甲苯、丙酮和乙酸乙酯在新型铂-钯/不锈钢丝网催化剂上的催化氧化

采用阳极氧化法制备了一种用于催化氧化处理挥发性有机化合物(VOCs)的0.1%Pt-0.5%Pd/不锈钢丝网(SSWM)催化剂. 活性测试结果表明, 0.1%Pt-0.5%Pd/不锈钢丝网催化剂具有较高的催化活性和热稳定性. 该催化剂上甲苯、丙酮和乙酸乙酯的完全氧化温度分别为220、260和280 ℃. 通过扫描电镜(SEM)、X射线光电子能谱(XPS)和超声波等手段对催化剂和不锈钢丝网进行了表征. SEM结果表明, 经阳极氧化工艺处理过的不锈钢金属丝网载体表面形成了一层沟壑形态的复合氧化膜. 该阳极氧化膜有利于活性组分Pd、Pt的分散.     

Pd-Mn/Stainless Steel Wire Mesh Catalyst for Catalytic Oxidation of Toluene,Acetone and Ethyl Acetate

A new 0.1%Pd‐6%Mn/stainless steel wire mesh catalyst was prepared and used for volatile organic compounds (VOC) elimination. The supported palladium and manganese catalyst over the stainless steel wire mesh was prepared by using an impregnation method. When an anodic oxidation technology was employed, an anodic oxidation membrane appeared on the stainless steel wire mesh. On the 0.1%Pd‐6%Mn/stainless steel wire mesh catalyst calcined at 500°C, the total oxidation of toluene, acetone and ethyl acetate was respectively at 260, 220 and 320°C. The activity could be stable for over 700 h for toluene oxidation. The scanning electron microscopy (SEM) investigation of the Pd‐Mn/stainless steel wire mesh catalyst shows that the presence of anodic oxidation membrane on the support surface is important for better dispersion of active phases.     

不锈钢丝网上Cu基催化剂的制备及反应性能

采用阳极氧化技术在不锈钢丝网上成功地自生长了结构致密的氧化物膜,并以此为载体,通过电化学沉积工艺制备了Cu/不锈钢丝网催化剂。以甲苯、丙酮、乙酸乙酯及二氯甲烷为模型反应,考察了4种不同种类挥发性有机化合物(VOCs)在该催化剂上的完全氧化活性。结果表明电化学沉积时间为15 min制备得到的催化剂上完全氧化丙酮、甲苯、乙酸乙酯及二氯甲烷的温度分别为240、220、260和440℃。在220℃反应条件下进行60 h的甲苯氧化稳定性试验结果显示该催化剂催化氧化甲苯的转化率一直保持98%以上,表现出较好的稳定性。扫描电镜,X射线衍射及X射线光电子能谱等表征结果表明,不锈钢丝网载体表面的阳极氧化物膜有利于提高活性组分的分散度。设计采用电沉积工艺大大提高了催化剂表面活性物种与载体的结合牢固度。     

0.1%Pt-0.02%Pd/不锈钢整体催化剂上丙酮氧化性能及稳定性(英文)

制备了0.1%Pt-0.02%Pd/不锈钢整体催化剂。选取不锈钢为该催化剂的载体,可克服传统γ-Al2O3和堇青石蜂窝载体热稳定性差的缺点。采用阳极氧化技术在不锈钢上自生长了结构致密的多孔阳极氧化膜,并在其上负载Pt和Pd制备得到挥发性有机物(VOCs)净化催化剂。结果表明,经500、800和1000℃不同温度焙烧后,该催化剂完全氧化丙酮的温度分别为160、160和200℃。该催化剂表现出以下优点:(a)高温稳定性能好;(b)低温催化活性高;(c)贵金属负载量低。通过SEM和EDX等技术对该催化剂的结构及活性组分分散情况进行了表征。     

Ce-Pt-Pd/不锈钢丝网催化剂的制备与催化性能

采用阳极氧化技术在不锈钢丝网上自生长了一层结构致密的阳极氧化膜,并以此为载体,制备出一种高活性、高稳定性的负载型Ce-Pt-Pd催化剂.考察了该系列催化剂对甲苯、丙酮和乙酸乙酯的氧化活性,并用扫描电镜、X射线光电子能谱和程序升温氧化技术对催化剂进行了表征.结果表明,不锈钢丝网载体表面自生长的氧化物膜十分有利于活性组分的负载,制得的催化剂具有较高的催化燃烧有机化合物的活性和稳定性.     

VOCs催化燃烧Pd-Y/不锈钢丝网催化剂的性能

采用经阳极氧化工艺处理后的不锈钢丝网作为催化剂载体,制备了Pd-Y/不锈钢丝网催化剂。考察了该催化剂对典型的挥发性有机物(VOCs)(甲苯、丙酮和乙酸乙酯)的催化燃烧性能,并用SEM、TPR技术对催化剂的形貌和氧化膜的结构组成进行了表征。结果表明：采用阳极氧化技术在不锈钢表面形成致密的多孔氧化膜,有利于活性组分的负载及均匀分散,明显提高了催化剂的燃烧活性和稳定性,延长了催化剂的使用寿命。Pd-Y/不锈钢丝网催化剂上3种VOCs的完全氧化温度分别为220、280和320 ℃。控制甲苯进料浓度为4～6 g·m     

制备蜂窝状筛网进行NH3选择性催化还原NO的反应

 制备了蜂窝状筛网催化剂，并用于以NH3为还原剂选择性催化还\r\n原NO的反应．蜂窝状筛网催化剂具有热响应迅速、传质系数较高、压力\r\n降适中、机械强度较高、几何可变形性、抗热震性能好、催化剂回收简\r\n便和成本较低等一系列优点．阐述了蜂窝状筛网催化剂的制备工艺，并\r\n采用扫描电镜、比表面积测定、X射线衍射、活性评价等手段考察了筛\r\n网预处理方法对其催化活性的影响．实验结果表明，最佳的预处理方法\r\n是首先经稀酸刻蚀，然后于500℃下焙烧20h．     

OL负载Cu催化剂及其催化氧化CO及乙酸乙酯性能

采用氧化还原法合成了层状锰氧化物(OL),并以OL为载体采用离子交换法制备了不同Cu负载量的Cu_x/OL催化剂。利用X射线衍射(XRD)、电子扫描电镜(SEM)、N_2吸附/脱附、H_2~-程序升温还原(H_2-TPR)、TG(热重)、X射线光电子能谱(XPS)、O_2-程序升温脱附(O_2-TPD)等技术对所制催化剂进行结构和织构表征,并对其催化氧化CO及乙酸乙酯活性进行了评价。结果表明,OL具有典型的层状锰氧化物结构,适量掺杂Cu对OL的结构和织构影响不大,但Cu的掺杂明显影响Cu_x/OL的还原性、氧移动性及催化剂表面Cu~(2+)/CuO、(Mn~(2+)+Mn~(3+))/Mn~(4+)和Oads/Olatt的比例。Cu_x/OL的催化性能与以上因素密切相关。在Cu_x/OL样品中,Cu_5/OL催化剂具有最佳的催化活性(CO催化氧化,T_(50)=70°C和T_(90)=100°C;乙酸乙酯催化氧化T50=160°C,T90=200°C)。同时,Cu_5/OL催化剂具有最佳的还原性能、氧移动性能和最多的Cu~(2+)、(Mn~(2+)+Mn~(3+))和表面吸附氧浓度。Cu_x/OL催化性能与铜锰之间相互作用、还原性和氧移动性能密切相关。     

钾改性Mn/Ce0.65Zr0.35O2催化剂催化氧化甲苯

Volatile organic compounds (VOCs) are both harmful to human health and the environment; however, catalytic combustion offers a promising method for VOC purification because of its high efficiency without secondary pollution. Although manganese-based catalysts have been well studied for VOC catalytic oxidation, their catalytic activity at low temperature must be improved. Alkali metals as promoters have the potential to modulate the electronic and structural properties of the catalysts, improving their catalytic activity. Herein, a Ce_0.65Zr_0.35O₂ support was prepared by co-precipitation and MnO_x/Ce_0.65Zr_0.35O₂ catalysts were obtained through the incipient-wetness impregnation method. The catalytic properties of K-modified MnO_x/Ce_0.65Zr_0.35O₂ for toluene oxidation with different molar ratios of K/Mn were investigated. In addition, the catalysts were characterized by XRD, UV/visible Raman, Hydrogen temperature program reduction (H₂-TPR), Oxygen temperature programmed desorption (O₂-TPD), X-ray photoelectron spectroscopy (XPS) and in situ diffuse reflectance FTIR spectroscopy (DRIFTS) experiments. The results showed that alkali metal doping with K significantly improved the catalytic activity. In particular, when the molar ratio of K/Mn was 0.2, the monolith catalyst Mn/Ce_0.65Zr_0.35O₂-K-0.2 exhibited the best performance with the lowest complete conversion temperature T₉₀ of 242 ℃ at a GHSV of 12000 h⁻¹. The XRD results suggested that MnO_x was uniformly distributed on the surface of the catalyst and that Mn⁴⁺ partially reduced to Mn³⁺ on the addition of K. The Raman spectrum demonstrated that with increasing K content, both the β- and α-MnO₂ phases coexisted on the Mn/Ce_0.65Zr_0.35O₂-K-0.2 catalyst, increasing the number of surface defect sites. The H₂-TPR experiment results confirmed that Mn/Ce_0.65Zr_0.35O₂-K-0.2 exhibited the lowest reduction temperature and good reducibility. From the O₂-TPD experiments, it was clear that Mn/Ce_0.65Zr_0.35O₂-K-0.2 contained the most surface adsorbed oxygen species and excellent lattice oxygen mobility, which benefitted the toluene oxidation activity. In addition, the XPS results suggested that the content of surface adsorbed oxygen species of the Mn/Ce_0.65Zr_0.35O₂-K-0.2 catalyst was the highest among all the tested samples. In addition, toluene-TPSR in N₂ as measured by in situ DRIFTs analysis demonstrated that available lattice oxygen was present in the Mn/Ce_0.65Zr_0.35O₂-K-0.2 catalyst. Therefore, the Mn/Ce_0.65Zr_0.35O₂-K-0.2 catalyst exhibited the best redox properties and oxygen mobility of the prepared samples and showed excellent activity toward toluene oxidation. Therefore, it was concluded that the addition of an appropriate amount of K improved the redox performance of the catalyst and increased the number of surface defect sites and mobility of the lattice oxygen of the catalyst as well as the concentration of the surface active oxygen species, thereby significantly improving catalytic ability.     

NiO/TiO2异质结构纳米管阵列膜对不锈钢的光生阴极保护及其储能性能

本工作通过修饰TiO₂制备半导体复合膜,提高其光吸收和光电化学性能,以期应用于光生阴极保护。先采用阳极氧化法在Ti表面制备TiO₂纳米管阵列膜,再应用水热处理法在膜表面沉积NiO纳米颗粒,形成具有异质结构纳米管复合膜。利用扫描电子显微镜、X-射线衍射、X-射线光电子能谱、紫外-可见吸收光谱、光致发光谱和光电化学技术对制备的纳米膜进行表征。结果表明,与纯TiO₂纳米管膜比较,NiO/TiO₂纳米管复合膜的光吸收扩展到可见光区。白光照射下,其在0.5 mol·L^?1 KOH和1 mol·L^?1 CH3OH混合液中的光电流密度达到176μA·cm^?2,是纯TiO₂纳米管膜的2倍。复合膜具有良好的光生阴极保护作用,与0.5 mol·L^?1 NaCl溶液中的403不锈钢耦连后,可使其电极电位下降440 mV,在光照2.5 h再转为暗态后,因具有电荷储存能力还可继续提供约15.5 h的阴极保护效应。     

22Cr双相不锈钢钝化膜组成及其半导体性能研究

借助于Mott-Schottky方程分析了成膜电位、成膜时间、成膜温度以及氯离子等因素对22Cr双相不锈钢在碳酸氢钠/碳酸钠缓冲溶液中所成钝化膜半导体性能的影响, 同时借助于X射线光电子能谱(XPS)技术分析了所成钝化膜的组成. 结果表明: 22Cr双相不锈钢在碳酸氢钠/碳酸钠缓冲溶液中所成钝化膜呈n-p型半导体结构, 钝化膜内施主/受主密度随成膜电位增加、成膜时间延长、成膜温度降低、以及介质中氯离子浓度的降低而减小, 同时膜对基体保护作用随这些因素变化而增强. 钝化膜的XPS分析表明, 钝化膜呈现双层结构, 外层膜主要由三价铁的氧化物(Fe2O3)组成, 内层膜主要由三价铬氧化物(Cr2O3)以及少量二价铁氧化物(FeO)组成.     

甲苯常压催化氧化制苯甲酸及其它芳烃的氧化反应的研究

以２５％甲苯无水乙酸作反应液，钴、锰和铵的混合盐作催化剂，乙腈作促进剂，纯氧为氧化剂，在１１０℃±２℃下，常压反应１５ｈ，苯甲酸收率达８５％。用该催化剂体系氧化其它芳烃时，亦可获得类似结果。若芳烃侧链烷基Ｒ＝Ｃ１～Ｃ６时，首先起反应的是与苯环相邻的碳原子，伯碳由醛变为酸；仲碳由酮升温后断链变酸；叔碳或烯键则直接断键变为酸。     

Application of Catalytic Wet Air Oxidation to Treatment of Landfill Leachate on Co／Bi Catalyst

Catalytic wet air oxidation(CWAO) was employed to reduce the organic compounds in landfill leachate and the effects of temperature, oxygen pressure, catalyst dosage, and concentration of the organic compounds on the TOC and CODcr removal rates were studied. The degradation kinetics of landfill leachate was also investigated and an exponential experiential model consisting of four influential factors was established to describe the reduction of the organic compounds in the landfill leachate. Meanwhile, the GC-MS technique was used to detect the components of the organic intermediates for the inference of the decomposition mechanisms of the organic compounds in landfill leachate. The results reveal that the reaction temperature and the catalyst dosage are the most important factors affecting the degradation reaction of the organic compounds and that the principal intermediates confirmed by GC-MS are organic acids at a percentage of more than 88% with no aldehydes or alcohols detected. The decomposition mechanisms of the organic compounds in landfill leachate were inferred based on the GC-MS information as follows;the activated gas phase O2 captured the hydrogen of the organic pollutants to produce free radicals, which then initiated the catalytic reaction. So most of the organic compounds were oxidized into CO2 and H2O ultimately. In general, catalytic wet air oxidation over catalyst Co3O4/Bi2O3 was a very promising technique for the treatment of landfill leachate.     

VOSO_4/活性炭上常压催化氧化乳酸乙酯合成丙酮酸乙酯

以氧化改性活性炭为载体,用浸渍法制备了系列VOSO4/活性炭催化剂(VO/ACO).采用FT-IR、XRD、ICP和比表面及孔结构测定等表征了催化剂组成与结构.考察了VO/ACO催化剂在常压分子氧氧化乳酸乙酯中的催化作用.结果表明,氧化活性炭是氧钒催化剂的有效载体,以pH=3的VOSO4溶液浸渍得到的VO-3/ACO催化剂具有优良的催化性能,在二氯乙烷中常压,80℃反应18 h,乳酸乙酯转化完全,丙酮酸乙酯的选择性达95.2%.催化剂重复使用三次后的性能基本保持不变.     

以Au(PPh3)(NO3)为前体的Au/NiO催化剂的制备及其对CO的催化氧化

采用有机金属配合物固载法,将金的有机配合物Ａｕ（ＰＰｈ３）（ＮＯ３）沉积于刚制备出的Ｎｉ（ＯＨ）２沉淀上,与其表面的－ＯＨ基反应,再于注动空气中程序升温焙烧,制和轩出了颗粒度小,分散度高的金催化剂,改变制备条件,研究其对催化剂活性的影响。结果表明,以Ｋ２ＣＯ３作为制备Ｎｉ（ＯＨ）２的沉淀剂,金担载量为３％（质量分数）,在焙烧温度为３００℃的条件下,制备出的负载型金催化剂Ａｕ／ＮｉＯ对ＣＯ的低温氧化     

铈的引入对负载钯阳极氧化膜不锈钢丝网催化剂结构和性能的影响

通过阳极氧化技术制备了一种新型的0.75%Ce-0.5%Pd/不锈钢丝网催化剂. 采用扫描电镜(SEM)和程序升温还原技术(TPR)对催化剂进行了表征. 考察了稀土铈的引入对催化剂上甲苯、丙酮和乙酸乙酯氧化活性的影响, 结果显示, 在不锈钢丝网载体表面处理过程中引入阳极氧化技术, 使之自组织生长了一层多孔氧化膜, 提供了活性组分CeO2和Pd相互作用的平台. 氧化铈的引入, 使不锈钢丝网载体表面的多孔氧化膜形成了独特的海绵状蜂窝结构, 有利于活性组分Pd的分散锚定. 0.75%Ce-0.5%Pd/不锈钢丝网催化剂对甲苯、丙酮和乙酸乙酯的完全转化温度分别为200, 240和260 ℃, 具有良好的催化消除活性. 催化剂的反应活性与稀土CeO2的引入及其在阳极氧化膜上形成独特的形貌有关.     

经阳极氧化处理的不锈钢负载贵金属新型催化剂用于挥发性有机化合物的治理

 催化氧化是一种处理VOCs有效的节能和经济的方法。不锈钢在工业上有很多的应用。由于其具有耐腐蚀性，而且其表面经阳极氧化能形成一层氧化膜，从而可应用于很多场合。但是以其为载体制成催化剂以处理VOCs还未见报告。本文介绍一种新型的催化剂，该催化剂以不锈钢阳极氧化膜为载体负载贵金属以用于VOCs处理。尤其是在经过1000℃的焙烧以后，对甲苯的燃烧仍然有良好的活性。 实验中的催化剂载体为不锈钢片（1Cr18Ni9Ti,0.3mm）。在30wt%的硫酸溶液中经过阳极氧化处理（选择40min，电流密度为1.5 A/dm3的条件）。然后在H2 [PtCl6] 和 PdCl2溶液中, 通过浸渍法将贵金属浸渍于载体而制得。 实验在固定床上进行，以甲苯为反应物，表1为评价结果。由表1可见Pt0.01wt%-Pd0.02wt%负载于不锈钢阳极氧化膜以后的催化剂，对于甲苯有良好的燃烧活性，尤其是，经过1000℃焙烧的催化剂的活性要比500℃ 和800℃ 被烧的催化剂的活性更高。 通过SEM表征了Pt0.01wt%-Pd0.02wt%不锈钢催化剂。图1a中空白的不锈钢载体的表面相对光滑，经过阳极氧化以后表面呈现均匀分布的微米粒径（0.3微末）复合氧化膜，与金属基体的接合牢固，表面的粗糙度也明显增加（Fig1b），可以有效地作为有机废气治理催化剂的担体。从而表现出较高的VOCs氧化活性。温度焙烧对催化剂的活性有很明显的影响，在经过500℃焙烧以后，催化剂表面有较大的颗粒团聚。随着温度提高到800℃和1000℃，其表面颗粒更趋于均匀且近似呈现一种接近纳米粒径的复合氧化膜结构；在甲苯的催化燃烧上，更是表现出很好的效果。 通过实验结果表明由于该催化剂具有很高VOCs去除活性，良好的热稳定性；催化剂容易加工成蜂窝，热稳定性好，机械强度高，抗机械震动，易导热的特性，在处理VOCs方面有很好的应用前景。     

Au/CeO2催化剂的制备及其对CO催化氧化性能的研究

采用水溶液沉淀法和沉积-沉淀法分别制备了CeO2载体及相应Au/CeO2催化剂,以CO氧化反应为表征反应,考察了载体制备条件,催化剂的焙烧温度、预处理温度和气氛以及活性组分负载量对催化剂性能的影响,并对催化剂进行了BET、XRD和TEM表征,分析了影响催化剂活性的原因.结果表明,载体的制备条件对催化剂的活性有一定影响,经微波处理的载体负载活性组分后,由于活性组分和载体的接触较紧密,因此有利于催化剂活性的提高.催化剂的最佳焙烧温度为300℃,最佳活化温度为300℃,气氛为空气,最佳金负载量为4%.     

N-Hydroxyphthalimide/Cobalt Acetate,a New Catalytic Oxidative System for the Synthesis of Benzimidazoles

Benzimidazoles are readily prepared from 1,2-phenylenediamine and an aldehyde using air and catalytic N-hydroxyphthalimide/Co(OAc)₂ as the oxidant. Both electron-donating and electron-withdrawing groups are tolerated.     

制备工艺条件对SO42-/TiO2-Al2O3-Al固体酸催化剂性能影响

采用铝阳极氧化法制备了Al2O3-Al-体型多孔氧化铝载体,再采用电沉积技术将TiO2沉积到氧化铝多孔的纳米孔道内,制备了催化精馏专用SO42-/TiO2-Al2O3-Al型固体酸催化剂,并以乙酸乙酯合成为模型反应,考察了水封条件,电沉积电压、电沉积时间等制备工艺条件对催化剂活性的影响.实验结果表明,适宜的制备条件为水封温度为50℃,水封时间为1 h,电沉积电压为6V,电沉积时间为30 min,在此制备条件下,醋酸转化率为31.34%.采用扫描电镜(SEM),X射线衍射分析(XRD)手段对所制备催化剂进行了表征.结果表明:阳极氧化铝膜的结构为无定型结构,TiO2在载体上呈高度分散状态.