Long circulating 10-hydroxycamptothecin-loaded nanoparticles fabricated from poly(ethylene glycol)/poly(L-lactic acid) multiblock copolymers

A series of poly(ethylene glycol) (PEG)/poly(L-lactic acid) (PLLA) multiblock copolymers were facilely synthesized using triphosgene as coupling agent. With the resulting multiblock copolymers, 10-hydroxycamptothecin (HCPT)-loaded nanoparticles were successfully prepared by dialysis method. The results obtained from dynamic light scattering (DLS) measurements confirmed that HCPT-loaded nanoparticles had the size of less than 200 nm and the average diameter decreased with increasing PLLA content. TEM images demonstrated that most of the drug-loaded nanoparticles had a distinct spherical shape and smooth surface without any aggregation. Atomic force microscopy (AFM) images further indicated that the nanoparticles were in spherical shape with smooth surface, no drug crystal was visualized on their surface. To investigate the drug state in HCPT-loaded nanoparticles, differential scanning calorimetry (DSC) and X-ray powder diffraction (XRD) measurements were carried out. The results from these tests suggested that HCPT was molecularly dispersed in the amorphous polymer matrix. Drug loading content and in vitro drug release behavior of HCPT-loaded nanoparticles showed dependence on polymer composition. Cytotoxicity test indicated that HCPT-loaded nanoparticles exhibited greatly superior cytotoxicity compared to free HCPT due to its molecular dispersion in the polymer matrix. Furthermore, the nanoparticles significantly increased the duration of the drug in circulation. All these results demonstrated that PEG/PLLA nanoparticles have great potential as promising delivery system for poorly soluble antitumor drugs.     

Preparation and characterization of poly(l,l-lactide)-b-poly(ethylene glycol)-b-poly(l,l-lactide) (PLLA-PEG-PLLA) microspheres having encapsulated tetracycline

Amphiphilic triblock copolymers, based on hydrophilic poly(ethylene glycol) (PEG) blocks and hydrophobic poly(l,l-lactide) (PLLA) blocks, were used as the matrix material for the preparation of tetracycline-loaded microspheres. The morphology and thermal properties of the biodegradable microspheres were evaluated. SEM showed the predominance of the spherical shape, however, it was possible to distinguish three patterns: rough or smooth surface or uneven collapsed volume. The FTIR analysis indicated good mechanical stability and structural integrity of the PLLA-PEG-PLLA copolymer??s microspheres enclosing tetracycline. By thermal analysis it was possible to see the marginal influence of tetracycline on the glass transition and melting temperatures of the PLLA-PEG-PLLA triblock copolymer, while the results by TG indicated the presence of tetracycline in the inner structure of the microspheres, which thermal decomposition leading to char formation was triggered by the drug??s presence.     

Cell Spheroid Formation on the Surface of Multi-Block Copolymers Composed of Poly(2-methoxyethyl acrylate) and Polyethylene Glycol

3D structured cells have great drug screening potential because they mimic in vivo tissues better than 2D cultured cells. In this study, multi-block copolymers composed of poly(2-methoxyethyl acrylate) (PMEA) and polyethylene glycol (PEG) are developed as a new kind of biocompatible polymers. PEG imparts non-cell adhesion while PMEA acts as an anchoring segment to prepare the polymer coating surface. The multi-block copolymers show higher stability in water than PMEA. A specific micro-sized swelling structure composed of a PEG chain is observed in the multi-block copolymer film in water. A single NIH3T3-3-4 spheroid is formed in 3 h on the surface of the multi-block copolymers with 8.4 wt% PEG. However, at a PEG content of 0.7 wt%, spheroid formed after 4 days. The adenosine triphosphate (ATP) activity of cells and the internal necrotic state of the spheroid change depending on PEG loading in the multi-block copolymers. As the formation rate of cell spheroid on low-PEG-ratio multi-block copolymers is slow, internal necrosis of cell spheroid is less likely to occur. Consequently, the cell spheroid formation rate by changing the PEG chain content in multi-block copolymers is successfully controlled. These unique surfaces are suggested to be useful for 3D cell culture.     

Surface characterization of poly(L-lactic acid)-methoxy poly(ethylene glycol) diblock copolymers by static and dynamic contact angle measurements, FTIR, and ATR-FTIR

The surface composition and surface free energy properties of two types of amphiphilic and semicrystalline diblock copolymers consisting of poly(L-lactic acid) coupled to (methoxy poly(ethylene glycol) (PLLA-MePEG) having differing block lengths of PEG were investigated by using static and dynamic contact angle measurements, transmission Fourier infrared spectroscopy (FTIR), and attenuated total reflection spectroscopy (ATR-FTIR) and compared with results obtained from PLLA and MePEG homopolymers. The contact angle results were evaluated by using the van Oss-Good method (acid-base method), and it was determined that the Lewis base surface tension coefficient (gamma-) of the copolymers increased with an increase of the PEG molar content at the copolymer surface. This result is in good agreement with the transmission FTIR and ATR-FTIR results but not proportional to them, indicating that the surfaces of the copolymers are highly mobile and that the molecular rearrangement takes place upon contact with a polar liquid drop. The dynamic contact angle measurements showed that the strong acid-base interaction between the oxygen atoms in the copolymer backbone of the relatively more hydrophilic PEG segments with the Lewis acidic groups of the polar and hydrogen-bonding water molecules enabled the surface molecules to restructure (conformational change) at the contact area, so that the PEG segments moved upward, whereas the apolar methyl pendant groups of PLLA segments buried downward.     

Nonisothermal crystallization behavior of the poly(ethylene glycol) block in poly(L‐lactide)–poly(ethylene glycol) diblock copolymers: Effect of the poly(L‐lactide) block length

The confined crystallization behavior, melting behavior, and nonisothermal crystallization kinetics of the poly(ethylene glycol) block (PEG) in poly(L ‐lactide)–poly(ethylene glycol) (PLLA–PEG) diblock copolymers were investigated with wide‐angle X‐ray diffraction and differential scanning calorimetry. The analysis showed that the nonisothermal crystallization behavior changed from fitting the Ozawa equation and the Avrami equation modified by Jeziorny to deviating from them with the molecular weight of the poly(L ‐lactide) (PLLA) block increasing. This resulted from the gradual strengthening of the confined effect, which was imposed by the crystallization of the PLLA block. The nucleation mechanism of the PEG block of PLLA15000–PEG5000 at a larger degree of supercooling was different from that of PLLA2500–PEG5000, PLLA5000–PEG5000, and PEG5000 (the numbers after PEG and PLLA denote the molecular weights of the PEG and PLLA blocks, respectively). They were homogeneous nucleation and heterogeneous nucleation, respectively. The PLLA block bonded chemically with the PEG block and increased the crystallization activation energy, but it provided nucleating sites for the crystallization of the PEG block, and the crystallization rate rose when it was heterogeneous nucleation. The number of melting peaks was three and one for the PEG homopolymer and the PEG block of the diblock copolymers, respectively. © 2006 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 44: 3215–3226, 2006     

Probing the micellization of diblock and triblock copolymers of poly(<Emphasis Type="SmallCaps">l</Emphasis>-lactide) and poly(ethylene glycol) in aqueous and NaCl salt solutions

The micelle formation of a series of amphiphilic block copolymers in aqueous and NaCl solutions was studied by a fluorescent probe technique using pyrene as a "model drug". These copolymers were synthesized from poly (ethylene glycol) (PEG) and l-lactide by a new calcium ammoniate catalyst. They had fixed PEG block lengths (44, 104 or 113 ethylene oxide units) and various poly(l-lactide) (PLLA) block lengths (15–280 lactide units). The critical micelle concentration (cmc) was found to decrease with increasing PLLA content. The distinct dissimilarity of the cmc values of diblock and triblock copolymers based on the same block length of PEG provided evidence for the different configurations of their micelles. It was also observed that the introduction of NaCl salt significantly contributed to a decrease in the cmcs of the copolymers with short PEG and PLLA blocks, while it had less influence on the cmcs of copolymers with long PEG or PLLA blocks. The dependence of partition coefficients ranging from 0.2×10⁵ to 1.9×10⁵ on the PLLA content in the copolymer and on the micelle configuration was also discussed. The contribution of NaCl salt to increasing the partition of pyrene into a micellar phase was observed.     

Preparation and characterization of biodegradable poly(l-lactide)/poly(ethylene glycol) microcapsules containing erythromycin by emulsion solvent evaporation technique

In this work, the producing of a biodegradable poly(l-lactide) (PLA)/poly(ethylene glycol) (PEG) microcapsule by emulsion solvent evaporation method was investigated. The effect of PEG segments added to the PLA microcapsules on the degradation, size distribution, and release behavior was studied. According to the results, PLA/PEG copolymer was more hydrophilic than PLA homopolymer, and with lower glass transition temperature. The surface of PLA/PEG microcapsules was not as smooth as that of PLA microcapsules, the mean diameters of prepared PLA and PLA/PEG microcapsules were 40 and 57 microm, respectively. And spherical forms were observed by the image analyzer and the scanning electron microscope (SEM). Drug release from microcapsules was affected by the properties of PLA/PEG copolymers determined by UV-vis spectra. It was found that the drug release rates of the microcapsules were significantly increased with adding of PEG, which explained by increasing hydrophilic groups.     

Drug release and biocompatibility of self‐assembled micelles prepared from poly (ɛ‐caprolactone/glycolide)‐poly (ethylene glycol) block copolymers

A series of poly(?‐caprolactone/glycolide)‐poly(ethylene glycol) (P(CL/GA)‐PEG) diblock copolymers were prepared by ring opening polymerization of a mixture of ?‐caprolactone and glycolide using mPEG as macro‐initiator and stannous octoate as catalyst. Self‐assembled micelles were prepared from the copolymers using nanoprecipitation method. The micelles were spherical in shape. The micelle size was larger for copolymers with longer PEG blocks. In contrast, the critical micelle concentration of copolymers increased with decreasing the overall hydrophobic block length. Drug loading and drug release studies were performed under in vitro conditions, using paclitaxel as a hydrophobic model drug. Higher drug loading was obtained for micelles with longer poly(ε‐caprolactone) blocks. Faster drug release was obtained for micelles of mPEG2000 initiated copolymers than those of mPEG5000 initiated ones. Higher GA content in the copolymers led to faster drug release. Moreover, drug release rate was enhanced in the presence of lipase from Pseudomonas sp., indicating that drug release is facilitated by copolymer degradation. The biocompatibility of copolymers was evaluated from hemolysis, dynamic clotting time, and plasma recalcification time tests, as well as MTT assay and agar diffusion test. Data showed that copolymer micelles present outstanding hemocompatibility and cytocompatibility, thus suggesting that P(CL/GA)‐PEG micelles are promising for prolonged release of hydrophobic drugs.     

Greatly enhanced hydrolytic degradation ability of poly(L-lactide) achieved by adding poly(ethylene glycol)

Plasticized poly(L-lactide)(PLLA) materials have been applied in many fields and the microstructure performance of such materials attracts much attention of researchers. However, few reports declared the hydrolytic degradation ability of the plasticized PLLA materials. In this article, a small quantity of poly(ethylene glycol)(PEG) was introduced into PLLA, which aimed to understand the hydrolytic degradation behavior of the plasticized PLLA materials. The microstructures of the plasticized samples were comparatively investigated using scanning electron microscopy(SEM), wide angle X-ray diffraction(WAXD), differential scanning calorimetry(DSC) and Flourier transform infrared spectroscopy(FTIR), etc. The results demonstrated that PEG improved the hydrophilicity of sample surface, and the relatively high content of PEG enhanced the crystallization ability of PLLA matrix. The hydrolytic degradation measurement was carried out at 60 ℃ in an alkaline solution of pH = 12. The results demonstrated that the plasticized PLLA samples exhibited accelerated hydrolytic degradation compared with the pure PLLA sample, and the hydrolytic degradation was also dependent on the PEG content. Further results demonstrated that PEG induced the change of hydrolytic degradation mechanism possibly due to the good dissolution ability of PEG in water, which provided more paths for the penetration of water. Furthermore, the microstructure evolution of the plasticized PLLA during the hydrolytic degradation process was also investigated, and the results demonstrated the occurrence of PLLA crystallization, which was possibly contributed to the decreased hydrolytic degradation rate observed at relatively long hydrolytic degradation time. This work is of great significance and may open a new way for promoting the reclamation of PLLA waste material.     

Quantitative analysis of biodegradable amphiphilic poly(L-lactide)-block-poly(ethyleneglycol)-blockpoly(L-lactide) by using TG, FTIR and NMR

The thermogravimetric analysis (TG) of two series of tri-block copolymers based on poly(L,L-lactide) (PLLA) and poly(ethyleneglycol) (PEG) segments, having molar mass of 4000 or 600 g mol^–1, respectively, is reported. The prepared block copolymers presented wide range of molecular masses (800 to 47500 g mol^–1) and compositions (16 to 80 mass% PEG). The thermal stability increased with the PLLA and/or PEG segment size and the tri-block copolymers prepared from PEG 4000 started to decompose at higher temperatures compared to those copolymers from PEG 600. The copolymers compositions were determined by thermogravimetric analysis and the results were compared to other traditional quantitative spectroscopic methods, hydrogen nuclear magnetic resonance spectrometry (¹HNMR) and Fourier transform infrared spectrometry (FTIR). The PEG 4000 copolymer compositions calculated by TG and by ¹HNMR, presented differences of 1%, demonstrating feasibility of using thermogravimetric analysis for quantitative purposes.     

Poly(ethylene glycol)/poly(ethyl cyanoacrylate) amphiphilic triblock copolymer nanoparticles as delivery vehicles for dexamethasone

Amphiphilic triblock copolymers, poly(ethyl cyanoacrylate)‐b‐poly(ethylene glycol)‐b‐poly(ethyl cyanoacrylate) (PECA‐b‐PEG‐b‐PECA), were synthesized via oxyanion‐initiated polymerization with sodium alcoholate‐terminated PEG as macroinitiator. PECA‐b‐PEG‐b‐PECA were characterized by gel permeation chromatography system, ¹H NMR and FTIR. The results indicate that the copolymerization is well controlled with narrow molecular weight distribution. The dexamethasone (DXM)‐loaded PECA‐b‐PEG‐b‐PECA nanoparticles (NPs) were prepared by nanoprecipitation technique and then characterized by Laser Particle Size Analyzer, ¹H NMR and transmission electron microscopy. The drug‐loaded PECA‐b‐PEG‐b‐PECA NPs are of spherical shape with average size of less than 100 nm. The drug‐loaded amount (DLA) and encapsulation efficiency of DLNPs were investigated by HPLC. The results show that DXM can be effectively incorporated into PECA‐b‐PEG‐b‐PECA NPs, which provides an optional delivery system for DXM and other hydrophobic drugs. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 7809–7815, 2008     

Controlled preparation of poly(ethylene glycol) and poly(L‐lactide) block copolymers in the presence of a monomer activator

Polymerization of L ‐lactide (LA) was performed in the presence of trifluoromethanesulfonic acid (CF₃SO₃H) via an activated monomer mechanism to synthesize various block copolymers composed of polyethyleneglycol (PEG) and poly(L ‐lactide) (PLLA). The PLLAs obtained had molecular weights close to theoretical values calculated from LA/PEG molar ratios and exhibited monomodal GPC curves. A ¹H NMR spectroscopic study showed that the LA carbonyl carbon signal exhibited a change in chemical shift to lower field, caused by electron delocalization of the carbonyl carbon by CF₃SO₃H. We successfully prepared PEG and PLLA block copolymers using this activated monomer mechanism. We concluded that synthesis proceeded by LA ring‐opening polymerization caused by PEG in the presence of CF₃SO₃H to yield PEG and PLLA block copolymers. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5917–5922, 2009     

Macromolecular Organization of Poly(L‐lactide)‐block‐Polyoxyethylene into Bio‐Inspired Nano‐Architectures

Block copolymers create various types of nano‐structures, e. g., spheres, rods, cubes, and lamellae. This review discloses the dynamic macromolecular organization of block copolymers comprising poly(L ‐lactide) (PLLA) and poly(oxyethylene) (PEG) that allows to simulate elaborate biological systems. The block copolymers, AB‐ (PLLA‐PEG) and ABA‐type (PLLA‐PEG‐PLLA), are synthesized by ordinary lactide polymerization to have a controlled block length. They are dispersed into an aqueous medium to prepare nano‐scale particles, consisting of hydrophobic PLLA and hydrophilic PEG in the core and shell, respectively. Then, the particles are placed on a flat substrate by the casting method. The particles are detected as discoids by AFM, having shrunk with loss of water. Heat‐treatment of these particles at 60°C (above T_g of PLLA) gives rise to a collapse into small fragments, which then aggregate into bands with nano‐size width and thickness. The PLLA‐PEG bands align parallel to each other, while the PLLA‐PEG‐PLLA bands form a characteristic network resembling the neuron system created in animal tissue. As analyzed by TEM diffraction, each is composed of α‐crystal of PLLA whose c‐axis (molecular axis) is perpendicular to the substrate surface. Based on this fact, a doubly twisted chain structure of PLLA is proposed in addition to a plausible mechanism for the self‐organization of the block copolymers. Derivatives of the PLLA‐PEG block copolymers can form far more interesting nano‐architectures. An equimolar mixture of enantiomeric copolymers, PLLA‐PEG‐PLLA and PDLA‐PEG‐PDLA, forms a hydrogel that is thermo‐responsive. The terminal‐modified poly(L ‐lactide)‐block‐polyoxyethylene monocinnamate (PLLA‐PEG‐C) forms a highly stabilized nanofiber by the photo‐reaction of the cinnamates placed in the outer layer of the nanobands.     

Characterization and release of triptolide-loaded poly (d,l-lactic acid) nanoparticles

Triptolide (TP), which has immunosuppressive effect, anti-neoplastic activity, anti-fertility function and severe toxicities on digestive, urogenital, blood circulatory system, was used as a model drug in this study. TP-loaded poly (d,l-lactic acid) (PLA) nanoparticles were prepared by the modified spontaneous emulsification solvent diffusion method (modified-SESD method). Dynamic light scattering system (DLS), transmission electron microscope (TEM), atomic force microscopy (AFM), differential scanning calorimetry (DSC), X-ray powder diffractometry and Fourier transform infra-red spectroscopy (FT-IR) were employed to characterize the nanoparticles fabricated for size and size distribution, surface morphology, the physical state of drug in nanoparticles, and the interaction between the drug and polymer. Encapsulation efficiency (EE) and the in vitro release of TP in nanoparticles were measured by the reverse phase high-performance liquid chromatography (RP-HPLC). The produced nanoparticles exhibited a narrow size distribution with a mean size of approximately 150 nm and polydispersity index of 0.088. The morphology of the nanoparticles exhibited a fine spherical shape with smooth surfaces without aggregation or adhesion. TP-entrapped in nanoparticles was found in the form of amorphous or semicrystalline. It was found that a weak interaction existed between the drug and polymer. In all experiments, more than 65% of EE were obtained. The in vitro release profile of TP from nanoparticles exhibited a typical biphasic release phenomenon, namely initial burst release and consequently sustained release. In this case, the particle size played an important role for the drug release. The modified-SESD method was a potential and advantage method to produce an ideal polymer nanoparticles for drug delivery system (DDS).     

Synthesis and characterization of multiblock copolymers based on L‐lactic acid,citric acid,and poly(ethylene glycol)

Because poly(L ‐lactic acid) (PLLA) is a biodegradable polyester with low immunogenicity and good biocompatibility, it is used as a biomaterial. However, hydrophobic PLLA does not have any reactive groups. Thus, its application is limited. To increase the hydrophilicity of PLLA and accelerate its degradation rate, functionalized pendant groups and blocks were introduced through copolymerization with citric acid and poly(ethylene glycol) (PEG), respectively. This article describes the synthesis and characterization of poly(L ‐lactic‐co‐citric acid) (PLCA)‐PLLA and PLCA‐PEG multiblock copolymers. The results indicated that the hydrolysis rate was enhanced, and the hydrophilicity was improved because of the incorporation of carboxyl groups in PLCA‐PLLA. The joining of the PEG block led to improved hydrophilicity of PLCA, and the degradation rate of PLCA‐PEG accelerated as compared with that of PLCA‐PLLA. © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2073–2081, 2003     

Novel pentablock copolymer (PLA–PCL–PEG–PCL–PLA)-based nanoparticles for controlled drug delivery: effect of copolymer compositions on the crystallinity of copolymers and in vitro drug release profile from nanoparticles

The purpose of this investigation was to design novel pentablock copolymers (polylactide–polycaprolactone–polyethylene glycol–polycaprolactone–polylactide) (PLA–PCL–PEG–PCL–PLA) to prepare nanoparticle formulations which provide continuous delivery of steroids over a longer duration with minimal burst effect. Another purpose was to evaluate the effect of poly(l-lactide) (PLLA) and poly(d,l-lactide) (PDLLA) incorporation on crystallinity of pentablock copolymers and in vitro release profile of triamcinolone acetonide (selected as model drug) from nanoparticles. PLA–PCL–PEG–PCL–PLA copolymers with different block ratio of PCL/PLA segment were synthesized. Release of triamcinolone acetonide from nanoparticles was significantly affected by crystallinity of the copolymers. Burst release of triamcinolone acetonide from nanoparticles was significantly minimized with incorporation of proper ratio of PDLLA in the existing triblock (PCL–PEG–PCL) copolymer. Moreover, pentablock copolymer-based nanoparticles exhibited continuous release of triamcinolone acetonide. Pentablock copolymer-based nanoparticles can be utilized to achieve continuous near–zero-order delivery of corticosteroids from nanoparticles without any burst effect.     

Nanocomposites of poly(l-lactide) and surface-grafted TiO2 nanoparticles: Synthesis and characterization

A new method of surface modification of TiO₂ nanoparticles by surface-grafting l-lactic acid oligomer was developed. The surface-grafting reaction was evaluated by Fourier transformation infrared (FTIR) and thermal gravimetric analysis (TGA). The results showed that l-lactic acid oligomer could be easily grafted onto the TiO₂ nanoparticles surface in the presence of stannous octanoate and the highest amount of grafted polymer was about 8.5% in weight. Transmission electron microscopy (TEM) and scanning electron microscopy (SEM) results showed that grafted TiO₂ (g-TiO₂) in chloroform or PLLA matrix approximated to uniform, while unmodified TiO₂ nanoparticles tended to aggregate. The tensile strength of this material was greatly improved by the addition of g-TiO₂ nanoparticles in poly(l-lactide) (PLLA) matrix. The tensile strength of the g-TiO₂/PLLA nanocomposite containing 5 wt.% of g-TiO₂ was 72 MPa, which was 23.1% higher than that of pure PLLA. Even though the incorporation of the TiO₂ nanoparticles into PLLA led to the deterioration of its elongation at break, the g-TiO₂/PLLA nanocomposite also exhibited better ductility than that of TiO₂/PLLA nanocomposite.     

Preparation and characterization of biodegradable nanoparticles based on amphiphilic poly(3-hydroxybutyrate)-poly(ethylene glycol)-poly(3-hydroxybutyrate) triblock copolymer

Amphiphilic triblock copolymers of poly(3-hydroxybutyrate)-poly(ethylene glycol)-poly(3-hydroxybutyrate) (PHB-PEG-PHB) were directly synthesized by the ring-opening copolymerization of β-butyrolactone monomer using PEG as macroinitiator. Their structure, thermal properties and crystallization were investigated by ¹H NMR, differential scanning calorimetry (DSC) and X-ray diffraction. It was found that both PHB and PEG blocks were miscible. With the increase in the PHB block length, the triblock copolymers became amorphous because amorphous PHB block remarkably depressed the crystallization of the PEG block. Biodegradable nanoparticles with core-shell structure were prepared in aqueous solution from the amphiphilic triblock copolymers, and characterized by ¹H NMR, SEM and fluorescence. The hydrophobic PHB segments formed the central solid-like core, and stabilized by the hydrophilic PEG block. The nanoparticle size was close related to the initial concentrations of the nanoparticle dispersions and the compositions of the triblock copolymers. Moreover, the PHB-PEG-PHB nanoparticles also showed good drug loading properties, which suggested that they were very suitable as delivery vehicles for hydrophobic drugs.     

Preparation, characterization and application of pyrene-loaded methoxy poly(ethylene glycol)–poly(lactic acid) copolymer nanoparticles

Pyrene-loaded biodegradable polymer nanoparticles were prepared by incorporating pyrene into the polymer nanoparticles formulated from amphiphilic diblock copolymer, methoxy poly(ethylene glycol)–poly(lactic acid) (MePEG–PLA). Their morphological structure and physical properties were characterized by nuclear magnetic resonance (NMR), dynamic light scattering, fluorescence spectroscopy, transmission electronic microscopy and zeta potential measurements. Further, MePEG–PLA nanoparticles containing pyrene as fluorescent marker were administered intranasally to rats, and the distribution of nanoparticles in the nasal mucosa and the olfactory bulb were visualized by fluorescence microscopy. NMR results confirmed that MePEG–PLA copolymer can form nanoparticles in water, and hydrophilic PEG chains were located on the surface of the nanoparticles. The particle size, zeta potential and pyrene loading efficiency of MePEG–PLA nanoparticles were dependent on the PLA block content in the copolymer. Following nasal administration, the absorption of nanoparticles across the epithelium was rapid, with fluorescence observed in the olfactory bulb at 5 min, and a higher level of fluorescence persisted in the olfactory mucosa than that in the respiratory mucosa. These results show that pyrene could serve as a useful fluorescence probe for incorporation into polymer nanoparticles to study tissue distribution and MePEG–PLA nanoparticles might have a great potential as carriers of hydrophobic drugs.     

Synthesis of poly(ethylene glycol)/polypeptide/poly(D,L‐lactide) copolymers and their nanoparticles

Core‐shell structured nanoparticles of poly(ethylene glycol) (PEG)/polypeptide/poly(D ,L ‐lactide) (PLA) copolymers were prepared and their properties were investigated. The copolymers had a poly(L ‐serine) or poly(L ‐phenylalanine) block as a linker between a hydrophilic PEG and a hydrophobic PLA unit. They formed core‐shell structured nanoparticles, where the polypeptide block resided at the interface between a hydrophilic PEG shell and a hydrophobic PLA core. In the synthesis, poly(ethylene glycol)‐b‐poly(L ‐serine) (PEG‐PSER) was prepared by ring opening polymerization of N‐carboxyanhydride of O‐(tert‐butyl)‐L ‐serine and subsequent removal of tert‐butyl groups. Poly(ethylene glycol)‐b‐poly(L ‐phenylalanine) (PEG‐PPA) was obtained by ring opening polymerization of N‐carboxyanhydride of L ‐phenylalanine. Methoxy‐poly(ethylene glycol)‐amine with a MW of 5000 was used as an initiator for both polymerizations. The polymerization of D ,L ‐lactide by initiation with PEG‐PSER and PEG‐PPA produced a comb‐like copolymer, poly(ethylene glycol)‐b‐[poly(L ‐serine)‐g‐poly(D ,L ‐lactide)] (PEG‐PSER‐PLA) and a linear copolymer, poly(ethylene glycol)‐b‐poly(L ‐phenylalanine)‐b‐poly(D ,L ‐lactide) (PEG‐PPA‐PLA), respectively. The nanoparticles obtained from PEG‐PPA‐PLA showed a negative zeta potential value of ?16.6 mV, while those of PEG‐PSER‐PLA exhibited a positive value of about 19.3 mV. In pH 7.0 phosphate buffer solution at 36 °C, the nanoparticles of PEG/polypeptide/PLA copolymers showed much better stability than those of a linear PEG‐PLA copolymer having a comparable molecular weight. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011