Influence of gel composition on the solubility parameter of poly(2‐hydroxyethyl methacrylate‐itaconic acid) hydrogels

The solubility parameters of pure poly(2‐hydroxyethyl methacrylate) (PHEMA) and poly(2‐hydroxyethyl methacrylate/itaconic acid) [P(HEMA/IA)] hydrogels were determined by 20 solvents with various solubility parameters in swelling experiments. The solubility parameter of pure PHEMA was 26.93 ± 0.46 (MPa)^1/2. The effect of mole percentages of itaconic acid (IA) in P(HEMA/IA) hydrogels on the solubility parameter was investigated. The measured values were compared to literature and solubility values theoretically determined by group contribution values of van Krevelen and Hoy. The incorporation of IA into the hydrogel system slightly increased the solubility parameter. © 2002 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 40: 1995–2003, 2002     

Synthesis and characterization of temperature‐ and pH‐sensitive hydrogels based on poly(2‐ethyl‐2‐oxazoline) and poly(D,L‐lactide)

A novel series of temperature‐ and pH‐sensitive hydrogels based on poly(2‐ethyl‐2‐oxazoline) and three‐arm poly(D,L ‐lactide) were synthesized via photocopolymerization. For the creation of polymeric networks, two types of macromers terminated with methacrylate groups were prepared: poly(2‐ethyl‐2‐oxazoline) dimethacrylate and three‐arm poly(D,L ‐lactide) trimethacrylate. The chemical structures were analyzed with ¹H NMR and Fourier transform infrared techniques. The thermal behaviors, morphologies, and swelling properties were measured for the characterization of the polymeric networks. All the poly(2‐ethyl‐2‐oxazoline)/three‐arm poly(D,L ‐lactide)hydrogels provided high water retention capacity and exhibited reversible swelling–shrinking behavior in response to temperature and pH variations. The hydrogels with higher poly(2‐ethyl‐2‐oxazoline) dimethacrylate contents were more effective in raising the swelling ratio and temperature and pH sensitivity. However, higher contents of three‐arm poly(D,L ‐lactide) trimethacrylate produced larger particles and pore sizes in the hydrogels. This study effectively proves that this unique combination of water swellability and biodegradability provides hydrogels with a much wider range of applications in biomedical fields. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1112–1121, 2002     

β‐Cyclodextrin hydrogel incorporating hydrophobically modified poly(N‐isopropylacrylamide) for a temperature‐dependent release

Hydrogels exhibiting a temperature‐dependent release were prepared by incorporating hydrophobically modified poly(N‐isopropylacrylamide) (HmPNIPAM) into β‐cyclodextrin hydrogels (β‐CD hydrogels). The specific loading of HmPNIPAM was about 0.0069 g HmPNIPAM/g β‐CD hydrogels. The incorporation of the polymer was qualitatively conformed by FT‐IR spectroscopy and SEM. The percent release of blue dextran in 24 hr at 20°C (about 77%) was markedly higher than those obtained at 35°C and 45°C (about 53 and 55%, respectively). At the higher temperatures, the volume of the hydrogel could decrease upon the thermal contraction of HmPNIPAM, leading to a smaller mesh and a suppressed release. In fact, the swelling ratio in 24 hr at 35°C and 45°C (about 396% and 405%, respectively) was obviously lower than that obtained at 20°C (about 465%). Copyright © 2011 John Wiley & Sons, Ltd.     

Surface modification of poly(2‐hydroxyethyl methacrylate) hydrogel for contact lens application

The present study examined poly(2‐hydroxyethyl methacrylate) (PHEMA)‐based hydrogels that have been extensively used in biomedical applications, including contact lens. In this research, we aimed to reduce adsorption of protein components from tears and bacterial deposition by surface modification of the hydrogel with different functional groups that included carboxylic acid, primary amine, and quaternary ammonium. The PHEMA was treated with a solution of sulfuric acid for partial hydrolysis of the HEMA ester groups to induce acid groups on the surface of the hydrogel. Carboxylic acid groups of the modified PHEMA were converted to primary amine and quaternary ammonium groups via carbodiimide chemistry. The surface physical and chemical properties of different samples were investigated by atomic force microscopy and X‐ray photoelectron spectroscopy, respectively. We conducted the bicinchoninic acid assay to evaluate protein deposition from artificial tear fluid on samples. Antibacterial properties of the modified hydrogels were investigated with a culture of Staphylococcus aureus, one of the major causes of eye infections. Our data showed that positively charged amine and ammonium groups efficiently resisted protein adsorption and bacterial deposition compared to alcohol and carboxylic acid groups.     

Interpretation of the polyelectrolyte and antipolyelectrolyte effects of poly(N‐vinylimidazole‐co‐sodium styrenesulfonate) hydrogels

Hydrogels of N‐vinylimidazole (VI) and sodium styrenesulfonate (SSS) were synthesized in aqueous solution by radical crosslinking copolymerization with N,N′‐methylene‐bis(acrylamide) as crosslinker. Swelling in several saline solutions was measured for hydrogel samples synthesized with different comonomer concentrations (C_T = 10, 25, or 40%) and with SSS mole fractions covering a broad range (f_SSS = 0–0.7), while the crosslinker ratio was 2 wt % in all cases. The degree of swelling in aqueous solution with a specific ionic strength (μ), plotted versus the SSS composition of the feed, shows a minimum for any set of samples synthesized with a fixed C_T. The dependence of swelling on μ shows both polyelectrolyte (f_SSS beyond the minimum) and antipolyelectrolyte behaviors (in the low f_SSS limit). It was found that the nonGaussian factor of the crosslinking density and the polymer‐solvent interaction parameter increase with f_SSS for any C_T. Moreover, in the low f_SSS limit, the osmotic swelling pressure is governed not only by the ionic contribution, but also by the polymer‐solvent mixing and, the concentration of mobile counterions inside the gel is not proportional to the net fixed charge but to the addition of cationic and anionic side groups, what discards the formation of ionic pairs. The antipolyelectrolyte effect is interpreted as due to the increasing protonation of VI as μ goes up. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 1683–1693, 2007     

Poly(methacrylamide‐co‐2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid) hydrogels: Investigation of pH‐ and temperature‐dependent swelling characteristics and their characterization

Novel poly(methacrylamide‐co‐2‐acrylamido‐2‐methyl‐ 1‐propanesulfonic acid) (poly(MAAm‐co‐AMPS)) hydrogels were synthesized by free radical polymerization of methacrylamide (MAAm) and 2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid (AMPS) in deionized water at 60 °C by using ammonium peroxydisulfate (APS), N,N′‐methylenebisacrylamide (MBAAm) and N,N,N′,N′‐tetramethylethylenediamine (TEMED) as initiator, crosslinker, and activator, respectively. To investigate the effects of feed content on the pH‐ and temperature‐dependent swelling behavior of poly(MAAm‐co‐AMPS), molar ratio of MAAm to AMPS in feed was varied from 90/10 to 10/90. Structural characterization of gels was performed by Fourier transform infrared (FTIR) spectroscopy using attenuated total reflectance (ATR) technique. Thermal and morphological characterizations of gels were performed by thermogravimetric analysis (TGA) and scanning electron microscopy (SEM), respectively. Although an apparent pH‐sensitivity was not observed for the poly(MAAm‐co‐AMPS) gels during the swelling in different buffer solutions, their temperature‐sensitivity became more evident with the increase in AMPS content of copolymer. Thermal stability of poly(MAAm‐co‐AMPS) gels increased with MAAm content. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Temperature‐induced spontaneous sol–gel transitions of poly(D,L‐lactic acid‐co‐glycolic acid)‐b‐poly(ethylene glycol)‐b‐poly(D,L‐lactic acid‐co‐glycolic acid) triblock copolymers and their end‐capped derivatives in water

The spontaneous hydrogel formation of a sort of biocompatible and biodegradable amphiphilic block copolymer in water was observed, and the underlying gelling mechanism was assumed. A series of ABA‐type triblock copolymers [poly(D,L ‐lactic acid‐co‐glycolic acid)‐b‐poly(ethylene glycol)‐b‐poly(D,L ‐lactic acid‐co‐glycolic acid)] and different derivatives end‐capped by small alkyl groups were synthesized, and the aqueous phase behaviors of these samples were studied. The virgin triblock copolymers and most of the derivatives exhibited a temperature‐dependent reversible sol–gel transition in water. Both the poly(D,L ‐lactic acid‐co‐glycolic acid) length and end group were found to significantly tune the gel windows in the phase diagrams, but with different behaviors. The critical micelle concentrations were much lower than the associated critical gel concentrations, and an intact micellar structure remained after gelation. A combination of various measurement techniques confirmed that the sol–gel transition with an increase in the temperature was induced not simply via the self‐assembly of amphiphilic polymer chains but also via the further hydrophobic aggregation of micelles resulting in a micelle network due to a large‐scale self‐assembly. The coarsening of the micelle network was further suggested to account for the transition from a transparent gel to an opaque gel. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 1122–1133, 2007     

Thermo‐ and pH‐induced phase transitions and network parameters of poly(N‐isopropylacrylamide‐ co‐2‐acrylamido‐2‐methyl‐propanosulfonic acid) hydrogels

Dual temperature‐ and pH‐sensitive hydrogels composed of N‐isopropylacrylamide (NIPAM) and 2‐acrylamido‐2‐methyl‐propanosulfonic acid (AMPS) were prepared by free‐radical crosslinking copolymerization in aqueous solution at 22 °C. The mole percent of AMPS in the comonomer feed was varied between 0.0 and 7.5, while the crosslinker ratio was fixed at 5.0/100. The effect of AMPS content on thermo‐ and pH‐ induced phase transitions as well as equilibrium swelling/deswelling, interior morphology and network structure was investigated. The volume phase transition temperature (VPT‐T) was determined by both swelling/deswelling measurements and differential scanning calorimetry (DSC) technique. In addition, the volume phase transition pH (VPT‐pH) was detected from the derivative of the curves of the swelling ratio (dQ_v/dpH) versus pH. The polymer‐solvent interaction parameter (χ) and the average molecular mass between crosslinks ( ) of hydrogels were calculated from swelling ratios in buffer solutions at various pHs. The enthalpy (ΔH) and entropy (ΔS) changes appearing in the χ parameter of hydrogels were also determined by using the modified Flory–Rehner equation. The negative values for ΔH and ΔS indicated that the hydrogels had a negative temperature‐sensitive property in water, that is, swelling at a lower temperature and shrinking at a higher temperature. It was observed that the experimental swelling data of hydrogels at different temperature agreed with the modified Flory‐Rehner approach based on the affine network model. © 2008 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 46: 1713–1724, 2008     

Synthesis,complex formation,and dilute‐solution associative behavior of linear poly(methacrylic acid)‐graft‐poly(2‐ethyl‐2‐oxazoline)*

Poly(methacrylic acid) (PMA) and poly(2‐ethyl‐2‐oxazoline) (PEOZO) are a polyacid/polybase pair capable of forming reversible, pH‐responsive, hydrogen‐bonding complexes stabilized by hydrophobic effects in aqueous media. Linear PMA was modified with long‐chain (number‐average molecular weight: 10,000) PEOZO via statistical coupling reactions in organic media to prepare a series of PMA‐graft‐PEOZO copolymers. Potentiometric titrations revealed that the presence of tethered PEOZO markedly increases the pK_a values for PMA‐g‐PEOZO copolymers as compared with simple PMA/PEOZO mixtures at degrees of ionization, α, between 0.0 and 0.1. The dilute‐solution PMA–PEOZO intramolecular association has been probed by monitoring the PEOZO NMR spin–spin (T₂) relaxation as a function of pH. Covalently attached PEOZO side chains participate in complexation at higher values of α than untethered PEOZO. Surprisingly, most PEOZO side chains did not take part in hydrogen bonding at low α, and the highest level of PEOZO incorporation induced a decrease in the number of PMA/PEOZO hydrogen bonds. The polymer self‐diffusion as a function of α was measured with dynamic light scattering. At low pH, the copolymers had no charge and they were in a collapsed form. At high pH, the expected conformational expansion of the PMA units was enhanced at moderate levels of PEOZO incorporation. However, the highest PEOZO incorporation induced the onset of intramolecular associations between PEOZO units along the copolymer chains. Low shear rheometry and light scattering measurements were used in conjunction with the T₂ NMR measurements to propose a model consistent with the aforementioned behavior. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2520–2533, 2004     

Incorporation of poly(2‐acrylamido‐2‐methyl‐N‐propanesulfonic acid) segments into block and brush copolymers by ATRP

2‐Acrylamido‐2‐methyl‐N‐propanesulfonic acid (AMPSA) was successfully polymerized via atom transfer radical polymerization (ATRP) using a copper chloride/2,2′‐bipyridine (bpy) catalyst complex after in situ neutralization of the acidic proton in AMPSA with tri(n‐butyl)amine (TBA). A 5 mol % excess of TBA was required to completely neutralize the acid and prevent protonation of the bpy ligand, as well as to avoid side reactions caused by large excess of TBA. The use of activators generated by electron transfer (AGET) ATRP with ascorbic acid as reducing agent resulted in both increased conversion of the AMPSA monomer during polymerization (up to 50% with a 0.8 [ascorbic acid]/[Cu(II)] ratio) and much shorter polymerization times (<30 min). Block copolymers and molecular brushes containing AMPSA side chains were prepared using this method, and the solution and surface behavior of these materials were investigated. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5386–5396, 2009     

Comprehensive study on the formation of polyelectrolyte complexes from (quaternized) poly[2‐(dimethylamino)ethyl methacrylate] and poly(2‐acrylamido‐2‐methylpropane sodium sulfonate)

Polyelectrolyte complexes (PECs) have been prepared from well‐defined (quaternized) poly[2‐(dimethylamino)ethyl methacrylate] (PDMAEMA) and high molecular weight poly(2‐acrylamido‐2‐methylpropane sodium sulfonate) (PAMPSNa) after a thorough study of their viscometric properties. The effect of pH and quaternization degree of PDMAEMA on PECs stoichiometry has been examined. PEC‐based materials have been characterized in terms of thermal stability, equilibrium swelling degree, and free/bound water composition. The stoichiometry and swellability of the physically crosslinked hydrogels obtained from fully quaternized PDMAEMA/PAMPSNa complexes do not depend on pH. In contrast, PECs made of non quaternized PDMAEMA and PAMPSNa are highly affected by pH, and could reversibly disintegrate at pH ≥ 9. Partially quaternized PDMAEMA/PAMPSNa PECs exhibit intermediate properties and form stable loose structures in the whole investigated pH range. Finally, stable dispersions of PECs nanoparticles have been successfully produced from dilute solutions of the complementary polyelectrolytes. The nanoparticle average diameter as determined by dynamic light scattering proved to depend on the molar fraction of DMAEMA‐based subunits and on the initial polyelectrolyte concentration. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5468–5479, 2006     

Synthesis and characterization of poly(ethylene glycol)‐based thermo‐responsive polyurethane hydrogels for controlled drug release

The thermo‐responsiveness, swelling and mechanical properties of a series of novel poly(ester‐ether urethane) hydrogels have been investigated. These thermo‐sensitive hydrogels were obtained by combining hydrophobic biodegradable poly(ε‐caprolactone) diols and hydrophilic two‐, three‐ and four‐arm hydroxyl terminated poly(ethylene glycol) (PEG) of various molecular weights, using hexamethylene diisocyanate, dichloroethane as solvent and a tin‐based catalyst. The use of multifunctional PEGs leads to the formation of covalent crosslinking points allowing an additional control of the swelling capability. Thus, it was found that tuning the hydrophilic/hydrophobic balance and the crosslinking degree by changing the composition, the swelling and the thermo‐responsive behavior of these hydrogels could be modulated. The obtained hydrogels showed a volume transition at around room temperature. Therefore, and taking into account their biocompatibility, these hydrogels show promising properties for biomedical applications, such as drug delivery. Thus, the loading and release of diltiazem hydrochloride, an antihypertensive drug used as model, were investigated. These new PEG polyurethane hydrogels were able to incorporate a high amount of drug providing a sustained release after an initial burst effect. Copyright © 2013 John Wiley & Sons, Ltd.     

Mizoroki–Heck and Suzuki–Miyaura reactions mediated by poly(2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid)‐stabilized magnetically separable palladium catalyst

The purpose of this work was to synthesize and characterize a new magnetic polymer nanosphere‐supported palladium(II) acetate catalyst for reactions requiring harsh conditions. In this regard, an air‐stable, moisture‐stable and highly efficient heterogenized palladium was synthesized by the coordination of palladium(II) acetate with poly(2‐acrylamido‐2‐methyl‐1‐propanesulfonic acid)‐grafted modified magnetic nanoparticles with a core–shell structure. The structure of the newly developed catalyst was characterized using various techniques. The catalytic activity of the resultant nano‐organometallic catalyst was evaluated in Mizoroki–Heck and Suzuki–Miyaura reactions to afford the corresponding coupling products in good to excellent yields. High selectivity as well as outstanding turnover number (14 143, 4900) and turnover frequency (28 296, 7424) values were recorded for the catalyst in Suzuki–Miyaura and Mizoroki–Heck reactions, respectively. Magnetic separation and recycling of the catalyst for at least six runs became possible without any significant loss of efficiency or any detectable palladium leaching.     

Impact of low‐molecular mass components (oligomers) on the glass transition in thin films of poly(methyl methacrylate)

Commercial polydisperse atactic poly(methyl methacrylate) (PMMA) exhibits a decreased glass transition temperature (T_g) when the film thickness is less than ～60 nm, whereas more model atactic PMMA shows an increased T_g in thin films supported on clean silicon wafers. NMR indicates no difference in tacticity, so the divergent thin film behavior appears related to the relative distribution of molecular mass. Extraction of some low molecular weight PMMA components from the commercial sample results in a significant modification of the thin film T_g compared with the initial PMMA fraction. The extracted sample exhibits initially a slight decrease in T_g as the film thickness is reduced below ～60 nm, but then T_g appears to increase for films thinner than 20 nm. These results illustrate the sensitivity of polymer thin film properties to low‐molecular mass components and could explain some of the contradictory reports on the T_g of polymer thin films that exist in the literature. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

Synthesis of cationic water‐soluble copolymers and hydrogels based on [2‐(methacryloyloxy)ethyl]trimethylammonium chloride and 2‐hydroxyethylacrylate and their complex formation with poly(acrylic acid)

Water‐soluble cationic copolymers and hydrogels were synthesized by radical copolymerization of [2‐(methacryloyloxy)ethyl]trimethylammonium chloride (MADQUAT) and 2‐hydroxyethylacrylate (HEA). The kinetics of copolymerization has been studied and the reactivity ratios were determined. It was found that MADQUAT exhibits higher reactivity in copolymerization. The complexation between linear MADQUAT‐HEA and linear poly(acrylic acid) (PAA) has been studied in aqueous solutions at different pH. It results in the formation of insoluble polyelectrolyte complexes, whose composition and stability to aggregate depends on MADQUAT content in copolymers and pH. The hydrogels were synthesized by three‐dimensional radical copolymerization of MADQUAT and HEA in the presence of a crosslinker. The effects of the feed mixture composition on yield and swelling properties of the hydrogels were studied. The interactions of these hydrogels with linear PAA result in formation of gel–polyelectrolyte complexes and contraction of the samples. It was found that the contraction depends on copolymer composition, PAA molecular weight, and solution pH. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44:845–853, 2006     

Site‐specific reversible immobilization and purification of His‐tagged protein on poly(2‐acetamidoacrylic acid) hydrogel beads

Ni²⁺‐complexed poly(2‐acetamidoacrylic acid) (PAAA) hydrogel beads were developed for the site‐specific reversible immobilization and purification of the histidine‐tagged green fluorescent protein (His‐tagged GFP). PAAA hydrogel beads were prepared by photopolymerization, and significantly improved mechanical properties of PAAA hydrogel beads were observed in comparison with PAAA hydrogel from our previous study. Confocal laser scanning microscopy was used to determine the binding of His‐tagged GFP to the hydrogel beads in three‐dimensional space. Photoluminescence spectroscopy revealed 89% of binding efficiency of His‐tagged GFP to the Ni²⁺‐PAAA hydrogel beads, 51% of yielding recovery. The maximum binding capacity of His‐tagged GFP was estimated to be 0.45 µg/mg of Ni²⁺‐PAAA hydrogel beads. The recombinant His‐tagged GFP from the soluble fraction of E. coli BL21(DE3) cell lysates was purified with Ni²⁺‐PAAA hydrogel beads. The major advantage of the Ni²⁺‐PAAA hydrogel beads system was simple preparation procedures of producing the matrix, because PAAA hydrogel beads had relatively enhanced mechanical strength than soft hydrogels. Copyright © 2012 John Wiley & Sons, Ltd.     

Miscibility and surface characterization of a poly(vinylidene fluoride)‐poly(vinyl methyl ketone) blend by inverse gas chromatography

The miscibility of blends of semicrystalline poly(vinylidene fluoride)(PVF₂) and poly(vinyl methyl ketone) (PVMK) along with surface characterization were investigated using the inverse gas chromatography method (IGC), over a range of blend compositions and temperatures. Three chemically different families, alkanes, acetates, and alcohols, were utilized for this study. The values of the PVF₂‐PVMK interaction parameters were found to be slightly positive for most of the solutes used, although some degree of miscibility was found at all compositions. Miscibility was greatest at a 50:50 w/w composition of the blend. The interaction parameters obtained from IGC are in excellent agreement with those obtained using calorimetry on the same blends. The calculated molar heat of sorption of alkanes, acetates, and alcohols into the blend layer reveal the impact of the combination of dispersive and hydrogen bonding forces on the interaction of solutes with the blend's backbone. The dispersive component of the surface energy was found to range from 18.70–64.30 mJ/m² in the temperature range of 82–163 °C. A comparison of the blend's surface energy with that of mercury and other polymers is given. © 2000 John Wiley & Sons, Inc. J Polym Sci B: Polym Phys 38: 1155–1166, 2000     

Investigation on the mechanical behavior of poly(2‐hydroxyethyl methacrylate) hydrogel membrane under compression in the assembly process of microfluidic system

A microfluidic system with an inserted membrane assembled using mechanical fastening process is described. The membrane is made of a biocompatible water swollen poly(2‐hydroxyethyl methacrylate) (PHEMA) hydrogel thin film as a sealing component. The hyperelastic characteristics of PHEMA membrane under the compression during fastening are investigated through numerical simulations, including strain and Von Mises stress distribution, and potential fracture in correlation with the microchannel's geometry and dimensions. To validate the modeling, the experiments have also been conducted to visualize the deformation induced in membrane and internal stress distribution using 3D optical measuring system. The results from this study have revealed the implications in connection with the mechanical behavior of the PHEMA membranes in the assembly of microfluidic system through mechanical fastening technique. This will ultimately assist to produce a guideline for the optimum design of microchannels in the uses of PHEMA membranes and associated assembly process. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 485–495