Decay of nano-islands located on Au(1 0 0) electrode in room temperature molten salt (EMImBF4)

The behaviour of nano-islands located on an Au(1 0 0) single crystal surface in contact with a room temperature molten salt, that is, 1-ethyl-3-methylimidazolium tetrafluoroborate (EMImBF₄), has been investigated using electrochemical atomic force microscopy (EC-AFM) under potential control. It was found from the in situ EC-AFM observations that a nano-island located on an Au(1 0 0) electrode collapses in EMImBF₄ in the potential range between −1.05 and 0.2 V (vs. Ag/Ag⁺ in EMImBF₄). It was also found that the nano-islands decay faster when the Au(1 0 0) electrode potential is more positive. These in situ EC-AFM observations reveal that the behaviour of the nano-island in the EMImBF₄ shown above is quite similar to that observed in a sulfuric acid aqueous solution.     

Thickness dependent stripe structure stability of Ag films on Si(1 1 1)-(4 × 1)-In substrate

The thickness dependent stripe structure stabilization of Ag films on Si(1 1 1)-(4 × 1)-In substrate is thermodynamically considered. It is found that for the stability of the structure, there is a competition between the sum of elastic energy and stacking fault energy in the film and the film-substrate interface energy. The presence of equilibrium of them leads to a critical film thickness. Beyond it, the stripe structure will transform into a flat one. Our prediction for n_c of Ag films shows reasonable agreement with experimental data. In addition, according to the established model, it is predicted that Au could also form the above stripe structure on this substrate with a similar n_c value of Ag.     

Growth mode and electronic structure of Au nano-clusters on NiO(0 0 1) and TiO2(1 1 0)

The growth mode and electronic structure of Au nano-clusters grown on NiO and TiO₂ were analyzed by reflection high-energy electron diffraction, a field-emission type scanning electron microscope, medium energy ion scattering and photoelectron spectroscopy. Au was deposited on clean NiO(0 0 1)-1 × 1 and TiO₂(1 1 0)-1 × 1 surfaces at room temperature with a Knudsen cell at a rate of 0.25-0.35 ML/min (1 ML = 1.39 × 10¹⁵ atoms/cm²:Au(1 1 1)). Initially two-dimensional (2D) islands with thickness of one Au-atom layer grow epitaxially on NiO(0 0 1) and then neighboring 2D-islands link each other to form three-dimensional (3D)-islands with the c-axis oriented to the [1 1 1] direction. The critical size to form 3D-islands is estimated to be about 5 nm². The shape of the 3D-islands is well approximated by a partial sphere with a diameter d and height h ranging from 2.0 to 11.8 nm and from 0.95 to 4.2 nm, respectively for Au coverage from 0.13 to 4.6 ML. The valence band spectra show that the Au/NiO and Au/TiO₂ surfaces have metallic characters for Au coverage above 0.9 ML. We observed Au 4f spectra and found no binding energy shift for Au/NiO but significant higher binding energy shifts for Au/TiO₂ due to an electron charge transfer from Au to TiO₂. The work function of Au/NiO(0 0 1) gradually increases with increase in Au coverage from 4.4 eV (NiO(0 0 1)) to 5.36 eV (Au(1 1 1)). In contrast, a small Au deposition(0.15 to 1.5 ML) on TiO₂(1 1 0) leads to reduction of the work function, which is correlated with an electron charge transfer from Au to TiO₂ substrate.     

Self-assembled germanium nano-clusters on silver(1 1 0)

The adsorption of germanium on Ag(1 1 0) has been investigated by scanning tunnelling microscopy (STM), as well as surface X-ray diffraction (SXRD). At 0.5 germanium monolayer (ML) coverage, Low Energy Electron Diffraction (LEED) patterns reveals a sharp c(4 × 2) superstructure. Based on STM images and SXRD measurements, we present an atomic model of the surface structure with Ge atoms forming tetramer nano-clusters perfectly assembled in a two-dimensional array over the silver top layer. The adsorption of the germanium atoms induces a weak perturbation of the Ag surface. Upon comparison with results obtained on the (1 1 1) and (1 0 0) faces, we stress the role played by the relative interactions between silver and germanium on the observed surface structures.     

Hydrogen adsorption on GaAs(0 0 1)-c(4 × 4)

Exposure of the As-terminated GaAs(0 0 1)-c(4 × 4) reconstructed surface to atomic hydrogen (H) at different substrate temperatures (50-480 °C) has been studied by reflection high-energy electron diffraction (RHEED) and scanning tunnelling microscopy (STM). Hydrogen exposure at low temperatures (∼50 °C) produces a disordered (1 × 1) surface covered with AsH_x clusters. At higher temperatures (150-400 °C) exposure to hydrogen leads to the formation of mixed c(2 × 2) and c(4 × 2) surface domains with H adsorbed on surface Ga atoms that are exposed due to the H induced loss of As from the surface. At the highest temperature (480 °C) a disordered (2 × 4) reconstruction is formed due to thermal desorption of As from the surface. The results are consistent with the loss of As from the surface, either through direct thermal desorption or as a result of the desorption of volatile compounds which form after reaction with H.     

Growth of oriented crystalline Ag nanoislands on air-exposed Si(0 0 1) surfaces

Growth of Ag islands under ultrahigh vacuum condition on air-exposed Si(0 0 1)-(2 × 1) surfaces has been investigated by in-situ reflection high energy electron diffraction (RHEED). A thin oxide is formed on Si via exposure of the clean Si(0 0 1)-(2 × 1) surface to air. Deposition of Ag on this oxidized surface was carried out at different substrate temperatures. Deposition at room temperature leads to the growth of randomly oriented Ag islands while well-oriented Ag islands, with (0 0 1)_Ag||(0 0 1)_Si, [1 1 0]_Ag||[1 1 0]_Si, have been found to grow at substrate temperatures of ≥350 °C in spite of the presence of the oxide layer between Ag islands and Si. The RHEED patterns show similarities with the case of Ag deposition on H-passivated Si(0 0 1) surfaces.     

Diffusion-limited electrodeposition of ultrathin Au films on Pt(1 1 1)

The electrodeposition of Au on Pt(1 1 1) from electrolytes containing μM concentrations of was studied by in situ scanning tunneling microscopy. Under these conditions the Au flux is limited by diffusion in the electrolyte over a wide potential range, which allows to assess the effect of the electrochemical environment on the growth kinetics. Similar to gas phase metal deposition Au film growth proceeds via nucleation and lateral growth of Au monolayer islands, with the saturation island density strongly depending on the deposition potential and on the anion species in the electrolyte. For deposition in H₂SO₄ solution the saturation island density continuously increases with increasing potential between −0.2 and 0.5 V (SCE), whereas in Cl-containing H₂SO₄ it first decreases and then increases again. Following nucleation and growth theories this behavior can be attributed to potential-induced changes of the Au surface mobility, caused by changes in the density and structure of coadsorbed sulfate/bisulfate and chloride adlayers. Under conditions of high Au surface mobility multilayer growth proceeds via a typical Stranski-Krastanov growth mode, with layer-by-layer growth of a pseudomorphic Au film up to 2 ML and 3D growth of structurally relaxed islands at higher coverage, indicating thermodynamic control under these conditions.     

SrTiO3(0 0 1) reconstructions: the (2 × 2) to c(4 × 4) transition

Scanning tunneling microscopy (STM) is used to investigate the (0 0 1) surface structure of Nb doped SrTiO₃ single crystals annealed in ultra high vacuum (UHV). Atomically resolved images of the (2 × 2) reconstructed surface are obtained after annealing a chemically etched sample. With further annealing dotted row domains appear, which coexist with the (2 × 2) reconstruction. The expansion of these domains with further annealing gives rise to the formation of a TiO₂ enriched c(4 × 4) reconstruction.     

Structures and stability of Ag clusters on Ag(1 1 1) and Ni(1 1 1) surfaces

The structures of the lowest total energy for small Ag_N clusters with N = 2-20, which are grown on Ag(1 1 1) and Ni(1 1 1) surfaces, have been determined using a combination of the embedded-atom method and the basin-hopping algorithm. It is found that the particularly stable Ag clusters with N<18 have similar geometries on both surfaces when comparing clusters of the same size. On the other hand, the geometries of the less stable Ag clusters in the same size range differ for the two surfaces. From N?18, the sizes of the particularly stable structures are different for the two different substrates. Due to the large size mismatch of the two types of atoms it is energetically unfavorable for Ag to form a pseudomorphic monolayer structures on Ni(1 1 1) and there is considerable strain produced at the interface. The effect of this strain and the increased adatom-substrate interactions lead to irregular and elongated structures of the adsorbed Ag clusters.     

Electron and lattice structure of ultra thin Ag films on Si(1 1 1) and Si(0 0 1)

We studied the low temperature (T ? 130 K) growth of Ag on Si(0 0 1) and Si(1 1 1) flat surfaces prepared by Si homo epitaxy with the aim to achieve thin metallic films. The band structure and morphology of the Ag overlayers have been investigated by means of XPS, UPS, LEED, STM and STS. Surprisingly a (√3 × √3)R30° LEED structure for Ag films has been observed after deposition of 2-6 ML Ag onto a Si(1 1 1)(√3 × √3)R30°Ag surface at low temperatures. XPS investigations showed that these films are solid, and UPS measurements indicate that they are metallic. However, after closer STM studies we found that these films consists of sharp Ag islands and (√3 × √3)R30°Ag flat terraces in between. On Si(0 0 1) the low-temperature deposition yields an epitaxial growth of Ag on clean Si(0 0 1)-2 × 1 with a twinned Ag(1 1 1) structure at coverage’s as low as 10 ML. Furthermore the conductivity of few monolayer Ag films on Si(1 0 0) surfaces has been studied as a function of temperature (40-300 K).     

High resolution scanning tunneling spectroscopy of ultrathin Pb on Si(1 1 1)-(6 × 6) substrate

The electronic structure of Si(1 1 1)-(6 × 6)Au surface covered with submonolayer amount of Pb is investigated using scanning tunneling spectroscopy. Already in small islands of Pb with thickness of 1 ML Pb_(1 1 1) and with the diameter of only about 2 nm we detected the quantized electronic state with energy 0.55 eV below the Fermi level. Similarly, the I(V) characteristics made for the Si(1 1 1)-(6 × 6)Au surface reveal a localized energy state 0.3 eV below the Fermi level. These energies result from fitting of the theoretical curves to the experimental data. The calculations are based on tight binding Hubbard model. The theoretical calculations clearly show prominent modification of the I(V) curve due to variation of electronic and topographic properties of the STM tip apex.     

In situ X-ray analysis of solid/electrolyte interfaces: electrodeposition of Cu and Co on Si(1 1 1):H and GaAs(0 0 1) and corrosion of Cu3Au(1 1 1)

Electrochemical deposition of Cu and Co in monolayer amounts on hydrogen terminated Si(1 1 1) was studied ex situ and in situ by X-ray techniques. The X-ray beam was found to have a strong effect on the deposit causing desorption under the beam. Cu deposition on GaAs(0 0 1) from UHV is compared with electrodeposited Cu on the same surface, elucidating similarities and differences of electrochemical and UHV deposition. Roughening due to corrosion of Cu₃Au(1 1 1) is observed by crystal truncation scattering. The observed behaviour of passivation of this surface is explained by the formation of Au clusters, increasingly covering the surface at higher oxidation potential.     

Study of c(2 × 2)-MnAu(0 0 1) layers on Mn(0 0 1) by means of scanning tunneling microscopy/spectroscopy

Intermixing, growth, geometric and electronic structures of gold films grown on antiferromagnetic stacking body-centered-tetragonal manganese (0 0 1) films were studied by means of scanning tunneling microscopy/spectroscopy at room temperature in ultra-high vacuum. We found stable ordered c(2 × 2)-MnAu(0 0 1) alloy layers after depositing Au on pure Mn layers. Since at the fourth layer (5 × 23)-like Au reconstruction appears instead of the c(2 × 2) structure and local density of states peaks obtained on the c(2 × 2)-MnAu surface disappear, pure Au layers likely grow from the fourth layer.     

Herringbone and triangular patterns of dislocations in Ag, Au, and AgAu alloy films on Ru(0 0 0 1)

We have studied the dislocation structures that occur in films of Ag, Au, and Ag_0.5Au_0.5 alloy on a Ru(0 0 0 1) substrate. Monolayer (ML) films form herringbone phases while films two or more layers thick contain triangular patterns of dislocations. We use scanning tunneling microscopy (STM) and low-energy electron diffraction (LEED) to determine how the film composition affects the structure and periodicity of these ordered structures. One layer of Ag forms two different herringbone phases depending on the exact Ag coverage and temperature. Low-energy electron microscopy (LEEM) establishes that a reversible, first-order phase transition occurs between these two phases at a certain temperature. We critically compare our 1 ML Ag structures to conflicting results from an X-ray scattering study [H. Zajonz et al., Phys. Rev. B 67 (2003) 155417]. Unlike Ag, the herringbone phases of Au and AgAu alloy are independent of the exact film coverage. For two layer films in all three systems, none of the dislocations in the triangular networks thread into the second film layer. In all three systems, the in-plane atomic spacing of the second film layer is nearly the same as in the bulk. Film composition does, however, affect the details of the two layer structures. Ag and Au films form interconnected networks of dislocations, which we refer to as “trigons.” In 2 ML AgAu alloy, the dislocations form a different triangular network that shares features of both trigon and moiré structures. Yet another well-ordered structure, with square symmetry, forms at the boundaries of translational trigon domains in 2 ML Ag films but not in Au films.     

Growth and thermal stability of ultra-thin Ag and Au layers on Mo(1 1 1) surface

The influence of temperature on the growth process of ultra-thin Ag and Au layers on the Mo(1 1 1) surface was investigated. At 300 K growth of the Stranski-Krastanov type was found for Ag; for Au growth of the monolayer plus simultaneous multilayers type was found, where a base layer is one physical layer. The first three geometrical adsorbed layers for Ag are thermally stable. For annealed Au layers triangle features with base side length from 15 to 35 Å were formed for θ < 6 monolayer (ML), and for θ > 6 ML part of the Au formed a flat adlayer with Au atoms grouped in equilateral triangles with side length 7 Å. The presence of Au layers does not cause faceting, layers are not smooth which could be caused by the fact that Au does not wets the substrate. For Ag thick layers reversible wetting/non-wetting transition was observed at 600 K. Ag layers on Mo(1 1 1) surface did not lead to faceting.     

Stranski-Krastanov like oxide growth on Ag(1 1 1) at atmospheric oxygen pressures

The oxidation behavior of Ag(1 1 1) was studied by means of in situ surface X-ray diffraction at atmospheric oxygen pressure. Exposure to 1 bar oxygen at 773 K reveals a competing growth of three different oxygen-induced structures on Ag(1 1 1), namely the well-known p(4 × 4) reconstruction, a surface oxide in a p(7 × 7) coincidence structure and the bulk oxide Ag₂O in orientation. The latter two exhibit the same honeycomb on hexagon arrangement of the Ag sublattice with respect to the Ag(1 1 1) surface. An inverted stacking of Ag planes in the bulk oxide islands is observed as compared to the Ag(1 1 1) substrate, which sheds new light on the Ag₂O formation process. Finally, we present a structural model of the p(7 × 7) reconstruction, based on a three-layer O-Ag-O slab of Ag₂O(1 1 1).     

Sulphur overlayers on the Au(1 1 0) surface: LEED and TPD study

The adsorption and desorption of sulphur on the clean reconstructed Au(1 1 0)-(1 × 2) surface has been studied by low energy electron diffraction, Auger electron spectroscopy and temperature programmed desorption. The results obtained show a complex behaviour of the S/Au(1 1 0) system during sulphur desorption at different temperatures. Two structures of the stable ordered sulphur overlayer on the Au(1 1 0) surface, p(4 × 2) and c(4 × 4), were found after annealing the S/Au(1 1 0) system at 630 K and 463 K, respectively. The corresponding sulphur coverage for these overlayers was estimated by AES signal intensity analysis of the Au NOO and S LMM Auger lines to be equal to 0.13 ML and 0.2 ML, respectively. Both sulphur structures appear after removing an excess of sulphur, which mainly desorbs at 358 K as determined from TPD spectra. Furthermore, it was not possible to produce the lower coverage p(4 × 2) sulphur structure by annealing the c(4 × 4) surface. In the case of the p(4 × 2) S overlayer on the Au(1 1 0)-(1 × 2) surface it is proposed that the sulphur is attached to “missing row” sites only. The c(4 × 4) S overlayer arises via desorption of S₂ molecules that are formed on the surface due to mobility of sulphur atoms after a prolonged anneal.     

Epitaxial growth of Co(0 0 0 1)hcp/Fe(1 1 0)bcc magnetic bi-layer films on SrTiO3(1 1 1) substrates

Co(0 0 0 1)_hcp/Fe(1 1 0)_bcc epitaxial magnetic bi-layer films were successfully prepared on SrTiO₃(1 1 1) substrates. The crystallographic properties of Co/Fe epitaxial magnetic bi-layer films were investigated. Fe(1 1 0)_bcc soft magnetic layer grew epitaxially on SrTiO₃(1 1 1) substrate with two type variants, Nishiyama–Wasserman and Kurdjumov–Sachs relationships. An hcp-Co single-crystal layer is obtained on Ru(0 0 0 1)_hcp interlayer, while hcp-Co layer formed on Au(1 1 1)_fcc or Ag(1 1 1)_fcc interlayer is strained and may involve fcc-Co phase. It has been shown possible to prepare Co/Fe epitaxial magnetic bi-layer films which can be usable for patterned media application.     

The CuGaSe2(0 0 1) surface: A (4 × 1) reconstruction

We report on the formation of a stable (4 × 1) reconstruction of the chalcopyrite CuGaSe₂(0 0 1) surface. Using Ar⁺ ion-bombardment and annealing of epitaxial CuGaSe₂ films grown on GaAs(0 0 1) substrates it was possible to obtain flat, well-ordered surfaces showing a clear (4 × 1) reconstruction. The cleanliness and structure were analyzed in situ by AES and LEED. AES data suggest a slight Se-enrichment and Cu-depletion upon surface preparation. Our results demonstrate that (0 0 1) surfaces of the Cu-III-VI₂(0 0 1) material can show stable, unfacetted surfaces.     

Reaction of water with Ce-Au(1 1 1) and CeOx/Au(1 1 1) surfaces: Photoemission and STM studies

This article reports photoemission and STM studies for the adsorption and dissociation of water on Ce-Au(1 1 1) alloys and CeO_x/Au(1 1 1) surfaces. In general, the adsorption of water at 300 K on disordered Ce-Au(1 1 1) alloys led to O-H bond breaking and the formation of Ce(OH)_x species. Heating to 500-600 K induced the decomposition or disproportionation of the adsorbed OH groups, with the evolution of H₂ and H₂O into gas phase and the formation of Ce₂O₃ islands on the gold substrate. The intrinsic Ce ↔ H₂O interactions were explored by depositing Ce atoms on water multilayers supported on Au(1 1 1). After adsorbing Ce on ice layers at 100 K, the admetal was oxidized immediately to yield Ce³⁺. Heating to room temperature produced finger-like islands of Ce(OH)_x on the gold substrate. The hydroxyl groups dissociated upon additional heating to 500-600 K, leaving Ce₂O₃ particles over the surface. On these systems, water was not able to fully oxidize Ce into CeO₂ under UHV conditions. A complete Ce₂O₃ → CeO₂ transformation was seen upon reaction with O₂. The particles of CeO₂ dispersed on Au(1 1 1) did not interact with water at 300 K or higher temperatures. In this respect, they exhibited the same reactivity as does a periodic CeO₂(1 1 1) surface. On the other hand, the Ce₂O₃/Au(1 1 1) and CeO_2−x/Au(1 1 1) surfaces readily dissociated H₂O at 300-500 K. These systems showed an interesting reactivity for H₂O decomposition. Water decomposed into OH groups on Ce₂O₃/Au(1 1 1) or CeO_2−x/Au(1 1 1) without completely oxidizing Ce³⁺ into Ce⁴⁺. Annealing over 500 K removed the hydroxyl groups leaving behind CeO_2−x/Au(1 1 1) surfaces. In other words, the activity of CeO_x/Au(1 1 1) for water dissociation can be easily recovered. The behavior of gold-ceria catalysts during the water-gas shift reaction is discussed in light of these results.