Ag/Yb掺杂对Ca_3Co_(3.9)Cu_(0.1)O_(9-δ)热电性能的影响

采用溶胶凝胶及冷压方法,通过在Ca_3Co_(3.9)Cu_(0.1)O_(9-δ)体系中引入不同量的Ag~+或Yb~(3+)离子来调控体系的热电性能,制备了可在300~880 K下稳定存在且热电性能优良的陶瓷材料Ca_(3-x)Ag_xCo_(3.9)Cu_(0.1)O_(9-δ)(x=0.1,0.15,0.2,0.3)和Ca_(3-y)Yb_yCo_(3.9)Cu_(0.1)O_(9-δ)(y=0.05,0.1,0.2,0.3).通过X射线衍射(XRD)和扫描电子显微镜(SEM)等测试手段对产物进行了表征,结果显示所制备的样品纯度较高,晶粒均匀,晶粒间较致密.适量的Ag~+,Yb~(3+)离子取代Ca~(2+)离子固溶到晶体中使制备的双掺杂材料晶胞体积发生了变化,但并未引起晶体对称结构的变化.电阻率和Seebeck系数的表征结果说明双掺杂优化了载流子的浓度,随着温度的升高电阻率不断减小,Seebeck系数不断增大.经过计算可知Seebeck系数的增大还有电子有效质量的贡献.热导率表征结果显示双掺杂体系的热导率随着温度的升高而减小,其中声子热导依然起主要作用,这与单掺杂体系的结果一致.随着温度的升高,双掺杂样品Ca_(2.7)Ag_(0.3)Co_(3.9)Cu_(0.1)O_(9-δ)在880 K下ZT值达到最大,为0.2.     

Ag~+,Sr~(2+),Yb~(3+)双掺杂对Ca_3Co_4O_(9-δ)热电性能的影响

采用溶胶-凝胶和冷压方法,在Ca3Co4O9-δ体系中引入不同量的Ag~+,Sr~(2+)或Yb~(3+)离子制备了可在300~870 K下稳定存在且热电性能优良的陶瓷材料Ca_(3-x-y)Ag_xSr_yCo_4O_(9-δ),Ca_(3-x-z)Ag_xYb_zCo_4O_(9-δ)和Ca_(3-y-z)Sr_yYb_zCo_4O_(9-δ)(x,y,z=0.1,0.15,0.2).通过X射线衍射(XRD)、傅里叶变换红外光谱(IR)和扫描电子显微镜(SEM)等手段对产物进行表征.结果显示,所制备的样品纯度较高,晶粒均匀,晶粒间较致密,适量的Ag~+,Sr~(2+),Yb~(3+)离子取代Ca~(2+)离子固溶到晶体中使制备的双掺杂材料晶胞体积发生了变化,但并未引起晶体对称结构的变化.电阻率和Seebeck系数结果表明,双掺杂优化了样品载流子的浓度,使样品电阻率不断减小,并使Seebeck系数的值不断增大.经过计算可知,Seebeck系数随电子有效质量的增大而增大.热导率结果表明,双掺杂的样品热导率随掺杂元素的不同而变化,计算结果显示声子热导依然在样品中占据主体贡献,这与Ca_3Co_4O_(9-δ)单掺杂Ag~+,Sr~(2+)或Yb~(3+)的结果吻合.随着温度的升高,双掺杂样品Ca_(2.7)Ag_(0.2)Yb_(0.1)Co_4O_(9-δ)在870 K下热电优值(ZT)值达到最大(0.18).     

Mixed conductivity, nonstoichiometric oxygen, and oxygen permeation properties in Co-Doped Sr3Ti2O(7-δ)

Electrical conductivity and oxygen permeation rates in Co-doped Sr(3)Ti(2)O(7-δ) with Ruddesden-Popper type structures were investigated. The effects of metal dopants (M) in the Ti site of Sr(3)Ti(2)(M)O(7-δ) on the mixed conductivity were also studied. Doping of Sr(3)Ti(2)O(7-δ) with Co was found to be effective for improving the electrical conductivity as well as the oxygen permeation rate, which could be assigned to the increased oxygen vacancy concentration by doping Co(3+) into Ti(4+) sites. The nonstoichiometric oxygen of these oxides was measured by using a thermal gravimetric method. The creation of oxygen vacancies, which is compensated with Co(3+) doping, leads to higher oxide ion conductivity. The oxygen permeation rate monotonously increased with increasing amounts of Co in the Ti site. Sr(3)Ti(0.8)Co(1.2)O(7-δ) exhibited high oxide ion conductivity and a large oxygen permeation rate. The highest oxygen permeation rate achieved a value of 2.02 cc min(-1) cm(-2) at 1273 K for Sr(3)Ti(0.8)Co(1.2)O(7-δ). Neutron diffraction analysis and redox titration suggests that the oxygen diffusion occurs through oxygen vacancies in the perovskite block, but not through excess oxygen in the rock salt block.     

Recent progress in oxide thermoelectric materials: p-type Ca3Co4O9 and n-type SrTiO3(-)

Thermoelectric energy conversion technology to convert waste heat into electricity has received much attention. In addition, metal oxides have recently been considered as thermoelectric power generation materials that can operate at high temperatures on the basis of their potential advantages over heavy metallic alloys in chemical and thermal robustness. We have fabricated high-quality epitaxial films composed of oxide thermoelectric materials that are suitable for clarifying the intrinsic "real" properties. This review focuses on the thermoelectric properties of two representative oxide epitaxial films, p-type Ca 3Co 4O 9 and n-type SrTiO 3, which exhibit the best thermoelectric figures of merit, ZT (= S (2)sigma Tkappa (-1), S = Seebeck coefficient, sigma = electrical conductivity, kappa = thermal conductivity, and T = absolute temperature) among oxide thermoelectric materials reported to date. In addition, we introduce the recently discovered giant S of two-dimensional electrons confined within a unit cell layer thickness ( approximately 0.4 nm) of SrTiO 3.     

Influence of a nano phase segregation on the thermoelectric properties of the p-type doped stannite compound Cu(2+x)Zn(1-x)GeSe4

Engineering nanostructure in bulk thermoelectric materials has recently been established as an effective approach to scatter phonons, reducing the phonon mean free path, without simultaneously decreasing the electron mean free path for an improvement of the performance of thermoelectric materials. Herein the synthesis, phase stability, and thermoelectric properties of the solid solutions Cu(2+x)Zn(1-x)GeSe(4) (x = 0-0.1) are reported. The substitution of Zn(2+) with Cu(+) introduces holes as charge carriers in the system and results in an enhancement of the thermoelectric efficiency. Nano-sized impurities formed via phase segregation at higher dopant contents have been identified and are located at the grain boundaries of the material. The impurities lead to enhanced phonon scattering, a significant reduction in lattice thermal conductivity, and therefore an increase in the thermoelectric figure of merit in these materials. This study also reveals the existence of an insulator-to-metal transition at 450 K.     

中温固体氧化物燃料电池复合阴极Pr0.6-zSr0.4Co0.8Fe0.2O3-δ-SDC性能研究

采用改进的溶胶-凝胶法合成固体氧化物燃料电池阴极系粉体Pr0.6-zSr0.4Co0.8Fe0.2O3-δ(PSCF)(z=0,0.02,0.05,0.1)。使用X射线衍射(XRD)、扫描电子显微镜(SEM)对其相结构与形貌进行了分析,结果表明:900℃以上焙烧后的阴极粉体Pr0.6-zSr0.4Co0.8Fe0.2O3-δ(z=0,0.02,0.05,0.1)为单一的钙钛矿结构。1000℃烧结的样品内粒子分布比较均匀,且颗粒内部存在一定程度的空隙,并与电解质附着情况良好。用直流四电极法测试阴极体系样品在400～750℃的电导率,发现各试样混合离子电子电导率均高于786 S.cm-1,能够满足固体氧化物燃料电池对阴极电导率的要求。用交流阻抗法测定PSCF-Ce0.8Sm0.2O1.9体系样品的阻抗谱,得到1000℃烧结的阴极体系对称电池在测试温度为750℃z=0,z=0.02,z=0.05时的极化电阻分别为0.041,0.040,0.034Ω.cm-2。     

Potential of Chevrel phases for thermoelectric applications

A low lattice thermal conductivity is one of the requirements to achieve high thermoelectric figures of merit. Several low thermal conductivity materials were identified and developed over the past few years at the Jet Propulsion Laboratory (JPL), including filled skutterudites and Zn₄Sb₃-based materials. A study of the mechanisms responsible for the high phonon scattering rates in these compounds has demonstrated that materials with structures that can accommodate additional atoms in their lattice are likely to possess low lattice thermal conductivity values. Chevrel phases (Mo₆Se₈-type) are just such materials and are currently being investigated at JPL for thermoelectric applications. The crystal structures of the Chevrel phases present cavities which can greatly vary in size and can contain a large variety of atoms ranging from large ones such as Pb to small ones such as Cu. In these materials, small inserted atoms usually show large thermal parameters which indicate that they move around and can significantly scatter the phonons. The electronic and thermal properties of these materials can potentially be controlled by a careful selection of the filling element(s). We have synthesized (Cu, Cu/Fe, Ti)_xMo₆Se₈ samples and report in this paper on their thermoelectric properties. Approaches to optimize the properties of these materials for thermoelectric applications are discussed. Solid State Sciences, 1293-2558/99/7-8/© 1999 Éditions scientifiques et médicales Elsevier SAS. All rights reserved.     

Remarkable enhancement in thermoelectric performance of BiCuSeO by Cu deficiencies

A significant enhancement of thermoelectric performance in layered oxyselenides BiCuSeO was achieved. The electrical conductivity and Seebeck coefficient of BiCu(1-x)SeO (x = 0-0.1) indicate that the carriers were introduced in the (Cu(2)Se(2))(2-) layer by Cu deficiencies. The maximum of electrical conductivity is 3 × 10(3) S m(-1) for Bicu(0.975)Seo at 650 °C, much larger than 470 S m(-1) for pristine BiCuSeO. Featured with very low thermal conductivity (～0.5 W m(-1) K(-1)) and a large Seebeck coefficient (+273 μV K(-1)), ZT at 650 °C is significantly increased from 0.50 for pristine BiCuSeO to 0.81 for BiCu(0.975)SeO by introducing Cu deficiencies, which makes it a promising candidate for medium temperature thermoelectric applications.     

Nanostructured Bi(2-x)Cu(x)S3 bulk materials with enhanced thermoelectric performance

Nanostructured Bi(2-x)Cu(x)S(3) (x = 0, 0.002, 0.005, 0.007, 0.01, 0.03) thermoelectric polycrystals were fabricated by combining mechanical alloying (MA) and spark plasma sintering (SPS) methods. The effect of Cu content on the microstructure and thermoelectric property of Bi(2-x)Cu(x)S(3) bulk samples was investigated. It was found that the subtle tailoring of Cu content could reduce both the electrical resistivity and the thermal conductivity at the same time, and consequently enhancing the thermoelectric property. A low electrical resistivity of 1.34 × 10(-4)Ω m(-1) and a low thermal conductivity of 0.52 W m(-1) K(-1) were obtained for the Bi(1.995)Cu(0.005)S(3) sample at 573 K. The low thermal conductivity is supposed to be due to the nanoscopic Cu-rich regions embedded in the host matrix. A peak ZT value of 0.34 at 573 K was achieved for the Bi(1.995)Cu(0.005)S(3) composition, which is the highest value in the Bi(2)S(3) system reported so far.     

(Ce0.9Nd0.1)1-xMoxO2-δ(0.00≤x≤0.10)的合成、表征与电性能

采用溶胶-凝胶法合成(Ce0.9Nd0.1)1-xMoxO2-δ(x=0.00、0.02、0.05、0.10)氧化物,通过X射线衍射(XRD)、场发射扫描电镜(FESEM)等手段对氧化物进行结构表征,交流阻抗谱测试电性能.结果表明:所有样品均为单一萤石立方结构;少量MoO3的加入提高了材料的致密性,降低了材料的总电阻、晶界电阻和晶界电阻在总电阻中所占比例,提高了材料的电导率.1200 ℃烧结样品24 h,测试温度700℃时,(Ce0.9Nd0.1)1-xMoxO2-δ(x=O.00)总电导率和晶界电导率分别为0.05和O.19 S·m-1,掺Mo材料(Ce0.9Nd0.1)1-xMoxO2(x=0.02)的总电导率和晶界电导率分别为2.42和3.96 S·m-1.     

An X-ray absorption spectroscopic study on mixed conductive La0.6Sr0.4Co0.8Fe0.2O(3-δ) cathodes. I. Electrical conductivity and electronic structure

The electrical conduction mechanism of mixed conductive perovskite oxides, La(0.6)Sr(0.4)Co(0.8)Fe(0.2)O(3-δ), for cathode materials of solid oxide fuel cells has been investigated from electronic structural changes during oxygen vacancy formation. La(0.6)Sr(0.4)Co(0.8)Fe(0.2)O(3-δ) was annealed under various oxygen partial pressures p(O(2))s at 1073 K and quenched. Iodometric titration indicated that the oxygen nonstoichiometry of La(0.6)Sr(0.4)Co(0.8)Fe(0.2)O(3-δ) depended on the annealing p(O(2)), with more oxygen vacancies introduced at lower than at higher p(O(2))s. X-Ray absorption spectroscopic measurements were performed at the O K-, Co L-, Fe L-, Co K-, and Fe K-edges. The valence states of the Co and Fe ions were investigated by the X-ray absorption near edge structure (XANES) at the Co and Fe L(III)-edges. While the Fe average valence was almost constant, the valence of the Co ions decreased with oxygen vacancy introduction. The O K-edge XANES spectra indicated that electrons were injected into the Co 3d/O 2p hybridization state with oxygen vacancy introduction. Both absorption edges at the Co and Fe K-edge XANES shifted towards lower energies with oxygen vacancy introduction. The shift at the Co K-edge resulted from the decrease in the Co average valence and that at the Fe K-edge appeared to be caused by changes in the coordination environment around the Fe ions. The total conductivity of La(0.6)Sr(0.4)Co(0.8)Fe(0.2)O(3-δ) decreased with decreasing p(O(2)), due to a decreasing hole concentration.     

CaMn(1-x)Nb(x)O3 (x < or = 0.08) perovskite-type phases as promising new high-temperature n-type thermoelectric materials

Perovskite-type CaMn(1-x)Nb(x)O(3+/-delta) (x = 0.02, 0.05, and 0.08) compounds were synthesized by applying both a "chimie douce" (SC) synthesis and a classical solid state reaction (SSR) method. The crystallographic parameters of the resulting phases were determined from X-ray, electron, and neutron diffraction data. The manganese oxidations states (Mn(4+)/Mn(3+)) were investigated by X-ray photoemission spectroscopy. The orthorhombic CaMn(1-x)Nb(x)O(3+/-delta) (x = 0.02, 0.05, and 0.08) phases were studied in terms of their high-temperature thermoelectric properties (Seebeck coefficient, electrical resistivity, and thermal conductivity). Differences in electrical transport and thermal properties can be correlated with different microstructures obtained by the two synthesis methods. In the high-temperature range, the electron-doped manganate phases exhibit large absolute Seebeck coefficient and low electrical resistivity values, resulting in a high power factor, PF (e.g., for x = 0.05, S(1000K) = -180 microV K(-1), rho(1000K) = 16.8 mohms cm, and PF > 1.90 x 10(-4) W m(-1) K(-2) for 450 K < T < 1070 K). Furthermore, lower thermal conductivity values are achieved for the SC-derived phases (kappa < 1 W m(-1) K(-1)) compared to the SSR compounds. High power factors combined with low thermal conductivity (leading to ZT values > 0.3) make these phases the best perovskitic candidates as n-type polycrystalline thermoelectric materials operating in air at high temperatures.     

Remarkable dependence of electrochemical performance of SrCo0.8Fe0.2O(3-δ) on A-site nonstoichiometry

SrCo(0.8)Fe(0.2)O(3-δ) is a controversial material whether it is used as an oxygen permeable membrane or as a cathode of solid oxide fuel cells. In this paper, carefully synthesized powders of perovskite-type Sr(x)Co(0.8)Fe(0.2)O(3-δ) (x = 0.80-1.20) oxides are utilized to investigate the effect of A-site nonstoichiometry on their electrochemical performance. The electrical conductivity, sintering property and stability in ambient air of Sr(x)Co(0.8)Fe(0.2)O(3-δ) are critically dependent on the A-site nonstoichiometry. Sr(1.00)Co(0.8)Fe(0.2)O(3-δ) has a single-phase cubic perovskite structure, but a cobalt-iron oxide impurity appears in A-site cation deficient samples and Sr(3)(Co, Fe)(2)O(7-δ) appears when there is an A-site cation excess. It was found that the presence of the cobalt-iron oxide improves the electrochemical performance. However, Sr(3)(Co, Fe)(2)O(7-δ) has a significant negative influence on the electrochemical activity for intermediate-temperature solid oxide fuel cells (IT-SOFCs). The peak power densities with a single-layer Sr(1.00)Co(0.8)Fe(0.2)O(3-δ) cathode are 275, 475, 749 and 962 mW cm(-2) at 550, 600, 650 and 700 °C, respectively, values which are slightly lower than those for Sr(0.95)Co(0.8)Fe(0.2)O(3-δ) (e.g. 1025 mW cm(-2) at 700 °C) but much higher than those for Sr(1.05)Co(0.8)Fe(0.2)O(3-δ) (e.g. only 371 mW cm(-2) at 700 °C). This remarkable dependence of electrochemical performance of the Sr(x)Co(0.8)Fe(0.2)O(3-δ) cathode on the A-site nonstoichiometry reveals that lower values of electrochemical activity reported in the literature may be induced by an A-site cation excess. Therefore, to obtain a high performance of Sr(x)Co(0.8)Fe(0.2)O(3-δ) cathode for IT-SOFCs, an A-site cation excess must be avoided.     

Evolution of cobalt spin states and magnetic coupling along the SrCo(1-x)Sb(x)O(3-δ) system: correlation with the crystal structure

The oxides of the SrCo(1-x)Sb(x)O(3-δ) perovskite family have been recently designed, characterized and described as cathode materials for solid-oxide fuel cells with competitive power performance in the temperature range 750-850 °C. They feature a number of interesting properties including a good electronic conductivity, low electrode polarization resistance and adequate thermal expansion; the crystal structure adopts a 3C corner-linked perovskite network with a considerable number of oxygen vacancies. This paper reports on the effects of Sb-doping on the crystal structure features, the Co oxidation state and magnetic properties related to the presence of spin-state transitions in the Co cations. A phase transition was observed from the tetragonal P4/mmm space group for x≤ 0.15 to the cubic Pm ?3m space group in the x = 0.2 composition from neutron powder diffraction data. For the tetragonal phases the oxygen vacancies were found to be ordered and localized in the axial O2 and equatorial O3 atoms surrounding the Co2 positions. A noticeable distortion of CoO(6) octahedra is observed for x = 0.05 and 0.1, exhibiting a charge-ordering with a mixed oxidation state of Co(3+/4+) at Co1 sites and Co(3+) at Co2 positions: the Jahn-Teller Co(3+) in an intermediate-spin configuration is responsible for the octahedral distortion. Increasing Sb contents promotes a higher average oxidation state of cobalt, from a valence of 3.2+ for x = 0.05 to 3.4+ for x = 0.2, inducing a decrease of the oxygen vacancies and favouring a random distribution over a Pm ?3m cubic symmetry. All the samples present an antiferromagnetic behaviour with a G-type (k = 0) magnetic structure. The increase of the Sb content induces the weakening of the crystal field (Δ(cf)) in the octahedral environment promoting the Co spin-transition from the intermediate-spin to the high-spin configuration, as evidenced by the decrease of the octahedral distortion, increment of the unit-cell volume and enhancement of the ordered magnetic moment.     

Keggin结构钴取代硅钨酸盐聚苯胺掺杂材料的合成及性质

以Keggin结构钴取代杂多硅钨酸盐异构体α，β_i-K_6-nH_n[SiW₁₁Co(H₂O)O₃₉]·xH₂O( β_i=β₁，β₂，β₃)为掺杂剂，采用固相合成法制备了4种聚苯胺掺杂材料。用元素分析、红外光谱、紫外-可见光谱、SEM、X-射线粉末衍射、热重分析等对材料进行了表征，测定了材料的热稳定性、荧光性和导电性。实验结果表明：合成的掺杂态聚苯胺新材料具有较好的热稳定性、荧光性和导电性，室温电导率为7.5 × 10^-2 S·cm^-1，每种掺杂材料都有一个荧光发射峰，其发光中心来自于掺杂态聚苯胺极化子能带与价带之间的跃迁。     

Oxygen surface exchange kinetics of SrTi(1-x)Fe(x)O(3-δ) mixed conducting oxides

The oxygen surface exchange kinetics of mixed conducting perovskite oxides SrTi(1-x)Fe(x)O(3-δ) (x = 0, 0.01, 0.05, 0.35, 0.5) has been investigated as a function of temperature and oxygen partial pressure using the pulse-response (18)O-(16)O isotope exchange (PIE) technique. Arrhenius activation energies range from 140 kJ mol(-1) for x = 0 to 86 kJ mol(-1) for x = 0.5. Extrapolating the temperature dependence to the intermediate temperature range, 500-600 °C, indicates that the rate of oxygen exchange, in air, increases with increasing iron mole fraction, but saturates at the highest iron mole fraction for the given series. The observed behavior is concomitant with corresponding increases in both electronic and ionic conductivity with increasing x in SrTi(1-x)Fe(x)O(3-δ). Including literature data of related perovskite-type oxides Ba(0.5)Sr(0.5)Co(0.8)Fe(0.2)O(3-δ), La(0.6)Sr(0.4)Co(0.2)Fe(0.8)O(3-δ), La(0.6)Sr(0.4)CoO(3-δ), and Sm(0.5)Sr(0.5)CoO(3-δ), a linear relationship is observed in the log-log plot between oxygen exchange rate and oxide ionic conductivity with a slope fairly close to unity, suggesting that it is the magnitude of the oxide ionic conductivity that governs the rate of oxygen exchange in these solids. The distribution of oxygen isotopomers ((16)O(2), (16)O(18)O, (18)O(2)) in the effluent pulse can be interpreted on the basis of a two-step exchange mechanism for the isotopic exchange reaction. Accordingly, the observed power law dependence of the overall surface exchange rate on oxygen partial pressure turns out to be an apparent one, depending on the relative rates of both steps involved in the adopted two-step scheme. Supplementary research is, however, required to elucidate which of the two possible reaction schemes better reflects the actual kinetics of oxygen surface exchange on SrTi(1-x)Fe(x)O(3-δ).     

Nanostructured AgPb(m)SbTe(m+2) system bulk materials with enhanced thermoelectric performance

Nanostructured Ag0.8Pbm+xSbTem+2 (m = 18, x = 4.5) system thermoelectric materials have been fabricated by combining mechanical alloying (MA) and spark plasma sintering (SPS) methods followed by annealing for several days to investigate the effect on microstructure and thermoelectric performance. It was found that appropriate annealing treatment could reduce both the electrical resistivity and the thermal conductivity at the same time, consequently greatly enhancing the thermoelectric performance. A low electrical resistivity of 2 x 10-3 Ohm-cm and low thermal conductivity of 0.89 W m-1 K-1 were obtained for the sample annealed for 30 days at 700 K. The very low thermal conductivity is supposed to be due to the nanoscopic Ag/Sb-rich regions embedded in the matrix. A high ZT value of 1.5 at 700 K has been achieved for the sample annealed for 30 days.     

Phase equilibria,crystal structure at 1373 K and properties of complex oxides in the Nd–Co–Fe–O system

Phase equilibria in the Nd–Co–Fe–O system were systematically studied at 1373 K in air. The homogeneity range and crystal structure of solid solution NdCo_1–xFe_xO₃ (0.0 ≤ x ≤ 1.0) have been studied by the X-ray powder diffraction method. The structural parameters of complex oxides have been refined by the full-profile Rietveld method. It was shown that all oxides reveal practically stoichiometric oxygen composition within the entire temperature range under investigation. The values of thermal expansion coefficients for the cobaltites NdCo_1–xFe_xO₃ (x = 0.3, 0.7) have been calculated within the wide temperature range in air. Chemical stability of NdCo_1–xFe_xO₃ (x = 0.3, 0.7) in respect to the solid electrolyte materials (Ce_0.8Sm_0.2O_2–δ and La_0.88Sr_0.12Ga_0.82Mg_0.18O3-δ) was examined. Electrical conductivity of NdCo_1–xFe_xO₃ (x = 0.3, 0.7) was measured as a function of temperature within the range 300–1373 K in air. It was shown that substitution of cobalt for iron leads to the decrease of conductivity. The isothermal-isobaric cross-section of the phase diagram for the Nd–Co–Fe–O system at 1373 K in air has been presented.     

铈基与钴基Co3O4-CeO2氧载体上甲烷化学链转化特性: 产物选择性控制

采用水热法制备了Co₃O₄/CeO₂(x)[x为钴铈原子摩尔比n(Co):n(Ce)=6:49:1]和Ce_1-yCo_yO_2-δ(y=0.10.4)2个系列复合氧化物, 并表征了材料的物理化学性质, 考察了这些氧化物作为氧载体参与甲烷化学链转化(化学链燃烧和化学链部分氧化)的反应性能. 结果表明, 2类复合氧化物的甲烷反应活性均明显优于单一氧化物CeO₂或Co₃O₄, 但2类氧载体上的甲烷反应产物的选择性具有明显差异. Ce_1-yCo_yO_2-δ氧载体形成了Ce-Co-O固溶体, 储氧能力明显增强, 体相晶格氧迁移速率与甲烷活化速率匹配较好, 甲烷反应产物以CO和H₂的合成气为主, 有利于甲烷的化学链部分氧化. Co₃O₄/CeO₂(x)氧载体中CeO₂与Co₃O₄之间的相互作用改善了材料的储氧能力和氧化活性, 其与甲烷反应时主要生成CO₂, 有利于甲烷化学链燃烧. 连续性化学链循环实验表明, 2类氧载体均具有较好的再生性能和循环稳定性.     

Large thermal conductivity reduction induced by La/O vacancies in the thermoelectric LaCoO3 system

A series of compact La/O-vacant La(1-x)CoO(3-y) compounds were prepared by a cold high-pressure procedure, and their thermoelectric (TE) properties were investigated. Compared with the ion-substituted hole-type LaCoO(3) systems (e.g., La(1-x)Sr(x)CoO(3)), the thermal conduction of La(1-x)CoO(3-y) is noticeably reduced by the La/O vacancies, whereas the electric transport is less influenced, which results in an efficient ZT enhancement. We demonstrate that the large thermal conductivity reduction originates from the strong point-defect scattering, and La(1-x)CoO(3-y) can be rationalized as a partially filled solid solution: La(1-x)?(x)CoO(3-y)?(y), where ? denotes a vacancy. Such intrinsic thermal conductivity suppression provides an effective pathway for the design of better TE materials.