沉淀剂种类对水煤气变换Au/Fe2O3催化剂结构和催化性能的影响

 采用7种沉淀剂(K2CO3, Na2CO3, NH4OH, (NH4)2CO3, NaOH, KOH和尿素)通过共沉淀法制备了低温水煤气变换(WGS) Au/Fe2O3催化剂,考察了沉淀剂种类对其催化性能的影响. 通过N2吸附, X射线荧光光谱、 X射线衍射、 H2程序升温还原和CO程序升温脱附等表征手段,探讨了不同沉淀剂影响Au/Fe2O3催化剂WGS性能的原因. 结果表明,采用K2CO3和Na2CO3制备的催化剂样品在200 ℃以上具有较好的活性和稳定性,其中K2CO3是最佳沉淀剂. 而采用NH4OH和(NH4)2CO3制备的样品的催化活性相对较低,在200 ℃达到峰值. 由其它3种沉淀剂制备的样品的催化活性都较差, CO转化率最高只有35%. 沉淀剂种类不仅明显地影响金离子和铁离子的共沉淀,而且会明显地影响共沉淀物在后续焙烧过程中的结晶行为. 前者将影响金的负载量,后者则影响金粒子的分散度以及氧化铁载体的还原性质和对CO的吸脱附性能. Au/Fe2O3催化剂的低温高活性及其稳定性归因于高度分散的金粒子及其与易被还原的氧化铁载体间的协同作用. 催化剂中金负载量增大、金粒子分散度提高以及氧化铁晶粒减小均有利于其催化性能的提高.     

不同沉淀剂制备的铁基催化剂对浆态床F-T合成反应的催化性能

 以FeSO4·xH2O为铁源,分别以Na2CO3和氨水为沉淀剂制备了目标组成相同的两种Fe-Cu-K-SiO2催化剂样品. 采用原子发射光谱、低温N2吸附、X射线衍射、X射线光电子能谱和Mssbauer谱等技术对催化剂进行了表征. 在n(H2)/n(CO)=0.67,WHSV=2000 h-1,p=1.5 MPa和θ=250 ℃的条件下,在带搅拌器的浆态床反应器中考察了催化剂对F-T合成反应的活性、选择性和稳定性. 结果表明,以氨水为沉淀剂的催化剂具有较大的比表面积,还原态催化剂体相中能产生较多的铁碳化物物种. 在600 h的运行实验中,两种催化剂样品均表现出良好的反应初活性,CO转化率超过80%,但氨水沉淀催化剂的稳定性明显高于Na2CO3沉淀催化剂,前者在650 h内的失活速率仅为0.01%/h. 两种催化剂样品均表现出较低的甲烷选择性和较高的重质烃选择性,在实验运行期间,CH4选择性均保持在3%左右,C5+的选择性则保持在84%左右.     

浸渍/共沉淀法对BaO改性单Pd催化剂净化甲醇汽油车尾气性能的影响(英文)

采用浸渍和共沉淀两种方法分别制备了Ba O改性的Pd/CeO2-ZrO2-La2O3-Al2O3催化剂。运用N2吸附-脱附,X射线衍射(XRD),H2程序升温还原(H2-TPR),NH3程序升温脱附(NH3-TPD),透射电子显微镜(TEM)和X射线光电子能谱(XPS)对催化剂进行表征,并考察其对甲醇,CO,C3H8和NO的催化性能。活性测试结果表明,Ba O的引入可明显改善Pd催化剂对甲醇,CO,C3H8和NO的催化活性,且浸渍法最佳,起燃温度(T50)分别降低了43,31,45和35℃。XRD,H2-TPR及XPS结果表明,浸渍法引入Ba O主要通过表面改性方式,强化Pd-Ce界面间的相互作用,改善催化剂的还原性能,进而提高催化剂的低温活性;而共沉淀法则是通过结构改性方式增加CeO2晶格缺陷,加速活性氧物种的流动,Ce3+浓度的增加是促使CO氧化活性显著提高的主要原因。     

改性沉积-沉淀法制备Au/Fe2O3水煤气变换反应催化剂

采用共沉淀法、沉积-沉淀法和改性沉积-沉淀法制备了Au/Fe2O3催化剂,运用N2吸附、X射线衍射、X射线光电子能谱和透射电镜等技术对其进行了表征,考察了制备方法对Au/Fe2O3催化剂水煤气变换反应催化活性的影响.结果表明,改性沉积-沉淀法制备的催化剂具有最好的催化活性,150℃时CO转化率达82.3%.该催化剂比表面积较大,金粒子尺寸(3~5nm)较小且分布均匀.载体氧化铁以无定形态和结晶态共存,金与载体间存在较强的相互作用,这对催化剂活性的提高起着重要作用.     

硫酸钠对Mn/SiO2催化剂结构及其甲烷氧化偶联反应性能的影响

 采用等体积浸渍法制备了Na2SO4改性的Mn/SiO2催化剂,考察了Mn-Na2SO4/SiO2催化剂中各组分对甲烷氧化偶联合成C2产物(C2H4+C2H6)的影响,并采用X射线衍射、 X射线光电子能谱、 Raman光谱和程序升温还原等手段表征了催化剂中的物相结构、表面组分价态与含量以及氧化还原性能. 结果表明,在Mn/SiO2催化剂中添加Na2SO4可使载体SiO2由无定形转变为α-方石英相,使催化剂表面的Mn物种由Mn3O4转变为Mn2O3, 从而大大提高了甲烷转化率和目标产物C2的选择性. 因此,推测Mn2O3物种在反应条件下构成了甲烷氧化偶联反应的活性中心.     

Al_2_O3·Na_2O·xH_2O/NaOH/Al(OH)_3催化剂催化木质素水蒸气气化制氢研究(英文)

考察了催化剂Al2O3.Na2O.xH2O/NaOH/Al(OH)3催化木质素水蒸气气化制氢及其影响因素。结果表明,木质素气化的产氢速率随Na2O/C比值的升高而升高;木质素在较低的温度下气化时,较高的水蒸气流速有利于抑制CO和CO2的生成。产氢速率随水蒸气流速的增大而增大。催化剂中的铝酸钠水合物受热分解产生的水可导致催化剂中的NaOH组分产生更多的Na+和OH-离子。更多的Na+和OH-离子可使木质素中C—H键的键能更显著的降低。木质素在473 K~973 K气化的氢转化程度可达134.94%,这表明催化剂Al2O3.Na2O.xH2O/NaOH/Al(OH)3对木质素低温水蒸气气化制氢具有较好的催化活性。     

制备条件对新型糠醛加氢催化剂性能的影响

采用共沉淀法制备CuO-ZnO-Al2O3-MnO2复合氧化物为活性组分体系的新型铜基催化剂,并评价其在糠醛选择性加氢制备糠醇过程中的活性,比较Na2CO3、NH4HCO3、H2C2O4三种沉淀剂制得催化剂的活性差异并通过TPR、XRD、ICP、BET等手段表征,结果表明:用Na2CO3作沉淀剂制得催化剂转化率最高.进一步对制备条件进行考察,发现采用Al(OH)3的添加形式和并流共沉淀法有利于提高催化剂的活性,而助剂Mg的添加能有效提高催化剂稳定性.     

Mn_xCo_(3-x)O_4复合氧化物及改性催化剂催化分解N_2O

用共沉淀法制备了一组不同组成的MnxCo3-xO4尖晶石型复合氧化物,表面负载碱金属助剂制备改性催化剂,用于催化分解N2O.用X射线衍射(XRD)、N2物理吸附(BET)、红外光谱(FTIR)、扫描电镜(SEM)、H2程序升温还原(H2-TPR)、X射线光电子能谱(XPS)等技术表征催化剂结构.考察了复合氧化物组成、碱金属助剂类型、钾前驱物等制备参数对催化剂结构和催化活性的影响.结果表明:添加助剂K、Cs降低了催化剂表面Co、Mn元素的电子结合能,弱化了Co—O和Mn—O键,有利于氧物种的脱除,提高了催化剂活性.优化出了活性较高的催化剂K/Mn0.4Co2.6O4(K2CO3),有氧无水、有氧有水气氛400℃连续反应50 h,N2O转化率分别保持100%和74.2%,催化剂稳定性较高.     

改性介孔 Al2O3 负载锰基催化剂的结构及其催化氧化与抗硫性能

 采用分步浸渍法分别制备了 LaCeZr 和 YCeZr 组合助剂改性的介孔 Al2O3 负载的 Mn 基系列氧化物催化剂, 用 X 射线衍射、氮气吸附-脱附、X 射线吸收精细结构、X 射线光电子能谱和程序升温还原等方法对催化剂进行了表征, 探讨了催化剂中 Mn 物种的存在形式及其还原性能, 并与样品催化 CO 和 C3H8 的氧化活性相关联. 结果表明, 样品中 Mn 物种主要以 Mn3O4 形式存在, 该物种在不同样品中与载体的作用强弱不同, 从而表现出不同的还原性能和催化活性. 助剂改性有效抑制了 Mn-Al 之间的相互作用, 提高了 Mn–O 键的活动度, 从而提高了催化剂的氧化活性. 相比于 YCeZr 助剂, LaCeZr 助剂改性更大程度上提高了 Mn 物种的还原性, 因而大大提高了催化剂的氧化性能. 650 oC 焙烧的 LaCeZr 组合助剂改性的介孔 Al2O3 负载的 Mn 氧化物催化剂, 在 0.035% SO2 存在的条件下对 CO 的氧化活性并未下降, 对 C3H8 的氧化活性下降幅度也较小, 表现出优越的抗硫性能和氧化性能.     

费托合成:SiO_2和Al_2O_3负载的Co_2C催化剂的表征和评价

采用CO碳化SiO2和Al3O4负载的Co(NO3)2的方法制备了SiO2和Al3O4负载的Co2C催化剂,采用N2物理吸附、X射线衍射和H2-程序升温还原技术对催化剂进行了表征,并用于催化费托合成反应中.结果显示,需要较长碳化时间才可合成负载的Co2C催化剂;所制催化剂表现出CO加氢生成高碳醇的催化性能,其原因可能在于催化剂表面存在的金属Co物种使CO解离,表面Co物种有利于CO插入,从而导致醇的生成,但体相Co2C则不具有催化活性.     

Effect of CO_2 on the structural variation of Na_2WO_4/Mn/SiO_2 catalyst for oxidative coupling of methane to ethylene

In this work,the influence of CO2 on the structural variation and catalytic performance of Na2WO4/Mn/Si O2 for oxidative coupling of methane to ethylene was investigated. The catalyst was prepared by impregnation method and characterized by XRD,Raman and XPS techniques. Appropriate amount of CO2 in the reactant gases enhanced the formation of surface tetrahedral Na2WO4 species and promoted the migration of O in MOx,Na,W from the catalyst bulk to surface,which were favorable for oxidative coupling of methane. When the molar ratio of CH4/O2/CO2 was 3/1/2,enriched surface tetrahedral Na2WO4 species and high surface concentration of O in MOx,Na,W were detected,and then high CH4 conversion of 33.1% and high C2H4 selectivity of 56.2% were obtained. With further increase of CO2 in the reagent gases,the content of active surface tetrahedral Na2WO4 species and surface concentration of O in MOx,Na,W decreased,while that of inactive species(Mn WO4 and Mn2O3) increased dramatically,leading to low CH4 conversion and low C2H4 selectivity. It could be speculated that Na2WO4 crystal was transformed into Mn WO4 crystal with excessive CO2 added under the reaction conditions. Pretreatment of Na2WO4/Mn/Si O2 catalyst by moderate amount of CO2 before OCM also promoted the formation of Na2WO4 species.     

Insights into the oxidation and decomposition of CO on Au/alpha-Fe2O3 and on alpha-Fe2O3 by coupled TG-FTIR

CO oxidation and decomposition behaviors over nanosized 3% Au/alpha-Fe2O3 catalyst and over the alpha-Fe2O3 support were studied in situ via thermogravimetry coupled to on-line FTIR spectroscopy (TG-FTIR), which was used to obtain temperature-programmed reduction (TPR) curves and evolved gas analysis. The catalyst was prepared by a sonication-assisted Au colloid based method and had a Au particle size in the range of 2-5 nm. Carburization studies of H 2-prereduced samples were also made in CO gas. According to gravimetry, for the 3% Au/alpha-Fe2O3 catalyst, there were three distinct stages of CO interaction with the Au catalyst but only two stages for the catalyst support. At low temperatures (相似文献   

富氧条件下Ag/Al2O3-Cu/Al2O3组合催化剂催化乙醇选择性还原NOx

 在富氧条件下,以乙醇为还原剂,考察了不同金属负载量的Ag/Al2O3和Cu/Al2O3催化剂选择性还原NOx的活性. 结果表明,4%Ag/Al2O3和10%Cu/Al2O3分别为各自体系中的最佳催化剂. 4%Ag/Al2O3具有很高的选择性催化还原NOx的活性,但同时会产生一定量的副产物CO. 10%Cu/Al2O3选择性催化还原NOx的活性不高,但却具有很好的消除CO的活性. 将4%Ag/Al2O3和10%Cu/Al2O3以不同方式组合,其评价结果表明,4%Ag/Al2O3-10%Cu/Al2O3组合催化剂具有与单纯4%Ag/Al2O3相似的NOx脱除活性,同时能够完全消除反应过程中产生的CO,并且能大大降低尾气中乙醇和乙醛的浓度.     

Rh/SiO_2催化剂上甲烷部分氧化制合成气的反应机理

采用原位Raman光谱技术,在原料气中的O2未完全耗尽的条件下,对CH4部分氧化制合成气反应的Rh/SiO2催化剂床层前部贵金属物种的化学态以及由CH4解离所生成的碳物种进行了表征.在此基础上采用脉冲反应和同位素示踪技术,比较了CH4的部分氧化及其与H2O和CO2的重整等反应对催化剂床层氧化区内CO和H2生成的相对贡献,并将实验结果与Ra-man光谱表征结果进行了关联.结果表明,在600°C下将还原后的4%Rh/SiO2催化剂切入CH4:O2:Ar=2:1:45原料气,催化剂床层前部未检测到铑氧化物的Raman谱峰,但可清晰检测到源于CH4解离的碳物种;在700°C和接触时间小于1ms的条件下,催化剂床层的氧化区内已有大量CO和H2生成,在相同的实验条件下,CH4与H2O或CO2重整反应对氧化区内合成气生成的贡献则很小;以CH4:16O2:H218O:He=2:1:2:95为原料气的同位素示踪实验结果表明,在原料气中16O2未完全耗尽的情况下,反应产物中C16O的含量占CO生成总量的92.3%,表明CO主要来自CH4的部分氧化反应.上述结果均表明,在O2存在下Rh/SiO2催化剂上CO和H2可以通过CH4直接解离和部分氧化机理生成.     

La2O3/MgO催化剂上的甲烷氧化偶联

研究了甲烷在La_2O_3/MgO催化剂上的氧化偶联。发现制备过等对催化剂的行为有显著影响。比较了催化剂的反应性能和体相结构,表明在MgO上存在着三种La_2O_3的状态:高分散La_2O_3是最活泼的;La(OH)_3不太活泼;而呈六方晶相的La_2O_3晶粒活性最低。在催化剂中加入Na_2CO_3和K_2CO_3可以改进催化剂的活性和选择性。还考察了反应条件如温度和空速的影响。     

273 K下Na2CO3-Na2SO4-Na2B4O7-H2O四元体系介稳相平衡的实验研究

采用等温蒸发法研究了四元体系Na2CO3-Na2SO4-Na2B4O7-H2O在273 K时的介稳相平衡及平衡液相的密度. 利用溶解度数据绘制了该四元体系273 K下的相图. 研究结果表明, 该四元体系有异成分复盐2Na2SO4·Na2CO3形成. 相图中有2个共饱点、5条单变量曲线和4个结晶相区. 4个结晶相区分别为盐Na2CO3·10H2O, Na2SO4·10H2O, Na2B4O7·10H2O和2Na2SO4·Na2CO3的结晶区. 复盐2Na2SO4·Na2CO3同时存在于包含Na2CO3-Na2SO4-H2O三元体系的其它四元体系或高元体系中. 在273 K介稳平衡相图中, 碳酸钠以Na2CO3·10H2O形式析出; 硫酸钠以Na2SO4·10H2O的形式析出; 硼酸钠的完整分子式为Na2B4O5(OH)4·8H2O. Na2CO3对Na2B4O7有盐析作用.     

制备方法及焙烧温度对Co3O4/CeO2催化剂上CO低温氧化反应的影响

 分别采用沉淀氧化法、均匀沉淀法及络合燃烧法制备了Co3O4/CeO2复合氧化物催化剂,并在干燥及湿气条件下进行了CO氧化反应. 结果表明,采用沉淀氧化法经538 K焙烧制得的Co3O4/CeO2催化剂具有优异的CO低温氧化活性和较高的抗湿性能. 在196 K条件下,该催化剂上CO氧化的转化率为99%, 并且可连续保持400 min以上; 当温度上升到298 K时,经过 2400 min反应后, CO的转化率仍可达到94%; 当反应气中含3.1%湿气,温度为383 K时,经过2400 min反应后, CO的转化率仍保持在79%. 实验表明, Co3O4/CeO2催化剂的制备方法及焙烧温度对Co3O4与CeO2之间的相互作用有显著的影响,进而影响催化剂催化CO低温氧化的活性.     

催化热解生物质制取富氢气体的研究

在实验室自制的固定床反应器上, 考察了秸秆和锯屑的热解行为, 研究了热解产物分布特别是富氢气体的体积分数和产率, 着重研究了（5种金属氧化物和2种碳酸盐催化剂）的催化效果。结果表明,温度从500 ℃提高到850 ℃, 秸秆和锯屑的热解气产率分别从29.0%提高到40.6%, 35.0％提高到46.5%, 而对应的富氢气体的体积分数分别从41.2％提高到48.2%, 40.6％提高到47.0%；在5种金属氧化物中，Cr2O3显示了最好的催化效果，在750 ℃时对应的热解气产率与不使用催化剂相比提高了10％，富氢气体的体积分数提高了13％；催化剂（CaCO3和Na2CO3）占生物质的质量分数对热解气和富氢气体产率有明显的影响，当质量分数从0增加到30％时， 热解气和富氢气体产率增加较明显，而后其值的增加可以忽略， 因此推荐使用的催化剂质量分数为30％。     

CO2选择性氧化甲烷制C2烃催化剂La2O3/ZnO的氧化还原和CO2吸附性能

Ｌａ２Ｏ３／ＺｎＯ催化剂体系在以二氧化碳作为氧化剂的甲烷氧化偶联反应中具有很高的Ｃ２烃选择性和稳定性．采用ＣＯ２－ＴＰＤ－ＭＳ和ＴＰＲ技术考察了Ｌａ２Ｏ３／ＺｎＯ对ＣＯ２的吸附性质及其氧化还原行为．结果表明：（１）Ｌａ２Ｏ３／ＺｎＯ催化剂体系存在着强、弱两种碱中心，其中弱碱中心数量随样品中Ｌａ２Ｏ３含量增加而减少，强碱中心强度随样品中Ｌａ２Ｏ３含量增加而增强．（２）由于组分相互作用，高温下，Ｌａ２Ｏ３／ＺｎＯ易产生晶格氧空位，使之对ＣＯ２的吸附增强，吸附后的ＣＯ２与晶格氧作用形成立方晶型Ｌａ２Ｏ２ＣＯ３．（３）Ｌａ２Ｏ３／ＺｎＯ表面的Ｌａ３＋和Ｚｎ２＋可以部分被还原，由于组分间的相互作用，使得二者的还原都较单一组分存在时更难．（４）Ｈ２－ＣＯ２－Ｈ２氧化还原循环实验表明，Ｌａ２Ｏ３／ＺｎＯ表面被部分还原后，ＣＯ２可以将部分被还原的表面再氧化．在此基础上对Ｌａ２Ｏ３／ＺｎＯ催化剂上甲烷与ＣＯ２转化为Ｃ２烃的机制也进行了讨论．     

有氧气氛中碱金属改性CuAl复合氧化物催化分解N2O的活性

合成了Cu/Al原子比分别为2.0、3.1、4.1的CuAl类水滑石样品,焙烧得到CuAl复合氧化物。在Cu/Al原子比为3.1的CuAl氧化物表面浸渍碱金属盐溶液,制备改性CuAl复合氧化物,用AES、XRD、FT-IR、BET、H₂-TPR、XPS等技术对催化剂进行了结构表征,考察了CuAl复合氧化物组成、碱金属助剂类型和K的前驱物对改性催化剂在有氧气氛中催化分解N₂O活性的影响。结果表明,Na、K、Cs改性CuAl复合氧化物均提高了催化剂活性,但K助剂的增强效应最显著;钾的不同前驱物改性CuAl复合氧化物的催化活性有显著差异,加入碳酸钾、草酸钾提高了催化剂的活性,而加入醋酸钾、硝酸钾反而降低了催化剂活性。优化出的K改性CuAl复合氧化物催化剂在含氧含水气氛的N₂O分解反应中表现出了较高的活性。