Sol-gel法制备掺钕钛酸铅铁电薄膜

采用sol-gel法在P型Si(111)衬底上制备了Pb0.85Nd0.1TiO3(PNT) 薄膜.用X射线衍射技术研究了退火温度对薄膜结构和结晶性的影响.同时还研究了薄膜的介电、铁电和绝缘性能.结果发现在600℃下退火1h的PNT薄膜呈钙钛矿结构;在0～5V范围内,薄膜的漏电流密度小于1.00×10-5A/cm2;在±5V的偏压范围内,C-V记忆窗口宽度为2V;在零电压下,时间保持长达105～106s; 在室温100kHz下,其介电常数为31.60,介电损耗为0.12.     

La0.5Sr0.5CoO3/Pb(Zr0.4Ti0.6)O3/La0.5Sr0.5CoO3铁电电容器的结构和性能研究

采用磁控溅射法和脉冲激光沉积法,在SrTiO3(001)衬底上制备了La0.5Sr0.5CoO3(70 nm)/Pb(Zr0.4Ti0.6)O3(70 nm)/La0.5Sr0.5CoO3(70 nm) (LSCO/PZT/LSCO)铁电电容器异质结.X射线衍射结果表明:LSCO和PZT薄膜均为外延结构.在5 V的外加电压下, LSCO/PZT/LSCO电容器具有较低的矫顽电压(0.49 V),较高的剩余极化强度(41.7 μC/cm2 )和较低的漏电流密度(1.97×10-5 A/cm2),LSCO/PZT/LSCO电容器的最大介电常数为1073.漏电流的分析表明:当外加电压小于0.6 V时,电容器满足欧姆导电机制;当外加电压大于0.6 V时,符合空间电荷限制电流(SCLC)导电机制.     

0.87Na0.5Bi0.5TiO3-0.13PbTiO3薄膜的MOSD+Dipping制备

采用MOSD+Dipping方法在P型Si(111)衬底上制备了0.87Na0.5Bi0.5TiO3-0.13PbTiO3薄膜.用X射线衍射技术研究了薄膜的结构和结晶性.用原子力显微镜分析了薄膜的表面形貌.同时还研究了薄膜的存储性能.     

(La0.5Sr0.5)CoO3为电极的Pb(Zr0.4Ti0.6)O3和Pb(Zr0.2Ti0.8)O3铁电电容器结构及电学性能

分别采用磁控溅射法和溶胶-凝胶法(Sol-gel)制备了(La0.5Sr0.5)CoO3(LSCO)和Pb(Zr1-xTix)O3(PZT)薄膜,在Pt(111)/Ti/SiO2/Si基片上构架了LSCO/Pb(Zr0.4Ti0.6)O3(PZT(40/60))/LSCO和LSCO/Pb(Zr0.2Ti0.8)O3(PZT(20/80))/LSCO铁电电容器,研究了两种铁电电容器的结构和性能。XRD结构分析表明:两种四方相的不同Zr/Ti比例的PZT薄膜均为结晶良好的多晶钙钛矿结构。在5 V测试电压下,LSCO/PZT(40/60)/LSCO和LSCO/PZT(20/80)/LSCO两种铁电电容器的剩余极化强度(Pr)和矫顽场(Ec)分别为:28μC/cm2和1.2 V以及32μC/cm2和2 V。相对于PZT(40/60),PZT(20/80)具有较大的剩余极化强度和矫顽场,是由于其矩形度(c/a)较大。两种电容器都具有较好的脉宽依赖性和抗疲劳性。在5 V的测试电压下,LSCO/PZT(40/60)/LSCO电容器的漏电流密度为3.2×10-5A/cm2,LSCO/PZT(20/80)/LSCO电容器的漏电流密度为3.11×10-4A/cm2,经拟合分析发现:在0～5 V的范围内,两种电容器都满足欧姆导电机制。     

非晶Ni-Al阻挡层对快速退火制备的硅基Ba0.6Sr0.4TiO3薄膜结构及物性影响的研究

应用非晶Ni-Al薄膜作为扩散阻挡层,采用磁控溅射法和溶胶-凝胶法在Pt/TiO2/SiO2/Si(001)衬底上制备了Pt/Ni-Al/Ba0.6Sr0.4TiO3/Ni-Al/Pt电容器结构,研究了在650～800 ℃温度范围内快速退火(RTA)工艺对电容器结构和物理性能的影响.结果表明:在外加电场为-100 kV/cm时,700 ℃和750 ℃退火样品的介电常数达到最大,分别为150和170.非晶Ni-Al薄膜的应用可以有效地降低BST薄膜的漏电流密度.650 ℃退火样品在整个测试电场范围内满足欧姆导电机制;700 ℃、750 ℃和800 ℃退火样品分别在电压低于-3.67 V、-2.65 V和-2.14 V时满足欧姆导电机制,在电压高于-3.67 V、-2.65 V和-2.14 V时满足普尔-弗兰克导电机制.     

水热法制备纳米Co0.5Zn0.5Fe2O4工艺条件试验研究

采用水热法合成纳米Co0.5Zn0.5Fe2O4粉体,并借助X射线衍射仪(XRD)、透射电子显微镜(TEM)、矢量网络分析仪(VNA)研究工艺条件(晶化温度、晶化时间)对Co0.5Zn0.5Fe2O4物相、形貌及吸波性能的影响.结果表明,当晶化时间为8 h、晶化温度为180℃时制备出纯相的尖晶石结构的纳米Co0.5Zn0.5Fe2O4,样品形貌为类球形,平均粒径为10～15 nm.在1～18 GHz频段内,样品在16.47 GHz处的反射率达到-33.9 dB,吸波性能最好.     

溶胶-凝胶法制备Na0.5Bi0.5TiO3-K0.5Bi0.5TiO3体系无铅压电陶瓷的研究

采用溶胶-凝胶法制备(1-x)Na0.5Bi0.5 TiO3-xK0.5Bi0.5TiO3体系无铅压电陶瓷.XRD分析表明,用溶胶-凝胶法可以在650℃下合成具有钙钛矿结构的(1-x)Na0.5Bi0.5TiO3-xK0.5Bi0.5TiO3粉体,且在x=0.18～0.30之间存在三方-四方准同型相界(MPB).陶瓷的压电性能参数表明,该体系在MPB组成范围内具有最佳的压电性能:x=0.30时,压电常数d33达到最大值(d33=150 Pc·N-1),平面机电耦合系数kp与介电常数εH33T/ε0均在x=0.26时达到最大值,分别为36.7;和1107.     

化学溶液分解法制备Sm0.5Bi3.5Ti3O12铁电薄膜

采用化学溶液分解法(CSD)在Si衬底上制备了Sm0.5Bi3.5Ti3O12 (SmBT0.5)薄膜.用X射线衍射技术分析了薄膜的结构和结晶性,用原子力显微镜描述了薄膜的表面形貌;并研究了薄膜的存储性以及介电性能.结果表明,在700℃下退火1h得到了结晶性较好,表面致密的多晶薄膜.该薄膜显示了良好铁电和介电性能.     

(001)高度择优取向Ba0.6Sr0.4TiO3/Pt异质结的结构及性能

采用射频磁控溅射法结合高真空后退火处理,在MgO(001)单晶基片上制备了Pt薄膜.应用脉冲激光沉积法在Pt/MgO上进一步生长了Ba0.6Sr0.4TiO3(BST)薄膜.借助X射线衍射仪(XRD)、铁电测试仪、LCR表研究了BST/Pt/MgO的结构和性能.研究发现,700 ℃真空退火可以保证Pt薄膜在MgO基片上实现(001)高度择优生长,以(001)Pt薄膜为模板,可以进一步获得(001)高度择优取向具有铁电性能BST薄膜.在100 Hz测试频率下,BST薄膜最大介电常数为1100、调谐率为81;、品质因数为21;在7 V的电压下,漏电流密度1.85×10-5 A/cm2,进一步分析表明,BST薄膜在0～2.6 V之间满足欧姆导电机制,在2.6～7 V之间满足普尔-弗兰克导电机制.     

含NiTi阻挡层的硅基(La0.5Sr0.5)CoO3/Pb(Zr0.4Ti0.6)O3/(La0.5Sr0.5)CoO3铁电电容器异质结

应用磁控溅射法制备的非晶NiTi薄膜作阻挡层,在Si (100)衬底上构造了(La0.5Sr0.5)CoO3/ Pb(Zr0.4Ti0.6)O3/(La0.5Sr0.5)CoO3(LSCO/PZT/LSCO)铁电电容器异质结,研究了Pb(Zr0.4Ti0.6)O3铁电薄膜的结构和物理性能.实验发现LSCO/PZT/LSCO铁电电容器具有良好的电学性能,在417kV/cm的驱动场强下,PZT铁电电容器具有较低的矫顽场强(125kV/cm)和较高的剩余极化强度(19.0μC/cm2),良好电容-电压特性(C-V)和保持特性,铁电电容器经过1010次反转后,极化强度没有明显下降,表明了非晶NiTi薄膜可以用作高密度硅基铁电存储器的扩散阻挡层.     

织构化K0.5Na0.5NbO3无铅压电陶瓷的性能研究

以分析纯Na2CO3、Bi2O3和Nb2O5为原料,以NaCl为熔盐,采用二次熔盐法和拓扑化学反应法合成各向异性片状NaNbO3粉体.以该片状NaNbO3粉体为模板品粒,以固相法合成的NaNbO3和KNbO3粉体为基料,采用流延工艺制备出较高取向度的织构化K0.5Na0.5NbO3(KNN)无铅压电陶瓷,系统研究了模板含量、烧结温度和保温时间等工艺参数对织构化KNN陶瓷显微结构和压电性能的影响规律.研究结果表明:随着模板含量的增加,陶瓷的取向度逐渐增加,当模板含量为15 wt;时,陶瓷的取向度可达0.69,当模板含量为10 wt;,1100 ℃下保温5 h烧结,可以获得具有一定织构度(f=0.58)的KNN陶瓷,并表现出优异的压电性能,d33=128 pC/ N.     

Carrier Scattering Mechanisms in GaS0.5Se0.5 Layered Crystals

Systematic dark electrical resistivity and Hall mobility measurements have been carried out in the temperature range 150‐400 K on n‐type GaS_0.5Se_0.5 layered crystals. The analysis of temperature dependent electrical resistivity and carrier concentration reveals the extrinsic type of conduction with a donor impurity level located at 0.44 eV, donor and acceptor concentrations of 3.4 ×10¹⁷ and 4.1×10¹⁶ cm^‐3, respectively, and an electron effective mass of 0.41 m₀. The Hall mobility is limited by the electron‐phonon short‐range interactions scattering at high temperatures combined with the ionized impurity scattering at low temperatures. The electron‐phonon short‐range interactions scattering mobility analysis reveals an electron‐phonon coupling constant of 0.25 and conduction band deformation potential of 5.57 eV/Å.     

柠檬酸盐法制备(Na0.5 Bi0.5)1-xBaxTiO3压电陶瓷的极化特性研究

采用柠檬酸盐法合成了具有单一钙钛矿结构的(Nao5Bio5)1-xBaxTiO3(x=0,x=0.04)超细粉料,并研究了陶瓷样品的极化特性、压电性能和铁电性能.研究结果表明,柠檬酸与金属离子的摩尔比(C/M)控制在1.2～1.6、前驱体液的pH值控制在7～9范围内可以得到均匀透明的溶胶和凝胶,凝胶在600℃下热处理1h后可形成单一钙钛矿结构的超细粉料.XRD研究结果表明,x=0和x=0.04时陶瓷样品均为三方钙钛矿结构.极化电压和极化温度对陶瓷样品的压电性能有很大影响,而极化时间对压电性能的影响则不显著.Ba2+的固溶改善了陶瓷样品的铁电性能,有利于材料极化性能和压电性能的提高.与常规固相法制备的同种组成样品相比,柠檬酸盐法制备的(Nao5Bi0.5)1-xBaxTiO3(x=0,x=0.04)陶瓷具有较好的压电性能.     

Direct preparation of K0.5Na0.5NbO3 powders

K_0.5Na_0.5NbO₃ powders have been directly synthesized by an alternative solid–state method. Stoichimometric mixture of ammonium niobium oxalate and C₄H₄O₆KNa·4H₂O were calcined in temperature range from 500 to 800 °C for 3 h. The precursor and calcination products were characterized with respect to stoichiometry, purity, crystalline structure, particle size and powder morphology using X–ray diffraction (XRD), X‐ray fluorescence (XRF) spectrometer, scanning electron microscope (SEM), Fourier transform infrared (FTIR) spectra, thermogravimetric (TG) analysis, differential scanning calorimetry (DSC) and UV–Vis diffuse reflectance (UV–Vis) spectroscopy. XRD and XRF results reveal that stoichiometric K_0.5Na_0.5NbO₃ powders could be synthesized by the method. The particle size is about 68 nm for the precursor calcined at 500 °C according to XRD data, which is in good agreement with SEM data. The average band gap energy is estimated to be 3.18 eV by UV–vis diffuse reflectance spectra. (© 2011 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

Li0.5Bi0.5MoO4对Li2Zn2(MoO4)3陶瓷的微波介电性能影响

采用传统固相反应法制备了xLi_0.5Bi_0.5MoO₄-(1-x)Li₂Zn₂(MoO₄)₃ [xLBM-(1-x)LZM]复合陶瓷,研究添加不同质量分数(x=25%,30%,35%,40%和45%)的LBM对LZM陶瓷的烧结特性、物相组成、微观结构以及微波介电性能的影响。结果表明:添加一定量的LBM不仅能将LZM的谐振频率温度系数(τ_f)调节近零,还能降低LZM的烧结致密化温度;LBM可与LZM共存,且不发生化学反应生成其他新相。随着LBM添加量增加,复合陶瓷的烧结致密化温度逐渐降低、体积密度先增大后减小、介电常数(ε_r)与τ_f逐渐增大而品质因数(Q×f)逐渐减小。当LBM添加量为40%时,LZM-LBM复合陶瓷在600 ℃烧结2 h获得最大体积密度为4.41 g/cm³,以及优异的微波介电性能:ε_r为13.8,Q×f为28 581 GHz,τ_f为-4×10^-6/℃。     

Microwave dielectric properties of La(1‐2x/3)Bax(Mg0.5Sn0.5)O3 ceramics

This study examined the potential applications of microwave dielectric properties of La_(1‐2x/3)Ba_x(Mg_0.5Sn_0.5)O₃ ceramics in rectenna. The La_(1‐2x/3)Ba_x(Mg_0.5Sn_0.5)O₃ ceramics were prepared by the conventional solid‐state method with various sintering temperatures. An apparent density of 6.62 g/cm³, a dielectric constant of 20.3, a quality factor of 51,700 GHz, and a temperature coefficient of resonant frequency of ‐78.2 ppm/K were obtained for La_2.98/3Ba_0.01(Mg_0.5Sn_0.5)O₃ ceramics that were sintered at 1550 °C for 4 h. (© 2010 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)     

无铅高居里点BaTiO3-Bi0.5K0.5TiO3陶瓷的制备及其PTC性能的研究

采用固相反应法制备了(1-χ)BaTO3-χBi0.5K0.5TiO33(BT-BKT,χ=0,0.1和0.2),对陶瓷样品进行X射线衍射、扫描电镜、介电常数-温度及电阻率-温度测试分析,研究了掺杂BKT对该系统陶瓷相组成、显微结构和电性能的影响.结果表明:BaTi3,陶瓷的晶格参数c轴值随着BKT含量的增加基本不变,而a轴值有所减小.BT-BKT陶瓷的居里温度(Tc)随着BKT的加入向高温移动,当χ=0.1和0.2时,Tc分别提高至170℃和185℃左右;但室温电阻率随着BKT含量的增加明显增大.     

Na/Bi配比对0.94(Bi0.5+xNa0.5-x)TiO3-0.06BaTiO3压电陶瓷组织结构与性能的影响

采用传统固相烧结方法制备出0.94(Ri0.5+xNa0.5-x)TiO3-0.06BaTiO3(BNBT6)二元系无铅压电陶瓷(x分别为0,0.08;,0.12;,0.16;,0.24;和0.50;摩尔分数),系统地研究了不同Na/Bi配比对BNT基陶瓷材料物相结构、显微组织和压电、介电性能的影响.结果表明:添加不同的Na/Bi,所制备的BNBT6压电陶瓷组织分布均匀、致密度高,存在三方-四方共存的准同型相界结构,且不同的Na/Bi配比不影响陶瓷的相结构,但其烧结性能及电性能与Na/Bi配比密切相关,当x=0.16;时,BNBT6陶瓷样品的性能最佳,相对密度达到97;,在1 kHz的测试频率下,BNBT6陶瓷样品的压电常数d33为138 PC/N、介电常数εr为1486、介电损耗tanδ为2.1;、机械品质因数Qm为217.