Magnetic and transport properties of SmCoAsO1−xFx

A series of SmCoAsO_1−xF_x (with x=0, 0.05, 0.1, and 0.2) samples have been prepared by solid state reactions. X-ray powder diffraction proved that all samples can be indexed as a tetragonal ZrCuSiAs-type structure. A clear shrinkage of the lattice constants a and c with increasing F content indicated that F has been doped into the lattice. The magnetic and transport properties of the samples have been investigated. Parent SmCoAsO compound exhibited complicated magnetism including antiferromagnetism, ferromagnetism, and ferrimagnetism. For the fluorine doped samples, the antiferromagnetic Néel temperatures were almost independent of the F content and metamagnetic transitions were observed below antiferromagnetic Néel temperatures. With increasing F content, high temperature (below 142 K) ferrimagnetic state gradually changed to ferromagnetic state. In the resistivity result, metallic conduction in the region of 2-300 K and Fermi liquid behavior at low temperatures were shown in all samples. Transport properties at applied magnetic fields showed anomalies at low temperatures.     

Magnetic properties for the Cu2MnSnSe4 and Cu2FeSnSe4 compounds

Magnetic susceptibility χ measurements in the range from 2 to 300 K were carried out on samples of the Cu₂FeSnSe₄ and Cu₂MnSnSe₄ compounds. It was found that Cu₂FeSnSe₄ was antiferromagnetic showing ideal Curie-Weiss behavior with a Néel temperature T_N of about 19 K and Curie-Weiss temperature θ=−200 K, while for Cu₂MnSnSe₄ the behavior was spin-glass with a freezing temperature T_f of about 22 K and Curie-Weiss temperature θ=−25 K. The spin-glass order parameter q(T), determined from the susceptibility data, was found to be in agreement with the prediction of conventional spin-glass theory.     

Kondo behaviour of the solid solution (Ce1−xLax)PtGa

The solid solution (Ce_1−xLa_x)PtGa has been studied through X-ray diffraction, magnetization (σ(B)), magnetic susceptibility (χ(T)), electrical resistivity (ρ(T)), magnetoresistivity (MR) and heat capacity (C_P(T)) measurements. The Néel temperature (T_N=3.3 K) for CePtGa is lowered upon La substitution as observed from χ(T) and ρ(T) measurements. The Kondo temperature T_K as calculated from MR measurements is comparable to T_N and also decreases with La substitution. The volume dependence of T_K is in accordance with the compressible Kondo lattice model and a Doniach diagram of the results is presented. C_P(T) measurements are presented for CePtGa, Ce_0.2La_0.8PtGa and LaPtGa and the results are discussed in terms of the electronic and magnetic properties. Other features of interest are anomalies in ρ(T) and C_P(T) due to crystalline electric field effects and metamagnetism as observed in σ(B) studies for samples with 0≤x≤ 0.3.     

High field ESR measurements of spin gap system MCu2(PO4)2

Submillimeter and millimeter wave ESR measurements of spin gap systems SrCu₂(PO₄)₂ and PbCu₂(PO₄)₂, which have four kinds of dimers, have been performed to investigate the magnetic properties of spin gap systems using the pulsed magnetic field up to 35T. The observed ESR spectra of powder sample SrCu₂(PO₄)₂ show sharp and single peak in the temperature range from 4.2 to 80 K. The anisotropy of the g-values turned out to be very small compared to the usual anisotropic powder spectra of copper compounds. The dynamical properties will be discussed from the temperature dependence measurements.     

Local order and structural transitions in the molecule-based layer ferrimagnet (n-C4H9)4N FeFe(C2O4)3

Local structural order and temperature-dependent structural variation have been studied in the molecular-based layer ferrimagnet (n-C₄H₉)₄N Fe^IIFe^III(C₂O₄)₃ by EXAFS and high resolution X-ray powder diffraction. The EXAFS spectra measured at the Fe K-edge are successfully modelled by successive O, C, O and metal shells, showing that even when there is extensive structural disorder due to stacking faults, the local structural order in this class of ferrimagnets is fully retained. In this salt, which shows remarkable negative magnetisation at low temperature (Néel class Q), the EXAFS Debye-Waller factor has a discontinuity at 40 K, corresponding to one found in the magnetisation. At the same temperature there is also a change in the expansion of the lattice as evidenced by the high resolution X-ray powder diffraction.     

Dependence of Néel temperature on the particle size of MnFe2O4

Mn-ferrite nanoparticles having diameter in the range 17-45 nm were synthesized by modified co-precipitation method using metal nitrate solutions. Different concentrations of NaOH were found to affect the growth of particle size. Néel temperature (T_N) was found to increase with increasing particle size. The obtained Néel temperature was higher than that of the bulk. The shift in the Néel temperature is described by the finite size-scaling theory [T_N(d)−T_N(bulk)]/T_N(bulk)=(d/d₀)^−1/v, where d is particle size, v=0.6±0.1 and d₀=1.7±0.1 nm.     

Mössbauer study of CoFeRhO4

CoFeRhO₄ has been studied by Mössbauer spectroscopy and X-ray diffraction. The crystal is found to have a cubic spinel structure with the lattice constant a₀=8.451±0.005 Å. The iron ions are in ferric states. The temperature dependence of the magnetic hyperfine field is analyzed by the Néel theory of ferrimagnetism. The intersublattice superexchange interaction is antiferromagnetic and strong with a strength of J_AB=−12.39k_B while the intrasublattice superexchange interactions are weak with strengths of J_AA=−4.96k_B and J_BB=6.20k_B. As the temperature increases toward the Néel temperature T_N, a systematic line broadening effect in the Mössbauer spectrum is observed and interpreted to originate from different temperature dependences of the magnetic hyperfine fields at various iron sites.     

Proton NMR study of α-MnH0.06

Proton nuclear magnetic resonance (NMR) spectra and spin-lattice relaxation rates for the solid solution α-MnH_0.06 have been measured over the temperature range 11-297 K and the resonance frequency range 20-90 MHz. A considerable shift and broadening of the proton NMR line and a sharp peak of the spin-lattice relaxation rate are observed near 130 K. These effects are attributed to the onset of antiferromagnetic ordering below the Néel temperature T_N≈130 K. The proton NMR line does not disappear in the antiferromagnetic phase; this suggests a small magnitude of the local magnetic fields at H-sites in α-MnH_0.06. The spin-lattice relaxation rate in the paramagnetic phase is dominated by the effects of spin fluctuations.     

Spin-glass-like behavior in ZnxCryAlzSe4

The magnetic and electrical properties of the Al-doped polycrystalline spinels Zn_xCr_yAl_zSe₄ (0.13≤z≤0.55) with the antiferromagnetic (AFM) order and semiconducting behavior were investigated. A complex antiferromagnetic structure below a Néel temperature T_N≈23 K for the samples with z up to 0.4 contrasting with the strong ferromagnetic (FM) interactions evidenced by a large positive Curie-Weiss temperature θ_CW decreasing from 62.2 K for z=0.13 to 37.5 K for z=0.55 was observed. Detailed investigations revealed a divergence between the zero-field-cooling (ZFC) and field-cooling (FC) susceptibilities at temperature less than T_N suggesting bond frustration due to competing ferromagnetic and antiferromagnetic exchange interactions in the compositional range 0.13≤z≤0.4. Meanwhile, for z=0.55 a spin-glass-like behavior of cluster type with randomly oriented magnetic moments is observed as the ZFC-FC splitting goes up to the freezing temperature T_f=11.5 K and the critical fields connected both with a transformation of the antiferromagnetic spin spiral via conical magnetic structure into ferromagnetic phase disappear.     

Magnetic properties and magnetic structures of Sr3−xCaxRu2O7

We have measured magnetization curves and powder neutron diffraction of double-layered Ruddlesden-Popper type ruthenate Sr_3−xCa_xRu₂O₇ (x=1.5, 2.0 and 3.0). The field dependence of the magnetization revealed that the transition field of metamagnetic transition along the b-axis shifted to lower fields and that the transition became broad with increasing Sr content. The slope of the magnetization curve also increased with increasing Sr content below the metamagnetic transition. These results indicate that an itinerant component is partly introduced by the Sr substitution. From the magnetic reflection, on cooling below T_N, an additional reflection was observed at (0 0 1) for each x, and the amplitude increased with decreasing temperature. The observed diffraction patterns are very similar to those of Ca₃Ru₂O₇. We conclude that the magnetic structure of the antiferromagnetic ordered phase is basically the same structure with that of Ca₃Ru₂O₇.     

Hopping conductivity of Ni-doped p-CdSb in strong magnetic fields

Magnetoresistance (MR) of oriented single crystals of the anisotropic semiconductor p-CdSb doped with 2 at% of Ni is investigated between T=1.5 and 300 K in transversal pulsed magnetic fields up to B=30 T. In fields B∼4-15 T at T below 4.2 K, the resistivity obeys the law ln ρ∼η[B?(B)]^1/2 with ?(B)=a(0)/a(B), where a is the carrier localization radius and parameter η depends on a(0), on the acceptor concentration N_A and on the direction of the magnetic field with respect to the crystallographic axes, but does not depend on T. Such behavior gives evidence for MR realized by hopping charge transfer over the nearest-neighbor sites in strong magnetic field. The analysis of the experimental data yields the values of η, agreeing with calculated ones within an error of 10%, taking into account the effects of the anisotropy of the acceptor states and of the explicit dependence of a(B) due to the increase in the activation energy of shallow acceptors in magnetic field and the sensitivity of the metal-insulator transition to B.     

Spin-glass-like behaviour and magnetic order in Mn[Cr0.5Ga1.5]S4 spinels

Magnetization and susceptibility were investigated as a function of temperature and magnetic field in polycrystalline Mn[Cr_0.5Ga_1.5]S₄ spinel. The dc susceptibility measurements at 919 Oe showed a disordered ferrimagnetic behaviour with a Curie-Weiss temperature θ_CW=−55 K and an effective magnetic moment of 5.96 μ_B close to the spin-only value of 6.52 μ_B for Cr³⁺ and Mn²⁺ ions in the 3d³ and 3d⁵ configurations, respectively. The magnetization measured at 100 Oe revealed the multiple magnetic transitions with a sharp maximum at the Néel temperature T_N=3.9 K, a minimum at the Yafet-Kittel temperature T_YK=5 K, a broad maximum at the freezing temperature T_f=7.9 K, and an inflection point at the Curie temperature T_C=48 K indicating a transition to paramagnetic phase. A large splitting between the zero-field-cooled (ZFC) and field-cooled (FC) magnetizations at a temperature smaller than T_C suggests the presence of spin-glass-like behaviour. This behaviour is considered in a framework of competing interactions between the antiferromagnetic ordering of the A(Mn) sublattice and the ferromagnetic ordering of the B(Cr) sublattice.     

Impurity-induced magnetic order in the mixture of two spin gap systems (CH3)2CHNH3CuCl3 and (CH3)2CHNH3CuBr3

The ground state of the solid solution of the two spin gap systems (CH₃)₂CHNH₃CuCl₃ and (CH₃)₂CHNH₃CuBr₃ has been investigated by ¹H NMR. The existence of a magnetic ordering in the sample with the Cl-content x=0.85 was clearly demonstrated by a drastic splitting in a resonance line at low temperatures below T_N=13.5 K. The observed NMR spectra in the ordered state was qualitatively consistent with the simple antiferromagnetic state.     

Antiferromagnetic phase transition in garnet-type AgCa2Co2V3O12 and AgCa2Ni2V3O12

Antiferromagnetic phase transition in two vanadium garnets AgCa₂Co₂V₃O₁₂ and AgCa₂Ni₂V₃O₁₂ has been found and investigated extensively. The heat capacity exhibits sharp peak due to the antiferromagnetic order with the Néel temperature T_N=6.39 K for AgCa₂Co₂V₃O₁₂ and 7.21 K for AgCa₂Ni₂V₃O₁₂, respectively. The magnetic susceptibilities exhibit broad maximum, and these T_N correspond to the inflection points of the magnetic susceptibility χ a little lower than T(χ_max). The magnetic entropy changes from zero to 20 K per mol Co²⁺ and Ni²⁺ ions are 5.31 J K⁻¹ mol-Co²⁺-ion⁻¹ and 6.85 J K⁻¹ mol-Ni²⁺-ion⁻¹, indicating S=1/2 for Co²⁺ ion and S=1 for Ni²⁺ ion. The magnetic susceptibility of AgCa₂Ni₂V₃O₁₂ shows the Curie-Weiss behavior between 20 and 350 K with the effective magnetic moment μ_eff=3.23 μ_B Ni²⁺-ion⁻¹ and the Weiss constant θ=−16.4 K (antiferromagnetic sign). Nevertheless, the simple Curie-Weiss law cannot be applicable for AgCa₂Co₂V₃O₁₂. The complex temperature dependence of magnetic susceptibility has been interpreted within the framework of Tanabe-Sugano energy diagram, which is analyzed on the basis of crystalline electric field. The ground state is the spin doublet state ²E(t₂⁶e) and the first excited state is spin quartet state ⁴T₁(t₂⁵e²) which locates extremely close to the ground state. The low spin state S=1/2 for Co²⁺ ion is verified experimentally at least below 20 K which is in agreement with the result of the heat capacity.     

Strong dependence of ferrimagnetic properties on Na concentration in Na-K alloy clusters incorporated in low-silica X zeolite

Na concentration (x) dependence of ferrimagnetic properties is investigated for Na-K alloy clusters incorporated in low-silica X (LSX) zeolite. In the LSX zeolite, β-cages of inner diameter ≈7 Å are arranged in a diamond structure, and supercages of inner diameter ≈13 Å are formed among them. The used LSX zeolite contains xNa⁺ and (12−x)K⁺ cations per β-cage or supercage. Guest nK atoms are loaded into the zeolite, namely the loading density is given by n per β-cage. The samples at x=4 have been reported to show Néel’s N-type ferrimagnetism in the specific region of n. This ferrimagnetism is explained by the model of antiferromagnetic coupling between two non-equivalent magnetic sublattices of clusters, the ones in β-cages and the others in supercages. In the present study, the value of x is changed from 4 to 0. Ferrimagnetic properties are found to show strong x-dependence. A systematic increase in loading densities of ferrimagnetic region is clearly observed with decreasing x. A remarkable change in temperature dependence of spontaneous magnetization is observed depending on x. Na⁺ cations are known to be mainly distributed in β-cages. Hence, the decrease in Na concentration is proposed to change the electronic potential depth for clusters in β-cage, which leads to important differences in the interaction between electrons localized in β-cages and those in supercages.     

Magnetic properties of compounds in the system CaBaCo4−x−yZnxAlyO7 (x=0,1,2, y=0,1)

The magnetic properties of four compounds in the series CaBaCo_4−x−yZn_xAl_yO₇ (x=0,1,2, y=0,1) were investigated. Using AC-susceptibility and DC-magnetometry, magnetic transitions (T_fs) were found for all four compositions in the range 50-3 K. The data from the AC measurements proved to be frequency dependent: T_f increases with higher frequencies. An energy-loss in the magnetic coupling, indicated as contributions in the imaginary part of the magnetic susceptibility (χ″), was seen for every compound and its maximum appeared just below the maximum χ′. Modelling the data with Arrhenius-, Vogel-Fulcher-, and the power-law made it possible to relate the four compounds to spin-glass materials. The Casimir-du Pré relation was used to extract average relaxation times at T_f. The DC magnetisations clearly show differences between field-cooled and zero-field-cooled measurements. None of the compounds exhibit any metamagnetic properties up to 8 T. A new method is presented to calculate the saturation fields using DC data. Relaxation measurements on three compounds indicate that the systems relax very fast, in contrast to spin-glasses. Aging does not affect the fast relaxations. The compounds are interpreted as disordered anti-ferromagnets with spin-glass features.     

Electrical and magnetic properties of TmCoIn5 and YbCoIn5 single crystals

Electrical and magnetic properties of TmCoIn₅ and YbCoIn₅ single crystals were investigated by means of electrical resistivity and magnetization measurements in the temperature range from 300 to 0.5 K under the magnetic field up to 5 T. TmCoIn₅ is an antiferromagnetic metal with a Néel temperature T_N=2.6 K. YbCoIn₅ shows non-magnetic behavior, reflecting of divalent Yb ion.     

Magnetism of ErNi2B2C investigated with a two-ion model for rare-earth antiferromagnets

A two-ion model for rare-earth antiferromagnets was employed in the present work to study the magnetic and thermodynamic properties of ErNi₂B₂C, and derive an analytic formula for the Néel temperature of the compound with the quantum perturbation theory. To apply the theory, four new base functions had to be composed due to the special forms of its crystal-field (CF) wavefunctions. Our theoretical analysis suggested that the magnetic behavior of the compound be governed by these low-lying CF levels in the temperature region at least up to 100 K.     

Li- and V-NMR study of LiVS2

⁷Li- and ⁵¹V-NMR have been measured to make clear the electronic state in a two-dimensional triangular lattice LiVS₂. Knight shift of both ⁷Li- and ⁵¹V-NMR is almost independent of temperature below the phase transition temperature T_c of about 310 K from the paramagnetic state to non-magnetic state. The ⁵¹V- spin-lattice relaxation rate 1/T₁ reveals an exponential temperature dependence below T_c, indicating a gap structure of electronic state. These results are consistent with a non-magnetic state with a trimer singlet of V³⁺ spins below T_c.     

Electron hopping mechanism in hematite (α-Fe2O3)

The frequency dependence of the real (?′) and imaginary (?″) parts of the dielectric constant of polycrystalline hematite (α-Fe₂O₃) has been investigated in the frequency range 0-100 kHz and the temperature range 190-350 K, in order to reveal experimentally the electron hopping mechanism that takes place during the Morin transition of spin-flip process. The dielectric behaviour is described well by the Debye-type relaxation (α-dispersion) in the temperature regions T<233 K and T>338 K. In the intermediate temperature range 233 K<T<338 K a charge carrier mechanism takes place (electron jump from the O²⁻ ion into one of the magnetic ions Fe³⁺) which gives rise to the low frequency conductivity and to the Ω-dispersion. The temperature dependence of relaxation time (τ) in the −ln τ vs 10³/T plot shows two linear regions. In the first, T<238 K, τ increases with increasing T implying a negative activation energy −0.01 eV, and in the second region T>318 K τ decreases as the temperature increases implying a positive activation energy 0.12 eV. The total reorganization energy (0.12-0.01) 0.11 eV is in agreement with the adiabatic activation energy 0.11 eV given by an ab initio model in the literature. The temperature dependence of the phase shift in the frequencies 1, 5, 10 kHz applied shows clearly an average Morin temperature T_Mo=284±1 K that is higher than the value of 263 K corresponding to a single crystal due to the size and shape of material grains.