Study of radiation-induced polymerization of vinyl monomers adsorbed on inorganic substances. IV. Dose rate and temperature dependences in the styrene–silica gel system

In order to elucidate the mechanism of radiation-induced polymerization of styrene adsorbed on silica gel, the effects of dose rate and irradiation temperature were studied in detail. Monomer conversion increased with increasing dose rate and temperature. At the same conversion, the percent grafting increased with decreasing dose rate and also with increasing temperature. In general, GPC spectra of graft polymers and homopolymers showed two peaks; the ratio of the two peaks changed with dose rate and irradiation temperature. The dose-rate exponents of the polymerization rate of four peaks were different from each other. The activation energies of radical polymerization and cationic polymerization were about 2.6 kcal/mole and 0 kcal/mole, respectively. Based on the results obtained, a reaction mechansim is proposed.     

Radiation-induced polymerization of 1,1,2-trichlorobutadiene

The γ-ray-induced polymerization of 1,1,2-trichlorobutadiene, m.p. ?48.5°C., was investigated in the temperature range from +55 to ?196°C. In the liquid state, the following results were obtained: (1) the rate decreases with decrease of temperature (E_a = 8.0 kcal./mole); (2) the dose rate dependences of rate and of molecular weight are 0.49 and ?0.25, respectively; (3) the reaction is inhibited by DPPH; (4) the structure of the polymer is predominantly 1,4 units. It was concluded that the liquid-state polymerization proceeds by a radical mechanism, and the radical yield was found to be 19.7. In the solid state, the following results were obtained: (1) the rate is considerably higher than in the liquid state immediately above the melting point and gradually decreases with decrease of temperature (E_a = 0.34 kcal./mole); (2) the dependence of the rate on dose rate is unity while the molecular weight is independent of the dose rate; (3) the reaction rate is unaffected by DPPH and accelerated by dimethylformamide; (4) the structure of the polymer, 3,4 units, is completely different from that of the polymer obtained in the liquid-state polymerization. The solid-state polymerization is probably of a different nature and is not well elucidated.     

Polymerization of styrene with ZrCl4 and ZrCl3 in combination with Al(C2H5)3

The polymerization of styrene with two catalyst systems consisting of Al(C₂H₅)₃ in combination with ZrCl₄ or ZrCl₃ has been studied. The rate of polymerization with catalyst concentration was first-order with ZrCl₄ system and second-order with ZrCl₃ system, but at higher catalyst concentrations in both cases, the rate progressively decreases and finally attains a low value. The rate of polymerization is, however, proportional to the square of the monomer concentration in both the cases. The overall energy of activation was 10.9 kcal./mole and 6.45 kcal./mole in these systems. The polymers obtained with ZrCl₄ were of lower molecular weights as compared to those obtained with ZrCl₃. The polymers in both the cases had amorphous character.     

Study of radiation-induced polymerization of vinyl monomers adsorbed on inorganic substances. V. Effects of p-benzoquinone and dose rate on methyl methacrylate–silica gel system

In order to elucidate the mechanism of radiation-induced polymerization of methyl methacrylate adsorbed on silica gel, the effects of p-benzoquinone addition and dose rate were studied in detail. Most of the polymerization is inhibited by p-benzoquinone at levels above 10^-2 mole/l. The GPC spectra of both graft polymers and homopolymers show two peaks. The high molecular weight material appears to have been formed by polymerization by a radical mechanism, because these peaks decrease as p-benzoquinone concentration increases; on the other hand, their low molecular weight polymers seem to be products of an ionic polymerization mechanism because those peaks are almost not affected by p-benzoquinone. The four GPC peaks differ in dose rate dependences of their polymerization rate. The dose-rate exponents of polymerization rate were obtained for the four GPC peaks. The behavior of the low molecular weight peaks of graft polymers and homopolymers were quite different, suggesting that the polymers differ considerably in formation mechanism.     

Ferric oxide-catalyzed polymerization of methyl methacrylate

The polymerization of methyl methacrylate was carried out in water at various concentrations of sodium bisulfite, ferric oxide, and methyl methacrylate at 30, 40, and 50°C. The effect of ferric oxide on the rate of polymerization was studied at 50°C. Rates of polymerization increased in the presence of ferric oxide. For example, the rate of polymerization increased from 3.4 × 10^?5 mole/l.-sec to 11.8 × 10^?5 mole/l.-sec when the ferric oxide concentration was varied from 0 to 15 g/l. water. The molecular weight of the polymer decreased from an average of 1.4 × 10⁶ in the absence of ferric oxide to 2.8 × 10⁵ when the ferric oxide was present. The variation of molecular weight of the polymers with temperature and conversion was studied. At a fixed conversion of 80%, the average molecular weight decreased from 3.4 × 10⁵ at 30°C to 2.2 × 10⁵ at 50°C. The average molecular weight was also found to increase with increasing monomer and initiator concentrations. It increased from 8.1 × 10⁴ to 5.3 × 10⁵ and from 3.4 × 10⁵ to 8.9 × 10⁵ as the initiator and monomer concentrations increased from 0.01 to 0.05 mole/l. and from 0.235 to 0.705 mole/l., respectively. The apparent energy of activation for the polymerization was found to be 15.6 and 9.7 kcal/mole in absence and in presence of ferric oxide, respectively.     

Radiation-induced polymerization at high pressure of cis- and trans-1,3,3,3-tetrafluoropropene in bulk and with tetrafluoroethylene

The radiation-induced polymerization of cis- and trans-1,3,3,3-tetrafluoropropene in bulk and with tetrafluoroethylene was studied at pressures between 5000 and 15000 atm and temperatures between 21 and 100°C. At 10³ rad/hr the homopolymerization rates range from about 10^?4 to 1%/hr. The activation enthalpy and volume are about 8 kcal/mole (33 kJ/mole) and ?10 cm³/mole, respectively, for both isomers. The cis isomer polymerizes about twice as rapidly as the trans isomer. The latter freezes in the experimental range of temperature and pressure; the polymerization rate is very low in solid phase. Polymer intrinsic viscosities increase with polymerization pressure and decrease with polymerization temperature; the largest value obtained was 0.23 dl/g. In the copolymerizations all reactivity ratios favor incorporation of tetrafluoroethylene by factors of 6–16. The preference is stronger when the trans isomer is used.     

Electroinitiated cationic polymerization of styrene by direct electron transfer

We have studied by cyclic voltammetry the mechanisms of electron transfer and peak potentials of eleven alkenes, propylene oxide, propylene sulfide, and carbon disulfide. We have also studied the cationic polymerization of styrene in acetonitrile solution initiated by controlled potential electrolysis at the anodic peak potential of styrene. The electrolyte used was tetrabutylammonium fluoborate, which was not electroactive at the electrolysis potential, and the reference electrode was a Ag⁰/Ag⁺ electrode. The electrochemical studies show that direct electron transfer from styrene is the initiation steps. Plots of reacted monomer concentrations versus time are sigmoidal curves. The propagation rate constant was found from a kinetic relationship based on an autocatalytic reaction. The activation energy is 15.6 kcal/mole at 20°C. The current behavior and effect of stirring on polymerization rate suggest that the growth of polymer takes place partially on the electrode surface.     

Polymerization initiated by an electron donor–acceptor complex. Part I. Polymerization of methyl methacrylate initiated by liquid sulfur dioxide–pyridine complex in the presence of carbon tetrachloride

The polymerization of methyl methacrylate can be initiated by a charge-transfer complex of liquid sulfur dioxide and pyridine in the presence of carbon tetrachloride. The molar ratio of sulfur dioxide and pyridine which participated in the complex was found from a spectrophotometric study to be 2:1. The polymerization proceeds through free-radical intermediates. The overall rate of polymerization is proportional to the square root of the concentration of the complex, and the values of k_p/k_t^1/2 under the various polymerization conditions were satisfactorily consistent with the literature value. For the activation energy of the overall reaction, 8.2 kcal./mole was obtained, and for initiation, 9.7 kcal./mole was evaluated from the values of k_p/k_t^1/2. It was deduced from a kinetic mechanism for the initiation that a primary radical may be produced from the reduction of carbon tetrachloride by an associated complex consisting of liquid sulfur dioxide–pyridine complex and the monomer.     

Kinetics of free-radical polymerization of p-vinylbenzyl methyl ether: Crosslinking by initiator free radicals

Kinetics of polymerization of p-vinylbenzyl methyl ether at low conversion either in bulk or in benzene have been found to be quite similar to those of the unsubstituted monomer styrene. Rates of polymerization initiated by peroxides or α,α′-azobisisobutyronitrile over the temperature range 50–70°C. have been found to be proportional to [Monomer][Initiator]^1/2 with an activation energy difference E_propagation – 1/2 E_termination ≈ 6 kcal./mole. Azo initiation leads to essentially unbranched poly(vinyl-benzyl methyl ether) even at very high conversions, whereas initiation of undiluted monomer by diacyl peroxides results in some crosslinking at high conversion. Use of biacetyl as a photoinitiator of polymerization over the temperature range 0–60°C. with either bulk monomer or monomer solutions in benzene has been found in each instance to yield crosslinked, insoluble polymers at low degrees of conversion. Benzene solutions of soluble polymer have been converted to high molecular weight branched polymers by free radicals generated by photolysis of biacetyl, and a substantial preference of methyl free radicals to abstract benzyl hydrogens of poly(p-vinylbenzyl methyl ether) rather than add to solvent benzene has been observed.     

Free-radical polymerizations initiated by triethylaluminum–cuprous chloride mixtures

Methyl methacrylate was polymerized by triethylaluminum—cuprous chloride catalyst. A study of the polymerization kinetics indicated that the overall rate was represented by the equation, R_p = K[AlEt₃] [CuCl]^½ [M]². The overall activation energy was 16.5 kcal/mole. From ESR measurement and the results of copolymerization of methyl methacrylate with styrene, it was suggested that the catalytic system has the character of a radical initiator. A polymerization scheme was also proposed.     

Radical polymerization behavior of hydroxystyrenes

Homopolymerizations of m- and p-hydroxystyrene and their copolymerizations with styrene and methyl methacrylate by use of azobisisobutyronitrile as initiator were investigated, and the results were compared with those obtained previously o-hydroxystyrene. Intrinsic viscosities of m- and p-hydroxystyrene polymers obtained by bulk and solution polymerizations were ca. 2 to 3 times larger than those of o-hydroxystyrene polymers obtained by the similar conditions. The structures of the polymers thus produced were investigated by infrared and ultraviolet spectroscopy. These studies suggested that all of the homopolymers consisted mainly of structures of normal vinyl type polymer. R_p was proportional to [I]^0.52 for m-hydroxystyrene and to [I]^0.50 for p-hydroxystyrene, for o-hydroxystyrene R_p was proportional to [I]^0.72. A reasonable chain transfer mechanism for these monomers was postulated. The apparent activation energies of polymerization for m- and p-hydroxystyrene were found to be 20.1, and 18.0 kcal/mole, respectively, compared to the value of 21.5 kcal/mole for o-hydroxystyrene. Monomer reactivity ratios and Q ? e values for m- and p-hydroxystyrene were determined, and the results were also compared with the case of o-hydroxystyrene. Copolymerization generally gave a polymer with relatively high intrinsic viscosity, even in the case of o-hydroxystyrene.     

Kinetics and thermodynamics of anionic polymerization of 2-methoxy-2-oxo-1,3,2-dioxaphosphorinane

Kinetic activation parameters and thermodynamic functions describing the reversible anionic polymerization of 2-methoxy-2-oxo-1,3,2-dioxaphosphorinane (1,3-propylene methyl phosphate) were determined. Enthalpy and entropy of the anionic propagation ? depropagation equilibrium were found to be close to those found previously by the present authors for the cationic polymerization, while the activation parameters of propagation and depropagation differ substantially for both processes and reflect the differences in the involved mechanisms. Thus, data for anionic polymerization (and cationic polymerization in parentheses) are: ΔH_1s° = ?0.7 kcal/mole (?1.1); ΔS_1s° = ?2.8 cal/mole-deg (?5.4); ΔH_p^? = 26.7 kcal/mole, and ΔS_p^? = ?6.1 cal/mole-deg. The polymers obtained have low degrees of polymerization (DP _n ≤ 10) because of the extensive chain transfer, leaving cyclic end groups in macromolecules. The presence, structure and concentration of the end groups have been determined by ¹H-, ³¹P-, and ¹³C-NMR spectra.     

Vinyl Polymerization. 269. Polymerization of Methyl Methacrylate Initiated by p,p'-Dimethoxydiphenyldiazomethane

Using p,p'-dimethoxydiphenyldiazomethane (DMDM) as initiator, the polymerization of methyl methacrylate (MMA) in benzene or in bulk was carried out. The initial rate of polymerization, R_p, was found to be expressed by the following equation:

R_p = k[DMDM]^0.53 [MMA]^0.84

The polymerization was confirmed to proceed by a radical mechanism. The over-all activation energy for the polymerization in benzene was calculated as 19.3 kcal/mole. The rate of thermal decomposition of DMDM was also measured in benzene and the rate equation was obtained as follows:

k_d (sec^?1) = 1.0 × 10¹⁵ exp (^?29.1 kcal/RT) (for 50-80°C)

Explanations of these observations are discussed in connection with those of the preceding papers.     

Molecular weight distributions in radiation-induced polymerization. III. γ-Ray-induced polymerization of styrene at low temperatures

The kinetics of the γ-radiation-induced polymerization of styrene was studied at radiation intensities of 8 × 10⁴, 2.4 × 10⁵, 3.1 × 10⁵, and 8.3 × 10⁵ rad/hr over a temperature range of ?10°C to 30°C. The water content of the irradiated samples varied from 1.0 × 10^?3 to 7.5 × 10^?3 mole/l. The power dependence of the rate of polymerization on the dose rate at ?10°C varied from 0.53 to 0.71 as the water content of the sample varied from 7.5 × 10^?3 to 1.0 × 10^?3 mole/l. A value of 3.1 kcal/mole was determined for the overall activation energy. Molecular weight distribution studies by gel-permeation chromatography indicated the presence of two distinct peaks. The contribution of each peak was dependent on specific experimental parameters. Kinetic data and molecular weight distribution data indicate the coexistence of two propagating species. Analysis of the data strongly suggests that a free-radical mechanism and a cationic mechanism are involved.     

Radiation-Induced Polymerization of Tetrafluoroethylene in Solution

Polymerization of tetrafluoroethylene in monochlorodifluoromethane was carried out at low temperatures with -prays from a ⁶⁰Co source. An activation energy of 4.3 kcal/mole was obtained for the in-source polymerization, and this is higher than that of bulk polymerization, 2.7 kcal/mole. It was found that a remarkable postpolymerization takes place even if the reaction system is in liquid state. A kinetic treatment for the postpolymerization is described.     

The effect of organic nitriles on the radiation induced polymerization of styrene

The effect of a range of 10 organic nitriles on the radiation-induced polymerization of styrene was studied. A dose rate of 4.4 rad s^?1 was used. A rate of polymerization of styrene (1.744 mol L^?1 of toluene solution) of 5.0 × 10^?7 mol L^?1 s^?1 was found. With organic nitriles present (styrene:nitrile ratio of 1:0.28) the rate of polymerization increased. Rates in the range of 5.5 × 10^?7 ?5.2 × 10^?6 mol L^?1 s^?1, depending on the nitrile present, were obtained. The polymers were partially characterized and evidence of involvement of each of the nitriles in the polymer chains was revealed. The increase in rate of polymerization has been attributed to the part played by nitrile radicals in the initiation of styrene polymerization. Radical yield values [as G(nitrile radical)] were derived from the relevant rate expressions. Values ranged from 2.7 to 49.5, depending on the particular nitrile. Corresponding values of G(nitrile radical) in the range of 5.1–129.4 were obtained by the manipulation of number-average molar mass data. Values of k_pk_t of approximately 2 × 10^?5 L mol^?1 s^?1 were found. Trommsdorff types of effect are absent from these systems.     

Effect of amines on vinyl polymerization initiated by chromous acetate–alkyl halide systems

The radical polymerization of vinyl monomers initiated by Cr²⁺–RX in the presence of various amines was studied in DMF at 30°C. Polyamines able to form the chelate complex with Cr²⁺ accelerated the rate of polymerization of styrene in the following order: ethanolamine > triethylenetetramine > diethylenetriamine > ethylenediamine. However, aliphatic monoamine, hexamethylenediamine, and aromatic diamine did not have any effect on the polymerization. These results suggest that the effect of multidentate ligands may be associated with chelating effects which affect the electron transfer ability of the metal complex. An apparent activation energy of 8.2 kcal/mole for the polymerization of styrene was obtained in the presence of ethanolamine. With the Cr²⁺–CHCl₃ system, on addition of ethanolamine, the polymerization of methyl methacrylate was accelerated, and acrylonitrile and vinyl chloride, could be polymerized.     

Alternating copolymerization of ethylene with maleic anhydride

The copolymerization of ethylene with maleic anhydride was carried out with γ-radiation and a radical initiator, i.e., 2,2′-azobisisobutyronitrile and diisopropyl peroxydicarbonate under pressure at various reaction conditions. The homopolymerization of neither monomer was observed in this system. In the γ-ray-initiated copolymerization the G value (polymerized monomer molecules per 100 e.v.) was shown to be between 10³ and 10⁴. It was found that the dose rate exponent of the rate is approximately unity, and the rate is proportional to the amount of ethylene monomer. Apparent activation energies of 1.8 and 27.5 kcal./mole were obtained for γ-ray-initiated and AIBN-initiated copolymerization, respectively. Since the composition of copolymer is independent of monomer molar ratio and the molar ratio of ethylene to maleic anhydride in the polymer is approximately unity, the monomer reactivity ratios were obtained as r_E ? 0 and r_M ? 0 for γ-ray-initiated polymerization at 40°C. Alternating copolymerization was, therefore, concluded to occur. Infrared analysis of the copolymer is almost consistent with this. The copolymer in the solid state is amorphous. It is soluble in water, cyclohexane, and dimethylformamide and insoluble in lower alcohols, ether, and aromatic hydrocarbons. The aqueous solution of polymer gave a strong acid.     

Cyclopolymerization of isoprene with VCl4–AlEt2Br catalyst system

Isoprene was polymerized at 30°C with VCl₄–AlEt₂Br catalyst system in n-hexane. A linear dependence of rate of polymerization on the monomer and catalyst concentrations was found. The overall activation energy was 8.96 kcal/mole. Infrared spectra of polyisoprene showed the presence of cyclic structure, indicating a cationic mechanism of polymerization.     

Polymerization initiated by an electron donor–acceptor complex. VI. Polymerization of methyl methacrylate initiated by a liquid SO2–nicotine complex and carbon tetrachloride

A kinetic study has been made of polymerization of methyl methacrylate initiated by an electron donor–acceptor complex of liquid SO₂ (electron acceptor) and nicotine (donor) in the presence of carbon tetrachloride. It is concluded that the polymerization proceeds through free-radical intermediates similar to the cases of liquid SO₂–pyridine and liquid SO₂–poly(2-vinylpyridine) complexes. The overall rate of polymerization is proportional to the square root of both liquid SO₂ and nicotine concentrations, and the values of k_p/k_t^½ under various polymerization conditions are in satisfactory agreement with the literature values. For the activation energy of initiation, 13.6 kcal/mole is estimated from the k_p/k_t^½ values obtained at temperatures ranging from 0 to 80°C.