Doping and temperature dependence of inversion symmetry breaking in La2−xSrxCuO4

The doping dependence of the Raman spectra of high quality La_2−xSr_xCu^16,18O₄ polycrystalline compounds has been investigated at low temperatures. It is shown that symmetry forbidden bands peaked at ∼150 cm⁻¹, ∼280 cm⁻¹, and ∼370 cm⁻¹ are activated in the (xx/yy) polarization Raman spectra due to the local breaking of the inversion symmetry mainly at low temperatures and for doping concentrations for which the compound is superconducting. The apparent A₁-character of the activated modes in the symmetry reduced phase indicates a reduction from the D_2h to C_2v or D₂ crystal symmetries, which associates the observed modes to specific IR-active phonons with eigenvectors mainly along the c-axis. The temperature and doping dependence of this inversion symmetry breaking and the superconducting transition temperature are very similar, though the symmetry reduction occurs at significantly higher temperatures.     

The effect of duration of diffusion on Ag diffusion coefficients in YBa2Cu3O7

The Ag diffusion in superconducting YBa₂Cu₃O₇ (YBaCuO) ceramic has been studied over the duration of the diffusion range 5-24 h in the temperature range 700-850 °C by the energy-dispersive X-ray fluorescence (EDXRF) technique. For the excitation of silver atoms, an annular Am-241 radioisotope source (50 mCi) emitting 59.543 keV photons was used. The temperature dependences of silver diffusion coefficients in grains (D₁) and over the grain boundaries in the range 700-850 °C (D₂) are described by the relations D₁=1.4×10⁻² exp[−(1.18±0.10)/kT] and D₂=3.1×10⁻⁴ exp[−(0.87±0.10)/kT].     

Growth temperature dependence of the hysteretic behavior of Ni0.5Zn0.5Fe2O4 thin films

Herein, a discussion of the effect of deposition temperature on the magnetic behavior of Ni_0.5Zn_0.5Fe₂O₄ thin films. The thin films were grown by r.f. sputtering technique on (1 0 0) MgO single-crystal substrates at deposition temperatures ranging between 400 and 800 °C. The grain boundary microstructure was analyzed via atomic force microscopy (AFM). AFM images show that grain size (φ∼70-112 nm) increases with increasing deposition temperature, according to a diffusion growth model. From magneto-optical Kerr effect (MOKE) measurements at room temperature, coercive fields, H_c, between 37and 131 Oe were measured. The coercive field, H_c, as a function of grain size, reaches a maximum value of 131 Oe for φ ∼93 nm, while the relative saturation magnetization exhibits a minimum value at this grain size. The behaviors observed were interpreted as the existence of a critical size for the transition from single- to multi-domain regime. The saturation magnetization (21 emu/g<M_s<60 emu/g) was employed to quantify the critical magnetic intergranular correlation length (L_c≈166 nm), where a single-grain to coupled-grain behavior transition occurs. Experimental hysteresis loops were fitted by the Jiles-Atherton model (JAM). The value of the k-parameter of the JAM fitted by means of this model (k/μ_o∼50 A m²) was correlated to the domain size from the behavior of k, we observed a maximum in the density of defects for the sample with φ∼93 nm.     

Structure, magnetic and optical properties of polycrystalline Co-doped TiO2 films

Co-doped TiO₂ films were fabricated under different conditions using reactive facing-target magnetron sputtering. Co doping improves the transformation of TiO₂ from anatase phase to rutile phase. The chemical valence of doped Co in the films is +2. All the films are ferromagnetic with a Curie temperature above 340 K. The average room-temperature moment per Co of the Co-doped TiO₂ films fabricated at 1.86 Pa decreases from 0.74 μ_B at x=0.03 to 0.02 μ_B at x=0.312, and decreases from 0.54 to 0.04 μ_B as x increases from 0.026 to 0.169 for the Co-doped TiO₂ films fabricated at 0.27 Pa. The ferromagnetism originates from the oxygen vacancies created by Co²⁺ dopants at Ti⁴⁺ cations. The optical band gaps value (E_g) of the Co-doped TiO₂ films fabricated at 1.86 Pa decreases linearly from 3.35 to 2.62 eV with the increasing x from 0 to 0.312. For the Co-doped TiO₂ films fabricated at 1.86 Pa, the E_g decreases linearly from 3.26 to 2.53 eV with increasing x from 0 to 0.350.     

Temperature-dependent photoluminescence in La2/3Ca1/3MnO3

Visible photoluminescence and its temperature dependence of La_2/3Ca_1/3MnO₃ in the temperature range 138-293 K were measured. It was observed that the main broad band centered at ∼1.77 eV with the shoulders at ∼1.57 and ∼1.90 eV existed in the entire temperature range. It can be well fitted by three Gaussian curves B₁, B₂ and B₃ centered at ∼1.52, ∼1.75 and ∼1.92 eV, respectively. The intensities of the peak B₁ and B₂ vary as temperature increases. In the entire temperature range, the intensity of B₁ increases with increasing temperature, whereas that of B₂ decreases. The photoluminescence mechanisms for La_2/3Ca_1/3MnO₃ are presented based on the electronic structures formed by the interactions among spin, charge and lattice, in which B₁ was identified with the charge transfer excitation of an electron from the lower Jahn-Teller split e_g level of a Mn³⁺ ion to the e_g level of an adjacent Mn⁴⁺ ion, B₂ is assigned to the transition between the spin up and spin down e_g bands separated by Hund's coupling energy E_J and B₃ is attributed to the transition, determined by the crystal field energy E_C, between a t_2g core electron of Mn³⁺ to the spin up e_g bands of Mn⁴⁺ by a dipole allowed charge transfer process.     

Refractive index, oscillator parameters and temperature-tuned energy band gap of Tl4In3GaS8-layered single crystals

Transmission and reflection measurements in the wavelength region 450-1100 nm were carried out on Tl₄In₃GaS₈-layered single crystals. The analysis of the room temperature absorption data revealed the presence of both optical indirect and direct transitions with band gap energies of 2.32 and 2.52 eV, respectively. The rate of change of the indirect band gap with temperature dE_gi/dT=-6.0×10⁻⁴ eV/K was determined from transmission measurements in the temperature range of 10-300 K. The absolute zero value of the band gap energy was obtained as E_gi(0)=2.44 eV. The dispersion of the refractive index is discussed in terms of the Wemple-DiDomenico single-effective-oscillator model. The refractive index dispersion parameters: oscillator energy, dispersion energy, oscillator strength and zero-frequency refractive index were found to be 4.87 eV, 26.77 eV, 8.48×10¹³ m⁻² and 2.55, respectively.     

Superconductivity of powder-in-tube Sr0.6K0.4Fe2As2 wires

Nb-sheathed Sr_0.6K_0.4Fe₂As₂ superconducting wires have been fabricated using the powder-in-tube (PIT) method for the first time and the superconducting properties of the wires have been investigated. The transition temperature (T_c) of the Sr_0.6K_0.4Fe₂As₂ wires is confirmed to be as high as 35.3 K. Most importantly, Sr_0.6K_0.4Fe₂As₂ wires exhibit a very weak J_c-field dependence behavior even the temperature is very close to T_c. The upper critical field H_c2(0) value can exceed 140 T, surpassing those of MgB₂ and all the low temperature superconductors. Such high H_c2 and superior J_c-field performance make the 122 phase SrKFeAs wire conductors a powerful competitor potentially useful in very high field applications.     

The size and strain effects on the Raman spectra of Ce1−xNdxO2−δ (0≤x≤0.25) nanopowders

Ultrafine Ce_1−xNd_xO_2−δ (x=0-0.25) powders were synthesized by self-propagating room temperature synthesis. Raman spectra were measured at room temperature in the 300-700 cm⁻¹ spectral range. The shift and asymmetric broadening of the Raman F_2g mode at about 454 cm⁻¹ in pure and doped ceria samples could be explained with combined size and inhomogenous strain effects. Increased concentration of O²⁻ vacancies with doping is followed by an appearance of new Raman feature at about 545 cm⁻¹.     

Synthesis, microstructure and photoluminescence of Eu/Tb activated Y2SiO5 nanophosphors by new silicate sources

Y_2−xTb_xSiO₅ and Y_2−xEu_xSiO₅ nanophosphors with seven different kinds of silicate sources were synthesized by sol-gel method. The structures have been investigated to be composed of nanometer-size grains of 30-60 nm through X-ray diffraction (XRD) and scanning electron microscopy (SEM) was used to compare the different morphology of patterns from seven different silicon sources. The photoluminescence of Y_2−xTb_xSiO₅ was investigated as a function of silicate sources and the results revealed that these nanometer materials showed the characteristic emission ⁵D₄ → ⁷F_J (J = 6, 5, 4, 3) of Tb ions. The characteristic emission ⁵D₀ → ⁷F_J (J = 1, 2, 4) of Eu ions was also found in the materials of Y_2−xEu_xSiO₅.     

High-resolution photoemission study of FeSr2YCu2O7+δ

We have performed high-resolution photoemission spectroscopy (PES) on FeSr₂YCu₂O_7+δ, of which superconductivity of T_c=49 K was recently reported. We clearly observed opening of a d-wave-like superconducting gap and estimated the maximum gap value (Δ_max) to be 10 meV at 15 K. This gap value gives 2Δ_max/k_BT_c∼5, suggesting a strong-coupling nature of superconductivity in FeSr₂YCu₂O_7+δ. Comparative PES study with superconducting and insulating samples shows that the valence band is rigidly shifted as a function of doping without evolution of additional states within the insulating gap.     

Ferromagnetism at 300 K in spin-coated films of Co doped anatase and rutile-TiO2

Thin films of Ti_1−xCo_xO₂ (x=0 and 0.03) have been prepared on sapphire substrates by spin-on technique starting from metalorganic precursors. When heat treated in air at 550 and 700 °C, respectively, these films present pure anatase and rutile structures as shown both by X-ray diffraction and Raman spectroscopy. Optical absorption indicate a high degree of transparency in the visible region. Such films show a very small magnetic moment at 300 K. However, when the anatase and the rutile films are annealed in a vacuum of 1×10⁻⁵ Torr at 500 and 600 °C, respectively, the magnetic moment, at 300 K, is strongly enhanced reaching 0.36μ_B/Co for the anatase sample and 0.68μ_B/Co for the rutile one. The ferromagnetic Curie temperature of these samples is above 350 K.     

On the high-resistivity contacts to YBa2Cu3O7 thin films, electrical behavior in the regime of high temperatures and high-bias voltages

We prepared in-situ Au contacts on high-quality epitaxial YBa₂Cu₃O₇ (YBCO) films. Very high specific contact resistivity values up to ∼10⁻² Ω cm² at 4.2 K were obtained on 12×5 μm² contact areas. This resistivity value decreased by two orders of magnitude as the temperature was raised to room temperature. In the temperature range T<200 K, the contacts showed non-ohmic behavior suggesting the presence of a well-defined insulating native Y-Ba-Cu-O barrier between the two electrodes. The electrical transport in this barrier layer was analyzed in the limit of high temperatures and high voltages to follow Mott's variable-range hopping conduction mechanism with physically reasonable parameters describing the localized states in the barrier. The high-resistivity contacts were tested successfully in quasiparticles injection experiments where the critical current I_c of the YBCO microbridge could be strongly suppressed on injection of an additional current through the contact into the superconducting channel.     

Structure and superconductivity of Mg1−xPbxB2

A series of polycrystalline samples of Mg_1−xPb_xB₂ (0≤x≤0.10) were prepared by a solid state reaction method and their structure, superconducting transition temperature and transport properties were investigated by means of X-ray diffraction (XRD) and resistivity measurements. Mg_1−xPb_xB₂ compounds were shown to adopt an isostructural AlB2-type hexagonal structure in a relatively small range of lead concentration, x≤0.01. The crystalline lattice constants were evaluated and were found to exhibit slight length compression as x increases. The superconducting transition temperature (T_c) steadily decreases with Pb doping. It is suggested that the mechanism of superconductivity reduction by lead doping can be attributed to the chemical pressure effect.     

Electromechanical properties and dielectric behavior of (Bi1/2Na1/2)(1−1.5x)BixTiO3 lead-free piezoelectric ceramics

Bismuth doped bismuth sodium titanate ceramics [(Bi_1/2Na_1/2)_(1−1.5x)Bi_xTiO₃, x=0 to 0.06] were prepared, and the resulting effects on the microstructure and dielectric properties were examined. All of the Bi-doped ceramics exhibited a single phase of perovskite structure with rhombohedral symmetry. The poling leakage current was significantly reduced by the doping of Bi, facilitating the poling process of the ceramics. The doping with Bi enhances the piezoelectric properties and increases the dielectric constant and the dielectric loss of the ceramics. At 2 mol% Bi-doping level, the ceramics exhibit a large remanent polarization of 47 μC/cm² and a relatively low coercive field of 71 kV/cm, while their d₃₃ and k_p reach a maximum value of 95 pC/N and 21%, respectively.     

Effect of heating rates on microstructure and superconducting properties of pure MgB2

The influence of different heating rates, ranging from 5 to 30 K min⁻¹, on the microstructure and superconducting of the MgB₂ bulk was investigated. No obvious variation in the grain size was found for the samples heated from 5 K min⁻¹ to 20 K min⁻¹ except for the changes in morphologies. Moreover, the grain refinement was obtained under the heating rate of 30 K min⁻¹. The critical current density (J_c) suggested that the 5 K min⁻¹ sample had the best performance in high field. Here, the differential thermal analysis (DTA) was employed to analyze the kinetics of MgB₂ phase formation with the different heating rates. The results showed that the large amount of MgB₂ formed at low temperature, which lead to compact structures under the slow heating rate. The fast heating rate would promote the evaporation of Mg at high temperature, which was considered to generate the vacancy and impurities in the sample.     

Magnetic properties and microstructure study of high coercivity Au/FePt/Au trilayer thin films

High-coercivity Au(60 nm)/FePt(δ nm)/Au(60 nm) trilayer samples were prepared by sputtering at room temperature, followed by post annealing at different temperatures. For the sample with δ=60 nm, L1₀ ordering transformation occurs at 500 °C. Coercivity (H_c) is increased with the annealing temperature in the studied range 400–800 °C. The H_c value of the trilayer films is also varied with thickness of FePt intermediate layer (δ), from 27 kOe for δ=60 nm to a maximum value of 33.5 kOe for δ=20 nm. X-ray diffraction data indicate that the diffusion of Au atoms into the FePt L1₀ lattice is negligible even after a high-temperature (800 °C) annealing process. Furthermore, ordering parameter is almost unchanged as δ is reduced from 60 to 15 nm. Transmission electron microscope (TEM) photos indicate that small FePt Ll₀ particles are dispersed amid the large-grained Au. We believe that the high coercivity of the trilayer sample is attributed to the small and uniform grain sizes of the highly ordered FePt particles which have perfect phase separation with Au matrix.     

Switching phenomenon and optical properties of Se85Te10Bi5 films

Se₈₅Te₁₀Bi₅ films of different thicknesses ranging from 126 to 512 nm have been prepared. Energy-dispersive X-ray (EDX) spectroscopy technique showed that films are nearly stoichiometric. X-ray diffraction (XRD) measurements have showed that the Se₈₅Te₁₀Bi₅ films were amorphous. Electrical conduction activation energy (ΔE_σ) for the obtained films is found to be 0.662 eV independent of thickness in the investigated range. Investigation of the current voltage (I-V) characteristics in amorphous Se₈₅Te₁₀Bi₅ films reveals that it is typical for a memory switch. The switching voltage V_th increases with the increase of the thickness and decreases exponentially with temperature in the range from 298 to 383 K. The switching voltage activation energy (ε) calculated from the temperature dependence of V_th is found to be 0.325 eV. The switching phenomenon in amorphous Se₈₅Te₁₀Bi₅ films is explained according to an electrothermal model for the switching process. The optical constants, the refractive index (n) and the absorption index (k) have been determined from transmittance (T) and reflectance (R) of Se₈₅Te₁₀Bi₅ films. Allowed non-direct transitions with an optical energy gap (E_g^opt) of 1.33 eV have been obtained. ΔE_σ is almost half the obtained value of E_g^opt, which suggested band to band conduction as indicated by Davis and Mott.     

Structural and optical properties of a-Si1−xCx:H films synthesized by dc magnetron sputtering technique

Hydrogenated amorphous SiC films (a-Si_1−xC_x:H) were prepared by dc magnetron sputtering technique on p-type Si(1 0 0) and corning 9075 substrates at low temperature, by using 32 sprigs of silicon carbide (6H-SiC). The deposited a-Si_1−xC_x:H film was realized under a mixture of argon and hydrogen gases. The a-Si_1−xC_x:H films have been investigated by scanning electronic microscopy equipped with an EDS system (SEM-EDS), X-ray diffraction (XRD), secondary ions mass spectrometry (SIMS), Fourier transform infrared spectroscopy (FTIR), UV-vis-IR spectrophotometry, and photoluminescence (PL). XRD results showed that the deposited film was amorphous with a structure as a-Si_0.80C_0.20:H corresponding to 20 at.% carbon. The photoluminescence response of the samples was observed in the visible range at room temperature with two peaks centred at 463 nm (2.68 eV) and 542 nm (2.29 eV). In addition, the dependence of photoluminescence behaviour on film thickness for a certain carbon composition in hydrogenated amorphous SiC films (a-Si_1−xC_x:H) has been investigated.     

A variable temperature EPR study of the manganites (La1/3Sm2/3)2/3SrxBa0.33−xMnO3 (x=0.0, 0.1, 0.2, 0.33): Small polaron hopping conductivity and Griffiths phase

Four manganite samples of the series, (La_1/3Sm_2/3)_2/3Sr_xBa_0.33−xMnO₃, with x=0.0, 0.1, 0.2 and 0.33, were investigated by X-band (∼9.5 GHz) electron paramagnetic resonance (EPR) in the temperature range 4-300 K. The temperature dependences of EPR lines and linewidths of the samples with x=0.0, 0.1 and 0.2, containing Ba²⁺ ions, exhibit similar behavior, all characterized by the transition temperatures (T_C) to ferromagnetic states in the 110-150 K range. However, the sample with x=0.33 (containing no Ba²⁺ ions) is characterized by a much higher T_C=205 K. This is due to significant structural changes effected by the substitution of Ba²⁺ ions by Sr²⁺ ions. There is an evidence of exchange narrowing of EPR lines near T_min, where the linewidth exhibits the minimum. Further, a correlation between the temperature dependence of the EPR linewidth and conductivity is observed in all samples, ascribed to the influence of small-polaron hopping conductivity in the paramagnetic state. The peak-to-peak EPR linewidth was fitted to ΔB_pp(T)=ΔB_pp,min+A/Texp(−E_a/k_BT), with E_a=0.09 eV for x=0.0, 0.1 and 0.2 and E_a=0.25 eV for x=0.33. From the published resistivity data, fitted here to σ(T)∝1/T exp(−E_σ/k_BT), the value of E_σ, the activation energy, was found to be E_σ=0.18 eV for samples with x=0.0, 0.1 and 0.2 and E_σ=0.25 eV for the sample with x=0.33. The differences in the values of E_a and E_σ in the samples with x= 0.0, 0.1and 0.2 and x=0.33 has been ascribed to the differences in the flip-flop and spin-hopping rates. The presence of Griffiths phase for the samples with x=0.1 and 0.2 is indicated; it is characterized by coexistence of ferromagnetic nanostructures (ferrons) and paramagnetic phase, attributed to electronic phase separation.     

Superparamagnetic behavior of La0.67Sr0.33MnO3 nanoparticles prepared via sol-gel method

Magnetic nanoparticles of La_0.67Sr_0.33MnO₃ (LSMO) manganite were prepared by sol-gel method. Phase formation and crystal structure of the synthesized powder were examined by the X-ray diffraction (XRD) using the Rietveld analysis. The mean particle size was determined by the transmission electron microscopy (TEM). Infrared transmission spectroscopy revealed that stretching and bending modes are influenced by calcinations temperature. The temperature dependence of the ac magnetic susceptibility was measured at different frequencies and ac magnetic fields in the selected ranges of 40-1000 Hz and 80-800 A/m, respectively. The temperature dependence of ac susceptibility shows a characteristic maxima corresponding to the blocking temperature near room temperature. The frequency dependence of the blocking temperature is well described by the Vogel-Fulcher law. By fitting the experimental data with this law, the relaxation time τ₀=1.7×10⁻¹² s, characteristic temperature T₀=262±3 K, anisotropy energy E_a/k=684±15 K and effective magnetic anisotropy constant k_eff=2.25×10⁴ erg/cm³ have been obtained. dc Magnetization measurement versus magnetic field shows that some of LSMO nanoparticles are blocked at 293 K. The role of magnetic interparticle interactions on the magnetic behavior is also investigated.