Preparation and characteristics of Pr1.6Sr0.4NiO4+YSZ as composite cathode of solid oxide fuel cells

Composite cathodes of (1?x wt%)Pr_1.6Sr_0.4NiO₄+(x wt%)Y₂O₃-stabilized ZrO₂ (YSZ; x=0, 10, 20, 30, 40) abbreviated as Pr_1.6Sr_0.4NiO₄+xYSZ, were prepared. The composite cathodes with x>0 matched with electrolyte YSZ in thermal expansion coefficient (TEC) better than the cathode Pr_1.6Sr_0.4NiO₄ did. Pr_1.6Sr_0.4NiO₄+20YSZ exhibited the best performance on cathode overpotential and impedance. When the cathode overpotential was 0.1 V, the polarization current density of Pr_1.6Sr_0.4NiO₄+20YSZ was 0.28 A cm^?2, which is about 5.6 times higher than that of Pr_1.6Sr_0.4NiO₄, 0.05 A cm^?2. The area-specific resistance (ASR) for Pr_1.6Sr_0.4NiO₄+20YSZ was about 17.7% of that for Pr_1.6Sr_0.4NiO₄ at 750 °C.     

Impact of synthesis technique on the structure and electrochemical characteristics of Pr0.6Sr0.4Co0.2Fe0.8O3 − δ (PSCF) cathode material

Effect of preparation method for Pr_0.6Sr_0.4Co_0.2Fe_0.8O_3 − δ (PSCF) on its electrochemical performance was investigated. Powder samples were synthesized by hexamethylenetetramine (HMTA) and EDTA-citric acid (EC) techniques, respectively. The particles synthesized by HMTA were smaller than those prepared by EC method as proved by TEM. X-ray photoelectron spectroscopy illuminated that more oxygen sites including oxygen vacancy on the surface of HMTA-derived PSCF exist than that of EC-derived PSCF. The area specific resistance (ASR) value of HMTA-derived PSCF cathode was as low as 0.454 Ω cm² at 600 °C, whereas the ASR value of EC-derived PSCF was 0.641 Ω cm². The results in the present study demonstrated the advantages of the HMTA method in the synthesis of highly catalytic active PSCF oxide powder for SOFCs.     

Thermal, electrical, and electrochemical properties of Lanthanum-doped Ba0.5Sr0.5 Co0.8Fe0.2O3-δ

Crystal structure, thermogravimetry (TG), thermal expansion coefficient (TEC), electrical conductivity and AC impedance of (Ba_0.5Sr_0.5)_1-xLa_xCo_0.8Fe_0.2O_3-δ (BSLCF; 0.05?x?0.20) were studied in relation to their potential use as intermediate temperature solid oxide fuel cell (IT-SOFC) cathode. A single cubic pervoskite was observed by X-ray diffraction (XRD). The TEC of BSLCF was increasing slightly with the increasing content of La, and all the compounds showed abnormal expansion at high temperature. Proved by the TG result, it was associated with the loss of lattice oxygen. The electrical conductivity, which is the main defect of Ba_0.5Sr_0.5 Co_0.8Fe_0.2O_3-δ (BSCF), was improved by La doping, e.g., the compound of x=0.20 demonstrated a conductivity of σ=376 S cm⁻¹ at 392 °C. The increase of electrical conductivity resulted from the increased concentration of charge carrier induced by La doping. In addition, the AC impedance revealed the better electrochemical performance of BSLCF. For example, at 500 °C, the sample with composition x=0.15 yielded the resistance values of 2.12 Ω cm², which was only 46% of BSCF.     

Effect of fabrication parameters on the electrical conductivity of YxSr1−xTiO3 for anode materials

Yttrium-doped strontium titanate (Y_xSr_1−xTiO₃), as probable anode material for SOFC, was prepared by solid-state reaction. The solubility of yttrium in SrTiO₃ at different temperatures was examined and the electrical conductivities of Y_xSr_1−xTiO₃ were measured from 500 to 1000 °C. The effects of doping amount, fabrication atmosphere, and sintering temperature on the electrical conductivity of Y_xSr_1−xTiO₃ were investigated. Y_xSr_1−xTiO₃ with x=0.08 was found to give the maximum electrical conductivity, 71 S/cm at 800 °C in pure hydrogen. Reducing atmospheres and appropriate sintering temperatures play a positive role in improving the electrical conductivity.     

Strongly oriented BST films on La0.9Sr1.1NiO4 electrodes deposited on various substrates for integration of high capacitances on silicon

In this study, we demonstrate the successful oriented growth of Ba_0.6Sr_0.4TiO₃(h 0 0)/La_0.9Sr_1.1NiO₄(0 0 l) stacks by pulsed laser deposition on SiO₂/Si for application in integrated capacitances. We show that for specific deposition conditions the La_0.9Sr_1.1NiO₄ layer spontaneously grows along its c-axis both on SiO₂/Si and on Pt/Ti/SiO₂/Si substrates, serving as a template for the subsequent oriented growth of Ba_0.6Sr_0.4TiO₃ (BST). Moreover, as the resistivity of the La_0.9Sr_1.1NiO₄ layer is ∼1 mΩ cm, it also fulfills the function of bottom electrode for integration of perovskite-based capacitors on silicon. This holds the promise of integrating epitaxial BST with very high dielectric constant compared to polycrystalline BST films. Still, preliminary capacitance measurements on Al/BST/La_0.9Sr_1.1NiO₄/SiO₂/Si capacitors indicate that the stack deposition needs further optimization.     

Growth and spectroscopic characterization of Er: Sr3Y(BO3)3 crystal

This paper reports the growth and spectroscopic characterization of Er³⁺:Sr₃Y(BO₃)₃ crystal. Er³⁺:Sr₃Y(BO₃)₃ crystal with dimensions up to ∅20×35 mm³ has been grown by Czochralski method. The polarized spectroscopic properties of Er³⁺:Sr₃Y(BO₃)₃ crystal were investigated. Based on the Judd-Ofelt theory, the effective intensity parameters Ω_t were obtained: Ω₂=1.71×10⁻²⁰ cm², Ω₄=1.39×10⁻²⁰ cm², Ω₆=0.74×10⁻²⁰ cm² for π-polarization, and Ω₂=1.77×10⁻²⁰ cm², Ω₄=1.44×10⁻²⁰ cm², Ω₆=0.65×10⁻²⁰ cm² for σ-polarization. The emission cross-section σ_em was calculated to be 4.75×10⁻²¹ cm² for π-polarization at 1536 nm and 6.30×10⁻²¹ cm² for σ-polarization at 1537 nm. The investigated results showed that Er³⁺:Sr₃Y(BO₃)₃ crystal may be regarded as a potential laser host material for 1.55 μm IR solid-state lasers.     

Magnetic and electrical properties of amorphous Ge1−xCrx thin films grown by low temperature vapor deposition

Amorphous Ge_1−xCr_x thin films are deposited on (1 0 0)Si by using a thermal evaporator. Amorphous phase is obtained when Cr concentration is lower than 30.7 at%. The electrical resistivities are 1.89×10⁻³–0.96×10² Ω cm at 300 K, and decrease with Cr concentration. The Ge_1−xCr_x thin films are p-type. The hole concentrations are 5×10¹⁶–7×10²¹ cm⁻³ at 300 K, and increase with Cr concentration. Magnetizations are 7.60–1.57 emu/cm³ at 5 K in the applied field of 2 T. The magnetizations decrease with Cr concentration and temperature. Magnetization characteristics show that the Ge_1−xCr_x thin films are paramagnetic.     

Metamagnetic transition and magnetocaloric effect in charge-ordered Pr0.68Ca0.32−xSrxMnO3 (x=0, 0.1, 0.18, 0.26 and 0.32) compounds

In this study, magnetic and magnetocaloric properties of Pr_0.68Ca_0.32−xSr_xMnO₃ (x=0, 0.1, 0.18, 0.26 and 0.32) compounds were investigated. X-ray results indicated that all the samples have a single phase of orthorhombic symmetry. The orthorhombic unit cell parameters increase with the increase in Sr content. Large negative magnetic entropy changes (−26.2 J/kg K at 38 K and 5 T for x=0 and −6.5 J/kg K at 83 K and 6 T for x=0.1) were attributed to ultrasharp metamagnetic transitions. The peak value of ΔS_m decreased from −4.1 J/kg K for x=0.18 sample to −2.4 J/kg K for x=0.32 at 1 T magnetic field.     

Fabrication and characterization of epitaxial Sr0.6Ba0.4Nb2O6/La0.7Sr0.3CoO3 heterostructures

Epitaxial Sr_0.6Ba_0.4Nb₂O₆(SBN60)/La_0.7Sr_0.3CoO₃ heterostructures were fabricated on LAO(0 0 1) substrates using pulsed laser deposition (PLD). Their structural properties were investigated by X-ray diffraction. The θ-2θ scans showed single crystalline Sr_1−xBa_xNb₂O₆ (SBN) and La_xSr_1−xCoO₃ (LSCO) layers with a 〈0 0 1〉 orientations perpendicular to the substrate plane. Phi scans on the (2 2 1) plane of SBN layer indicated that the films have two in-plane orientations with respect to the substrate. The SBN unit cells were rotated in the plane of the film by ±18.4° as well as ±45° with respect to the LAO substrate. This rotation was explained by considering the lattice matching between films and substrate, and minimization of electrostatic energy. Spectroellipsometry (SE) was used to characterize the depth profile, the microstructural inhomogeneities, including voids and surface roughness, refractive indices and extinction coefficients of the films.     

Investigation of spectroscopic properties and thermal stability of Er/Yb-co-doped Bi2O3-B2O3-Ga2O3 glasses

A series of Er³⁺/Yb³⁺-co-doped 60Bi₂O₃-(40−x) B₂O₃ -xGa₂O₃ (BBGA x=0, 4, 8, 12, 16 mol%) glasses have been prepared. The absorption spectra, emission spectra, fluorescence lifetime of Er³⁺:⁴I_13/2 level and thermal stability were measured and investigated. Three Judd-Ofelt intensity parameters Ω_t (t=2,4,6) (Ω₂=(4.67-5.93)×10⁻²⁰ cm², Ω₄=(1.50-1.81)×10⁻²⁰ cm², Ω₆=(0.92-1.17)×10⁻²⁰ cm²) of Er³⁺ ions were calculated by Judd-Ofelt theory. It is found that the Ω₆ first increases with the increase of Ga₂O₃ content from 0 to 8 mol% and then decreases, which is mainly affected by the number of non-bridging oxygen ions of the glass network. The high peak of stimulated emission cross-section () of Er³⁺: ⁴I_13/2→⁴I_15/2 transition were obtained according to McCumber theory and broad full width at half maximum (FWHM=69-76 nm) of the ⁴I_13/2→⁴I_15/2 transition of Er³⁺ ions were measured. The results indicate that these new BBGA glasses can be used as a candidate host material for potential broadband optical amplifiers.     

Luminescence of Ce and Pr doped Sr2Mg(BO3)2 under VUV-UV and X-ray excitation

This report presents the luminescence properties of Ce³⁺ and Pr³⁺ activated Sr₂Mg(BO₃)₂ under VUV-UV and X-ray excitation. The five excitation bands of crystal field split 5d states are observed at about 46 729, 44 643, 41 667, 38 314 and 29 762 cm⁻¹ (i.e. 214, 224, 240, 261 and 336 nm) for Ce³⁺ in the host lattice. The doublet Ce³⁺ 5d→4f emission bands were found at about 25 840 and 24 096 cm⁻¹ (387 and 415 nm). The influence of doping concentration and temperature on the emission characteristics and the decay time of Ce³⁺ in Sr₂Mg(BO₃)₂ were investigated. For Pr³⁺ doped samples, the lowest 5d excitation band was observed at about 42017 cm⁻¹ (238 nm), a dominant band at around 35714 cm⁻¹ (280 nm) and two shoulder bands were seen in the emission spectra. The excitation and emission spectra of Ce³⁺ and Pr³⁺ were compared and discussed. The X-ray excited luminescence studies show that the light yields are ∼3200±230 and ∼1400±100 photons/MeV of absorbed X-ray energy for the samples Sr_1.86Ce_0.07Na_0.07Mg(BO₃)₂ and Sr_1.82Pr_0.09Na_0.09Mg(BO₃)₂ at RT, respectively.     

Photoluminescence properties of Sr1-xSi2O2N2: Eux as green to yellow-emitting phosphor for blue pumped white LEDs

This study evaluated potential applications of green to yellow-emitting phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) in blue pumped white light emitting diodes. Sr_1-xSi₂O₂N₂: Eu²⁺_x was synthesized at different Eu²⁺ doping concentrations at 1450 °C for 5 h under a reducing nitrogen atmosphere containing 5% H₂ using a conventional solid reaction method. The X-ray diffraction patterns of the prepared phosphor (Sr_1-xSi₂O₂N₂: Eu²⁺_x) were indexed to the SrSi₂O₂N₂ phase and an unknown intermediate phase. The photoluminescence properties of these phosphors (Sr_1−xSi₂O₂N₂: Eu²⁺_x) showed that the samples were excited from the UV to visible region due to the strong crystal field splitting of the Eu²⁺ ion. The emission spectra under excitation of 450 nm showed a bright color at 545-561 nm. The emission intensity increased gradually with increasing Eu²⁺ doping concentration ratio from 0.05 to 0.15. However, the emission intensity decreased suddenly when the Eu²⁺ concentration ratio was >0.2. As the doping concentration of Eu²⁺ was increased, there was a red shift in the continuous emission peak. These results suggest that Sr_1-xSi₂O₂N₂: Eu₂⁺_x phosphor can be used in blue-pumped white light emitting diodes.     

Preparation, structure and oxide ion conductivity in Ce6−xYxMoO15−δ (x=0.1-1.4) solid solutions

The Ce_6−xY_xMoO_15−δ solid solution with fluorite-related structure have been characterized by differential thermal analysis/thermogravimetry (DTA/TG), X-ray diffraction (XRD), IR, Raman, scanning electric microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) methods. The electric conductivity of samples is investigated by Ac impedance spectroscopy. An essentially pure oxide-ion conductivity of the oxygen-deficiency was observed in pure argon, oxygen and air. The highest oxygen-ion conductivity was found in Ce_5.5Y_0.5MoO_15−δ ranging from 5.9×10⁻⁵ (S cm⁻¹) at 300 °C to 1.3×10⁻² (S cm⁻¹) at 650 °C, respectively. The oxide-ion conductivities remained stable over 80 h-long test at 800 °C. These properties suggested that significant oxide-ionic conductivity exists in these materials at moderately elevated temperatures.     

Influence of B2O3 to the inhomogeneous broadening and spectroscopic properties of Er/Yb codoped fluorophosphate glasses

In a three-components fluorophosphate glass system, the introduction of H₃BO₃ brings some valuable influence to the spectroscopic and thermal properties of the glasses. With H₃BO₃ increases from 2 to 20 mol%, Ω₆, S_ed4I13/2, FWHM, T_g and fluorescence lifetime change from 3.21×10⁻²⁰ cm², 1.77×10⁻²⁰ cm², 45 nm, 480 °C and 8.8 ms to 4.66×10⁻²⁰ cm², 2.11×10⁻²⁰ cm², 50 nm, 541 °C and 7.4 ms, respectively. σ_abs, σ_emi, FWHM×τ_f×σ_emi has a maximum when H₃BO₃ is 11 mol%. T_g and T_x−T_g increases with H₃BO₃ introduction. Results showed that in fluorophosphate glasses, proper amount of B₂O₃ can be used as a modifier to suppress upconversion and improve spectroscopic properties, broadband property and crystallization stability of the glasses while keeps the fluorescence lifetime relatively high.     

Room temperature magnetoresistance in Ln2/3A1/3MnO3 manganites

The investigation of the manganites La_2/3−xPr_xSr_1/3MnO₃, La_2/3Sr_1/3−xCa_xMnO₃ and La_2/3+xCa_1/3−2xAg_xMnO₃, which all exhibit Mn³⁺:Mn⁴⁺=2, shows that it is possible to reach high magnetoresistance at room temperature, up to 21% under 1.2 T. These materials are compared to La_5/6Ag_1/6MnO₃ which corresponds to the same Mn³⁺:Mn⁴⁺ ratio and exhibits a magnetoresistance of 25% in this field. An interesting feature deals with the value of the insulator-metal transition temperature T_IM, often higher than T_C, especially for Ag-based compounds. It is suggested that the latter results either from a better oxygenation of the surface of the grains or from a migration of silver toward the surface.     

Growth and spectral properties of Nd:GdVO4 laser crystal

In this paper, the Czochralski growth, absorption spectra, and photoluminescence spectra of Nd:GdVO₄ crystals are studied. From its absorption spectra, Nd:GdVO₄ is found to exhibit an anisotropic optical absorption effect, and its effective Judd-Ofelt parameters are calculated: Ω₂=10.281×10⁻²⁰ cm², Ω₄=5.426×10⁻²⁰ cm² and Ω₆=9.943×10⁻²⁰ cm². By these parameters, the absorption oscillator strengths, emission oscillator strengths, transition probabilities, fluorescence branch ratios, energy lifetimes, and integrated emission cross-sections are also derived. The photoluminescence spectra of Nd:GdVO₄ crystal consist of a wide emission band of host and the characteristic emission bands of Nd³⁺. Based on the excitation spectrum, both the two evident peaks locating at 345 and 371 nm are ascribed to the characteristic excitation of Nd³⁺, and an energy transfer from the host to its doping Nd³⁺ ions is indicated.     

Defect formation and transport in mixed-conducting La0.90Sr0.10Al0.85−xFexMg0.15O3−δ

The redox behavior of perovskite-type La_0.90Sr_0.10Al_0.85−xFe_xMg_0.15O_3−δ (x=0.20-0.40) mixed conductors was analyzed by the Mössbauer spectroscopy and measurements of the total conductivity and Seebeck coefficient in the oxygen partial pressure range from 10⁻²⁰ to 0.5 atm at 1023-1223 K. The results combined with oxygen-ion transference numbers determined by the faradaic efficiency technique in air, were used to calculate defect concentrations, mobilities, and partial ionic and p- and n-type electronic conductivities as a function of oxygen pressure. The redox and transport processes can be adequately described in terms of oxygen intercalation and iron disproportionation reactions, with the thermodynamic functions independent of defect concentrations. No essential delocalization of the electronic charge carriers was found. The oxygen non-stoichiometry values estimated from the conductivity vs. p(O₂) dependencies, coincide with those evaluated from the Mössbauer spectra.     

Dielectric properties of valence compensated Ca1−xBixTi1−xCrxO3 perovskite prepared using the sol-gel process

Ca_1−xBi_xNb_1−xCr_xO₃ (x=0.01-0.5) ceramic powders were synthesized using the sol-gel process. The single-phase solids can be presented at x=0.01 and 0.03. The coexistence of orthorhombic perovskite and the secondary phase of BiCrO₃ was verified, as presented for x=0.05-0.5. Grains with a micro-cube topography were obtained for x=0.3-0.5. The average grain size is about 0.4 and 1.1 μm for x=0.3 and 0.5, respectively. The highest dielectric constant peak was measured at around 55 °C for x=0.5 and at 75 °C for x=0.3. The high dielectric constant was caused by the formation of barrier layers at the interface of the bi-phase mixed ceramics. Space charge polarization contributed to the observed behavior.     

Spectral properties of Nd:Ca2Nb2O7 crystal

This paper reports the spectral properties of Nd³⁺:Ca₂Nb₂O₇. The spectral parameters of Nd³⁺ in Nd³⁺:Ca₂Nb₂O₇ crystal have been investigated based on Judd-Ofelt theory. The spectral parameters were obtained. The parameters of line strengths Ω_λ are Ω₂=4.967×10⁻²⁰ cm², Ω₄=5.431×10⁻²⁰ cm², Ω₆=5.693×10⁻²⁰ cm². The radiative lifetime, the fluorescence lifetime and the quantum efficiency are 122 μs, 103 μs and 84.4%, respectively. The fluorescence branch ratios calculated: β₁=0.425, β₂=0.479, β₃=0.091, β₄=0.004. The emission cross section at 1068 nm is 6.204×10⁻²⁰ cm².     

Tailoring mixed proton-electronic conductivity of BaZrO3 by Y and Pr co-doping for cathode application in protonic SOFCs

BaZr_0.8 − xPr_xY_0.2O_3 − δ (BZPYx, 0.1 ≤ x ≤ 0.4) perovskite oxides were investigated for application as cathode materials for intermediate temperature solid oxide fuel cells based on proton conducting electrolytes (protonic-SOFCs). The BZPYx reactivity with CO₂ and water vapor was evaluated by thermogravimetric and X-ray diffraction analyses, and good chemical stability was observed for each BZPYx composition. Conductivity measurements of BZPYx sintered pellets were performed as a function of temperature and p_O2 in humidified atmospheres, corresponding to cathode operating condition in protonic-SOFCs. Different conductivity values and activation energies were measured depending on the Pr content, suggesting the presence of different charge carriers. For all the compositions, the partial electronic conductivity, calculated from conductivity measurements at different p_O2, increased with increasing the temperature from 500 to 700 °C. Furthermore, the larger the Pr content, the larger the electronic conductivity. BaZr_0.7Pr_0.1Y_0.2O_3 − δ and BaZr_0.4Pr_0.4Y_0.2O_3 − δ showed mostly pure proton and electron conductivity, respectively, whereas the intermediate compositions showed mixed proton/electronic conductivity. Among the two mixed proton/electronic conductors, BaZr_0.6Pr_0.3Y_0.2O_3 − δ presented the larger conductivity, which coupled with its good chemical stability, makes this perovskite oxide a candidate cathode materials for protonic-SOFCs.