Temperature-programmed desorption of n-hexane from hydrated HZSM-5 and NH4ZSM-5 zeolites

Temperature-programmed desorption coupled with mass spectrometer as a detector (TPD), IR and ¹³C NMR measurements are used to study the adsorption of n-hexane on hydrated HZSM-5 and NH₄ZSM-5 zeolites. The ¹³C NMR measurements show that n-hexane can access the pore structure of ZSM-5 zeolites previously saturated with water. TPD spectra of n-hexane are monitored in the temperature region 50–300°C, in the case of fully or partially hydrated samples; two-stage desorption of n-hexane is found. Simultaneous desorption of water and n-hexane in the same temperature region are found, in all investigated samples.     

Na_2CO_3溶液处理对Ni-Mo/HZSM-5分子筛硫醚化催化性能的影响

采用Na2CO3溶液对ZSM-5分子筛进行碱处理,考察了处理温度和处理时间对ZSM-5分子筛结构特征和物化性能的影响。利用XRD、N2吸附-脱附、XRF、SEM及NH3-TPD表征对处理前后样品进行分析。以正丁硫醇和异戊二烯组成的模型化合物为原料,对碱处理后含微-介孔HZSM-5分子筛制得的Ni-Mo/HZSM-5催化剂进行硫醚化活性评价。结果表明,Na2CO3溶液处理没有破坏原分子筛晶体形貌,保持微孔结构的同时,适当的提高处理温度和延长处理时间有利于ZSM-5分子筛比表面积、外比表面积、介孔孔容和平均孔径的增大,并调节了酸性质。但过长的处理时间并不利于介孔的生成和酸性的调变。经90℃的Na2CO3溶液处理5 h得到催化剂表现较高硫醚化活性,正丁硫醇和异戊二烯转化率分别可达92.36%和97.33%。由此,Na2CO3溶液处理可提高催化剂硫醚化活性,且改性过程温和可控。     

MoCI_5在HZSM-5和APO-5上的负载及调变作用

MoCl_5在HZSM-5和APO-5上没有发生“双聚”,沸石的酸性对MoCl_5负载量的影响大于孔结构。APO-5负载MoCl_5后,仅生成数量和强度都很小的B酸中心。Mo-ZSM-5沸石在MTG反应中有Mo和Al的表面迁移,负载的MoCl_5通过氧化-还原及水解等过程产生羟基,增加了ZSM-5沸石的B酸量,通过B酸-L酸中心的电子协同效应增加载体的B酸强度,调变了催化剂的酸性分布。     

多级孔ZSM-5分子筛的合成及其在甲醇脱水制二甲醚反应中的应用

以四丙基氨为微孔模版剂,阳离子高分子聚合物为介孔模版剂,合成了具有多级介孔的ZSM-5分子筛,并用于甲醇气相脱水合成二甲醚.结果表明,加入阳离子高分子聚合物后,合成的HZSM-5分子筛样品既保持了其MFI典型结构,又呈现了多级介孔特征;随着阳离子高分子聚合物模板剂加入量的增加,其多级介孔特征更为明显.具有多级介孔的HZSM-5分子筛表现出比常规微孔HZSM-5分子筛高的反应稳定性和二甲醚选择性,这主要是由于其织构和酸性的双重作用.     

含锆ZSM-5分子筛上丙烯齐聚反应的研究

以正丁胺(NBA)为模板剂，通过水热法直接合成了Zr/ZSM-5分子筛。XRD分析表明Zr/ZSM-5分子筛结晶度良好，但衍射峰的强度稍有差别。SEM显示样品分子筛表面规整，为3 μm～5 μm的棒状晶体。采用NH3-TPD法对分子筛进行了酸性测试，结果表明，在锆质量分数0.2%～1.2%，分子筛的中强酸和强酸量随锆质量分数的增加而增大，并向高温方向偏移。丙烯齐聚催化反应的活性评价结果显示，中强酸和强酸的量对Zr/HZSM-5催化性能有显著影响，在反应过程中对链的增长起促进作用。     

Microwave synthesis,characterization and catalytic properties of titanium-incorporated ZSM-5 zeolite

Titanium-incorporated ZSM-5 zeolites (Si/Al = 50–200 and Si/Ti = 70) were successfully synthesized in a one-step sol-gel process under microwave irradiation. The characteristics of Ti-ZSM-5 zeolites were investigated using X-ray power diffraction, UV/Vis-DRS, FT-IR spectroscopy and solid-state ²⁷Al-NMR to monitor the physico-chemical properties. Simultaneously, the acidic properties were characterized by the NH₃-TPD profile. The characterization results revealed that the Ti⁴⁺ and Al³⁺ ions were well incorporated into the framework of Ti-ZSM-5 zeolite. The prepared zeolite was moderately active but selective in the dehydration of methanol to dimethyl ether.     

低硅铝比ZSM-5分子筛的合成及其正庚烷裂化反应性能

以氨水为矿化剂,通过添加NH₄⁺离子水热合成了具有较低骨架硅铝比的ZSM-5分子筛。通过X射线衍射(XRD)、扫描电镜(SEM)、固体核磁共振(MAS-NMR)等表征手段,研究了硅源、铝源、矿化剂、阳离子等对ZSM-5分子筛的结晶度、形貌尺寸和骨架硅铝比等的影响,研究了ZSM-5分子筛的骨架硅铝比对正庚烷催化裂化反应的影响。研究表明,投料硅铝比越低,铝原子越难进入到分子筛骨架中;当氨水为矿化剂、正硅酸四乙酯为硅源时可以合成骨架硅铝比较低的氢型ZSM-5分子筛,添加NH₄⁺离子可以增强骨架铝的嵌入,进一步降低分子筛的骨架硅铝比(24.2)。正庚烷裂化反应结果表明,降低分子筛的骨架硅铝比可以提高正庚烷裂化反应的活性,但会降低低碳烯烃的选择性。     

Thermal and hydrothermal stabilities of the alkali-treated HZSM-5 zeolites

HZSM-5 zeolites with the micro-mesopore hierarchical porosity have been prepared by the post-synthesis of alkali-treatment, and their thermal and hydrothermal stabilities were studied using DTA, XRD, and NH3-TPD characterization techniques. Compared to the unmodified zeolite, the thermal and hydrothermal stabilities of the alkali-treated ZSM-5 zeolites were slightly deteriorated because of the introduction of mesopores caused by the desilication. Nevertheless, the alkali-treated zeolite framework could be maintained until the temperature increased to 1175 ℃.     

纳米薄层HZSM-5分子筛催化甲醇制丙烯

在合成系列硅铝比纳米薄层HZSM-5分子筛的基础上,研究了纳米薄层HZSM-5分子筛催化甲醇制丙烯(MTP)的反应性能.在固定床微反装置上详细考察了工艺条件对纳米薄层HZSM-5分子筛催化性能的影响,同时与纳米HZSM-5分子筛对MTP反应的催化性能进行了比较.结果表明,纳米薄层HZSM-5分子筛具有较高的目的产物选择性和较长的催化寿命.在适宜硅铝比(n(SiO2)/n(Al2O3)=213)和反应条件下(温度470°C,甲醇质量空速为3 h-1),丙烯的选择性达到46.7%,三烯(乙烯、丙烯和C4烯烃)选择性达到78.7%.其中,丙烯/乙烯的质量比可达到6.5,是纳米HZSM-5分子筛的2倍,而芳烃的选择性比纳米分子筛明显降低.这是因为纳米薄层HZSM-5分子筛比纳米HZSM-5分子筛具有较宽的(010)晶面、较大的外比表面积和介孔孔容.     

Developments and structures of mesopores in alkaline-treated ZSM-5 zeolites

ZSM-5 zeolites with SiO₂/Al₂O₃ molar ratio of 24 were treated in 0.05 M aqueous sodium hydroxide solution at 325 K in different periods. The samples were characterized by means of nitrogen adsorption at 77 K, field emission scanning electron microscopy, X-ray diffractometry, and Fourier transform infrared spectroscopy. Analysis of the experimental results showed that the alkaline treatment periods have influence on the developments and structures of mesopores in the alkaline-treated ZSM-5 zeolites. Alkaline treatment initially develops mesopores mainly from the boundary portion of MFI zeolites to the bulk, while prolonged treatment destroys the mesopores, and an optimum mesoporosity is obtained by the treatment for 1.5 h. On the other hand, crystallinities and short-range order in alkaline treated zeolites have remained virtually unchanged according to the examination from X-ray diffractometry and Fourier transform infrared spectroscopy.     

氟改性对纳米 HZSM-5 分子筛催化甲醇制丙烯的影响

 在比较了纳米和微米 HZSM-5 分子筛催化甲醇制丙烯反应性能的基础上, 对纳米 HZSM-5 分子筛进行了氟改性. 利用透射电镜、N2 吸附、X 射线衍射、氨程序升温脱附和吡啶吸附-红外光谱技术对改性前后的样品进行了表征, 并在常压、500 oC 和甲醇空速 (WHSV) 为 1.0 h–1 的反应条件下, 在连续流动固定床微型反应器上考察了其催化甲醇制丙烯的性能. 结果表明, 当氟含量<10% 时, 随氟含量的增加, 改性纳米 HZSM-5 分子筛的酸量减少, 酸强度降低, 从而使丙烯选择性和催化剂稳定性不断提高. 但过量 (15%) 氟的改性使纳米 HZSM-5 分子筛的酸量、比表面积和孔容均明显减小, 致使其稳定性反而降低. 在适量 (10%) 氟改性的纳米 HZSM-5 分子筛上, 丙烯选择性和维持甲醇完全转化的反应时间分别由原来的 30.1% 和 75 h 增加到 46.7% 和 145 h.     

Crystallization of ZSM-12 Zeolite with Different Si/Al Ratio

In this work the acid properties of a series of HZSM-12 zeolites with different Si/Al ratio were studied. The ZSM-12 crystals were synthesized by the hydrothermal method starting from a gel with the following molar composition: 20MTEA:10Na₂O:x Al₂O₃:100SiO₂:2000H₂O, with x = 0.50, 0.67, 1, 1.25 and 2, respectively. The gels were crystallized at 140^∘C for 6 days, then washed, dried and calcined to remove the MTEA template. The samples were ion-exchanged with an ammonium chloride solution and calcined again to obtain the zeolites in the acid form. The materials thus obtained were characterized by XRD, SEM, BET, TG and n-butylamine adsorption. The Si/Al ratio in the reaction mixture affects the amount of zeolite produced and the size of the particles. The XRD analysis indicated that the ZSM-12 zeolite crystallizes in a pure form only with Si/Al ratio above 33. The SEM analysis showed the presence of crystallites with very well defined prismatic shapes. The removal of the MTEA of the pores of the ZSM-12 by TG indicated that there are two kinds of internal sites occupied by MTEA inside the structure. The BET area of the ZSM-12 decreases proportionally with the crystallinity of materials. The desorption of n-butylamine showed that the acid site density is proportional to aluminum content, but the Si/Al ratio shows little influence on the relative strengths of these sites.     

分子筛催化剂的失活与积炭

分子筛催化剂的失活与积炭刘中民，陈国权，王清遐，梁娟，蔡光宇（中国科学院大连化学物理研究所，大连１１６０２３）关键词分子筛，结炭，催化剂失活，甲醇转化，ＨＺＳＭ－５结炭是酸性分子筛催化剂失活的主要因素．本文通过具有碳链增长、环化、烷基化等多种反应途径...     

ZSM-5分子筛上烷基化过程中“反向效应”的产生及其克制方法

在综述甲苯择形烷基化机理并分析产生“反效应”的原因的基础上,提出了克制的“反向效应”的设想。Ｓｂ２Ｏ３,ＴｉＣｌ４,ＳｉＣｌ４,Ｈ３ＰＯ４,Ｍｇ（Ａｃ）２等化合物对分子筛进行改性,测定改性前后分子筛的表面酸性与孔结构,关联乙基化反应结果,证实中强酸中心在乙基化反应中的重要作用,认为保持孔道的畅通是解决“反应效应”的关键。并采用了Ｋ－Ｍｇ改性,制备出对甲苯乙基化具有高初活性和高对位选择性的催化剂。     

LaHZSM—5沸石的制备及其裂解性能研究

用常压和水热法制备了具有不同交换度的LaHZSM-5沸石,以XPS、IR、XRD及正十五烷裂解对其进行了表征。结果表明,水热法可获得较高交换度的LaHZSM-5沸石。La~(3+)交换的沸石较相同Si/Al比的HZSM-5沸石活性高,对气体的选择性降低,提高了C_(5～10)馏分的选择性。     

ROLE OF Ga AND Pt-Ga IN THE CONVERSION OF PROPANE OVER Ga/HZSM-5 AND Pt-Ga/HZSM-5

为获得较高的Ｃ２选择性，在加水（水蒸气）条件下，研究了添加ＣａＯ对甲烷氧化偶联Ｌａ２Ｏ３催化剂的影响。发现ＣａＯ的添加提高了Ｌａ２Ｏ３催化剂的活性，同时水的添加明显地提高了催化剂的Ｃ２选择性。在加水条件下，Ｌａ２Ｏ３－ＣａＯ催化剂获得了较好的结果，其ＣＨ４转换率为２０％，Ｃ２选择性超过８０％。利用ＸＲＤ和ＸＰＳ技术对催化剂进行了表征，并对加水和不加水条件下的催化剂性能与结构变化的关系进行了讨论     

EFFECT OF SULFURIZATION ON THE PIIYSICAL ANDCATALYTIC PROPERTIES OF HZSM-5 ZEOLITES

IntroductionZSM-5zeoliteshavebeenwidelyemployedinthefieldofhydrocarbonconversion.UtiliZationofMo-containingandKorBamodifiedZSM-5zeolitestOactivatemethaneandtOpreparelightolefinsfromparaffinshavebeenreportedinourpreviouspapersll'2].However,littleattentionh…     

Acid properties of the HZSM-12 zeolite with different Si/Al ratio by thermo-programmed desorption

In this work was studied the acid properties of a series of HZSM-12 zeolites with different Si/Al molar ratio. The samples of ZSM-12 were synthesized by the hydrothermal method starting from a gel with the following molar composition: 20MTEA:10Na₂O:xAl₂O₃:100SiO₂:200H₂O, where: x=2, 1, 0.67 and 0.50, respectively. After the synthesis, the samples of ZSM-12 were ion-exchanged NH₄Cl solution to obtain zeolite in the acid form (HZSM-12). The acid properties were evaluated by n-butylamine thermodesorption in a TG equipment at three different heating rates. The model-free kinetic model was applied in the TG integral curves to estimate the apparent activation energy (E _a) of the n-butylamine desorption process. The results obtained showed that the HZSM-12 zeolite presents two kinds main of acid sites: one with E _a in the range of 115-125 kJ mol^-1 classified as weak and other kind with E _a varying of 230-250 kJ mol^-1 classified as strong. This revised version was published online in July 2006 with corrections to the Cover Date.     

晶种导向干凝胶法制备成型ZSM-5分子筛

在干凝胶法制备ZSM-5 分子筛的体系中添加晶种导向剂, 控制分子筛的生长, 制备了纳米沸石组装的无粘结剂成型多级孔ZSM-5 分子筛, 一步完成纳米分子筛的制备及组装成型, 即克服了传统纳米粒子难以过滤分离的问题, 同时组装所形成的多级孔有助于改善分子在催化剂内的扩散, 从而提高催化反应效率. 以硅胶、薄水铝石为原料, 四丙基氢氧化铵(TPAOH)和ZSM-5 晶种导向胶作为粘结剂, 通过混捏、挤条得到直径2 mm的条状前驱物, 随后通过干凝胶转换法制备成型分子筛. 所用晶种导向剂组成为0.35TPAOH:1SiO₂:20H₂O:4C₂H₅OH. 通过X射线衍射(XRD), 热重(TG)分析和傅里叶变换红外(FTIR)光谱等方法对分子筛晶化过程进行了表征, 结果表明晶种导向剂加入量对分子筛生长速度及多级孔结构均有影响. 当所加晶种导向剂中TPAOH与SiO₂的摩尔比为0.025时, 经过3 h晶化, 分子筛相对结晶度达到100%. 扫描电镜(SEM)结果表明, 合成的分子筛尺寸约为200 nm, 组装形成的多级孔分子筛的介孔体积为0.28 cm³·g^-1. 通过NH₃ 程序升温脱附(NH₃-TPD)考察了所得成型分子筛的酸性, 发现该分子筛酸性与市售的粉末H-ZSM-5分子筛类似.     

金属改性P/HZSM-5分子筛催化乙醇芳构化

以P/HZSM-5分子筛为基础, 通过浸渍法制备了Cr、Co、Cu、Zn等金属改性的M-P/HZSM-5分子筛. 采用X射线衍射(XRD), 比表面积(BET)和氨气程序升温(NH₃-TPD)等方法对其进行了表征, 并考察了其催化乙醇芳构化的活性. 结果表明, 改性后的ZSM-5分子筛保持原有的骨架结构, 但比表面积降低, 酸性分布发生变化; Cu-P/HZSM-5分子筛有较高催化活性. P和Cu的负载量分别为3%和5%, 先浸渍P再浸渍Cu, 反应温度400 °C, 质量空速(WHSV)为1.0 h^-1时轻质芳烃(BTX)收率可达到57.6%.