钙钛矿型LaxSr1－xNi1－yCoyO3光电催化活性研究

用甘氨酸-硝酸盐燃烧合成法, 制备La_xSr_1－xNi_1－yCo_yO₃复合氧化物的陶瓷粉末, 对钙钛矿氧化物进行了XRD结构分析. 在通氧或不通氧下测试氧还原和氧析出的循环伏安曲线. 结果表明: 该氧电极具有双功能催化特性, 但不完全可逆. 利用汞灯作为激发光源, 进行几种水溶性染料和五种混合染料光解实验, 利用紫外-可见、红外以及人工神经网络光度法研究La_xSr_1－xNi_1－yCo_yO₃的催化性能. 结果表明: La_xSr_1－xNi_1－yCo_yO₃ (x＝0.7, 0.9, 1; y＝0.3, 0.75)复合氧化物都具有较强光催化特性; La_xSr_1－xNi_1－yCo_yO₃的光催化活性高于La_xSr_1－xNiO₃, 这与B位离子(Ni^2—, Co^2－)的电子构型有关; Co^2＋的加入可使La_xSr_1－xNiO₃的光催化活性有所提高.     

空气中合成固溶体荧光粉Ba2(Zn, Mg)Si2O7:Ce3+,Eu2+,Eu3+及其发光特性

采用高温固相法在空气中合成了Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu,yCe³⁺系列荧光粉。分别采用X-射线衍射和荧光光谱对所合成荧光粉的物相和发光性质进行了表征。在紫外光330~360 nm激发下,固溶体荧光粉Ba_1.97-yZn_1-xMg_xSi₂O₇:0.03Eu的发射光谱在350~725 nm范围内呈现多谱峰发射,360和500 nm处有强的宽带发射属于Eu²⁺离子的4f⁶5d¹-4f⁷跃迁,590~725 nm红光区窄带谱源于Eu³⁺的⁵D₀-⁷F_J (J=1,2,3,4)跃迁,这表明,在空气气氛中,部分Eu³⁺在Ba_1.97-yZn_1-xMg_xSi₂O₇基质中被还原成了Eu²⁺;当x=0.1时,荧光粉Ba_1.97Zn_0.9Mg_0.1Si₂O₇:0.03Eu的绿色发光最强,表明Eu³⁺被还原成Eu²⁺离子的程度最大。当共掺入Ce³⁺离子后,形成Ba_1.97-yZn_0.9Mg_0.1Si₂O₇:0.03Eu,yCe³⁺荧光粉体系,其发光随着Ce³⁺离子浓度的增大由蓝绿区经白光区到达橙红区;发现名义组成为Ba_1.96Zn_0.9Mg_0.1Si₂O₇:0.01Ce³⁺,0.03Eu的荧光粉的色坐标为(0.323,0.311),接近理想白光,是一种有潜在应用价值的白光荧光粉。讨论了稀土离子在Ba₂Zn_0.9Mg_0.1Si₂O₇基质中的能量传递与发光机理。     

CeCl3-CdCl2-H2O和CeCl3-CdCl2-HCl-H2O的相平衡

测定了三元系CeCl₃-CdCl₂-H₂O (25 ℃)和四元系CeCl₃-CdCl₂-HCl(～8.4％)-H₂O(25 ℃) 的相平衡溶度数据,绘制了相应的溶度图.该三元系是由5个固相区CdCl₂&;#8226;2.5H₂O(原始盐)、CdCl₂&;#8226;H₂O(原始盐)、6CdCl₂&;#8226;CeCl₃&;#8226;14H₂O、4CdCl₂&;#8226;CeCl₃&;#8226;12H₂O、CeCl₃&;#8226;7H₂O(原始盐)组成的复杂体系.该四元系是由5个固相区CdCl₂&;#8226;H₂O(原始盐)、9CdCl₂&;#8226;CeCl₃&;#8226;19H₂O、6CdCl₂&;#8226;CeCl₃&;#8226;14H₂O、4CdCl₂&;#8226;CeCl₃&;#8226;12H₂O、CeCl₃&;#8226;7H₂O(原始盐)组成的复杂体系.其中6CdCl₂&;#8226;CeCl₃&;#8226;14H₂O在该三元系是介稳化合物.9CdCl₂&;#8226;CeCl₃&;#8226;19H₂O 、6CdCl₂&;#8226;CeCl₃&;#8226;14H₂O和4CdCl₂&;#8226;CeCl₃&;#8226;12H₂O用X射线粉末衍射及TG-DTG和DSC等方法进行了研究,并对X射线粉末衍射进行了指标化.     

Bi2WO6量子点(QDs)修饰Bi2MoO6-xF2x异质结的构筑及其催化活性增强机理

采用简单沉积-沉淀法合成了Bi₂WO₆@Bi₂MoO_6-xF_2x（BWO/BMO6-xF2x）异质结,借助XRD、XPS、TEM、SEM、EDS、UV-Vis-DRS、PC和EIS等测试技术对其组成、形貌、光吸收特性和光电化学性能等进行系统表征,并以模型污染物罗丹明B（RhB）的光催化降解作为探针反应来评价Bi₂WO₆@Bi₂MoO_6-xF_2x异质结的光催化活性增强机制。形貌分析表明,所得Bi₂MoO₆微球由大量厚度为20~50 nm的纳米片组成;FE-SEM和HR-TEM分析表明,尺寸约为10 nm的Bi₂WO₆量子点均匀沉积在Bi₂MoO_6-xF_2x微球表面,形成新颖的Bi₂WO₆@Bi₂MoO_6-xF_2x异质结;与纯Bi₂MoO₆或者Bi₂WO₆相比,1∶1Bi₂WO₆@Bi₂MoO_6-xF_2x异质结表现出更好的光催化活性和光电流性质,其对RhB光催化降解的表观速率常数分别为纯BMO和BWO的6.4和11.6倍。PC和EIS图谱分析表明,Bi₂WO₆量子点表面沉积显著提高Bi₂MoO_6-xF_2x光生电子/空穴的分离效率和迁移速率;活性物种捕获实验证明了·O₂^-和h⁺是主要的活性物种。根据实验结果,探讨了F^-掺杂和Bi₂WO₆量子点之间的协同效应对Bi₂MoO₆的光催化活性的影响机制。     

纳米钙钛矿LaxSr1-xFe1-yCoyO3复合氧化物的制备和表征

用甘氨酸-硝酸盐燃烧合成法，制备La_xSr_1-xFe_1-yCo_yO₃复合氧化物的陶瓷粉末，对该钙钛矿型氧化物进行了XRD、IR、紫外漫反射光谱及循环伏安曲线分析。结果表明：该复合氧化物粉体平均晶粒为15.3～29.8 nm,为立方和正交晶系。该氧电极具有双功能催化特性，但不完全可逆。对水溶液染料进行光解实验，利用紫外-可见、人工神经网络光度法研究La_xSr_1-xFe_1-yCo_yO₃的催化性能。结果表明：CO²⁺的加入可使La_xSr_1-xFeO₃的光催化活性有所提高，B位离子(Fe³⁺，CO²⁺)改变与加入，使La_xSr_1-xFe_1-yCo_yO₃(x=0.7，0.3；y=0.3，0.9，1)光催化活性高于La_xSr_1-xFeO₃。同时，对5种染料进行紫外光解，在0.75 h，脱色率大于91%，并为动力学一级反应。     

三元体系YCl3-CdCl2-H2O和四元体系YCl3-CdCl2-HCl(～8.8%)-H2O (25 ℃)的相平衡及其固相新化合物的研究

The equilibrium solubilities of the ternary system YCl₃-CdCl₂-H₂O, the quaternary system YCl₃-CdCl₂-HCl(～8.8%)-H₂O were determined at 25 ℃ and the phase diagrams were constructed. The results show that the ternary system was complicated with six equilibrim solid phases CdCl₂·2.5H₂O, CdCl₂·H₂O, 8CdCl₂·YCl₃·15H₂O (8∶1 type), 4CdCl₂·YCl₃·13H₂O(4∶1 type), 5CdCl₂·2YCl₃·26H₂O (5∶2 type) and YCl₃·6H₂O. The quaternary system was also complicated with four equilibrim solid phase CdCl₂·H₂O, 4CdCl₂·YCl₃·13H₂O (4∶1 type), 5CdCl₂·2YCl₃·26H₂O(5∶2 type) and YCl₃·6H₂O. Among the three new compounds 8CdCl₂·YCl₃·15H₂O, 4CdCl₂·YCl₃·13H₂O and 5CdCl₂·2YCl₃·26H₂O, 8CdCl₂·YCl₃·15H₂O was a kind of metastable compound only in ternary system, and it was changed into 4CdCl₂·YCl₃·13H₂O with time. Both 4∶1 type and 5∶2 type existed in ternary and quaternary system, but they were also congruently soluble compounds in quaternary system. They have been prepared from the system and have been characterized by XRD, TC-DTG and DSC.     

层状O2结构锂锰氧化物Li0.60[MgxCoyMn1-x-y]O2的制备及结构表征

本文采用离子交换法分别制备了双复合锂锰氧化物Li_0.60[Mg_xMn_1-x]O₂(0.05 ≤ x ≤ 0.15)和三复合锂锰氧化物Li_0.60[Mg_xCo_yMn_1-x-y]O₂(x=0.05，0.05 ≤      

纳米Mn-Zn铁氧体的制备和研究

Nanosize manganese zinc ferrites were fabricated by hydrothermal precipitation route using Fe₂(SO₄)₃, ZnSO₄·7H₂O, MnSO₄·H₂O as material, then some calcinated at 500 ℃ and studied by XRD, TEM, IR and VSM. The results showed that the products were spinel crystal structure and uniformly sized nanoparticles (15～25 nm) with little aggregation. The analysis of IR showed that the superficial water can be eliminated, but that was embedded in crystal lattice can not be removed by calcinating. The effect Zn content x on the lattice (a) of nanosize Mn_1-xZn_xFe₂O₄ was also discussed. The lattice of nanosize Mn_1-xZn_xFe₂O₄ decreases with x increasing; and its value deviated the standard lattice (a₀) of normal size manganese zinc ferrites. A lot of water was absorbed during the hydrothermal process owing to the large surface of nanosize particles. The change of magnetic properties of Mn_xZn_1-xFe₂O₄ with x increasing was studied: nanosize Mn_xZn_1-xFe₂O₄ particles synthesized by us exhibited peculiar magnetic properties curve with Zn content (x) increasing, Superparamagnetic behaviors of the synthesized ZnFe₂O₄ samples were confirmed by magnetic characterization, which can be explained by the difference between the distribution of the metal ions (Mn²⁺, Zn²⁺ and Fe³⁺) among the tetrahedral (A) and the octahedral (B) sites of nanosize ferrite and that of bulk ferrite.     

La-Ce对PbTiO3陶瓷气相扩渗生成La2Ti6O15CeTi21O38的陶瓷材料及其电性能

报道了采用气相法对PbTiO₃陶瓷扩渗La-Ce混合稀土元素的研究. 在气相扩渗过程中, La, Ce与PbTiO₃陶瓷组元发生了复杂反应,生成了稀土化合物La₂Ti₆O₁₅和CeTi₂₁O₃₈, 制备出未见报道的La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料, 经测试其导电性能发生了十分显著的变化. La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料的室温电阻率从2.0 ×10¹⁰ W·m下降为0.248 W·m,而且随着温度的变化, 晶粒电阻呈现明显的PTCR效应,而晶界电阻随着温度的升高,呈急剧连续降低状态,总电阻的变化规律与晶界电阻的变化相一致, 试样总电阻的PTCR效应已不存在, 近趋导体. 经XPS测试分析, 进一步证实了La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料中铅、钛等元素均有变价, 因而导致了La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料电阻率的降低, 测试结果还首次给出了La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料中各元素结合能位置的峰值. TG-DTA热分析表明La₂Ti₆O₁₅-CeTi₂₁O₃₈-PbTiO₃陶瓷材料具有较好的高温热稳定性.     

掺杂和取代对红色荧光材料SrAl12O19:Mn4+发光性能的影响

SrAl₁₂O₁₉：Mn⁴⁺是一种用于高显色性白光发光二极管的候选红色荧光材料。本论文研究了Mg²⁺、Zn²⁺和Ge⁴⁺离子的掺杂效应以及Ga³⁺、Ca²⁺和Ba²⁺离子的取代效应对SrAl₁₂O₁₉：Mn⁴⁺荧光材料性能的影响。样品通过高温固相反应制备,焙烧温度在1 250~1 500 ℃之间。利用X射线衍射技术表征了材料的相纯度,用荧光激发光谱和发射光谱表征了材料的荧光性能。研究结果指出,与未进行Mg²⁺或Zn²⁺掺杂的样品相比,Mg²⁺或Zn²⁺离子对Al³⁺格位的掺杂可以使材料的发光强度提高~60%,其原因被认为是掺杂促进了激活剂Mn⁴⁺离子进入晶格,其过程可以表示为：MO+MnO₂⇔M_Al^''+M_Al^·+3O_O^×（M=Mg,Zn）,电子顺磁共振谱支持这一结果。Ge⁴⁺离子的掺杂使材料的发光性能明显下降。Ga³⁺离子可以取代Al³⁺离子形成全范围的固溶体,其中少量Ga³⁺离子的掺杂可以使材料的荧光发射强度提高~13%,而掺杂量进一步提高使材料的荧光性能下降。Ca²⁺和Ba²⁺对Sr²⁺的取代仅形成有限范围的固溶体。Ca²⁺的取代使材料的发光性能提高;而 Ba²⁺的取代使材料的发光强度下降。