Influence of metal organic and inorganic precursors on spray pyrolyzed ceramic MgO (2 0 0) thin films for epitaxial over layers

The MgO (2 0 0) surface is widely used as a substrate for epitaxial growth of superconducting and ferro-electric films. Highly oriented, single crystalline, extremely flat and transparent MgO films have been successfully deposited on quartz substrates by the chemical spray pyrolysis technique using economically viable metal organic and inorganic precursors under optimized conditions at the substrate temperature of 600 °C. Thermal analysis (TGA/DTA) in the temperature range 30-600 °C with the heating rate of 10 °C/min revealed the decomposition behavior of the precursors and confirmed the suitable substrate temperature range for film processing. The heat of reaction, ΔH due to decomposition of metal organic precursor contributed additional heat energy to the substrate for better crystallization. The intensity of the (2 0 0) peak in X-ray diffraction (XRD) measurements and the smooth surface profiles revealed the dependency of precursor on film formation. The compositional purity and the metal-oxide bond formation were tested for all the films. UV-Vis-NIR optical absorption in the 200-1500 nm range revealed an optical transmittance above 80% and the absorption edge at about 238 nm corresponding to an optical band gap E_g = 5.25 eV. Scanning electron microscopy (SEM) and atomic force microscopy (AFM) micrographs of MgO films confirmed better crystallinity with larger grain size (0.85 μm) and reduced surface roughness (26 nm), respectively.     

HVPE growth of semi-polar (1 1 2¯ 2)GaN on GaN template (1 1 3)Si substrate

The hydride-vapour-phase-epitaxial (HVPE) growth of semi-polar (1 1 2¯ 2)GaN is attempted on a GaN template layer grown on a patterned (1 1 3) Si substrate. It is found that the chemical reaction between the GaN grown layer and the Si substrate during the growth is suppressed substantially by lowering the growth temperatures no higher than 900 °C. And the surface morphology is improved by decreasing the V/III ratio. It is shown that a 230-μm-thick (1 1 2¯ 2)GaN with smooth surface is obtained at a growth temperature of 870 °C with V/III of 14.     

Epitaxial growth of tin oxide film on TiO2(1 1 0) using molecular beam epitaxy

Growth of tin oxide thin films using molecular beam epitaxy in a pyrolyzed nitrogen dioxide atmosphere on a titanium dioxide (1 1 0) substrate was investigated using X-ray photoelectron spectroscopy (XPS), electron diffraction, and atomic force microscopy (AFM). Properties of deposited films were studied for their dependence on substrate temperature and oxidation gas pressure. Analyses using XPS data revealed that tin atoms were fully oxidized to Sn⁴⁺ and SnO₂ films were grown epitaxially in deposition conditions of substrate temperatures of 627 K or higher and NO₂ pressure greater than 3×10⁻³ Pa. At a substrate temperature of 773 K, a smooth surface with atomic steps was visible in the SnO₂ films, but above or below this temperature, fine grains with crystal facets or porous structures appeared. At pressures of 8×10⁻⁴ to 3×10⁻⁴ Pa, the randomly oriented SnO phase was dominantly grown. Further decreasing the pressure, the Sn metal phase, which was epitaxially crystallized at less than 500 K, was also grown.     

Growth of epitaxial ZnO films on Si (1 1 1) substrates with Cr compound buffer layer by plasma-assisted molecular beam epitaxy

Single crystalline ZnO film was grown on (1 1 1) Si substrate through employing an oxidized CrN buffer layer by plasma-assisted molecular beam epitaxy. Single crystalline characteristics were confirmed from in-situ reflection high energy electron diffraction, X-ray pole figure measurement, and transmission electron diffraction pattern, consistently. Epitaxial relationship between ZnO film and Si substrate is determined to be (0 0 0 1)_ZnO‖(1 1 1)_Si and [1 1 2¯ 0]_ZnO‖[0 1 1]_Si. Full-width at half-maximums (FWHMs) of (0 0 0 2) and (1 0 1¯ 1) X-ray rocking curves (XRCs) were 1.379° and 3.634°, respectively, which were significantly smaller than the FWHMs (4.532° and 32.8°, respectively) of the ZnO film grown directly on Si (1 1 1) substrate without any buffer. Total dislocation density in the top region of film was estimated to be ∼5×10⁹ cm⁻². Most of dislocations have a screw type component, which is different from the general cases of ZnO films with the major threading dislocations with an edge component.     

Characterizations of GaN films and AlGaN/GaN heterostructures on vicinal sapphire (0 0 0 1) substrates grown by MOCVD

GaN films and AlGaN/GaN heterostructures grown on vicinal sapphire (0 0 0 1) substrates by metalorganic chemical vapor deposition (MOCVD) are investigated. It is found that surface morphologies of GaN films depend on the vicinal angle, however, they are not sensitive to the inclination directions of the substrate. The optimized vicinal angle for obtaining excellent surface morphology is around 0.5°. This conclusion is also confirmed by characterizing the electrical property of two-dimensional electron gas (2DEG) in the AlGaN/GaN heterostructure.     

The effects of annealing on non-polar (1 1 2¯ 0) a-plane GaN films

Non-polar a-plane (1 1 2¯ 0) GaN films were grown on r-plane sapphire by metal–organic vapor phase epitaxy and were subsequently annealed for 90 min at 1070 °C. Most dislocations were partial dislocations, which terminated basal plane stacking faults. Prior to annealing, these dislocations were randomly distributed. After annealing, these dislocations moved into arrays oriented along the [0 0 0 1] direction and aligned perpendicular to the film–substrate interface throughout their length, although the total dislocation density remained unchanged. These changes were accompanied by broadening of the symmetric X-ray diffraction 1 1 2¯ 0 ω-scan widths. The mechanism of movement was identified as dislocation glide, occurring due to highly anisotropic stresses (confirmed by X-ray diffraction lattice parameter measurements) and evidenced by macroscopic slip bands observed on the sample surface. There was also an increase in the density of unintentionally n-type doped electrically conductive inclined features present at the film–substrate interface (as observed in cross-section using scanning capacitance microscopy), suggesting out-diffusion of impurities from the substrate along with prismatic stacking faults. These data suggest that annealing processes performed close to film growth temperatures can affect both the microstructure and the electrical properties of non-polar GaN films.     

Epitaxial growth of ZnO films on thin FeO(1 1 1) layers

Thin FeO(1 1 1) buffer layers prepared on Mo(1 1 0) substrate were used to grow ordered ZnO films under ultrahigh vacuum condition, and were in situ characterized by various surface analytical techniques. A chemical interaction between Zn (or ZnO) and FeO(1 1 1) can effectively lower the interfacial energy, which is in favor of an epitaxial growth of ZnO on FeO layers. Compared with the MgO(1 1 1) buffer layer used for the growth of ZnO(0 0 0 1) on sapphire (0 0 0 1) surface, the FeO(1 1 1) thin films might be a better one because it is more thermally stable. Our experimental results provide constructive information on the growth mechanism of ZnO-based materials, which is helpful for further understanding the growth mechanism of related oxide materials.     

Heteroepitaxial growth of InN layers on (1 1 1) silicon substrates

Indium nitride (InN) layers were grown on (1 1 1) silicon substrates by reactive magnetron sputtering using an indium target. Atomic force microscope, X-ray diffraction, and Raman spectroscopy analysis revealed that highly c-axis preferred wurtzite InN layers with very smooth surface can be obtained on (1 1 1) silicon substrates at a substrate temperature as low as 100 °C. The results indicate that the reactive sputtering is a promising growth technique for obtaining InN layers on silicon substrates at low substrate temperature with low cost and good compatibility with microelectronic silicon-based devices.     

Growth of thick GaInN on grooved (1 0 1¯ 1¯) GaN/(1 0 1¯ 2¯) 4H-SiC

We succeeded in growing high-crystalline-quality thick (1 0 1¯ 1¯) Ga_0.92In_0.08N films on a grooved (1 0 1¯ 1¯) GaN/(1 0 1¯ 2¯) 4H-SiC underlying layer. We also fabricated GaInN/GaN multiple quantum wells (MQWs) with a peak wavelength of 580 nm on a high-crystalline-quality thick GaInN film. The photoluminescence intensity of the MQWs is about six times higher than that of MQWs grown on planar GaN and twice as high as that of MQWs grown on a GaN underlying layer having the same grooved structure.     

Molecular beam epitaxial growth of hexagonal boron nitride on Ni(1 1 1) substrate

We demonstrate hexagonal boron nitride (h-BN) epitaxial growth on Ni(1 1 1) substrate by molecular beam epitaxy (MBE) at 890 °C. Elemental boron evaporated by an electron-beam gun and active nitrogen generated by a radio-frequency (RF) plasma source were used as the group-III and -V sources, respectively. Reflection high-energy electron diffraction revealed a streaky (1×1) pattern, indicative of an atomically flat surface in the ongoing growth. Correspondingly, atomic force microscopy images exhibit atomically smooth surface of the resulting h-BN film. X-ray diffraction characterization confirmed the crystallinity of the epitaxial film to be h-BN, and its X-ray rocking curve has a full-width at half-maximum of 0.61°, which is the narrowest ever reported for h-BN thin film. The epitaxial alignments between the h-BN film and the Ni substrate were determined to be [0 0 0 1]_h−BN∥[1 1 1]_Ni, [1 1 2¯ 0]_h−BN∥[1¯ 1 0]_Ni, and [1 1¯ 0 0]_h−BN∥[1¯ 1¯ 2]_Ni.     

Structural,electrical and optical properties of SnO2 films deposited on Y-stabilized ZrO2 (1 0 0) substrates by MOCVD

SnO₂ films have been deposited on Y-stabilized ZrO₂ (YSZ) (1 0 0) substrates at different substrate temperatures (500–800 °C) by metalorganic chemical vapor deposition (MOCVD). Structural, electrical and optical properties of the films have been investigated. The films deposited at 500 and 600 °C are epitaxial SnO₂ films with orthorhombic columbite structure, and the HRTEM analysis shows a clear epitaxial relationship of columbite SnO₂(1 0 0)||YSZ(1 0 0). The films deposited at 700 and 800 °C have mixed-phase structures of rutile and columbite SnO₂. The carrier concentration of the films is in the range from 1.15×10¹⁹ to 2.68×10¹⁹ cm⁻³, and the resistivity is from 2.48×10⁻² to 1.16×10⁻² Ω cm. The absolute average transmittance of the films in the visible range exceeds 90%. The band gap of the obtained SnO₂ films is about 3.75–3.87 eV.     

Spectrometric and ellipsometric studies of (1 − x)TiO2 · xLn2O3 (Ln = Nd, Sm, Gd, Er, Yb) thin films

Spectrometric and ellipsometric studies of (1 − x)TiO₂ · xLn₂O₃ (Ln = Nd, Sm, Gd, Er, Yb; x = 0.33, 0.5) thin films at room temperature were performed. The obtained dispersion dependences of refractive indices are successfully described by the optical-refractometric relation. The dependence of optical pseudogap and refractive indices on composition and molar mass of the films is investigated. The influence of compositional disordering on the energy width of the exponential absorption edge is studied.     

Epitaxial films of metals from the platinum group (Ir,Rh, Pt and Ru) on YSZ-buffered Si(1 1 1)

In the present work we have grown twin-free single crystal metal films of iridium (Ir), rhodium (Rh), platinum (Pt) and ruthenium (Ru) on silicon (1 1 1) substrates via an yttria-stabilized zirconia (YSZ) buffer layer. A prerequisite for the realisation of heteroepitaxial metal films without additional texture components was the twin-free deposition of the YSZ films by pulsed laser deposition (PLD). For the metal films on top, a novel two-step growth process was applied with an extremely low deposition rate for the first 20 nm. For all metals, a drastic texture improvement by up to a factor of 9 could be observed compared to the oxide buffer layer. Minimum values were 0.18° (Ir) and 0.12° (Rh) for tilt and twist, respectively. For all four metals investigated, twin-free epitaxial films could be grown on YSZ/Si(1 1 1) whereas the twinning problem for platinum films was solved by decoupling the Pt-YSZ interface via an additional iridium interlayer. The grown metal/YSZ/Si(1 1 1) multilayer samples offer the possibility to integrate a variety of interesting nanostructures and functional materials on silicon. They are now available in 4 in wafer size.     

Maskless selective growth of semi-polar (1 12¯ 2) GaN on Si (3 1 1) substrate by metal organic vapor phase epitaxy

Semi-polar (1 1 2¯ 2) GaN layers were selectively grown by metal organic chemical vapor phase epitaxy on patterned Si (3 1 1) substrates without SiO₂ amorphous mask. The (1 1 2¯ 2) GaN layers could be selectively grown only on Si (1 1 1) facets when the stripe mask width was narrower than 1 μm even without SiO₂. Inhomogeneous spatial distribution of donor bound exciton (DBE) peak in low-temperature cathodoluminescence (CL) spectra was explained by the difference of growth mode before and after the coalescence of stripes. It was found that the emission intensity related crystal defects is drastically decreased in case of selective growth without SiO₂ masks as compared to that obtained with SiO₂ masks.     

GaN grown on (1 1 1) single crystal diamond substrate by molecular beam epitaxy

GaN epilayers are grown on (1 1 1) oriented single crystal diamond substrate by ammonia-source molecular beam epitaxy. Each step of the growth is monitored in situ by reflection high energy electron diffraction. It is found that a two-dimensional epitaxial wurtzite GaN film is obtained. The surface morphology is smooth: the rms roughness is as low as 1.3 nm for 2×2 μm² scan. Photoluminescence measurements reveal pretty good optical properties. The GaN band edge is centred at 3.469 eV with a linewidth of 5 meV. These results demonstrate that GaN heteroepitaxially grown on diamond opens new rooms for high power electronic applications.     

Influence of substrate temperature on nitridation of (0 0 1) GaAs using RF-radical source

The mechanism of nitridation of (0 0 1) GaAs surface using RF-radical source was systematically studied with changing substrate temperature, nitridation time and supplying As molecular beam. It was found from atomic forth microscopy (AFM) measurements that supplying As is very important to suppress the re-evaporation of As atoms and to keep the surface smooth. Reflection high-energy electron diffraction (RHEED) measurements shows that surface lattice constant (SLC) of GaAs of 0.565 nm decreases with increasing the substrate temperature and that it finally relaxes to the value of c-GaN of 0.452 nm, at 570 °C in both [1 1 0] and [1¯ 1 0] directions without concerning with the supply of As molecular beam. But, in the medium temperature range (between 350 and 520 °C), SLC of [1 1 0] direction was smaller than that of [1¯ 1 0] direction. This suggests a relation between the surface structure and the relaxing mechanism of the lattice. The valence band discontinuity between the nitridated layer and the GaAs layer was estimated by using X-ray photoemission spectroscopy (XPS). It was between 1.7 and 2.0 eV, which coincides well with the reported value of c-GaN of 1.84 eV. This suggests that the fabricated GaN layer was in cubic structure.     

Growth of GaN based structures on Si(1 1 0) by molecular beam epitaxy

The growth of GaN based structures on Si(1 1 0) substrates by molecular beam epitaxy using ammonia as the nitrogen precursor is reported. The structural, optical and electrical properties of such structures are assessed and are quite similar to the ones obtained on Si(1 1 1) in-spite of the very different substrate surface symmetry. A threading dislocation density of 3.7×10⁹ cm⁻² is evaluated by transmission electron microscopy, which is in the low range of typical densities obtained on up to 2 μm thick GaN structures grown on Si(1 1 1). To assess the potential of such structure for device realization, AlGaN/GaN high electron mobility transistor and InGaN/GaN light emitting diode heterostructures were grown and their properties are compared with the ones obtained on Si(1 1 1).     

Reduction of dislocations in a (1 1 2¯ 2)GaN grown by selective MOVPE on (1 1 3)Si

Two-step selective epitaxy (SAG/ELO) of (1 1 2¯ 2)GaN on (1 1 3)Si substrate is studied to reduce the defect density in the epitaxial lateral overgrowth. The first SAG/ELO is to prepare a (1 1 2¯ 2)GaN template on a (1 1 3)Si and the second SAG/ELO is to get a uniform (1 1 2¯ 2)GaN. It is found that the reduction of the defect density is improved by optimizing the mask configuration in the second SAG/ELO. The minimum dark spot density obtained is 3×10⁷/cm², which is two orders of magnitude lower than that found in a (0 0 0 1)GaN grown on (1 1 1)Si.     

MBE growth of PbSe thin film with a 9×10 cm etch-pits density on patterned (1 1 1)-oriented Si substrate

PbSe thin film was grown on a patterned Si substrate with (1 1 1)-orientation by molecular-beam epitaxy (MBE). On the mesa, a low dislocation density of 9×10⁵ cm⁻² was confirmed by the etch-pits density (EPD) wet-etching technique. The photoluminescence (PL) intensity at room temperature from the low dislocation PbSe film was much higher than that from the PbSe film grown on the planar area, which further indicated the high-quality of PbSe thin film grown on patterned Si substrate.     

Theoretical investigation on the decomposition process of GaN(0 0 0 1) surface under a hydrogen atmosphere

The activation energies for Ga and N desorption from a GaN surface were calculated using the density functional theory to understand the detailed decomposition process of the hydrogen terminated GaN(0 0 0 1) Ga and N surfaces under a hydrogen atmosphere. It was found that the Ga atoms on the hydrogen terminated GaN(0 0 0 1) Ga surface desorbed as GaH molecules from the surface while the N atoms on the hydrogen terminated GaN(0 0 0 1) N surface desorbed as NH₃ molecules from the surface. The desorption energies of GaH and NH₃ on the hydrogen terminated surface were more consistent with the previous experimental values than those on the ideal surface. These results suggest that the initial surface structure of the GaN(0 0 0 1) surface is terminated with hydrogen.