Bismuth aluminoborate Bi<Subscript>0.96</Subscript>Al<Subscript>2.37</Subscript>(B<Subscript>4</Subscript>O<Subscript>10</Subscript>)O: Synthesis and crystal structure

The crystal structure of a new bismuth aluminoborate Bi_0.96Al_2.37(B₄O₁₀)O is studied by single-crystal X-ray diffraction. The Bi_0.96Al_2.37(B₄O₁₀)O single crystals are hexagonal (space group \(P\bar 6\) 2m). The unit cell parameters are as follows: a = b = 4.587(4) Å, c = 2.253(9) Å, α = β = 90°, γ = 120°, V = 168.60 ų, Z = 1.     

Characterization of NiFe<Subscript>2</Subscript>O<Subscript>4</Subscript> nanoparticles synthesized by various methods

Microwave-induced combustion with glycine, CTAB-assisted hydrothermal process with NaOH and NH3, EDTA assisted-hydrothermal methods have been applied to prepare NiFe₂O₄ nanoparticles for the first time. Structural and magnetic properties of the products were investigated by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), transmison electron microscopy (TEM), Fourier transform infrared spectroscopy (FTIR), and electron spin resonance spectrometry (EPR). TEM measurements showed that morphology of the product depends on the synthesis method employed. The average cystallite size of NiFe₂O₄ nanoparticles was in the range of 14–59 nm as measured by XRD. The uncoated sample (Method A) had an EPR linewidth of 1973 Oe, the coated samples reached lower values. The magnetic dipolar interactions existing among the Ni ferrite nanoparticles are reduced by the coatings, which could cause the decrease in the linewidth of the EPR signals. Additionally, the linewidth increases with an increase in the size and the size distribution of nanoparticles.     

Composition of the gas phase over Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and the enthalpies of atomization of AlO,Al<Subscript>2</Subscript>O,and Al<Subscript>2</Subscript>O<Subscript>2</Subscript>

The A1, O, AlO, A1₂O, Al₂O₂, WO₂, and WO₃, partial pressures in the vapor over Al₂O₃ in a tungsten Knudsen effusion cell between 2300 and 2600 K were derived from A1⁺, O⁺, AlO⁺, A1₂O⁺, Al₂O₂⁺, WO₂⁺, and WO₃⁺, ion intensities. The mass spectrometer was calibrated against the equilibrium constant of the WO₃(g) = WO₂(g) + O(g) reaction. Refined values of the ionization cross sections of AlO and A1₂O₂ were used in the partial pressure calculations. The enthalpies of atomization of aluminum suboxides were determined to be Δ_at H ^o(AlO, g, 0) = 510.7 ± 3.3 kJ mol⁻¹, Δ_at H ^o(Al₂O, g, 0) = 1067.2 ± 6.9 kJ mol⁻¹, and Δ_at H ^o(Al₂O₂, g, 0) = 1556.7 ± 9.9 kJ mol⁻¹.     

Characteristics of CuAl<Subscript>2</Subscript>-Cu<Subscript>9</Subscript>Al<Subscript>4</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> nanocomposites synthesized by mechanical treatment

Summary Reactive milling of Cu-hydroxycarbonate - powder aluminium mixture brings many complex chemical reactions such as decomposition, aluminothermic reduction and mechanical alloying resulting in the formation of nanometer size composites that contain intermetallic phases, -Cu₉Al₄ and -CuAl₂, with aluminium oxide.     

Kinetic studies on the hydrogenation of nitrate in water using Rh/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> and Rh-Cu/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> catalysts

Liquid-phase reduction NO ₃ ⁻ using monometallic and bimetallic catalysts (5% Rh/Al₂O₃, 5% Rh-0.5% Cu/Al₂O₃, 5% Rh-1.5% Cu/Al₂O₃, 5% Rh-5% Cu/Al₂O₃ and a physical mixture of 5% Rh/Al₂O₃ and 1.5% Cu/Al₂O₃) was studied in a slurry reactor operating at atmospheric pressure. Kinetic measurements were performed for a low concentration of nitrate (0.4 × 10⁻³−3.2 × 10⁻³ mol dm⁻³) and the temperature range 293–313 K. From the experimental data, it was found that the reduction of nitrate is first order with respect to nitrate. On the basis of the rate constants, the apparent activation energy was established using a graphic method. Published in Russian in Kinetika i Kataliz, 2007, Vol. 48, No. 6, pp. 881–886. This article was submitted by the authors in English.     

Microstructure and Conduction of Composites Bi<Subscript>2</Subscript>CuO<Subscript>4</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript> Near the Eutectic Melting Point

Microstructure and conduction of ceramic composites Bi₂CuO₄ + xBi₂O₃ (x = 5, 10, 15, 20 wt %) near the eutectic melting point (770°C) are studied. Bismuth oxide, initially randomly distributed over the ceramics bulk, after quenching from temperatures exceeding the eutectic melting point, becomes localized at triple junctions and grain boundaries in Bi₂CuO₄, which is caused by wetting grain boundaries and forming a liquid-channel structure. The jumpwise change in the composites’ conductivity near 730 and 770°C caused by polymorphic transformation of Bi₂O₃ and the eutectic melting with simultaneous formation of a liquid-channel structure. Transport numbers of the oxygen ion are measured at 770°C by coulomb-volumetric method. The conduction by oxygen ions increases in the composites with decreasing average size of Bi₂CuO₄ crystallites.__________Translated from Elektrokhimiya, Vol. 41, No. 5, 2005, pp. 596–601.Original Russian Text Copyright © 2005 by Lyskov, Metlin, Belousov, Tret’yakov.     

Conductivity of Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>-NiO composites

The conductivity and transport number of oxygen ions of Bi₂O₃-(10, 30, 50) vol % NiO composites are measured using the four-probe and coulomb-volumetric methods at various temperatures. It is shown that the Bi₂O₃-50 vol % NiO composite exhibits a high mixed ionic-electronic conductivity in the temperature range from 730 to 800°C.     

Synthesis and crystal structure of strontium borate Sr<Subscript>4</Subscript>B<Subscript>14</Subscript>O<Subscript>25</Subscript>

The new compound Sr₄B₁₄O₂₅ (4SrO · 7B₂O₃) corresponding to an oxide ratio of 4: 7 has been identified and synthesized in the SrO-B₂O₃ system. The crystal structure of the compound has been determined (space group Cmc2₁, a = 7.734(5) Å, b = 16.332(5) Å, c = 14.556(5) Å, Z = 4, 702 F(hkl), R = 0.078). The borate anions form a three-dimensional framework consisting of borate groups of two types: three-ring structures (2□, Δ) and BO₃ triangles. Layers formed by 14-membered rings composed of boron-oxygen tetrahedra and triangles packed within the layer according to the herringbone pattern can be distinguished in the framework. The strontium atoms are located on the mirror symmetry planes between these layers. The compound is metastable and decomposes, on long-term storage, into strontium di- and metaborate.     

2-pyrrolidone - capped Mn<Subscript>3</Subscript>O<Subscript>4</Subscript> nanocrystals

Water-soluble Mn₃O₄ nanocrystals have been prepared through thermal decomposition in a high temperature boiling solvent, 2-pyrrolidone. The final product was characterized with XRD, SEM, TEM, FTIR and Zeta Potential measurements. Average crystallite size was calculated as ∼15 nm using XRD peak broadening. TEM analysis revealed spherical nanoparticles with an average diameter of 14±0.4 nm. FTIR analysis indicated that 2-pyrrolidone coordinates with the Mn₃O₄ nanocrystals only via O from the carbonyl group, thus confining their growth and protecting their surfaces from interaction with neighboring particles.      

Comparative Study of the Oxygen Storage Capacity of Pt/M<Subscript>x</Subscript>O<Subscript>y</Subscript>/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> Systems

The oxygen storage capacity of 1% Pt/15% M_xO_y/Al₂O₃ systems containing a rare-earth or an alkaline-earth metal oxide or TiO₂ as the oxygen-storing component was studied. Oxygen storage capacity was evaluated as the amount of C₃H₈ reacting at 400°C with oxygen that was taken up by the catalyst during oxidative treatment. The systems containing a rare-earth metal oxide or TiO₂ possess the highest oxygen storage capacity among the catalysts examined (80 and 75 µmol C₃H₈/g Cat, respectively). Of the BaO and SrO systems, the latter is of interest, although its oxygen storage capacity (∼27 µmol C₃H₈/g Cat) is somewhat lower than the oxygen storage capacity of any rare-earth metal oxide or the TiO₂ system.__________Translated from Kinetika i Kataliz, Vol. 46, No. 4, 2005, pp. 585–589.Original Russian Text Copyright © 2005 by Sinel’nikov, Tolkachev, Stakheev.     

Thermal synthesis of the CeO<Subscript>2</Subscript>-PrO<Subscript>2</Subscript>-Nd<Subscript>2</Subscript>O<Subscript>3</Subscript>pigments

Summary The synthesis of new compounds based on the CeO₂-PrO₂-Nd₂O₃system, which can be used as pigments for colouring of ceramic glazes, is investigated in our laboratory. The optimum conditions for the syntheses of these compounds have been estimated. The methods of thermal analysis provided first information about the temperature region of the formation of the pigments investigated. The synthesis of these compounds was followed by thermal analysis using STA 449/C Jupiter (Netzsch, Germany).     

Physicochemical properties and mixed electronic and ionic conduction of composite ceramics in the system ZrO<Subscript>2</Subscript>-Bi<Subscript>2</Subscript>CuO<Subscript>4</Subscript>-Bi<Subscript>2</Subscript>O<Subscript>3</Subscript>

Composites ZrO₂-(Bi₂CuO₄+ 20 wt % Bi₂O₃) (50–80 vol % ZrO₂) are synthesized and their physicochemical properties are studied. It is demonstrated that the composites comprise triple-phase mixtures of ZrO₂ of a monoclinic modification, Bi₂CuO₄, and solid solution Bi_2?x Zr _x O_{3 + x/2} and retain their mechanical strength up to 800°C. Impedance spectroscopy is used to examine their electroconductivity at 700–800°C in the interval of partial oxygen pressures extending from 37 to 2.1 × 10⁴ Pa. Contributions made by electronic and ionic constituents to their overall conductivity are evaluated. The best specimens’ conductivity is ～0.01 S cm^?1, with the electronic and ionic transport numbers nearly equal. The composite consisting of 50 vol % ZrO₂ and 50 vol % (Bi₂CuO₄ + 20 wt % Bi₂CuO₄) is tested in the role of an oxygen-separating membrane. The selective flux of oxygen in the temperature interval 750–800°C amounts to (2.2–6.3) × 10^?8 mol cm^?2 s^?1, testifying that these materials may be used as gas-separating membranes.     

Prediction of new A<Subscript>3+</Subscript>B<Subscript>3+</Subscript>C<Subscript>2+</Subscript>O<Subscript>4</Subscript> compounds

Hitherto unprepared ABCO₄ compounds (where A and B stand for tervalent metals (r _A ≥ r _B) and C stands for a divalent metal) are predicted. Criteria are found to predict the possibility for these compounds to crystallize in some type of structure (K₂NiF₄, CaFe₂O₄, YbFe₂O₄, or spinel) at room temperature and atmospheric pressure. The prediction is based only on the properties of elements and simple oxides. A special software system for computer-aided analysis of information is used for calculations involving pattern recognition based on use case.     

High-temperature X-ray study of the formation and delamination of manganese-alumina spinel Mn<Subscript>1.5</Subscript>Al<Subscript>1.5</Subscript>O<Subscript>4</Subscript>

The behavior of the manganese-alumina system with Mn:Al = 1:1 on heating in air and vacuum was studied. The starting samples were mixtures of β-Mn₃O₄, α-Mn₂O₃, and γ-Al₂O₃. On heating to 950°C in air, the samples were partially oxidized into α-Mn₂O₃, and corundum α-Al₂O₃ formed along with mixed manganese-alumina cubic spinel, whose composition was close to Mn₂AlO₄. In vacuum at 1200°C, the starting sample with a ratio of Mn:Al = 1:1 transformed into the manganese-alumina spinel Mn_1.5Al_1.5O₄, which retained its cubic structure after slow cooling in vacuum. When cooled in air, this solid solution delaminated, and a nanocrystalline Mn_2.8Al_0.2O₄ phase formed, whose structure was β-Mn₃O₄ type tetragonal spinel.     

Trimetallic NiMoW/Al<Subscript>2</Subscript>O<Subscript>3</Subscript> hydrotreating catalyst based on H<Subscript>4</Subscript>SiMo<Subscript>3</Subscript>W<Subscript>9</Subscript>O<Subscript>40</Subscript> mixed heteropoly acid

Trimetallic NiMoW/Al₂O₃ catalyst was prepared using mixed H₄SiMo₃W₉O₄₀ heteropoly acid of Keggin structure and nickel citrate. Bimetallic NiMo/Al₂O₃ and NiW/Al₂O₃ catalysts based on H₄SiMo₁₂O₄₀ and H₄SiW₁₂O₄₀, respectively, were synthesized as reference samples. The use of mixed H₄SiMo₃W₉O₄₀ heteropoly acid as an oxide precursor allows the tungsten sulfidation degree and the degree of promotion of active phase particles to be increased. The hydrodesulfurization activity is enhanced as compared to NiW/Al₂O₃ catalyst. The synergistic enhancement of the activity of the NiMo₃W₉/Al₂O₃ catalyst relative to the bimetallic analogs is probably caused by formation of new mixed promoted active sites for direct desulfurization.     

Effect of the modifier ion on the properties of MgFe<Subscript>2</Subscript>O<Subscript>4</Subscript> and ZnFe<Subscript>2</Subscript>O<Subscript>4</Subscript> pigments

Magnesium and zinc ferrites have been prepared by the polymeric precursor method. The organic material decomposition was studied by thermogravimetry (TG) and differential thermal analysis (DTA). The variation of crystalline phases and particle morphology with calcination temperature were investigated using X-ray diffraction (XRD) and scanning electronic microscopy (SEM), respectively. The colors of the ferrites were evaluated using colorimetry. Magnesium ferrite crystallizes above 800°C, presenting a yellow- orange color with a reflectance peak at the 600–650 nm range, while zinc ferrite crystallizes at 600°C, with a reflectance peak between 650–700 nm, corresponding to the red-brick color.     

Laser assisted selective chemical metalization of Al<Subscript>2</Subscript>O<Subscript>3</Subscript> films

Thick aluminum oxide films are prepared on Al plates by anodizing. On the ceramic surface thus obtained a very thin Ag film is deposited via vacuum thermal evaporation. The Ag/Al₂O₃/Al samples prepared are irradiated by Nd:YAG laser through a suitable metal mask in order to remove the top metal film in the exposed areas. Thus, a negative silver image of the copied mask is obtained. Further, the samples are processed in Ni electroless chemical bath activated by the rest of silver. All processing steps are studied by scanning electron microscopy (SEM). EDS X-ray mapping is applied to study the final distribution of Al and Ni in the processed areas. In addition, the DC conductivity of the fabricated Ni wires obtained is measured. The proposed new method for selective chemical deposition of electroconductive Ni onto laser microstructured Ag/Al₂O₃/Al samples is simple, versatile and not restricted to the metal/ceramic system studied as well as to the electroless deposited metal.     

Changes in the heat capacity of Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-Cr<Subscript>2</Subscript>O<Subscript>3</Subscript> solid solutions near the point of antiferromagnetic phase transition in Cr<Subscript>2</Subscript>O<Subscript>3</Subscript>

Al₂O₃-Cr₂O₃ solid solutions with 0, 4, 7, 10 and 20 mol% of corundum were synthesized using a high-pressure/high-temperature apparatus and characterized by X-ray powder diffraction. Calorimetric measurements were carried out using DSC-111 (Setaram). Heat capacity was measured by the enthalpy method in a temperature range of 260–340 K, near magnetic phase transition in pure Cr₂O₃ (305 K). Magnetic contribution into the heat capacity was derived and found to change irregularly with the composition.     

Behavior of the Al<Subscript>2</Subscript>O<Subscript>3</Subscript>-ZrO<Subscript>2</Subscript> System at High Temperatures

The system Al₂O₃-ZrO₂ at temperatures of up to 2100°C was studied by differential thermal analysis.__________Translated from Zhurnal Prikladnoi Khimii, Vol. 78, No. 3, 2005, pp. 353–356.Original Russian Text Copyright © 2005 by Kamaev, Archugov, Mikhailov.