Blue‐light‐emitting polyfluorene functionalized with triphenylamine and cyanophenylfluorene bipolar side chains

A new bipolar conjugated polyfluorene copolymer with triphenylamine and cyanophenylfluorene as side chains, poly{[9,9‐di(triphenylamine)fluorene]‐[9,9‐dihexyl‐fluorene]‐[2,7‐bis(4′‐cyanophenyl)‐9,9′‐spirobifluorene]} ( PTHCF ), was synthesized for studying the polymer backbone emission. Its absolute weight‐average molecular weight was determined as 4.85 × 10⁴ by using gel permeation chromatography with a multiangle light scattering detector. In contrast to the electronic absorption spectrum in dilute solution, the absorbance of PTHCF in thin film was slightly blue shifted. By comparison of the solution and thin‐film photoluminescence (PL) spectra, a red shift of Δλ = 8–9 nm was observed in the thin‐film PL spectrum. The HOMO and LUMO energy levels of the resulting polymer were electrochemically estimated as ?5.68 and ?2.80 eV, respectively. Under the electric‐field intensity of 4.8 × 10⁵ V cm^?1, the obtained hole and electron mobilities were 2.41 × 10^?4 and 1.40 × 10^?4 cm² V^?1 s^?1, respectively. An electroluminescence device with configuration of ITO/PEDOT:PSS/ PTHCF _70%+PBD_30%/CsF/Ca/Al exhibited a deep‐blue emission as a result of excitons formed by the charges migrating along the full‐fluorene main chain. The incorporation of the bipolar side chains into the polymer structure prevented the intermolecular interaction of the fluorene moieties, balance charge injection/transport, and thereby improve the polymer backbone emission. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

Two‐photon excitation and optical limiting in polyfluorene derivatives

Fluorene‐based polymers are widely known materials due to a combination of features such as photoluminescence and electroluminescence, oxidative stability, and film‐forming ability. However, studies reporting nonlinear optical properties in this class of conjugated polymer are scarce. Here, we report a new class of polyfluorene derivatives poly(9,9′‐n‐dihexyl‐2,7‐fluorenedilvinylene‐alt‐1,4‐phenylenevinylene), poly(9,9′‐n‐dihexyl‐2,7‐fluorenedilvinylene‐alt‐2,5‐thiophene), and poly[(9,9‐di‐hexylfluorenediylvinylene‐alt‐1,4‐phenylenevinylene)‐co‐((9,9′‐(3‐t‐butylpropanoate) fluorene‐1,4‐phenylene)] displaying high two‐photon absorption (2PA) in the spectral range from a 490 to 1100 nm. The 2PA cross‐section peak values for these materials are as high as 3000 Göppert Mayer (1 GM = 1 × 10^?50 cm⁴ s/photon), which is related to the high degree of conjugation along the polymer backbone. The polymers that were used in this study presented a strong two‐photon luminescence and also displayed optical limiting behavior, which, in combination with their well‐established properties, make them highly suitable for nonlinear optical devices. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 50: 148–153, 2012     

Synthesis and property of polyoxazolidone having fluorene moiety by polyaddition of diisocyanate and diepoxide

Polyoxazolidones having fluorenyl group were synthesized by polyaddition of 9,9‐diglycidyl fluorene with various diisocyanates. The polymer from 9,9‐diglycidyl fluorene and methylenediphenyl 4,4′‐diisocyanate was afforded in high yield although polydispersity of the polymer was found relatively broad. The IR spectrum of the obtained polymer showed two absorption in carbonyl region. One of them was assigned to the expected oxazolidone, while the other at 1710 cm^?1 appeared due to a carbonyl group of the isocyanurate moieties produced by cyclotrimerization of isocyanate. It is assumed that the cyclotrimerization would cause the broad polydispersity caused by the branched structure formed by isocyanurate. The polymers obtained with three kinds of diisocyanates (methylenediphenyl 4,4'‐diisocyanate, 1,6‐hexamethylene diisocyanate, 1,4‐phenylene diisocyanate) showed high thermal stability, as their T_d10 was depended on the structure of diisocyanate. All polymers had high transparency in a visible region. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1755–1760     

Synthesis and properties of new fluorene‐based polyquinoxalines with an ether linkage in the main chain for light‐emitting diodes

A new series of fluorene‐based polyquinoxalines with an ether linkage in the main chain were prepared by the polycondensation reaction between a tetraketone monomer and 3,3′,4,4′‐tetraaminodiphenyl ether. The polycondensation was usually carried out in m‐cresol. The resulting polymers ( P1 – P3 ) [ P1 = poly(quinoxaline‐co‐9,9‐dihexyl‐2,7‐dimethyl‐9H‐fluorene) P2 = poly(quioxaline‐co‐9,9‐dihexyl‐9‐pentyl‐2,7‐di‐p‐tolyl‐9H‐fluorene) P3 = poly(quioxaline‐co‐9,9‐bis‐(4‐methoxy‐phenyl)‐2,7‐dimethyl‐9H‐fluorene)] showed good solubility in common organic solvents and high thermal stability with only a 5% weight loss up to 440 °C. P1 and P2 had very high glass‐transition temperatures of 212 and 223 °C, respectively, whereas P3 did not show any phase‐transition temperature in repeated scans up to 300 °C. All the polymers in photoluminescence showed blue emissions in the range of 432–465 nm, both in chloroform solutions and in thin films. Light‐emitting diode devices of the configuration indium tin oxide/poly(3,4‐ethylenedioxythiophene)/polymer:poly(N‐vinylcarbazole) blend (2:8)/LiF/Al were fabricated with P1 or P2 and emitted blue light with electroluminescence peak wavelengths of 434 and 448 nm, respectively. The maximum brightness and the external quantum efficiency of P1 were 0.56 μW/cm² at 29 V and 0.056%, whereas P2 showed 0.50 μW/cm² at 34 V and a relatively low value of 0.015%, respectively. Cyclic voltammetry studies revealed that these polymers possessed low‐lying ionization potential energy levels ranging from ?5.49 to ?5.86 eV and low‐lying electron affinity energy levels ranging from ?2.65 to ?2.88 eV. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 1189–1198, 2006     

Optical and electronic properties of fluorene‐based copolymers and their sensory applications

A series of novel, fluorene‐based conjugated copolymers, poly[(9,9‐bis{propenyl}‐9H‐fluorene)‐co‐(9,9‐dihexyl‐9H‐fluorene)] ( P1 ), poly[(9,9‐bis{carboxymethylsulfonyl‐propyl}fluorenyl‐2,7‐diyl)‐co‐(9,9‐dihexyl‐9H‐fluorene)] ( P2 ) and poly[(9,9‐dihexylfluorene)‐co‐alt‐(9,9‐bis‐(6‐azidohexyl)fluorene)] ( P3 ), are synthesized by Suzuki coupling reactions and their electrochemical properties, in the form of films, are investigated using cyclic voltammetry. The results reveal that the polymer films exhibit electrochromic properties with a pseudo‐reversible redox behavior; transparent in the neutral state and dark violet in the oxidized state. Among the three polymers, P2 possesses the shortest response time and the highest coloration efficiency value. These polymers emit blue light with a band gap value of around 2.9 eV and have high fluorescent quantum yields. Their metal ion sensory abilities are also investigated by titrating them with a number of different transition metal ions; all of these polymers exhibit a higher selectivity toward Fe³⁺ ions than the other ions tested with Stern–Volmer constants of 4.41 × 10⁶M^?1, 3.28 × 10⁷M^?1, 1.25 × 10⁶M^?1, and 6.56 × 10⁶M^?1 for P1 , P2 , water soluble version of P2 ( P2S ) and P3 , respectively. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Synthesis of 9,9‐bis(4‐aminophenyl)fluorene‐based benzoxazine and properties of its high‐performance thermoset

A benzoxazine ( P‐bapf ) based on 9,9‐bis(4‐aminophenyl)fluorene (BAPF), phenol, and formaldehyde was successfully prepared using two‐pot and one‐pot procedures. In the two‐pot approach, BAPF initially reacted with 2‐hydroxybenzaldehyde, leading to 9,9‐bis(4‐(2‐hydroxybenzylideneimino)phenyl)fluorene. The imine linkages of 9,9‐bis(4‐(2‐hydroxybenzylideneimino)phenyl)fluorene were then reduced by sodium borohydride, forming 9,9‐bis(4‐(2‐hydroxybenzylamino)phenyl)fluorene. Finally, paraformaldehyde was added to induce ring closure condensation, forming benzoxazine ( P‐bapf ). In the one‐pot approach, P‐bapf was obtained directly by reacting BAPF, phenol, and paraformaldehyde in various solvents. Among the solvents, we found that using toluene/ethanol (2/1, v/v) as a solvent leads to the best purity and yield. No gelation was observed in the preparation. The structure of the resulting benzoxazine was confirmed by ¹H, ¹³C, ¹H? ¹H and ¹H? ¹³C NMR spectra. P‐bapf exhibits a photoluminescent emission at 395 nm under an excitation of 275 nm. After curing, the resulting P‐bapf thermoset exhibits T_g as high as 236 °C, and the T_g can be further increased to 260 °C by copolymerization with an equal equivalent of cresol novolac epoxy. The 5% degradation temperature of the P‐bapf thermoset reaches as high as 413 °C (N₂) and 431 °C (air). The refractive index at 589 nm is as high as 1.70, demonstrating a high refractive index characteristic of fluorene linkage. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Enhanced efficiency of polyfluorene derivatives: Organic–inorganic hybrid polymer light‐emitting diodes

Two novel organic–inorganic hybrid polyfluorene derivatives, poly{(9,9′‐dioctyl‐2,7‐fluorene)‐co‐(9,9′‐di‐POSS‐2,7‐fluorene)‐co‐[2,5‐bis(octyloxy)‐1,4‐phenylene]} (PFDOPPOSS) and poly{(9,9′‐dioctyl‐2,7‐fluorene)‐co‐(9,9′‐di‐POSS‐2,7‐fluorene)‐co‐bithiophene} (PFT2POSS), were synthesized by the Pd‐catalyzed Suzuki reaction of polyhedral oligomeric silsesquioxane (POSS) appended fluorene, dioctyl phenylene, and bithiophene moieties. The synthesized polymers were characterized with ¹H NMR spectroscopy and elemental analysis. Photoluminescence (PL) studies showed that the incorporation of the POSS pendant into the polyfluorene derivatives significantly enhanced the fluorescence quantum yields of the polymer films, likely via a reduction in the degree of interchain interaction as well as keto formation. Additionally, the blue‐light‐emitting polyfluorene derivative PFDOPPOSS showed high thermal color stability in PL. Moreover, single‐layer light‐emitting diode devices of an indium tin oxide/poly(3,4‐ethylene dioxythiophene):poly(styrene sulfonate)/polymer/Ca/Al configuration fabricated with PFDOPPOSS and PFT2POSS showed much improved brightness, maximum luminescence intensity, and quantum efficiency in comparison with devices fabricated with the corresponding pristine polymers PFDOP and PFT2. In particular, the maximum external quantum efficiency of PFT2POSS was 0.13%, which was twice that of PFT2 (0.06%), and the maximum current efficiency of PFT2POSS was 0.38 cd/A, which again was twice that of PFT2 (0.19 cd/A). © 2006 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 44: 2943–2954, 2006     

Synthesis and properties of conjugated copolycondensates consisting of carbazole‐2,7‐diyl and fluorene‐2,7‐diyl

Carbazole and fluorene‐based random and alternating copolycondensates were synthesized to develop high‐performance blue light‐emitting polymers by improving electron injection ability of poly(N‐aryl‐2,7‐carbazole)s that showed intense blue electroluminescence (EL) with good hole‐injection and ‐transport ability. These copolycondensates absorbed light energy at about λ_max = 390 nm in CHCl₃ and 400 nm in film state, and fluoresced at about λ_max = 417 nm in CHCl₃ and 430 nm in the thin film state. Energy gaps between highest occupied molecular orbital (HOMO) and lowest unoccupied molecular orbital (LUMO) of them were about 2.9 eV, and the energy levels of LUMO situated lower than that of corresponding polycarbazole. Polymer light‐emitting diode devices having configuration of indium tin oxide/poly(3,4‐ethylenedioxythiophene)‐poly(styrenesulfonate)/polymer/CsF/Al using the copolycondensates, poly(N‐arylcarbazole‐2,7‐diyl), and poly(9,9‐dialkylfluorene‐2,7‐diyl), emitted bluish EL at operating voltages lower than 7 V. The device embedded the random copolycondensate showed notably higher performance with maximum luminance of 31,200 cd m^?2 at 11.0 V, and the current efficiencies observed under operating voltages lower than 7 V were higher than those of the other devices. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

Low thresholds for a nonconventional polymer blend—Amplified spontaneous emission and lasing in F81−x:SYx system

A mixture of two polymer materials, poly (9,9‐dioctylfluorene) (F8), and one of the poly(para‐phenylenevinylene) derivatives, superyellow (SY) have been used to make F8_1?x:SY_x polymer blend system. Under a 3–5 ns pulsed‐laser excitation, this system showed excellent optical properties with low threshold values of ≈14 µJ/cm² and ≈8 µJ/cm² for amplified spontaneous emission and optically pumped lasing, respectively. The proposed system was also electroluminescent and an interesting candidate for future research on polymer injection lasers. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2016 , 54, 15–21     

Molecular orientation of aromatic polycarbonates containing fluorene side chains by polarized infrared spectroscopy and birefringence analysis

The molecular orientation of an aromatic polycarbonate containing fluorene side chains was investigated by polarized infrared spectroscopy and birefringence analyses. The copolymers were synthesized from 2,2‐bis(4‐hydroxyphenyl)propane (BPA), 9,9‐bis(4‐hydroxy‐3‐methylpheny)fluorene (BMPF), and phosgene by interfacial polycondensation. The 1449‐cm^?1 band of the uniaxially oriented films, stretched at the glass‐transition temperature (T_g) plus 5 °C, was assigned to various combinations of CC stretching and CH in‐plane bending vibrations in the fluorene ring, and the transition moment angle was estimated to be 90°. The intrinsic birefringence of aromatic polycarbonate films with BMPF molar ratios ranging from 0.5 to 1 was obtained with the 1449‐cm^?1 band. The copolymer was estimated to show zero intrinsic birefringence at the BMPF molar ratio of 0.75, and the BMPF homopolymer showed negative intrinsic birefringence. A linear relationship between the volume fraction of BMPF units and the intrinsic birefringence indicated that the two monomer units of BPA and BMPF in each copolymer were not independent, and an intrinsic birefringence could be defined even in the copolymer. The sign of the photoelastic coefficient in the homopolymer with BMPF units was positive. The different signs of the photoelastic coefficient and the intrinsic birefringence suggest that the fluorene side‐chain orientation induced by stress in the glass state is quite different from the orientation of the uniaxially oriented films stretched at T_g + 5 °C. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1554–1562, 2003     

Incorporation of different conjugated linkers into low band gap polymers based on 5,6‐Bis(octyloxy)‐2,1,3 benzooxadiazole for tuning optoelectronic properties

Four new 2,1,3‐benzooxadiazole‐based donor–acceptor conjugated polymers, namely poly{9‐(9‐heptadecanyl)‐9H‐carbazole‐alt‐5,6‐bis(octyloxy)‐4,7‐di(selenophen‐2‐yl)benzo[c][1,2,5]oxadiazole)}(PSBSC), poly{9‐(9‐heptadecanyl)‐9H‐carbazole‐alt‐5,6‐bis(octyloxy)‐4,7‐di(furan‐2‐yl)benzo[c][1,2,5]oxadiazole)}(PFBFC), poly{9,9‐dioctyl‐9H‐fluorene‐alt‐5,6‐bis(octyloxy)‐4,7‐di(selenophen‐2‐yl)benzo[c][1,2,5]oxadiazole)}(PSBSFL), and poly{9,9‐dioctyl‐9H‐fluorene‐alt‐5,6‐bis(octyloxy)‐4,7‐di(furan‐2‐yl)benzo[c][1,2,5]oxadiazole)}(PFBFFL), were synthesized via Stille polycondensation reaction. All polymers were found to be soluble in common organic solvents such as chloroform, tetrahydrofuran, and chlorobenzene. Their structures were verified by ¹H‐NMR and the molecular weights were determined by gel permeation chromatography (GPC). The polymer films exhibited broad absorption bands. Among all polymers, photovoltaic cells based on the device structure of ITO/PEDOT:PSS/PSBSC:PC₇₁BM(1:3, w/w)/LiF/Al revealed an open‐circuit voltage of 0.62 V, a short circuit current of 7.63 mA cm^?2 and a power conversion efficiency of 1.89%. This work demonstrates a good example for tuning absorption range, energy level, and photovoltaic properties of the polymers with different spacers and donor units can offer a simple and effective method to improve the efficiency of PSCs. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 2459–2467     

A novel photo‐acid generator bound molecular glass resist with a single protecting group

A novel photo‐acid generator (PAG) bound molecular glass photoresist with a single protecting group has been developed as a promising resist material for use in microelectronics. This single component molecular resist was prepared in four steps starting from 9,9‐bis(4‐hydroxyphenyl)fluorene. The single component molecular resist exhibited good thermal properties, such as a 10% weight loss temperature of 200 °C and a glass transition temperature of 91 °C. This resist showed a good sensitivity of 60 μC/cm² with e‐beam exposure (50 keV). On the other hand, the fine pattern with a half‐pitch of 50 nm in the presence of 4 wt % quencher, trioctylamine, was obtained using electron‐beam (100 keV) lithography. The LER value was 8.2 nm (3σ, 60 nm half‐pitch patterns). © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Synthesis and characterization of indenofluorene‐based copolymers containing 2,5‐bis(2‐thienyl)‐N‐arylpyrrole for bulk heterojunction solar cells and polymer light‐emitting diodes

Two novel alternating π‐conjugated copolymers, poly[2,8‐(6,6′,12,12′‐tetraoctyl‐6,12‐dihydroindeno‐[1,2b]fluorene‐ alt‐5(1‐(2,6‐diisopropylphenyl)‐2,5‐di(2‐thienyl)pyrrole) ( P1 ) and poly[2,8‐(6,6′,12,12′‐tetraoctyl‐6,12‐dihydroindeno‐[1,2b]fluorene‐ alt‐5(1‐(p‐octylphenyl)‐2,5‐di(2‐thienyl)pyrrole) ( P2 ), were synthesized via the Suzuki coupling method and their optoelectronic properties were investigated. The resulting polymers P1 and P2 were completely soluble in various common organic solvents and their weight‐average molecular weights (M_w) were 5.66 × 10⁴ (polydispersity: 1.97) and 2.13× 10⁴ (polydispersity: 1.54), respectively. Bulk heterojunction (BHJ) solar cells were fabricated in ITO/PEDOT:PSS/polymer:PC₇₀BM(1:5)/TiO_x/Al configurations. The BHJ solar cell with P1 :PC₇₀BM (1:5) has a power conversion efficiency (PCE) of 1.12% (J_sc= 3.39 mA/cm², V_oc= 0.67 V, FF = 49.31%), measured using AM 1.5 G solar simulator at 100 mW/cm² light illumination. We fabricated polymer light‐emitting diodes (PLEDs) in ITO/PEDOT:PSS/emitting polymer:polyethylene glycol (PEG)/Ba/Al configurations. The electroluminescence (EL) maxima of the fabricated PLEDs varied from 526 nm to 556 nm depending on the ratio of the polymer to PEG. The turn‐on voltages of the PLEDs were in the range of 3–8 V depending on the ratio of the polymer to PEG, and the maximum brightness and luminance efficiency were 2103 cd/m² and 0.37 cd/A at 12 V, respectively. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3169–3177, 2010     

Synthesis and characterization of poly(1,4‐bis((E)‐2‐(3‐dodecylthiophen‐2‐yl)vinyl)benzene) derivatives

New amorphous semiconducting copolymers, poly(9,9‐dialkylfluorene)‐alt‐(3‐dodecylthienyl‐divinylbenzene‐3‐dodecylthienyl) derivatives (PEFTVB and POFTVB), were designed, synthesized, and characterized. The structure of copolymers was confirmed by H NMR, IR, and elemental analysis. The copolymers showed very good solubility in organic solvents and high thermal stability with high T_g of 178–185 °C. The weight average molecular weight was found to be 107,900 with polydispersity of 3.14 for PEFTVB and 76,700 with that of 3.31 for POFTVB. UV–vis absorption studies showed the maximum absorption at 428 nm (in solution) and 435 nm (in film) for PEFTVB and at 430 nm (in solution) and 436 nm (in film) for POFTVB. Photoluminescence studies showed the emission at 498 nm (in solution) and 557 nm (in film) for PEFTVB and at 498 nm (in solution) and 536 nm (in film) for POFTVB. The solution‐processed thin‐film transistors showed the carrier mobility of 2 × 10^?4 cm² V^?1 s^?1 for PEFTVB‐based devices and 2 × 10^?5 cm² V^?1 s^?1 for POFTVB‐based devices. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 3942–3949, 2010     

Poly(thienylene‐vinylene‐thienylene) with cyano substituent: Synthesis and application in field‐effect transistor and polymer solar cell

A novel conjugated polymer, poly(thienylene‐vinylene‐thienylene) with cyano substituent ( CN‐PTVT ) was synthesized via Stille coupling for the application in air stable field‐effect transistor and polymer solar cell. The polymer was characterized by ¹H NMR, elemental analysis, UV‐vis absorption and photoluminescence spectroscopy, TGA, cyclic voltammetry and XRD analysis. CN‐PTVT exhibits a good thermal stability with 5% weight loss at 306 °C. The FET hole mobility of the polymer reached 5.9 × 10^?3 cm² V^?1 s^?1 with I_on/I_off ratio of 4.9 × 10⁴, which is one of the highest performance among the air‐stable amorphous polymers. The polymer solar cell based on CN‐PTVT as donor and PCBM as acceptor shows a relatively high open‐circuit voltage of 0.82 V and a power conversion efficiency of 0.3% under the illumination of AM1.5, 100 mW/cm². © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4028–4036, 2009     

Characterization of two‐ and three‐photon absorption of polyfluorene derivatives

Fluorene‐based polymer derivatives are promising materials for organic electronic devices because of their photoluminescence and electroluminescence, good film‐forming ability, and favorable chemical and thermal properties. Although optical properties of polyfluorene have already been reported, most of the studies focused on the linear optical properties, whereas nonlinear optical characteristics have only recently received more detailed attention. Here, we report on two polyfluorene derivatives, poly(9,9′‐n‐dihexyl‐2,7‐fluorenediyl) (LaPPS 10) and poly(9,9′‐n‐dihexyl‐2,7‐fluorene‐diyl‐vinylene) (LaPPS 38), which present intense nonlinear absorption and fluorescence. Two‐photon absorption cross‐section properties of both polymers were characterized in the spectral range from 500 nm up to 900 nm, reaching peak values around 2000 Göppert Mayer units. Optical limiting behavior and two‐photon‐induced fluorescence of both polymers have also been investigated. Furthermore, the first molecular hyperpolarizability of the polymers was also studied using hyper‐Rayleigh scattering. In addition, the three‐photon absorption (3PA) spectra of both materials were also investigated, and 3PA cross‐section values in the order of 1 × 10^?78 cm⁶ s² photon^?2 were observed. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part B: Polym. Phys. 2014 , 52, 747–754     

Deep‐blue light‐emitting polyfluorenes containing spiro[fluorene‐9,9′‐thioxanthene‐S,S‐dioxide] isomers

Blue light‐emitting polyfluorenes, PPF‐FSOs and PPF‐SOFs were synthesized via introducing spiro[fluorene‐9,9′‐thioxanthene‐S,S‐dioxide] isomers (2,7‐diyl and 2′,7′‐diyl) (FSO/SOF) into the poly[9,9‐bis(4‐(2‐ethylhexyloxy) phenyl)fluorene‐2,7‐diyl] (PPF) backbone, respectively. With the increasing contents of FSO and SOF moieties, the absorption and PL spectra of PPF‐FSOs show slight red shift, while that of PPF‐SOFs exhibit blue shift, respectively. The HOMO and LUMO levels reduce gradually with increasing SOF unit in PPF‐SOFs. The polymers emit blue light peaked around 430–445 nm and show an excellent spectral stability with the variation in current densities. The distinctly narrowing EL spectra were observed with the incorporation of isomers in the polymers. The full width at half maximum reduced by 15 nm for PPF‐SOFs, resulting in a blue shift with the CIE coordinates from (0.16, 0.11) to (0.16, 0.08). With a device configuration of ITO/PEDOT:PSS/EML/CsF/Al, a maximum luminance efficiency (LE_max) of 2.00 cd A^?1, a maximum external quantum efficiency (EQE_max) of 3.76% with the CIE coordinates of (0.16, 0.08) for PPF‐SOF15 and a LE_max of 1.68 cd A^?1, a EQE_max of 2.38% with CIE (0.16, 0.12) for PPF‐FSO10 were obtained, respectively. The result reveals that spiro[fluorene‐9,9′‐thioxanthene‐S,S‐dioxide] isomers are promising blocks for deep‐blue light‐emitting polymers. © 2017 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2017 , 55 , 2332–2341     

Significantly improved photovoltaic performances of the dithiophene‐benzothiadiazole‐alt‐fluorene copolymers by incorporating carbazole units in fluorene moiety

To exploit an effective way to improve polymeric photovoltaic performance, a series of dithiophene‐benzothiadiazole‐alt‐fluorene copolymers containing carbazole groups at C‐9 positions of the alternating fluorene units (PFO‐FCz‐DBT) were synthesized and characterized. The effect of the carbazole groups on the optophysical, electrochemical, and photovoltaic properties of these copolymers was investigated. By comparison, this type of copolymers with carbazole units exhibited significantly improved photovoltaic properties than poly(2,7‐(9,9‐dioctyl‐fluorene)‐alt‐5,5‐(4′,7′‐di‐2‐thienyl‐2′,1′,3′‐benzothiadiazole) (PFO‐DBT) in the bulk heterojunction solar cells. A maximum power‐conversion efficiency (PCE) of 2.41% and a highest short‐circuit current density (J_sc) of 9.68 mA cm^?2 were obtained for the PFO‐FCz‐DBT30, which are about two times higher than the corresponding levels for the PFO‐DBT30. This work demonstrated that introducing a hole‐transporting carbazole unit into copolymer is a simple and effective method to improve the J_sc and PCE. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Enhanced dispersion of nanotubes in organic solvents by donor–acceptor interaction between functionalized poly(phenylacetylene) chains and carbon nanotube walls

Phenylacetylene derivatives containing carbazole ( 1 ) and fluorene ( 2 ) moieties were polymerized by [Rh(nbd)Cl]₂ into corresponding polymers P 1 and P 2 of high molecular weights (M_w ～ 150 × 10³–465 × 10³) in high yields (up to 98%). The polymers were characterized by NMR, IR, UV, PL, and CV techniques. Hybrids of the polymers with multiwalled carbon nanotubes (MWNTs) were prepared by simply mixing the two components in common organic solvents such as dichloromethane. The solvating power of the polymer carrying the electron‐donating carbazolyl pendant (P 1 ) is stronger than that of its counterpart carrying fluorenyl pendant (P 2 ), due to the stronger donor–acceptor (D–A) interaction between the P 1 chains and the MWNT walls. This work clearly manifests that D–A effect plays an important role in the polymer‐aided MWNT dispersion in organic solvents. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 4995–5005, 2009     

Facile electrochemical preparation of poly(9,9‐dichlorofluorene), a new polyfluorene derivative as green light emitter

High‐quality poly(9,9‐dichlorofluorene) (PDCF), a new part soluble polyfluorene derivative, was easily synthesized electrochemically by direct anodic oxidation of 9,9‐dichlorofluorene (DCF) in boron trifluoride diethyl etherate (BFEE) containing 15% (by volume) trifluoroacetic acid (TFA). It was hard for DCF to deposit on the electrode in neutral solvents such as CH₃CN system. This methodology may help promotion of researches to reveal unknown properties and applications of polyfluorene materials. PDCF films with conductivity of 3.3 × 10^?2 S cm^?1 obtained from this media show good redox activity and thermal stability. The structure and morphology of the polymer were studied by UV–vis, FTIR, ¹H NMR spectra, and scanning electron microscopy, respectively. The results of quantum chemistry calculations and the spectroscopies of dedoped PDCF indicate that the polymerization of DCF mainly occurs via C₍₂₎ and C₍₇₎ position. Fluorescent spectral studies indicate that PDCF film with high fluorescence quantum yields and photochemical stability is a novel green light emitter. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 1791–1799, 2010