Reactivity to sulphur of clean and pre-oxidised Cu(1 1 1) surfaces

The reactivity of clean and pre-oxidised Cu(1 1 1) surfaces exposed to sulphur (H₂S) has been studied at room temperature by Auger electron spectroscopy, low energy electron diffraction and scanning tunneling microscopy. On the clean surface, the sulphur-saturated surface structure is dominated by the or so-called “zigzag” superstructure. It is shown that a single orientation domain is favoured by the slight misorientation (∼2°) of the surface with respect to the (1 1 1) plane. Scanning tunneling microscopy measurements also revealed two minority structures. Pre-oxidation was performed by exposure to 1.5 × 10⁴ L of O₂ at 300 °C. Under exposure to H₂S (1 × 10⁻⁷ mbar) at room temperature, the oxygen is totally substituted by sulphur. Once initiated, sulphur adsorption seems to propagate to cover the whole surface on the O-covered surface faster than on the clean Cu(1 1 1). At saturation by adsorbed sulphur, the surface is completely covered by the superstructure of highest coverage. This enhanced uptake of sulphur is assigned to the surface reconstruction of the copper surface induced by the pre-oxidation, causing a stronger reactivity of the Cu atoms released by the decomposition of the oxide.     

Reaction of SO2 with Cu/TiO2(1 1 0): Effects of size and metal-oxide interactions in the chemical activation of Cu nanoparticles

The reaction of SO₂ with stoichiometric TiO₂(1 1 0), partially reduced TiO_2 − x(1 1 0) and Cu/TiO₂(1 1 0) was investigated using synchrotron based X-ray photoemission spectroscopy. SO₂ adsorbs on perfect TiO₂(1 1 0) forming SO₄ species at room temperature, while SO₂ dissociatively adsorbs on partially reduced TiO_2 − x(1 1 0) forming SO₄, SO₃ as well as two sulfide species. SO₂ exposure to Cu particles supported on perfect TiO₂(1 1 0) can lead to the formation of SO₄, SO₃ and sulfide species. When depositing Cu on SO₄/TiO₂(1 1 0) at room temperature, the dissociation efficiency of Cu atoms is much higher than that of Cu deposited on TiO₂(1 1 0) prior to SO₂ dosing. The post-deposited Cu atoms can efficiently contact and react with SO₄ species before they form Cu-Cu bonds and big clusters. Small Cu nanoparticles supported on TiO₂(1 1 0) are more reactive towards SO₂ than surfaces of bulk copper. The chemical reactivity of the Cu/TiO₂(1 1 0) system increases with Cu coverage until reaching a maximum at θ_Cu = 0.5-0.8 ML. After this point, an increase in Cu coverage leads to the formation of big Cu particles and the reactivity of the system decrease to that typical of bulk Cu. A comparison with results for SO₂/Cu/MgO(0 0 1) indicates that the effects of size and metal ↔ oxide interactions are important for the chemical activation of Cu nanoparticles on titania.     

Adsorption dynamics of O2 on Cu(1 0 0)

We have studied the adsorption of O₂ on the Cu(1 0 0) surface using both static potential energy surface (PES) calculations and ab initio molecular dynamics. The dynamical calculations complement the PES results, revealing steering effects which could not be predicted based on the static calculations only. We study the effect of oxidation and Ag doping on O₂ adsorption dynamics. The results are discussed in the light of recent molecular beam experiments.     

Density functional theory investigation of the structure of SO2 and SO3 on Cu(1 1 1) and Ni(1 1 1)

Density functional theory (DFT) slab calculations, mainly using the generalised gradient approximation, have been used to investigate the minimum energy structures of molecular SO₂ and SO₃ on Cu(1 1 1) and Ni(1 1 1) surfaces. On Ni(1 1 1) the optimal local adsorption structures are in close agreement with experimental results for both molecular species obtained using the X-ray standing wavefield technique, although for adsorbed SO₂ the energetic difference between two alternative lateral positions of the lying-down molecule on the surface is marginally significant. On Cu(1 1 1) the results for adsorbed SO₂, in particular, were sensitive to the DFT functional used in the calculations, but in all cases failed to reproduce the experimentally-established preference for adsorption with the molecular plane perpendicular to the surface. This result is discussed in the context of previously published DFT results for these species adsorbed on Cu(1 0 0). The optimal geometry found for SO₃ on Cu(1 1 1) is similar to that on Ni(1 1 1), providing agreement with experiment regarding the molecular orientation but not the adsorption site.     

Adsorption of glycine on a NiAl(1 1 0) alloy surface

The adsorption and desorption of glycine (NH₂CH₂COOH), vacuum deposited on a NiAl(1 1 0) surface, were investigated by means of Auger electron spectroscopy (AES), low energy electron diffraction (LEED), temperature-programmed desorption, work function (Δφ) measurements, and ultraviolet photoelectron spectroscopy (UPS). At 120 K, glycine adsorbs molecularly forming mono- and multilayers predominantly in the zwitterionic state, as evidenced by the UPS results. In contrast, the adsorption at room temperature (310 K) is mainly dissociative in the early stages of exposure, while molecular adsorption occurs only near saturation coverage. There is evidence that this molecularly adsorbed species is in the anionic form (NH₂CH₂COO⁻). Analysis of AES data reveals that upon adsorption glycine attacks the aluminium sites on the surface. On heating part of the monolayer adsorbed at 120 K is converted to the anionic form and at higher temperatures dissociates further before desorption. The temperature-induced dissociation of glycine (<400 K) leads to a series of similar reaction products irrespective of the initial adsorption step at 120 K or at 310 K, leaving finally oxygen, carbon and nitrogen at the surface. AES and LEED measurements indicate that oxygen interacts strongly with the Al component of the surface forming an “oxide”-like Al-O layer.     

Adsorption and reaction of bicyclic hydrocarbons at Pt(1 1 1) and Sn/Pt(1 1 1) surface alloys: trans-decahydronaphthalene (C10H18) and bicyclohexane (C12H22)

Adsorption and desorption of trans-decahydronaphthalene (C₁₀H₁₈) and bicyclohexane (C₁₂H₂₂) can be used to probe important aspects of non-specific dehydrogenation leading to surface carbon accumulation and establish better estimates of activation energies for C-H bond cleavage at Pt-Sn alloys. This chemistry was studied on Pt(1 1 1) and the (2 × 2)-Sn/Pt(1 1 1) and (√3 × √3)R30°-Sn/Pt(1 1 1) surface alloys by using temperature programmed desorption (TPD) mass spectroscopy and Auger electron spectroscopy (AES). These hydrocarbons are reactive on Pt(1 1 1) surfaces and fully dehydrogenate at low coverages to produce H₂ and surface carbon during TPD. At monolayer coverage, 87% of adsorbed C₁₀H₁₈ and 75% C₁₂H₂₂ on Pt(1 1 1) desorb with activation energies of 70 and 75 kJ/mol, respectively. Decomposition of C₁₀H₁₈ is totally inhibited during TPD on these Sn/Pt(1 1 1) alloys and decomposition of C₁₂H₂₂ is reduced to 10% of the monolayer coverage on the (2 × 2)-Sn/Pt(1 1 1) alloy and totally inhibited on the (√3 × √3)R30°-Sn/Pt(1 1 1) alloy. C₁₀H₁₈ and C₁₂H₂₂ are more weakly chemsorbed on these two alloys compared to Pt(1 1 1) and these molecules desorb in narrow peaks characteristic of each surface with activation energies of 65 and 73 kJ/mol on the (2 × 2) alloy and 60 and 70 kJ/mol on the (√3 × √3)R30°-Sn/Pt(1 1 1) alloy, respectively. Alloyed Sn has little influence on the monolayer saturation coverage of these two molecules, and this is decreased only slightly on these two Sn/Pt(1 1 1) alloys. The use of these two probe molecules enables an improved estimate of the activation energy barriers E* to break aliphatic C-H bonds in alkanes on Sn/Pt alloys; E* = 65-73 kJ/mol on the (2 × 2)-Sn/Pt(1 1 1) alloy and E* ? 70 kJ/mol on the (√3 × √3)R30°-Sn/Pt(1 1 1) alloy.     

Co on thin Al2O3 films grown on Ni3Al(1 0 0)

The growth of Co on thin Al₂O₃ layers on Ni₃Al(1 0 0) was investigated by Auger electron spectroscopy, high resolution electron energy loss spectroscopy (EELS), and scanning tunneling microscopy. At 300 K, Co grows in three-dimensional clusters on top of the Al₂O₃ layer. A defect structure of the alumina layer plays a crucial role during the early stage of Co growth. After deposition of 10 Å of Co, a complete screening of the dipoles of the Al₂O₃ layer due to the Co film is found in the EELS measurements. Annealing the Co film reveals a process of coalescence of Co clusters and, above 700 K, diffusion of the Co atoms through the oxide film into the substrate takes place.     

Oxygen-induced nano-faceting of Ir(2 1 0)

The adsorption of oxygen and the nanometer-scale faceting induced by oxygen have been studied on Ir(2 1 0). Oxygen is found to chemisorb dissociatively on Ir(2 1 0) at room temperature. The molecular desorption process is complex, as revealed by a detailed kinetic analysis of desorption spectra. Pyramid-shaped facets with {3 1 1} and (1 1 0) orientations are formed on the oxygen-covered Ir(2 1 0) surface when annealed to T?600 K. The surface remains faceted for substrate temperatures T<850 K. For T>850 K, the substrate structure reverts to the oxygen-covered (2 1 0) planar state and does so reversibly, provided that oxygen is not lost due to desorption or via chemical reactions upon which the planar (2 1 0) structure remains. A clean faceted surface was prepared through the use of low temperature surface cleaning methods: using CO oxidation, or reaction of H₂ to form H₂O, oxygen can be removed from the surface while preserving (“freezing”) the faceted structure. The resulting clean faceted surface remains stable for T<600 K. For temperatures above this value, the surface irreversibly relaxes to the planar state.     

O2 dissociation on Pd(2 1 1) and Cu(2 1 1) surfaces

We have performed ab initio Density Functional Theory (DFT) based calculations to observe the reactivity of the Pd(2 1 1) and Cu(2 1 1) surfaces towards O₂. In order to properly address the adsorption dynamics, the static potential energy surface calculations have been complemented with first principles molecular dynamics calculations, which reveal interesting steering effects that complicate the dissociation dynamics. We have found that on both surfaces the step microfacets are very reactive and the dissociation of the O₂ molecule at room temperature occurs mostly on those sites.     

The adsorption and dissociation of O2 molecular precursors on Cu: the effect of steps

The adsorption and dissociation of dioxygen on Cu steps are studied using periodic self-consistent density functional theory (PW91-GGA) calculations. Cu steps are modeled with a Cu(2 1 1) surface. The results are compared with those on the flat Cu(1 1 1) surface. The adsorption of both atomic and molecular oxygen is enhanced on the stepped surface: the binding energy of atomic oxygen is −4.5 eV at its preferred site on the relaxed Cu(2 1 1) surface vs. −4.3 eV at its preferred site on the relaxed Cu(1 1 1) surface, and the binding energy of the molecular oxygen precursor is increased from ∼−0.6 to ∼−1.0 eV. Several possible O₂ dissociation paths at the edge of the Cu(2 1 1) step have been investigated. The activation energies range from 0.09 to 0.24 eV, comparable to a minimum activation energy of 0.20 eV found on Cu(1 1 1). However, compared to Cu(1 1 1) the paths on Cu(2 1 1) are stabilized in their entirety by the step by ∼0.5 eV in terms of initial state, transition state, and final state energies. The dissociation of O₂ precursors at the foot of the step is close to being barrier-less. Because of the small dissociation barrier on Cu(1 1 1), the effect of steps on O₂ dissociation is nevertheless not expected to be as pronounced as in other gas/metal systems.     

The CuGaSe2(0 0 1) surface: A (4 × 1) reconstruction

We report on the formation of a stable (4 × 1) reconstruction of the chalcopyrite CuGaSe₂(0 0 1) surface. Using Ar⁺ ion-bombardment and annealing of epitaxial CuGaSe₂ films grown on GaAs(0 0 1) substrates it was possible to obtain flat, well-ordered surfaces showing a clear (4 × 1) reconstruction. The cleanliness and structure were analyzed in situ by AES and LEED. AES data suggest a slight Se-enrichment and Cu-depletion upon surface preparation. Our results demonstrate that (0 0 1) surfaces of the Cu-III-VI₂(0 0 1) material can show stable, unfacetted surfaces.     

Initial stages of oxidation of Cu(1 1 1)

Several surface analysis techniques were combined to study the initial stages of oxidation of Cu(1 1 1) surfaces exposed to O₂ at low pressure (<5 × 10⁻⁶ mbar) and room temperature. Scanning tunneling microscopy (STM) results show that the reactivity is governed by the restructuring of the Cu(1 1 1) surface. On the terraces, oxygen dissociative adsorption leads to the formation of isolated O adatoms and clusters weakly bound to the surface. The O adatoms are located in the fcc threefold hollow sites of the unrestructured terraces. Friedel oscillations with an amplitude lower than 5 pm have been measured around the adatoms. At step edges, surface restructuring is initiated and leads to the nucleation and growth of a two-dimensional disordered layer of oxide precursor. The electronic structure of this oxide layer is characterised by a band gap measured by scanning tunneling spectroscopy to be ∼1.5 eV wide. The growth of the oxide islands progresses by consumption of the upper metal terraces to form triangular indents. The extraction of the Cu atoms at this interface generates a preferential orientation of the interface along the close-packed directions of the metal. A second growth front corresponds to the step edges of the oxide islands and progresses above the lower metal terraces. This is where the excess Cu atoms extracted at the first growth front are incorporated. STM shows that the growing disordered oxide layer consists of units of hexagonal structure with a first nearest neighbour distance characteristic of a relaxed Cu-Cu distance (∼0.3 nm), consistent with local Cu₂O(1 1 1)-like elements. Exposure at 300 °C is necessary to form an ordered two-dimensional layer of oxide precursor. It forms the so-called “29” superstructure assigned to a periodic distorted Cu₂O(1 1 1)-like structure.     

Structure and dynamics of the missing-row reconstruction on O/Cu(0 0 1) and O/Ag(0 0 1)

The geometry and the vibrational properties of missing row reconstructed O/Cu(0 0 1) and O/Ag(0 0 1) surfaces are investigated by means of density functional theory and density functional perturbation theory, using the local density and the generalized-gradient approximations. Our results predict very similar structural and vibrational properties for the two reconstructed surfaces. In the case of copper our calculations reproduce quite accurately the experimental results, while for the missing row reconstructed O/Ag(0 0 1) surface the agreement between theory and experiment is less satisfactory.     

LCAO study of the Cu(1 1 0)-p(2 × 1)O surface

We have performed semi-empirical LCAO calculations of the electronic structure of the Cu(1 1 0)-p(2 × 1)O surface. This has been done accounting for the Cu-Cu interactions by means of a recently proposed set of parameters, which give very good results for the bulk as well as for the surfaces of lowest Miller indices. Furthermore, the O-O interactions, which have been neglected in the preceding similar studies, have been taken into account. The resulting surface bands are in very good agreement with the overall set of the available experimental data. Several issues concerning the physical properties of this surface are addressed in the present paper: the changes induced on the clean surface bands by the adsorption and the reconstruction; the arrangement of the Cu and O atoms in the added rows; the position of the p_y antibonding band of the oxygen. In particular, we have found that the latter has an energy of −0.2 eV at the point. This result confirms an experimental indication in the same direction previously reported by Courths et al. [R. Courths, S. Hüfner, P. Kemkes, G. Wiesen, Surf. Sci. 376 (1997) 43].     

Oxidation and thermal reduction of the Cu(1 0 0) surface as studied using positron annihilation induced Auger electron spectroscopy (PAES)

Changes in the surface of an oxidized Cu(1 0 0) single crystal resulting from vacuum annealing have been investigated using positron annihilation induced Auger electron spectroscopy (PAES). PAES measurements show a large increase in the intensity of the annihilation induced Cu M_2,3VV Auger peak as the sample is subjected to a series of isochronal anneals in vacuum up to annealing temperature 300 °C. The intensity then decreases monotonically as the annealing temperature is increased to ∼600 °C. Experimental probabilities of annihilation of surface-trapped positrons with Cu 3p and O 1s core-level electrons are estimated from the measured intensities of the positron annihilation induced Cu M_2,3VV and O KLL Auger transitions. Experimental PAES results are analyzed by performing calculations of positron surface states and annihilation probabilities of surface-trapped positrons with relevant core electrons taking into account the charge redistribution at the surface, surface reconstructions, and electron-positron correlations effects. The effects of oxygen adsorption on localization of positron surface state wave function and annihilation characteristics are also analyzed. Possible explanation is proposed for the observed behavior of the intensity of positron annihilation induced Cu M_2,3VV and O KLL Auger peaks and probabilities of annihilation of surface-trapped positrons with Cu 3p and O 1s core-level electrons with changes of the annealing temperature.     

In situ XPS study of Pd(1 1 1) oxidation. Part 1: 2D oxide formation in 10 mbar O2

The oxidation of the Pd(1 1 1) surface was studied by in situ XPS during heating and cooling in 3 × 10⁻³ mbar O₂. A number of adsorbed/dissolved oxygen species were identified by in situ XPS, such as the two dimensional surface oxide (Pd₅O₄), the supersaturated O_ads layer, dissolved oxygen and the R 12.2° surface structure.Exposure of the Pd(1 1 1) single crystal to 3 × 10⁻³ mbar O₂ at 425 K led to formation of the 2D oxide phase, which was in equilibrium with a supersaturated O_ads layer. The supersaturated O_ads layer was characterized by the O 1s core level peak at 530.37 eV. The 2D oxide, Pd₅O₄, was characterized by two O 1s components at 528.92 eV and 529.52 eV and by two oxygen-induced Pd 3d_5/2 components at 335.5 eV and 336.24 eV. During heating in 3 × 10⁻³ mbar O₂ the supersaturated O_ads layer disappeared whereas the fraction of the surface covered with the 2D oxide grew. The surface was completely covered with the 2D oxide between 600 K and 655 K. Depth profiling by photon energy variation confirmed the surface nature of the 2D oxide. The 2D oxide decomposed completely above 717 K. Diffusion of oxygen in the palladium bulk occurred at these temperatures. A substantial oxygen signal assigned to the dissolved species was detected even at 923 K. The dissolved oxygen was characterised by the O 1s core level peak at 528.98 eV. The “bulk” nature of the dissolved oxygen species was verified by depth profiling.During cooling in 3 × 10⁻³ mbar O₂, the oxidised Pd²⁺ species appeared at 788 K whereas the 2D oxide decomposed at 717 K during heating. The surface oxidised states exhibited an inverse hysteresis. The oxidised palladium state observed during cooling was assigned to a new oxide phase, probably the R 12.2° structure.     

Characterisation of the interaction of glycine with Cu(1 0 0) and Cu(1 1 1)

Reflection-absorption infrared spectroscopy (RAIRS) has been used to characterise the interaction of standard and fully deuterated glycine with Cu(1 0 0) and Cu(1 1 1). RAIRS shows clearly that the surface interaction leads to formation of the adsorbed deprotonated glycinate (NH₂CH₂COO-) species, with some evidence for changes in orientation with coverage previously seen on Cu(1 1 0). Qualitative low energy electron diffraction observations were also conducted to characterise the long-range ordering, although effects of electron-beam-induced radiation damage limited the information obtained. Nevertheless, the results do suggest some subtle isotopic-mass-related structural variations. The results are discussed in the context of previously published scanning tunnelling microscopy and photoelectron diffraction measurements.     

Insulating properties of ultrathin KF layers on Cu(1 0 0): Resonant Auger spectroscopy

Solid-state effects in the creation and decay of K 2p core excitations in thin KF films on Cu(1 0 0) surface have been studied in resonant Auger spectra, excited using synchrotron radiation. The spectra of films of various thickness starting from a single monolayer were measured.The photoabsorption spectra reveal crystal field splitting already at film thickness of about 1 monolayer. The Auger decay spectra of the K 2p⁻¹3d core excitations in films of thickness up to 2 monolayers exhibit a band characteristic of the decay of core ionised states, showing that the excited electron delocalises into substrate before the core hole decays. In thicker films the coexistence of the decay of excited states in the bulk of the KF crystalline film and of ionised states at the KF-metal interface is observed, indicating that the charge transfer probability from the upper layers of the film into the metallic substrate is strongly reduced.     

Interdiffusion of adsorbed Pb and Bi on Cu(1 0 0)

The impingement and interdiffusion of adsorbed Pb and Bi layers spreading from separated 3D pure bulk sources on Cu(1 0 0) has been studied, at T = 513 K, by in situ scanning Auger microscopy. When the leading edges of the pure Pb and Bi diffusion profiles impinge, they both consist of low-coverage lattice gas surface alloyed phases. In these low-coverage phases, Pb displaces surface alloyed Bi and the point of intersection of the profiles drifts towards the Bi source. These features lead to the conclusion that Pb atoms are more strongly bound at surface alloyed sites in Cu(1 0 0) than Bi atoms. Once the total coverage (Pb + Bi) on the substrate reaches about one monolayer, Pb and Bi are dealloyed from the substrate, and the interdiffusion profiles become essentially symmetric. Pb and Bi mix in all proportions, with an interdiffusion coefficient of ∼10⁻¹³ m²/s. This is considerably smaller than the self-diffusion coefficients previously observed for pure Pb and Bi in their respective high-coverage phases, indicating that the mechanism of interdiffusion is different from that of self-diffusion. As interdiffusion proceeds, the point of intersection of the Pb and Bi profiles reverses its drift direction, leading to the conclusion that binding of Bi atoms to the Cu(1 0 0) substrate is stronger than that of Pb atoms in the highest-coverage surface dealloyed layers.     

An ordered surface ternary alloy of a c(6 × 4) structure formed on Cu(0 0 1) by substitutional coadsorption of Mg and Bi

A c(6 × 4) structure formed on Cu(0 0 1) by the coadsorption of Mg and Bi atoms at room temperature has been determined by a tensor low energy electron diffraction analysis. It is an ordered surface ternary alloy with a thickness of single layer, in which Mg, Bi and Cu atoms are mixed in the top layer. In the primitive unit cell, there are one Mg, four Bi, six Cu atoms and one vacancy in the top layer, and substituted Mg and Bi atoms form MgBi₄ plane clusters being arranged in the c(6 × 4) order. Structural parameters show that Mg-Bi bond distances in the MgBi₄ cluster are 3.01 and 3.07 Å, which are shorter than the summation of metallic radii of Mg and Bi. It is concluded that a direct, attractive interaction between Mg and Bi atoms plays critical role in the formation of the c(6 × 4) structure.