Spectroscopic properties of Er-doped Na2O-Sb2O3-B2O3-SiO2 glasses

Spectroscopic properties of Er³⁺-doped Na₂O-Sb₂O₃-B₂O₃-SiO₂ glasses have been investigated for developing 1.5-μm broadband fiber amplifiers. An intense 1.5-μm near infrared emission with a broad full width at half maximum (FWHM) of 88 nm has been obtained for Er³⁺-doped 5Na₂O-20Sb₂O₃-35B₂O₃-40SiO₂ glass upon excitation with a 980 nm laser diode. The obtained emission cross-section of the ⁴I_13/2 → ⁴I_15/2 transition and the lifetime of the ⁴I_13/2 level of Er³⁺ ions are 6.8 × 10⁻²¹ cm² and 0.36 ms, respectively. It is noted that the product of the emission cross-section and the FWHM of the glass, σ_e × FWHM, is as great as 598.4 × 10⁻²¹ cm² nm, which is comparable or higher than that of Er³⁺-doped bismuth-based and tellurite-based glasses. These special optical properties encourage in identifying them as important materials for potential applications in high performance optics and optical communication networks.     

Investigation of infrared emission and lifetime in Tm-doped 75TeO2:20ZnO:5Na2O (mol%) glasses: Effect of Ho and Yb co-doping

In this paper we describe fabrication and characterization of rare-earth-doped active tellurite glasses to be used as active laser media for fiber lasers emitting in the 2 μm region. The base composition is (mol%): 75TeO₂-20ZnO-5Na₂O with different concentrations of Tm³⁺, Yb³⁺ and Ho³⁺ as dopants or co-dopants. Optical properties of doped glasses were studied and pumping at 800 nm and at 980 nm were tested in order to compare the efficiency of two pumping mechanisms. Optical characterization carried out on glasses containing only Tm³⁺ ions indicated the optimum concentration of Tm₂O₃ in terms of emission efficiency as 1 wt%. The addition of 5 wt% of Yb₂O₃ to Tm³⁺-doped glasses led to the best results in terms of intensity of fluorescence emission and of lifetime values. Yb and Ho co-doped Tm-tellurite glass was measured in emission.     

Studies of some mechanical and optical properties of: (70 − x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Specimens of the glassy system: (70 − x)TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by the melt-quenching. An ultrasonic pulse-echo technique was employed, at 5 MHz, for measuring: the ultrasonic attenuation, longitudinal and shear wave velocities, elastic moduli, Poisson ratio, Debye temperature and hardness of the present glasses. It is found that the gradual replacement of TeO₂ by Li₂O in the glass matrix up to 30 mol% leads to decrease the average crosslink density and rigidity of prepared samples which affects the properties, i.e., the hardness, ultrasonic wave velocities and elastic moduli are decreased, while the Poisson ratio and the ultrasonic attenuation are increased. Also, optical absorption spectra were recorded in the range, 200-800 nm for these glasses. The obtained results showed that a gradual shift in the fundamental absorption edge toward longer wavelengths occurred. Values of both of the optical energy gap, E_opt, and width tails, ΔE, are determined. It is observed that E_opt is decreased and ΔE increased with the increase of Li₂O in the glass matrix up to 30 mol%. The compositional dependences of the above properties are discussed and correlated to the structure of tested glasses.     

Spectroscopic investigation and optical characterization of novel highly thulium doped tellurite glasses

In this paper, optical properties of 75TeO₂-20ZnO-5Na₂O host glass doped with concentration of Tm³⁺ up to 10 %mol were studied in order to assess the most suitable rare earth content for short cavity fiber lasers. Raman spectroscopy revealed a change in the glass structure while increasing Tm³⁺ content, similar to the well known addition of alkali ions in a glass. Influence of the fabrication process on the OH⁻ content was determined by FTIR measurements. Refractive index of Tm³⁺ doped tellurite glasses was measured at five different wavelengths ranging from 533 nm to 1533 nm. Lifetime and emission spectra measurements of the Tm³⁺ doped tellurite glasses are reported.     

Spectroscopic properties of Er-doped xGeO2-(80 − x)TeO2-10ZnO-10BaO glasses

Erbium-doped glasses with composition xGeO₂-(80 − x)TeO₂-10ZnO-10BaO were prepared by melt-quenching technique. The phonon sideband spectra and the optical absorption band edges for the host matrix were confirmed by means of the spectral measurements. Standard Judd-Ofelt calculations have been completed to these glasses. The dependence of up-conversion and infrared emission under 980 nm excitation on the glass composition was studied. The quantum efficiencies for the ⁴I_13/2 → ⁴I_15/2 transition of trivalent erbium in the glasses were estimated.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

Structure and properties of glasses in ZnO-P2O5-TeO2 system

Glasses in the ternary ZnO-P₂O₅-TeO₂ system were prepared and studied in two compositional series (100 − x)[0.5ZnO-0.5P₂O₅]-xTeO₂ (X-series) and 50ZnO-(50 − y)P₂O₅-yTeO₂ (Y-series) within the concentration range of x = 0-60 and y = 0-40 mol% TeO₂. Their structure was studied by Raman and ³¹P MAS NMR spectroscopies. The incorporation of TeO_x units into the structural network is associated with the depolymerisation of phosphate chain structure as revealed by both methods. At a high TeO₂ content isolated PO₄ tetrahedra are formed in the structure of glass series Y, while diphosphate O₃P-O-PO₃ groups are present in the structure of the glass series X. In the structure of glass series Y tellurium atoms form predominantly TeO₃ trigonal pyramids, whereas in the X glass series TeO₄ trigonal bipyramids prevail in the glass structure. The addition of TeO₂ to the parent zinc metaphosphate glass results in a decrease of glass transition temperature in both compositional series associated with the replacement of stronger P―O bonds by weaker Te―O bonds.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.     

Luminescence of GeO2 glass, rutile-like and α-quartz-like crystals

The luminescence of GeO₂ rutile-like crystals was studied. Crystals were grown from a melt of germanium dioxide and sodium bicarbonate mixture. Luminescence of the crystal was compared with that of sodium germanate glasses produced in reduced and oxidized conditions. A luminescence band at 2.3 eV was observed under N₂ laser (337 nm). At higher excitation photon energies and X-ray excitation an additional band at 3 eV appears in luminescence. The band at 2.3 eV possesses intra-center decay time constant about 100 μs at 290 K and about 200 μs at low temperature. Analogous luminescence was obtained in reduced sodium germanate glasses. No luminescence was observed in oxidized glasses under nitrogen laser, therefore the luminescence of rutile-like crystal and reduced sodium germanate glass was ascribed to oxygen-deficient luminescence center modified by sodium. The band at 2.3 eV could be ascribed to triplet-singlet transition of this center, whereas the band at 3 eV, possessing decay about 0.2 μs, could be ascribed to singlet-singlet transitions. Both bands could be excited in recombination process with decay kinetics determined by traps, when excitation realized by ArF laser or ionizing irradiation with X-ray or electron beam. Another luminescence band at 3.9 eV in GeO₂ rutile-like crystal was obtained under ArF laser in the range 100-15 K. Damaging e-beam irradiation of GeO₂ crystal with α-quartz structure induces similar luminescence band.     

Structure and properties of glasses in the MI + M2S + (0.1Ga2S3 + 0.9GeS2), M = Li, Na, K and Cs, system

The structure and properties of glasses in the MI + M₂S + (0.1Ga₂S₃ + 0.9GeS₂), M = Li, Na, K and Cs, system were studied using Raman, IR spectroscopy, DSC and density measurements to help better understand the ionic transport in these glasses. The glass forming ranges of these ternary glasses were compared to those of the binary alkali sulfide and germanium sulfide systems. The more extensive glass forming range in the Na₂S system was used to examine the more extensive changes of structure and properties of these glasses as a function of Na₂S content. As expected, non-bridging sulfurs (NBS) form with the addition of alkali sulfide. Unlike their oxide counterparts, however, the alkali sulfide doped glasses appear to support longer-range super-structural units. For example, evidence that the adamantine-like structure exists in the K₂S and Cs₂S modified glasses is found in the Raman spectra of the glasses. The structural role of the alkali iodide addition was also explored since the addition of alkali iodide helps to improve the conductivity. For most of these glasses, as observed in many other oxide glasses, the added MI dissolves interstitially into the glass structure network without changing the alkali sulfide network structure. In 0.6Na₂S + 0.4(0.1Ga₂S₃ + 0.9GeS₂) glasses, however, the added NaI may affect the glass structure as it causes systematic changes in the frequency of the Ge-S network mode as seen in the Raman spectra.     

Anionic structure and elasticity of Na2O-MgO-SiO2 glasses

The structure and elastic properties of a series of xNa₂O · MgO · 4SiO₂ glasses have been studied using both Raman and Brillouin spectroscopy. Relative to Na₂O-SiO₂ glasses, the maximum abundance for phyllosilicate structural units in the present glasses shows a lag of 0.5 units in the number of non-bridging oxygen per silicon atom (NBO/Si). This phenomenon has been attributed to the decrease in the average coordination number of modifying cations due to the presence of Mg²⁺. It has also been found that the decomposition of both metasilicate and disilicate (dimerized SiO₄) anionic structural units in Na₂O-SiO₂ glasses are enhanced by the addition of MgO. However, the presence of Mg²⁺ does not cause a considerable effect on the decomposition of phyllosilicate structural unit. The acoustic data have revealed that both shear and Young’s moduli of the present glasses decrease with increasing NBO/Si (the variation in bulk modulus is reversed, however). The resistance to shear deformation for the anionic structural units in silicate glasses has been found to decrease in the following order: tectosilicate > phyllosilicate > metasilicate > disilicate > orthosilicate. The relative contribution of the various anionic structural units to the bulk modulus of a glass remains to be determined. The ideal mixing model using Makishima-Mackenzie’s relationship for predicting Young’s modulus is not applicable to the present glasses.     

Application of the constant stoichiometry grouping concept to the Raman spectra of Pb(PO3)2-TeO2 glasses

Pb(PO₃)₂-TeO₂ glasses in the whole range of glass composition were first obtained and their properties (refractive index, density, T_g and light scattering losses) were determined. Based on the vibrational spectroscopy data a new approach was applied to investigate the interactions of initial oxides in melts resulted in so-called constant stoichiometry groupings (CSGs) formation symbolizing intermediate range order in glasses. Vibrational spectra of glasses are interpreted as a superposition of unchangeable spectral forms (principal spectral components (PSCs)) belonging to CSGs: PbO · P₂O₅, TeO₂ · 2PbO · 2P₂O₅, TeO₂ · PbO · P₂O₅, TeO₂, and possibly 2TeO₂ · PbO · P₂O₅ and 6TeO₂ · PbO · P₂O₅. In this work Multivariate Data Analysis has been applied as the independent mathematical tool to decompose Raman spectra of glasses and reveal the number of PSCs. It is shown that application of factor analysis results in the same five PSCs that confirms our data obtained from the CSG concept. This concept allows also the prediction of the existence of unknown compounds, and correspondingly some crystals (TeO₂⋅ 2PbO⋅2P₂O₅ and others) were revealed by XRPD of the crystallized glasses. The CSG concept opens the way for elaboration of low scattering glasses as candidates for Raman amplifiers. It is shown that Pb(PO₃)₂-TeO₂ glasses with small content of TeO₂ are of interest to photonic technology.     

Development and characterizations of BaO-CaO-Al2O3-SiO2 glass-ceramic sealants for intermediate temperature solid oxide fuel cell application

Several compositions based on BaO-CaO-Al₂O₃-SiO₂ (BCAS) glass system have been studied in this investigation to see their applicability as sealant for solid oxide fuel cell (SOFC). The glasses as well as the corresponding glass-ceramics have been systematically characterized by differential thermal analysis, dilatometry, X-ray diffractometry, electron microscopy and impedance analysis to examine their suitability as sealant. While the glass transition temperature (T_g) determined from DTA are within 600-665 °C, the coefficient of thermal expansion (CTE) can be tailored between 9.5 and 13.0 × 10⁻⁶ K⁻¹. These glasses are found to be well adhered with metallic interconnects, such as commercial ferritic steel (Crofer22APU), at an optimum sealing temperature of 850 °C. The shrinkage behavior of the developed glasses in their pellet form has also been investigated. The resistivities of the glass-ceramics, as obtained from impedance analysis, are found to be within 10⁴-10⁶ Ω cm at 800 °C. Under sandwiched condition between two metals, some of the developed compositions are found to maintain this high resistivity even after 100 h of operation. One of the glass compositions has shown a low leak-rate of the order of ∼10⁻⁷ Pa m² s⁻¹.     

Optical properties of and concentration quenching in Bi2O3-B2O3-Ga2O3 glasses

Er₂O₃-doped Bi₂O₃-B₂O₃-Ga₂O₃ glasses were prepared by the conventional melt-quenching method, and the Er³⁺:⁴I_13/2 → ⁴I_15/2 fluorescence properties are studied for different Er³⁺ concentrations. when the Er₂O₃ concentration increases from 0.03 to 3.0 mol%, the measured lifetime of Er³⁺:⁴I_13/2 level decrease from 2.24 to 0.9 m s, and from 0.25 to 0.20 m s for the Er³⁺:⁴I_11/2 level. The fast energy migration among Er³⁺ ions cause the reduction of lifetime of the ⁴I_13/2 level, whereas the change in the ⁴I_11/2 level is mainly due to a cooperative upconversion process (⁴I_11/2, ⁴I_11/2) → (⁴F_7/2, ⁴I_15/2). Based on the dipole-dipole interaction theory, the interaction parameter, C_Er,Er, for the migration rate of Er³⁺:⁴I_13/2 ↔ ⁴I_13/2 was calculated to be 32 × 10⁻⁴⁰ cm⁶ s⁻¹.     

Optical Properties of Bi2O3-TeO2-B2O3 Glasses

Glasses of the Bi₂O₃-TeO₂-B₂O₃ ternary system were developed and their linear and nonlinear optical properties were investigated. The absorption edges of these glasses were found to be 367-384 nm with a good transmittance in visible wavelength, although they exhibit the refractive indices as high as 1.98-2.12 at 633 nm. The absorption edges are quite steep and they are analyzed by the Urbach theory. The obtained Urbach energies of these glasses are 73-79 meV which are comparable to silica glasses. The high refractive index and its glass composition dependency are discussed according to the basics of the electronic polarizability and optical basicity. The high third order nonlinear susceptibility χ⁽³⁾ = 2.0 × 10^− 12 esu at 800 nm was also obtained in the 36Bi₂O₃-18TeO₂-46B₂O₃ glass.     

Structural analysis of Cd-Te-O films prepared by RF reactive sputtering

Crystalline and microcrystalline Cd-Te-O samples have been obtained by RF reactive sputtering from a CdTe target using N₂O as oxidant. The growth conditions were substrate temperatures of 323 K, 573 K and 773 K and cathode voltage of −400 V, corresponding to 30 W of forward power. The samples were studied by micro-Raman spectroscopy, X-ray diffraction and optical transmittance. The films are remarkably transparent in the visible range, with transmittances about 88% at 400 nm and band gap energies above the absorption edge of the glass substrates. Although only the samples prepared at 773 K present defined diffraction peaks, the analysis of the Raman spectra indicate that samples prepared at 323 K and 573 K have a defined microstructure indeed. The spectra fitting performed by comparison with pattern compounds demonstrate that Cd-Te-O films are formed of Te-O units similar to those present in metal oxide-doped tellurite glasses, such as TeO₃ and TeO_3 + 1 linked through Cd-O bonds. As the substrate temperature increases the microstructure evolves from a γ-TeO₂ richer state to Cd_xTe_yO_z. In the crystalline sample the main phase identified was CdTeO₃ even though evidence of other phases was observed.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.     

Laser-induced crystallization of β′-RE2(MoO4)3 ferroelectrics (RE: Sm, Gd, Dy) in glasses and their surface morphologies

The glasses with the compositions of 21.25RE₂O₃-63.75MoO₃-15B₂O₃ (RE: Sm, Gd, Dy) were prepared and the formation of β′-RE₂(MoO₄)₃ ferroelectrics was confirmed in the crystallized glasses obtained through a conventional crystallization in an electric furnace. The features of the glass structure and crystallization behavior were clarified from measurements of Raman scattering spectra. Continuous-wave Nd:YAG laser with a wavelength of 1064 nm (laser power: 0.6-0.9 W, laser scanning speed: S = 1-16 μm/s) was irradiated to 10.625Sm₂O₃-10.625Gd₂O₃ (or Dy₂O₃)-63.75MoO₃-15B₂O₃ glasses, and the structural modification was induced at the glass surface. At the scanning speed of S = 10 μm/s, crystal lines consisting of β′-Gd_2−xSm_x(MoO₄)₃ or β′-Dy_2−xSm_x(MoO₄)₃ crystals were patterned on the glass surface. It was found that those crystal lines have the surface morphology with periodic bumps. At S = 1 μm/s, it was found that crystal lines consist of the mixture of paraelectric α-Gd_2−xSm_x(MoO₄)₃ and ferroelectric β′-Gd_2−xSm_x(MoO₄)₃ crystals, indicating the phase transformation from the β′ phase to the α phase during laser irradiation. Homogeneous crystal lines with β′-RE₂(MoO₄)₃ ferroelectrics have not been written in this study, but further research is continuing.     

The structure and optical properties of GeO2-GeS2 glasses

Oxy-chalcogenide glasses with compositions of xGeO₂-(100 − x)GeS₂, where 0 ? x ? 100 mol%, have been prepared and studied in terms of their structures and optical properties. X-ray fluorescence spectroscopy shows that Ge:S ratio can deviate from GeS₂ by ∼10 at.%, depending critically upon the preparation conditions. Raman scattering spectroscopy suggests that stoichiometric GeO₂-GeS₂ glasses have a heterogeneous structure in the scale of 1-100 nm. The optical gaps are nearly constant at 3.0-3.5 eV for glasses with 0 ? x ? 80 mol% and abruptly increase to ∼6 eV in GeO₂. This dependence suggests that the optical gap is governed by GeS₂ clusters, which are isolated and/or percolated. Composition-deviated glasses appear as orange and brown, and these glasses seem to have more inhomogeneous structures.