Preparation of ZrO2-TiO2-CeO2 and Its Application in the Selective Catalytic Reduction of NO with NH3

TiO₂,ZrO₂-TiO₂,andZrO₂-TiO₂-CeO₂ were prepared by co-precipitation method and characterized by X-ray diffraction (XRD), specific surface area measurements (BET), temperature programmed desorption (NH₃-TPD), oxygen storage capacity (OSC), and temperature programmed reduction (H₂-TPR). The results showed that ZrO₂-TiO₂-CeO₂ exhibited large number of surface strong acid, possessed some oxygen storage capacity, and strong redox property. The three materials were used as supports and the monolith catalysts were prepared with 1% (w) V₂O₅ and 9% (w)WO₃ for selective catalytic reduction (SCR) of NO with ammonia in the presence of excessive O₂, and the results of catalytic activity showed that the catalyst used ZrO₂-TiO₂-CeO₂ as support yielded nearly 100% NO conversion at 275 °C at a gas hourly space velocity (GHSV) of 10000 h⁻¹, and it had the best catalytic activity and showed great potential for practical application.     

Al含量对Pt-SO2-4 /ZrO2-Al2O3固体超强酸催化

通过向SO^2-₄ /ZrO₂催化剂中同时引入适量的Pt和Al₂O₃, 制备出了具有较高催化性能和稳定性的Pt-SO^2-₄ /ZrO₂-Al₂O₃型固体超强酸催化剂. 以正戊烷异构化反应为探针, 考察了Al含量对催化剂性能的影响; 并采用X射线衍射(XRD)、比表面积测定(BET)、红外(IR)光谱、程序升温还原(TPR)、热重-差热分析(TG-DTA)和氨-程序升温脱附(NH₃-TPD)手段对催化剂进行了表征. 结果表明, Al能够提高ZrO₂的晶化温度, 抑制硫的分解, 增加催化剂的比表面积, 增强硫氧键的结合, 提高催化剂的还原性能, 增加催化剂的酸强度和酸总量. 当Al₂O₃含量(质量分数, w)为5.0%时, Pt-SO^2-₄ /ZrO₂-Al₂O₃固体超强酸催化剂的催化活性最好, 在100 h内异戊烷收率可稳定在52.0%以上, 选择性在98.2%以上.     

Catalytic Performance of Spherical MCM-41 Modified with Copper and Iron as Catalysts of NH3-SCR Process

Spherical MCM-41 with various copper and iron loadings was prepared by surfactant directed co-condensation method. The obtained samples were characterized with respect to their structure (X-ray diffraction, XRD), texture (N₂ sorption), morphology (scanning electron microscopy, SEM), chemical composition (inductively coupled plasma optical emission spectrometry, ICP-OES), surface acidity (temperature programmed desorption of ammonia, NH₃-TPD), form, and aggregation of iron and copper species (diffuse reflectance UV-Vis spectroscopy, UV-Vis DRS) as well as their reducibility (temperature programmed reduction with hydrogen, H₂-TPR). The spherical MCM-41 samples modified with transition metals were tested as catalysts of selective catalytic reduction of NO with ammonia (NH₃-SCR). Copper containing catalysts presented high catalytic activity at low-temperature NH₃-SCR with a very high selectivity to nitrogen, which is desired reaction products. Similar results were obtained for iron containing catalysts, however in this case the loadings and forms of iron incorporated into silica samples very strongly influenced catalytic performance of the studied samples. The efficiency of the NH₃-SCR process at higher temperatures was significantly limited by the side reaction of direct ammonia oxidation. The reactivity of ammonia molecules chemisorbed on the catalysts surface in NO reduction (NH₃-SCR) and their selective oxidation (NH₃-SCO) was verified by temperature-programmed surface reactions.     

合成方法对Rh/CeO2-ZrO2-La2O3催化剂的结构、表面性能及DeNOx活性的影响

用沉积沉淀法合成两种不同系列的CeO2-ZrO2-La2O3混合氧化物(ZrO2和La2O3沉积CeO2粒子(标记为A-x)以及CeO2和La2O3沉积ZrO2粒子(标记为B-x)),并用作Rh催化剂的载体。XRD、拉曼、TPR、XPS和O2脉冲等表征结果显示出不同的沉积顺序将导致不同的结构和氧化还原性能,且B-x具有更高的氧迁移性、储氧能力和表面Ce浓度。当其负载Rh后,Rh/B-x催化剂具有更高的NO和CO转化率及N2选择性,且Ce的最佳含量为50at%。这可能归因于Rh负载于富铈表面形成更多有利于NO分解的表面Ce3+活性位。     

ZrO4/SiO2-Al2O3催化肉桂醛MPV转移加氢性能

以九水合硝酸铝（Al（NO₃）₃·9H₂O）与正硅酸乙酯（TEOS）为前驱盐,采用溶胶-凝胶法制备一系列不同Al₂O₃含量的SiO₂-Al₂O₃复合氧化物,并通过浸渍硝酸氧锆引入ZrO₂,制备ZrO₂/SiO₂-Al₂O₃复合氧化物催化剂,考察催化剂在肉桂醛（CAL）MPV转移加氢中的催化性能,并结合N₂物理吸附、X射线粉末衍射（XRD）、傅里叶变换红外光谱（FTIR）、NH₃-程度升温脱附（NH₃-TPD）、Py-原位红外（Py-IR）等技术,研究催化剂结构、织构以及表面性质与其催化性能间的构效关系.研究表明,所制备的催化剂均以L酸为主,并含有少量B酸中心,这使得加氢产物以肉桂醇（COL）为主,并含有少量1-苯丙烯-2-丙基醚（CPE）.Al₂O₃含量不仅影响催化剂表面的酸中心数量,而且对催化剂的织构参数有较大影响.随Al₂O₃含量的增加,催化剂表面L酸与B酸中心均有所增加,而孔径则持续变小,这使得催化反应呈现CAL转化率先增加后减少、目标产物COL选择性先稍有减小后有所增加的趋势.在Si/Al比为2时,催化剂具有最优的催化性能,优化反应条件下,CAL转化率达96%,目标产物COL选择性达90%.     

以ZrO2-TiO2为载体的整体式锰基催化剂应用于低温NH3-SCR反应

以MnO2为活性组分, Fe2O3为助剂, 制备了以TiO2及ZrO2-TiO2为载体的整体式催化剂. 考察了它们在不同温度焙烧后应用于富氧条件下, NH3选择性催化还原(NH3-SCR)氮氧化物的低温反应性能和高温稳定性. 用X射线衍射(XRD)实验、比表面积测定(BET)、储氧性能测定(OSC)及程序升温还原(H2-TPR)等方法对催化剂进行了表征. 结果表明, 以ZrO2-TiO2为载体的催化剂具有很好的高温热稳定性, 并具有较高的比表面积和储氧能力, 同时具有较强的氧化能力. 催化剂的活性测试结果表明, 以ZrO2-TiO2为载体的整体式锰基催化剂明显地提高了NH3-SCR反应的低温活性, 具有良好的应用前景.     

WO_3对MnO_x-CeO_2/ZrO_2-TiO_2整体式催化剂NH_3选择性催化还原NO_x性能的影响

以ZrO2-TiO2为载体,MnOx-CeO2为活性组分,WO3为助剂制备了MnOx-CeO2/WO3/ZrO2-TiO2整体式催化剂,考察了添加不同质量分数的WO3对低温氨选择性催化还原(NH3-SCR)氮氧化物反应性能的影响.通过低温N2吸附-脱附,X射线衍射(XRD),X射线光电子能谱(XPS),NH3程序升温脱附(NH3-TPD)等手段对催化剂进行表征.实验结果表明,与未添加WO3的催化剂相比,含有10.0%(w)WO3的催化剂具有较好的织构性能,且具有较多的中强酸位,较好的氧化性能,表现出良好的NH3-SCR活性和较宽的活性温度窗口(空速为10000h-1时,在144-374℃之间,NOx转化率为90%以上),该催化剂在低温净化氮氧化物中具有潜在的应用前景.     

国产航空煤油裂解催化剂Pt/ZrxTixAl1-2xO2的性能

采用共沉淀法制备了一系列Zr_xTi_xAl_1-2xO₂复合氧化物载体材料,考察了其作为裂解催化剂载体对航空煤油裂解反应的影响.?采用全自动吸附仪、X射线衍射、扫描电镜/能谱仪联用、NH₃-程序升温脱附等手段对催化剂进行了表征.?结果表明,当ZrO₂：TiO₂：Al₂O₃质量比为1：1：3时催化剂具有最大的比表面积和孔容;具有最强的表面酸性和最集中的强酸中心密度,且具有良好的再生功能.?实验结果表明,载体ZrO₂：TiO₂：Al₂O₃质量比为1：1：3时催化剂上650?℃裂解产气量较热裂解提高了2.1倍,700?℃时提高1.4倍.?另外,该系列载体材料经1000?℃焙烧5?h后,所制得的催化剂几乎失去了催化活性.     

ZrO_2负载Pt催化巴豆醛选择性加氢

以高比表面积ZrO2为载体,采用浸渍法制备了负载型Pt催化剂,应用于常压下气相巴豆醛加氢反应,考察了Pt负载量和H2还原温度等对巴豆醛选择性加氢性能的影响.实验结果表明,Pt负载量(质量分数)为3%的3Pt/ZrO2催化剂经500℃还原后,具有较高的巴豆醛选择性加氢性能:巴豆醛转化率为27%,巴豆醇的选择性为55%.X射线粉末衍射(XRD)分析,CO化学吸附,NH3程序升温脱附(NH3-TPD)表征结果表明Pt/ZrO2催化剂上Lewis强酸中心和适宜的Pt颗粒(约为8nm)有利于巴豆醛选择性加氢生成巴豆醇.     

CuFe-SAPO-34分子筛的结构和催化性能研究

采用一步水热合成法,通过调变初始凝胶中的硅铁比,制备系列铜铁含量不同的CuFe-SAPO-34催化剂用于NH₃选择性催化还原NO_x反应（NH₃-SCR）,并采用ICP、XRD、SEM、BET、H₂-TPR等方法对其结构进行表征.结果表明,CuFe-SAPO-34催化剂具有典型的CHA结构,Cu和Fe均处于分子筛载体的离子交换位.当初始凝胶SiO₂/Fe₂O₃=10时,Cu_2.5Fe_3.1-SAPO-34催化剂具有最大的比表面积和孔容.掺杂适量的Fe,可提高活性物种Cu²⁺的比例及其氧化还原性能,显著降低Cu物种的聚集程度.NH₃-SCR反应结果表明,Cu_2.5Fe_3.1-SAPO-34催化剂具有最宽的反应温度窗口.与Cu-SAPO-34相比,Fe的掺杂显著提高了其高温段的催化活性和低温抗水能力,提高了Cu-CHA催化剂在实际应用中的稳定性.     

以四乙基氢氧化铵为模板并通过转晶法合成高硅铝比的SSZ⁃13沸石分子筛

使用四乙基氢氧化铵为有机模板剂,以低硅铝比(nSiO2/nAl2O3)的Y分子筛为铝源,通过转晶法制备结晶度良好的SSZ?13沸石分子筛。从凝胶配比方面考察了不同原料组成对分子筛合成的影响,并通过X射线衍射(XRD)、扫描电子显微镜(SEM)及电感耦合等离子体(ICP)表征水热反应过程中的物相、形貌、硅铝比等变化,揭示分子筛合成过程。氨选择性催化还原(NH3?SCR)反应显示该分子筛具有优异的催化活性,为其工业上的广泛应用提供了可能性。     

非晶态ZrO_2镶嵌的超细CeO_2催化HCl氧化

采用不同方法制备了铈锆复合氧化物催化剂用于催化HCl氧化反应。自发沉积策略制备的CeO_2@ZrO_2催化剂中,超细CeO_2纳米粒子均匀的镶嵌于非晶态ZrO_2中。CeO_2粒子显著的"尺寸效应"使得该催化剂具有更高的Ce~(3+)和氧空位浓度,而较高的Ce~(3+)和氧空位浓度使得催化剂具有优异的低温氧化还原性能和储释氧能力。催化性能测试表明,CeO_2@ZrO_2催化剂展现出最好的催化活性(1.90 gCl2·gcat~(-1)·h~(-1)),同时CeO_2粒子周围非晶态的ZrO_2阻碍CeO_2的高温烧结,提高了该催化剂的稳定性。     

非晶态ZrO2镶嵌的超细CeO2催化HCl氧化

采用不同方法制备了铈锆复合氧化物催化剂用于催化HCl氧化反应。自发沉积策略制备的CeO₂@ZrO₂催化剂中,超细CeO₂纳米粒子均匀的镶嵌于非晶态ZrO₂中。CeO₂粒子显著的“尺寸效应”使得该催化剂具有更高的Ce³⁺和氧空位浓度,而较高的Ce³⁺和氧空位浓度使得催化剂具有优异的低温氧化还原性能和储释氧能力。催化性能测试表明,CeO₂@ZrO₂催化剂展现出最好的催化活性（1.90 g_Cl2·g_cat^-1·h^-1）,同时CeO₂粒子周围非晶态的ZrO₂阻碍CeO₂的高温烧结,提高了该催化剂的稳定性。     

Synthesis and properties of MoO3/ZrO2 solid acid catalysts for the preparation of polydimethylsiloxane (PDMS) via octamethylcyclotetrasiloxane (D4) ring-opening

A series of MoO₃/ZrO₂ catalysts were prepared by impregnation method, and characterized by X-ray diffraction (XRD), specific surface area (BET) and temperature-programmed desorption of NH₃ (NH₃-TPD). The polydimethylsiloxane (PDMS) was prepared by ring-opening polymerization from D₄ and MM with MoO₃/ZrO₂ catalysts. The effects of MoO₃/ZrO₂ catalysts preparation conditions on PDMS molecular weight and reaction conversion rate were discussed. Moreover, the effects of reaction conditions on the ring-opening polymerization were also studied. During the preparation of PDMS, the molecular weight of the product can be controlled by adjusting the mass ratio of D₄:MM. The MoO₃/ZrO₂ catalyst was compared with other catalysts during the ring-opening process, and the repeated times of MoO₃/ZrO₂ catalysts were also studied. The results showed that MoO₃/ZrO₂ catalyst had more excellent catalytic performance, for ring-opening process, and when the repeated times was more than 5, the catalytic activity decreased significantly. In addition, the kinetics of D₄ ring-opening polymerization with the MoO₃/ZrO₂ catalyst was investigated.     

NH3-SCR脱硝催化剂抗硫性能的研究进展

氮氧化物(NO_x)是一种重要的大气污染物, 它造成严重的环境问题, 同时威胁人类健康. 以钢铁烧结烟气为代表的固定源和以柴油机尾气为代表的移动源是氮氧化物的主要来源. 氨气选择性催化还原法(NH₃-SCR)是目前最有效且应用最广泛的NO_x脱除技术. 然而, 无论是固定源还是移动源上NH₃-SCR催化剂, 都不可避免地会被SO₂毒化, 造成催化剂失活, 限制了NH₃-SCR技术的进一步应用. 因此, 研究NH₃-SCR催化剂的SO₂中毒机制以及提高催化剂的抗硫性能至关重要. 我们对固定源脱硝的金属氧化物和移动源上脱硝的Cu基分子筛这两类不同催化剂体系的SO₂中毒机制的研究进展进行了介绍, 并对这两种催化剂上提高抗硫性能改性方法的研究进展进行了评述, 为未来的研究提供了参考.     

铜物种对Cu/Fe2O3水煤气变换反应催化剂性能的影响

采用共沉淀法制备了系列铜负载量不同的Cu/Fe₂O₃水煤气变换(WGS)催化剂,并考察了铜负载量对催化剂结构和水煤气变换反应性能的影响. 结果表明,Cu/Fe₂O₃催化剂呈现出良好的水煤气反应性能,当CuO质量分数为20%时,催化剂的WGS性能最优,250 ℃时CO转化率高达97.2%,同时热稳定性也最好. 运用X射线粉末衍射(XRD)、N₂物理吸脱附和H₂程序升温还原(H₂-TPR)等手段对Cu/Fe₂O₃催化剂的物相、织构特征及还原性能进行了表征,结果表明,CuFe₂O₄物种的存在极大地改善了催化剂的还原性能和WGS反应活性. 这是由于CuFe₂O₄特殊的尖晶石结构有利于Cu微晶的稳定;同时,CuFe₂O₄在低温下即被还原为单质铜,有利于促进催化剂体系中电子的转移. 此外,通过(NH₄)₂CO₃溶液处理,研究了独立相CuO对Cu/Fe₂O₃催化剂WGS反应性能的影响,结果发现,独立相CuO的存在,有利于H原子在各组分传递,从而促进催化剂的CuFe₂O₄的还原,改善Cu/Fe₂O₃催化剂的WGS反应性能.     

Deactivation and regeneration of the B2O3/TiO2-ZrO2 catalyst in the vapor phase Beckmann rearrangement of cyclohexanone oxime

The deactivation and regeneration of B₂O₃/TiO₂-ZrO₂ catalyst for the vapor phase Beckmann rearrangement of cyclohexanone oxime to -caprolactam were studied. The fresh, deactivated and regenerated catalysts were characterized by using adsorption of nitrogen, X-ray diffraction (XRD), thermogravimetry (TG) and NH₃-temperature-programmed desorption (NH₃-TPD) techniques. The crystal structure and pore size distribution of the catalyst were retained after reaction, but the number of acid sites decreased significantly. There was a relationship between the amount of coke deposited on the catalyst and the decline in catalytic activity. These results suggest that the coke deposition on the surface of catalyst is mainly responsible for the catalyst deactivation. The catalytic activity can be recovered completely after calcining the deactivated catalyst in air flow at 600 °C for 8 h.     

以ZrO2-TiO2为载体的整体式锰基催化剂应用于低温NH3-SCR反应

以MnO2为活性组分,Fe2O3为助剂,制备了以TiO2及ZrO2-TiO2为载体的整体式催化剂.考察了它们在不同温度焙烧后应用于富氧条件下,NH3选择性催化还原.(NH3-SCR)氮氧化物的低温反应性能和高温稳定性.用X射线衍射(XRD)实验、比表面积测定(BET)、储氧性能测定(OSC)及程序升温还原(H2-TPR)等方法对催化剂进行了表征.结果表明,以ZrO2-TiO2为载体的催化剂具有很好的高温热稳定性,并具有较高的比表面积和储氧能力.同时具有较强的氧化能力.催化剂的活性测试结果表明,以ZrO2-TiO2为载体的整体式锰基催化剂明显地提高了NH3-SCR反应的低温活性,具有良好的应用前景.     

焙烧温度对MnOx-CeO2-WO3-ZrO2催化剂上NH3选择性还原NO的影响

采用共沉淀法制备了MnO_x-CeO₂-WO₃-ZrO₂催化剂,考察了催化剂焙烧温度对O₂和H₂O存在下NH₃选择性催化还原（NH₃-SCR） NO的影响,并利用低温N₂吸附、X射线衍射（XRD）、透射电镜（TEM）、X射线光电子能谱（XPS）、NH₃程序升温脱附（NH₃-TPD）和CO脉冲反应对催化剂进行了表征. 结果表明在NH₃-SCR反应中,催化剂的低温活性随焙烧温度的提高而降低,这是由于催化剂表面化学吸附氧和酸性位减少引起的;催化剂的高温活性随焙烧温度的提高先增加后减小,这与催化剂表面最易释放氧数量的变化趋势相反. 700 ℃焙烧的催化剂具有良好的低温活性和最宽的反应温度窗口,在空速为90000 h^-1的条件下,该催化剂的起燃温度（50% NO转化率）为189 ℃,且反应温度在218-431 ℃范围内,NO转化率可达到80%-100%.     

三维有序大孔Ag/ZrO2-TiO2：制备及紫外光催化降解染料和水杨酸性能

采用聚苯乙烯(PS)微球作为模板剂,经溶胶-凝胶及煅烧后处理的方法制备了三维有序大孔(3DOM)复合材料Ag/ZrO2-TiO2。通过FTIR、XRD、XPS、N2吸附-脱附和SEM-EDS等对其进行了表征。结果显示,经PS微球作用后的复合材料Ag/ZrO2-TiO2具有锐钛矿晶型结构,其Ag以单质形式存在。该复合材料的孔结构高度有序,属三维有序大孔,平均孔直径为120 nm,孔壁由紧密堆积的Ag/ZrO2-TiO2纳米晶粒组成,孔收缩率约为40%。该复合材料表现出较好的紫外光催化降解水杨酸和甲基橙等染料性能,其活性明显高于商用光催化剂(Degussa P-25)、Ag/ZrO2-TiO2和3DOM ZrO2-TiO2,在90 min内对甲基橙的降解率达80.1%。