MgFe₂O₄ nanoparticles were hydrothermally synthesized at 150 ℃ using iron nitrate [Fe(NO₃)₃·9H₂O], magnesium nitrate [Mg(NO₃)₂·6H₂O] and sodium hydroxide (NaOH) as starting materials by carefully controlling the reaction conditions. The influences of several factors such as presence or absence of Na⁺, molar ratio of Fe³⁺ / Mg²⁺, concentration of mental ions, temperature and reaction time on resultant products were investigated in the hydrothermal process. The sample was characterized by X-ray diffraction (XRD) and transmission electron microscopy (TEM), and its magnetic properties were measured using vibrating sample magnetometer (VSM).     

草酸盐共沉淀法制备Y1.84La0.16O3纳米粉体

Nanopowder of Y_1.84La_0.16O₃ was prepared by oxalate co-precipitation method. The powder was characterized by TG-DTA, XRD and TEM. The results show that the precursor is Re₂(NO₃)₂(C₂O₄)₂·2H₂O (Re=Y, La), and the Y_1.84La_0.16O₃ nanopowders produced by calcining the precursor at 1 000 ℃ for 4 h are 20～40 nm spherical particles and well dispersed. The powders were with high sintering activity and could be fabricated to transparent ceramic without additive at 1 450～1 550 ℃ in H₂ atmosphere for 3 hours. The total transmission of the transparent ceramic could reach 80%.     

Bi2Fe4O9纳米粉体:水热法制备及表征

Bi₂Fe₄O₉ nanoparticles were prepared at low temperature via a facile, one-step hydrothermal synthesis process using iron(Ⅲ) nitrate nonahydrate(Fe(NO₃)₃·9H₂O) and bismuth nitrate pentahydrate (Bi(NO₃)₃·5H₂O) as starting materials and sodium hydroxide (NaOH) as the precipitant and mineralizer. XRD results indicate that the as-prepared nanoparticles are pure Bi₂Fe₄O₉. SEM images reveal that the as-prepared Bi₂Fe₄O₉ nanoparticles have a sheet-like morphology. The Bi₂Fe₄O₉ nanoparticles thus obtained are paramagnetic at room temperature as shown by magnetic measurements.     

由镁、铝醇盐配合物合成纳米粒子MgAl2O4尖晶石

Mg and Al alkoxide complex was synthesized in a cell without battery separator by electrochemical dissolution of aluminum for 6 h and magnesium for 1.8 h at 45 ℃ in ethanol solution of 0.04 mol·dm^-3 (Bu₄N)Br with a current density of 100 mA·cm^-2. IR and Raman spectroscopy were used to characterize the structure of the precursor of MgAl₂O₄. The results show that the current efficiency attains 98.4% and the precursor is MgAl₂(OCH₂CH₃)₅(acac)₃. The acac^- group-containing precursor could prevent it from agglomeration. The xerogel was obtained by drying in vacuum for 24 h and hydrolysis under pH≈8.5 of the precursor, which was heated at 350 ℃ for 2 h to obtain the nano-MgAl₂O₄ powder. XRD and TEM were used to investigate the structure of nano-MgAl₂O₄. The result suggests that the xerogel with an average particle size of 10 nm and the Nano-sized Spinel MgAl₂O₄ Particle of 12 nm thus obtained are with high purity.     

LiV3O8的合成及其电化学性能研究

The layered trivanadate, LiV₃O₈, was prepared by sol-gel method with LiOH, V₂O₅ and H₂O₂ as initial reagents. The materials at different heat treatment conditions were characterized by XRD and TG-DTA. Their electrochemical behaviors were studied by galvanostatic charge-discharge and cyclic voltammetry. The results show that LiV₃O₈ prepared by sintering at 300 ℃ for 16 h has higher capacity, and its initial discharge capacity is 333.1 mAh·g^-1, and maintains a discharge capacity of 302.8 mAh·g^-1 after 10 cycles at 0.2 C and the voltage range of 1.8～4.0 V.     

球形Gd2O3∶Eu纳米发光材料的制备

Spherical nanometer Gd₂O₃∶Eu luminescent materials were prepared by homogeneous precipitation method, and the properties were studied also. TG, FTIR and XRD analysis showed that the precursor was carbonate, the cubic Gd₂O₃was obtained after calcination. TEM photographs indicated that the samples were spherical and well dispersed with nanometer and submicrometer size of 200～300 nm which is the nanoparticles’ aggregate. The mechanics of agglomerating growth is also discussed. ED photograph showed that the particle was crystalline. The PL analysis exhibited that CTB band of nanometer Gd₂O₃∶Eu was of 17 nm red shift to bulk materials, and the emission peak was broadened due to the surface and interface effect of nanocrystals.     

La2(CO3)3纳米线的微乳液法制备与表征

La₂(CO₃)₃ nanowires were prepared in the nonionic surfactant microemulsion(Triton X-100/cyclohexane/water)system. Transmission electron microscopy (TEM) and selected area electronic diffraction (SAED) were used to characterize the shape and size of the products. The results showed that the pH value and concentration of mother solution, temperature and aging time all could affect the morphology and size of the La₂(CO₃)₃ nanowires. The lengths of the nanowires were more than 10 μm and the diameters were in the range of 30～200 nm.     

无氨湿法制备纳米晶In2O3及表征

Preparation of In₂O₃nano-scale powders by ultrasonic and homogeneous precipitation, using metal In and urea as raw materials, was reported for the first time, while the effects of reaction temperature, the ratio of the materials and the pH etc. on the preparation was dicussed. This method can be operated and industrialized easily with very low cost． The structural properties of precursor and In₂O₃were characterized by TG-DTA, XRD, ESCA and TEM. The results show that In₂O₃produced are very pure, monophase and spherical nano-scale powders with average size of 25 nm.     

(ZrO2)1-x(Yb2O3)x纳米晶的水热法合成及其烧结体的电性能

(ZrO₂)_1-x(Yb₂O₃)_x (x=0.07, 0.09, 0.11) nanocrystallites were hydrothermally prepared in basic media by using co-precipitated Zr(OH)₄ and Yb(OH)₃ as precursor. The nanocrystallites have small particle sizes of 5.8~7.5 nm, narrow size distribution, less agglomeration and high sinterability. The oxide-ionic conduction properties of the prepared ceramics were investigated by means of AC impedance spectroscope, oxygen concentration cell at 600~1 000 ℃. The results show that the ceramic with x=0.09 is superior to the ceramics with x=0.07 and 0.11 in oxide-ionic conduction.     

γ-Fe2O3纳米粉的低热固相制备及其电磁损耗特性(英)

The Fe(OH)₃ precursor was prepared by solid -state reaction with Fe(NO₃)₃·9H₂O, NaOH and dispersed poly-ethylene glycol at low heating temperature(25 ℃). Synthesis of iron oxide (γ-Fe₂O₃) nanoparticle was achieved by thermal decomposition of Fe(OH)₃·xH₂O precursor. The nanoparticle was characterized by TG-DTA, X-ray diffra-ction, TEM etc. The results showed that the nanoparticle was composed of γ-Fe₂O₃ and was a better absorber for electromagnetic wave within the low frequency band.     

二氧化碳和丙烯直接合成甲基丙烯酸的NiPMo/TiO2催化剂的研究

用溶胶-凝胶法以磷钼酸(MPA)的镍盐溶液水解钛酸四丁酯制备了NiPMo/TiO2催化剂.使用ICP、 XRD、 TG-DTA、 IR、 TPD-MS和微反应技术研究了催化剂的化学组成、热稳定性、化学吸附性质和催化反应性能.杂多钼酸盐与TiO2通过O2-在TiO2表面发生了键合.在623 K下,杂多阴离子仍保持原有的Keggin结构.CO2在Lewis酸位Ni(Ⅱ)和Lewis碱位Ni-O-Mo的桥氧协同作用下生成CO2卧式吸附态Ni(Ⅱ)←O-(CO)←(O--Ni).丙烯有多种吸附态在催化剂上吸附.在563 K、 1 MPa和空速1500 h-1的反应条件下,丙烯的摩尔转化率为3.2%,产物MAA选择性为95%.     

CoFe2O4自形成磁性液体场致结构化对磁化的影响

The Langevin paramagnetic theory can’t describe the relation between magnetization of ferrofluids and applied magnetic field. The structuralization of ferrofluids, which is considered the main influence factor of the magnetization, is regarded. The part of magnetization works is deposited when the structure is forming. This action influences the magnetization of ferrofluids directly or indirectly. On the base of the “compressing” model, the Langevin function that usually describes the magnetization of ferrofluid is modified, and a well-fitted curve is obtained. An equation of the relation between the equivalent volume fraction after being “compressed” and the intensity of magnetic field is discovered, which approximately describes the process of magnetization. The relation between the approximate initial susceptibility and the volume fraction can be obtained from modified formula.     

Highly regioselective Buchwald–Hartwig amination at C-2 of 2,4-dichloropyridine enabling a novel approach to 2,4-bisanilinopyridine (BAPyd) libraries

The highly regioselective Buchwald–Hartwig amination at C-2 of the cheap and readily accessible reagent, 2,4-dichloropyridine with a range of anilines and heterocyclic amines is described. This new methodology is robust and provides a facile access to 4-chloro-N-phenylpyridin-2-amines on 0.25 mol scale. These intermediates undergo a further Buchwald–Hartwig amination at higher temperature to enable rapid exploration of the chemical space at C-4 and to provide a library of 2,4-bisaminopyridines.     

Sulfur-directed metal-free and regiospecific methyl C(sp3)–H imidation of thioanisoles

Regiospecific and direct imidation of the methyl C(sp³)–H bond of thioanisoles is realized under mild and metal-free conditions with N-fluorobis(benzenesulfonyl)imide as an oxidant and nitrogen source. Proposed mechanism suggests that thionium ion intermediates and a Pummerer-type reaction are involved. The imidation has advantages such as high step-economy, excellent functionality tolerance, and regiospecificity, giving structurally diverse imidation products.     

Selective syntheses of 2H-1,3-oxazines and 1H-pyrrol-3(2H)-ones via temperature-dependent Rh(II)-carbenoid-mediated 2H-azirine-ring expansion

The Rh(II)-catalyzed reaction of 2-carbonyl-substituted 2H-azirines with ethyl 2-cyano-2-diazoacetate or 2-diazo-3,3,3-trifluoropropionate provides an easy access to 2H-1,3-oxazines and 1H-pyrrol-3(2H)-ones. These compounds can be selectively prepared from the same starting material using temperature as the only varied parameter. The 2-azabuta-1,3-diene intermediate, a common precursor for both heterocyclic products, isomerizes into 2H-1,3-oxazine under kinetic control, while 1H-pyrrol-3(2H)-one is the sole product of the reaction at elevated temperatures. According to DFT-calculations a one-atom oxazine ring contraction involving ring-opening to a 2-azabuta-1,3-diene intermediate, followed by a 1,5- and 1,2-prototropic shift leads to the consecutive formation of imidoylketene and azomethine ylide, which then further undergo cyclization to the pyrrole derivative.     

Copper catalyzed/mediated synthetic methodology for ebselen and related isoselenazolones

Scope of the copper catalyzed/mediated selenium-nitrogen coupling reaction has been studied for the synthesis of isoselenazolones. It is noticed that the 2-chloro, 2-bromo-, and 2-iodo-aryl amides substrates can be exploited in the selenium-nitrogen coupling reaction by employing 25-100 mol % of CuI/1,10-phenanthroline (L) and potassium carbonate as a base in DMF. Furthermore, electron rich 2-chloro-arylamides also underwent selenium-nitrogen coupling reaction to give biologically important selenium-nitrogen heterocycles. Also, copper-catalyzed selenium-nitrogen coupling reaction has been meticulously applied for the synthesis of diaryl diselenides having methoxy, amine, and amide functionality from respective aryl iodides in the presence of stoichiometric amount of succinimide as an external Se-N coupling partner.     

Knoevenagel condensation catalyzed by novel Nmm-based ionic liquids in water

A series of novel N-methyl morpholine (Nmm) based ionic liquids with 1,2-propanediol group were synthesized and used as catalysts for Knoevenagel condensation at room temperature in water. Under the effect of the catalyst, various aldehydes or aliphatic ketones could react with a wide range of activated methylene compounds well, including malononitrile, alkyl cyanoacetate, cyanoacetamide, β-diketone, barbituric acid, 2-arylacetonitrile and thiazolidinedione. Furthermore, most of the products could be separated just by filtrating and washing with water. Additionally, the catalyst is recyclable and applicable for the large-scale synthesis.     

Construction of polyheterocyclic spirotetrahydrothiophene derivatives via sulfa-Michael/aldol cascade reaction

A series of polyheterocyclic spirotetrahydrothiophene derivatives were obtained in moderate to excellent yields via a catalyst-free sulfa-Michael/aldol cascade reaction of chalcones 1 and commercially available 1,4-dithiane-2,5-diol 2 under mild conditions. We also present the first asymmetric sulfa-Michael/aldol cascade reaction of chalcones 1 and commercially available 1,4-dithiane-2,5-diol 2 with moderate to good enantioselectivities catalyzed by readily available chiral phase-transfer catalysts (PTCs).     

Suzuki-Miyaura reactions of the soluble guanylate cyclase inhibitor NS2028: a non-product specific route to C-8 substituted analogues

Both soluble guanylate cyclase (sGC) inhibitors ODQ 1 and NS2028 2 are synthesized via improved protocols. In the former case treating 3,4-dihydroquinoxalin-2(1H)-one oxime 8, which can be prepared in two steps from 1,2-benzenediamine, with 1,1′-carbonyldiimidazole (CDI) gives the dihydro-ODQ 10 that in the presence of KMnO₄ oxidises to give ODQ 1 in an overall yield of 46% starting from 1,2-benzenediamine. In the latter case, the synthesis affords NS2028 2 from 2-amino-4-bromophenol 3 in three steps with an overall yield of 85% and avoids the need for chromatography. Furthermore, Suzuki-Miyaura reaction conditions are described that enable the preparation of 8-aryl and 8-heteroaryl derivatives of NS2028 directly from NS2028 2. Finally, demethylation of the 8-(methoxyphenyl) substituted analogues afforded the 8-(hydroxyphenyl) derivatives 40-42. All new products are fully characterised.