The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2

Glasses with the compositions xNa₂O · 10MgO · (90 − x)SiO₂, 10Na₂O · xMgO · (90 − x)SiO₂, 5Na₂O · 15MgO · xAl₂O₃ · (80 − x)SiO₂, xNa₂O · 10MgO · 10Al₂O₃ · (80 − x)SiO₂, 10Na₂O · 10MgO · xAl₂O₃ · (80 − x)SiO₂, 10Na₂O · 5MgO · 10Al₂O₃ · (80 − x)SiO₂ were melted and studied using UV-vis-NIR spectroscopy in the wavenumber range from 5000 to 30 000 cm⁻¹. At [Al₂O₃] > [Na₂O], the UV-cut off is strongly shifted to smaller wavenumbers and the NIR peak at around 10 000 cm⁻¹ attributed to Fe²⁺ in sixfold coordination gets narrower. Furthermore, the intensity of the NIR peak at 5500 cm⁻¹ increases. This is explained by the incorporation of iron in the respective glass structures.     

Point defect formation and annihilation in silica glass by heat-treatment: Role of water and stress

It was discovered that E′ centers were created by heat-treatment when silica glass contains water and has residual stress. Silica glass samples were heat-treated at 1000 °C for various lengths of time in 355 torr (47 000 Pa) water vapor pressure and dry nitrogen gas atmospheres. The electron paramagnetic resonance (EPR) signal of E′ centers increased initially with heat-treatment time in both atmospheres but then decreased afterwards in the wet atmosphere. It is known that water molecules eliminate paramagnetic defects, such as E′ centers and non-bridging oxygen hole centers (NBOHCs) by reacting with these defects in the glass, transforming them to non-paramagnetic species such as Si-OH or Si-H. The present study indicates that water molecules are also capable of initially creating paramagnetic defects in the glass structure by breaking the silica network structure in the presence of stress. The present observation may be relevant to mechanical strength reduction of silica glasses, which is commonly observed in the presence of water and stress.     

Thermal and some physical properties of glasses in the La2O3−CaO−B2O3 ternary system

Glasses in the La₂O₃−CaO−B₂O₃ ternary system were studied. The glass forming range as determined by the appearance of the annealed cast was found to match previously published findings. Clear glasses were formed in the composition range of 5.7−19.1 mol% La₂O₃ with constant B₂O₃ content of 71.4 mol%, and in glasses of constant La₂O₃:CaO ratio of 1:4 with B₂O₃ content in the range of 71.4-55.0 mol%. The non-linear optical crystalline phase La₂Ca₂B₁₀O₁₉ was crystallized from the clear glasses after heat treatments, as determined by powder XRD. Two types of the LaBO₃ crystalline phases were detected in the partially and the fully crystallized glass compositions outside the glass forming range. Data are reported for the glass transition temperature (T_g), dilatometric softening point (T_d), linear coefficient of expansion (α), onset crystallization temperature (T_x), exothermal peak temperature (T_P), density (ρ) and index of refraction (n_D) in the clear glasses.     

Solubility of glasses in the system P2O5-CaO-MgO-Na2O-TiO2: Experimental and modeling using artificial neural networks

Phosphate glasses in the system P₂O₅-CaO-MgO-Na₂O-TiO₂ for use as degradable implant materials were produced. In order to classify their solubility behavior, dissolution experiments were performed in deionized water for 60 min at 98 °C. Resulting solutions were analyzed using ICP-OES. In addition, pH measurements were carried out in physiological NaCl solution. With increasing phosphorus oxide content, the glasses showed a higher solubility and gave lower pH values in aqueous solution. This was caused by changes in the glass structure, as long phosphate chains are more susceptible to hydration than smaller phosphate groups. These changes in glass structure were followed by ³¹P MAS-NMR experiments. Increasing sodium oxide concentrations in exchange for calcium or magnesium oxide also increased the glass solubility by disrupting ionic cross links between chains. By contrast, addition of titania made the glasses more stable towards dissolution by cross linking smaller phosphate groups. The aim of this study was to find a relationship between glass composition and solubility behavior. As classical linear methods of data analysis were unsuitable due to the complexity of the relationship, preliminary artificial neural networks analyses were performed and were found to be an interesting tool for modeling the solubility behavior of phosphate glasses.     

Sulfur behavior in silicate glasses and melts: Implications for sulfate incorporation in nuclear waste glasses as a function of alkali cation and V2O5 content

The presence of sulfur in radioactive waste to be incorporated in borosilicate glasses entails difficulties mainly due to the relatively low solubility of sulfates in the vitreous phase. In this work a study is presented on the effects of the ratio R = [Na₂O]/[B₂O₃], the type of sulfate added and the addition of V₂O₅ on the incorporation of sulfates in borosilicate glasses. Glass samples were prepared at the laboratory scale (up to 50-100 g) by melting oxide and sulfate powders under air in Pt/Au crucibles. XRF and ICP/AES chemical analysis, SEM/EDS, microprobe WDS and Raman spectroscopy were employed to characterize the fabricated samples. The main experimental results confirm that the incorporation of sulfates in borosilicate glasses is favored by the network depolymerization, which evolves with the ratio R. The addition of V₂O₅ seems to accelerate the kinetics of sulfur incorporation in the glass and, probably, increase the sulfate solubility by modifying the borate network and fostering the formation of voids of shape and size compatible with the sulfur coordination polyhedron in the glassy network. The kinetics of X₂SO₄ incorporation in the glass seems to be slower when X = Cs.     

Characterization of new sulfur and selenium-based glasses containing lead iodide

The aim of this work is to investigate and qualify vitreous regions in new chalcogenide systems containing highly polarizable elements like S, Se, As, Sb, Bi, Pb and I. The sulfur based system, As₂S₃-Sb₂S₃-Bi₂S₃-PbI₂, as well as the selenium containing glasses As₂Se₃-Sb₂Se₃-PbI₂ have been studied. Large vitreous regions have been defined in the both systems: sulfur and selenium. Indeed, several glass compositions can accept in the vitreous network a molar concentration near 50% of PbI₂. Physical properties such as glass transition temperature, crystallization temperature, optical transmission, band-gap wavelength have been measured versus glassy compositions.     

Remark on the optical gap in ZnO-Bi2O3-TeO2 glasses

Four ZnO-Bi₂O₃-TeO₂ glasses were prepared from high purity (4N5) oxides. From measurements of the optical transmission on very thin bulk samples the optical gap was determined at around 3.55 eV for the glasses studied. The temperature dependence of the optical gap was also determined from the room temperature close up to 500 K. Preliminary Raman scattering measurements indicate that with a decrease in TeO₂ content, TeO₄ trigonal bipyramid transformation proceeds into TeO₃ trigonal pyramids.     

The application of differential thermal analysis to the study of isothermal and non-isothermal crystallization kinetics of coal fly ash based glasses

The crystallization kinetics of glasses obtained from coal fly ash was investigated by both isothermal and non-isothermal methods using differential thermal analysis (DTA) data. In DTA experiments, glass samples having coarse (800-1000 μm) and fine (<180 μm) particle sizes were used and the results were compared. The Avrami exponent (n) was calculated by means of Johnson-Mehl-Avrami (JMA) and Ozawa equations. Calculated kinetic parameters indicated that the appropriate crystallization mechanisms were bulk and surface crystallization for coarse and fine particles, respectively. Isothermal and non-isothermal DTA experiments showed that the crystallization activation energies of coarse glasses are changed in the range of 444-578 kJ/mol, while the crystallization activation energies of fine glasses are changed in the range of 610-662 kJ/mol. It was found that crystallization activation energies of fine glasses are higher than those of the coarse glasses. Results showed that isothermal and non-isothermal crystallization kinetics of glasses produced from coal fly ash is in agreement within the experimental error.     

Development and properties of a glass made from MSWI bottom ash

A uniform shiny black-coloured glass was obtained using bottom ash produced by a Portuguese municipal solid waste incinerator (MSWI). The bottom ash was the single batch material used in the formation of the glass, which was obtained by vitrification of the solid waste at 1400 °C for 2 h. Under these conditions, a homogeneous melt with an appropriate viscosity to be shaped was obtained, indicating the suitability of this waste material to be employed in the development of vitreous products. The characterization of the resulting glass was performed in order to assess its structural, physical, mechanical, thermal and chemical features. The glass had a density of 2.69 g cm⁻³, a hardness of 5.5 GPa, a fracture strength of 75 MPa, a thermal expansion coefficient of 9.5 × 10⁻⁶ °C⁻¹ and it exhibited a very good chemical stability. In summary, the MSWI bottom ash glass has good mechanical and chemical properties and may, therefore, be used in several applications, particularly as a construction material.     

The synthesis of aligned silicon nanowires under ambient atmospheric pressure

Highly ordered amorphous silicon nanowires were successfully synthesized from single crystalline silicon wafer at the pyrolysis temperature of 1050 °C under ambient atmospheric pressure. Both poly (phenylcarbyne) and nickel nitrate played important roles in the growth of silicon nanowires. The fabrication of ordered silicon nanowires was controllable and repeatable, confirmed by the experimental results. The morphology and microstructure analysis of the as-obtained samples showed the highly ordered amorphous silicon nanowires were obtained, determined by scanning electron microscopy, transmission electron microscopy, X-ray photoelectron spectroscopy, and FT-infrared spectroscopy. A solid-liquid-solid growing process was proposed.     

Crystallization behavior of glasses in the system of Na2O-CaO-MgO-Fe2O3-Al2O3-SiO2 with high contents of nickel oxide

The structural behavior of nickel oxide in glassy and glass-ceramic materials, obtained in the system of Na₂O-CaO-MgO-Fe₂O₃-Al₂O₃-SiO₂, was investigated. The influence of the NiO content on the vitrification, crystallization, structure and exploitation properties of two model compositions, with different ratios [CaO]/[MgO] was analyzed. On the basis of DSC and XRD data, it is shown that NiO promoted the formation of bunsenite crystals, as nuclei for crystallization. On the other hand, NiO promoted formation of pyroxenes even for compositions with low MgO contents, which formed gehlenite without NiO admixtures. It is shown that in the composition with relatively high MgO contents, NiO could participate in the formation of two types of pyroxenes with the structure and chemical composition similar to (MgO_0.4NiO_0.6)(CaO_0.9NiO_0.1)Si₂O₆ and diopside-hedenbergite solid solutions. The optimal contents of NiO in both model compositions was about of 7 wt%, since higher contents reduced the exploitation properties. The glass-ceramics with optimal contents of NiO were also produced using Ni bearing galvanic slurry and coal ash; the resulting materials showed similar exploitation properties to those mentioned above.     

Ac conductivity and dielectric relaxation in ionically conducting soda-lime-silicate glasses

The frequency dependent conductivity and dielectric relaxation of alkali ions in some soda-lime-silicate (Na₂O-CaO-SiO₂) glasses are investigated over a frequency range from 50 Hz to 1 MHz and in a temperature range from room temperature to 603 K by using alternating current impedance spectroscopy. The conductivity isotherms show a transition from frequency independent dc region to dispersive region where the conductivity continuously increases with increasing frequency. The electric modulus representation has been used to provide comparative analysis of the ion transport properties in these glasses. The scaling behavior of imaginary part of electric modulus indicates that all dynamical processes occurring at different frequencies give the same activation energy.     

Glass formation ability and mechanical properties of Ti40Cu40Zr10Ni10 alloy

Melt-spun ribbon and bulk samples in cylindrical rod form with diameter ranging from 2 mm to 4 mm of Ti₄₀Cu₄₀Zr₁₀Ni₁₀ alloy were prepared by melt-spinning technique and copper mould casting method, respectively. The microstructure, thermal stability and mechanical properties of the bulk samples were investigated. A completely glassy single phase is formed in the 2 mm rod sample. Increasing the diameter of the rod samples resulted in the formation of CuTi crystalline phase in the 3 mm and 4 mm rod samples. The 2 mm single glassy rod sample exhibited a large supercooled liquid region ΔT_x = 58 K and γ = T_x/(T_g + T_l) is 0.390, which indicated that the alloy possessed a good glass-forming ability. The bulk samples also exhibited good mechanical properties. The 2 mm rod sample showed the highest yield strength of about 2086 MPa. The 3 mm rod sample not only showed high yield strength of about 2000 MPa, but also enhanced plastic strain of about 0.71%.     

A critical analysis of the glass-forming ability of alloys

Several empirical rules have been proposed during the past few years to synthesize bulk metallic glasses. But, the real reasons for the improved glass-forming ability of these alloys are still not clear and the ability to design alloy compositions to enable synthesis of larger diameter rods has not improved. The present work conducts a critical analysis of the existing data in terms of the different glass-forming criteria and concludes that the available parameters cannot satisfactorily predict the GFA and explain all the observed data. Reasons for this failure have been suggested.     

Crystallization behaviors of Al-Ni-La amorphous alloys with trace Ti and B

Effects of the single or simultaneous addition of trace Ti and B (?1 at.%) on the glass-forming ability (GFA) and crystallization behaviors of Al₈₈Ni₆La₆ and Al₈₉Ni₆La₅ amorphous alloys were investigated by X-ray diffraction and differential scanning calorimetry. The addition of trace Ti and B deteriorates the GFA, but improves the thermal stability especially if Ti is added singly. The crystallization onset temperature T_x1 of the first exothermic peak increases by 29.5 and 18.0 K when 1% of the Al atoms in Al₈₈Ni₆La₆ and Al₈₉Ni₆La₅ are replaced by Ti, respectively. However, the primary phase during annealing remains unchanged.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.     

Vitrification and crystallization in the system of K2O-B2O3-TiO2

The vitrification and crystallization behavior of melts produced at 1400 °C in the ternary system of K₂O-B₂O₃-TiO₂ is investigated. It is shown that there are two fields of compositions (indicated in mol%) which allow obtaining the glass-ceramic materials with continuous glassy matrix after the cooling of molten compositions. In the first field [TiO₂] = 25-57, [K₂O] = 30-50 and [B₂O₃] = 0-25, the glass-ceramics consisted of the potassium-titanium-borate glassy phase and different crystalline potassium titanates (K₄Ti₃O₈, K₂Ti₂O₅, K₂Ti₄O₉, K₂Ti₆O₁₃). The ratio of TiO₂:K₂O in the obtained titanates increases with [TiO₂] and [B₂O₃]. In the second field, [TiO₂] = 7-37, [K₂O] = 0-25 and [B₂O₃] = 52-93, the obtained glass-ceramics consisted of a similar vitreous phase, as mentioned above, and TiO₂ crystals. During the cooling of the melts, short whiskers-like crystals of anatase formed in the compositions with relatively low [TiO₂] and relatively high [K₂O], whereas long fiber-shaped crystals of rutile appeared with the compositions characterized with relatively high [TiO₂] and relatively low [K₂O]. The possible application of the obtained glass-ceramic materials as a source of fibrous TiO₂, for composite reinforcement, and as solid lubricants is discussed.     

Electric conductivity of glasses in the system Na2O/CaO/SiO2/Fe2O3

The addition of polyvalent transition metal ions to the usually insulating traditional soda-lime-silica glasses can lead to semiconducting properties. We report on synthesis of glasses and glass-ceramics in a soda-lime-silicate based system containing Fe₂O₃ in the concentration range from 5 to 30 mol%. Two sub-systems were considered, in one of them the ratio [Na₂O]/[Fe₂O₃] was varied while in the other one, the ratio [SiO₂]/[Fe₂O₃] was changed. The phase composition of the synthesized products was characterized by X-ray diffraction and energy dispersive X-ray analysis, while the electrical properties were studied by impedance spectroscopy. Partially crystallized non-reduced samples are semiconducting even at room temperature while the glassy samples (both reduced and non-reduced) exhibit semiconducting properties at temperatures equal or larger than 100 °C. An attempt is done to predict the physical approximation explaining the conduction process in the glasses.     

Plasticity induced by nanoparticle dispersions in bulk metallic glasses

We show room temperature plasticity in several ZrCu-based bulk metallic glasses (BMG) after dispersions of crystalline nanoparticles were generated prior to mechanical testing. BMGs are heated in synchrotron light in transmission such that annealing can be interrupted at the very first detection of nucleation of the crystallites. Effect of embedded nanocrystals on the mechanical properties of BMG-Composites was investigated by compressive testing. When nanocrystal dispersions were generated, zirconium-copper-based BMGs that initially showed no plastic deformation prior to fracture, exhibited ductile behavior in compression with about 10% deformation.