Sulfonated poly(arylene thioether phosphine oxide)s copolymers for proton exchange membrane fuel cells

High molecular weight sulfonated poly(arylene thioether phosphine oxide)s (sPATPO) with various sulfonation degrees were prepared directly by aromatic nucleophilic polycondensation of 4,4′-thiobisbenzenethiol with sulfonated bis(4-fluorophenyl) phenyl phosphine oxide and bis(4-fluorophenyl) phenyl phosphine oxide. sPATPO in the acid form with sulfonation degrees of 60–100% exhibits a glass transition temperature higher than 230 °C and a 5% weight loss temperature above 400 °C, indicating high thermal stability. sPATPO with a high sulfonation degree shows high proton conductivity and good resistance to swelling as well. For instance, sPATPO-70 displays the conductivity of 0.0783 S/cm and a swelling ratio of 11.6% at 90 °C. TEM micrographs showed that sPATPO membranes with a high sulfonation degree could form continuous ion channels, which are favorable for improving the proton conductivity but harmful to remaining the mechanical property. The membranes are expected to show good performances in fuel cell applications.     

含全氟联苯结构的磺化聚二氮杂萘酮醚氧膦质子交换膜的制备与性能

将全氟联苯、 二(4-氟苯基)苯基氧膦与4-(4′-羟基)苯基-2,3-二氮杂萘酮共聚, 合成了含全氟联苯结构的聚二氮杂萘酮醚氧膦, 再经磺化反应, 制备了含全氟联苯结构的磺化聚二氮杂萘酮醚氧膦(sPEPOF-x, x为含氟重复单元的摩尔分数)质子交换膜. 由于强疏水全氟联苯结构促进了聚合物膜的亲水/疏水微相分离, 提高了质子电导率, 降低了溶胀率, sPEPOF质子交换膜表现出优良的综合性能. 在80 ℃下, sPEPOF-25质子交换膜的溶胀率仅为10%, 约为Nafion 117的一半, 而其电导率为0.099 S/cm, 约为Nafion 117的1.2倍, 且耐氧化稳定性好, 热稳定性高, 具有潜在的应用前景.     

Locally sulfonated poly(ether sulfone)s with highly sulfonated units as proton exchange membrane

Novel locally sulfonated poly(ether sulfone)s with highly sulfonated units were successfully synthesized for fuel cell applications. Poly(ether sulfone)s were prepared by the nucleophilic substitution of bis(4‐fluorophenyl) sulfone with 1,2,4,5‐tetrakis([1,1′‐biphenyl]‐2‐oxy)‐3,6‐bis(4‐hydroxyphenoxy)benzene and bis(4‐hydroxyphenyl) sulfide, followed by oxidation using m‐chloroperoxybenzoic acid. The desired highly sulfonated units were easily introduced by postsulfonation and each one had ten sulfonic acid groups. The sulfonated polymers gave tough, flexible, and transparent membranes by solvent casting. The high contrast in polarity between highly sulfonated units and hydrophobic poly(ether sulfone) units enabled the formation of defined phase‐separated structures and well‐connected proton paths. The sulfonated polymers exhibited excellent proton conductivity over a wide range of relative humidities. The proton conductivity of the sulfonated polymer with an ion exchange capacity value of 2.38 mequiv/g was comparable to that of Nafion 117 even at 30% relative humidity. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3444–3453, 2009     

Direct copolymerization of sulfonated poly(phthalazinone arylene ether)s for proton‐exchange‐membrane materials

Sulfonated poly(phthalazinone ether ketone) (SPPEK) copolymers and sulfonated poly(phthalazinone ether sulfone) (SPPES) copolymers containing pendant sodium sulfonate groups were prepared by direct copolymerization. The reaction of disodium 3,3′‐disulfonate‐4,4′‐difluorobenzophenone (SDFB‐Na), 4,4′‐difluorobenzophenone (DFB), and 4‐(4‐hydroxyphenyl)‐1(2H)‐phthalazinone (DHPZ) at 170 °C in N‐methyl‐2‐pyrrolidione containing anhydrous potassium carbonate gave SPPEKs. SPPESs were similarly obtained with 3,3′‐disulfonate‐4,4′‐difluorophenyl sulfone, 4‐fluorophenyl sulfone (DFS), and DHPZ as monomers. The sulfonic acid groups, being on deactivated positions of the polymer backbone, were expected to be hydrolytically more stable than postsulfonated polymers. Fourier transform infrared and ¹H NMR were used to characterize the structures and degrees of sulfonation of the sulfonated polymers. Membrane films of SPPEKs with SDFB‐Na/DFB molar feed ratios of up to 60/40 and SPPESs with sulfonated 4‐fluorophenyl sulfone/DFS molar feed ratios of up to 50/50 were cast from N,N‐dimethylacetamide polymer solutions. Membrane films in acid form were then obtained by the treatment of the sodium‐form membrane films in 2 N sulfuric acid at room temperature. An increase in the number of sulfonate groups in the copolymers resulted in an increased glass‐transition temperature and enhanced membrane hydrophilicity. The sodium‐form copolymers were thermally more stable than their acid forms. The proton conductivities of the acid‐form copolymers with sulfonated monomer/unsulfonated monomer molar feed ratios of 0.5 and 0.6 were higher than 10^?2 S/cm and increased with temperature; they were less temperature‐dependent than those of the postsulfonated products. SPPESH‐50 showed higher conductivity than the corresponding postsulfonated poly(phthalazinone ether sulfone). © 2003 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 41: 2731–2742, 2003     

Polyelectrolytes for Fuel Cells Made of Sulfonated Poly(phthalazinone ether ketone)s

Novel sulfonated poly(phthalazinone ether ketone)s were synthesized directly by aromatic nucleophilic polycondensation of 4‐(4‐hydroxyphenyl)phthalazinone with various ratios of 5,5′‐carbonylbis(2‐fluorobenzenesulfonate) to 4,4′‐difluorobenzophenone. The 10% weight loss temperature of the products is higher than 500°C. The resulting ionomers show low swelling (14.7, 16.7 and 17.8%), while the corresponding IEC are 1.58, 1.88 and 2.16 meq/g, respectively. The low swelling results from hydrogen bonding. The membranes show very good perspectives in polymer electrolyte membrane fuel cell applications.     

Sulfonated polybenzimidazoles: Proton conduction and acid–base crosslinking

A series of soluble, benzimidazole‐based polymers containing sulfonic acid groups (SuPBI) has been synthesized. SuPBI membranes resist extensive swelling in water but are poor proton conductors. When blended with high ion exchange capacity (IEC) sulfonated poly(ether ether ketone) (SPEEK), a polymer that has high proton conductivity but poor mechanical integrity, ionic crosslinks form reducing the extent of swelling. The effect of sulfonation of PBI on crosslinking in these blends was gauged through comparison with nonsulfonated analogs. Sulfonic acid groups present in SuPBI compensate for acid groups involved in crosslinking, thereby increasing IEC and proton conductivity of the membrane. When water uptake and proton conductivity were compared to the IEC of blends containing either sulfonated or nonsulfonated PBI, no noticeable distinction between PBI types could be made. Comparisons were also made between these blends and pure SPEEK membranes of similar IEC. Blend membranes exhibit slightly lower maximum proton conductivity than pure SPEEK membranes (60 vs. 75 mS cm^?1) but had significantly enhanced dimensional stability upon immersion in water, especially at elevated temperature (80 °C). Elevated temperature measurements in humid environments show increased proton conductivity of the SuPBI membranes when compared with SPEEK‐only membranes of similar IEC (c.f. 55 for the blend vs. 42 mS cm^?1 for SPEEK at 80 °C, 90% relative humidity). © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3640–3650, 2010     

Preparation and characterization of branched and linear sulfonated poly(ether ketone sulfone) proton exchange membranes for fuel cell applications

Branched sulfonated poly(ether ketone sulfone)s (Br‐SPEKS) were prepared with bisphenol A, bis(4‐fluorophenyl)sulfone, 3,3′‐disodiumsulfonyl‐4,4′‐difluorobenzophenone, and THPE (1,1,1‐tris‐p‐hydroxyphenylethane), respectively, at 180 °C using potassium carbonate in NMP (N‐methylpyrrolidinone). THPE, as a branching agent, was used with 0.4 mol % of bisphenol A to synthesize branched copolymers. Copolymers containing 10–50 mol % disulfonated units were cast from dimethylsulfoxide solutions to form films. Linear sulfonated poly(ether ketone sulfone)s (SPEKS) were also synthesized without THPE. The films were converted from the salt to acid forms with dilute hydrochloric acid. A series of copolymers were studied by Fourier transform infrared, ¹H‐NMR spectroscopy, differential scanning calorimetry (DSC), and thermogravimetric analysis (TGA). Sorption experiments were conducted to observe the interaction of sulfonated polymers with water and methanol. The ion‐exchange capacity (IEC), a measure of proton conductivity, was evaluated. The synthesized Br‐SPEKS and SPEKS membranes exhibit conductivities (25 °C) from 1.04 × 10^?3 to 4.32 × 10^?3 S/cm, water swell from 20.18 to 62.35%, IEC from 0.24 to 0.83 mequiv/g, and methanol diffusion coefficients from 3.2 × 10^?7 to 4.7 × 10^?7 cm²/S at 25 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 1792–1799, 2008     

Synthesis and properties of novel benzimidazole‐containing sulfonated polyethersulfones for fuel cell applications

A novel series of benzimidazole‐containing sulfonated poly(arylene sulfones)s with controllable amount of basic 2,6‐bis(benzimidazol‐2‐yl)pyridine (BIP) and sulfonic acid groups have been prepared by the copolycondensation of a new BIP‐containing arylene difluoride monomer (DFSBIP) with a sulfonated arylene difluoride (DSDFS) and 4,4′‐biphenol (BP). All the resulting polymers have high molecular weights, good thermal stability, and can form uniform and tough membranes by simple solution casting. Because of the strong acid–base interaction between BIP and sulfonic acid groups, ionic crosslinking networks forms that resulted in polymer membranes with good dimensional stability in water even at high temperature (e.g., 100 °C). The ion exchange capacity (IEC) of the polymer membranes was investigated through a new simple pH‐determination method. A comparison between the experimental IEC values with the calculated ones based on the polymer structures indicated that each BIP unit interacted with one sulfonic acid group. Thus, by controlling the relative content of BIP units and sulfonate groups in the polymers, the intra‐ and intermolecular acid–base interactions could be readily optimized so as to achieve polymers with high IEC values, high proton conductivities as well as low swelling ratios, demonstrating good potential for proton exchange membrane applications. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 1920–1929, 2009     

Synthesis and properties of novel sulfonated (co)polyimides bearing sulfonated aromatic pendant groups for PEFC applications

Novel sulfonated diamines bearing aromatic pendant groups, namely, 3,5‐diamino‐3′‐sulfo‐4′‐(4‐sulfophenoxy) benzophenone (DASSPB) and 3,5‐diamino‐3′‐sulfo‐4′‐(2,4‐disulfophenoxy) benzophenone (DASDSPB), were successfully synthesized. Novel side‐chain‐type sulfonated (co)polyimides (SPIs) were synthesized from these two diamines, 1,4,5,8‐naphthalene tetracarboxylic dianhydride (NTDA) and nonsulfonated diamines such as 4,4′‐bis(3‐aminophenoxy) phenyl sulfone (BAPPS). Tough and transparent membranes of SPIs with ion exchange capacity of 1.5–2.9 meq g^?1 were prepared. They showed good solubility and high thermal stability up to 300 °C. They showed isotropic membrane swelling in water, which was different from the main‐chain‐type and sulfoalkoxy‐based side‐chain‐type SPIs. The relative humidity (RH) and temperature dependence of proton conductivity were examined. At low RH, the novel SPI membranes showed much higher conductivity than the sulfoalkoxy‐based SPIs. They showed comparable or even higher proton conductivity than Nafion 112 in water at 60 °C (>0.10 S cm^?1). The membrane of NTDA‐DASDSPB/BAPPS (1/1)‐s displayed reasonably high proton conductivities of 0.05 and 0.30 S cm^?1 at 50 and 100% RH, respectively, at 120 °C. © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2862–2872, 2006     

Substituents effect on the properties of sulfonated polyimide copolymers

A series of sulfonated polyimide (SPI) copolymers containing methyl, methoxy, or fluorine groups were synthesized to elucidate the substituents effect on their proton conducting properties as well as thermal, hydrolytic, and oxidative stability for polymer electrolyte membrane fuel cell applications. SPIs of high molecular weight (M_w > 200 kDa, M_n > 80 kDa) along with the ion exchange capacity (IEC) varying between 1.34 and 1.91 mequiv/g were obtained, which gave tough, ductile, and flexible membranes by solution casting. The thermal properties of the SPIs were dominated by the electronic structure of the sulfonated aromatic rings. The electron‐donating methyl groups lowered the thermal decomposition temperature. The hydrolytic and oxidative stability was roughly in the order of IEC (the higher IEC membranes were less stable). Fluorine groups, either as ? F or ? CF₃, had negative effect on the hydrolytic and oxidative stability. In the water uptake and proton conductivity, hydrophobic components are rather more influential than the substituents. It was found out that the SPI(5, 8, 0.7) containing bis(phenoxy)biphenylene sulfone moieties as a rigid hydrophobic component showed the best balanced properties in terms of the stability and the proton conductivity for its rather low IEC. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 46: 4469–4478, 2008     

Crosslinked sulfonated polyimide networks as polymer electrolyte membranes in fuel cells

Sulfonated polyimides with tertiary nitrogen in the polymer backbone were synthesized with 1,4,5,8‐naphthalenetetracarboxylic dianhydride, 4,4′‐diaminobiphenyl 2,2′‐disulfonic acid, 2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane, and diaminoacrydine hemisulfate. They were crosslinked with a series of dibromo alkanes to improve the hydrolytic stability. The crosslinked sulfonated polyimide films were characterized for their thermal stability, ion‐exchange capacity (IEC), water uptake, hydrolytic stability, and proton conductivity. All the sulfonated polyimides had good thermal stability and exhibited a three‐step degradation pattern. With an increase in the alkyl chain length of the crosslinker, IEC decreased as 1.23 > 1.16 > 1.06 > 1.01, and the water uptake decreased as 7.29 > 6.70 > 6.55 > 5.63. The order of the proton conductivity of the crosslinked sulfonated polyimides at 90 °C was as follows: polyimide crosslinked with dibromo butane (0.070) > polyimide crosslinked with dibromo hexane (0.055) > polyimide crosslinked with dibromo decane (0.054). The crosslinked polyimides showed higher hydrolytic stability than the uncrosslinked polyimides. Between the crosslinked polyimides, the hydrolytic stability decreased with an increase in the alkyl chain length of the crosslinker. The crosslinked and uncrosslinked sulfonated polyimides exhibited almost the same proton conductivities. © 2005 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 43: 2370–2379, 2005     

Fluoride‐terminated hyperbranched poly(arylene ether phosphine oxide)s via nucleophilic aromatic substitution

A series of AB_x‐type triarylphosphine oxide monomers, bis‐(4‐fluorophenyl)‐(4‐hydroxyphenyl)phosphine oxide ( 4a ), bis‐(3,4‐difluorophenyl)‐(4‐hydroxyphenyl)phosphine oxide ( 4b ), and 4‐hydroxyphenyl‐bis‐(3,4,5‐trifluorophenyl)phosphine oxide ( 4c ) were prepared, characterized, and polymerized under nucleophilic aromatic substitution conditions [N‐methylpyrrolidone (NMP), K₂CO₃] to provide the corresponding hyperbranched poly(arylene ether phosphine oxide)s with number‐average molecular weights ranging from 9200 to 14,600 Da. NMR spectroscopic analysis indicated the presence of highly branched products with an approximate degree of branching of 0.57. The polymers were soluble in a variety of typical organic solvents and displayed excellent thermal stability. © 2002 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 40: 1456–1467, 2002     

Sulfonated poly(ether sulfone)s with binaphthyl units as proton exchange membranes for fuel cell application

Sulfonated poly(ether sulfone)s containing binaphthyl units (BNSHs) were successfully prepared for fuel cell application. BNSHs, which have very simple structures, were easily synthesized by postsulfonation of poly(1,1′‐dinaphthyl ether phenyl sulfone)s and gave tough, flexible, and transparent membranes by solvent casting. The BNSH membranes showed low water uptake compared to a typical sulfonated poly(ether ether sulfone) (BPSH‐40) membrane with a similar ion exchange capacity (IEC) value and water insolubility, even with a high IEC values of 3.19 mequiv/g because of their rigid and bulky structures. The BNSH‐100 membrane (IEC = 3.19 mequiv/g) exhibited excellent proton conductivity, which was comparable to or even higher than that of Nafion 117, over a range of 30–95% relative humidity (RH). The excellent proton conductivity, especially under low RH conditions, suggests that the BNSH‐100 membrane has excellent proton paths because of its high IEC value, and water insolubility due to the high hydrophobicity of the binaphthyl structure. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 5827–5834, 2009     

Synthesis and properties of sulfonated polyimides from homologous sulfonated diamines bearing bis(aminophenoxyphenyl)sulfone

Three homologous sulfonated diamines bearing a bis(aminophenoxyphenyl)sulfone structure, namely, bis[4‐(4‐aminophenoxy)phenyl]sulfone‐3,3′‐disulfonic acid (pBAPPS‐3DS), bis[4‐(4‐aminophenoxy)phenyl]sulfone‐2,2′‐disulfonic acid (pBAPPS‐2DS), and bis[4‐(4‐aminophenoxy)‐2‐(3‐sulfobenzoyl)phenyl]sulfone (pBAPPS‐2DSB), were synthesized. A series of sulfonated polyimides (SPIs) were synthesized from 1,4,5,8‐naphthalene tetracarboxylic dianhydride, these sulfonated diamines, and nonsulfonated diamines, and their properties were investigated in comparison with those reported for the SPIs from another homologous diamine or bis[4‐(3‐aminophenoxy)phenyl]sulfone‐3,3′‐disulfonic acid (mBAPPS‐3DS). These SPIs were soluble in common aprotic solvents and showed reasonably high proton conductivity, except for pBAPPS‐2DS‐based SPIs, the conductivity of which was slightly lower because of the lower water uptake. The water stability of these SPIs considerably depended on the structure of the sulfonated diamines and was in the order of pBAPPS‐2DSB ≈ pBAPPS‐2DS > pBAPPS‐3DS ? mBAPPS‐3DS. Their water stability was much lower than that of the SPIs from 4,4′‐bis(4‐aminophenoxy)biphenyl‐3,3′‐disulfonic acid. The reason was discussed on the basis of the basicity of the sulfonated diamine and the solubility property of the SPIs. © 2007 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 45: 2797–2811, 2007     

Synthesis of sulfonated aromatic poly(ether amide)s and their application to proton exchange membrane fuel cells

A series of wholly aromatic sulfonated poly(ether amide)s (SPEAs) containing a sulfonic acid group on the dicarbonyl aromatic ring were prepared via a polycondensation reaction of sulfonated terephthalic acid (STA), terephthalic acid (TA), and aromatic diamine monomers. The degree of sulfonation was readily controlled by adjusting the monomer feed ratio of STA and TA in the polymerization process, and randomly sulfonated polymers with an ion exchange capacity (IEC) of 1.0–1.8 mequiv/g were prepared using this protocol. The chemical structures of randomly sulfonated polymers were characterized using NMR and FT‐IR spectroscopies. Gel permeation chromatography analysis of SPEAs indicated the formation of high‐molecular‐weight sulfonated polymer. Tough and flexible SPEA membranes were obtained from solution of N,N‐dimethylacetamide, and thermogravimetric analysis of these membranes showed a high degree of thermal stability. Compared with previously reported sulfonated aromatic polyamides, these new SPEAs showed a significantly lower water uptake of 10–30%. In proton conductivity measurements, ODA‐SPEA‐70 (IEC = 1.80 mequiv/g), which was obtained from polycondensation of 4,4′‐oxydianiline and 70 mol % STA, showed a comparable proton conductivity (105 mS/cm) to that of Nafion 117 at 80 °C. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 485–496, 2009     

Synthesis and characterization of sulfonated homo‐ and co‐polyimides based on 2,4 and 2,5‐diaminobenzenesulfonic acid for proton exchange membranes

A series of sulfonated homo‐ and random co‐polyimides (co‐SPI) based on 2,4‐diaminobenzenesulfonic acid (2,4‐DABS) and 2,5‐diaminobenzenesulfonic acid (2,5‐DABS) has been synthesized via conventional two‐step polyimidization method. 2,4‐DABS and 2,5‐DABS were used as sulfonated diamine compounds, 4,4′‐oxydianiline (ODA) and 4,4′‐diaminodiphenyl sulfone (DDS) were used as non‐sulfonated diamine compounds. Mixtures of sulfonated and non‐sulfonated diamine compounds were reacted with benzophenonetetracarboxylic dianhydride (BTDA) to obtain co‐SPI membranes. Molar ratios of sulfonated to non‐sulfonated diamine were systematically varied to produce copolymers of controlled compositions. The co‐SPIs were evaluated for thermal oxidative stability, ion exchange capacity (IEC), water uptake, proton conductivity, solubility, and hydrolytic stability. Proton conductivity and hydrolytic stability of the co‐SPIs were compared with the fully aromatic polyimide, homo‐SPIs (BTDA/2,4‐DABS and BTDA/2,5‐DABS). Regarding thermogravimetric analysis (TGA) analysis, it is concluded that desulfonation temperature in the range of 200–350°C suggests high stability of sulfonic acid groups. co‐SPIs with 40 mol% of 2,4‐DABS showed similar or higher proton conductivity than Nafion® 117 in water. Proton conductivity values of the co‐SPIs were mainly a function of IEC and water uptake. Consequently, the optimum concentration of 2,4‐DABS was found to be in the range of 30–40 mol% from the viewpoint of proton conductivity, IEC, and hydrolytic stability. Copyright © 2008 John Wiley & Sons, Ltd.     

Structure–property correlations of sulfonated polyimides. I. Effect of bridging groups on membrane properties

A series of six‐membered sulfonated polyimides were synthesized using 1,4,5,8‐naphthalenetetracarboxylic dianhydride, 4,4′‐diaminobiphenyl 2,2′‐disulfonic acid as the sulfonated diamine, and various nonsulfonated diamine monomers having different bridging groups. These bulky bridging groups have the capacity to increase hydrolytic stability and proton conductivity. Polyimides with bulky bridging groups showed increased solubility but exhibited lower thermal stability. The ion exchange capacity and water uptake reduced with increase in the bulkiness of the bridging group. This was attributed to the increase in the molecular weight of the repeating unit and hence effectively reduced the sulfonic acid content. In low temperatures, the conductivity was lower than Nafion®115 and, with increase in temperature, the conductivity rapidly increased and exhibited better conductivity than Nafion®115. Polyimides with bulky bridging groups 4‐amino phenyl sulfone, and 2‐bis[4‐(4‐aminophenoxy)phenyl]hexafluoropropane showed higher conductivity than other polyimides and Nafion®115 despite low ion exchange capacity. The hydrolytic stability of the polyimides with bulky bridging groups was higher than the polyimides with less bulky atoms because of the imparted flexibility. © 2004 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 42: 3612–3620, 2004     

Polymer blend for fuel cells based on SPEKK: Effect of cocontinuous morphology on water sorption and proton conductivity

Proton‐exchange membranes (PEM), suitable for micro and small sized fuel cells, were obtained by blending sulfonated poly(ether ketone ketone) (SPEKK) polymers with different ionic exchange capacity (IEC). This approach was used to limit the amount of swelling caused by water sorption without significantly decreasing the proton conductivity of the membrane. In particular a membrane with a cocontinuous biphasic morphology was obtained by blending two SPEKKs, with respectively, an IEC equal to 1.2 and 2.08 in the weight ratio 60/40, casted from 5% (w/v) solutions in dimethylacetamide. The effect of a cocontinuous morphology on water sorption and proton conductivity in comparison to neat SPEKK was investigated. In the range of temperatures between 40 and 70 °C, which is typical for small and micro fuel cells conditions, it was found that the ratio of proton conductivity to water sorption could be maximized. This has been attributed to the presence of percolative pathways for proton transport provided by the cocontinuous morphology along with the constraint effect of the less sulfonated component on the overall capacity of swelling of the membrane. © 2007 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 45: 395–404, 2007     

Synthesis and characterization of novel polyimide from bis‐(3‐aminophenyl)‐4‐(trifluoromethyl)phenyl phosphine oxide

A novel diamine, bis‐(3‐aminophenyl)‐4‐(trifluoromethyl)phenyl phosphine oxide (mDA3FPPO), containing phosphine oxide and fluorine moieties was prepared via the Grignard reaction from an intermediate, 4‐(trifluoromethyl)phenyl diphenyl phosphine oxide, that was synthesized from diphenylphosphinic chloride and 4‐(trifluoromethyl)bromobenzene, followed by nitration and reduction. The monomer was characterized by Fourier transform infrared (FTIR), ¹H NMR, ³¹P NMR, ¹⁹F NMR spectroscopies; elemental analysis; melting point measurements; and titration and was used to prepare polyimides with a number of dianhydrides such as pyromellitic dianhydride (PMDA), 5,5′‐[2,2,2‐trifluoro‐1‐(trifluoromethyl)ethyliden]‐bis‐1,3‐isobenzofuranedione (6FDA), 3,3′,4,4′‐benzophenone tetracarboxylic dianhydride (BTDA), and 4,4′‐oxydiphthalic dianhydride (ODPA). Polyimides were synthesized via a conventional two‐step route; preparation of polyamic acids, followed by solution imidization, and the molecular weight were controlled to 20,000 g/mol. Resulting polyimides were characterized by FTIR, NMR, DSC, and intrinsic viscosity measurements. Refractive‐index, dielectric constant, and adhesive properties were also determined. The properties of polyimides were compared with those of polyimides prepared from 1,1‐bis‐(4‐aminophenyl)‐1‐phenyl‐2,2,2‐trifluoroethane (3FDAm) and bis‐(3‐aminophenyl) phenyl phosphine oxide (mDAPPO). The polyimides prepared from mDA3FPPO provided high glass‐transition temperatures (248–311 °C), good thermal stability, excellent solubility, low birefringence (0.0030–0.0036), low dielectric constants (2.9–3.1), and excellent adhesive properties with Cu foils (107 g/mm). © 2001 John Wiley & Sons, Inc. J Polym Sci Part A: Polym Chem 39: 3335–3347, 2001     

Highly phosphonated poly(N‐phenylacrylamide) for proton exchange membranes

A novel highly phosphonated poly(N‐phenylacrylamide) ( PDPAA ) with an ion‐exchange capacity (IEC) of 6.72 mequiv/g was synthesized by the radical polymerization of N‐[2,4‐bis(diethoxyphosphinoyl)phenyl]acrylamide ( DEPAA ), followed by the hydrolysis with trimethylsilyl bromide. Then, the crosslinked PDPAA membrane was successfully prepared by the electrophilic substitution reaction between the aromatic rings of PDPAA and the carbocation formed from hexamethoxymethylmelamine (CYMEL) as a crosslinker in the presence of methanesulfonic acid. The crosslinked PDPAA membrane had high oxidative stability against Fenton's reagent at room temperature. The proton conductivity of the crosslinked PDPAA membrane was 8.8 × 10^?2 S/cm at 95% relative humidity (RH) and 80 °C, which was comparable to Nafion 112. Under low RH, the crosslinked PDPAA membrane showed the proton conductivity of 1.9 × 10^?3 and 4.7 × 10^?5 S/cm at 50 and 30% RH, respectively. The proton conductivity of the crosslinked PDPAA membrane lied in the highest class among the reported phosphonated polymers, and, consequently, the very high local concentration of the acids of PDPAA (IEC = 6.72 mequiv/g) achieved high and effective proton conduction under high RH. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010