Boronic Acid Functionalized Core–Shell Polymer Nanoparticles Prepared by Distillation Precipitation Polymerization for Glycopeptide Enrichment

The boronic acid‐functionalized core–shell polymer nanoparticles, poly(N,N‐methylenebisacrylamide‐co‐methacrylic acid)@4‐vinylphenylboronic acid (poly(MBA‐co‐MAA)@VPBA), were successfully synthesized for enriching glycosylated peptides. Such nanoparticles were composed of a hydrophilic polymer core prepared by distillation precipitation polymerization (DPP) and a boronic acid‐functionalized shell designed for capturing glycopeptides. Owing to the relatively large amount of residual vinyl groups introduced by DPP on the core surface, the VPBA monomer was coated with high efficiency, working as the shell. Moreover, the overall polymerization route, especially the use of DPP, made the synthesis of nanoparticles facile and time‐saving. With the poly(MBA‐co‐MAA)@VPBA nanoparticles, 18 glycopeptides from horseradish peroxidase (HRP) digest were captured and identified by MALDI‐TOF mass spectrometric analysis, relative to eight glycopeptides enriched by using commercially available meta‐aminophenylboronic acid agarose under the same conditions. When the concentration of the HRP digest was decreased to as low as 5 nmol, glycopeptides could still be selectively isolated by the prepared nanoparticles. Our results demonstrated that the synthetic poly(MBA‐co‐MAA)@VPBA nanoparticles might be a promising selective enrichment material for glycoproteome analysis.     

Facile Access to Hydroxy‐Functional Core–Shell Microspheres via Grafting of Ethylene Oxide by Anionic Ring‐Opening Polymerization

We present a facile access route to hydroxy‐functional narrow disperse microspheres of well‐defined grafting density (GD). Ethylene oxide has been grafted from highly crosslinked poly(divinyl benzene) microspheres by anionic ring‐opening polymerization using sec‐butyllithium as activator together with the phosphazene base t‐BuP₄. Initially, core microspheres have been prepared by precipitation polymerization utilizing divinyl benzene (DVB, 80 wt.‐%). The grafting of poly(ethylene oxide) (PEO) from the surface resulted in the formation of functional core–shell microspheres with hydroxy‐terminal end groups. The number average particle diameter of the grafted microspheres was 3.6 µm and the particle weight increased by 5.7%. The microspheres were characterized by SEM, FT‐IR spectroscopy, elemental analysis, and fluorescence microscopy. The surface GD (determined via two methods) was 1.65 ± 0.06 and 2.09 ± 0.08 chains · nm⁻², respectively.

     

Synthesis of Well‐Defined Amphiphilic Core–Shell Particles Containing Amine‐Rich Shells

A new route to synthesize amphiphilic core–shell particles that consist of well‐defined hydrophobic polymer cores and poly(vinylamine) (PVAm) shells has been developed. The PVAm was treated with a small amount of tert‐butyl hydroperoxide to generate free radicals that subsequently initiated both graft‐ and homo‐polymerization of vinyl monomer such as n‐butyl acrylate, methyl methacrylate, and styrene. Stable particles in the range from 100 to 250 nm in diameter with very narrow size distributions (polydispersity index between 1.08 and 1.15) were produced in high yields. TEM images of the particles revealed that they had well‐defined core–shell nanostructures with thick and hairy PVAm shells. The structures of the vinyl monomer and water‐soluble polymer were found to strongly influence the formation of particles and their sizes.

     

Highly Conductive Core–Shell Nanocomposite of Poly(N‐vinylcarbazole)–Polypyrrole with Multiwalled Carbon Nanotubes

In this communication, the synthesis, characterization, and properties of highly conductive core–shell nanocomposites of poly(N‐vinylcarbazole) (PNVC)–polypyrrole (PPY) copolymers with multi‐walled carbon nanotubes (MWCNTs) are described. A unique free‐radical coupling reaction between PNVC and PPY cation radicals in chloroform solvent, using feric chloride as an oxidant, in the presence of suspended MWCNTs in the reaction medium, was used for the synthesis of nanocomposite. Field‐emission scanning and transmission electron microscopy studies showed the formation of the core–shell nanocomposite. Raman spectrocopy results as well as thermogravimetric analysis supported the electron microscopic observations. The resulting PNVC–PPY copolymer‐coated MWCNTs showed an unprecedentedly increased value of direct electrical conductivity (bulk) compared to the conductivity of all samples even with pure MWCNTs.

     

A Facile Synthesis of Cu NPs and Ag NPs Coated by PS with Core–Shell Structure by Precipitation Polymerization

Copper nanoparticles (Cu NPs ) coated with polystyrene (PS ) (Cu NPs @PS ) were prepared by precipitation polymerization. First, Cu NPs were prepared by chemical reduction using cupric acetate as precursor, sodium polyacrylate (PAANa ) as stabilizer, and hydrazine hydrate as reducing agent. Then Cu NPs were coated by precipitation polymerization using styrene as monomer, 3‐(trimethoxysilyl) propyl acrylate as co‐monomer, and 2, 2‐azobisisobutyronitrile (AIBN ) as initiator. Ultraviolet–visible (UV –vis) spectroscopy and transmission electron microscopy (TEM ) results showed that stable composite particles could be synthesized by precipitation polymerization. The amount of PAANa had a significant effect on the size of Cu NPs . The addition of more PAANa resulted in smaller Cu NPs . The spherical Cu NPs became nanowires when increasing the stirring rate from 350 to 700 rpm during precipitation polymerization. Ag NPs @PS with core–shell structure were also prepared by this method, which appears to be universal.     

Synthesis of gold–poly(methyl methacrylate) core–shell nanoparticles by surface‐confined atom transfer radical polymerization at elevated temperature

Surface‐confined atom transfer radical polymerization was used to prepare gold nanoparticle–poly(methyl methacrylate) core–shell particles at elevated temperature. First, gold nanoparticles were prepared by the one‐pot borohydride reduction of tetrachloroaurate in the presence of 11‐mercapto‐1‐undecanol (MUD). MUD‐capped gold nanoparticles were then exchanged with 3‐mercaptopropyltrimethoxysilane (MPS) to prepare a self‐assembled monolayer (SAM) of MPS on the gold nanoparticle surfaces and subsequently hydrolyzed with hydrochloric acid. The extent of exchange of MUD with MPS was determined by NMR. The resulting crosslinked silica‐primer layer stabilized the SAM of MPS and was allowed to react with the initiator [(chloromethyl)phenylethyl] trimethoxysilane. Atom transfer radical polymerization was conducted on the Cl‐terminated gold nanoparticles with the CuCl/2,2′‐bipyridyl catalyst system at elevated temperature. The rates of polymerization with the initiator‐modified gold nanoparticles exhibited first‐order kinetics with respect to the monomer, and the number‐average molecular weight of the cleaved graft polymer increased linearly with the monomer conversion. The presence of the polymer on the gold nanoparticle surface was identified by Fourier transform infrared spectroscopy and transmission electron microscopy. © 2005 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 43: 3631–3642, 2005     

Sequential Polymer Precipitation of Core–Shell Microstructured Composites with Giant Permittivity

Polymeric core–shell microstructures have been constructed through a new method, namely sequential precipitation, which is intrinsically a self‐assembly and phase separation process. High‐quality poly(vinyldene fluoride)–polycarbonate–lithium perchlorate composite films with spherical core–shell microstructures have been prepared and determined to consist of conducting cores and insulating shells. Because of the percolation effect, the resulting materials present a dielectric constant as high as 10⁴–10⁷ at the threshold.

     

Magneto‐Optical Studies of HgTe/HgxCd1−xTe(S) Core–Shell Nanocrystals

The synthesis and magneto‐optical properties of HgTe nanocrystals capped with Hg_xCd_1?xTe(S) alloyed shells have been investigated. The magneto‐optical measurements included the use of optically detected magnetic resonance (ODMR) and circular polarized photoluminescence (CP‐PL) spectroscopy. The PL spectra suggest the existence of luminescence events from both the core HgTe and the Hg_xCd_1?xTe(S) shells. The continuous‐wave (cw) and time‐resolved ODMR measurements revealed that the luminescence at the shell regime is associated with a trap‐to‐band recombination emission. The electron trap is comprised of a Cd–Hg mixed site, confirming the existence of an alloyed Hg_xCd_1?xTe(S) composition. The ODMR data and the CP‐PL measurements together revealed the g‐values of the trapped electron and the valence band hole.     

One‐Pot Fabrication of Rattle‐Like Capsules with Multicores by Pickering‐Based Polymerization with Nanoparticle Nucleation

Rattle‐like polymer capsules with multicores in one shell are facilely fabricated by oil‐in‐water Pickering emulsion polymerization for the first time. The oil phase contains hydrophobic silica nanoparticles dispersed in polymerizable monomer, styrene, and unpolymerizable solvent, hexadecane. The multicore rattle‐like capsules are facilely produced after the polymerization of monomers in the oil droplets. The key point of this one‐pot method lies in the nucleation of hydrophobic silica and the phase separation between the resulting polystyrene and hexadecane. The influences of the contents of silica, hexadecane, cross‐linker, and stabilizer on the structure and morphology of rattle‐like capsules are systematically investigated. Moreover, functionalization of the rattle‐like capsules can be developed easily by varying hydrophobic nucleation nanoparticles in the oil phase. This work opens up a new route to fabricate multilevel capsules or spheres.

     

Synthesis of CuCorePtShell Nanoparticles as Model Structures for Core–Shell Electrocatalysts by Direct Platinum Electrodeposition on Copper

The synthesis of Cu(core)Pt(shell) model catalysts by the direct electrochemical deposition of Pt on Cu particles is presented. Cu particles with an average diameter of 200 nm have been deposited on glassy‐carbon electrodes by double pulse electrodeposition from a copper sulfate solution. Subsequent deposition from a platinum nitrate solution under potential control allows for a high selectivity of the Pt deposition towards Cu. Using a combination of cyclic voltammetry, XPS and sputtering, the structure of the generated particles has been analyzed and their core–shell configuration proven. It is shown that the electrocatalytic activity for the oxygen reduction is similar to that of other PtCu catalyst systems. The synthesized structures could allow for the analysis of structure–activity relations of core–shell catalysts on the way to the simple and controlled synthesis of supported Cu(core)Pt(shell) nanoparticles as oxygen reduction catalysts.     

Core–Shell Structured Polystyrene/BaTiO3 Hybrid Nanodielectrics Prepared by In Situ RAFT Polymerization: A Route to High Dielectric Constant and Low Loss Materials with Weak Frequency Dependence

A novel route to prepare core–shell structured nanocomposites with excellent dielectric performance is reported. This approach involves the grafting of polystyrene (PS) from the surface of BaTiO₃ by an in situ RAFT polymerization. The core–shell structured PS/BaTiO₃ nanocomposites not only show significantly increased dielectric constant and very low dielectric loss, but also have a weak frequency dependence of dielectric properties over a wide range of frequencies. In addition, the dielectric constant of the nanocomposites can also be easily tuned by varying the thickness of the PS shell. Our method is very promising for preparing high‐performance nanocomposites used in energy‐storage devices.     

Fabrication of Selenium/Carbon Core–Shell Submicrowires and Carbon Submicrotubes by a Facile Solution Process

We show a facile one‐step surfactant‐assisted solution process to fabricate selenium/carbon (Se/C) coaxial core–shell submicrowires and their transformation into carbon submicrotubes by dissolution of the Se cores at ambient temperature. The formation process of the Se/C core–shell submicrowires was investigated. The results of the investigation and further experiments confirm that the thickness of the carbon shell could be tailored by controlling the experimental conditions. The as‐synthesized Se/C core–shell submicrowires and the carbon submicrotubes are potentially useful in applications such as in nanodevices or biomedicine.     

Facile Synthesis of Ge@C Core–Shell Nanocomposites for High‐Performance Lithium Storage in Lithium‐Ion Batteries

Herein, we report a facile and “green” synthetic route for the preparation of Ge@C core–shell nanocomposites by using a low‐cost Ge precursor. Field‐emission scanning electron microscopy and transmission electron microscopy analyses confirmed the core–shell nanoarchitecture of the Ge@C nanocomposites, with particle sizes ranging from 60 to 100 nm. Individual Ge nanocrystals were coated by a continuous carbon layer, which had an average thickness of 2 nm. When applied as an anode materials for lithium‐ion batteries, the Ge@C nanocomposites exhibited a high initial discharge capacity of 1670 mAh g^?1 and superior rate capability. In particular, Ge@C nanocomposite electrodes maintained a reversible capacity of 734 mAh g^?1 after repeated cycling at a current density of 800 mA g^?1 over 100 cycles.     

Synergistic Effect of SnO2/ZnWO4 Core–Shell Nanorods with High Reversible Lithium Storage Capacity

High reversible lithium storage capacity is obtained from novel SnO₂/ZnWO₄ core–shell nanorods. At C/20 (20 h per half cycle) rate, the reversible capacity of SnO₂/ZnWO₄ core–shell nanorods is as high as 1000 mAh g^?1, much higher than that of pure ZnWO₄, SnO₂, or the traditional theoretical result of the simple mixture. Such performance can be attributed to the synergistic effect between the nanostructured SnO₂ and ZnWO₄. The distinct electrochemical activity of ZnWO₄ nanorods probably activates the irreversible capacity of the SnO₂ nanoparticles. These results indicate that high‐performance lithium ion batteries can be realized by introducing the synergistic effect of one‐dimensional core–shell nanocomposites.     

One‐Pot Synthesis of Multifunctional Polymers by Light‐Controlled Radical Polymerization and Enzymatic Catalysis with Candida antarctica Lipase B

The preparation of multifunctional polymers and block copolymers by a straightforward one‐pot reaction process that combines enzymatic transacylation with light‐controlled polymerization is described. Functional methacrylate monomers are synthesized by enzymatic transacylation and used in situ for light‐controlled polymerization, leading to multifunctional methacrylate‐based polymers with well‐defined microstructure.

     

Polystyrene‐Supported Core–Shell Beads with Aluminium MOF Coating for Extraction of Organic Pollutants

Aluminium‐based metal–organic framework (MOF) coatings on polystyrene bead surfaces were easily synthesized by reacting an intermediate metal hydroxide coating with an organic linker. Several different sizes of polystyrene beads were coated with aluminium metal hydroxide to construct Al@PS core–shell bead materials. The activated Al@PS core–shell beads were involved to make a homogenous MOF‐based layer in the presence of the organic linker. By using different sizes of the PS support the size of MOFs on the PS composites could be fine‐tuned under specific reaction conditions. MOF‐coated core–shell bead materials (Al‐1,4‐NDC@PS and MIL‐53(Al)@PS) were characterized using various analytical techniques. Al‐1,4‐NDC@PS and MIL‐53(Al)@PS were evaluated for solid‐phase microextraction (SPME) of hydrophobic polycyclic aromatic hydrocarbons (PAHs) and hydrophilic non‐steroidal anti‐inflammatory drugs (NSAIDs), respectively. Al‐1,4‐NDC@PS‐1000 displayed high extraction recoveries ranging from 79.2 % to 99.8 % in the SPME of PAHs. Meanwhile, MIL‐53(Al)@PS‐1000 showed 85.9–99.0 % extraction recoveries in the SPME of NSAIDs. These results show that the proposed approach holds potential to extract organic analytes on an industrial scale.