非晶态锂离子导体B2O3-0.7Li2O-0.7LiCl-xAl2O3-0.1V2O5的电学性质和电子自旋共振研究

对两种非晶态B₂O₃-0.7Li₂O-0.7LiCl-xAl₂O₃-0.1V₂O₅(x=0.05和0.15),用差热分析、电导率测量、X射线衍射和电子自旋共振进行研究,发现:1)V₂O₅不仅作非晶网络形成剂,而且改变了晶化过程;2)对B₂O₃-Li_{2关键词：}     

高温氢退火还原V2O5制备二氧化钒薄膜及其性能的研究

过渡金属氧化物二氧化钒(VO₂)在温度340 K附近会发生金属绝缘体的转变(metal-insulator transition, MIT). 基于金属绝缘体的转变性质, VO₂薄膜材料具有很好的应用前景. 本文首先采用脉冲激光沉积制备了高质量的V₂O₅薄膜, 再通过高温氢退火还原V₂O₅薄膜制备出VO₂多晶薄膜. 研究了不同的退火温度、退火时间、退火气氛对VO₂薄膜制备的影响, 采用X射线衍射、X射线光电子能谱、变温电阻特性测量等手段对样品进行分析, 发现在H₂(5%)/Ar退火气氛下, 在一定的退火温度范围内(500–525 ℃), 退火 3 h, 得到了B相和M相共存的VO₂薄膜, 具有M相的VO₂的MIT特性, 而相同退火温度下退火时间达到4.5 h, 薄膜完全变成B相的VO₂. 通过纯Ar气氛下对B相VO₂再退火, 得到了转变温度为350 K, 电阻突变接近4个数量级的M相的VO₂薄膜. 实现了VO₂的B相和M相的相互转变. 关键词： 2薄膜')" href="#">VO₂薄膜 金属绝缘体转变 氢退火     

超高温度系数V0.97W0.03 O2多晶薄膜的制备研究

将V₂O₅粉体与WO₃粉体均匀混合并压制成靶，用离子束增强沉积加后退火技术在SiO₂衬底上制备掺钨VO₂多晶薄膜.X射线衍射表明，薄膜取向单一，为VO₂结构的［002］相,晶格参数d比VO₂粉晶增大约0.34%；薄膜从半导体相向金属相转变的相变温度约28；室温(300 K)时的电阻-温度系数(TCR)可大于10%/K，是目前红外热成像薄膜TCR的四倍.W离子的半径大于V离子的半径，W的掺入在薄膜中引入了张应力,使薄膜相变温度降低到室温附近，是IBED V_0.97W_0.03O₂薄膜的室温电阻温度系数提高的原因. 关键词： 二氧化钒薄膜 薄膜掺杂 离子束增强沉积     

基于旋涂法和电子束蒸发法制备的V2O5/Ag/V2O5叠层透明导电薄膜

利用溶胶-凝胶技术与电子束蒸镀相结合的方法在常温下制备了叠层V₂O₅/Ag/V₂O₅（VAV）透明导电薄膜,研究了各层薄膜厚度对叠层结构光电特性的影响。用原子力显微镜、紫外-可见光分光光度计、四探针电阻仪及开尔文探针对样品的表面形貌、光电性能及功函数等性质进行了表征。实验结果表明,该薄膜具有良好的光学和电学性质,可见光（380~780 nm）平均透过率达75%,迁移率为16.89 cm²/（V·s）,载流子浓度为－1.043×10²² cm^-3,方块电阻值为15.1 Ω/□,功函数为5.17 eV。该制备方法降低了V₂O₅薄膜的工艺制备难度,为该材料在太阳能电池中的应用创造了良好的前期基础。     

CeO2/Nb2O5界面效应对提高CeO2氧敏特性的XPS研究

用射频/直流磁控溅射法制备了CeO₂/Nb₂O₅双层氧敏薄膜，利用X射线光电子能谱(XPS)，描述并解释了单层CeO₂薄膜中氧随温度变化的动力学行为，以及CeO₂/Nb₂O₅薄膜界面对氧敏特性的影响.通过对Ce3d XPS谱的高斯拟合，计算了Ce³⁺浓度并给出了判定Ce⁴⁺还原的标志.结果表明，界面效应可以提高CeO₂/Nb₂O₅薄膜中Ce⁴⁺的还原能力，使之远远高于单层CeO₂薄膜，这对薄膜的氧敏特性是极为有利的. 关键词：     

Li2O-Nb2O-SiO2系统非晶态离子导体的结构与电学性能

本文采用红外吸收光谱法、X射线散射法和EXAFS方法研究了LiO-Nb₂O-SiO₂系统非晶态离子导体的结构,认为Nb⁵⁺在非晶结构网络中主要是以[NbO₆]形式存在。非晶结构随Nb₂O₅含量的多少而变化。低Nb₂O₅含量时,[NbO₆]相互间以边相连,并与[SiO₄]组成多元环后,形成非晶网络结构。高Nb₂O₅含量时,非晶网络结构主要是以角顶相连的[NbO₆]所组成。根据电导测试结果,讨论了结构与电学性能的关系,认为Li₂O含量在0.45左右,Nb₂O₅,含量在0.3左右组成的非晶材料有最高的电导率。 关键词：     

Eu3+掺杂钛酸钇晶态薄膜的制备与高效红色荧光发射

采用溶胶-凝胶法制备了Eu³⁺掺杂的钛酸钇晶态发光薄膜。通过X射线衍射(XRD)对薄膜的结构和结晶过程进行了分析,利用荧光分光光度计对薄膜的发光性质开展了测试和研究。XRD结果表明,薄膜包含立方相Y_xTi_1-xO_1-0.5x晶粒,该晶粒属立方晶系,Fm3m(225)空间群,晶胞参数a=0.530nm,晶粒尺寸约为17nm。荧光光谱表明,Eu³⁺掺杂的Y_xTi_1-xO_1-0.5x薄膜显示了强的红光发射,其中Eu³⁺的⁵D₀→⁷F₂超灵敏跃迁为最强一组。紫外氙灯、准分子激光器、汞灯等是这种发光薄膜的有效激发源。     

氧化钒薄膜微观结构的研究

采用直流磁控反应溅射在Si(100)衬底上溅射得到(001)取向的V₂O₅薄膜.x射线衍射(XRD)、扫描电镜(SEM)和傅里叶变换红外光谱(FTIR)的结果表明，氧分压影响薄膜的成分和生长取向，在氧分压0.4Pa时溅射得到(001)取向的纳米V₂O₅薄膜，即沿c轴垂直衬底方向取向生长的薄膜.V₂O₅薄膜经过真空退火得到(001)取向的VO₂薄膜，晶体颗 关键词： 微观结构 氧化钒薄膜 择优取向 直流磁控溅射     

氧压对SrTiO3和SrNb0.2Ti0.8O3薄膜晶格参数的影响及激光感生热电电压效应

采用脉冲激光沉积技术制备了SrTiO₃和SrNb_0.2Ti_0.8O₃薄膜.X射线衍射分析表明在LaAlO₃(100)单晶平衬底上生长的SrTiO₃及SrNb_0.2Ti_0.8O₃薄膜是沿［001］取向的近外延生长.随着氧压在一定范围内逐渐增大,SrTiO₃薄膜的晶格参数减小,而SrNb_0.2Ti_0.8O₃薄膜的晶格参数先减小后增大.同时摸索出制备具有二维电子气超晶格(SrTiO₃/SrNb_0.2Ti_0.8O₃)_L的最佳氧压为1.0×10^-2Pa.另外在LaAlO₃(100)倾斜衬底上制备的SrNb_0.2Ti_0.8O₃薄膜中观察到激光感生热电电压效应. 关键词： 0.2Ti_0.8O₃薄膜')" href="#">SrNb_0.2Ti_0.8O₃薄膜 晶格参数 激光感生热电电压 脉冲激光沉积     

InP/SiO2纳米复合膜的微观结构和光学性质

应用射频磁控共溅射方法在石英玻璃和抛光硅片上制备了InP/SiO₂复合薄膜,并在几种条件下对这些薄膜进行退火.X射线光电子能谱和卢瑟福背散射实验结果表明,复合薄膜中InP和SiO₂的化学组分都大体上符合化学计量配比.X射线衍射和激光喇曼谱实验结果都证实了复合薄膜中形成了InP纳米晶粒.磷气氛保护下的高温(520℃)退火可以消除复合薄膜中残存的In和In₂O₃并得到了纯InP/SiO₂纳米复合薄膜.实验观察到了室温下纳米复合薄膜的明显的光学吸收边蓝移现象和光学非线性的极大增强 关键词： InP 纳米晶粒 微观结构 光学性质     

Influence of the laser wavelength on the epitaxial growth and electrical properties of La0.8Sr0.2MnO3 films grown by excimer laser-assisted MOD

Epitaxial La_1−xSr_xMnO₃ (LSMO) films were prepared by excimer laser-assisted metal organic deposition (ELAMOD) at a low temperature using ArF, KrF, and XeCl excimer lasers. Cross-section transmission electron microscopy (XTEM) observations confirmed the epitaxial growth and homogeneity of the LSMO film on a SrTiO₃ (STO) substrate, which was prepared using ArF, KrF, and XeCl excimer lasers. It was found that uniform epitaxial films could be grown at 500 °C by laser irradiation. When an XeCl laser was used, an epitaxial film was formed on the STO substrate at a fluence range from 80 to 140 mJ/cm² of the laser fluence for the epitaxial growth of LSMO film on STO substrate was changed. When the LaAlO₃ (LAO) substrate was used, an epitaxial film was only obtained by ArF laser irradiation, and no epitaxial film was obtained using the KrF and XeCl lasers. When the back of the amorphous LSMO film on an LAO substrate was irradiated using a KrF laser, no epitaxial film formed. Based on the effect of the wavelength and substrate material on the epitaxial growth, formation of the epitaxial film would be found to be photo thermal reaction and photochemical reaction. The maximum temperature coefficient of resistance (TCR) of the epitaxial La_0.8Sr_0.2MnO₃ film on an STO substrate grown using an XeCl laser is 4.0%/K at 275 K. XeCl lasers that deliver stabilized pulse energies can be used to prepare LSMO films with good a TCR.     

Analyses of surface coloration on TiO2 film irradiated with excimer laser

TiO₂ film of around 850 nm in thickness was deposited on a soda-lime glass by PVD sputtering and irradiated using one pulse of krypton-fluorine (KrF) excimer laser (wavelength of 248 nm and pulse duration of 25 ns) with varying fluence. The color of the irradiated area became darker with increasing laser fluence. Irradiated surfaces were characterized using optical microscopy, scanning electron microscopy, Raman spectroscopy and atomic force microscopy. Surface undergoes thermal annealing at low laser fluence of 400 and 590 mJ/cm². Microcracks at medium laser fluence of 1000 mJ/cm² are attributed to surface melting and solidification. Hydrodynamic ablation is proposed to explain the formation of micropores and networks at higher laser fluence of 1100 and 1200 mJ/cm². The darkening effect is explained in terms of trapping of light in the surface defects formed rather than anatase to rutile phase transformation as reported by others. Controlled darkening of TiO₂ film might be used for adjustable filters.     

Damage performance of TiO2/SiO2 thin film components induced by a long-pulsed laser

In order to study the long-pulsed laser induced damage performance of optical thin films, damage experiments of TiO₂/SiO₂ films irradiated by a laser with 1 ms pulse duration and 1064 nm wavelength are performed. In the experiments, the damage threshold of the thin films is measured. The damages are observed to occur in isolated spots, which enlighten the inducement of the defects and impurities originated in the films. The threshold goes down when the laser spot size decreases. But there exists a minimum threshold, which cannot be further reduced by decreasing the laser spot size. Optical microscopy reveals a cone-shaped cavity in the film substrate. Changes of the damaged sizes in film components with laser fluence are also investigated. The results show that the damage efficiency increases with the laser fluence before the shielding effects start to act.     

Crystallization of amorphous Ge2Sb2Te5 films induced by a single femtosecond laser pulse

Crystallization is achieved in amorphous Ge₂Sb₂Te₅ films upon irradiation with a single femtosecond laser pulse. Transmission electron microscopy images evidence the morphology of the crystallized spot which depends on the fluence of the femtosecond laser pulse. Fine crystalline grains are induced at low fluence, and the coarse crystalline grains are obtained at high fluence. At the damage fluence, ablation of the films occurs.     

准分子激光作用下二氧化钛的表面变性

适当能量密度的准分子激光作用于二氧化钛时，电导性能发生了显著的变化，室温下从原来的绝缘体转变为半导体，同时表面颜色也发生了变化．利用X射线衍射、X射线光电子能谱及显微分析等多种测试方法进行了分析、比较，确定了该过程是由于短脉冲的准分子激光作用，造成了二氧化钛的快速升温熔化和快速冷凝重构，导致氧的缺位，引起了化学配比偏离．用热传导方程对能量密度阈值进行了近似估算，结果与实验基本相符 关键词：     

Preparation of the La0.8Sr0.2MnO3 films on STO and LAO substrates by excimer laser-assisted metal organic deposition using the KrF laser

La_0.8Sr_0.2MnO₃ films were prepared on SrTiO₃ (STO) and LaAlO₃ (LAO) substrates using excimer laser-assisted metal organic deposition (ELAMOD). For the LAO substrate, no epitaxial La_0.8Sr_0.2MnO₃ film was obtained by laser irradiation in the fluence range from 60 to 110 mJ/cm² with heating at 500 °C. On the other hand, an epitaxial La_0.8Sr_0.2MnO₃ film on the STO substrate was formed by laser irradiation in the fluence range from 60 to 100 mJ/cm² with heating at 500 °C. To optimize the electrical properties for an IR sensor, the effects of the laser fluence, the irradiation time and the film thickness on the temperature dependence of the resistance and temperature coefficient of resistance (TCR: defined as 1/R·(dR/dT)) of the LSMO films were investigated. An LSMO film on the STO substrate that showed the maximum TCR of 3.9% at 265 K was obtained by the ELAMOD process using the KrF laser.     

Investigation on upconversion photoluminescence of Bi3TiNbO9:Er:Yb thin films

Bi₃TiNbO₉:Er³⁺:Yb³⁺ (BTNEY) thin films were fabricated on fused silica by pulsed laser deposition. It was demonstrated that different laser fluence and substrate temperature during growth of BTNEY upconversion photoluminescence (UC-PL) samples control the film’s grain size and hence influences the UC-PL properties. The average grain size of BTNEY thin films deposited on fused silica substrates with laser fluence 4, 5, 6, and 7 J/cm² are 30.8, 35.9, 40.6, and 43.4 nm, respectively. The 525 nm emission intensities increase with the deposition laser fluence and the emission intensities of BTNEY thin film deposited under 700 and 600 °C are almost 24 and 4 times, respectively, as strong as those of samples under 500 °C. The grain size of BTNEY thin film increases with the increasing temperature. UC-PL of BTNEY films is enhanced by increasing grain size of the films.     

La2/3Ca1/3MnO3薄膜的光致电阻率变化特性

射频磁控溅射法制备了La_2/3Ca_1/3MnO₃纳米薄膜(LCMO).该薄膜发生FM-PM相变的转变点温度为T_c≈308K（近似为电阻峰值温度T_p）；在不同温度下的光电导性质实验表明所制备的LCMO薄膜在连续激光作用时低温段（Tc）表现为光致电阻率增大效应，即ΔR/R＞0，并在R-T曲线拐点附近取得极大值，（ΔR/R）_max=43.5%；当T>T关键词： 钙钛矿薄膜 光响应 电子自旋 小极化子     

Different crystallization processes of as-deposited amorphous Ge2Sb2Te5 films on nano- and picosecond single laser pulse irradiation

The crystallization dynamics of as-deposited amorphous Ge₂Sb₂Te₅ films induced by nano- and picosecond single laser pulse irradiation is studied using in situ reflectivity measurements. Compared with nanosecond laser pulse, the typical recalescence phenomenon did not appear during the picosecond laser pulse-induced crystallization processes when the pulse fluence gradually increased from crystallization to ablation threshold. The absence of melting and recalescence phenomenon significantly decreased the crystallization time from hundreds to a few tens of nanoseconds. The role of pulse duration time scale on the crystallization process is qualitatively analyzed.     

Femtosecond laser patterning of Ta0.1W0.9Ox/ITO thin film stack

Selective laser patterning of thin films in a multilayered structure is an emerging technology for process development and fabrication of optoelectronics and microelectronics devices. In this work, femtosecond laser patterning of electrochromic Ta_0.1W_0.9O_x film coated on ITO glass has been studied to understand the selective removal mechanism and to determine the optimal parameters for patterning process. A 775 nm Ti:sapphire laser with a pulse duration of 150 fs operating at 1 kHz was used to irradiate the thin film stacks with variations in process parameters such as laser fluence, feedrate and numerical aperture of objective lens. The surface morphologies of the laser irradiated regions have been examined using a scanning electron microscopy and an optical surface profiler. Morphological analysis indicates that the mechanism responsible for the removal of Ta_0.1W_0.9O_x thin films from the ITO glass is a combination of blistering and explosive fracture induced by abrupt thermal expansion. Although the pattern quality is divided into partial removal, complete removal, and ITO film damage, the ITO film surface is slightly melted even at the complete removal condition. Optimal process window, which results in complete removal of Ta_0.1W_0.9O_x thin film without ablation damage in the ITO layer, have been established. From this study, it is found that focusing lens with longer focal length is preferable for damage-free pattern generation and shorter machining time.