Direct copolymerization of sulfonated poly(phthalazinone arylene ether)s for proton‐exchange‐membrane materials

Sulfonated poly(phthalazinone ether ketone) (SPPEK) copolymers and sulfonated poly(phthalazinone ether sulfone) (SPPES) copolymers containing pendant sodium sulfonate groups were prepared by direct copolymerization. The reaction of disodium 3,3′‐disulfonate‐4,4′‐difluorobenzophenone (SDFB‐Na), 4,4′‐difluorobenzophenone (DFB), and 4‐(4‐hydroxyphenyl)‐1(2H)‐phthalazinone (DHPZ) at 170 °C in N‐methyl‐2‐pyrrolidione containing anhydrous potassium carbonate gave SPPEKs. SPPESs were similarly obtained with 3,3′‐disulfonate‐4,4′‐difluorophenyl sulfone, 4‐fluorophenyl sulfone (DFS), and DHPZ as monomers. The sulfonic acid groups, being on deactivated positions of the polymer backbone, were expected to be hydrolytically more stable than postsulfonated polymers. Fourier transform infrared and ¹H NMR were used to characterize the structures and degrees of sulfonation of the sulfonated polymers. Membrane films of SPPEKs with SDFB‐Na/DFB molar feed ratios of up to 60/40 and SPPESs with sulfonated 4‐fluorophenyl sulfone/DFS molar feed ratios of up to 50/50 were cast from N,N‐dimethylacetamide polymer solutions. Membrane films in acid form were then obtained by the treatment of the sodium‐form membrane films in 2 N sulfuric acid at room temperature. An increase in the number of sulfonate groups in the copolymers resulted in an increased glass‐transition temperature and enhanced membrane hydrophilicity. The sodium‐form copolymers were thermally more stable than their acid forms. The proton conductivities of the acid‐form copolymers with sulfonated monomer/unsulfonated monomer molar feed ratios of 0.5 and 0.6 were higher than 10^?2 S/cm and increased with temperature; they were less temperature‐dependent than those of the postsulfonated products. SPPESH‐50 showed higher conductivity than the corresponding postsulfonated poly(phthalazinone ether sulfone). © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2731–2742, 2003     

Synthesis and properties of multiblock copoly(arylene ether)s containing superacid groups for fuel cell membranes

A series of block copoly(arylene ether)s containing pendant superacid groups were synthesized, and their properties were investigated for fuel cell applications. Two series of telechelic oligomers, iodo‐substituted oligo(arylene ether ketone)s and oligo(arylene ether sulfone)s, were synthesized. The degree of oligomerization and the end groups were controlled by changing the feed ratio of the monomers. The nucleophilic substitution polymerization of the two oligomers provided iodo‐substituted precursor block copolymers. The iodo groups were converted to perfluorosulfonic acid groups via the Ullmann coupling reaction. The high degree of perfluorosulfonation (up to 83%) was achieved by optimizing the reaction conditions. Tough and bendable membranes were prepared by solution casting. The ionomer membranes exhibited characteristic hydrophilic/hydrophobic phase separation with large hydrophilic clusters (ca. 10 nm), which were different from that of our previous random copolymers with similar molecular structure. The block copolymer structure was found to be effective in improving the proton‐conducting behavior of the superacid‐modified poly(arylene ether) ionomer membranes without increasing the ion exchange capacity (IEC). The highest proton conductivity was 0.13 S/cm at 80 °C, 90% relative humidity, for the block copolymer ionomer membrane with IEC = 1.29 mequiv/g. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Synthesis and characterization of multiblock partially fluorinated hydrophobic poly(arylene ether sulfone)‐hydrophilic disulfonated poly(arylene ether sulfone) copolymers for proton exchange membranes

Hydrophobic‐hydrophilic sequence multiblock copolymers, based on alternating segments of phenoxide terminated fully disulfonated poly(arylene ether sulfone) (BPS100) and fluorine‐terminated poly(arylene ether sulfone) (6FBPS0) were synthesized and evaluated for application as proton exchange membranes. By utilizing mild reaction conditions the ether–ether interchange reactions were minimized, preventing the randomization of the multiblock copolymers. Tough, ductile, transparent membranes were solution cast from the block copolymers and were characterized with regard to intrinsic viscosity, morphology, water uptake, and proton conductivity. The conductivity values of the 6FBPS0‐BPSH100 membranes were compared to Nafion 212 and a partially fluorinated sulfonated poly(arylene ether sulfone) random copolymer (6F40BP60). The nanophase separated morphology was confirmed by transmission electron microscopy and small angle X‐ray scattering, and enhanced proton conductivity at reduced relative humidity was observed with longer block lengths. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Performance assessment of hybrid multiblock copolymers included with ionic liquid for fuel cell applications

To improve the proton conductivity and thermal stability of proton exchange membrane, hybrid poly (arylene ether) multiblock copolymers were synthesized by using 6F-bisphenol A monomer. The hydrophobic oligomers poly (arylene ether sulfone) containing 6F-bisphenol A with varying molecular weight were copolymerised with hydrophilic oligomer disulfonated poly (arylene ether ketone) containing pendant carboxylic acid group to prepare multiblock copolymers. For further enhancing the proton conductivity, ionic liquid is embedded into the synthesized multiblock copolymers to fabricate the hybrid multiblock membranes. The ¹H NMR studies confirmed the synthesis of oligomers and multiblock copolymers whereas the FT-IR spectra revealed the interaction of ionic liquid with the multiblock copolymers. The proton conductivity of the membranes has also been examined at different temperatures and the activation energy required for the proton transport was calculated by using Arrhenius equation. At 30 °C, the maximum proton conductivity of 0.14 S/cm were shown by hybrid membrane (with 50% ionic liquid, 6FB1/I.L-50%), which is of 3.5 times greater than that of pristine 6FB1 membrane. Compared with pristine membranes, the hybrid membranes exhibit improved oxidative, thermal and mechanical stability. Moreover, the scanning electron microscopy (SEM) investigation depicts better phase separation in hybrid membranes than pristine membranes by forming ionic clusters. The membranes have been tested in H₂/O₂ fuel cell and their performance is compared with the state-of-art Nafion 117 membrane.     

Novel thin-film composite membranes with improved water flux from sulfonated cardo poly(arylene ether sulfone) bearing pendant amino groups

A new class of polymeric amine, namely, sulfonated cardo poly(arylene ether sulfone) (SPES-NH₂) was synthesized and used for the preparation of thin-film composite membrane. The TFC membranes were prepared on a polysulfone supporting film through interfacial polymerization with trimesoyl chloride (TMC) solutions and amine solutions containing SPES-NH₂ and m-phenylenediamine (MPDA). The resultant membranes were characterized with water permeation performance, chemical structure, hydrophilicity of active layer and membrane morphology including top surface and cross-section. The membrane prepared under the optimum condition showed the salt rejection and water flux reached 97.3% and 51.2 L/m² h, respectively. The high salt rejection and water flux was attributed to the rigid polymer backbone and the presence of strong hydrophilic sulfonic groups.     

Synthesis and structure–property relationships of poly(sulfone)s for anion exchange membranes

Membranes based on cationic polymers that conduct anions are important for enabling alkaline membrane fuel cells and other solid-state electrochemical devices that operate at high pH. Anion exchange membranes with poly(arylene ether sulfone) backbones are demonstrated by two routes: chloromethylation of commercially available poly(sulfone)s or radical bromination of benzylmethyl moieties in poly(sulfone)s containing tetramethylbisphenol A monomer residues. Polymers with tethered trimethylbenzyl ammonium moieties resulted from conversion of the halomethyl groups by quaternization with trimethyl amine. The water uptake of the chloromethylated polymers was dependent on the type of poly(sulfone) backbone for a given IEC. Bisphenol A-based Udel® poly(sulfone) membranes swelled in water to a large extent while membranes from biphenol-based Radel® poly(sulfone), a stiffer backbone than Udel, only showed moderate water uptake. The water uptake of cationic poly(sulfone)s was further reduced by synthesizing tetramethylbisphenol A and 4,4′-biphenol-containing poly(sulfone) copolymers where the ionic groups were clustered on the tetramethylbisphenol A residues. The conductivity of all samples scaled with the bulk water uptake. The hydration number of the membranes could be increased by casting membranes from the ionic form polymers versus converting the halomethyl form cast polymers to ionic form in the solid state. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2013, 51, 1790–1798, 2013     

Synthesis and characterization of partially disulfonated hydroquinone‐based poly(arylene ether sulfone)s random copolymers for application as proton exchange membranes

Partially disulfonated hydroquinone (HQ)‐based poly(arylene ether sulfone) random copolymers were synthesized and characterized for application as proton exchange membranes. The copolymer composition was varied in the degree of disulfonation. The copolymers were characterized by ¹H NMR, Differential Scanning Calorimetry (DSC), and other analytical techniques. The copolymer with a 25% degree of disulfonation showed the best balance between water uptake and proton conductivity. The copolymers showed substantially reduced methanol permeability compared with Nafion® and satisfactory direct methanol fuel cell performance. The methanol selectivity improved significantly in comparison to Nafion® 117. At a given ionic composition, the HQ‐based system showed higher water uptake and proton conductivity than the biphenol‐based (BPSH‐xx) poly(arylene ether sulfone)s copolymers. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 384–391, 2009     

Segmented sulfonated poly(arylene ether sulfone)‐b‐polyimide copolymers for proton exchange membrane fuel cells. I. Copolymer synthesis and fundamental properties

Segmented disulfonated poly(arylene ether sulfone)‐b‐polyimide copolymers based on hydrophilic and hydrophobic oligomers were synthesized and evaluated for use as proton exchange membranes (PEMs). Amine terminated sulfonated poly (arylene ether sulfone) hydrophilic oligomers and anhydride terminated naphthalene based polyimide hydrophobic oligomers were synthesized via step growth polymerization including high temperature one‐pot imidization. Synthesis of the multiblock copolymers was achieved by an imidization coupling reaction of hydrophilic and hydrophobic oligomers oligomers in a m‐cresol/NMP mixed solvent system, producing high molecular weight tough and ductile membranes. Proton conductivities and water uptake increased with increasing ion exchange capacities (IECs) of the copolymers as expected. The morphologies of the multiblock copolymers were investigated by tapping mode atomic force microscopy (TM‐AFM) and their measurements revealed that the multiblock copolymers had well‐defined nano‐phase separated morphologies which were clearly a function of block lengths. Hydrolytic stability test at 80 °C water for 1000 h showed that multiblock copolymer membranes retained intrinsic viscosities of about 80% of the original values and maintained flexibility which was much improved over polyimide random copolymers. The synthesis and fundamental properties of the multiblock copolymers are reported here and the systematic fuel cell properties will be provided in a separate article. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 4879–4890, 2007     

Thermostable ultrafiltration and nanofiltration membranes from sulfonated poly(phthalazinone ether sulfone ketone)

Modification of poly(phthalazinone ether sulfone ketone) (PPESK) by sulfonation with concentrated or fuming sulfuric acid was carried out in order to prepare thermally stable polymers as membrane materials having increased hydrophilicity and potentially improved fouling-resistance. The sulfonated poly(phthalazinone ether sulfone ketone)s (SPPESK) were fabricated into ultrafiltration (UF) and nanofiltration (NF) asymmetric membranes. The effects of SPPESK concentration and the type and concentration of additives in the casting solution on membrane permeation flux and rejection were evaluated by using an orthogonal array experimental design in the separation of polyethyleneglycol (PEG12000 and PEG2000) and Clayton Yellow (CY, MW 695). One UF membrane formulation type had a 98% rejection rate for PEG12000 and a high pure water flux of 867 kg m⁻² h⁻¹. All the NF membranes made in the present study had rejections of ≥96%, and one had a high water flux of 160 kg m⁻² h⁻¹. Several of the NF membrane formulation types had ∼90% rejection for CY. When the membranes were operated at higher temperatures (80°C), the rejection rates declined slightly and pure water flux was increased more than two-fold. Rejection and flux values returned to previous values when the membranes were operated at room temperature again. Mono- and divalent salt rejections and fluxes were studied on an additional NF membrane set.     

Influence of chemical composition and sequence length on the transport properties of proton exchange membranes

One of the integral parts of the fuel cell is the proton exchange membrane. Our research group has been engaged in the past few years in the synthesis of several sulfonated poly(arylene ether) random copolymers. The copolymers were varied in both the bisphenol structure as well as in the functional groups in the backbone such as sulfone and ketones. To compare the effect of sequence length, multiblock copolymers based on poly(arylene ether sulfone)s were synthesized. This paper aims to describe our investigation of the effect of chemical composition, morphology, and ion exchange capacity (IEC) on the transport properties of proton conducting membranes. The key properties examined were proton conductivity, methanol permeability, and water self diffusion coefficient in the membranes. It was observed that under fully hydrated conditions, proton conductivity for both random and block copolymers was a function of IEC and water uptake. However, under partially hydrated conditions, the block copolymers showed improved proton conductivity over the random copolymers. The proton conductivity for the block copolymer series was found to increase with increasing block lengths under partially hydrated conditions. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 2226–2239, 2006     

Understanding properties of copoly(arylene ether nitrile)s high-performance polymer electrolyte membranes for fuel cells from molecular dynamics simulations

Sulfonated poly(arylene ether ether nitrile) (m-SPAEEN) copolymers are reported to have the property of reduced water uptake compared with other hydrocarbon membranes, such as sulfonated polysulfones or polyketones, with similar ion exchange capacity. It is believed that this difference is largely due to the nitrile group. In this study, to investigate the effect of the nitrile group on properties of polymer electrolyte membranes for fuel cell applications, we carried out a series of molecular dynamics (MD) simulations. We compared the results of MD simulations for m-SPAEEN and sulfonated poly(arylene ether sulfone)s (BPSH). We found that water molecules hydrate not only the sulfonate (SO₃ ^?) groups of m-SPAEEN but also other hydrophilic functional groups in the copolymers. Results showed that hydration around the nitrile group in m-SPAEEN and around the sulfone (SO₂) group in BPSH differs in features related to water uptake: The former exhibits uptake of fewer water molecules than does the latter. This difference in hydration features causes m-SPAEEN to have a relatively low water-uptake level compared with BPSH.     

Co‐poly(aryl ether sulfone)s containing phthalimidine moiety in the main chain

Several new co‐poly(arylene ether sulfone)s have been prepared by the reaction of 4,4′‐fluorodiphenyl sulfone (FDS) with different bisphenols namely 4,4′‐isopropylidenediphenol (BPA), 4,4′‐hexafluoroisopropylidenediphenol (6F‐BPA), and N‐phenyl‐3,3‐bis(4‐hydroxyphenyl)phthalimidine(PA). The homo‐poly(arylene ether sulfone)s are named as 1a, 2a, and 3a. The copolymers namely 2b, 2c, 2d and 3b, 3c, 3d have been prepared, respectively, on reaction of FDS with BPA or 6F‐BPA using different molar ratios of PA such as 25, 50, and 75. The poly(aryl ether sulfone)s 1a containing PA unit in the main chain showed a very high glass transition temperature of 280°C and an outstanding thermal stability up to 510°C for 5% weight loss under synthetic air. Depending on the mole% of PA, the glass transition temperatures of the copolymers can be varied. The polymers were soluble in a wide range of organic solvents. Transparent thin films of these polymers exhibited tensile strengths upto 84 MPa and Young's modulus up to 3.16 GPa. The films of these polymers showed low water absorption of 0.24%. Copyright © 2009 John Wiley & Sons, Ltd.     

Amphiphilic PPESK-g-PEG graft copolymers for hydrophilic modification of PPESK microporous membranes

Amphiphilic graft copolymers comprising poly(phthalazinone ether sulfone ketone) (PPESK) backbones and poly(ethylene glycol) (PEG) side chains were synthesized and blended into PPESK casting solutions to prepare hydrophilic and anti-fouling microporous membranes. The graft copolymer was prepared by a modified Williamson etherification method. Sodium alkoxide of methoxyl PEG (PEG-ONa) was used to react with chloromethylated PPESK (CMPPESK). FT-IR spectroscopy, ¹H NMR and solid-state ¹³C CP-MAS NMR analysis confirmed the covalent linking of PEG with PPESK backbones. The incorporation ratio of PEG calculated from ¹H NMR was in agreement with that from TGA tests. The graft products were added into PPESK casting solutions to prepare composite porous membranes using phase inversion method. X-ray photoelectron spectroscopy (XPS) and water contact angle examinations indicated that the grafting copolymers were preferentially excluded to the membrane-coagulant interface during membrane forming, contributing the membranes with improved hydrophilicity and surface wettability. Compared with the neat membrane, the blend membranes exhibited a larger surface pore size and less susceptible to protein fouling.     

Synthesis and characterization of multiblock copolymers based on hydrophilic disulfonated poly(arylene ether sulfone) and hydrophobic partially fluorinated poly(arylene ether ketone) for fuel cell applications

Sulfonated fluorinated multiblock copolymers based on high performance polymers were synthesized and evaluated for use as proton exchange membranes (PEMs). The multiblock copolymers consist of fully disulfonated poly(arylene ether sulfone) and partially fluorinated poly(arylene ether ketone) as hydrophilic and hydrophobic segments, respectively. Synthesis of the multiblock copolymers was achieved by a condensation coupling reaction between controlled molecular weight hydrophilic and hydrophobic oligomers. The coupling reaction could be conducted at relatively low temperatures (e.g., 105 °C) by utilizing highly reactive hexafluorobenzene (HFB) as a linkage group. The low coupling reaction temperature could prevent a possible trans‐etherification, which can randomize the hydrophilic‐hydrophobic sequences. Tough ductile membranes were prepared by solution casting and their membrane properties were evaluated. With similar ion exchange capacities (IECs), proton conductivity and water uptake were strongly influenced by the hydrophilic and hydrophobic block sequence lengths. Conductivity and water uptake increased with increasing block length by developing nanophase separated morphologies. Atomic force microscopy (AFM) and transmission electron microscopy (TEM) experiments revealed that the connectivity of the hydrophilic segments was enhanced by increasing the block length. The systematic synthesis and characterization of the copolymers are reported. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 214–222, 2010     

含蒽醌结构聚芳醚砜的合成及表征

以4,4'-二氟二苯砜,4,4'-联苯二酚及1,5-二氯蒽醌为原料,采用亲核缩聚方法将具有良好热稳定性的蒽醌生色团分子以共价键方式引入到聚芳醚砜体系中,制备出了蒽醌含量分别为10%、20%及30%的热分解温度在500℃以上的新型耐高温有机高分子染料.该系列聚合物具有较高的分子量和良好的溶解性.利用红外光谱(FTIR)、核磁共振(1H-NMR)等表征方法确定了聚合物的结构;利用紫外-可见光谱测试(UV-Vis)初步研究了聚合物的光谱学特性;利用差示扫描量热测试(DSC)和热失重分析测试(TGA)研究了聚合物的热性能.     

Photochemical modification of 10 kDa polyethersulfone ultrafiltration membranes for reduction of biofouling

Poly(ether sulfone) 10 kDa ultrafiltration membranes were modified by photolysis using ultraviolet light and graft polymerization of hydrophilic monomers onto the membrane surface to create more hydrophilic and lower fouling membrane surfaces. The modified membrane surfaces were characterized by FTIR/ATR and captive bubble contact angle measurements to determine chemical and hydrophilicity changes during modification. The modified membranes were compared with an unmodified poly(ether sulfone) (control) membrane as well as a commercial regenerated cellulose and a low protein adsorbing poly(ether sulfone) membrane using a newly developed standardized filtration protocol with 1 wt% bovine serum albumin. The best performing modified membrane was with N-vinyl-2-pyrrolidinone and showed a 25% increase in hydrophilicity, a 49% decrease in bovine serum albumin fouling, and a 4% increase in bovine serum albumin retention compared to the unmodified poly(ether sulfone) membrane. While the regenerated cellulose membrane had the lowest fouling and the low protein adsorbing membrane had the highest flux of all tested membranes, the N-vinyl-2-pyrrolidinone-modified membranes had the best combination of low fouling and high flux.     

Linear and Hyperbranched Poly(arylene ether)s from a New Semifluorinated AB Monomer

A new trifluoromethyl-activated AB monomer has been successfully synthesized by Pd-initiated coupling of 4-bromo anisole with 4-fluoro-3-trifluoromethylphenylboronic acid followed by demethylation. The monomer leads to a semifluorinated poly(arylene ether) by nucleophilic displacement polymerization reaction. The AB monomer has been further copolymerized with a corresponding AB ₂ monomer to form the corresponding semifluorinated hyperbranched (hb) poly(arylene ether). The resulting linear and hb poly(arylene ether)s exhibited weight average molecular weight of 75700 and 144100 g/mol, respectively. The hb copolymer exhibited better solubility in different organic solvents compared to the linear poly(arylene ether). The polymers showed excellent thermal stability up to 522°C at 10% wt loss in air and glass transition temperatures as high as 187°C. The mechanical properties of the linear poly(arylene ether) film 1a exhibited tensile strength at break of 89 MPa, elongation at break of up to 3% and a Young’s modulus value of 2.66 GPa. The films of the polymers were hydrophobic in nature and showed water contact angle as high as 93.6°.     

Synthesis and Properties of Novel Side‐Chain Sulfonated Poly(Arylene Ether Sulfone)s for Proton Exchange Membranes

A series of novel side‐chain sulfonated poly(arylene ether sulfone) (SPAES) multiblock and random copolymers were synthesized by condensation polymerization from a new disulfonated aryl sulfone monomer, 4,4′‐difluoro‐2,2′‐bis(3‐sulfobenzoyl)diphenyl sulfone disodium salt (DFBSPS). The chemical structures of DFBSPS and the SPAESs were characterized by proton nuclear magnetic resonance (¹H NMR) and Fourier transform infrared (FTIR) spectra. The SPAES membranes prepared by solution cast method exhibited high tensile strength (50–71 MPa) and high radical oxidative stability. They could keep their morphology and maintain proton conductivities after hydrolysis test in 95 °C water for 1000 h. They also showed smaller swelling ratio in in‐plane direction than in through‐plane direction and such an anisotropic effect was more significant for the multiblock copolymers than for the random ones. The multiblock copolymer membranes exhibited higher proton conductivity than the random ones with similar ion exchange capacities (IECs). Preliminary hydrogen‐oxygen fuel cell tests were performed at 60 °C and 80% relative humidity (RH). The results showed that the single cell equipped with the multibiock copolymer membrane SB3 exhibited 0.12 W cm^?2 higher maximum output power density than the one equipped with the random copolymer membrane SR3 (with the same IEC), indicating much better performance of the former. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 2304–2313     

SYNTHESIS OF AN AMPHIPHILIC PPESK-g-P(PEGMA) GRAFT COPOLYMER VIA ATRP AND ITS USE IN BLEND MODIFICATION OF PPESK MEMBRANES

Preparation of an amphiphilic graft copolymer having poly(phthalazinone ether sulfone ketone)(PPESK) as main chains was carried out by atom transfer radical polymerization(ATRP).The precursor,chloromethylated PPESK (CMPPESK),was prepared by using chioromethylether as chloromethylation agent.Then,poly(ethylene glycol) methyl ether methacrylate(PEGMA) was used as monomer to synthesize PPESK-g-P(PEGMA) by ATRP method under the catalysis of a cuprous chloride/2,2'-bipyridyl system.PPESK/PPESK-g-P(PEGMA) blen...     

Syntheses and Surface Properties of Polyacrylonitrile-based Copolymer Membranes Containing Sugar Moieties

Introduction Asatypeofwidelyusedmembranematerials, polyacrylonitrile(PAN)hasbeeninvestigatedby manyresearchersinthefieldsofpervaporation,ul- trafiltration,anddialysis[1_4].However,PAN- basedmembranesarerelativelyhydrophobicwitha lowbiocompatibility.Thesepropertieslimittheir furtherapplicationsinaqueoussolutionseparation andtheirusageasbiomedicaldevices.Muchatten- tionhasbeenpaidtoimprovingthecharacteristics ofPAN-basedmembranes.Thecopolymerization ofANwithhydrophilicmonomersisconsideredas…