强烈阳极氧化法快速制备多孔氧化铝模板

In the electrolyte of oxalic acid/alcohol/aqueous solution, highly-ordered porous anodic aluminum oxide(AAO) template was fabricated by hard anodization. The surface morphology and the structure of AAO template were characterized by Field-Emission Scanning Electron Microscope(FE-SEM) and XRD, respectively. The effects of different factors including alcohol type, ratio of alcohol to water, and oxalic acid concentration on the ordering degree and pore diameter of AAO template were investigated. Under the glycol to water ratio of 1∶1(by volume) with an oxalic acid concentration of 0.5 mol·L^-1, and voltage at 160 V, the obtained AAO template was hexangular arrangement with pore diameter of 80 nm and pores spacing of 120 nm, the growth rate was 51.9 μm·h^-1.     

多孔阳极氧化铝膜的制备研究

在直流恒压下,在不同的酸性溶液中对铝片实施两步阳极氧化制备多孔氧化铝膜,在磷酸溶液中制得的模板孔径大,并且电解时间缩短,加快了制备模板的过程。同时利用阳极氧化初期电流密度的变化,分析了多孔氧化铝膜的形成机理。     

硫酸/草酸混酸电解液中阳极氧化法制备多孔阳极氧化铝模板

Well ordered porous anodic alumina (PAA) film was prepared on pure Al substrate using sulfuric/oxalic acid mixture as electrolyte with different ratios, the best regular PAA film with an average diameter of 45 nm was obtained using 1∶1 sulfuric/oxalic (molar concentration) mixed acid at 26 V. Addition of oxalic acid into sulfuric acid electrolyte resulted in the increase of anodizing current density, indicating a faster formation rate of PAA film. In 1∶1 sulfuric/oxalic acid electrolyte, the current density was the biggest, which illustrated that the formed barrier layer was the thinnest. Besides, addition of oxalic acid increased the stress of oxide film, accordingly changed the self-organized process of PAA film. XPS results indicate that the PAA film is mainly composed of amorphous alumina independent of oxalic acid addition.     

二次阳极氧化方法制备有序多孔氧化铝膜

通过二次阳极氧化方法制备多孔氧化铝膜与一次阳极氧化方法制备多孔氧化铝膜孔排布规律性的对比,结果发现,二次阳极氧化方法制取的多孔氧化铝膜孔排布规律性明显好于一次阳极氧化法制取的多孔膜.在几个微米范围内,孔呈理想的六角排布.去除一次阳极氧化膜后,二次阳极氧化得以在更良好的表面进行,制取的氧化铝膜孔规律性和有序度更高.有序区域的尺寸与晶粒内的亚晶大小有一定关系.     

纳米孔阵列阳极氧化铝膜的制备和表征

本文通过在0℃、0.5mol·L^-1的草酸溶液中阳极氧化高纯铝片的方法制得了阳极氧化铝(AAO)膜，并用扫描电子显微镜(SEM)和原子力显微镜(AFM)对AAO膜的形貌和结构进行了表征。结果表明，阻挡层AAO膜中大小一致的膜胞在铝/氧化铝界面上排成六方形阵列;有孔层AAO膜中含有高度有序的纳米孔阵列和膜胞阵列，并且孔的直径和膜胞的尺寸都具有较窄的分布。另外，考察了阳极氧化电压对膜胞尺寸、孔径大小、孔密度和膜胞密度的影响，表明在一定的电压范围内，膜胞和孔径都随电压的升高而增大，而孔密度和膜胞密度却随电压的升高而减小。     

铝合金表面用化学刻蚀和阳极氧化法制备的超疏水膜层的耐蚀性能

通过化学刻蚀和阳极氧化在AA2024铝合金表面制备超疏水表面。当化学刻蚀时间超过3 min时,表面在很宽pH值范围内显示出水静态接触角大于150°。SEM和AFM照片表明化学刻蚀时间决定了试样表面形貌和粗糙度。FTIR用来研究氟硅烷(G502)与AA2024表面的结合。结果说明FAS(氟硅烷)分子与铝合金表面的三氧化二铝发生反应,并在阳极氧化膜层表面展示出优异的结合性能。超疏水表面的耐腐蚀性能通过在质量分数为3.5%的NaCl溶液中进行动电位极化和交流阻抗(EIS)测试。电化学测试结果和等效电路模型显示出超疏水表面显著改善抗腐蚀性能。     

特殊型纳米多孔阳极氧化铝模板的制备

多孔阳极氧化铝(PAA)模板具有六角有序排列的柱形孔,且孔径均匀可调,加之其良好的机械和热稳定性,在纳米材料领域得到了广泛研究和应用。近年来,人们通过改变铝阳极氧化条件制备出了多种特殊型纳米PAA模板,并利用这些模板结合物理或化学方法成功地合成了多种新型纳米功能材料。本文在简要介绍常规纳米PAA模板制备的基础上,较全面地综述了诸如孔道呈分叉形、锯齿形、骨形、倒圆锥形,孔洞呈菱形、三角形、正方形,孔道或孔壁结构呈周期性变化等特殊型纳米PAA模板的制备,揭示了电场强度和电解液种类、温度在PAA孔洞形貌尺寸调控方面的重要性,并展望了这类模板的发展方向及应用前景。     

多孔氧化铝有序膜的制备研究

本文用阳极氧化法分别在硫酸和草酸电解液中成功制备出高度有序、具有纳米级孔洞的氧化铝有序阵列模板。采用饱和HgCl₂去除Al基体后,得到典型六方形结构的多孔Al₂O₃有序膜。通过改变氧化电压、氧化时间等条件使模板的孔径、孔深可调、膜厚度可控,并系统研究了对模板有序性、孔径、膜厚度等的影响因素,总结出制备Al₂O₃有序膜的最佳工艺。     

不锈钢基材超亲水吸附材料的制备与吸附性能研究

随着科技的发展以及材料在生活中的广泛应用,人们的需求不再局限于普通材料,还将目光投向具有更大市场的亲水材料.近年来,人们使用各种方法制备亲水材料,如溶胶凝胶法、等离子体处理法等等.本文作者将以SUS304与SUS201两种常见的不锈钢基材为实验材料,通过化学氧化法对其进行表面处理,并利用扫描电子显微镜(SEM)与X射线能量色散谱(EDS)对处理前后不锈钢基材的表面性质进行分析,通过显微照片确定处理后不锈钢基材表面水的接触角数据,并利用荧光光谱法评价亲水不锈钢表面的吸附性能.     

用AFM研究阳极氧化铝的不稳定生长

用原子力显微镜(AFM)研究了多孔阳极氧化铝(AAO)模板的不稳定生长. 结果表明:AAO模板的不稳定生长导致了纳米孔道结构有序度的降低.在H₃PO₄溶液中生长的AAO模板孔道结构稳定性较差;而在H₂C₂O₄溶液中生长的AAO模板稳定性依赖于氧化电压和电流密度,在低电压和电流密度下稳定性较好,高电压和电流密度下稳定性较差. 充分利用这种不稳定生长特性,通过控制AAO模板的阳极氧化条件,可得到具有分枝孔道结构的特殊模板,这为利用模板法制备各种Y形或T形纳米线、管提供了新的发展空间.     

Fabrication of Multicomponent Polymer Nanostructures Containing PMMA Shells and Encapsulated PS Nanospheres in the Nanopores of Anodic Aluminum Oxide Templates

Multi‐component polymer nanomaterials have attracted great attention because of their applications in areas such as biomedicine, tissue engineering, and organic solar cells. The precise control over the morphologies of multi‐component polymer nanomaterials, however, is still a great challenge. In this work, the fabrication of poly(methyl methacrylate)(PMMA)/poly­styrene (PS) nanostructures that contain PMMA shells and encapsulated PS nanospheres is studied. The nanostructures are prepared using a triple solution wetting method with anodic aluminum oxide (AAO) templates. The nanopores of the templates are wetted sequentially by PS solutions in dimethylformamide (DMF), PMMA solutions in acetic acid, and water. The compositions and morphologies of the nanostructures are controlled by the interactions between the polymers, solvents, and AAO walls. This work not only presents a feasible method to prepare multi‐component polymer nanomaterials, but also leads to a better understanding of polymer‐solvent interactions in confined geometries.

     

铝基阳极氧化铝模板水热法制备TiO2纳米管阵列

在(NH4)2TiF6的水溶液中,以铝基阳极氧化铝为模板,采用水热法制备了TiO2纳米管阵列. 使用场发射扫描电镜和X射线衍射对水热合成产物进行了表征. 实验结果表明,水热处理所得TiO2纳米管阵列具有特殊的形貌,其表面为连续的多孔状,断面为不连续、相互分离的管状;管口和管壁分别由平均粒度约45和25 nm的微细TiO2颗粒紧密堆积而成. 采用本方法制备的TiO2纳米管阵列无需热处理便已具有明显的锐钛矿型晶相特征.     

Effect of Nonsolvent on the Formation of Polymer Nanomaterials in the Nanopores of Anodic Aluminum Oxide Templates

We study the effect of nonsolvent on the formation of polymer nanomaterials in the nanopores of porous templates. Water (nonsolvent) is added into a poly (methyl methacrylate) (PMMA) solution in dimethylformamide (DMF) confined in the nanopores of an anodic aluminum oxide (AAO) template. Water forms a wetting layer on the pore wall and causes the PMMA solution to be isolated in the center of the nanopore, resulting in the formation of PMMA nanospheres or nanorods after the solvent is evaporated. The formation of the polymer nanomaterials induced by nonsolvent is found to be driven by the Rayleigh‐instability‐type transformation. Without adding the nonsolvent, PMMA chains precipitate on the walls of the nanopores after the solvent is evaporated, and PMMA nanotubes are obtained.     

大长径比有序多孔阳极氧化铝模板的制备及用于镍纳米线阵列

报道一种恒电流二次氧化制备大长径比(>1000)阳极氧化铝(AAO)模板的方法,研究氧化时间和氧化电流密度分别对制备的AAO模板的表面形貌、孔径大小、厚度等的影响.结果表明,AAO模板的表面形貌及厚度n受m氧、厚化度电约流为密2度00及μ氧m、化长时径间比的为影10响0;-当13氧00化的电高流质密量度A为AO8模m板A·.c采m用-2电时化,氧学化沉1积8方h能法在制制备备出的孔A径A为O模15板0-的20孔0中成功制备了Ni纳米线阵列,分别用扫描电镜(SEM)、高分辨透射电镜(HRTEM)、X射线衍射(XRD)和X射线能量散射光谱(EDS)对其进行了表征;结果显示,制备的Ni纳米线排列整齐有序,每根Ni纳米线直径几乎相同,约150nm,长度约为180-200μm,长径比为1200-1300,与AAO模板的参数一致.研究了Ni纳米线阵列的长径比对其磁性能的影响,发现大长径比的Ni纳米线阵列具有明显的磁各向异性,而长径比约为200的Ni纳米线阵列未表现出明显的磁各向异性.本文结果表明,恒电流二次氧化方法能制备大长径比的AAO模板,并能用于制备大长径比的一维纳米材料阵列,可望在制备具有特殊光学、磁学等性能材料方面得到应用.     

酸根离子掺杂对多孔阳极氧化铝光致发光特性的影响

采用电化学二次阳极氧化法分别在纯硫酸、纯草酸及硫酸-草酸混合电解液中制备了3个系列的多孔阳极氧化铝(AAO)样品, 考察了它们在250 nm光激发下的光致发光(PL)特性. 研究结果表明, 各系列AAO样品在350～450 nm波段范围内的PL谱形均完全相似, 具有相同的发光中心, 即氧空位缺陷态; 掺杂进入AAO样品的SO₄^2-和C₂O₄^2-分解形成的发光中心对应的光发射分别在288和328 nm附近; 对于硫酸-草酸混合电解液中生长的AAO样品, 其在328 nm附近的发光峰随着硫酸-草酸体积比的增大呈先增大后减少的变化, 而288 nm附近的发光峰却由基本消失到逐渐显现. 初步分析了该现象的成因.     

Preparation of Polyelectrolyte Nanotubes by a Pressure filter-template Technique Using Microporous Anodic Aluminum Oxide (AAO) as the Template

Polyelectrolyte nanotubes of poly(sodium 4‐styrene‐sulfonate) (PSS) with cationic poly(diallyl dimethyl ammonium chloride) (PDDA) (PSS/PDDA) were fabricated by a pressure‐filter‐template technique using microporous anodic aluminum oxide (AAO) as the template. UV‐Vis spectroscopy, scanning electron microscopy (SEM), transmission electron microscopy (TEM), X‐ray diffraction (XRD) and infrared spectroscopy (FT‐IR) were applied to characterize the obtained PSS/PDDA nanotubes. The results have shown that the PSS/PDDA nanotubes exhibit an amorphous structure and have the outer diameter of 200 nm and length of 25 µm respectively, which are in good agreement with the dimensions of the AAO template pores. The wall thickness of the nanotubes may be controlled by the number of the self‐assembled layers. Formation of the nanotubes follows a layer‐by‐layer (LbL) mechanism due to the electrostatic interactions, where the SO^?₃ groups of PSS are first adsorbed on the Lewis acid sites of AAO template pores.     

贫水电解质体系制备多孔阳极氧化铝模板的研究

在有机溶剂为主的含草酸电解质中,研究了大孔径有序度高的阳极氧化铝(AAO)的一步法电化学制备.实验证实,电解质中水含量的降低能够有效抑制铝的电氧化速率和溶解速率,使得其氧化膜孔道的生长能够稳定进行,所得到的六方孔道排列有序度明显高于纯水溶剂制备的电解质体系下的产物.考察了水含量、有机溶剂种类以及电解质浓度对AAO模板孔道形貌的影响.结果表明,有机溶剂贫水电解质体系使得电氧化电压的选取范围比水溶液电解质体系更宽,孔径连续可调,反应条件温和.该方法适合于制备均匀大孔径的AAO模板.