Synthetic pathway to functional block copolymers with pendent triphenylamine and ethynylpyridine: Effect of countercation on anionic polymerization behavior

The block copolymerization of 4,4′‐vinylphenyl‐N,N‐bis(4‐tert‐butylphenyl)benzenamine ( A ) with 2‐(2‐(4‐vinylphenyl)ethynyl)pyridine ( B ) was performed using sec‐butyllithium (s‐BuLi) as an initiator in the absence and presence of potassium tert‐butoxide (KOBu^t) in tetrahydrofuran (THF) at ?78 °C. The block copolymerization was not successful in the absence of KOBu^t, whereas the well‐defined diblock copolymer (poly( A ‐b‐ B )) containing pendent triphenylamine and ethynylpyridine was successfully synthesized in the presence of excess KOBu^t due to the change in the countercation from Li⁺ to K⁺ and the suppression of ion dissociation by the salt common effect. The poly( A ‐b‐ B )s had predictable molecular weights (M_n = 4,900–20,000 g/mol) and narrow molecular weight distributions (M_w/M_n = 1.13–1.15). In addition, the resulting block copolymer showed good solubility and excellent thermal properties. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4233–4239     

Effect of isomeric pyridine moieties in ethynylstyrene derivatives on their anionic polymerization

The anionic polymerization behaviors of ethynylstyrene derivatives containing isomeric pyridine moieties, 2‐(2‐(4‐vinylphenyl)ethynyl)pyridine ( A ), 3‐(2‐(4‐vinylphenyl)ethynyl)pyridine ( B ), and 4‐(2‐(4‐vinylphenyl)ethynyl)pyridine ( C ), were investigated in the identical conditions. The anionic polymerization of A – C was performed with (diphenylmethyl)potassium (Ph₂CHK) in tetrahydrofuran (THF) at ?78 °C. The polymerization of A proceeded quantitatively at –78 °C for 4 h, and the resulting poly( A ) possessed predictable molecular weights (M_n = 3300–68,500) and narrow molecular weight distributions (MWDs) (M_w/M_n = 1.04–1.11). In contrast, the anionic polymerization of B was not performed at –78 °C for 4 h due to the occurrence of side reactions. The monomer B was quantitatively recovered after the reaction. In the polymerization of C performed at –78 °C for 6 h, observed M_n values of the resulting poly( C ) were in good agreement with calculated molecular weights based on monomer to initiator ratios, but the MWDs were somewhat broad (M_w/M_n = 1.23–1.31). To estimate the reactivity of A and to characterize its living nature, the block copolymerization of A with 2‐vinylpyridine (2VP) and methyl methacrylate (MMA) was performed. The well‐defined block copolymers, poly(2VP)‐b‐poly( A ) and poly( A )‐b‐poly(MMA), were successfully synthesized without any additives. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Doubly thermoresponsive brush‐linear‐linear ABC triblock copolymer nanoparticles prepared through dispersion RAFT polymerization

Doubly thermoresponsive ABC brush‐linear‐linear triblock copolymer nanoparticles of poly[poly(ethylene glycol) methyl ether vinylphenyl]‐block‐poly(N‐isopropylacrylamide)‐block‐polystyrene [P(mPEGV)‐b‐PNIPAM‐b‐PS] containing two thermoresponsive blocks of poly[poly(ethylene glycol) methyl ether vinylphenyl] [P(mPEGV)] and poly(N‐isopropylacrylamide) (PNIPAM) are prepared by macro‐RAFT agent mediated dispersion polymerization. The P(mPEGV)‐b‐PNIPAM‐b‐PS nanoparticles exhibit two separate lower critical solution temperatures or phase‐transition temperatures (PTTs) corresponding to the linear PNIPAM block and the brush P(mPEGV) block in water. Upon temperature increasing above the first and then the second PTT, the hydrodynamic diameter (D_h) of the triblock copolymer nanoparticles undergoes an initial shrinkage at the first PTT and the subsequent shrinkage at the second PTT. The effect of the chain length of the PNIPAM block on the thermoresponsive behavior of the triblock copolymer nanoparticles is investigated. It is found that, the longer chains of the thermoresponsive PNIPAM block, the greater contribution on the transmittance change of the aqueous dispersion of the triblock copolymer nanoparticles. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2266–2278     

RAFT‐mediated emulsion polymerization of styrene using brush copolymer as surfactant macro‐RAFT agent: Effect of the brush copolymer sequence and chemical composition

The nonionic amphiphilic brush polymers such as poly[poly(ethylene oxide) methyl ether vinylphenyl‐co‐styrene] trithiocarbonate [P(mPEGV‐co‐St)‐TTC] and poly[poly(ethylene oxide) methyl ether vinylphenyl‐b‐styrene‐b‐poly(ethylene oxide) methyl ether vinylphenyl] trithiocarbonate [P(mPEGV‐b‐St‐b‐mPEGV)‐TTC] with different monomer sequence and chemical composition are synthesized and their application as macro‐RAFT agent in the emulsion RAFT polymerization of styrene is explored. It is found that the monomer sequence in the brush polymers exerts great influence on the emulsion RAFT polymerization kinetics, and the fast polymerization with short induction period in the presence of P(mPEGV‐co‐St)‐TTC is demonstrated. Besides, the chemical composition in the brush polymer macro‐RAFT agent effect on the emulsion RAFT polymerization is investigated, and the macro‐RAFT agent with high percent of the hydrophobic PS segment leads to fast and well controlled polymerization. The growth of triblock copolymer colloids in the emulsion polymerization is checked, and it reveals that the colloidal morphology is ascribed to the hydrophobic PS block extension, and the P(mPEGV‐co‐St) block almost have no influence just on the size of the colloids. This may be the first example to study the monomer sequence and the chemical composition in the macro‐RAFT agent on emulsion RAFT polymerization, and will be useful to reveal the block copolymer particle growth. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Block and random copolymerization of ε‐caprolactone,L‐, and rac‐lactide using titanium complex derived from aminodiol ligand

A series of di‐ and triblock copolymers [poly(L ‐lactide‐b‐ε‐caprolactone), poly(D,L ‐lactide‐b‐ε‐caprolactone), poly(ε‐caprolactone‐b‐L ‐lactide), and poly(ε‐caprolactone‐b‐L ‐lactide‐b‐ε‐caprolactone)] have been synthesized successfully by sequential ring‐opening polymerization of ε‐caprolactone (ε‐CL) and lactide (LA) either by initiating PCL block growth with living PLA chain end or vice versa using titanium complexes supported by aminodiol ligands as initiators. Poly(trimethylene carbonate‐b‐ε‐caprolactone) was also prepared. A series of random copolymers with different comonomer composition were also synthesized in solution and bulk of ε‐CL and D,L ‐lactide. The chemical composition and microstructure of the copolymers suggest a random distribution with short average sequence length of both the LA and ε‐CL. Transesterification reactions played a key role in the redistribution of monomer sequence and the chain microstructures. Differential scanning calorimetry analysis of the copolymer also evidenced the random structure of the copolymer with a unique T_g. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Polymerization and copolymerization of functionalized 2‐alkoxy‐1‐methylenecyclopropanes to form new polymers having alkoxy substituents

The polymers with functionalized alkoxy groups and with narrow molecular weight distribution (M_w/M_n < 1.12) are obtained from the living polymerization of 2‐alkoxy‐1‐methylenecyclopropanes using π‐allylpalladium complex, [(PhC₃H₄)Pd(μ‐Cl)]₂, as the initiator. The polymers with oligoethylene glycol groups in the alkoxy substituent are soluble in water, and hydroboration of the C?C double bond and ensuing addition of the OH groups to C?N bond of alkyl isocyanate produce the polymers with urethane pendant groups. The reaction decreases solubility of the polymer in water significantly. Di‐ and triblock copolymers of the 2‐alkoxy‐1‐methylenecyclopropanes are prepared by consecutive addition of the two or three 2‐alkoxy‐1‐methylenecyclopropane monomers to the Pd initiator. The polymers which contain both hydrophobic butoxy or tert‐butoxy group and hydrophilic oligoethylene glycol group dissolve in water and/or organic solvents, depending on the substituents. The ¹H NMR spectrum of poly( 1a ‐b‐ 1h ) (? (CH₂C(?CH₂)CHOBu)_n? (CH₂C(?CH₂)CH(OCH₂CH₂)₃OMe)_m? ) in D₂O solution exhibits peaks because of the butoxy and ?CH₂ hydrogen in decreased intensity, indicating that the polymer forms micelle particles containing the hydrophilic segments in their external parts. Aqueous solution of the polymer with a small amount of DPH (DPH = 1,6‐diphenyl‐1,3,5‐hexatriene) shows the absorbance due to DPH at concentration of the polymer higher than 5.82 × 10^?5 g mL^?1. Other block copolymers such as poly( 1b ‐b‐ 1h ) and poly( 1a ‐b‐ 1g ) also form the micelles that contain DPH in their core. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 959–972, 2009     

Synthesis of star‐shaped poly(D,L‐lactic acid‐alt‐glycolic acid)‐b‐poly(L‐lactic acid) with the poly(D,L‐lactic acid‐alt‐glycolic acid) macroinitiator and stannous octoate catalyst

Two types of three‐arm and four‐arm, star‐shaped poly(D,L ‐lactic acid‐alt‐glycolic acid)‐b‐poly(L ‐lactic acid) (D,L ‐PLGA50‐b‐PLLA) were successfully synthesized via the sequential ring‐opening polymerization of D,L ‐3‐methylglycolide (MG) and L ‐lactide (L ‐LA) with a multifunctional initiator, such as trimethylolpropane and pentaerythritol, and stannous octoate (SnOct₂) as a catalyst. Star‐shaped, hydroxy‐terminated poly(D,L ‐lactic acid‐alt‐glycolic acid) (D,L ‐PLGA50) obtained from the polymerization of MG was used as a macroinitiator to initiate the block polymerization of L ‐LA with the SnOct₂ catalyst in bulk at 130 °C. For the polymerization of L ‐LA with the three‐arm, star‐shaped D,L ‐PLGA50 macroinitiator (number‐average molecular weight = 6800) and the SnOct₂ catalyst, the molecular weight of the resulting D,L ‐PLGA50‐b‐PLLA polymer linearly increased from 12,600 to 27,400 with the increasing molar ratio (1:1 to 3:1) of L ‐LA to MG, and the molecular weight distribution was rather narrow (weight‐average molecular weight/number‐average molecular weight = 1.09–1.15). The ¹H NMR spectrum of the D,L ‐PLGA50‐b‐PLLA block copolymer showed that the molecular weight and unit composition of the block copolymer were controlled by the molar ratio of L ‐LA to the macroinitiator. The ¹³C NMR spectrum of the block copolymer clearly showed its diblock structures, that is, D,L ‐PLGA50 as the first block and poly(L ‐lactic acid) as the second block. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 40: 409–415, 2002     

Effect of polystyrene‐b‐poly(ethylene oxide) on self‐assembly of polystyrene‐b‐poly(N‐isopropylacrylamide) in aqueous solution

Mixed micelles of polystyrene‐b‐poly(N‐isopropylacrylamide) (PS‐b‐PNIPAM) and two polystyrene‐b‐poly(ethylene oxide) diblock copolymers (PS‐b‐PEO) with different chain lengths of polystyrene in aqueous solution were prepared by adding the tetrahydrofuran solutions dropwise into an excess of water. The formation and stabilization of the resultant mixed micelles were characterized by using a combination of static and dynamic light scattering. Increasing the initial concentration of PS‐b‐PEO in THF led to a decrease in the size and the weight average molar mass (〈M_w〉) of the mixed micelles when the initial concentration of PS‐b‐ PNIPAM was kept as 1 × 10^?3 g/mL. The PS‐b‐PEO with shorter PS block has a more pronounced effect on the change of the size and 〈M_w〉 than that with longer PS block. The number of PS‐b‐PNIPAM in each mixed micelle decreased with the addition of PS‐b‐PEO. The average hydrodynamic radius 〈R_h〉 and average radius of gyration 〈R_g〉 of pure PS‐b‐PNIPAM and mixed micelles gradually decreased with the increase in the temperature. Both the pure micelles and mixed micelles were stable in the temperature range of 18 °C–39 °C. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 48: 1168–1174, 2010     

Synthesis and micellization of thermoresponsive galactose‐based diblock copolymers

Thermoresponsive double hydrophilic diblock copolymers poly(2‐(2′‐methoxyethoxy)ethyl methacrylate‐co‐oligo(ethylene glycol) methacrylate)‐b‐poly(6‐O‐methacryloyl‐D ‐galactopyranose) (P(MEO₂MA‐co‐OEGMA)‐b‐PMAGP) with various compositions and molecular weights were obtained by deprotection of amphiphilic diblock copolymers P(MEO₂MA‐co‐OEGMA)‐b‐poly(6‐O‐methacryloyl‐1,2:3,4‐di‐O‐isopropylidene‐D ‐galactopyranose) (P(MEO₂MA‐co‐OEGMA)‐b‐PMAlpGP), which were prepared via reversible addition‐fragmentation chain transfer (RAFT) polymerization using P(MEO₂MA‐co‐OEGMA) as macro‐RAFT agent. Dynamic light scattering and UV–vis studies showed that the micelles self‐assembled from P(MEO₂MA‐co‐OEGMA)‐b‐PMAlpGP were thermoresponsive. A hydrophobic dye Nile Red could be encapsulated by block copolymers P(MEO₂MA‐co‐OEGMA)‐b‐PMAGP upon micellization and released upon dissociation of the formed micelles under different temperatures. The galactose functional groups in the PMAGP block have specific interaction with HepG2 cells, and P(MEO₂MA‐co‐OEGMA)‐b‐PMAGP has potential applications in hepatoma‐targeting drug delivery and biodetection. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis and characterization of novel biodegradable block copolymer poly(ethylene glycol)‐block‐poly(L‐lactide‐co‐2‐methyl‐2‐carboxyl‐propylene carbonate)

An amphiphilic block copolymer, poly(ethylene glycol)‐block‐poly(L ‐lactide‐co‐2‐methyl‐2‐benzoxycarbonyl‐propylene carbonate) [PEG‐b‐P(LA‐co‐MBC)], was synthesized in bulk by the ring‐opening polymerization of L ‐lactide with 2‐methyl‐2‐benzoxycarbonyl‐propylene carbonate (MBC) in the presence of poly(ethylene glycol) as a macroinitiator with diethyl zinc as a catalyst. The subsequent catalytic hydrogenation of PEG‐b‐P(LA‐co‐MBC) with palladium hydroxide on activated charcoal (20%) as a catalyst was carried out to obtain the corresponding linear copolymer poly(ethyleneglycol)‐block‐poly(L ‐lactide‐co‐2‐methyl‐2‐carboxyl‐propylenecarbonate) [PEG‐b‐P(LA‐co‐MCC)] with pendant carboxyl groups. DSC analysis indicated that the glass‐transition temperature (T_g) of PEG‐b‐P(LA‐co‐MBC) decreased with increasing MBC content in the copolymer, and T_g of PEG‐b‐P(LA‐co‐MCC) was higher than that of the corresponding PEG‐b‐P(LA‐co‐MBC). The in vitro degradation rate of PEG‐b‐P(LA‐co‐MCC) in the presence of proteinase K was faster than that of PEG‐b‐P(LA‐co‐MBC), and the cytotoxicity of PEG‐b‐P(LA‐co‐MCC) to chondrocytes from human fetal arthrosis was lower than that of poly(L ‐lactide). © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4771–4780, 2005     

Synthesis of polyimides containing triphenylamine‐substituted triazole moieties for polymer memory applications

A series of thermally stable aromatic polyimides containing triphenylamine‐substituted triazole moieties ( AZTA‐PI )s were prepared and characterized. The glass transition temperatures (T_g) of the polyimides were found to be in the range of 262–314 °C. The polyimides obtained by chemical imidization had inherent viscosities of 0.25–0.44 dL g^?1 in N‐methyl‐2‐pyrrolidinone. The number average molecular weights (M_n) and weight average molecular weights (M_w) were 1.9–3.2 × 10⁴ and 3.2–5.6 × 10⁴, respectively, and the polydispersity indices (PDI = M_w/M_n) were in the range of 1.70–1.78. A resistive switching device was constructed from the 4,4′‐hexafluoroisopropylidenediphthalic dianhydride‐based soluble polyimide ( AZTA‐PIa ) in a sandwich structure of indium‐tin oxide/polymer/Al. The as‐fabricated device can be switched from the initial low‐conductivity (OFF) state to the high‐conductivity (ON) state at a switching threshold voltage of 2.5 V under either positive or negative electrical sweep, with an ON/OFF state current ratio in the order of 10⁵ at ?1 V. The device is able to remain in the ON state even after turning off the power or under a reverse bias. The nonvolatile and nonrewritable natures of the ON state indicate that the device is a write‐once read‐many times (WORM) memory. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Novel thermoresponsive fluorinated double‐hydrophilic poly{[N‐(2,2‐difluoroethyl)acrylamide]‐b‐[N‐(2‐fluoroethyl)acrylamide]} block copolymers

Novel thermoresponsive double‐hydrophilic fluorinated block copolymers were successfully synthesized by reversible addition‐fragmentation chain transfer (RAFT) polymerization. Poly[N‐(2,2‐difluoroethyl)acrylamide] (P2F) was synthesized via RAFT polymerization of N‐(2,2‐difluoroethyl)acrylamide (M2F) using 2‐dodecylsulfanylthiocarbonylsulfanyl‐2‐methylpropionic acid (DMP) as the chain transfer agent (CTA) and 2,2′‐azobisisobutyronitrile (AIBN) as the initiator. The resulting P2F macroCTA was further chain extended with N‐(2‐fluoroethyl)acrylamide (M1F) to yield poly{[N‐(2,2‐difluoroethyl)acrylamide]‐b‐[N‐(2‐fluoroethyl)acrylamide]} (P2F‐b‐P1F) block copolymers with different lengths of the P1F block. Molecular weight and molecular weight distribution were determined by gel permeation chromatography. The average molecular weight (M_n) of the resulting polymers ranged from 2.9 × 10⁴ to 5.8 × 10⁴ depending on the length of the P1F block. The molecular weight distribution was low (M_w/M_n = 1.11–1.19). Turbidimetry by UV‐Visble (UV‐Vis) spectroscopy, dynamic light scattering, and in situ temperature‐dependent ¹H NMR measurements demonstrated that the P2F block underwent a thermal transition from hydrophilic to hydrophobic, which in turn induced self‐assembly from unimers to aggregates. Transmission electron microscopy studies demonstrated that polymeric aggregates formed from an aqueous solution of P2F‐b‐P1F at 60 °C were disrupted by cooling down to 20 °C and regenerated by heating to 60 °C. Temperature‐triggered release of a model hydrophobic drug, coumarin 102, was also demonstrated. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Synthesis and characterization of chiral poly(l‐lactide‐b‐hexyl isocyanate) macromonomers with norbornenyl end groups and their homopolymerization through ring opening metathesis polymerization to afford polymer brushes

We report the synthesis of the novel half‐titanocene alkoxide complex bischloro‐η⁵‐cyclopentadienyl(bicyclo[2.2.1]‐hept‐5‐en‐2‐oxy) titanium (IV), [CpTiCl₂(O‐NBE)]. This complex was employed for the synthesis of chiral poly(l ‐lactide‐b‐hexyl isocyanate) diblock copolymer bearing a norbornene end group with sequential addition of monomers. The poly(hexyl isocyanate) block is chiral due to the last l ‐lactide unit of the poly(l ‐lactide) block. This macromonomer was polymerized towards a chiral polymer brush structure with polynorbornene backbone and chiral poly(l ‐lactide‐b‐hexyl isocyanate) side chains using Grubbs first‐generation catalyst. The polymers were characterized using size exclusion chromatography (SEC), nuclear magnetic resonance (NMR), and circular dichroism (CD) spectroscopy and their thermal properties were investigated by thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) analysis. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55, 1102–1112     

Synthesis and properties of high‐molecular‐weight stereo di‐block polylactides with nonequivalent D/L ratios

Di‐stereoblock polylactides (di‐sb‐PLA: PLLA‐b‐PDLA) having high molecular weight (M_n > 100 kDa) were successfully synthesized by two‐step ring‐opening polymerization (ROP) of L ‐ and D ‐lactides using tin(2‐ethylhexanoate) as a catalyst. By optimizing the polymerization conditions, the block sequences were well regulated at non‐equivalent feed ratios of PLLA and PDLA. This synthetic method consisted of three stages: (1) polymerization of either L ‐ or D ‐lactide to obtain a PLLA or PDLA prepolymer with a molecular weight less than 50 kDa, (2) purification of the obtained prepolymer to remove residual lactide, and (3) polymerization of the enantiomeric lactide in the presence of the purified prepolymer. Their ¹³C and ³¹P NMR spectra of the resultant di‐sb‐PLAs strongly supported their di‐stereo block structure. These di‐sb‐PLAs, having weight‐average molecular weights higher than 150 kDa, were fabricated into polymer films by solution casting and showed exclusive stereocomplexation. The thermomechanical analysis of the films revealed that their heat deformation temperature was limited probably because of their low crystallinity owing to the non‐equivalent PLLA/PDLA ratio. The blend systems of the di‐sb‐PLAs having complementary stereo‐sequences (the one with a long PLLA block and the other with long PDLA block) were also prepared and characterized to enhance the sc crystallinity. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 794–801, 2010     

Synthesis,characterization, effect of architecture on crystallization,and spherulitic growth of poly(L‐lactide)‐b‐poly(ethylene oxide) copolymers with different branch arms

Well‐defined poly(L ‐lactide)‐b‐poly(ethylene oxide) (PLLA‐b‐PEO) copolymers with different branch arms were synthesized via the controlled ring‐opening polymerization of L ‐lactide followed by a coupling reaction with carboxyl‐terminated poly(ethylene oxide) (PEO); these copolymers included both star‐shaped copolymers having four arms (4sPLLA‐b‐PEO) and six arms (6sPLLA‐b‐PEO) and linear analogues having one arm (LPLLA‐b‐PEO) and two arms (2LPLLA‐b‐PEO). The maximal melting point, cold‐crystallization temperature, and degree of crystallinity (X_c) of the poly(L ‐lactide) (PLLA) block within PLLA‐b‐PEO decreased as the branch arm number increased, whereas X_c of the PEO block within the copolymers inversely increased. This was mainly attributed to the relatively decreasing arm length ratio of PLLA to PEO, which resulted in various PLLA crystallization effects restricting the PEO block. These results indicated that both the PLLA and PEO blocks within the block copolymers mutually influenced each other, and the crystallization of both the PLLA and PEO blocks within the PLLA‐b‐PEO copolymers could be adjusted through both the branch arm number and the arm length of each block. Moreover, the spherulitic growth rate (G) decreased as the branch arm number increased: G_{6sPLLA‐b‐PEO} < G_{4sPLLA‐b‐PEO} < G_{2LPLLA‐b‐PEO} < G_{LPLLA‐b‐PEO}. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2034–2044, 2006     

Diels‐alder click reaction for the preparation of polycarbonate block copolymers

The Diels‐Alder reaction as a click reaction strategy is applied to the preparation of well‐defined polycarbonate (PC)‐block copolymers. A well‐defined α‐anthracene‐terminated polycarbonate (PC‐anthracene) is prepared using 9‐anthracene methanol as an initiator in the ring opening polymerization of benzyl 5‐methyl‐2‐oxo‐1,3‐dioxane‐5‐carboxylate in CH₂Cl₂ at room temperature for 5 h. Next, a well‐defined α‐furan protected maleimide‐terminated‐poly(ethylene glycol) (PEG₁₁‐MI or PEG₃₇‐MI), ‐poly(methyl methacrylate) (PMMA₂₆‐MI), and ‐poly(ε‐caprolactone) (PCL₂₇‐MI) were clicked with the PC‐anthracene at reflux temperature of toluene to yield their corresponding PC‐based block copolymers (PC‐b‐PEG, PC‐b‐PMMA, and PC‐b‐PCL). The homopolymer precursors and their block copolymers were characterized by using the GPC, NMR and UV analysis. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Diblock copolymer–azobenzene complexes through hydrogen bonding: Self‐assembly and stable photoinduced optical anisotropy

We have demonstrated the preparation of a series of photoaddressable supramolecular block copolymers by mixing a carboxy‐terminated azobenzene derivative, 6‐[4‐(4′‐cyanophenylazo)phenyloxy]hexanoic acid (AZO), and two polystyrene‐b‐poly(4‐vinylpiridine) (PS‐b‐P4VP) block copolymers. AZO can be selectively attached to the P4VP block of PS‐b‐P4VP through hydrogen bonding interactions. The assembly of AZO with vinylpyridine group‐containing polymers was initially investigated on a model system composed of P4VP homopolymer and AZO. Homogeneous liquid crystalline materials were obtained for ratios of AZO to vinylpyridine repeating unit, x, lower or equal to 0.50. Mixtures with higher x resulted in heterogeneous materials showing clear macrophase separation. Accordingly, a series of hydrogen‐bonded complexes of PS‐b‐P4VP and AZO, PS‐b‐P4VP(AZO)_x, with x = 0.25 and x = 0.50 were prepared. Lamellar and spherical morphologies were observed for the complexes based on PS24‐b‐P4VP9.5 (M_n,PS = 24,000, M_n,P4VP = 9500) and PS24‐b‐P4VP1.9 (M_n,PS = 24,000, M_n,P4VP = 1900), respectively. Photoinduced orientation of the azobenzene units was obtained in films of P4VP(AZO)_x and PS‐b‐P4VP(AZO)_x with x = 0.25 and 0.50 by using 488 nm linearly polarized light and characterized through birefringence and dichroism measurements. This investigation shows a versatile and less laborious approach to azobenzene‐containing polymer materials with low chromophore content, of interest in optical application. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Titanium‐mediated [CpTiCl2(OEt)] ring‐opening polymerization of lactides: A novel route to well‐defined polylactide‐based complex macromolecular architectures

Among three cyclopentadienyl titanium complexes studied, CpTiCl₂(OEt), containing a 5% excess CpTiCl₃, has proven to be a very efficient catalyst for the ring‐opening polymerization (ROP) of L ‐lactide (LLA) in toluene at 130 °C. Kinetic studies revealed that the polymerization yield (up to 100%) and the molecular weight increase linearly with time, leading to well‐defined PLLA with narrow molecular weight distributions (M_w/M_n ≤ 1.1). Based on the above results, PS‐b‐PLLA, PI‐b‐PLLA, PEO‐b‐PLLA block copolymers, and a PS‐b‐PI‐b‐PLLA triblock terpolymer were synthesized. The synthetic strategy involved: (a) the preparation of OH‐end‐functionalized homopolymers or diblock copolymers by anionic polymerization, (b) the reaction of the OH‐functionalized polymers with CpTiCl₃ to give the corresponding Ti‐macrocatalyst, and (c) the ROP of LLA to afford the final block copolymers. PMMA‐g‐PLLA [PMMA: poly(methyl methacrylate)] was also synthesized by: (a) the reaction of CpTiCl₃ with 2‐hydroxy ethyl methacrylate, HEMA, to give the Ti‐HEMA‐catalyst, (b) the ROP of LLA to afford a PLLA methacrylic‐macromonomer, and (c) the copolymerization (conventional and ATRP) of the macromonomer with MMA to afford the final graft copolymer. Intermediate and final products were characterized by NMR spectroscopy and size exclusion chromatography, equipped with refractive index and two‐angle laser light scattering detectors. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 1092–1103, 2010     

Syntheses,characterization, and properties of multiblock copolymers consisting of polyisobutylene and poly(L‐lactide) segments

The syntheses of {‐poly(L ‐lactide) (PLLA)‐b‐polyisobutylene (PIB)‐}_n multiblock copolymers were accomplished for the first time by chain extension of PLLA‐b‐PIB‐b‐PLLA triblock copolymers. Well‐defined PLLA‐b‐PIB‐b‐PLLA triblock copolymers with predictable M_ns, low PDIs (1.10–1.18) and excellent blocking efficiencies were prepared by anionic ring‐opening polymerizations of L ‐lactide initiated with hydroxyallyl telechelic PIB (HO‐Allyl‐PIB‐Allyl‐OH) in toluene at 110 °C. The triblock copolymers were successfully chain extended with 4,4′‐methylenebis(phenylisocyanate) (MDI) to obtain the multiblock copolymers with good gravimetric yields of ～86 to 96%. The chain‐extended polymers were soluble in a range of common organic solvents. The block copolymers showed two glass transition temperatures in differential scanning calorimetric analysis for the PIB and PLLA blocks indicating microphase separation, which was supported by atomic force microscopy images. The as‐synthesized compression molded multiblock copolymers exhibited tensile strengths in the range of 8–24 MPa with elongations at break in the range of 2.5–400%. The static and dynamic mechanical properties showed a strong dependence on the relative PLLA content in the copolymer. The dynamic mechanical analysis also indicated microphase separation at higher PLLA compositions. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3490–3505, 2009     

Synthesis of biodegradable thermoplastic elastomers from ε‐caprolactone and lactide

This article reports the synthesis and the properties of novel thermoplastic elastomers of A‐B‐A type triblock copolymer structure, where the hard segment A is poly(l ‐lactide) (PLLA) and the soft segment B is poly(ε‐caprolactone‐stat‐d ,l ‐lactide) (P(CL‐stat‐DLLA)). The P(CL‐stat‐DLLA) block with DLLA content of 30 mol % was applied because of its amorphous nature and low glass transition temperature (T_g = approximately ?40 °C). Successive polymerization of l ‐lactide afforded PLLA‐block‐P(CL‐stat‐DLLA)‐block‐PLLAs, which exhibited melting temperature (T_m = approximately 150 °C) for the crystalline PLLA segments and still low T_g (approximately ?30 °C) of the soft segments. The triblock copolymers showed very high elongation at break up to approximately 2800% and elastic properties. The corresponding d ‐triblock copolymers, PDLA‐block‐P(CL‐stat‐DLLA)‐block‐PDLAs (PDLA = poly(d ‐lactide)) were also prepared with the same procedure using d ‐lactide in place of l ‐lactide. When the PLLA‐block‐P(CL‐stat‐DLLA)‐block‐PLLA was blended with PDLA‐block‐P(CL‐stat‐DLLA)‐block‐PDLA, stereocomplex crystals were formed to enhance their T_m as well as tensile properties. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 489–495