The influences of supersaturation on LPE growth of GaN single crystals using the Na flux method

The dependency of LPE growth rate and dislocation density on supersaturation in the growth of GaN single crystals in the Na flux was investigated. When the growth rate was low during the growth of GaN at a small value of supersaturation, the dislocation density was much lower compared with that of a substrate grown by the Metal Organic Chemical Vapor Deposition method (MOCVD). In contrast, when the growth rate of GaN was high at a large value of supersaturation, the crystal was hopper including a large number of dislocations. The relationship between the growth conditions and the crystal color in GaN single crystals grown in Na flux was also investigated. When at 800 °C the nitrogen concentration in Na–Ga melt was low, the grown crystals were always tinted black. When the nitrogen concentration at 850 °C was high, transparent crystals could be grown.     

Ammonothermal epitaxy of wurtzite GaN using an NH4I mineralizer

Purely wurtzite phase needle crystals and epitaxial layers of GaN were grown by the ammonothermal method using an NH₄I mineralizer. The inclusion of zincblende phase GaN was effectively eliminated by increasing the growth temperature higher than 500 °C. Accordingly, an approximately 20-μm-thick GaN epitaxial layer was achieved on the Ga-polar face of a c-plane GaN seed wafer at 520 °C. Although the characteristic deep state emission band dominated the room temperature photoluminescence spectrum, the near-band-edge emission of GaN was observed for both the needle crystals and the epitaxial layers. These results encourage one to grow better quality GaN crystals at a high growth rate under high-temperature growth conditions.     

Evidence of free carrier concentration gradient along the c-axis for undoped GaN single crystals

Results of measurements of infrared reflectivity and micro-Raman scattering on the undoped GaN high pressure grown single crystals are reported. These crystals have usually a high electron concentration due to unintentional doping by oxygen. We show, by the shift of the plasma edge (infrared reflectivity measurements), that the free electron concentration is always higher on the (0 0 0  )N face of the GaN single crystal than on the (0 0 0 1)Ga face. In order to determine the profile of the free carrier concentration, we performed transverse micro-Raman scattering measurements along the (0 0 0 1) c-axis of the crystal with spatial resolution of 1 μm. Micro-Raman experiments give a quantitative information on the free carrier concentration via the longitudinal optical phonon–plasmon (LPP) coupling modes. Thus, by studying the behavior of the LPP mode along the c-axis, we found the presence of a gradient of free electrons. We suppose that this gradient of electrons is due to the gradient of the main electron donor, in undoped GaN single crystals, i.e. oxygen impurity. We propose a growth model which explains qualitatively the incorporation of oxygen during the growth of GaN crystal under high pressure of nitrogen.     

Structure of nanocrystalline ammonothermal GaN in dependence of temperature and type of acidic mineralizer

This study investigated ammonothermal synthesis of nanocrystalline gallium nitride (GaN) in supercritical ammonia with acidic mineralizers NH₄X (X=Cl, Br, I) at 400–500 °C. Results showed that three types of acidic mineralizers could effectively accelerate the formation of GaN. The mixed hexagonal/cubic phase fractions and lattice parameters of nanocrystalline GaN were calculated by the Rietveld refinement method. SEM showed an agglomerate of nanocrystalline GaN. A considerable amount of GaN was synthesized using NH₄Cl as the mineralizer, however, there was no yield using NH₄Br or NH₄I at 400 °C. For acidic mineralizers, both hexagonal structures (wurtzite) and cubic structures (zincblende) were obtained in ammonothermal synthesis by XRD and Raman measurement. GaN synthesized with NH₄Br and NH₄I showed mixed phases of hexagonal-GaN (h-GaN) and cubic-GaN (c-GaN) at 450–500 °C. In the case of NH₄Cl mineralizer, GaN only exhibited mixed phases of h-GaN and c-GaN at 500 °C, but pure h-GaN at 400–450 °C. Based on the results, NH₄Cl favored pure h-GaN, and NH₄Br and NH₄I favored c-GaN at 400–450 °C.     

Ca3N2 as a flux for crystallization of GaN

In this work Ca₃N₂ was investigated as a potential flux for crystallization of GaN. Melting temperature of the potential flux at high N₂ pressure evaluated by thermal analysis as 1380 °C is in good agreement with the theoretical prediction. It is shown that Ca₃N₂ present in the liquid gallium in small amount (1 at%) dramatically accelerates synthesis of GaN from its constituents. On the other hand, it does not influence significantly the rate of GaN crystallization from solution in gallium in temperature gradient for both unseeded and seeded configurations. However the habit and color of the spontaneously grown GaN crystals change drastically. For 10 mol% Ca₃N₂ content in the liquid Ga it was found that the GaN thick layer and GaN crystals (identified by micro-Raman scattering measurements) were grown on the substrate. For growth from molten Ca₃N₂ (100%) with GaN source, the most important observations were (i) GaN source material was completely dissolved in the molten Ca₃N₂ flux and (ii) after experiment, GaN crystals were found on the sapphire substrate.     

The influence of indium on the growth of GaN from solution under high pressure

The influence of significant fraction (10–50 mole%) indium in liquid gallium on GaN crystallization from a ternary Ga–In–N solution was analyzed. Crystallization experiments of GaN on GaN-sapphire templates from Ga–In solutions, at 1350–1450 °C, with prior to the growth seed wetting at 1500 °C, and 1.0 GPa N₂ pressure, without solid GaN source showed faster growth of GaN on the seed (by a factor of 1.5–2) than using pure gallium solvent. Nevertheless the new grown crystals were morphologically unstable. The instability was reduced by decrease of the wetting temperature down to 1100 °C or by omitting the wetting procedure entirely, which indicated that GaN dissolves much faster in Ga–In melt than in pure Ga and that the unstable growth was caused most likely by complete dissolution of GaN template before the growth. It was observed that the crystals grown on bulk GaN substrates did not show morphological instability observed for GaN-sapphire templates. The influence of indium on thermodynamic and thermal properties of the investigated system is discussed.     

Deposition of bulk GaN from solution in gallium under high N2 pressure on silicon carbide and sapphire substrates

Results of high-pressure directional growth of GaN on foreign substrates: SiC, sapphire and GaN/sapphire MOCVD templates are presented. The role of nitrogen pressure and supersaturation in the growth process is discussed. The conditions for stable growth of the nitride are determined. The results of the crystallization process are compared with those obtained for directional growth on pressure grown GaN crystals.     

Recent achievements in AMMONO-bulk method

In this paper we present progress made recently in the development of the growth of truly bulk GaN crystals by the ammonothermal method in basic environment. High quality 2-in c-plane GaN seeds are shown. Non-polar wafers can also be cut out from thick GaN crystals grown by ammonothermal method. Perfect crystallinity manifests in very narrow peaks in X-ray rocking curves (the full width at half maximum equals about 15 arcsec). GaN epilayers deposited on these substrates exhibit intrinsic narrow exciton lines, which are very sensitive to the optical selection rules typical for hexagonal symmetry, proving the truly non-polar character of such AMMONO-GaN substrates. Other challenges like homogenous insulating properties or high p-type conductivity have been also accomplished by means of ammonothermal method. Semi-insulating crystals of resistivity up to 10¹¹ Ω cm and p-type conductivity within hole concentration up to 10¹⁸ cm⁻³ are already available in diameters up to 1.5-in.     

Improvement of crystal quality in ammonothermal growth of bulk GaN

Several key improvements in crystal quality of bulk GaN grown by the ammonothermal method are presented. Full width at half maximum of (0 0 2) X-ray rocking curve was reduced to 53 and 62 arcsec for Ga-side and N-side, respectively. Transparent bulk GaN crystal was also demonstrated. Oxygen and sodium concentrations were reduced to mid-10¹⁸ and mid-10¹⁵ cm⁻³, respectively. We are currently searching for a growth condition that produces transparent bulk GaN with high structural quality and low impurities. Small-sized, semi-transparent GaN wafers were fabricated by slicing the grown bulk GaN crystals, which demonstrate the high feasibility of ammonothermal growth for production of GaN wafers.     

Growth and characterization of CdSe single crystals by modified vertical vapor phase method

Good quality, large single crystals of CdSe were grown by the modified growth method (i.e., vertical unseeded vapor phase growth with multi-step purification of the starting material in the same quartz ampoule without any manual transfer between the steps). Lower temperature gradients (8–9°C/cm) at the growth interface were used for the crystal growth. As-grown CdSe crystals was characterized by X-ray diffraction, scanning electron microscopy, energy dispersive analyzer of X-rays, high-resistance instrument measurement, and etch-pit observation. It is found that there are two cleavage faces of (1 0 0) and (1 1 0) orientations on the crystal, the resistivity is about 10⁸ Ω cm, and the density of etch pits is about 10^3–4/cm². The crystal was cut into wafers and was fabricated into detectors. The detectors were tested using an ²⁴¹Am radiation source. γ-ray spectra at 59.5 keV were obtained. The results demonstrated that the quality of the as-grown crystals was good. The crystals were useful for fabrication of room-temperature-operating nuclear radiation detectors. Therefore, the modified growth technique is a promising, convenient, new method for the growth of high-quality CdSe single crystals.     

GaN single crystals of different habit grown from solution at near atmospheric pressure

Near atmospheric pressure solution growth is one of the many developing methods for growing bulk GaN from solution. Apart from other approaches, this method holds certain advantages, such as relatively low growth pressure and temperature, and the ability to grow high quality GaN crystals with different orientations by varying the solvent composition. GaN whiskers of millimeter scale size with exceptional mechanical and optical properties were grown from solution. Crystals of near isotropic shape were also grown from solution by manipulating additives in the basic solvent.     

Crystallographic and dielectric properties of flux grown (B′B″: InNb, InTa, YbNb, YbTa and MgW) single crystals

Single crystals of PbIn_1/2Nb_1/2O₃ (PIN), PbIn_1/2Ta_1/2O₃ (PIT), PbYb_1/2Nb_1/2O₃ (PYN), PbYb_1/2Ta_1/2O₃ (PYT) and PbMg_1/2W_1/2O₃ (PMW) have been grown by the flux method. The PbO-based solvents were used. Transparent, light yellow and arrow like shaped PIN and PIT crystals of the perovskite structure were obtained. Small amounts of red and of octahedron habit PIN and PIT crystals of the pyrochlore type were simultaneously grown. In the case of PYN, PYT and PMW only the crystals of the perovskite structure have been grown. The transparent and brown PYN and PYT crystals of octahedron habit were obtained. The transparent, light yellow and of octahedron or truncated octahedron shape PMW crystals were grown. The crystals were characterised by X-ray and dielectric studies. They showed that as-grown PIN crystals are nearly disordered, exhibit the rhombohedral distortion of the pseudo-perovskite unit cell and reveal relaxor behaviour. The partially ordered PIT crystals show monoclinic distortion and undergo antiferroelectric–paraelectric phase transition. The PYN, PYT and PMW single crystals, characterised by chemical order in the B′/B″ ion sublattice, exhibit orthorhombic symmetry and undergo the first-order antiferroelectric–paraelectric phase transitions.     

Flux growth of PbMg1/3Ta2/3O3 single crystals

Single crystals of PbMg_1/3Ta_2/3O₃ (PMT) were grown by the flux method. The PbO–Pb₃O₄–B₂O₃ system was used as a solvent. Transparent and light yellow PMT single crystals of rectangular shape and dimensions up to 10×6×4 mm³ were obtained. For the applied growth conditions only, the crystals of the perovskite structure were grown. X-ray diffraction tests showed that at room temperature PMT exhibits cubic symmetry with lattice parameter a=4.042(1) Å. Dielectric studies pointed to relaxor properties of PMT. The characteristic broad and frequency-dependent maximum of dielectric permittivity was observed at 179.7 K (1 kHz).     

Ammonothermal crystal growth of gallium nitride – A brief discussion of critical issues

The acidic ammonothermal technique is used to develop a technology for production of free-standing gallium nitride (GaN) crystals to match the demand driven by the device technology for the wide-band-gap semiconductor group-III element nitrides. Here we report on advances toward a deeper understanding of parameters that govern mass transport and seeded crystallization of GaN under the conditions of acidic ammonothermal crystal growth with the ultimate goal to improve the process control. Comparison with the basic ammonothermal environment has been made.     

Single crystal growth of copper phthalocyanine using exaltation–evaporation growth method

A new method of growing single crystal for β-form copper phthalocyanine (CuPc) is presented in this paper. Melted anthracene was used as solvent of CuPc. The method, vaporizing the solvent using an automatic exaltation machine, was employed to grow CuPc single crystals. The needle-like single crystals of CuPc up to 11.6 mm in length were obtained by applying this method. The influences of different temperatures, exaltation speeds and concentrations on the single crystals growth were also discussed. The method was called exaltation–evaporation growth method.     

Growth and morphology of ruby crystals with unusual chromium concentration

Single crystals of ruby have been obtained from fluxed melts based on the systems Li₂O–MoO₃, Li₂O–WO₃, Na₂O–WO₃, 2PbO–3V₂O₅, PbO–V₂O₅–WO₃, PbF₂–Bi₂O₃ and Na₃AlF₆ by both the TSSG method and spontaneous crystallization at the temperatures 1330–900 °C. Al₂O₃ solubility has been measured for the flux composition of 2Bi₂O₃–5PbF₂ in the temperature range 1200–1000 °C and dissolution enthalpy has been defined as 29.4 KJ/Mol. The composition of grown crystals was studied by electron microprobe analysis. The synthetic ruby contains from 0.51 to 6.38 at% of chromium admixture depending on the crystal growth conditions. Experimental results on growth conditions, composition and morphology of grown crystals are presented for each flux and temperature interval.     

Reduction of threading dislocations in migration enhanced epitaxy grown GaN with N-polarity by use of AlN multiple interlayer

High quality GaN layer was obtained by insertion of high temperature grown AlN multiple intermediate layers with migration enhanced epitaxy method by the RF-plasma assisted molecular beam epitaxy on (0 0 01) sapphire substrates. The propagating behaviors of dislocations were studied, using a transmission electron microscope. The results show that the edge dislocations were filtered at the AlN/GaN interfaces. The bending propagation of threading dislocations in GaN above AlN interlayers was confirmed. Thereby, further reduction of dislocations was achieved. Dislocation density being reduced, the drastic increase of electron mobility to 668 cm²/V s was obtained at the carrier density of 9.5×10¹⁶ cm⁻³ in Si doped GaN layer.     

Synthesis, growth of organic nonlinear optical crystal: Semicarbazone of 2-amino-5-chloro-benzophenone (S2A5CB) and its characterisation

A new organic crystal of semicarbazone of 2–amino–5–chloro–benzophenone has been grown as a single crystal by slow evaporation solution growth technique for the first time in the literature. The grown crystal has been characterised by proton nuclear magnetic resonance spectral analysis and single crystal and powder X-ray diffraction studies. Functional groups of the crystallised molecules were confirmed by FT-IR and FT-Raman analyses. Mechanical strength of the crystals was studied by microhardness test. Optical transparency of the grown crystals has been studied by UV-Visible spectra. The second harmonic generation property of the compound was analysed.     

Growth and spectroscopic properties of Er single doped and Er–Yb co-doped YAl3(BO3)4 crystals

Er³⁺-doped and Er³⁺–Yb³⁺ co-doped yttrium aluminum borate (YAB) single crystals have been grown by the top-seeded solution growth method using a new flux system, namely NaF–MoO₃–B₂O₃. The Er³⁺ concentrations were 1.3 mol% for both single doped and co-doped crystals and the Yb³⁺ concentration in the Er³⁺–Yb³⁺ co-doped crystal was 20.0 mol% in the raw materials. The distribution coefficients of Er³⁺ single doped and Er³⁺–Yb³⁺ co-doped crystals were measured. The polarized absorption and fluorescence spectra of Er³⁺–Yb³⁺ co-doped crystal were recorded and compared with those of Er³⁺ single doped crystal. The results demonstrate that Er³⁺–Yb³⁺ co-doped YAB crystal is a potential candidate for 1.55 μm laser materials.     

Overgrowth of GaN on Be-doped coalesced GaN nanocolumn layer by rf-plasma-assisted molecular-beam epitaxy—Formation of high-quality GaN microcolumns

GaN crystals were overgrown on GaN nanocolumn platforms with a Be-doped coalesced layer by rf-plasma-assisted molecular-beam epitaxy (rf-MBE). The overgrown GaN included large micrometer-scale hexagonal columnar crystals. These microcrystals were named ‘microcolumns’ and showed high optical properties comparable to those of GaN bulk crystals grown by hydride vapor phase epitaxy (HVPE).