水蒸气处理对ZSM-5酸性及其催化丁烯裂解性能的影响

 考察了水蒸气处理温度和时间对ZSM-5分子筛酸性及其催化丁烯裂解性能的影响. 结果表明,通过水蒸气处理可降低ZSM-5分子筛的酸量和酸强度,明显提高产物中丙烯与乙烯的选择性和收率,抑制副产物芳烃和低碳烷烃的生成. 用柠檬酸脱除水蒸气处理过程中产生的非骨架铝,可提高ZSM-5分子筛孔道的容碳能力,从而提高催化剂的稳定性. 考察了反应条件对催化剂性能的影响,结果表明较佳的反应条件为WHSV=3.5～8.8 h-1,p=0.06～0.1 MPa,θ=600～620 ℃.     

ZSM-5分子筛晶粒尺寸对C4烯烃催化裂解制丙烯的影响

 采用水热法合成了晶粒尺寸分别为20～30,1～2和0.2～0.3 μm的三种ZSM-5分子筛样品,并用SEM,XRD,氮低温物理吸附,NH3-TPD和TGA等技术对ZSM-5分子筛进行了表征,以考察其晶粒尺寸对C4烯烃裂解生产丙烯过程中催化剂活性和稳定性的影响. 结果表明,在常压,WHSV=10 h-1和550 ℃的条件下,以ZSM-5分子筛为催化剂,通过C4烯烃的催化裂解可以获得高收率的丙烯,反应初期丙烯的单程收率可达38%; 尽管三种晶粒尺寸的分子筛具有相近的比表面积和总酸量,但小晶粒的ZSM-5分子筛(粒径0.2～0.3 μm)具有微孔短、外比表面积大和孔口多等特点,因而表现出较强的容积炭能力和较好的稳定性; 小晶粒的ZSM-5分子筛催化剂经过10次再生重复使用,其催化生成丙烯的收率没有明显降低.     

碱金属盐对ZSM-5分子筛晶化的影响

Effect of different alkali metal salts on the crystal size and the crystallization rate of ZSM-5 zeolite was de-tailedly investigated in this paper. The samples prepared by adding the different alkali metal salts were character-ized by using XRD， TEM， TG-DSC， BET and IR techniques. The XRD results showed that， for the nanosized ZSM-5 zeolite， the characteristic peaks broadened on the XRD patterns in comparison with the microsized ZSM-5 zeolite. The SEM results verified that the crystal size of zeolites prepared by adding different alkali metal salts had different results， and adding NaCl， NaC₂H₃O₂ and KCl showed the better effect of reducing crystal size， which are about of 40～60nm size. The crystallization curve of adding the different alkali metal salts suggested that the crystallization rate was significantly affected by the anions in the alkali metal salt besides the cations. Moreover， the crystal size likewise depended on the anion in the alkali metal salt. In addition， the BET results suggested that the nanosized ZSM-5 zeolite possessed a larger outer surface area in comparison with the microsized ZSM-5 zeolite. The thermostability of the samples was determined by TG-DSC technique， indicating that the nanosized ZSM-5 zeolite had a poor thermostability as compared with the microsized ZSM-5 zeolite. The possible difference of the samples with different crystal sizes on IR spectra was also given.     

ZSM-5分子筛催化JP-10裂解的研究

考察了ZSM-5分子筛催化高密度碳氢燃料JP-10的裂解情况. 在500～650 ℃温度范围内, 与热裂解相比, 分子筛催化可显著提高裂解转化率, 主要产物有甲烷、乙烷、乙烯、丙烷和丙烯, 以及苯和苯的同系物等. 在较高温度时, 由于氢转移反应, 产物中出现了茚、萘等低氢碳比化合物, 会影响燃料的燃烧性能, 应用时需要根据性能要求在高裂解转化率与低芳烃收率之间进行权衡. 通过裂解产物分析, 结合量子化学计算, 探讨了JP-10催化裂解的可能历程, 并对实验结果进行了解释.     

纳米ZSM-5用于石脑油催化裂化的最新进展(英文)

综述了纳米ZSM-5在石脑油催化裂解中的应用.比较了纳米ZSM-5和毫米级ZSM-5对产物选择性、反应转化率和催化剂寿命的影响.纳米ZSM-5的应用不仅延长了催化剂寿命,而且表现出更稳定的轻质烯烃选择性.讨论了反应条件,如温度和进料对纳米ZSM-5催化性能的影响,发现高温和线式烷烃作为进料时可提高轻质烯烃的选择性和反应转化率.     

低硅铝比ZSM-5分子筛上C4烃的催化裂解反应

以低硅铝比(n(SiO2)/n(Al2O3)=20-45)的ZSM-5分子筛为催化剂, 研究了混合C4烃的催化裂解反应, 并对不同硅铝比的ZSM-5分子筛进行了酸性表征. 混合C4烃的催化裂解反应结果表明, 低硅铝比的ZSM-5分子筛具有较高的低温催化活性, 高硅铝比ZSM-5分子筛催化剂上乙烯和丙烯的收率高于低硅铝比ZSM-5分子筛催化剂, 低硅铝比ZSM-5分子筛上苯和甲苯的收率高于高硅铝比ZSM-5分子筛催化剂. 在反应温度为625 ℃时, 硅铝比为20的ZSM-5分子筛催化剂上乙烯、丙烯、苯和甲苯的总收率可达79.42%. 酸性表征结果表明, 硅铝比低的ZSM-5分子筛具有更多的Bronsted(B)酸酸量、Lewis(L)酸酸量及总酸酸量, 这是低硅铝比ZSM-5分子筛具有低温高活性及高的苯和甲苯收率的原因.     

微波辐射下稀土交换ZSM-5分子筛的制备及裂解反应研究

借助微波技术制备出一系列具有不同La³⁺交换度的LaHZSM-5样品。初步探讨了微波强度、微波作用时间及Si/Al比对交换度的影响。对其表面酸性的考察发现,样品均含有B酸和L酸中心,并且随La³⁺进入ZSM-5沸石的量的不同,强弱酸中心的强度与数量均有所改变。对样品催化性能的研究结果表明,催化活性与La³⁺含量及酸量呈顺变关系。     

ZSM-5分子筛水蒸气选择性脱铝及其对乙醇转化制丙烯的影响

采用水蒸气对ZSM-5分子筛进行后处理,系统考察了水蒸气处理时间和处理温度对分子筛孔结构、骨架铝分布、酸性及乙醇转化制丙烯的影响.研究结果表明,随着水蒸气处理时间的延长及处理温度的升高,分子筛结晶度和比表面积明显下降.27Al NMR及Co(Ⅱ)交换-ICP结果显示,在水蒸气作用下,分子筛骨架上孤立铝(Alsingle...     

ZSM-5/ZSM-57复合分子筛催化剂上混合C4烃的催化转化反应

以ZSM-5/ZSM-57复合分子筛为催化剂, 考察了其对混合C4烃催化转化的反应性能. 采用氨程序升温脱附(NH3-TPD)和吡啶吸附傅立叶变换红外(FT-IR)光谱技术表征复合分子筛的酸性质. 结果表明, 当复合分子筛中ZSM-5的含量较低时, 比ZSM-5具有更高的催化活性及乙烯和丙烯选择性, 这是因为此时复合分子筛酸强度较高、酸量较多, 且小孔ZSM-57有利于乙烯和丙烯的择形反应. 而当复合分子筛中ZSM-5的含量较高时, 具有较高的苯和甲苯选择性, 其原因可能是其孔结构及共晶生长时的结构匹配性对芳构化反应有利.     

ZSM-5沸石分子筛增产丙烯表面改性的研究进展

丙烯是极其重要的有机化工原料,其中用于聚丙烯占58%,用于丙烯腈、羰基合成醇、环氧丙烷和异丙苯分别占10%、8%、7%和6%左右.全球丙烯需求年均增长率为5.6%,而2007年之前乙烯需求年均增长率仅为4.6%[1～2].     

Synergistic effect of W and P on ZSM-5 and its catalytic performance in the cracking of heavy oil

In order to develop the conversion of heavy oil with a high yield of propylene in the catalytic cracking process, ZSM-5 zeolite was modified by tungsten and phosphorus, which was proved to be an effective method. Characterization results show that the improvement of catalytic performance could be correlated to the interaction of phosphorus and tungsten species on ZSM-5. P inhibited the aggregation of tungsten species on ZSM-5 and was conductive to convert the tungsten species with octahedral coordination into tetrahedral coordination. And this ultimately led to that more acid sites were reserved after hydrothermal treatment in the tungsten and phosphorus co-modified ZSM-5 catalyst. Phosphorus species played an important role to restrain the dehydrogenation activity of tungsten. In addition, a model reflecting the interaction between tungsten species and ZSM-5 framework was proposed.     

Synergistic effect of W and P on ZSM-5 and its catalytic performance in the cracking of heavy oil

In order to develop the conversion of heavy oil with a high yield of propylene in the catalytic cracking process, ZSM-5 zeolite was modified by tungsten and phosphorus, which was proved to be an effective method. Characterization results show that the improvement of catalytic performance could be correlated to the interaction of phosphorus and tungsten species on ZSM-5. P inhibited the aggregation of tungsten species on ZSM-5 and was conductive to convert the tungsten species with octahedral coordination into tetrahedral coordination. And this ultimately led to that more acid sites were reserved after hydrothermal treatment in the tungsten and phosphorus co-modified ZSM-5 catalyst. Phosphorus species played an important role to restrain the dehydrogenation activity of tungsten. In addition, a model reflecting the interaction between tungsten species and ZSM-5 framework was proposed.     

ZSM-5/Y复合分子筛在烃类催化裂化催化剂中的应用研究

以大庆减压蜡油为原料，考察了水热脱铝ZSM-5/Y复合分子筛的催化裂化性能，并与经同样条件水热脱铝的ZSM-5和Y型沸石的机械混合分子筛进行了对比研究。结果表明，与机械混合样品相比，复合分子筛具有较大的柴油产率和气体产率，汽油产率降低。从复合分子筛结构和ZSM-5的择形催化两方面分析了复合分子筛和机械混合分子筛裂化性能差别的原因。复合分子筛的聚集体结构不利于大分子进入分子筛结构中进行裂化，有利于汽油组分的裂化。气体数据分析支持了复合分子筛的结构特点。     

低硅铝比ZSM-5分子筛的合成及其正庚烷裂化反应性能

以氨水为矿化剂,通过添加NH₄⁺离子水热合成了具有较低骨架硅铝比的ZSM-5分子筛。通过X射线衍射(XRD)、扫描电镜(SEM)、固体核磁共振(MAS-NMR)等表征手段,研究了硅源、铝源、矿化剂、阳离子等对ZSM-5分子筛的结晶度、形貌尺寸和骨架硅铝比等的影响,研究了ZSM-5分子筛的骨架硅铝比对正庚烷催化裂化反应的影响。研究表明,投料硅铝比越低,铝原子越难进入到分子筛骨架中;当氨水为矿化剂、正硅酸四乙酯为硅源时可以合成骨架硅铝比较低的氢型ZSM-5分子筛,添加NH₄⁺离子可以增强骨架铝的嵌入,进一步降低分子筛的骨架硅铝比(24.2)。正庚烷裂化反应结果表明,降低分子筛的骨架硅铝比可以提高正庚烷裂化反应的活性,但会降低低碳烯烃的选择性。     

不同硅铝比ZSM-5分子筛作为助催化剂在渣油裂化中的应用

采用不同方法表征了硅铝比(SiO2/Al2O3)为33、266和487的质子型ZSM-5分子筛,并研究了ZSM-5分子筛作为助催化剂在渣油裂解中的应用。与USY分子筛基催化剂混合后,在固定流化床上,评价了ZSM-5分子筛助催化剂的催化裂化性能。研究发现,提高ZSM-5分子筛硅铝比,可以有效抑制混合催化剂对汽油烯烃的裂解,从而避免了汽油烷烃的大量损失。加入ZSM-5助催化剂后,伴随着液化气(LPG)产率的增加,异丁烷和异戊烷产率增加,这可能是由USY基催化剂和ZSM-5助催化剂的综合效应引起的。汽油烷烃和芳烃含量的变化,引起了汽油辛烷值的增加。高硅铝比ZSM-5分子筛(硅铝比为266和487)不仅可以显著改善汽油的辛烷值,而且有效避免了汽油的大量损失。催化汽油辛烷值的改善主要是由于高硅铝比ZSM-5分子筛具有适宜的芳构化和异构化活性,这些变化主要源于高硅铝比ZSM-5分子筛小的孔道直径和适宜的酸性。     

高浓度体系制备ZSM-5分子筛及碱处理后甲醇制丙烯性能

在高浓度体系下,以粗孔硅胶和偏铝酸钠为原料,TPABr为模板剂,水热晶化法制备了ZSM-5分子筛,单釜产率23％.用不同浓度的氢氧化钠溶液对ZSM-5分子筛进行改性,采用XRD、FT-IR、SEM、NH3-TPD、XRF、N2物理吸附等方法对改性前后的样品进行了表征,并考察了改性后ZSM-5分子筛甲醇催化转化制丙烯(MTP)反应性能.结果表明,氢氧化钠改性未破坏分子筛的骨架结构,改性后样品的酸量、介孔孔容和BET比表面积均有增加,从而改善了催化剂的抗积碳性能和反应性能.在MTP反应中,增产丙烯的效果不明显,但表现出了更好的催化稳定性(催化剂使用寿命从85 h提升至110 h),并且有利于提高副产物汽油组分(∑C5+)的产量.     

FCC汽油二次裂化增产丙烯过程中主要影响因素的研究

利用提升管中试实验装置,研究了催化汽油二次裂化制丙烯过程中热裂化、氢转移反应的特点和影响因素,给出了不同反应条件对丙烯选择性的影响,考察了丙烯选择性最大点处热裂化反应、氢转移反应的变化。研究结果表明,采用适当的反应温度和剂油比以及缩短反应时间能有效抑制热裂化反应和氢转移反应的发生,提高丙烯的选择性。