预处理条件对用于CO2加氢的超细CuO—ZnO—SiO2催化剂性能的影响

采用ＸＲＤ、ＢＥＴ、ＴＰＲ手段，研究了焙烧还原温度对超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的性质及其ＣＯ２加氢反应催化活性的影响，胶体在５７３－７７３Ｋ范围内焙烧生成ＣｕＯ、ＣＵ２Ｏ、ＺｎＯ晶相，随着焙烧温度继续升高，ＣｕＯ和ＺｎＯ晶粒逐渐变大，但催化剂的比表面积和孔容变化不不，在９７３Ｋ焙烧后出现Ｚｎ２ＳｉＯ４晶相，使催化剂比表积和孔容积变小，导致催化剂活性降低，焙地催化剂活性的影响在于对ＣＯ２加氢     

锰助剂对Fe／ZrO2催化剂F—T反应催化性能的影响

应用ＸＲＤ，ＸＰＳ，Ｍｏｓｓｂａｕｅｒ谱，ＴＰＲ，ＣＯ化学吸附ＣＯ－ＴＰＤ，ＣＯ＋Ｈ２反应性能测试等手段研究了锰助剂对Ｆ－Ｔ合成制低碳烯烃Ｍｎ－Ｆｅ／ＺｒＯ２催化剂结构及催化性能的影响。结果表明，与Ｆｅ／Ｚｒ催化相比，加锰助剂后的催化剂Ｆ－Ｔ反应催化活性上升，甲烷选择性降低，低碳烯烃选择性增加。     

助剂对超细CuO－ZnO－SiO_2催化剂性质和CO_2加氢反应性能的影响

研究了９种助剂对用于ＣＯ２加氢反应的超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂性能的影响，并进行了ＸＲＤ和ＴＰＲ表征．结果表明，助剂影响超细催化剂的性质和催化性能，ＴｉＯ２、ＣｅＯ２、ＭｇＯ和Ｌａ２Ｏ３是ＣＯ２加氢合成甲醇的超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂体系的优良助剂．在含有不同助剂的ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂体系内存在ＣｕＯ和ＺｎＯ晶相，但除ＣｅＯ２以外，其它的助剂都可能以微晶或无定型的形式存在．ＴＰＲ研究表明，添加的助剂除ＣｅＯ２以外，都使超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的还原温度提高，而且助剂对ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂活性的影响，按照助剂对ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂还原温度的影响进行了探讨     

超细CuO／ZnO／SiO2催化上CO2和CO加氢反应对比—CO2加氢反应机理

在超细ＣｕＯ／ＺｎＯ／ＳｉＯ２催化剂体系上，对比研究了ＣＯ２和ＣＯ加氢性能，并就ＣＯ２加氢的反应机理进行了探讨。考察了接触时间和反应压力对ＣＯ２加氢的主要产物甲醇和ＣＯ分布的影响。     

助剂SiO2对CO2加氢制二甲醚催化剂Cu-ZnO/HZSM-5性能的影响

 考察了助剂SiO2对CO2加氢合成二甲醚催化剂Cu-ZnO/HZSM-5性能的影响,并用X射线衍射、程序升温还原和X射线光电子能谱等手段对催化剂进行了表征. 结果表明,加入少量的SiO2即可显著提高CO2的转化率、二甲醚的选择性以及二甲醚和甲醇的总选择性,并降低副产物CO的选择性,同时改善催化剂的稳定性; 但SiO2加入量大时,催化活性反而降低. SiO2的存在可使焙烧后催化剂的晶型结构发生改变,促进CuO和ZnO的分散,并提高CuO的还原温度. SiO2的加入抑制了反应过程中催化剂上Cu0和ZnO晶粒的长大,对活性物种Cu0有稳定作用,从而有利于提高催化剂的活性和稳定性.     

Fe—Silicalite—2催化剂表面CO2加氢反应性能的研究

研究了Ｆｅ／Ｓｉｌｉｃａｌｉｔｅ－２催化剂ＣＯ２加氢低碳烯烃反应性能，利用ＣＯ２－ＴＰＤ，ＣＯ２／Ｈ２－ＴＰＳＲ和ＣＯ／Ｈ２－ＴＰＳＲ表征手段，考察了铁含量及ＭｎＯ助剂对Ｆｅ／Ｓｉｌｉｃａｌｉｔｅ－２催化剂ＣＯ２吸附脱附及加氢反应性能的影响，表明随铁含量增加可提高催化剂对ＣＯ２的吸附能力，有利于提高ＣＯ２加氢反应的转化率。     

锰基催化剂上CO2加氢反应性能的研究

研究了Ｍｎ基催化上ＣＯ２的加氢反应性能，结果表明：ＣＯ２活化吸附量的增加有利于ＣＯ２转化率的提高。Ｍｎ具有较好的ＣＯ２加氢生成ＣＯ的催化活性，ＣｕＯ，Ｆｅ２Ｏ３的ＺｎＯ的加入使催化剂活性得到进一步的提高；ＮｉＯ的加入增加了催化剂的Ｈ２活化吸附量，从而使催化剂对ＣＨ４的选择性得到提高，同时使ＣＯ２的转化率与Ｎｉ／γ－Ａｌ２Ｏ３相比略有下降。     

Ru作为Co—Mo／Al2O3加氢脱硫催化剂助剂的研究

用Ru改性的Ru-Co-Mo/Al_2O_3对噻吩加氢脱硫的催化性能进行了考察。结果表明,与Co-Mo/Al_2O_3相比,Ru-Co-Mo/Al_2O_3的加氢脱硫活性增高。通过CO、NO吸附的红外光谱实验证实,由于Ru的加入,吸附在Co和Mo中心上的特征谱带向低波数移动,且峰强度增强,这些结果提出了在硫化态Ru-Co-Mo/Al_2O_3上,Ru中心的部分d电子转移到Co、Mo中心的周围或由于Ru的存在促进了Co、Mo中心的还原。     

探究Cu/ZnO相互作用对CO2加氢制甲醇反应性能的影响

Using renewable green hydrogen and carbon dioxide (CO₂) to produce methanol is one of the fundamental ways to reduce CO₂ emissions in the future, and research and development related to catalysts for efficient and stable methanol synthesis is one of the key factors in determining the entire synthesis process. Metal nanoparticles stabilized on a support are frequently employed to catalyze the methanol synthesis reaction. Metal-support interactions (MSIs) in these supported catalysts can play a significant role in catalysis. Tuning the MSI is an effective strategy to modulate the activity, selectivity, and stability of heterogeneous catalysts. Numerous studies have been conducted on this topic; however, a systematic understanding of the role of various strengths of MSI is lacking. Herein, three Cu/ZnO-SiO₂ catalysts with different strengths of MSI, namely, normal precipitation Cu/ZnO-SiO₂ (Nor-CZS), co-precipitation Cu/ZnO-SiO₂ (Co-CZS), and reverse precipitation Cu/ZnO-SiO₂ (Re-CZS), were successfully prepared to determine the role of such interactions in the hydrogenation of CO₂ to methanol. The results of temperature-programmed reduction (H₂-TPR) and X-ray photoelectron spectroscopy (XPS) characterization illustrated that the MSI of the catalysts was considerably affected by the precipitation sequence. Fourier transform infrared reflection spectroscopy (FT-IR) results indicated that the Cu species existed as CuO in all cases and that copper phyllosilicate was absent (except for strong Cu-SiO₂ interaction). Transmission electron microscopy (TEM), X-ray diffraction (XRD), and N₂O chemical titration results revealed that strong interactions between the Cu and Zn species would promote the dispersion of Cu species, thereby leading to a higher CO₂ conversion rate and improved catalytic stability. As expected, the Re-CZS catalyst exhibited the highest activity with 12.4% CO₂ conversion, followed by the Co-CZS catalyst (12.1%), and the Nor-CZS catalyst (9.8%). After the same reaction time, the normalized CO₂ conversion of the three catalysts decreased in the following order: Re-CZS (75%) > Co-CZS (70%) > Nor-CZS (65%). Notably, the methanol selectivity of the Re-CZS catalyst was found to level off after a prolonged period, in contrast to that of Co-CZS and Nor-CZS. Investigation of the structural evolution of the catalyst with time on stream revealed that the high methanol selectivity of the catalyst was caused by the reconstruction of the catalyst, which was induced by the strong MSI between the Cu and Zn species, and the migration of ZnO onto Cu species, which caused an enlargement of the Cu/ZnO interface. This work offers an alternative strategy for the rational and optimized design of efficient catalysts.     

预处理条件对用于CO_2加氢的超细CuO－ZnO－SiO_2催化剂性能的影响

采用ＸＲＤ、ＢＥＴ、ＴＰＲ手段，研究了焙烧和还原温度对超细ＣｕＯ－ＺｎＯ－ＳｉＯ２催化剂的性质及其ＣＯ２加氢反应催化活性的影响．胶体在５７３－７７３Ｋ范围内焙烧生成ＣｕＯ、Ｃｕ２Ｏ、ＺｎＯ晶相，随着焙烧温度继续升高，ＣｕＯ和ＺｎＯ晶粒逐渐变大，但催化剂的比表面积和孔容变化很小．在９７３Ｋ焙烧后出现Ｚｎ２ＳｉＯ４晶相，使催化剂比表积和孔容变小，导致催化剂活性降低．焙烧温度对催化剂活性的影响大于对ＣＯ２加氢产物分布的影响．在５４８－６４８Ｋ范围内，催化剂还原温度对其催化活性影响不大．７０３Ｋ高温还原后，可能由于Ｃｕ０晶粒的出现，使得催化剂的活性下降．ＴＰＲ研究结果进一步表明，焙烧温度影响ＣｕＯ同ＺｎＯ、ＳｉＯ２之间的相互作用和催化剂的还原行为．     

助剂Mn对CO2加氢制二甲醚CuO-ZnO-ZrO2/HZSM-5催化剂的结构和性能影响

以无水乙醇为溶剂,草酸为沉淀剂,采用悬浮共沉淀法,一步合成Mn改性的CuO-ZnO-ZrO2/HZSM-5双功能催化剂.并研究了该催化剂在CO2加氢合成二甲醚反应中的催化性能,考察了助剂锰的添加量对催化剂性能的影响,并采用XRD、BET、TPR、NH3-TPD和XPS对催化剂结构进行表征.结果表明,双功能催化剂性能与助剂锰的添加量有密切联系,适量锰的加入可提供合适的表面酸性,提高二甲醚的选择性,降低副产物CO的选择性.表征结果表明,加入Mn可以促进CuO的分散,并降低CuO的还原温度,增加催化剂的比表面积,提高Cu+/Cu0比,从而能促进CO2的转化,有利于提高催化剂的活性.     

助剂对Ni/海泡石催化剂加氢性能的影响

以海泡石为载体,Ｎｉ为活性组,用浸渍法制备了一系列含不同助剂的Ｎｉ基海泡石催化剂,以ＣＯ２甲烷化及苯加氢为探针反应,研究了催化剂的活性及抗硫性能,用Ｈ２－ＴＰＤ、ＸＰＳ、活性表面积及活化能的测定等于段,对催化剂进行表征,并从热力学上探讨ＣＯ２甲烷化的适宜温度。实验结果表明,海泡石或助剂的加入,能使镍晶粒变小,增加活性镍的表面积以及使镍原子的电子云密度升高,从而提高了催化剂的活性和使用寿命。能使镍晶     

CO2加氢制低碳醇CuFe基催化剂中的Mn助剂效应

采用共沉淀法制备了一系列Mn掺杂的CuFeZnK催化剂, 研究了Mn助剂对催化剂的结构及催化CO₂加氢制低碳醇合成性能的影响. 结果表明, 引入适量的Mn(质量分数2.1%)能有效提高低碳醇的选择性和时空收 率(STY), 在320 ℃和5 MPa的条件下, CO₂的转化率为29.4%, 低碳醇选择性(CO-free)达到23.2%, 时空收率达到41.1 mg·{\mathrm{g}}_{\mathrm{c}\mathrm{a}\mathrm{t}}^{-\mathrm{1}}·h^?1, 且低碳醇在总醇中的比例达到96.9%. 利用X射线衍射(XRD)、 N₂吸附-脱附实验、 X射线光电子能谱(XPS)、 透射电子显微镜(TEM)和氢气程序升温还原(H₂-TPR)等手段对制得催化剂进行表征, 结果表明, 适量Mn可以起到结构助剂的作用, 减小Cu颗粒尺寸的同时促进Fe₅C₂相的形成, 从而构建丰富的Cu-Fe₅C₂活性界面, 用于低碳醇合成. 而过量的Mn反而会堵塞催化剂的孔道, 覆盖活性位点, 降低了催化性能.     

ZrO2—SiO2负载Cu—Ni催化剂的CO2加氢反应性能

采用表面反应改性法,制备了ZrO2-SiO2（ZrSiO)表面复合物载体,用等体积浸渍法制备了ZrSiO担载的Cu-Ni双金属催化剂,借助BET、TPR、IR和微反等技术,研究了ZrSiO及其负载的Ni、Cu双金属催化剂的表面构造,化学吸附及催化CO2加氢的反应性能,结果表明,ZrSiO表面主要是价联型结构,ZrO2引入SiO2表面,可以有效地促进CuO和NiO的还原,在ZrSiO负载的Cu-Ni催化剂表面的Cu或Ni位,CO2发生化学 吸附形成线、剪式、卧式吸附态,在该催化剂上CO2的加氢反应产物主要是CH3OH3、CH4、CO和H2O生成CH3OH的选择性与催化剂组成及反应条件密切相关,在适当的条件,CH3OH的选择性大于90％。     

助剂TiO2对CO2催化加氢制甲醇催化剂CuO-ZnO-Al2O3性能的影响

采用共沉淀法,用助剂TiO2对CuO-ZnO-Al2O3催化剂改性,TiO2由钛酸正丁酯水解而得,并考察了其在CO2催化加氢制甲醇反应中的催化性能.在反应温度260℃、压力2.6 MPa、H2∶CO2 =3∶1(体积比)、SV=3600 mL/(g·h)条件下,与空白样CuO-ZnO-Al2O3比较,结果显示,TiO2...     

Ru助剂对Co/SiO2催化剂费托合成反应性能的影响

 考察了 Ru 助剂 (0.17%?9.96%) 对 Co/SiO2 催化剂结构及其费托合成反应性能的影响. 结果表明, Ru 助剂可降低 Co/SiO2 催化剂的还原温度, 从而提高其还原度. 光电子能谱和扩展 X 吸收射线精细结构研究表明, 即使 Ru 含量高达 9.96%, 在 Co/SiO2 催化剂焙烧过程中也未观察到 Ru 物种与 Co 物种作用形成的化合物. 还原后催化剂中 Ru 趋向于与 Co 物种紧密接触且分散在催化剂表面. H2 程序升温脱附结果表明, 随着 Ru 含量的增加, 位于反应温度附近的 H2 脱附峰面积增加, 即此时催化剂吸附 H2 能力提高, 因此反应活性单调增加, 但存在最佳 Ru 含量, 此时 C5+选择性最高.