The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Effect of pressure on the refractive index and relative density of the CaO · Al2O3 · 6SiO2 glass

The refractive index for glass of the CaO · Al₂O₃ · хSiO₂ system with х = 6 in the range of pressures up to 6.0 GPa was measured using a polarization-interference microscope and an apparatus with diamond anvils. The changes in the relative density characterizing the compressibility of glass were estimated from the measured refractive indices within the framework of the theory of photoelasticity. The data were compared with the previous data for glasses of the same system with х = 2 and 4. The most compressible of the three glasses in the range 2.0-6.0 GPa was the CaO · Al₂O₃ · 6SiO₂ glass. For glasses with х = 2, 4 and 6 we calculated the degrees of polymerization of silicon-aluminum-oxygen network, NBO/T (NBO - non-bridging oxygen), which are determined as the ratio of the number of gram-ions of non-bridging oxygen atoms to the total number of gram-ions of network formers. The structure-chemical parameter NBO/T was calculated with due regard for the formation of triclusters and highly coordinated aluminum. The degree of polymerization of the CaO · Al₂O₃ · хSiO₂ glasses increases with increasing х, which agrees with the change of their relative density under pressure.     

Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Specimens of the glassy system: (70 − x)TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO₂ by Li₂O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200-800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E_opt, and width tails, ΔE, are determined. It is observed that E_opt is decreased and ΔE increased with the increase of Li₂O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.     

Three-dimensional structure of fast ion conducting 0.5Li2S + 0.5[(1 − x)GeS2 + xGeO2] glasses from high-energy X-ray diffraction and reverse Monte Carlo simulations

A high-energy X-ray diffraction study has been carried out on a series of 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses with x = 0.0, 0.1, 0.2, 0.4, 0.6 and 0.8. Structure factors were measured to wave vectors as high as 30 Å⁻¹ resulting in atomic pair distribution functions with high real space resolution. The three dimensional atomic-scale structure of the glasses was modeled by reverse Monte Carlo simulations based on the diffraction data. Results from the simulations show that at the atomic-scale 0.5Li₂S + 0.5[(1 − x)GeS₂ + xGeO₂] glasses may be viewed as an assembly of independent chains of (Li^+-S)₂GeS_2/2 and (Li^+-O)₂GeO_2/2 tetrahedra as repeat units, where the Li ions occupy the open space between the chains. The new structure data may help understand the reasons for the sharp maximum in the Li⁺ ion conductivity at x ∼ 0.2.     

Thermal dissolution of Ag(Cu) in amorphous Ge(Sx Se1 − x)2 system

Thermally induced solid state reaction of Ag(Cu) into thin Ge(S_x Se_1 − x)₂ films with x = 0, 0.1, 0.4 and 1.0 was investigated using a step by step technique in order to design films with exact Ag(Cu) concentrations for applications in integrated IR optical devices. A thin film of Ag(Cu) was deposited on top of the host Ge(S_x Se_1 − x)₂ films followed by annealing in vacuum at constant temperature, which resulted in homogeneous films of good optical quality. The variation in Ag(Cu) concentration in the films ranged between 5 and 35 at.%. The kinetics of the diffusion and dissolution of metal in the host films was measured by optically monitoring the change in thickness of doped chalcogenide during consecutive thermal annealing steps. The kinetics studies revealed that the thermal dissolution rate of the Cu is greater than that of Ag. Optical UV-VIS transmission spectra of chalcogenide glass layers, undoped and thermal doped by Ag(Cu), were measured to establish the optical properties of the films. The spectra were analyzed using the technique proposed by Swanepoel and the results show that the addition of metal increases the absorption coefficient in the power-law regime and consequently the optical gap decreases and the refractive index increases. The amorphous character of the films was checked by X-ray diffraction which confirmed the amorphous structure of all Ag(Cu)GeSSe thin films.     

Compositional dependence of the optical properties of amorphous Sb2Se3−xSx thin films

Thin films of Sb₂Se_3−xS_x solid solutions (x = 0, 1, 2, and 3) were deposited by thermal evaporation of presynthesized materials on glass substrates held at room temperature. The films compositions were confirmed by using energy dispersive analysis of X-rays (EDAX). X-ray diffraction studies revealed that all the as-deposited films as well as those annealed at T_a < 423 K have amorphous phase. The optical constants (n, k) and the thickness (t) of the films were determined from optical transmittance data, in the spectral range 500-2500 nm, using the Swanepoel method. The dispersion parameters were determined from the analysis of the refractive index. An analysis of the optical absorption spectra revealed an Urbach’s tail in the low absorption region, while in the high absorption region an indirect band gap characterizes the films with different compositions. It was found that the optical band gap energy increases quadratically as the S content increases.     

Effects of Nb2O5 Replacement by Er2O3 on elastic and structural properties of 75TeO2-(10 − x)Nb2O5-15ZnO-(x)Er2O3 glass

Tellurite 75TeO₂-(10 − x)Nb₂O₅-15ZnO-(x)Er₂O₃; (x = 0.0-2.5 mol%) glass system with concurrent reduction of Nb₂O₅ and Er₂O₃ addition have been prepared by melt-quenching method. Elastic properties together with structural properties of the glasses were investigated by measuring both longitudinal and shear velocities using the pulse-echo-overlap technique at 5 MHz and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Shear velocity, shear modulus, Young's modulus and Debye temperature were observed to initially decrease at x = 0.5 mol% but remained constant between x = 1.0 mol% to x = 2.0 mol%, before increasing back with Er₂O₃ addition at x = 2.5 mol%. The initial drop in shear velocity and related elastic moduli observed at x = 0.5 mol% were suggested to be due to weakening of glass network rigidity as a result of increase in non-bridging oxygen (NBO) ions as a consequence of Nb₂O₅ reduction. The near constant values of shear velocity, elastic moduli, Debye temperature, hardness and Poisson's ratio between x = 0.5 mol% to x = 2.0 mol% were suggested to be due to competition between bridging oxygen (BO) and NBO ions in the glass network as Er₂O₃ gradually compensated for Nb₂O₅. Further addition of Er₂O₃ (x > 2.0 mol%) seems to further reduce NBO leading to improved rigidity of the glass network causing a large increase of ultrasonic velocity (v_L and v_S) and related elastic moduli at x = 2.5 mol%. FTIR analysis on NbO₆ octahedral, TeO₄ trigonal bipyramid (tbp) and TeO₃ trigonal pyramid (tp) absorption peaks confirmed the initial formation of NBO ions at x = 0.5 mol% followed by NBO/BO competition at x = 0.5-2.0 mol%. Appearance of ZnO₄ tetrahedra and increase in intensity of TeO₄ tbp absorption peaks at x = 2.0 mol% and x = 2.5 mol% indicate increase in formation of BO.     

Spectroscopic properties of Er-doped xGeO2-(80 − x)TeO2-10ZnO-10BaO glasses

Erbium-doped glasses with composition xGeO₂-(80 − x)TeO₂-10ZnO-10BaO were prepared by melt-quenching technique. The phonon sideband spectra and the optical absorption band edges for the host matrix were confirmed by means of the spectral measurements. Standard Judd-Ofelt calculations have been completed to these glasses. The dependence of up-conversion and infrared emission under 980 nm excitation on the glass composition was studied. The quantum efficiencies for the ⁴I_13/2 → ⁴I_15/2 transition of trivalent erbium in the glasses were estimated.     

Crystallization kinetics of Fe73.5−xMnxCu1Nb3Si13.5B9 (x = 0, 1, 3, 5, 7) amorphous alloys

In this study, we have investigated the effect of substituting Mn for Fe on the crystallization kinetics of amorphous Fe_73.5−xMn_xCu₁Nb₃Si_13.5B₉ (x = 1, 3, 5, 7) alloys. The samples were annealed at 550 °C and 600 °C for 1 h under an argon atmosphere. The X-ray diffraction analyses showed only a crystalline peak belonging to the α-Fe(Si) phase, with the grain size ranging from 12.2 nm for x = 0 to 16.7 nm for x = 7. The activation energies of the alloys were calculated using Kissinger, Ozawa and Augis-Bennett models based on differential thermal analysis data. The Avrami exponent n was calculated from the Johnson-Mehl-Avrami equation. The activation energy increased up to x = 3, then decreased with increasing Mn content. The values of the Avrami exponent showed that the crystallization is typical diffusion-controlled three-dimensional growth at a constant nucleation rate.     

Transport property and structural characterization studies on (1 − x)[0.75AgI:0.25AgCl]:xTiO2 conducting composite electrolyte system

Transport property and structural investigation have been carried out on newly synthesized Ag⁺ ion conducting composite electrolyte system. The composite electrolyte system (1 − x)[0.75AgI:0.25AgCl]:xTiO₂, where 0 ? x ? 0.5 (in molar weight fraction) has been synthesized by melt quenching and annealing methods. The chemical compound TiO₂ (second phase dispersoid) dispersed in different compositions in a quenched (0.75AgI:0.25AgCl) mixed system/solid solution; this solid solution was used as a first phase host salt in place of AgI. The different preparation routes were adopted for the composite electrolyte system. Composition x = 0.1 exhibited highest conductivity at room temperature. The composite system 0.9[0.75AgI:0.25AgCl]:0.1TiO₂ was synthesized at different soaking times by melt quenching method. The system exhibited optimum conductivity at 20 min soaking time (σ_rt ≈ 1.4 × 10⁻³ S/cm). The ac conductivity has been measured from Z′-Z″ (Cole-Cole) complex impedance plots using impedance spectroscopic (IS) technique. The electrical conductivity as a function of temperature and frequency has been studied, and activation energy E_a, was calculated from Arrhenius plots for all compositions (0 ? x ? 0.5). The dc conductivity value has been evaluated from Log σ vs. log f plots. Structural characterization studies were carried out by X-ray diffraction (XRD) and differential thermal analysis (DSC) techniques.     

Preparation, phase transformation and microstructure of ZrxTi1−xO2 (x = 0.1-0.9) fine fibers

Zr_xTi_1−xO₂ (x = 0.1-0.9) fibers were prepared by the sol-gel dry-spinning method. Polyacetylacetonatozirconium (PAZ) and tetrabutyl titanate (C₁₆H₃₆O₄Ti) were used as raw materials. The green fibers were obtained from the amorphous spinnable solution and then heat-treated to convert into polycrystalline fibers. The main phase changes from TiO₂ to zirconium titanate (ZT) and then tetragonal ZrO₂ with increasing ZrO₂ content. The crystallization temperature varied with the molar ratio of Zr:Ti. The heat-treated fibers at 1050 °C have few pores and no cracks with diameters of 10-20μm and lengths of 1-5 cm.     

Insulator-like electrical transport in structurally ordered Al65Cu20+xRu15−x (x = 1.5, 1.0, 0.5, 0.0 and −0.5) icosahedral quasicrystals

Low-temperature resistivities, in zero-field and 8 T field, and magnetoresistance have been measured down to 1.4-300 K for stable icosahedral quasicrystals Al₆₅Cu_20+xRu_15−x (x = 1.5, 1.0, 0.5, 0.0 and −0.5). The analysis of the magnetoresistance data shows an overwhelming presence of anti weak-localization effect (τ_so ∼ 10⁻¹² s). But the sample with x = −0.5 shows anomalous magnetoresistance and the anti weak-localization effect breaks down (τ_so to be 10⁻¹⁵ s). The in-field σ-T between 5 K and 20 K, for x = 1.0, 0.5, 0.0 and −0.5 samples, and between 1.4 K and 40 K for x = 1.5 sample, follow a power-law behavior with an exponent of 0.5 and above ∼30 K the exponent ranges from 1.17 to 1.58. The observed power-laws basically characterize the presence of critical regime of the metal-insulator (MI) transition, dominated by electron-electron and electron-phonon inelastic scattering events respectively. In samples with x = 1.0, 0.5, 0.0 and −0.5 the in field σ-T has been found to follow ln σ-vs-T^1/4 below 5 K, which indicates the presence of variable range hopping. The observed transport features indicate the occurrence of proximity of metal-insulator transition in these Al-Cu-Ru quasicrystal samples.     

Structure of partially reduced xPbO (1 − x)SiO2 glasses: combined EXAFS and MD study

We have studied the structure of partially reduced lead-silicate glasses using combined EXAFS (extended X-ray absorption fine structure) and MD (molecular dynamics) methods. The analysis was performed for glasses of x[(1 − p)Pb pPbO] (1 − x)SiO₂ composition, x = 0.3, 0.5, 0.7, where parameter (1 − p) describes the degree of reduction, i.e. the content of the granular metallic phase, appearing as the result of the reduction process (e.g. annealing in hydrogen atmosphere). In the EXAFS experiment (1 − p) was expressed via the time of reduction realized at 400 °C (1.5 h, 24 h, 70 h), whereas in the MD simulations it was determined precisely by using proper numbers of particles (corresponding to (1 − p) = 0.0, 0.25, 0.5, 0.75 and 1.0). In the paper we describe in detail the local structure around lead atoms and its changes in the function of glass composition and reduction degree. The tendency for agglomeration of Pb⁰ into clusters, the formation of the granular metallic phase, and continuity of silica and lead oxide subnetworks are discussed. A good agreement between EXAFS-extractcd and MD-extracted parameters of the short-range structure encouraged us to preform a medium-range order analysis, based on the MD simulations only. Moreover, combining the EXAFS and MD methods we could correlate the reduction time (technological parameter) with the degree of reduction (1 − p) and the actual state of the granular structure. The latter relation may be useful for controlled production of reduced glasses of pre-requcstcd physical properties.     

Effect of carbon on the microstructural evolution of Zr66.7−xNi33.3Cx (x = 0, 1, 3) alloys during mechanical alloying

In the present paper, the effect of carbon on the microstructural evolution of Zr_66.7−xNi_33.3C_x (x = 0, 1, 3) alloys during mechanical alloying has been investigated using X-ray diffraction (XRD), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results show that these three alloys undergo similar amorphization and crystallization processes, and the final milling product is a metastable fcc-Zr_66.7−xNi_33.3C_x phase. The carbon addition can shorten the milling time for the complete amorphization reaction and enhance the stability of the formed amorphous alloy, which can suppress the mechanically induced amorphous-crystalline phase transformation with further increasing milling time.     

Low-temperature/high-temperature AlN superlattice buffer layers for high-quality AlxGa1−xN on Si (1 1 1)

We present MOVPE-grown, high-quality Al_xGa_1−x N layers with Al content up to x=0.65 on Si (1 1 1) substrates. Crack-free layers with smooth surface and low defect density are obtained with optimized AlN-based seeding and buffer layers. High-temperature AlN seeding layers and (low temperature (LT)/high temperature (HT)) AlN-based superlattices (SLs) as buffer layers are efficient in reducing the dislocation density and in-plane residual strain. The crystalline quality of Al_xGa_1−xN was characterized by high-resolution X-ray diffraction (XRD). With optimized AlN-based seeding and SL buffer layers, best ω-FWHMs of the (0 0 0 2) reflection of 540 and 1400 arcsec for the (1 0 1¯ 0) reflection were achieved for a ∼1-μm-thick Al_0.1Ga_0.9N layer and 1010 and 1560 arcsec for the (0 0 0 2) and (1 0 1¯ 0) reflection of a ∼500-nm-thick Al_0.65Ga_0.35N layer. AFM and FE-SEM measurements were used to study the surface morphology and TEM cross-section measurements to determine the dislocation behaviour. With a high crystalline quality and good optical properties, Al_xGa_1−x N layers can be applied to grow electronic and optoelectronic device structures on silicon substrates in further investigations.     

Structural,electrical and optical properties of SnO2 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

SnO₂ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates at different substrate temperatures (500–800 °C) by metalorganic chemical vapor deposition (MOCVD). Structural, electrical and optical properties of the films have been investigated. The films deposited at 500 and 600 °C are epitaxial SnO₂ films with orthorhombic columbite structure, and the HRTEM analysis shows a clear epitaxial relationship of columbite SnO₂(1 0 0)||YSZ(1 0 0). The films deposited at 700 and 800 °C have mixed-phase structures of rutile and columbite SnO₂. The carrier concentration of the films is in the range from 1.15×10¹⁹ to 2.68×10¹⁹ cm⁻³, and the resistivity is from 2.48×10⁻² to 1.16×10⁻² Ω cm. The absolute average transmittance of the films in the visible range exceeds 90%. The band gap of the obtained SnO₂ films is about 3.75–3.87 eV.     

Thermodynamical miscibility in 0.8[xB2O3-(1 − x)P2O5]-0.2K2O glasses

The thermodynamical miscibility in 0.8[xB₂O₃-(1 − x)P₂O₅]-0.2K₂O glasses has been studied by measuring the glass transition temperature and the mixing enthalpy. Measurements have been performed by differential scanning calorimeter and hydrofluoric acid solution calorimetry at 298 K. The enthalpies of mixing are significantly negative over the whole range of composition. The results are discussed in terms of intermolecular associations.     

Combined in-situ SAXS/WAXS and HRTEM study on crystallization of (Cu60Co40)1 − xZrx metallic glasses

CuZr as well as CoZr are well known metallic glass-formers in a wide compositional range. Since the binary Cu-Co system exhibits a metastable liquid-liquid miscibility gap, i.e. Cu and Co tend to separate from each other, the ternary Cu-Co-Zr system is a promising candidate to form phase separated glass-glass composites. In this work (Cu₆₀Co₄₀)_1 − xZr_x metallic glasses with relatively low Zr contents of x = 37 and x = 32 were prepared by melt spinning and investigated by in-situ small-angle and wide-angle X-ray scattering (SAXS/WAXS) and differential scanning calorimetry (DSC). Certain heat treated samples were additionally investigated by high-resolution transmission electron microscopy (HRTEM). Even for x = 32 there are no indications for any kind of phase separation in the as-quenched state within experimental resolution, i.e. the critical temperature T_c for a liquid-liquid phase separation has already decreased from 1556 K for binary Cu₆₀Co₄₀ to a temperature below the glass transition temperature T_g = 762(5)K found for (Cu₆₀Co₄₀)₆₈Zr₃₂. Combined in-situ SAXS/WAXS and HRTEM investigations reveal that thermal annealing also does not induce an amorphous-amorphous phase separation. Instead the formation of nano crystallites of a so far unknown Cu-rich/Zr-poor phase with relatively low activation energy for crystallization E_a = 116(7) kJ/mol at temperatures far below the crystallization temperature deduced from DSC measurements is observed.     

Crystal/glass phase change in K1−xRbxSb5S8 (x = 0.25, 0.50, 0.75) studied through thermal analysis techniques

K_1−xRb_xSb₅S₈ (x = 0.25, 0.5, 0.75) is a well-defined single-phase system that undergoes a reversible phase-change. We determined the activation energy of glass transition and crystallization, respectively, for the three compositions using the Kissinger and Ozawa-Flynn-Wall equations. The results have shown that for K_0.25Rb_0.75Sb₅S₈ the crystallization mechanism could be interpreted in terms of a single-step reaction. For the other two compositions the glass-to-crystal transformation is a process of increasing mechanistic complexity with time and it involves simultaneously several different nucleation and growth events. The slope of the lines in the Avrami plots was observed to be independent of heating rate for K_0.25Rb_0.75Sb₅S₈ and the mean value of the activation energy was found to be 262 ± 6 kJ/mol. For the other two compositions, the slope varies with the heating rate. In the K_0.25Rb_0.75Sb₅S₈ glasses, bulk nucleation with three-dimensional crystal growth appears to dominate the phase-change process.     

Thermal conductivity and specific heat of bulk amorphous chalcogenides Ge20Te80−xSex (x = 0,1,2,8)

Bulk amorphous chalcogenide samples of Ge₂₀Te_80−xSe_x (x = 0, 1, 2, 8) have been prepared using a melting-quench method, and characterized by the differential scanning calorimetry, X-ray powder diffraction, high-resolution transmission electron microscopy, specific heat and thermal conductivity measurements. The low temperature specific heat measurements identified some localized low-frequency oscillation modes (Einstein modes) in conjunction with a Debye-like behavior. It was found that with increasing Se concentration the characteristic Debye temperature did not change whereas the Einstein temperature slightly decreased. The lattice thermal conductivity of all Ge₂₀Te_80−xSe_x samples exhibited typical amorphous heat conduction behavior, which has been discussed in connection with the phonon mean free path and in the context of a phenomenological model of heat conduction for highly disordered system.