Physicochemical studies of phosphate based P2O5-Na2O-CaO-TiO2 glasses for biomedical applications

Glasses P₂O₅-Na₂O-CaO-TiO₂ with different TiO₂ contents and fixed P₂O₅ (45 wt%) and CaO (24 wt%) have been prepared employing the normal melting and annealing technique. Measurements such as ultrasonic velocity, attenuation, solubility and pH have been carried out in all the compositions of the glasses. It is interesting to note that the above measured ultrasonic parameters exhibit an abnormal behavior (minimum) at 0.5 wt% of TiO₂ content, beyond which an increase in these parameters with increasing TiO₂ content is observed. The maximum pH values and Ca²⁺ ion release have been observed for the TiO₂ free glass those compositions with and the low TiO₂(?1.0 wt%) content. As the content of the TiO₂ increases, the solubility of the glasses decreases. The observed weight loss reveals two stages of phosphate dissolution kinetics i.e. the first stage, in which the weight loss is proportional to t^1/2, and a second stage in which a linear behavior is observed.     

Synthesis and characterization of calcium phosphate based bioactive quaternary P2O5-CaO-Na2O-K2O glasses

Calcium phosphate based bioactive quaternary glass systems P₂O₅-CaO-Na₂O-K₂O were prepared by melt growth technique. Glasses were prepared in five different compositions by fixing P₂O₅ at 47 mol% and CaO at 30.5 mol% and by varying the K₂O and Na₂O concentrations. The structural properties of the glasses are analyzed using X-ray diffraction (XRD) studies and scanning electron microscopy (SEM) studies; and the composition of the glasses are studied using energy dispersive X-ray spectrum (EDS). The microhardness of the glass systems are studied by Vickers hardness measurements and the bioactivity of the glasses are studied using in vitro study. The thermal properties have been examined by means of thermogravimetric analysis (TGA) and differential thermal analysis (DTA). The ultrasonic velocity measurements show that the addition of K₂O contents produces non-bridging oxygen ion and hence weaken of the glass structure. The weakening of the glass structure reduces the ultrasonic velocity and hence an increase in attenuation.     

Sulfur behavior in silicate glasses and melts: Implications for sulfate incorporation in nuclear waste glasses as a function of alkali cation and V2O5 content

The presence of sulfur in radioactive waste to be incorporated in borosilicate glasses entails difficulties mainly due to the relatively low solubility of sulfates in the vitreous phase. In this work a study is presented on the effects of the ratio R = [Na₂O]/[B₂O₃], the type of sulfate added and the addition of V₂O₅ on the incorporation of sulfates in borosilicate glasses. Glass samples were prepared at the laboratory scale (up to 50-100 g) by melting oxide and sulfate powders under air in Pt/Au crucibles. XRF and ICP/AES chemical analysis, SEM/EDS, microprobe WDS and Raman spectroscopy were employed to characterize the fabricated samples. The main experimental results confirm that the incorporation of sulfates in borosilicate glasses is favored by the network depolymerization, which evolves with the ratio R. The addition of V₂O₅ seems to accelerate the kinetics of sulfur incorporation in the glass and, probably, increase the sulfate solubility by modifying the borate network and fostering the formation of voids of shape and size compatible with the sulfur coordination polyhedron in the glassy network. The kinetics of X₂SO₄ incorporation in the glass seems to be slower when X = Cs.     

The effect of PbF2 content on the microstructure and upconversion luminescence of Er-doped SiO2-PbF2-PbO glass ceramics

The Er³⁺ doped transparent oxyfluoride glass ceramics were obtained by appropriate heat treatment of the precursor glasses with composition (mol%) 50SiO₂-xPbF₂-(50 − x)PbO-0.5ErF₃. The microstructure and optical properties of the glasses and glass ceramics were determined by differential scanning calorimetry (DSC), X-ray diffraction (XRD), absorption spectra and luminescence spectra. The intensity of upconversion luminescence significantly increased in glass ceramics compared to that in precursor glass. The emission bands centered around 660 nm (⁴F_9/2 → ⁴I_15/2) and 410 nm (²H_9/2 → ⁴I_15/2) were simultaneously observed in glass ceramics but cannot be seen in the corresponding precursor glass. The influence of different PbF₂ content on the microstructure and upconversion luminescence of the samples was analyzed in detail. The results indicated that with the increase of PbF₂ content, the Ω₂ was almost the same and the ratios of red to green upconversion luminescence decreased in glass ceramics.     

Glass formation in the MoO3-CuO-PbO system

Glasses in the MoO₃-CuO-PbO system are obtained at high cooling rates (10⁴-10⁵ K/s) and characterized using X-ray diffraction (XRD), differential thermal analysis (DTA), infrared (IR) and X-ray photoelectron spectroscopy (XPS). Two glass formation regions are determined: one with compositions having a high MoO₃ content (50-80 mol%) and the other in the PbO-rich compositions (65-80 mol%). In the region of MoO₃-rich compositions the building units of the amorphous network are МоО₆, МоО₄ and CuO₄ groups. For these high MoO₃ contents and respectively low PbO concentrations, the lead oxide is supposed to act as a network modifier while at high content PbO is found to be the main glass network former. In latter case the structure of glasses is formed by chains of PbO_n (n = 3, 4) polyhedra, between which there are isolated MoO₄ and CuO₄ complexes. IR and XPS data reveal the existence of Mo-O-Mo, Mo-O-Me(Me’) (where Me = Cu²⁺, Cu¹⁺ and Me’ = Pb) and Me(Me’)-O-Me(Me’) bonds in the amorphous network. Surprising result is found for low PbO content (10 mol%) where the lead oxide acts as glass network modifier: the actual MoO₃ content drops strongly which is accompanied with a significant increase of the actual CuO content with respect to their nominal MoO₃-CuO composition. Such effect is not observed in PbO-rich composition (70 mol%) where PbO has a role of network former.     

The structure and optical properties of GeO2-GeS2 glasses

Oxy-chalcogenide glasses with compositions of xGeO₂-(100 − x)GeS₂, where 0 ? x ? 100 mol%, have been prepared and studied in terms of their structures and optical properties. X-ray fluorescence spectroscopy shows that Ge:S ratio can deviate from GeS₂ by ∼10 at.%, depending critically upon the preparation conditions. Raman scattering spectroscopy suggests that stoichiometric GeO₂-GeS₂ glasses have a heterogeneous structure in the scale of 1-100 nm. The optical gaps are nearly constant at 3.0-3.5 eV for glasses with 0 ? x ? 80 mol% and abruptly increase to ∼6 eV in GeO₂. This dependence suggests that the optical gap is governed by GeS₂ clusters, which are isolated and/or percolated. Composition-deviated glasses appear as orange and brown, and these glasses seem to have more inhomogeneous structures.     

Thermal and some physical properties of glasses in the La2O3−CaO−B2O3 ternary system

Glasses in the La₂O₃−CaO−B₂O₃ ternary system were studied. The glass forming range as determined by the appearance of the annealed cast was found to match previously published findings. Clear glasses were formed in the composition range of 5.7−19.1 mol% La₂O₃ with constant B₂O₃ content of 71.4 mol%, and in glasses of constant La₂O₃:CaO ratio of 1:4 with B₂O₃ content in the range of 71.4-55.0 mol%. The non-linear optical crystalline phase La₂Ca₂B₁₀O₁₉ was crystallized from the clear glasses after heat treatments, as determined by powder XRD. Two types of the LaBO₃ crystalline phases were detected in the partially and the fully crystallized glass compositions outside the glass forming range. Data are reported for the glass transition temperature (T_g), dilatometric softening point (T_d), linear coefficient of expansion (α), onset crystallization temperature (T_x), exothermal peak temperature (T_P), density (ρ) and index of refraction (n_D) in the clear glasses.     

Phase separation and crystallization in the system SiO2-Al2O3-P2O5-B2O3-Na2O glasses

The phase separation and crystallization behavior in the system (80 − X)SiO₂ · X(Al₂O₃ + P₂O₅) · 5B₂O₃ · 15Na₂O (mol%) glasses was investigated. Glasses with X = 20 and 30 phase separated into two phases, one of which is rich in Al₂O₃-P₂O₅-SiO₂ and forms a continuous phase. Glasses containing a larger amount of Al₂O₃-P₂O₅ (X = 40 and 50) readily crystallize and precipitates tridymite type AlPO₄ crystals. It is estimated that the phase separation occurs forming continuous Al₂O₃-P₂O₅-SiO₂ phase at first, and then tridymite type AlPO₄ crystals precipitate and grow in this phase. Highly transparent glass-ceramics comparable to glass can be successfully obtained by controlling heat treatment precisely. The crystal size and percent crystallinity of these transparent glass-ceramics are 20-30 nm and about 50%, respectively.     

Thermal and optical investigation of EuF3-doped lead fluorogermanate glasses

Europium-doped lead germanate and lead fluorogermanate glasses are studied by using differential thermal analysis, X-ray diffraction, photoluminescence and fluorescence lifetimes measurements of the ⁵D_j, j = 0, 1, 2 levels. PbF₂ addition increases the thermal stability of the lead germanate glass, while Eu³⁺ ions promote the crystallization of β-PbF₂:Eu³⁺ nano-crystals embedded in a glassy matrix. In the lead fluorogermanate glasses, Eu³⁺ ions exhibit a strong affinity for F⁻ ions although oxygen ions are much more numerous. It appears that luminescence concentration quenching is not important, while cross relaxation is very efficient in the glasses. The results allow to propose for these glasses a molecular model in which small fluorine rich island, incorporating the Eu³⁺ ions in low symmetry sites, are separated from each other by chains of germanate (GeO₄)⁴⁻ ions linked together.     

Crystallization processes of Li2O-Ga2O3-SiO2-NiO system glasses

Crystallization processes of Li₂O-Ga₂O₃-SiO₂-NiO system glasses have been studied by X-ray diffraction, differential calorimetry and optical absorption. Transparent glass-ceramic containing LiGa₅O₈:Ni²⁺ as the sole crystalline phase has been obtained from glass with the composition of 13Li₂O-23Ga₂O₃-64SiO₂-0.1NiO (in mol%) by the heat treatment in the temperature range from 923 to 953 K. It was revealed that the specific surface area of samples enhances crystallization of LiGaSi₂O₆ but obstructed that of LiGa₅O₈. LiGa₅O₈ grew to nano-sized crystallites dispersed in the glass matrices and did not affect the transparency seriously. In contrast, LiGaSi₂O₆ grew to crystallites with diameters more than 100 nm on the surface and made the glasses opaque. Optical absorption measurements revealed that doped Ni²⁺ occupied five-folded trigonal bipyramidal sites in the as-quenched glass matrices but six-folded octahedral sites of precipitated LiGa₅O₈ in the glass-ceramics. It was confirmed that transparent glass-ceramic containing Ni²⁺:LiGa₅O₈ was effectively obtained by the heat treatment at a temperature of 953 K for 10 h.     

Effect of BaO content on the sintering and physical properties of BaO-B2O3-SiO2 glasses

A BaO-B₂O₃-SiO₂ glass system was chosen as a candidate composition for the application to Pb-free low temperature sinterable glass. The effect of BaO content on the crystallization, sintering behavior, and properties of the glasses was examined. Both the glass transition temperature and crystallization temperature decreased as the BaO content increased. Crystallization easily occurred during sintering with a BaO content of more than 50 mol%, which effectively inhibited the over-firing phenomenon. The dielectric characteristics and thermal expansion coefficient of the glasses were examined and the results were explained on the basis of the crystallization and densification of the specimens.     

Sodium tracer diffusion in glasses of the type (CaO·Al2O3)x(2 SiO2)1−x

Tracer diffusion coefficients of the radioactive isotope Na-22 were measured in glasses of the type (CaO·Al₂O₃)_x(2 SiO₂)_1−x to study the diffusion of sodium as a function of glass composition, x, temperature and initial water content. The diffusion of Na-22 in glasses diffusion-annealed in dry air can always be well described by a single tracer diffusion coefficient, but sometimes not in samples annealed in common air. It was found that the sodium tracer diffusion coefficient decreases by about six orders of magnitude when the glass composition x changes from 0 to 0.75 at 800 °C. The temperature dependence of the diffusion of sodium seems to decrease as the silica content increases. Variations of the initial water content in some of the glasses investigated did not very significantly influence the rate of the tracer diffusion of sodium.     

Electric conductivity of glasses in the system Na2O/CaO/SiO2/Fe2O3

The addition of polyvalent transition metal ions to the usually insulating traditional soda-lime-silica glasses can lead to semiconducting properties. We report on synthesis of glasses and glass-ceramics in a soda-lime-silicate based system containing Fe₂O₃ in the concentration range from 5 to 30 mol%. Two sub-systems were considered, in one of them the ratio [Na₂O]/[Fe₂O₃] was varied while in the other one, the ratio [SiO₂]/[Fe₂O₃] was changed. The phase composition of the synthesized products was characterized by X-ray diffraction and energy dispersive X-ray analysis, while the electrical properties were studied by impedance spectroscopy. Partially crystallized non-reduced samples are semiconducting even at room temperature while the glassy samples (both reduced and non-reduced) exhibit semiconducting properties at temperatures equal or larger than 100 °C. An attempt is done to predict the physical approximation explaining the conduction process in the glasses.     

Development and characterizations of BaO-CaO-Al2O3-SiO2 glass-ceramic sealants for intermediate temperature solid oxide fuel cell application

Several compositions based on BaO-CaO-Al₂O₃-SiO₂ (BCAS) glass system have been studied in this investigation to see their applicability as sealant for solid oxide fuel cell (SOFC). The glasses as well as the corresponding glass-ceramics have been systematically characterized by differential thermal analysis, dilatometry, X-ray diffractometry, electron microscopy and impedance analysis to examine their suitability as sealant. While the glass transition temperature (T_g) determined from DTA are within 600-665 °C, the coefficient of thermal expansion (CTE) can be tailored between 9.5 and 13.0 × 10⁻⁶ K⁻¹. These glasses are found to be well adhered with metallic interconnects, such as commercial ferritic steel (Crofer22APU), at an optimum sealing temperature of 850 °C. The shrinkage behavior of the developed glasses in their pellet form has also been investigated. The resistivities of the glass-ceramics, as obtained from impedance analysis, are found to be within 10⁴-10⁶ Ω cm at 800 °C. Under sandwiched condition between two metals, some of the developed compositions are found to maintain this high resistivity even after 100 h of operation. One of the glass compositions has shown a low leak-rate of the order of ∼10⁻⁷ Pa m² s⁻¹.     

Glass formation in the ternary Zr-Zr2Cu-Zr2Ni system

Glass formation and glass forming ability in the ternary Zr-Cu-Ni system were studied systematically. For Cu mold casting, the critical size for glass formation was found to be 1 mm in a relatively wide composition range of 56-64  at.% Zr, 16-26 at.% Cu and 16-24 at.% Ni. The phases competing with glass formation were found to be Zr, Zr₂Cu and Zr₂Ni. Despite the fact that Cu and Ni are completely miscible with each other, they cannot be regarded as simple substitution to each other in the case of glass formation in the Zr-Zr₂Cu-Zr₂Ni ternary eutectic system.     

Fabrication and properties of novel low-melting glasses in the ternary system ZnO-Sb2O3-P2O5

Glasses in the ternary system ZnO-Sb₂O₃-P₂O₅ were investigated as potential alternatives to lead based glasses for low temperature applications. The glass-forming region of ZnO-Sb₂O₃-P₂O₅ system has been determined. Structure and properties of the glasses with the composition (60 − x)ZnO-xSb₂O₃-40P₂O₅ were characterized by infrared spectra (IR), differential thermal analysis (DTA) and X-ray diffraction (XRD). The results of IR indicated the role of Sb³⁺ as participant in glass network structure, which was supported by the monotonic and remarkable increase of density (ρ) and molar volume (V_M) with increasing Sb₂O₃ content. Glass transition temperature (T_g) and thermal stability decreased, and coefficient of thermal expansion (α) increased with the substitution of Sb₂O₃ for ZnO in the range of 0-50 mol%. XRD pattern of the heat treated glass containing 30 mol% Sb₂O₃ indicated that the structure of antimony-phosphate becomes dominant. The improved water durability of these glasses is consistent with the replacement of easily hydrated phosphate chains by corrosion resistant P-O-Sb bonds. The glasses containing ?30 mol% Sb₂O₃ possess lower T_g (<400 °C) and better water durability, which could be alternatives to lead based glasses for practical applications with further composition improvement.     

Structure and properties of glasses in the MI + M2S + (0.1Ga2S3 + 0.9GeS2), M = Li, Na, K and Cs, system

The structure and properties of glasses in the MI + M₂S + (0.1Ga₂S₃ + 0.9GeS₂), M = Li, Na, K and Cs, system were studied using Raman, IR spectroscopy, DSC and density measurements to help better understand the ionic transport in these glasses. The glass forming ranges of these ternary glasses were compared to those of the binary alkali sulfide and germanium sulfide systems. The more extensive glass forming range in the Na₂S system was used to examine the more extensive changes of structure and properties of these glasses as a function of Na₂S content. As expected, non-bridging sulfurs (NBS) form with the addition of alkali sulfide. Unlike their oxide counterparts, however, the alkali sulfide doped glasses appear to support longer-range super-structural units. For example, evidence that the adamantine-like structure exists in the K₂S and Cs₂S modified glasses is found in the Raman spectra of the glasses. The structural role of the alkali iodide addition was also explored since the addition of alkali iodide helps to improve the conductivity. For most of these glasses, as observed in many other oxide glasses, the added MI dissolves interstitially into the glass structure network without changing the alkali sulfide network structure. In 0.6Na₂S + 0.4(0.1Ga₂S₃ + 0.9GeS₂) glasses, however, the added NaI may affect the glass structure as it causes systematic changes in the frequency of the Ge-S network mode as seen in the Raman spectra.     

Laser-induced crystallization of β′-RE2(MoO4)3 ferroelectrics (RE: Sm, Gd, Dy) in glasses and their surface morphologies

The glasses with the compositions of 21.25RE₂O₃-63.75MoO₃-15B₂O₃ (RE: Sm, Gd, Dy) were prepared and the formation of β′-RE₂(MoO₄)₃ ferroelectrics was confirmed in the crystallized glasses obtained through a conventional crystallization in an electric furnace. The features of the glass structure and crystallization behavior were clarified from measurements of Raman scattering spectra. Continuous-wave Nd:YAG laser with a wavelength of 1064 nm (laser power: 0.6-0.9 W, laser scanning speed: S = 1-16 μm/s) was irradiated to 10.625Sm₂O₃-10.625Gd₂O₃ (or Dy₂O₃)-63.75MoO₃-15B₂O₃ glasses, and the structural modification was induced at the glass surface. At the scanning speed of S = 10 μm/s, crystal lines consisting of β′-Gd_2−xSm_x(MoO₄)₃ or β′-Dy_2−xSm_x(MoO₄)₃ crystals were patterned on the glass surface. It was found that those crystal lines have the surface morphology with periodic bumps. At S = 1 μm/s, it was found that crystal lines consist of the mixture of paraelectric α-Gd_2−xSm_x(MoO₄)₃ and ferroelectric β′-Gd_2−xSm_x(MoO₄)₃ crystals, indicating the phase transformation from the β′ phase to the α phase during laser irradiation. Homogeneous crystal lines with β′-RE₂(MoO₄)₃ ferroelectrics have not been written in this study, but further research is continuing.     

Chemical durability of lead silicate glass in HNO3, HCl and H2SO4 aqueous acid solutions

Acid dissolution of silicate glasses with different lead contents was rigorously investigated. Aqueous solutions containing 0.5, 1, and 2 N HNO₃, HCl and H₂SO₄ were used to measure the durability of the glass probes. Scanning Electron Microscopy (SEM), Energy Dispersive Spectroscopy (EDS), Inductively Coupled Plasma (ICP), X-ray Diffraction (XRD) and weight loss analyses were used to evaluate the morphological/compositional changes of the probes, the ash deposit, and the aqueous solutions produced due to the dissolution of the glass specimens. Empirical results showed that any increase in the lead content of the probes deteriorated the durability of the glasses by accelerating the hydrolysis of the silica network. ZrO₂ and TiO₂ additions had inverse effect and improved the chemical durability and the practical life-time of the lead glasses.     

Thermo-optic properties of B2O3 doped Li2O-Al2O3-SiO2 glass-ceramics

Reduction in the temperature coefficient of the optical path length, dS/dT of Li₂O-Al₂O₃-SiO₂ glass-ceramics with near-zero thermal expansion coefficient was attempted using control of the temperature coefficient of electronic polarizability, ?, and the thermal expansion coefficient, α. The dS/dT value of 2.6 mol% B₂O₃-doped glass-ceramic was 12.5  × 10⁻⁶/°C, which was 0.9 ×  10⁻⁶/°C smaller than that of B₂O₃-free glass-ceramic. On the other hand, reduction in dS/dT through B₂O₃ doping was not confirmed in precursor glasses. Results showed that reduction in dS/dT of the glass-ceramic through B₂O₃ doping is caused by the reduction in ?. The reduction in ? from B₂O₃ doping was probably attributable to numerical reduction in non-bridging oxide ions with larger ? value by the concentration of boron ions in the residual glass phase. In addition, application of hydrostatic pressure during crystallization was effective to inhibit precipitation of β-spodumene solid solution, which thereby decreases dS/dT. The dS/dT value of B₂O₃-doped glass-ceramic crystallized under 196 MPa was 11.7 ×  10⁻⁶/°C. That value was slightly larger than that of silica glass. The α value of this glass-ceramic was smaller than that of silica glass.