Controlling grafting density and side chain length in poly(n‐butyl acrylate) by ATRP copolymerization of macromonomers

Atom transfer radical polymerization (ATRP) was used for the preparation and subsequent copolymerization of two acryloyl‐terminated poly(n‐butyl acrylate) macromonomers with different degrees of polymerization (DP_nBA = 25 and 42). Homopolymerization of the higher molecular weight macromonomer ( MM1 ; PnBA₄₂‐A, M_n = 5600, DP_MM = 42, M_w/M_n = 1.18) resulted in preparation of a densely grafted polymer with a narrow molecular weight distribution (M_w/M_n = 1.14), but with the limited degree of polymerization DP = 12. The ultimate degree of homopolymerization for the lower molecular weight macromonomer ( MM2 ; PnBA₂₅‐A, M_n = 3400, DP_MM = 25, M_w/M_n = 1.20) was higher, and DP increased from 12 to 22. The limited DP could be because of progressively increasing steric congestion for macromonomers in approaching the growing chain ends of densely grafted polymers. When MMs were copolymerized with nBA, the reactivity of MM was nearly the same as that of nBA monomer irrespective of the differences in the degree of polymerization of the MMs and the initial molar ratio of nBA to MM. Well‐defined graft polymers with different lengths of backbone and side chains, and different graft density were successfully prepared by “grafting through” ATRP. Tadpole‐shaped and dumbbell‐shaped graft polymers were also synthesized by ATRP. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 5454–5467, 2006     

Polymethylene‐block‐polystyrene copolymers: A new synthetic approach using a combination of polyhomologation and reversible addition‐fragmentation chain‐transfer polymerization and their microfibers and microspheres fabricated through electrospinning process

Well‐defined polymethylene‐block‐polystyrene (PM‐b‐PS) diblock copolymers were synthesized via a combination of polyhomologation of ylides and reversible addition‐fragmentation chain‐transfer (RAFT) polymerization of styrene. Trithiocarbonate‐terminated polymethylenes (PM‐TTCB) (M_n = 1400 g mol^?1; M_w/M_n = 1.09 and M_n = 2100 g mol^?1; M_w/M_n = 1.20) were obtained via an esterification of S?1‐dodecyl‐S′‐(α,α′‐dimethyl‐α″‐acetate) trithiocarbonate with hydroxyl‐terminated polymethylene synthesized via polyhomologation of ylides followed by oxidation. Then, a series of PM‐b‐PS (M_n = 5500–34,000 g mol^?1; M_w/M_n = 1.12–1.25) diblock copolymers were obtained by RAFT polymerization of styrene using PM‐TTCB as a macromolecular chain‐transfer agent. The chain structures of all the polymers were characterized by proton nuclear magnetic resonance (¹H NMR), gel permeation chromatography, and Fourier transform infrared spectroscopy. The thiocarbonylthio end‐group of PM‐b‐PS was transformed into thiol group by aminolysis and confirmed by UV–vis spectroscopy. In addition, microfibers and microspheres of such diblock copolymers were fabricated by electrospinning process and observed by scanning electron microscopy (SEM). © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013, 51, 2892–2899     

Well‐defined amphiphilic polymethylene‐b‐poly(acrylic acid) diblock copolymers: New synthetic strategy and their self‐assembly

Well‐defined amphiphilic polymethylene‐b‐poly (acrylicacid) diblock copolymers have been synthesized via a new strategy combining polyhomologation and atom transfer radical polymerization (ATRP). Hydroxyl‐terminated polymethylenes (PM‐OH) with different molecular weights and narrow molecular weight distribution are obtained through the polyhomologation of dimethylsulfoxonium methylides following quantitative oxidation via trimethylamine‐N‐oxide dihydrate. Subsequently, polymethylene‐based macroinitiators (PM‐MIs M_n = 1,300 g mol^?1 [M_w/M_n = 1.11] and M_n = 3,300 g mol^?1 [M_w/M_n = 1.04]) are synthesized by transformation of terminal hydroxyl group of PM‐OH to α‐haloester in ～100% conversion. ATRPs of tert‐butyl acrylate (t‐BuA) are then carried out using PM‐MIs as initiator to construct PM‐b‐P(t‐BuA) diblock copolymers with controllable molecular weight (M_n = 8,800–15,800 g mol^?1 M_w/M_n = 1.04–1.09) and different weight ratio of PM/P(t‐BuA) segment (1:1.7–1:11.2). The amphiphilic PM‐b‐PAA diblock copolymers are finally prepared by hydrolysis of PM‐b‐P(t‐BuA) copolymers and their self‐assembly behavior in water is preliminarily investigated via the determination of critical micelle concentrations, dynamic light scattering, and transmission electron microscope (TEM). © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Glycoconjugated polymer: Synthesis and characterization of poly(vinyl saccharide)‐block‐polystyrene‐block‐poly(vinyl saccharide) as an amphiphilic ABA triblock copolymer

Styrene (St) was polymerized with α,α′‐bis(2′,2′,6′,6′‐tetramethyl‐1′‐piperidinyloxy)‐1,4‐diethylbenzene ( 1 ) as an initiator (bulk, [St]/] 1 ] = 570) at 120 °C for 5.0 h to obtain polystyrene having 2,2,6,6‐tetramethylpiperidiloxy moieties on both sides of the chain ends ( 2 ) with a number‐average molecular weight (M_n) of 14,300 and a polydispersity index [weight‐average molecular weight/number‐average molecular weight (M_w/M_n)] of 1.14. 4‐Vinylbenzyl glucoside peracetate ( 3a ) was polymerized with 2 as a macromolecular initiator and dicumyl peroxide (DCP) as an accelerator in chlorobenzene at 120 °C. The polymerization with the [ 3a ]/[ 2 ]/[DCP] ratio of 30/1/1.2 for 5 h afforded a product in a yield of 73%; it was followed by purification with preparative size exclusion chromatography to provide the ABA triblock copolymer containing the pendant acetyl glucose on both sides of the chain ends ( 4a ; M_n = 21,000, M_w/M_n = 1.16). Similarly, the polymerization of 4‐vinylbenzyl maltohexaoside peracetate produced the ABA triblock copolymer containing the pendant acetyl maltohexaose on both side of the chain end ( 4b ; M_n = 31,800, M_w/M_n = 1.11). Polymers 4a and 4b were modified by deacetylation into amphiphilic ABA triblock copolymers containing the pendant glucose and maltohexaose as hydrophilic segment, 5a and 5b , respectively. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 3978–3985, 2006     

Influence of Sequential Modifications and Carbohydrate Variations in Synthetic AFGP Analogues on Conformation and Antifreeze Activity

Certain Arctic and Antarctic ectotherm species have developed strategies for survival under low temperature conditions that, among others, consist of antifreeze glycopeptides (AFGP). AFGP form a class of biological antifreeze agents that exhibit the ability to inhibit ice growth in vitro and in vivo and, hence, enable life at temperatures below the freezing point. AFGP usually consist of a varying number of (Ala‐Ala‐Thr)_n units (n=4–55) with the disaccharide β‐D ‐galactosyl‐(1→3)‐α‐N‐acetyl‐D ‐galactosamine glycosidically attached to every threonine side chain hydroxyl group. AFGP have been shown to adopt polyproline II helical conformation. Although this pattern is highly conserved among different species, microheterogeneity concerning the amino acid composition usually occurs; for example, alanine is occasionally replaced by proline in smaller AFGP. The influence of minor and major sequence mutations on conformation and antifreeze activity of AFGP analogues was investigated by replacement of alanine by proline and glycosylated threonine by glycosylated hydroxyproline. The target compounds were prepared by using microwave‐enhanced solid phase peptide synthesis. Furthermore, artificial analogues were obtained by copper‐catalyzed azide–alkyne cycloaddition (CuAAC): propargyl glycosides were treated with polyproline helix II‐forming peptides comprising (Pro‐Azp‐Pro)_n units (n=2–4) that contained 4‐azidoproline (Azp). The conformations of all analogues were examined by circular dichroism (CD). In addition, microphysical analysis was performed to provide information on their inhibitory effect on ice recrystallization.     

Styrene‐vinylferrocene random and block copolymers by TEMPO‐mediated radical polymerization

TEMPO‐mediated free radical polymerization was employed for homo‐ and copolymerization of vinylferrocene (Vfc). Homopolymerization of Vfc resulted in relatively narrow polydispersities (M_w/M_n = 1.24–1.8), however, molecular weights were limited to 4 800. Copolymerization with styrene afforded random copolymers with molecular weights (M_n) up to 10 000, narrow polydispersity (1.2 > M_w/M_n > 1.4) and up to 42 mol‐% Vfc. Block copolymers with PS block and P(S‐co‐Vfc) block with molecular weights (M_n) in the range of 9 000 to 17 600 (M_w/M_n > 1.3) were also prepared with up to 17 mol‐% vinylferrocene. DSC revealed two glass transition temperatures (T_g) evidencing phase separation.     

Synthesis and polymerization of N‐(4‐tetrahydropyranyl‐oxyphenyl)maleimide

N‐(4‐Tetrahydropyranyl‐oxy‐phenyl)maleimide (THPMI) was prepared and polymerized by radical or anionic initiators. THPMI could be polymerized by 2,2′‐azobis(isobutyronitrile) (AIBN) and potassium tert‐butoxide. Radical polymers (poly(THPMI)r) were obtained in 15–50% yields for AIBN in THF at 65°C after 2–5 h. The yield of anionic polymers (poly(THPMI)a) obtained from potassium tert‐butoxide in THF at 0°C after 20 h was 91%. The molecular weights of poly(THPMI)r and poly(THPMI)a were M_n = 2750–3300 (M_w/M_n = 1.2–3.3) and M_n = 11300 (M_w/M_n = 6.0), respectively. The difference in molecular weights of the polymers was due to the differences in the termination mechanism of polymerization and the solubility of these polymers in THF. The thermal decomposition temperatures were 205 and 365°C. The first decomposition step was based on elimination of the tetrahydropyranyl group from the poly(THPMI). Positive image patterns were obtained by chemical amplification of positive photoresist composed of poly(THPMI) and 4‐morpholinophenyl diazonium trifluoromethanesulfonate used as an acid generator. © 1999 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 37: 341–347, 1999     

Synthesis of well‐defined amphiphilic polymethylene‐b‐poly(ε‐caprolactone)‐b‐poly(acrylic acid) triblock copolymer via a combination of polyhomologation,ring‐opening polymerization,and atom transfer radical polymerization

Well‐defined amphiphilic polymethylene‐b‐poly(ε‐caprolactone)‐b‐poly(acrylic acid) (PM‐b‐PCL‐b‐PAA) triblock copolymers were synthesized via a combination of polyhomologation, ring‐opening polymerization (ROP), and atom transfer radical polymerization (ATRP). First, hydroxyl‐terminated polymethylenes (PM‐OH; M_n = 1100 g mol^?1; M_w/M_n = 1.09) were produced by polyhomologation followed by oxidation. Then, the PM‐b‐PCL (M_n = 10,000 g mol^?1; M_w/M_n = 1.27) diblock copolymers were synthesized via ROP of ε‐caprolactone using PM‐OH as macroinitiator and stannous octanoate (Sn(Oct)₂) as a catalyst. Subsequently, the macroinitiator transformed from PM‐b‐PCL in high conversion initiated ATRPs of tert‐butyl acrylate (^tBA) to construct PM‐b‐PCL‐b‐P^tBA triblock copolymers (M_n = 11,000–14,000 g mol^?1; M_w/M_n = 1.24–1.26). Finally, the PM‐b‐PCL‐b‐PAA triblock copolymers were obtained via the hydrolysis of the P^tBA segment in PM‐b‐PCL‐b‐P^tBA triblock copolymers. The chain structures of all the polymers were characterized by gel permeation chromatography, proton nuclear magnetic resonance, and Fourier transform infrared spectroscopy. Porous films of such triblock copolymers were fabricated by static breath‐figure method and observed by scanning electron microscope. The aggregates of PM‐b‐PCL‐b‐PAA triblock copolymer were studied by transmission electron microscope. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Synthesis of arborescent polystyrene by “click” grafting

A method was developed for the synthesis of arborescent polystyrene by “click” coupling. Acetylene functionalities were introduced on linear polystyrene (M_n = 5300 g/mol, M_w/M_n = 1.05) by acetylation and reaction with potassium hydroxide, 18‐crown‐6 and propargyl bromide in toluene. Polymerization of styrene with 6‐tert‐butyldimethylsiloxyhexyllithium yielded polystyrene (M_n = 5200 g/mol, M_w/M_n = 1.09) with a protected hydroxyl chain end. Deprotection, followed by conversions to tosyl and azide functionalities, provided the side chain material. Coupling with CuBr and N,N,N′,N″,N″‐pentamethyldiethylenetriamine proceeded in up to 94% yield. Repetition of the grafting cycles led to well‐defined (M_w/M_n ≤ 1.1) polymers of generations G1 and G2 in 84% and 60% yield, respectively, with M_n and branching functionalities reaching 2.8 × 10⁶ g/mol and 460, respectively, for the G2 polymer. Coupling longer (M_n = 45,000 g/mol) side chains with acetylene‐functionalized substrates was also examined. For a linear substrate, a G0 polymer with M_n = 4.6 × 10⁵ g/mol and M_w/M_n = 1.10 was obtained in 87% yield; coupling with the G0 (M_n = 52,000 g/mol) substrate produced a G1 polymer (M_n = 1.4×10⁶ g/mol, M_w/M_n = 1.38) in 28% yield. The complementary approach using azide‐functionalized substrates and acetylene‐terminated side chains was also investigated, but proceeded in lower yield. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 1730–1740     

Synthesis,structure, and property of well‐defined polymethylene‐based diblock copolymers by a combination of living polymerization of ylides and atom transfer radical polymerization

A combination of living polymerization of ylides and atom transfer radical polymerization (ATRP) was used successfully in the design and synthesis of well‐defined polymethylene‐b‐poly(methyl methacrylate) (PM‐b‐PMMA) and polymethylene‐b‐poly(n‐butyl acrylate) (PM‐b‐Pn‐BuA). Tripolymethylene borane were firstly synthesized by living polymerization of dimethylsulfoxonium methylides and then oxidated quantitatively through trimethylamine‐N‐oxide dihydrate to provide a series of low‐polydispersity hydroxyl‐terminated polymethylenes (PM‐OHs) with different molecular weight. Subsequently, such polymers were converted into polymethylene‐based macroinitiators (PM‐MIs, M_n(GPC) = 1900–10,400 g/mol; M_w/M_n = 1.12–1.23) in ～100% conversion. ATRPs of methyl methacrylate and n‐butyl acrylate were successfully conducted using PM‐MI to produce well‐defined diblock copolymers of PM‐b‐PMMA and PM‐b‐Pn‐BuA, respectively. The GPC traces indicated the successful extension of PMMA and Pn‐BuA segment (M_n(GPC) of PM‐b‐PMMA = 3980–10,100 g/mol; M_w/M_n = 1.16–1.22; M_n of PM‐b‐Pn‐BuA = 7400–9200 g/mol; M_w/M_n = 1.14–1.18). Atomic force microscopy (AFM) was used to characterize the structures of the precipitated PM‐b‐PMMA micelles, which were formed in toluene. The blend of LDPE/PMMA was prepared with PM‐b‐PMMA as compatibilizer. The scanning electron microscopy (SEM) results showed that the compatibilization of the LDPE/PMMA was improved greatly by the incorporation of PM‐b‐PMMA. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5671–5681, 2009     

Novel,biodegradable, functional poly(ester‐carbonate)s by copolymerization of trans‐4‐hydroxy‐L‐proline with cyclic carbonate bearing a pendent carboxylic group

Water‐soluble poly(ester‐carbonate) having pendent amino and carboxylic groups on the main‐chain carbon is reported for the first time. This article describes the melt ring‐opening/condensation reaction of trans‐4‐hydroxy‐N‐benzyloxycarbonyl‐L ‐proline (N‐CBz‐Hpr) with 5‐methyl‐5‐benzyloxycarbonyl‐1,3‐dioxan‐2‐one (MBC) at a wide range of molar fractions. The influence of reaction conditions such as catalyst concentration, polymerization time, and temperature on the number average molecular weight (M_n) and molecular weight distribution (M_w/M_n) of the copolymers was investigated. The polymerizations were carried out in bulk at 110 °C with 3 wt % stannous octoate as a catalyst for 16 h. The poly(ester‐carbonate)s obtained were characterized by Fourier transform infrared spectroscopy, ¹H NMR, differential scanning calorimetry, and gel permeation chromatography. The copolymers synthesized exhibited moderate molecular weights (M_n = 6000–14,700 g mol^?1) with reasonable molecular weight distributions (M_w/M_n = 1.11–2.23). The values of the glass‐transition temperature (T_g) of the copolymers depended on the molar fractions of cyclic carbonate. When the MBC content decreased from 76 to 12 mol %, the T_g increased from 16 to 48 °C. The relationship between the poly(N‐CBz‐Hpr‐co‐MBC) T_g and the compositions was in approximation with the Fox equation. In vitro degradation of these poly(N‐CBz‐Hpr‐co‐MBC)s was evaluated from weight‐loss measurements and the change of M_n and M_w/M_n. Debenzylation of 3 by catalytic hydrogenation led to the corresponding linear poly(ester‐carbonate), 4 , with pendent amino and carboxylic groups. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 2303–2312, 2004     

Synthesis of poly(p‐phenylene) macromonomers and multiblock copolymers

Rigid‐rod poly(4′‐methyl‐2,5‐benzophenone) macromonomers were synthesized by Ni(0) catalytic coupling of 2,5‐dichloro‐4′‐methylbenzophenone and end‐capping agent 4‐chloro‐4′‐fluorobenzophenone. The macromonomers produced were labile to nucleophilic aromatic substitution. The molecular weight of poly(4′‐methyl‐2,5‐benzophenone) was controlled by varying the amount of the end‐capping agent in the reaction mixture. Glass‐transition temperatures of the macromonomers increased with increasing molecular weight and ranged from 117 to 213 °C. Substitution of the macromonomer end groups was determined to be nearly quantitative by ¹H NMR and gel permeation chromatography. The polymerization of a poly(4′‐methyl‐2,5‐benzophenone) macromonomer [number‐average molecular weight (M_n) = 1.90 × 10³ g/mol; polydispersity (M_w)/M_n = 2.04] with hydroxy end‐capped bisphenol A polyaryletherketone (M_n = 4.50 × 10³ g/mol; M_w/M_n = 1.92) afforded an alternating multiblock copolymer (M_n = 1.95 × 10⁴ g/mol; M_w/M_n = 6.02) that formed flexible, transparent films that could be creased without cracking. © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3505–3512, 2001     

Synthesis of star‐shaped polystyrenes via nitroxide‐mediated stable free‐radical polymerization

High molecular weight star‐shaped polystyrenes were prepared via the coupling of 2,2,6,6‐tetramethyl‐1‐piperidinyloxy (TEMPO) terminated polystyrene oligomers with divinylbenzene (DVB) in m‐xylene at 138 °C. The optimum ratio of the coupling solvent (m‐xylene) to divinylbenzene was determined to be 9 to 1 based on volume. Linear polystyrene oligomers (M_n = 19,300 g/mol, M_w/M_n = 1.10) were prepared in bulk styrene using benzoyl peroxide in the presence of TEMPO at approximately 130 °C under an inert atmosphere. Coupling of the TEMPO‐terminated oligomers under optimum conditions resulted in a product with a number average molecular weight exceeding 300,000 g/mol (M_w/M_n = 3.03) after 24 h, suggesting the formation of relatively well‐defined star‐shaped polymers. Additionally, the intrinsic viscosities of the star‐shaped products were lower than calculated values for linear analogs of equivalent molecular weight, which further supported the formation of a star‐shaped architecture. © 2000 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 216–223, 2001     

Synthesis of well‐defined AB20‐type star polymers with cyclodextrin‐core by combination of NMP and ATRP

The synthesis of an AB₂₀‐type heteroarm star polymer consisting of a polystyrene arm and 20‐arms of poly(methyl methacrylate) or poly(tert‐butyl acrylate) was carried out using the combination of nitroxide‐mediated polymerization (NMP) and atom transfer radical polymerization (ATRP). The NMP of styrene was carried out using mono‐6‐[4‐(1′‐(2″,2″,6″,6″‐tetramethyl‐1″‐piperidinyloxy)‐ethyl)benzamido]‐β‐cyclodextrin peracetate ( 1 ) to afford end‐functionalized polystyrene with an acetylated β‐cyclodextrin (β‐CyD) unit (prepolymer 2 ) with a number‐average molecular weight (M_n) of 11700 and a polydispersity (M_w/M_n) of 1.17. After deacetylation of prepolymer 2 , the resulting polymer was reacted with 2‐bromoisobutyric anhydride to give end‐functionalized polystyrene with 20(2‐bromoisobutyrol)s β‐CyD, macroinitiator 4 . The copper (I)‐mediated ATRP of methyl methacrylate (MMA) and tert‐butyl acrylate (tBA) was carried out using macroinitiator 4 . The resulting polymers were isolated by SEC fractionation to produce AB₂₀‐type star polymers with a β‐CyD‐core, 5 . The well‐defined structure of 5 with weight‐average molecular weight (M_w)s of 13,500–65,300 and M_w/M_n's of 1.26–1.28 was demonstrated by SEC and light scattering measurements. The arm polymers were separated from 5 by destruction with 28 wt % sodium methoxide in order to analyze the details of their characteristic structure. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 4271–4279, 2005     

Microwave‐improved polymerization of ϵ‐caprolactone initiated by carboxylic acids

The ring‐opening polymerization of ε‐caprolactone (ε‐CL), initiated by carboxylic acids such as benzoic acid and chlorinated acetic acids under microwave irradiation, was investigated; with this method, no metal catalyst was necessary. The product was characterized as poly(ε‐caprolactone) (PCL) by ¹H NMR spectroscopy, Fourier transform infrared spectroscopy, ultraviolet spectroscopy, and gel permeation chromatography. The polymerization was significantly improved under microwave irradiation. The weight‐average molecular weight (M_w) of PCL reached 44,800 g/mol, with a polydispersity index [weight‐average molecular weight/number‐average molecular weight (M_w/M_n)] of 1.6, when a mixture of ε‐CL and benzoic acid (25/1 molar ratio) was irradiated at 680 W for 240 min, whereas PCL with M_w = 12,100 and M_w/M_n = 4.2 was obtained from the same mixture by a conventional heating method at 210 °C for 240 min. A degradation of the resultant PCL was observed during microwave polymerization with chlorinated acetic acids as initiators, and this induced a decrease in M_w of PCL. However, the degradation was hindered by benzoic acid at low concentrations. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 13–21, 2003     

Cobalt‐mediated radical polymerization routes to poly(vinyl ester) block copolymers

Cobalt‐mediated radical polymerizations (CMRPs) utilizing redox initiation are demonstrated to produce poly(vinyl ester) homopolymers derived from vinyl pivalate (VPv) and vinyl benzoate (VBz), and their block copolymers with vinyl acetate (VAc). Combining anhydrous Co(acac)₂, lauroyl peroxide, citric acid trisodium salt, and VPv at 30 °C results in controlled polymerizations that yield homopolymers with M_n = 2.5–27 kg/mol with M_w/M_n = 1.20–1.30. Homopolymerizations of scrupulously purified VBz proceed with lower levels of control as evidenced by broader polydispersities over a range of molecular weights (M_n = 4–16 kg/mol; M_w/M_n = 1.34–1.65), which may be interpreted in terms of the decreased nucleophilicity of these less electron donating propagating polymer chain ends. Based on these results, we demonstrate that sequential CMRP reactions present a viable route to microphase separated poly(vinyl ester) block copolymers as shown by small‐angle X‐ray scattering analyses. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Polymer grafting onto polyurethane backbone via Diels–Alder reaction

The aliphatic polyurethane with pendant anthracene moieties (PU‐anthracene) was prepared from polycondensation of anthracen‐9‐yl methyl 3‐hydroxy‐2‐(hydroxymethyl)‐2‐methylpropanoate (anthracene diol), 1 with hexamethylenediisocyanate in the presence of dibutyltindilaurate in CH₂Cl₂ at room temperature for 10 days. Thereafter, the PU‐anthracene (M_n,GPC = 12,900 g/mol, M_w/M_n = 1.87, relative to PS standards) was clicked with a linear α‐furan protected‐maleimide terminated‐poly(methyl methacrylate) (PMMA‐MI) (M_n,GPC = 2500 g/mol, M_w/M_n = 1.33), or ‐poly(ethylene glycol) (PEG‐MI) (M_n,GPC = 550 g/mol, M_w/M_n = 1.09), to result in well‐defined PU‐graft copolymers, PU‐g‐PMMA (M_n,GPC = 23800 g/mol, M_w/M_n = 1.65, relative to PS standards) or PU‐g‐PEG (M_n,GPC = 11,600 g/mol, M_w/M_n = 1.45, relative to PS standards) using Diels–Alder reaction in dioxane/toluene at 105 °C. The Diels–Alder grafting efficiencies were found to be over 93–99% using UV spectroscopy. Moreover, the structural analyses and the thermal transitions of all copolymers were determined via ¹H NMR and DSC, respectively. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 521–527     

Alkoxyamine‐mediated “living” radical polymerization: MS investigation of the early stages of styrene polymerization initiated by cumyl‐TEISO

A new series of 1,1,3,3‐tetraethylisoindoline‐2‐oxyl (TEISO)‐based alkoxyamines was prepared. The half‐lives for thermal dissociation indicated that the most sterically congested cumyl‐TEISO alkoxymine had the greatest potential as an initiator for the polymerization of monomers at lower temperatures. The polymerization of styrene at 110 °C gave a linear evolution of M_n with conversion in the early stages. Further evidence for the “living” nature was given by the polydispersities of the polymers that remained low (M_w/M_n = 1.13–1.27) throughout the polymerization (up to 80% conversion). No polymer was formed for the styrene system in a reasonable time below 100 °C. High‐performance liquid chromatographic/mass spectrometric investigations of the distribution of trapped oligomers containing one to nine monomer units formed at 60 °C revealed that the trapping of oligomeric cumyl–styryl radicals by TEISO is irreversible at this temperature. Methyl methacrylate polymerized with cumyl‐TEISO at 60–70 °C, although the initial high rates of polymerization soon decreased to zero at low conversions (10–15%), and the high polydispersities (M_w/M_n = 1.42–1.73) indicated significant side reactions. © 2001 John Wiley & Sons, Inc. J Polym Sci A: Polym Chem 39: 1232–1241, 2001     

Junction‐Controlled Topological Polymerization

Methodology that enables the controlled synthesis of linear and branched polymers from an identical monomer will be a novel pathway for polymer synthesis and processing. Herein we first describe the control of one or both of the C(3)‐C(3′) and C(6)‐C(6′) coupling reactions of carbazolyl. In a second approach, an identical monomer containing two carbazolyls is polymerized using chemical and electrochemical oxidizers, leading to topologically controllable growth of linear polymers in weak oxidizer or of cross‐linked polymer chains in strong oxidizer, with satisfactory long chain propagation of step growth polymerization (M_n=6.0×10⁴ g mol^?1, M_w/M_n=2.3). This very simple polymerization with cheap reagents and low levels of waste has provided a flexible pathway for synthesis and processing of polymers.     

ATNRC and SET‐NRC synthesis of PtBA‐g‐PEO well‐defined amphiphilic graft copolymers

A series of new well‐defined amphiphilic graft copolymers containing hydrophobic poly(tert‐butyl acrylate) backbone and hydrophilic poly(ethylene oxide) side chains were reported. Reversible addition‐fragmentation chain transfer homopolymerization of tert‐butyl 2‐((2‐bromopropanoyloxy)methyl)acrylate was first performed to afford a well‐defined backbone with a narrow molecular weight distribution (M_w/M_n = 1.07). The target poly(tert‐butyl acrylate)‐g‐poly(ethylene oxide) (PtBA‐g‐PEO) graft copolymers with low polydispersities (M_w/M_n = 1.18–1.26) were then synthesized by atom transfer nitroxide radical coupling or single electron transfer‐nitroxide radical coupling reaction using CuBr(Cu)/PMDETA as catalytic system. Fluorescence probe technique was employed to determine the critical micelle concentrations (cmc) of the obtained amphiphilic graft copolymers in aqueous media. Furthermore, PAA‐g‐PEO graft copolymers were obtained by selective acidic hydrolysis of hydrophobic PtBA backbone while PEO side chains kept inert. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012