Yb3+和Er3+共掺杂的Y2O3,Y2O2S和NaYS2粉末材料的上转换发光

在980 nm LED激光器激发下,研究了Yb3+-Er3+共掺杂的Y2O3,Y2O2S和NaYS2粉末材料的上转换发射特性。比较了Y2O3∶0.20 Yb3+,0.03Er3+和Y2O2S∶0.20 Yb3+,0.03Er3+以及NaYS2:0.20 Yb3+,0.03Er3+粉末样品的上转换发光光谱,探讨了Er3+上转换发射对基质的依赖性,分析了S2--Yb3+和S2--Er3+电荷转移态对Yb3+-Er3+间能量传递和能级间跃迁几率的影响,借助于能级图解释了在不同基质中Yb3+-Er3+间的能量传递和Er3+的上转换发光机制。     

Er3+,Yb3+共掺Gd2WO6荧光粉的下转换温度效应

采用共沉淀法制备了Er3+,Yb3+共掺Gd2WO6荧光粉,通过对浓度猝灭曲线的分析表明Er3+间的相互作用类型为电偶极-电偶极相互作用。分析了样品荧光的温度效应并得到摩尔分数为5%和20%的Er3+掺杂样品的激活能ΔE分别为0.27和0.29 eV。利用Er3+的2H11/2和4S3/2能级跃迁至基态的荧光强度比随温度变化这一特性研究了两个不同Er3+掺杂浓度样品的下转换温度效应,结果表明该材料体系具有良好的温度传感特性。     

Er3+/Yb3+共掺KLaF4纳米晶的制备和上转换发光

用水热法成功制备了Er3+/Yb3+共掺不同浓度比的KLaF4纳米晶,并在300℃氩气气氛下退火。利用X射线衍射谱(XRD)、透射电子显微镜(TEM)对样品的晶体结构和形貌进行了表征。测量了样品漫反射谱、980 nm激发下的上转换发射光谱和2H11/2能级的荧光寿命。研究结果表明:制备得到的样品为六方相的纳米棒,退火后纳米棒平均直径为28 nm,长为130 nm;在Er3+浓度一定的情况下,提高Yb3+掺杂量有利于增强973 nm附近光的吸收;980 nm的近红外光可上转换为较强的绿光和红光,且红绿光强度和2H11/2能级的平均荧光寿命均会随着Yb3+掺杂浓度的增加而下降。     

Yb3+/Er3+共掺BaGd2ZnO5上转换发光动力学过程的研究

BaGd2ZnO5∶Yb3+,Er3+是目前报道的上转换效率最高的发光材料,有广泛的应用前景,但到目前为止还没有关于该基质材料中Er3+发光动力学过程研究的报道。采用溶胶凝胶法制备BaGd2ZnO5∶Yb3+,Er3+上转换发光材料,测量不同激发密度下上转换光发射功率及上转换效率。数据表明:当激发密度较低时,绿色光发射强度与激发光功率的二次方成正比;激发密度较高时,与激发光功率的一次方成正比;上转换能量效率先增大后减小,具有一个极大值。通过建立不同激发密度下,Er3+离子4 S3/2能级上转换光发射速率方程模型,阐述了产生这一现象的动力学过程和绿色光发射产生的机理。在弱激发条件下,用方波调制的971nm LD激光激发BaGd2ZnO5∶Yb3+,Er3+样品,测量上转换绿光的上升和衰减过程,用Er3+离子4 S3/2能级的速率方程拟合绿光的上升和衰减过程确定相关参数,证实Er3+离子4 S3/2能级粒子布居主要来自于Yb3+→Er3+的能量传递。     

Er3+,Yb3+共掺杂NaGd（MoO4）2荧光粉的发光特性

采用高温固相法制备了Er3+,Yb3+共掺杂的NaGd(MoO4)2荧光粉,通过X射线衍射对样品的物相结构进行了分析,采用荧光光谱手段对样品的下转换发光特性和上转换发光特性进行了研究。通过对激发、发射光谱的分析,发现基质到Er3+存在有效的能量传递。通过对样品上转换发光光谱的分析,发现在不同Yb3+掺杂浓度样品中,红光和绿光上转换发光均为双光子过程,并对样品上转换发光强度与LD泵浦电流和掺杂离子浓度的关系进行了讨论。     

Gd3+掺杂对NaYF4∶Yb3+,Tm3+/Er3+3+纳米材料上转换荧光性能的影响

利用温和的溶剂热方法合成了具有上转换发光性能的Yb3+-Tm3+和Yb3+-Er3+共掺的纳米NaYGdF4。在该体系中, 通过调节Gd3+在基质中的掺杂量可以有效地控制产物的相变、尺寸以及上转换荧光性能。XRD和TEM分析结果表明, Gd3+的掺入在促进NaYF4纳米颗粒由立方相到六方相转变的同时有助于减小其尺寸。上转换光谱研究表明, 在Yb3+-Tm3+和Yb3+-Er3+共掺体系中, 可通过优化Gd3+的掺杂量来有效提高产物的上转换荧光强度。同时, 通过研究Tm3+和Er3+在不同可见光波段的发光强度与泵浦功率的关系探讨了上转换发光的机制。     

BaIn6Y2O13∶Yb3+, Er3+的制备及上转换发光性质的研究

采用高温固相法合成了不同Yb3+和Er3+掺杂浓度的BaIn₆Y₂O₁₃上转换发光材料。XRD数据显示,所合成的BaIn₆Y₂O₁₃∶Yb3+, Er3+属于六方晶系,引入激活剂并没有改变基质的晶体结构。利用971 nm半导体激光器激发样品,测量样品在不同激发光密度下上转换发射光谱和发射光功率,计算了上转换能量效率。数据表明在激发密度不变,激活剂浓度增加时,上转换光绿红比减小;激活剂浓度不变激发光密度增加时,发射光绿红比增大。分析表明是由于Er3+之间的交叉弛豫增强导致绿红比随激活剂掺杂浓度的增加而减小;Yb3+和Er3+之间的能量传递和Er3+的激发态吸收增强导致绿红比随激发密度的增加而增大。随着激发功率增加, 在较低激发功率时, 上转换绿光发射强度与激发功率的二次方成正比; 在较高激发功率时, 上转换绿光发射强度与激发功率的一次方成正比, 与报道的结果一致。能量效率存在极大值, 分别为0.38%(Yb3+掺杂浓度3%, Er3+掺杂浓度1%)和0.06%(Yb3+掺杂浓度9%, Er3+掺杂浓度3%), 产生极值的一个原因是4I_13/2亚稳态能级寿命较长, 聚集了大量电子, 使基态电子急剧减少, 导致上转换泵浦效率降低。     

Yb3+,Er3+离子共掺磷酸盐铒玻璃的Judd-Ofelt光谱参数与光谱性质

研究了含Er3+离子浓度较高(155×1020cm-3)的磷酸盐玻璃中Yb3+敏化离子浓度和Al2O3含量对Er3+离子光谱性质的影响.根据掺Er3+磷酸盐玻璃的吸收光谱,利用JuddOfelt理论计算了强度参数Ωt(t=2,4,6)、Er3+离子的4I132→4I152能级跃迁振子强度、自发辐射几率等光谱参数.用McCumber理论计算了Er3+离子的受激发射截面,结果表明Yb3+离子浓度不影响Er3+离子的受激发射截面,但会影响Er3+离子荧光强度,Yb3+含量越高,Er3+的荧光越强.对掺Er3+磷酸盐玻璃的荧光上转换光谱测试表明,Yb3+含量越高,上转换荧光越强,玻璃上转换主要表现为双光子吸收机理研究了含Er3+离子浓度较高(155×1020cm-3)的磷酸盐玻璃中Yb3+敏化离子浓度和Al2O3含量对Er3+离子光谱性质的影响.根据掺Er3+磷酸盐玻璃的吸收光谱,利用JuddOfelt理论计算了强度参数Ωt(t=2,4,6)、Er3+离子的4I132→4I152能级跃迁振子强度、自发辐射几率等光谱参数.用McCumber理论计算了Er3+离子的受激发射截面,结果表明Yb3+离子浓度不影响Er3+离子的受激发射截面,但会影响Er3+离子荧光强度,Yb3+含量越高,Er3+的荧光越强.对掺Er3+磷酸盐玻璃的荧光上转换光谱测试表明,Yb3+含量越高,上转换荧光越强,玻璃上转换主要表现为双光子吸收机理 关键词： Er3+离子 磷酸盐玻璃 光谱性质 JuddOfelt参数     

Tm3+/Yb3+/Er3+共掺氟氧硅酸盐玻璃的上转换发光特性

利用熔融法制备了Tm3+/Yb3+/Er3+共掺氟氧硅酸盐玻璃.在980nm LD激发下,研究了Tm3+离子和Er3+离子之间的能量传递和Tm3+离子的上转换荧光,分析了Tm3+离子的上转换机理,发现蓝色上转换荧光是三光子过程对应于1 G4→3 H6的跃迁,而红色上转换荧光是双光子过程对应于1 G4→3 F4的跃迁.比较不同掺杂摩尔分数的样品的荧光强度,发现Tm3+离子的最佳掺杂摩尔分数为0.2%.     

纳米NaYb1-xF4:Er3+x中Er3+/Yb3+掺杂浓度变化引起的相变和发光增强

在Yb3+和Er3+共掺杂氟化物纳米体系中,2％Er3+掺杂浓度为上转换发光的最佳浓度,高于这个浓度,随着Er3+掺杂浓度的增加,将发生严重上转换发光浓度猝灭,已为人们广泛认知和接受.本文合成了不同Er3+/Yb3+掺杂浓度比的NaYb1-x F4:Er3+x系列上转换发光纳米粒子.通过扫描电镜、XRD和荧光光谱等分析...     

Cooperative energy transfer and frequency upconversion in Yb3+-Tb 3+ and Nd 3+-Yb 3+-Tb 3+ codoped GdAl3(BO3)4 phosphors

Polycrystalline GdAl₃(BO₃)₄ phosphors codoped with Yb³⁺/Tb³⁺ and/or Nd³⁺/Yb³⁺/Tb³⁺ have been synthesized by combustion method. Upon excitation with a 980 nm laser diode, an intense green upconversion luminescence has been observed in GdAl₃(BO₃)₄:Yb,Tb phosphor. The quadratic dependence of the luminescence on the pump-laser power indicating a cooperative energy transfer process. Meanwhile, it is noticed that upon excitation with 808 nm laser diode, intense luminescence has clearly been detected in GdAl₃(BO₃)₄:Nd,Yb,Tb phosphor. The luminescence intensity exhibits also a quadratic dependence on incident pump-laser power. However, no green-emission has been observed in GdAl₃(BO₃)₄ phosphors codoped with Yb³⁺/Tb³⁺ or Nd³⁺/Tb³⁺ respectively upon excited at 808 nm laser diode. A proposed upconversion mechanism involving energy transfer from Nd³⁺ to Yb³⁺, and then a cooperative energy transfer process from two excited Yb³⁺ to Tb³⁺ has been presented.     

Stark splitting and energy transfer between Dy3+-Ho3+ and between Tb3+-Er3+ in calcium-lithium borate glass

Fluorescence spectrum of Dy³⁺, Dy³⁺-Ho³⁺, Tb³⁺ and Tb³⁺-Er³⁺ doped in calibo glass have been studied using Ar⁺ and excimer lasers. Non-radiative energy transfer from trivalent dysprosium and terbium (donors) to holmium and erbium (acceptors) respectively has been observed on the basis of decrease in the life time of the levels and reduction in fluorescence intensity of Dy³⁺ and Tb³⁺ on increasing Ho and Er concentrations. The interaction mechanism of donor and acceptor ions is found to be dipole-dipole in both cases. Various parameters such as donor-acceptor distances, non-radiative energy transfer efficiency (η) and energy transfer probability (P _da) have been computed. Stark splitting have also been marked in several intense transition of the two.     

Ce3+离子敏化Eu3+∶Cr3+∶Sm3+∶YAG外延层的荧光现象

对Ce3+ ∶Eu3+ ∶Cr3+ ∶Sm3+ ∶YAG处延层中的荧光敏化现象进行了报道和分析 ,在较高浓度的Ce3+ 离子掺杂时 ,外延层在蓝色、绿色波段出现了新的荧光谱线 ,可解释为在Ce3+ 离子敏化作用下 ,Eu3+ 离子产生了由高位激发态能级5Di(i=1,2 ,3)直接到基态能级7Fj(j =0 ,1,2 ,3)的辐射跃迁过程 ,并且这种Ce3+ ∶Eu3+ ∶Cr3+ ∶Sm3+ ∶YAG外延层还是一种新颖的白色单晶荧光材料。     

Eu3+ luminescence and Gd3+-Eu3+ energy transfer in K5Li2GdF10:Eu3+

Polycrystalline samples of europium-doped K₅Li₂GdF₁₀ have been obtained by a slow cooling of melted compound and investigated using spectroscopy methods. Luminescence from the ⁵ D ₂ level of Eu³⁺ is found to be weak. Intense visible emission upon excitation into the ⁵ D ₂ or higher energy levels has been attributed to overlapping transitions from long-lived ⁵ D ₁ and ⁵ D ₀ levels. A strong increase of the ⁵ D ₀ emission at the expense of the ⁵ D ₁ emission occurs between 5 K and 25 K without significant change of the ⁵ D ₁ lifetime. To account for this, it is supposed that both the radiative and the nonradiative transition rates are temperature-dependent. Efficient energy transfer from the ⁶ G _J levels of Gd³⁺ to Eu³⁺ ions has been evidenced by excitation spectra in the VUV region and VUV-excited luminescence. It has been concluded that the cross relaxation contributes to the energy-transfer process. Received: 8 May 2001 / Accepted: 11 May 2001 / Published online: 25 July 2001     

GdBO3：Pr3+，Yb3+中Pr3+到Yb3+的能量传递及发光性质

采用高温固相法制备了一系列单掺或双掺Pr3+和Yb3+的GdBO3材料,分别测试分析了材料的物相结构和发光性质。在446 nm蓝光( Pr3+：3 H4→3 P2)激发下,检测到Yb3+的近红外特征发射,表明样品中存在Pr3+到Yb3+的能量传递。 Pr3+的掺杂浓度一定时,样品的发光会随着Yb3+掺杂浓度的改变而发生变化。通过对比不同掺杂情况下Pr3+：3 P0能级的衰减曲线,发现随着Yb3+的掺杂浓度的增加,该能级的荧光寿命不断缩短;同时利用不同条件下的衰减特性计算得出不同 Yb3+掺杂浓度样品的能量传递效率。用 Inokuti-Hirayama模型分析表明Pr3+-Yb3+能量传递类型为偶极子-偶极子相互作用。     

Optical spectroscopy of Cr3+ and Cr3+-Tm3+ in alkaline silicate glasses

Conclusions Alkaline silicate glasses seem to be good candidates as host materials for codoping with Cr³⁺ and Tm³⁺. Cr³⁺ ions occupy mainly low-field sites in them, and their broadband emission overlaps Tm³⁺ excitation. As a consequence very high efficiency for the energy transfer Cr³⁺→Tm³⁺ is achieved with moderate concentrations of these ions. Moreover, the average lifetime of the Cr³⁺ ions in codoped glasses is long enough to allow significant energy storage by flashlamp pumping. Published in Zhurnal Prikladnoi Spektroskopii, Vol. 62, No. 5, pp. 115–120, September–October, 1995.     

LaOBr:Ce,Tb中Ce3+对Tb3+发光的影响

近年来人们对LaOBr:Tb的合成及其发光特性的研究日益增多。LaOBr:Tb不仅是良好的X光增感屏材料,也是较好的阴极射线发光材料。为了进一步提高它的亮度,降低了b的含量(因Tb很贵),寻求LaOBr中Tb3+发光的敏化剂是很重要的。     

LaOBr:Ce3+,Tb3+中Ce3+与Tb3+间能量传递

本文利用毫微秒技术在ns秒量级测量了不同浓度组分的LaOBr:Ce3+,Tb3+中Ce3+发射带的衰减常数τCe值和时间分辨光谱,确立了Ce3到Tb3+能量传递过程模型,建立了动力学方程和导出能量传递的计算公式。据此计算出Ce3+到Tb3+的能量传递几率和效率,得出Ce3+,Tb3+的最佳浓度。     

氟化物中Yb3+对Ho3+, Tm3+的直接敏化上转换作用

采用双掺杂(Yb^3 ／Ho^3 )和多掺杂(Ho^3 ／Yb^3 ／Tm^3 )方式,研究了氟化物中Yb^3 对Ho^3 ,Tm^3 的直接敏化上转换作用,并对它们在980nm激光激发下的上转换光谱特性进行了比较,对它们的上转换机理作了详细的讨论分析。观测到两处很强的上转换发光,分别是Yb^3 ／Ho^3 共掺杂体系中^5F4^5S2(Ho^3 )→^5Is(Ho^3 )的荧光跃迁和Ho^3 ／Yb^3 ／Tm^3 共掺杂体系中^3H4(Tm^3 )→H6(Tm^3 )的荧光跃迁。还发现由于添加了Tm^3 ,减弱了Yb^3 ／Ho^3 共掺杂体系中Ho^3 在可见光范围的上转换发光强度。