences exist on intermediate phases those may form during the decomposition. Using magnetic measurements we show that it is possible to distinguish between the spinels LiCo₂O₄ and Co₃O₄ and thereby follow the decomposition of Li_xCoO₂. We characterize the magnetic behavior of thermally aged Li_xCoO₂ (x = 0.98, 0.76, 0.55) with increasing annealing time. Our results reveal the appearance of magnetic ordering in the thermally degraded products. The detailed analysis illustrates that the formation of Co₃O₄ is preceded by the formation of a meta stable LiCo₂O₄ phase.     

Preparation and magnetic properties of the conductive Co(1−x)NixFe2O4/polyaniline microsphere composites

Core-shell Co_(1−x)Ni_xFe₂O₄/polyaniline nanoparticles, where the core was Co_(1−x)Ni_xFe₂O₄ and the shell was polyaniline, were prepared by the combination of sol-gel process and in-situ polymerization methods. Nanoparticles were investigated by Fourier transform spectrometer, X-ray diffraction diffractometer, Scanning electron microscope, Differential thermal analysis and Superconductor quantum interference device. The results showed that the saturation magnetization of pure Co_(1−x)Ni_xFe₂O₄ nanoparticles were 57.57 emu/g, but Co_(1−x)Ni_xFe₂O₄/polyaniline composites were 37.36 emu/g. It was attributed to the lower content (15 wt%), smaller size and their uneven distribution of Co_(1−x)Ni_xFe₂O₄ nanoparticles in the final microsphere composites. Both Co_(1−x)Ni_xFe₂O₄ and PANI/Co_(1−x)Ni_xFe₂O₄ showed superparamagnetism.     

Effects of applied magnetic field and pressures on the magnetic properties of nanocrystalline CoFe2O4 ferrite

Nanocrystalline CoFe₂O₄ ferrite with crystallite sizes of 30 nm have been successfully prepared by an emulsion method. X-ray diffractometer (XRD) shows that nanocrystalline CoFe₂O₄ ferrite possesses face center cubic structure. Crystal structure of the CoFe₂O₄ nanocrystals will not be changed by the applied magnetic field and pressures. The obtained CoFe₂O₄ nanocrystalline powders were pressed into thin columns with different pressures. Meanwhile, the dependences of the applied pressures and the direction of applied magnetic field on the magnetic properties of the CoFe₂O₄ nanocrystals were investigated in detail using vibrating sample magnetometer (VSM). The pressed CoFe₂O₄ nanocrystal gains the most excellent magnetisms in a parallel applied magnetic field.     

Microwave-assisted synthesis of SrFe12O19 hexaferrites

Ultra-fine and homogeneous SrFe₁₂O₁₉ hexaferrites were synthesized by a microwave-assisted calcination route. The calcined precursors were prepared by a sol-gel auto-combustion method using Fe(NO₃)₃·9H₂O, Sr(NO₃)₂ and citric acid as starting materials. The structures, powder morphology and magnetic properties of the products were characterized by X-ray diffraction, scanning electron microscope and vibrating sample magnetometer. The results showed that microwaves are helpful to reduce the calcination temperature and shorten the calcination time. The ferrites with saturation magnetization, remanence and intrinsic coercivity of 54.80 emu/g, 29.52 emu/g and 5261 Oe, respectively, were obtained in samples calcined at 800 °C for 80 min.     

Role of oxygen impurity in growth and magnetic properties of Ni83Fe17 permalloy thin films

To study the influence of oxygen impurities in the sputtering atmosphere on microstructure, and the magnetic and magnetotransport properties, thin films of Ni₈₃Fe₁₇ were deposited under dc magnetron sputtering technique into which regulated oxygen gas was introduced. The partial pressure of oxygen was varied from 2×10⁻⁷ to 3×10⁻⁶ mbar. X-ray diffraction patterns indicate the reduction of grain growth with increasing the oxygen partial pressure. The grain microstructure and the composition were confirmed through high resolution transmission electron microscopy attached with Scanning Transmission Electron Microscopy (STEM). Transition from canted to rectangular magnetic hysteresis loop was observed through magnetization measurements for samples prepared under higher oxygen partial pressure which implies the structural changes in the magnetic domain formation. These observations were further confirmed through the measurements of anisotropic magnetoresistance properties.     

Spectroscopic and laser properties of Nd:Gd0.8La0.2VO4 crystal

The polarised absorption and fluorescence spectra of Nd:Gd_0.8La_0.2VO₄ crystal are measured and compared to those of Nd:GdVO₄. CW laser properties of diode-pumped Nd:Gd_0.8La_0.2VO₄ crystal operating at fundamental wavelengths of 1.06 and 1.34 μm, as well as when intracavity frequency-doubled to 532 and 670 nm, have been studied. The maximum output powers at 1.06 μm, 1.34 μm, 532 nm and 670 nm are 1.18 W, 671 mW, 206 mW and 42 mW respectively, at a diode-launched pump power of 2.9 W. The threshold pump powers are 80, 267, 7 and 15 mW respectively.     

The magnetic properties of diluted CoFe2O4 nanomaterials

The magnetic properties of （Cox Fe1-x）A （Zn1-x Fe1＋x）B O4 are studied using mean-field theory and the probability distribution law to obtain the saturation magnetization, the coercive field, the critical temperature, and the exchange interactions with different values of D （nm） and x. High-temperature series expansions （HTSEs） combined with the Pade approximant are used to calculate the critical temperature of （CoxFe1-x）A（Znl-xFe1＋x）BO4, and the critical exponent associated with magnetic susceptibility is obtained.     

低维Bi2Fe4O9晶体的控制生长及其光催化性能研究

Low-dimensional Bi₂Fe₄O₉ nanosheets and microrods have been selectively prepared by a solvothermal method, from which the growth of the Bi₂Fe₄O₉ crystals can be controlled by the variation of reaction conditions. Structure determination showed that the nanosheets are mainly exposed by {001} facets while the microrods are exposed by {110} facets. Ab- sorption spectra revealed that there are two bandgaps observed for both nanosheets (at 1.9 and 1.55 eV) and microrods (1.7 and 1.45 eV), and they both would be available for the sunlight photocatalysis e ciently due to the intensive absorption ability in a wide region. Photocatalytic investigation demonstrated that the overall photocatalytic performance of the microrods is prior to that of the nanosheets due to the variation of bandgaps and exposed facets. The present report provides a useful alternative strategy for the controlling growth of nanostructures and/or microcrystals besides the present demonstration of the Bi₂Fe₄O₉ crystals with diflerent bandgaps and facets that would be able to tune the corresponding photocatalytic ability selectively.