Sodium tracer diffusion in glasses of the type (CaO·Al2O3)x(2 SiO2)1−x

Tracer diffusion coefficients of the radioactive isotope Na-22 were measured in glasses of the type (CaO·Al₂O₃)_x(2 SiO₂)_1−x to study the diffusion of sodium as a function of glass composition, x, temperature and initial water content. The diffusion of Na-22 in glasses diffusion-annealed in dry air can always be well described by a single tracer diffusion coefficient, but sometimes not in samples annealed in common air. It was found that the sodium tracer diffusion coefficient decreases by about six orders of magnitude when the glass composition x changes from 0 to 0.75 at 800 °C. The temperature dependence of the diffusion of sodium seems to decrease as the silica content increases. Variations of the initial water content in some of the glasses investigated did not very significantly influence the rate of the tracer diffusion of sodium.     

Crystallization behavior of (GeS2)0.1(Sb2S3)0.9 glass

The crystal growth kinetics of antimony trisulfide in (GeS₂)_0.1(Sb₂S₃)_0.9 glass has been studied by microscopy and DSC. The linear crystal growth kinetics has been confirmed in the temperature range 492 ? T ? 515 K (E_G = 405 ± 7 kJ mol⁻¹). The applicability of standard growth models has been assessed. From the crystal growth rate corrected for viscosity plotted as a function of undercooling it has been found that the most probable mechanism is interface controlled 2D nucleated growth. The non-isothermal DSC data, corresponding to the bulk sample, can be described by the Johnson-Mehl-Avrami equation.     

Structure and properties of Ni60(Nb100−xTax)34Sn6 bulk metallic glass alloys

Refractory bulk metallic glasses and bulk metallic glass composites are formed in quaternary Ni-Nb-Ta-Sn alloy system. Alloys of composition Ni₆₀(Nb_100−xTa_x)₃₄Sn₆ (x = 20, 40, 60, 80) alloys were prepared by injection-casting the molten alloys into copper molds. Glassy alloys are formed in the thickness of half mm strips. With thicker strips (e.g., 1 mm), Nb₂O₅ and Ni₃Sn phases and the amorphous phase form an in situ composite. Glass transition temperatures, crystallization temperatures, and ΔT_x, defined as T_x1 − T_g (T_x1: first crystallization temperature, T_g: glass transition temperature) of the alloys increase dramatically with increasing Ta contents. These refractory bulk amorphous alloys exhibit high Young’s modulus (155-170 GPa), shear modulus (56-63 GPa), and estimated yield strength (3-3.6 GPa).     

Sodium tracer diffusion in glasses of the type (Na2O)0.2[(BO1.5)x(SiO2)1 − x]0.8

Sodium tracer diffusion coefficients, D_Na*, have been measured in sodium borosilicate glasses of the type (Na₂O)_0.2[(BO_1.5)_x(SiO₂)_1 − x]_0.8 as a function of temperature and the composition parameter x. In these glasses, which can alternatively also be described by using the formula Na₂O·(2B₂O₃)_x·(4SiO₂)_1 − x, one network former unit, SiO₂, is replaced by another one, BO_1.5, while keeping the sodium concentration constant. At constant temperature, the tracer diffusion coefficient of sodium as a function of x has a shallow minimum at about x = 0.7. At temperatures below about 310 °C the temperature dependences of the measured tracer diffusion coefficients are of Arrhenius-type; at higher temperatures one observes an increase in the temperature dependence with increasing temperature. The activation energy derived from sodium tracer diffusion data for temperatures up to about 310 °C increases about linearly with increasing x from about 70 to 80 kJ/mol. The pre-exponential factor as a function of x varies by about one order of magnitude and has a minimum at about x = 0.4. Values derived for the Haven-ratio are smaller than one and show a shallow minimum as a function of x at around x = 0.75. Furthermore, it was investigated whether there is a significant, directly measurable uptake of water during annealing in moist atmospheres and whether water taken up from moist atmospheres can influence the diffusion of sodium.     

The effect of composition on UV-vis-NIR spectra of iron doped glasses in the systems Na2O/MgO/SiO2 and Na2O/MgO/Al2O3/SiO2

Glasses with the compositions xNa₂O · 10MgO · (90 − x)SiO₂, 10Na₂O · xMgO · (90 − x)SiO₂, 5Na₂O · 15MgO · xAl₂O₃ · (80 − x)SiO₂, xNa₂O · 10MgO · 10Al₂O₃ · (80 − x)SiO₂, 10Na₂O · 10MgO · xAl₂O₃ · (80 − x)SiO₂, 10Na₂O · 5MgO · 10Al₂O₃ · (80 − x)SiO₂ were melted and studied using UV-vis-NIR spectroscopy in the wavenumber range from 5000 to 30 000 cm⁻¹. At [Al₂O₃] > [Na₂O], the UV-cut off is strongly shifted to smaller wavenumbers and the NIR peak at around 10 000 cm⁻¹ attributed to Fe²⁺ in sixfold coordination gets narrower. Furthermore, the intensity of the NIR peak at 5500 cm⁻¹ increases. This is explained by the incorporation of iron in the respective glass structures.     

Laser-induced crystallization of β′-RE2(MoO4)3 ferroelectrics (RE: Sm, Gd, Dy) in glasses and their surface morphologies

The glasses with the compositions of 21.25RE₂O₃-63.75MoO₃-15B₂O₃ (RE: Sm, Gd, Dy) were prepared and the formation of β′-RE₂(MoO₄)₃ ferroelectrics was confirmed in the crystallized glasses obtained through a conventional crystallization in an electric furnace. The features of the glass structure and crystallization behavior were clarified from measurements of Raman scattering spectra. Continuous-wave Nd:YAG laser with a wavelength of 1064 nm (laser power: 0.6-0.9 W, laser scanning speed: S = 1-16 μm/s) was irradiated to 10.625Sm₂O₃-10.625Gd₂O₃ (or Dy₂O₃)-63.75MoO₃-15B₂O₃ glasses, and the structural modification was induced at the glass surface. At the scanning speed of S = 10 μm/s, crystal lines consisting of β′-Gd_2−xSm_x(MoO₄)₃ or β′-Dy_2−xSm_x(MoO₄)₃ crystals were patterned on the glass surface. It was found that those crystal lines have the surface morphology with periodic bumps. At S = 1 μm/s, it was found that crystal lines consist of the mixture of paraelectric α-Gd_2−xSm_x(MoO₄)₃ and ferroelectric β′-Gd_2−xSm_x(MoO₄)₃ crystals, indicating the phase transformation from the β′ phase to the α phase during laser irradiation. Homogeneous crystal lines with β′-RE₂(MoO₄)₃ ferroelectrics have not been written in this study, but further research is continuing.     

Electron spin resonance and magnetic studies on CaO-SiO2-P2O5-Na2O-Fe2O3 glasses

Room temperature electron spin resonance (ESR) spectra and temperature dependent magnetic susceptibility measurements have been performed to investigate the effect of iron ions in 41CaO · (52 − x)SiO₂ · 4P₂O₅ · xFe₂O₃ · 3Na₂O (2 ? x ? 10 mol%) glasses. The ESR spectra of the glass exhibited the absorptions centered at g ≈ 2.1 and g ≈ 4.3. The variation of the intensity and linewidth of these absorption lines with composition has been interpreted in terms of variation in the concentration of the Fe²⁺ and Fe³⁺ in the glass and the interaction between the iron ions. The magnetic susceptibility data were used to obtain information on the relative concentration and interaction between the iron ions in the glass.     

Thermal dissolution of Ag(Cu) in amorphous Ge(Sx Se1 − x)2 system

Thermally induced solid state reaction of Ag(Cu) into thin Ge(S_x Se_1 − x)₂ films with x = 0, 0.1, 0.4 and 1.0 was investigated using a step by step technique in order to design films with exact Ag(Cu) concentrations for applications in integrated IR optical devices. A thin film of Ag(Cu) was deposited on top of the host Ge(S_x Se_1 − x)₂ films followed by annealing in vacuum at constant temperature, which resulted in homogeneous films of good optical quality. The variation in Ag(Cu) concentration in the films ranged between 5 and 35 at.%. The kinetics of the diffusion and dissolution of metal in the host films was measured by optically monitoring the change in thickness of doped chalcogenide during consecutive thermal annealing steps. The kinetics studies revealed that the thermal dissolution rate of the Cu is greater than that of Ag. Optical UV-VIS transmission spectra of chalcogenide glass layers, undoped and thermal doped by Ag(Cu), were measured to establish the optical properties of the films. The spectra were analyzed using the technique proposed by Swanepoel and the results show that the addition of metal increases the absorption coefficient in the power-law regime and consequently the optical gap decreases and the refractive index increases. The amorphous character of the films was checked by X-ray diffraction which confirmed the amorphous structure of all Ag(Cu)GeSSe thin films.     

Electrical conductivity of NbN-SiO2 films obtained by ammonolysis of Nb2O5-SiO2 sol-gel derived coatings

The studies of electrical conductivity of NbN-SiO₂ films are reported. To obtain these films, sol-gel derived xNb₂O₅-(100 − x)SiO₂ (where x = 100, 90, 80, 70, 60, 50 mol%) coatings were nitrided at 1200 °C. The nitridation process leads to the formation of some disordered structures, with NbN metallic grains dispersed in insulating SiO₂ matrix. The structure of the samples was studied using X-ray diffraction (XRD) and atomic force microscopy (AFM). The electrical conductivity was measured with the conventional four-terminal method in the temperature range from 5 to 280 K. The superconducting transition was not observed even for the sample that does not contain silica. All the samples exhibit negative temperature coefficient of resistivity. The results of conductivity versus temperature may be described on the grounds of a model proposed for a weakly disordered system.     

Effects of Nb2O5 Replacement by Er2O3 on elastic and structural properties of 75TeO2-(10 − x)Nb2O5-15ZnO-(x)Er2O3 glass

Tellurite 75TeO₂-(10 − x)Nb₂O₅-15ZnO-(x)Er₂O₃; (x = 0.0-2.5 mol%) glass system with concurrent reduction of Nb₂O₅ and Er₂O₃ addition have been prepared by melt-quenching method. Elastic properties together with structural properties of the glasses were investigated by measuring both longitudinal and shear velocities using the pulse-echo-overlap technique at 5 MHz and Fourier Transform Infrared (FTIR) spectroscopy, respectively. Shear velocity, shear modulus, Young's modulus and Debye temperature were observed to initially decrease at x = 0.5 mol% but remained constant between x = 1.0 mol% to x = 2.0 mol%, before increasing back with Er₂O₃ addition at x = 2.5 mol%. The initial drop in shear velocity and related elastic moduli observed at x = 0.5 mol% were suggested to be due to weakening of glass network rigidity as a result of increase in non-bridging oxygen (NBO) ions as a consequence of Nb₂O₅ reduction. The near constant values of shear velocity, elastic moduli, Debye temperature, hardness and Poisson's ratio between x = 0.5 mol% to x = 2.0 mol% were suggested to be due to competition between bridging oxygen (BO) and NBO ions in the glass network as Er₂O₃ gradually compensated for Nb₂O₅. Further addition of Er₂O₃ (x > 2.0 mol%) seems to further reduce NBO leading to improved rigidity of the glass network causing a large increase of ultrasonic velocity (v_L and v_S) and related elastic moduli at x = 2.5 mol%. FTIR analysis on NbO₆ octahedral, TeO₄ trigonal bipyramid (tbp) and TeO₃ trigonal pyramid (tp) absorption peaks confirmed the initial formation of NBO ions at x = 0.5 mol% followed by NBO/BO competition at x = 0.5-2.0 mol%. Appearance of ZnO₄ tetrahedra and increase in intensity of TeO₄ tbp absorption peaks at x = 2.0 mol% and x = 2.5 mol% indicate increase in formation of BO.     

The structure and optical properties of GeO2-GeS2 glasses

Oxy-chalcogenide glasses with compositions of xGeO₂-(100 − x)GeS₂, where 0 ? x ? 100 mol%, have been prepared and studied in terms of their structures and optical properties. X-ray fluorescence spectroscopy shows that Ge:S ratio can deviate from GeS₂ by ∼10 at.%, depending critically upon the preparation conditions. Raman scattering spectroscopy suggests that stoichiometric GeO₂-GeS₂ glasses have a heterogeneous structure in the scale of 1-100 nm. The optical gaps are nearly constant at 3.0-3.5 eV for glasses with 0 ? x ? 80 mol% and abruptly increase to ∼6 eV in GeO₂. This dependence suggests that the optical gap is governed by GeS₂ clusters, which are isolated and/or percolated. Composition-deviated glasses appear as orange and brown, and these glasses seem to have more inhomogeneous structures.     

The effect of PbF2 content on the microstructure and upconversion luminescence of Er-doped SiO2-PbF2-PbO glass ceramics

The Er³⁺ doped transparent oxyfluoride glass ceramics were obtained by appropriate heat treatment of the precursor glasses with composition (mol%) 50SiO₂-xPbF₂-(50 − x)PbO-0.5ErF₃. The microstructure and optical properties of the glasses and glass ceramics were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), absorption spectra and luminescence spectra. The intensity of upconversion luminescence significantly increased in glass ceramics compared to that in precursor glass. The emission bands centered around 660 nm (⁴F_9/2 → ⁴I_15/2) and 410 nm (²H_9/2 → ⁴I_15/2) were simultaneously observed in glass ceramics but cannot be seen in the corresponding precursor glass. The influence of different PbF₂ content on the microstructure and upconversion luminescence of the samples was analyzed in detail. The results indicated that with the increase of PbF₂ content, the Ω₂ was almost the same and the ratios of red to green upconversion luminescence decreased in glass ceramics.     

Boron content dependance of magnetoimpedance in Fe91−xZr5BxNb4 alloys

A systematic investigation of the influence of B content on the magnetoimpedance (MI) effect in melt-spun Fe_91−xZr₅B_xNb₄ (FZBN, 0 ? x ? 30) ribbons has been performed within a frequency range, f ∼ 310-1110 kHz and under a varying dc magnetic field (H_dc) up to 70 Oe. The MI effect is not observed in the sample with x ? 5 but within the range 8 ? x ? 30. A distinct MI effect has been observed with a maximum change of 180% at around 1.1 MHz in the sample with x = 20, coincident with a saturation magnetic field of 66 Oe and a field sensitivity of about 7%/Oe. Magnetic measurements reveal that the MI effect and B content dependence of the effect are closely related to coercivity of the FZBN alloy series, except for the sample with 20 at.%. The drastic MI ratio observed in the sample with x = 20 is ascribed to its special microstructure. The mechanism of the MI effect in FZBN alloys and of the significant MI value appearing at a B content of x = 20 is discussed in this paper.     

Spectroscopic properties of Er-doped xGeO2-(80 − x)TeO2-10ZnO-10BaO glasses

Erbium-doped glasses with composition xGeO₂-(80 − x)TeO₂-10ZnO-10BaO were prepared by melt-quenching technique. The phonon sideband spectra and the optical absorption band edges for the host matrix were confirmed by means of the spectral measurements. Standard Judd-Ofelt calculations have been completed to these glasses. The dependence of up-conversion and infrared emission under 980 nm excitation on the glass composition was studied. The quantum efficiencies for the ⁴I_13/2 → ⁴I_15/2 transition of trivalent erbium in the glasses were estimated.     

The glass transition temperature and infrared absorption spectra of: (70−x)TeO2 + 15B2O3 + 15P2O5 + xLi2O glasses

Glasses of the system: (70−x) TeO₂ + 15B₂O₃ + 15P₂O₅ + xLi₂O, where x = 5, 10, 15, 20, 25 and 30 mol% were prepared by melt quench technique. Dependencies of their glass transition temperatures (T_g) and infrared (IR) absorption spectra on composition were investigated. It is found that the gradual replacement of oxides, TeO₂ by Li₂O, decreases the glass transition temperature and increases the fragility of the glasses. Also, IR spectra revealed broad weak and strong absorption bands in the investigated range of wave numbers from 4000 to 400 cm⁻¹. These bands were assigned to their corresponding bond modes of vibration with relation to the glass structure.     

Spectral properties of PbO-P2O5 glasses

The optical absorption spectra of xPbO-(100 − x) P₂O₅ glasses where x = 5, 10, 15, 20, 25, and 30 is reported. The spectral absorption of these glasses was measured in the spectral range 300-900 nm at room temperature. Optical absorption spectra show that the absorption edge has a tail extending towards lower energies. The edge shifts nearly linearly towards higher energies with increasing PbO content. The degree of the edge shift was found to depend on the PbO content and is mostly related to the structural rearrangement and the relative concentrations of the glass basic units. The optical energy gap increases, from 2.55 to 3.05 eV by increasing PbO content from 5 to 30 mol%. The width of the localized states is decreased by increasing PbO content.     

Non-isothermal crystallization kinetics study on new amorphous Ga20Sb5S75 and Ga20Sb40S40 chalcogenide glasses

Bulk glasses of the system Ga₂₀Sb_xS_80−x (x = 5 and 40) were prepared for the first time by the known melt quenching technique. Non-isothermal differential scanning calorimetric (DSC) measurements of as-quenched Ga₂₀Sb_xS_80−x (x = 5 and 40) chalcogenide glasses reveal that the characteristic temperatures e.g. the glass transition temperature (T_g), the temperature corresponding to the maximum crystallization rate (T_p) recorded in the temperature range 400-650 K for x = 5 and 480-660 K for x = 40 are strongly dependent on heating rate and Sb content. Upon heating, these glasses show a single glass transition temperature (T_g) and double crystallization temperatures (T_p1 and T_p2) for x = 5 which overlapped and appear as a single crystallization peak (T_p) for x = 40. The activation energies of crystallization E_c were evaluated by three different methods. The crystallization data were examined in terms of recent analysis developed for non-isothermal conditions. The crystalline phases resulting from (DSC) have been identified using X-ray diffraction.     

RDF analysis, positron annihilation and Raman spectroscopy of xTiO2-(60 − x)SiO2-40Na2O non-linear optical glasses: III. Non-bridging oxygen bonds tracing and structure analysis

xTiO₂-(60 − x)SiO₂-40Na₂O glasses have proven an interesting linear and non-linear optical properties [M. Abdel-Baki, F. Abdel Wahab, F. El-Diasty, Mater. Chem. Phys. 96 (2006) 201]. The investigated glasses show one order of magnitude enhancement for the second-order index of refraction and third-order optical susceptibility over some TiO₂ silicate glasses. In this work, we continue studying these glasses using three different techniques to analyze the glass structures seeking to provide a deep insight for the relation between structure, compositions and the optical characteristics of these glasses. Radial Distribution Function analysis (RDF) combined Raman spectroscopy are used to study these glasses. Positron annihilation lifetime spectroscopy and Doppler broadening measurements are carried out to investigate the change in the glass structure as the incorporation of TiO₂ concentration into glass. The origin of the non-bridging oxygen (NBO) bonds has been traced to correlate their existence with the measured non-linear optical properties of the investigated glasses.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Compositional dependence of the optical properties of amorphous Sb2Se3−xSx thin films

Thin films of Sb₂Se_3−xS_x solid solutions (x = 0, 1, 2, and 3) were deposited by thermal evaporation of presynthesized materials on glass substrates held at room temperature. The films compositions were confirmed by using energy dispersive analysis of X-rays (EDAX). X-ray diffraction studies revealed that all the as-deposited films as well as those annealed at T_a < 423 K have amorphous phase. The optical constants (n, k) and the thickness (t) of the films were determined from optical transmittance data, in the spectral range 500-2500 nm, using the Swanepoel method. The dispersion parameters were determined from the analysis of the refractive index. An analysis of the optical absorption spectra revealed an Urbach’s tail in the low absorption region, while in the high absorption region an indirect band gap characterizes the films with different compositions. It was found that the optical band gap energy increases quadratically as the S content increases.