Magnetic and electrical properties of amorphous Ge1−xCrx thin films grown by low temperature vapor deposition

Amorphous Ge_1−xCr_x thin films are deposited on (1 0 0)Si by using a thermal evaporator. Amorphous phase is obtained when Cr concentration is lower than 30.7 at%. The electrical resistivities are 1.89×10⁻³–0.96×10² Ω cm at 300 K, and decrease with Cr concentration. The Ge_1−xCr_x thin films are p-type. The hole concentrations are 5×10¹⁶–7×10²¹ cm⁻³ at 300 K, and increase with Cr concentration. Magnetizations are 7.60–1.57 emu/cm³ at 5 K in the applied field of 2 T. The magnetizations decrease with Cr concentration and temperature. Magnetization characteristics show that the Ge_1−xCr_x thin films are paramagnetic.     

Magnetic properties of nanocrystalline Co1−xZnxFe2O4 prepared by forced hydrolysis method

Nanocrystalline zinc-substituted cobalt ferrite powders, Co_1−xZn_xFe₂O₄ (x=0, 0.2, 0.4), were for the first time prepared by forced hydrolysis method. Magnetic and structural properties in these specimens were investigated. The average crystallite size is about 3.0 nm. When the zinc substitution increases from x=0 to x=0.4, at 4.2 K, the saturation magnetization increases from 72.1 to 99.7 emu/g and the coercive field decreases from 1.22 to 0.71 T. All samples are superparamagnetic at room temperature and ferrimagnetic at temperatures below the blocking temperature. The high value of the saturation magnetization and the very thin thickness of the disorder surface layer of all samples suggests that this forced hydrolysis method is suitable not only for preparing two metal element systems but also for three or more ones.     

Magnetic and transport properties in Sr1−xLaxFe1−xMnxO3

The magnetic and transport properties in the perovskite Sr_1−xLa_xFe_1−xMn_xO₃ have been explored. As x rises, the systemic ferromagnetism increases gradually and cluster-spin-glass state occurs in the low-temperature region. For 0.3?x?0.7, the ferromagnetic phase separation from the paramagnetic phase was observed from the results of electron-spin-resonance measurement. Although all samples show a semiconducting behavior, their transport properties are dominated by two different mechanisms, namely, the electronic transport of x?0.5 samples is realized by thermal activation but the variable-range hopping is applied in x?0.7 ones. The different transport mechanism can be understood from the Mn/Fe ions interaction.     

Structural and magnetic properties of SmCo7−xMox alloys

Phase structure and magnetic properties of the as-cast and as-milled/annealed SmCo_7−xMo_x (x=0, 0.1, 0.2, 0.3, 0.4) alloys have been systematically studied. It is found that all the as-cast series alloys are composed of the CaCu₅-type and Th₂Zn₁₇-type phases. Saturation magnetization of the samples decreases with the Mo content increasing. Intrinsic coercivities (_iH_c) of no more than 0.06 T are observed in these as-cast samples, due to their rather coarse grain microstructures with an average grain size of 50 μm. The as-milled/annealed SmCo_7−xMo_x powders crystallize in the disordered TbCu₇-type (1:7) structure with very fine nanograins, and a minor Co₃Mo phase appears in the samples with x=0.1-0.4. High _iH_c (?0.95 T) are achieved in these samples, with a maximum of 1.26 T located at x=0.2, which can be primarily attributed to strong pinning of the domain wall motion at the nanograin boundaries. The temperature coefficient (β) of the _iH_c is about −0.22%/°C in the temperature range of 25-400 °C for the as-milled/annealed samples.     

Microstructure characterization and magnetic behavior of NiAlxFe2−xO4 and Ni1−yMnyAl0.2Fe1.8O4 ferrites

NiAl_xFe_2−xO₄ and Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites were prepared by the conventional ceramic method and were characterized by X-ray diffraction, scanning electron microscopy, and magnetic measurements. The single spinel phase was confirmed for all prepared samples. A proper explanation of data is possible if the Al³⁺ ions are assumed to replace Fe³⁺ ions in the A and B sites simultaneously for NiAl_xFe_2−xO₄ ferrites, and if the Mn²⁺ ions are assumed to replace Ni²⁺ ions in the B sites for Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites. Microstructural factors play an important role in the magnetic behavior of Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites with large Mn²⁺ content.     

Magnetic behavior of the II-V-diluted magnetic semiconductor Cd1−xMnxSb

Polycrystalline samples of the II-V-diluted magnetic semiconductor Cd_1−xMn_xSb (x=0.05-0.20) were synthesized. Standard high temperature ceramic methods under an inert atmosphere were utilized for sample fabrication. Structural characterization was done using X-ray diffractometry (XRD), which indicated that a simple substitution of Mn for Cd is probably not occurring. Hysteresis, ac susceptibility, dc magnetization, and spontaneous magnetization measurements were performed for Cd_0.90Mn_0.10Sb. The hysteresis data indicated the presence of a ferromagnetic component. Ferromagnetism in the Cd_0.90Mn_0.10Sb system is likely due to two sources: Mn spins in small Mn-rich regions and a small amount of MnSb in a minority phase. Analysis of the spontaneous magnetization as a function of temperature for Cd_0.90Mn_0.10Sb yielded the value 0.172 for the critical exponent β. In MnSb, β was found to have the value 0.379, which is close to the theoretical value for 3D-Heisenberg systems. Thus, in Cd_0.90Mn_0.10Sb, the ferromagnetism is not of the 3D-Heisenberg type; rather, it is closer to 2D Ising behavior, indicating reduced effective dimensionality.     

Structural characterization and magnetization of Mg0.7Zn0.3SmxFe2−xO4 ferrites

Mg_0.7Zn_0.3Sm_xFe_2−xO₄ ferrites were prepared by the solid-state reaction method and were characterized by X-ray diffraction and magnetization measurements. A single spinel phase was obtained in the range 0.00?x?0.03$0.00?x?0.03$. The lattice parameter was found to increase at x=0.01$x=0.01$ and then decreases up to x=0.03$x=0.03$, which may indicate a distortion in the spinel lattice. The saturation magnetization was found to decrease with the increase in x up to 0.04, due to the replacement of the Fe³⁺ ions by the Sm³⁺ ions.     

Monodispersed nanocrystalline Co1–xZnxFe2O4 particles by forced hydrolysis: Synthesis and characterization

Zinc-substituted cobalt ferrites, Co_1–xZn_xFe₂O₄, were for the first time successfully prepared by forced hydrolysis method. The obtained materials are single phase, monodispersed nanocrystalline with an average grain size of about 3 nm. These materials are superparamagnetic at room temperature and ferrimagnetic at temperature lower than the blocking temperature. When the zinc substitution increases from x=0 to 0.4, at 4.2 K, the saturation magnetization increases from 72.1 to 99.7 emu/g. The high saturation magnetization of these samples suggests that this method is suitable for preparing high-quality nanocrystalline magnetic ferrites for practical applications.     

Li0.5Fe2.5−xMnxO4 ferrite sintered from microwave-induced combustion

Li_0.5Fe_2.5−xMn_xO₄ (0≦x≦1.0) powders with small and uniformly sized particles were successfully synthesized by microwave-induced combustion, using lithium nitrate, ferric nitrate, manganese nitrate and carbohydrazide as the starting materials. The process takes only a few minutes to obtain as-received Mn-substituted lithium ferrite powders. The resultant powders annealed at 650 ^°C for 2 h and were investigated by thermogravimeter/differential thermal analyzer (TG/DTA), X-ray diffractometer (XRD), transmission electron microscopy (TEM), vibrating sample magnetometer (VSM), and thermomagnetic analysis (TMA). The results revealed that the Mn content were strongly influenced the magnetic properties and Curie temperature of Mn-substituted lithium ferrite powder. As for sintered Li_0.5Fe_2.5−xMn_xO₄ specimens, substituting an appropriate amount of Mn for Fe in the Li_0.5Fe_2.5−xMn_xO₄ specimens markedly improved the complex permeability and loss tangent.     

Magnetic properties of electron-doped Y1−xCexMnO3 compounds

Cerium-doped Y_1−xCe_xMnO₃ compounds have been prepared in single-phase form for x=0 to 0.10. X-ray diffraction (XRD) patterns could be analyzed by using P6₃cm space group. Temperature variations of ac susceptibility and magnetization measurements show that these Ce-doped materials exhibit weak ferromagnetic transition. The observed ferromagnetic transition is attributed to the double exchange ferromagnetic interaction between Mn²⁺ and Mn³⁺ ions due to electron doping. The M–H loops exhibit hysteresis along with linear contribution and were analyzed based on bound magnetic polaron (BMP) model. Increase in saturation magnetization and decrease in BMP concentrations have been observed with increase in Ce doping.     

Structural and magnetic studies on mechanosynthesized BaFe12−xMnxO19

Barium hexaferrite powders with manganese substitution were prepared by mechanosynthesis. The structural and magnetic properties were characterized by X-ray diffractometer and vibration sample magnetometer, respectively. XRD patterns were refined by Rietveld method. Preferential site occupation of manganese ion was investigated by room temperature (RT) Mössbauer measurements. XRD results showed a single-phase barium hexaferrite with some residual hematite. Crystallite size was observed to decrease with substitution amount. Lower saturation magnetization and increased coercivity is observed in substituted samples. RT Mössbauer measurements showed that manganese ions preferentially occupy 12k, 4f₂, and 2a sites.     

Depth dependence of Néel wall pinning on amorphous CoxSi1−x films with diluted arrays of elliptical antidots

Diluted arrays of elliptical antidots have been fabricated by optical lithography, electron beam lithography and plasma etching on amorphous Co₇₄Si₂₆ magnetic films with a well-defined uniaxial anisotropy. The magnetic behavior of two identical antidot arrays but with different hole depth in comparison with film thickness has been studied by transverse magneto-optical Kerr effect. Significant differences appear in the coercivity depending on whether the magnetic film is completely perforated or not, indicating a much more effective domain wall pinning process when the depth of the holes is smaller than the magnetic film thickness.     

Fabrication and characterization of electrodeposited Co1−xCrx nanowires

Co_1−xCr_x   alloy nanowires with 0.01<x<0.93$0.01<x<0.93$ were fabricated by electrodeposition in a porous alumina membrane from an electrolyte containing Co and Cr ions. The composition, structure and magnetic properties of the nanowires have been characterized. Cobalt-rich nanowires were electrodeposited at a potential of −1.0 V relative to Ag/AgCl and chromium-rich nanowires were deposited beyond −3.5 V. The optimized processing conditions include hydrogen annealing to give hysteresis loops for the Co₈₀Cr₂₀ nanowires with coercivity of up to 200 mT and squareness of up to 0.95. Magnetization of the Co₈₀Cr₂₀ nanowire is 77 A m² kg⁻¹ and the energy product of the arrays is 35 kJ m⁻³.     

Permeability-frequency spectra of (Fe1−xcox)73.5Cu1Nb3Si13.5B9 nanocrystalline alloys under different magnetic fields

Under various amplitude of AC magnetic fields domain wall motion is the main mechanism in the magnetization process. This includes domain wall bulging and domain wall displacing. In this paper complex permeability-frequency spectra of (Fe_1−xCo_x)_73.5Cu₁Nb₃Si_13.5B₉ (x=0,0.5$x=0,0.5$) nanocrystalline alloys were measured as a function of the AC magnetic field, ranging from 0.001 to 0.04 Oe. Obvious changes have been found in complex permeability spectra for alloy x=0$x=0$ with the change of the amplitude of AC magnetic field, but variation of AC magnetic field has little effect on complex permeability spectra for alloy x=0.5$x=0.5$. This is attributed to the increased pinning field after substitution of Fe with Co in Fe_73.5Cu₁Nb₃Si_13.5B₉ nanaocrystalline alloy.     

Phase diagram of Fe1−xCox ultrathin film

Concentration-driven reorientation phase transitions in ultrathin magnetic films of FeCo alloy have been studied. It is established that, in addition to the easy-axis and easy-plane phases, a spatially inhomogeneous phase (domain structure), a canted phase, and also an “in-plane easy-axis” phase can exist in the system. The realization of the last phase is associated with the competition between the single-ion anisotropy and the magnetoelastic interaction. The critical values of Co concentration corresponding to the phase transitions are evaluated, the types of phase transitions are determined, and the phase diagrams are constructed.     

Effect of indium incorporation in Zn1−xCoxO thin films

In the present paper, the preliminary investigations of a series of ZnO thin films co-doped with indium and cobalt with an objective to elucidate the correlation, if any, between the carrier concentration and the induced room temperature ferromagnetism (RTFM), are presented. The single-phasic (Zn_99.5In_0.5)_1−xCo_xO thin films are deposited by spray pyrolysis. The substitution of Zn²⁺ by Co²⁺ has been established by optical transmission analysis of these films. The films are ferromagnetic at room temperature; and the magnetization has higher value for indium and cobalt co-doped thin film as compared with Zn0₉₀Co_0.1O thin film (having no indium).     

Soft magnetic properties and giant magneto-impedance effect of Fe73.5−xCrxSi13.5B9Nb3Au1 (x=1–5) alloys

In this paper, the effect of microstructural and surface morphological developments on the soft magnetic properties and giant magneto-impedance (GMI) effect of Fe_73.5−xCr_xSi_13.5B₉Nb₃Au₁ (x=1, 2, 3, 4, 5) alloys was investigated. It was found that the Cr addition causes slight decrease in the mean grain size of α-Fe(Si) grains. AFM results indicated a large variation of surface morphology of density and size of protrusions along the ribbon plane due to structural changes caused by thermal treatments with increasing Cr content. Ultrasoft magnetic properties such as the increase of magnetic permeability and the decrease of coercivity were observed in the samples annealed at 540 °C for 30 min. Accordingly, the GMI effect was also observed in the annealed samples.     

Hard magnetic properties of ErCo7−xCux [0.3⩽x⩽1] system

We report the observation of excellent hard magnetic properties on purely single phase ErCo_7−xCu_x compounds with x=0.3, 0.5, 0.8 and 1. Cu substitution leads to a decrease in the saturation magnetization, but enhances the uniaxial anisotropy in this system. The large anisotropy field (∼100 kOe) is attributed to the Er and the Co sublattices. Domain wall pinning effect seems to play a crucial role in determining the temperature and field dependences of magnetization in these compounds. The hard magnetic properties obtained at room temperature (RT) are comparable to the best results obtained in other RCo₇ based materials.     

Magnetoresistive properties of Zn1−xCoxFe2O4 ferrites

The magnetic and magnetoresistive properties of spinel-type Zn_1−xCo_xFe₂O₄ (x=0, 0.2 and 0.4) ferrites are extensively investigated in this study. A large negative magnetoresistance (MR) effect is observed in Zn_1−xCo_xFe₂O₄ ferrites of spinel structure. These materials are either ferrimagnetic or paramagnetic at room temperature, and show a spin-(cluster) glass transition at low temperatures, depending on the chemical compositions. The MR curves as a function of magnetic fields, MR(H), are parabolic at all temperatures for paramagnetic polycrystalline ZnFe₂O₄. The MR for ZnFe₂O₄ at 110 K in the presence of 9 T applied magnetic field is 30%. On the other hand, MR(H) are linear for x=0.2 and 0.4 ferrimagnetic Zn_1−xCo_xFe₂O₄ samples up to 9 T. The MR effect is independent of the sintering temperatures, and can be explained with the help of the spin-dependent scattering and the Yafet–Kittel angle of Zn_1−xCo_xFe₂O₄ mixed ferrites.     

Magnetic domain structure in Fe78.8−xCoxCu0.6Nb2.6Si9B9 nanocrystalline alloys studied by Lorentz microscopy

The magnetic domain structures of Fe_78.8−xCo_xCu_0.6Nb_2.6Si₉B₉ (x=0, 20, 40, 60) alloys are investigated by Lorentz microscopy coupled with the focused ion beam method. The specimen prepared using the FIB method is found to have a considerably more uniform thickness compared to that prepared using the ion-milling method. In Fe_38.8Co₄₀Cu_0.6Nb_2.6Si₉B₉ and Fe_18.8Co₆₀Cu_0.6Nb_2.6Si₉B₉ alloys, 180° domain walls extending in the direction of the induced magnetic anisotropy are observed. Analysis with Lorentz microscopy reveals that the width of the magnetic domains decreases with an increase in the cobalt content or the induced magnetic anisotropy K_u, that is, the domain width d is proportional to the induced magnetic anisotropy (K_u)^−1/4. On the other hand, in the in situ Lorentz microscopy observation as a function of temperature, magnetic ripple structures are found to appear in a localized area due to the fluctuation of magnetization vectors from 423 K. It is observed that the induced magnetic anisotropy caused by the applied magnetic field at 803 K is not suppressed by the magnetic ripple structures observed at 423–443 K.