稀土掺杂长余辉发光玻璃的研究

分别采用空气气氛和还原气氛,制备了稀土Eu₂O₃,Dy₂O₃掺杂的铝硅酸盐玻璃,利用荧光光谱仪对样品进行了测试。结果表明：空气气氛条件下制备的铝硅酸盐玻璃样品均不具备长余辉发光性能, 其激发光谱和发光光谱均是Eu3+的5D_i(i=0, 1)→7F_j(j=0～4)跃迁的典型光谱。经还原气氛处理后,单掺和双掺的铝硅酸盐玻璃样品均具有长余辉发光现象,单掺Eu2+的发光峰位于462 nm,而双掺Eu2+和Dy3+的发光峰位于457 nm,且双掺Eu2+和Dy3+的样品陷阱能级较深,样品的发光持续时间长达12 h以上。     

Spectral investigation of R,Ce:YAG(R: Pr~(3+), Eu~(3+), Gd~(3+)) single crystals and their applications in white LEDs

Eu3+, Pr3+, or Gd3+codoped Ce:YAG single crystals were grown by using the Czochralski method. The photoluminescence(PL) emission and excitation spectra and transmittance were measured and investigated. The additional red-emitting bands were observed in the PL emission spectra of Eu,Ce:YAG and Pr,Ce:YAG single crystals and the formation of noticeable peaks was studied with reference to the schematic energy level diagrams. A red-shifted phenomenon was observed in the PL emission spectrum of Gd,Ce:YAG. With codoped Eu3+, Pr3+, or Gd3+ions, warmer white light was achieved for the white light emitting diodes and the color rendering index became higher.     

Ce~(3+)和Tb~(3+)掺杂钆-钡-硅酸盐闪烁玻璃的发光性能

采用高温熔融法制备Ce~(3+)或Tb~(3+)单掺和Ce~(3+)/Tb~(3+)共掺钆-钡-硅酸盐闪烁玻璃。通过透射光谱、光致激发和发射光谱、X射线激发发射光谱及荧光衰减曲线等手段对其发光性能进行研究。实验结果表明:在紫外光的激发下,Tb~(3+)掺杂闪烁玻璃发出明亮的绿光(544 nm),而Ce~(3+)掺杂闪烁玻璃发出蓝紫光。对于Ce~(3+)/Tb~(3+)共掺闪烁玻璃,在紫外光和X射线激发下均观察到Ce~(3+)离子敏化Tb~(3+)离子发光的现象,这是由于存在Ce~(3+)→Tb~(3+)的能量转移。Ce~(3+)/Tb~(3+)共掺闪烁玻璃的最佳Ce2O3掺杂摩尔分数为0.2%,此时Ce~(3+)离子向Tb~(3+)离子的能量传递效率为45.7%。在X射线激发下,Ce_2O_3摩尔分数为0.2%的Ce~(3+)/Tb~(3+)共掺闪烁玻璃在544 nm处的发光强度是Bi_4Ge_3O_(12)(BGO)闪烁晶体在500 nm处发光强度的4.2倍,积分闪烁效率达到BGO晶体的55.6%,这有利于在高分辨率医学成像中降低辐射剂量。     

Ca8Mg(SiO4)4Cl2中Ce3+和Eu2+的光谱性质和能量传递

首次合成了Ｃｅ＾３＋和Ｅｕ＾２＋共激活氯硅酸镁钙Ｃａ８Ｍｇ（ＳｉＯ４）４Ｃｌ２：Ｃｅ＾３＋，Ｅｕ＾２＋高效绿色荧光粉，报道了它们的漫反射光谱、激发和发射光，观察到氯硅酸镁钙中Ｃｅ＾３＋ Ｅｕ＾２＋     

Er~(3+)/Ce~(3+)共掺TeO_2-Bi_2O_3-TiO_2玻璃的热稳定性和光谱特性研究

用高温熔融法制备了Er3+/Ce3+共掺新型碲酸盐玻璃(TeO2-Bi2O3-TiO2).采用差热分析方法研究了玻璃的热稳定性,测试并分析了不同Ce3+离子掺杂浓度下Er3+离子的吸收光谱、上转换光谱和荧光光谱特性.研究结果表明,制备的碲酸盐玻璃具有很好的热稳定性,玻璃析晶温度Tx与玻璃转变温度Tg之差(ΔT=Tx-Tg)达到了185℃,高于其它文献的报道;同时,Ce3+离子共掺引入的能量转移(Ce3+∶2F5/2+Er3+∶4I11/2→Ce3+∶2F7/2+Er3+∶4I13/2)有效地抑制了Er3+离子上转换发光并显著增强了1.53μm波段荧光强度,而发射截面随着Ce3+离子掺杂浓度相应增大.优异的热稳定性以及光谱性能揭示Er3+/Ce3+共掺碲酸盐玻璃是一种潜在的制备宽带掺铒光纤放大器的理想增益介质.     

Raman and optical absorption spectroscopic investigation of Yb-Er codoped phosphate glasses containing SiO_2

Yb-Er codoped Na2O-Al2O3-P2O5-xSiO2 glasses containing 0 - 20 mol% SiO2 were prepared successfully. The addition of SiO2 to the phosphate glass not only lengthens the bond between pS＋ and non-bridging oxygen but also reduces the number of P=O bond. In contrast with silicate glass in which there is only four-fold coordinated Si4＋, most probably there coexist [SiO4] tetrahedron and [SiO6] oetahedron in our glasses. Within the range of 0 - 20 mol% SiO2 addition, the stimulated emission cross-section of Era＋ ion only decreases no more than 10%. The Judd-Ofelt intensity parameters of Er3＋, Ω2 does not change greatly, but Ω4 and Ω6 decrease obviously with increasing SiO2 addition, because the bond between Er3＋ and O2- is more strongly eovalently bonded.     

Er3+/Yb3+共掺碲钨酸盐玻璃的热稳定性和1.5μm波段的光谱性质

制备了Er³⁺/Yb³⁺共掺的碲钨酸盐玻璃样品,TeO₂-WO₃-R_mO_n(R_mO_n=PbO,BaO,La₂O₃,Bi₂O₃),研究了样品的热稳定性和1.5μm波段的光谱性质。碲酸盐中引入WO₃的目的是为提高基质的声子能量,使Er³⁺离子⁴I_13/2→⁴I_15/2的多声子弛豫速率增加,从而提高⁴I_13/2能级上的Er³⁺离子数,这对提高1.5μm处的荧光强度有利,另外加入WO₃也能提高碲酸盐玻璃的抗析晶能力。测试了样品的FT-IR光谱,发现碲钨酸盐玻璃样品中存在着TeO₄、TeO₃、WO₄和WO₆结构体。周围环境的不对称性导致Er³⁺在1.5μm处的光谱有非均匀的展宽和大的受激发射截面。Er³⁺在70TeO₂-20WO₃-10Bi₂O₃玻璃中⁴I_13/2→⁴I_15/2能级发射的荧光半峰全宽(FWHM)为77nm,应用McCumber理论计算的受激发射截面(σ^peak)为1.03×10^-20cm²。其FWHM×σ_peak乘积远大于掺Er³⁺的铋酸盐、磷酸盐、碲酸盐和硅酸盐玻璃,说明碲钨酸盐玻璃是一种制备宽带光纤放大器优良基质材料。     

硼酸盐玻璃中Eu掺杂对Ag纳米颗粒的析出机制及其发光性质研究

采用高温熔融法制备了Eu-Ag共掺的硼酸盐玻璃,利用吸收光谱和发射光谱等研究了玻璃中网络形成体B₂O₃含量变化和Eu离子共掺对于Ag在基质中赋存状态的影响。在Eu-Ag共掺玻璃的吸收光谱中发现,随着B₂O₃含量的增加,Ag纳米颗粒在4 10 nm附近的宽带吸收强度逐渐下降;玻璃在340 nm光源激发下,位于350～600 nm的蓝绿光区出现一个Ag分子团簇的宽带发光,且其发光强度随B₂O₃含量的增加逐渐增强。在Eu或Ag单掺的玻璃中可分别观测到微弱的Eu3+或Ag分子团簇的本征发射,而Eu-Ag共掺样品中Eu3+和Ag分子团簇的发光都得到了显著的增强。并且Eu离子浓度的增加促进了Ag纳米颗粒在410 nm附近的宽带吸收。对Eu离子的添加促进Ag纳米颗粒析出的机理进行了讨论。同时,由于Eu3+的5D₀→7F_J的电子跃迁发射为橙红光,Ag纳米团簇可发射蓝绿光甚至黄光,因此通过玻璃结构的调控和Eu离子掺杂浓度的调节可以实现玻璃的白光发射,这有望成为潜在的白光LED用玻璃照明材料。     

EDWA基质玻璃中Er3+的光谱参数计算

对制备的不同掺杂Er3+浓度的硅酸盐玻璃,测定了吸收光谱和荧光光谱.根据玻璃的光谱特性计算了玻璃吸收面积并确定出体系的最佳掺杂Er2O3浓度为0.2左右.根据Judd-Ofelt理论拟合出光谱强度参数Ωλ(λ=2,4,6);结果分析表明:随着Er3+离子浓度的增加,光谱强度参数Ω2在增大,Ω6在减小,说明玻璃的共价性能增强,Er-O共价性增强.     

Broadband near-infrared emission in Er3+-Tm3+ codoped chalcohalide glasses

The near-IR emission spectra of Er3+-Tm3+ codoped 70GeS2-20In2S3-10CsI chalcohalide glasses were studied with an 808 nm laser as an excitation source. A broad emission extending from 1.35 to 1.7 microm with a FWHM of approximately 160 nm was recorded in a 0.1 mol.% Er2S3, 0.5 mol.% Tm2S3 codoped chalcohalide glass. The fluorescence decay curves of glasses were measured by monitoring the emissions of Tm3+ at 1460 nm and Er3+ at 1540 nm, and the lifetimes were obtained from the first-order exponential fit. The luminescence mechanism and the possible energy-transfer processes are discussed with respect to the energy-level diagram of Er3+ and Tm3+ ions.     

Ba2SiO4荧光粉中Ce3+和Eu2+的光谱性质和能量传递

采用高温固相法合成了绿色荧光粉Ba2SiO4:Ce3 ,Eu2 .测量了它们的吸收光谱、激发光谱和发射光谱,观察到了Ba2SiO4中Ce3 对Eu2 发光的敏化现象,发光的敏化作用缘于Ce3 和Eu2 之间的高效无辐射能量传递.     

Er3+和Yb3+共掺碲酸盐玻璃的光谱性质

研究了Er3+ 和Yb3+ 共掺碲酸盐玻璃的吸收和荧光光谱性质 ,分析了碲酸盐玻璃中Er3 + 的上转换发光机制 ,应用Judd Ofelt理论计算了玻璃的强度参量Ωt(t =2 ,4,6 ) ,分别为Ω2 =4.74× 10 - 2 0 cm2 ,Ω4=1.46× 10 - 2 0 cm2 ,Ω6 =0 .6 4× 10 - 2 0 cm2 ,计算了Er3+ 离子的自发跃迁几率、荧光分支比 ,应用McCumber理论计算了受激发射截面 ,并比较了Er3 + 在不同基质玻璃中的光谱特性。     

Effect of Tb3+ concentration on luminescence properties of Ce/Tb/Eu co-doped borosilicate glasses for white LEDs

Ce, Tb and Eu single and ternary doped borosilicate glasses were prepared and effect of Tb³⁺ concentration on luminescence properties of ternary co-doped glasses were analyzed by utilizing emission spectra, excitation spectra, the Commission International de I’Eclairage (CIE) colorimetric system and fluorescence decay curves. The results show that Tb³⁺ concentration significantly affects spectral intensities of ternary co-doped glasses when excited by near ultraviolet (NUV). With the increasing of Tb³⁺ concentration, the blue emission of Ce³⁺ is weakened and the red emission of Eu³⁺ is slightly enhanced. Both the color coordinates and correlated color temperatures (CCTs) can be adjusted by Tb³⁺ concentration. Besides, the energy transfers from Ce³⁺ to Tb³⁺ and from Tb³⁺ to Eu³⁺ were observed. Measured characteristic lifetimes of Tb³⁺ indicate that the energy transfer from Ce³⁺ to Tb³⁺ tends to predominate in whole process. The studies show that Ce/Tb/Eu ternary doped borosilicate glasses might be promising luminescence materials for NUV pumped white LEDs.     

Eu3+掺杂Bi2O3-TeO2-B2O3-ZnO玻璃光谱性质

测量了Eu3+（1 mol%）掺杂(60-χ)Bi2O3-χ TeO2-30B2O3-10ZnO（χ＝5,10,20,30,摩尔百分比）玻璃的吸收光谱、发射光谱、激发光谱以及声子边带谱.根据稀土离子Eu3+光学跃起矩阵元的特点,从发射光谱获得了Eu3+光学跃起的J-O参数Ω2与Ω4.结果显示,强度参量Ω2随着Bi2O3量的增加与TeO2量的减少而减小,表明材料的对称性提高, Eu-O键强减弱,共价性减弱.随着Bi2O3量的增加,电－声子偶合减弱,材料的热稳定性大幅度提高.     

CaO-B2O3-SiO2：Eu^2＋玻璃的合成及荧光光谱分析研究

在还原气氛中合成了CaO-B2O3-SiO2：Eu^2＋玻璃体系,研究了该玻璃体系中Eu^2＋的激发光谱和发射光谱,并归属了其相应的跃迁发射。研究了掺杂Eu^2＋浓度对其发光强度的影响,结果表明,Eu^2＋掺杂量在0.20%时发光强度达到最大值,在该玻璃体系中没有观察到浓度猝灭现象。研究了合成条件与Eu离子在玻璃中发光性质的关系,说明还原能力H2〉CO〉空气,空气几乎不具备还原能力。研究了玻璃中Eu^2＋的电子自旋共振谱（ESR）性质,证实了玻璃体系中Eu^2＋的存在,得到了玻璃体系中Eu^2＋的能级图。     

Tb/Eu 共掺锌硼磷酸盐白光发光玻璃的制备及其发光性能

采用熔体冷却法,通过控制玻璃基质组成及稀土离子添加量,制备了Tb、Eu单掺和Tb/Eu共掺的锌硼磷酸盐低熔点发光玻璃。测试了样品的红外光谱、吸收光谱、激发与发射光谱和荧光寿命,并计算CIE色坐标,研究了材料的微观结构及发光性能。结果表明：样品中部分Eu³⁺被还原为Eu²⁺,在380 nm波长激发下,Tb/Eu共掺发光玻璃同时出现Eu³⁺红光、Tb³⁺绿光和Eu²⁺蓝光的特征发射。增加基体中B₂O₃含量能强化玻璃网络结构,并改变Eu²⁺/Eu³⁺比例。发射光谱和荧光寿命测试表明,共掺的发光玻璃中存在Eu²⁺→Eu³⁺,Eu²⁺→Tb³⁺和Tb³⁺→Eu³⁺的能量传递。改变Tb、Eu的掺杂浓度能够有效改变发光玻璃的发光强度和颜色,最终得到色坐标为（0.318 7,0.286 1）、色温6 480 K的发光玻璃。     

在铕-2-噻吩甲酸-邻菲咯啉三元配合物中La3+对Eu3+的发光影响

合成了七种不同掺杂比例的稀土高氯酸盐(铕掺镧)与2-噻吩甲酸-邻菲咯啉的固态配合物,对配合物进行了元素分析、稀土络合滴定、摩尔电导测定,确定了配合物组成为(Eu1-xLax)·L3·phen·1/2H2O(x=0·000～0·200,L为2-噻吩甲酸,phen为邻菲咯啉),并测定了配体及配合物的IR谱及荧光激发和发射光谱。摩尔电导数据表明,此类配合物为非电解质。红外光谱测定表明,配体2-噻吩甲酸羧基氧与稀土离子配位,配体1,10-邻菲咯啉两个氮原子与稀土离子配位。荧光光谱测定表明,Eu3 处于无反演对称中心格位上,Eu3 配合物发射强度增大。配合物中La3 对Eu3 的发光产生敏化增强效应,当La3 掺入量为0·005mol时敏化强度最大,随着La3 浓度的增大,对Eu3 的发光敏化强度降低。     

Eu/Tm/Tb掺杂硼硅酸盐玻璃的发光性能

采用熔融淬冷法制备了性能优越的Eu/Tm/Tb单掺、双掺和三掺的硼硅酸盐玻璃。测试了样品的激发和发射光谱,计算了CIE色坐标,研究了紫外激发下Eu/Tm/Tb掺杂的硼硅酸盐玻璃的发光性能。结果表明:在361 nm激发下,随着Tm~(3+)加入到Eu_2O_3掺杂的硼硅酸盐样品中,观察到Tm~(3+)的459 nm(1D_2→3F_4)锐线特征发射峰,同时由于Eu~(3+),Eu2+→Tm~(3+)的能量传递的存在降低了Eu2+的437 nm宽带峰及Eu~(3+)的589nm(5D0→7F1)和612 nm(5D_0→7F_2)的特征发射峰强度。在377 nm激发下,Eu/Tm/Tb三掺样品能够同时出现红、绿和蓝光。调节Eu2O3的含量能有效改变发光玻璃的发光强度和颜色,最终得到色坐标为(0.33,0.386 7)的发光玻璃。     

自蔓延高温合成掺杂SrAl2O4稀土长余辉发光粉的研究

在600℃下用自蔓延高温法制备了SrAl2O4∶Eu2+0.012 5,RE3+0.012 5(RE3+=Ce3+,Pr3+,Nd3+,Tb3+,Dy3+),SrAl2O4∶Eu2+0.012 5,M0.012 5(M=Li+,Be2+,Cd2+,Mn2+,Cu2+,Ag+,Zn2+,pb2+),SrAl2O4∶Eu2...     

硼酸盐玻璃中某些稀土离子的浓度效应及其能量传递过程

本文系统地报道了硼酸盐玻璃中Ce3+、Sm33+、Eu3+、Ga3+、Tb3+、Dy3+浓度效应,观察到Eu3+、Gd3+、Tb3+在硼酸盐玻璃中随浓度增加其发光强度增强,而Ce3+、Sm3+、Dy3+当其浓度增加到一定数值后,发光强度反而减弱,初步探讨了不同浓度效应的原因.本文还观察到硼玻璃中某些稀土离子对Eu3+、Tb3+离子发光的敏化作用,及讨论了Gd3+和Eu3+、Tb3+之间的能量传递过程,计算其能量传递的效率和几率.估计了能量传递的规律机理.