非晶高聚物对聚(ε-己内酯)在其与苯乙烯-丙烯腈共聚物相容共混物中球晶生长速率的影响

本文研究了聚(ε-己内酯)(PCL)在其与苯乙烯-丙烯腈共聚物(SAN)的相容共混物中球晶生长速率与共混组成和结晶温度的关系.发现聚己内酯的球晶生长速率随着SAN的含量增加而下降.由于PCL与SAN是相容共混物,因此在用二次成核动力学方程描述PCL球晶生长速率时,我们引进了相互作用参数X.结果由共混体系的结晶动力学方程计算到的X值与由平衡熔点下降方法计算到的X_(23)值是相同的;而PCL晶体的折叠表面自由能则随着SAN含量的增加而下降.这些结果说明非晶高聚物SAN有碍于PCL球晶的生长.     

非晶高聚物对聚(ε-己内酯)在其与苯乙烯-丙烯腈共聚物相容共混物中球晶生长速率的影响

 本文研究了聚(ε-己内酯)(PCL)在其与苯乙烯-丙烯腈共聚物(SAN)的相容共混物中球晶生长速率与共混组成和结晶温度的关系.发现聚己内酯的球晶生长速率随着SAN的含量增加而下降.由于PCL与SAN是相容共混物,因此在用二次成核动力学方程描述PCL球晶生长速率时,我们引进了相互作用参数X.结果由共混体系的结晶动力学方程计算到的X值与由平衡熔点下降方法计算到的X₂₃值是相同的;而PCL晶体的折叠表面自由能则随着SAN含量的增加而下降.这些结果说明非晶高聚物SAN有碍于PCL球晶的生长.     

聚(ε-己内酯)(PCL)/苯乙烯-丙烯腈共聚物(SAN)共混物的研究

在0～30%PCL组成范围内的标题共混物,其DSC谱图上只出现单一的玻璃化转变,且位于两个纯组份之问。在红外光谱上,对于熔融状态的PCL/SAN共混物,观察到PCL的羧基峰随着SAN混入量的增加而移向低频。说明PCL分子与SAN分子之间存在着特殊的相互作用。从熔融下降计算的相互作用参数结果表明,PCL/SAN共混物在热力学上是相容的。     

电子束辐照法制备交联共混物聚(ε-己内酯)/苯乙烯-丙烯腈共聚物的结晶动力学研究

将线形聚(ε-己内酯)(PCL)、苯乙烯-丙烯腈共聚物(SAN)和三烯丙基异三聚氰酸酯(TAIC)熔融共混,通过电子束辐照法制备了3组凝胶含量不同的交联PCL和PCL/SAN共混物样品.采用相差显微镜(PCOM)观察发现PCL与SAN具有良好的相容性.利用示差扫描量热法(DSC)和偏光显微镜(POM)研究了交联PCL和PCL/SAN共混物的等温结晶动力学和非等温结晶行为.结果表明,当体系交联程度相近时,交联聚己内酯的结晶动力学随SAN含量的增加而明显减慢.在SAN含量相同时,交联聚己内酯的结晶速率随交联程度增大而减小.对分离提取的线形和交联组分进行结晶动力学的研究则表明SAN引入对PCL的结晶速率起到了关键性的抑制作用.     

聚(ε-己内酯)/苯乙烯-丙烯腈共聚物共混物的形态研究

本文研究了聚(ε-己内酯)(PCI/苯乙烯-丙烯腈共聚物(SAN)共混物的形态。采用差示扫描量热计(DSC)测量了PCL/SAN共混物中的PCL结晶度随着SAN含量的增加而下降;当SAN浓度达到60wt％。以上时,PCI的结晶度趋于零。通过偏光显微镜可以观察到在含高浓度PCI的共混物中,PCL是以球晶形式存在的。样品是由PCL球晶充满的,但是随着SAN含量的增加,PCL球晶半径减小,球晶结构逐渐变得不规整,而X-射线衍射测试了不同组成的PCL/SAN共混物中PCL的晶胞参数没有改变,说明SAN没有进入到PCL的晶胞内。以小角X-射线散射结果发现PCI片晶之间的距离随着SAN含量的增加而增大。以上说明SAN分子与没有结晶的PCL形成无定形相夹在PCL的片晶之间。     

苯乙烯-丁二烯-苯乙烯/聚乙烯基甲基醚共混体系相容性的FT-IR及DSC研究

嵌段高聚物、均聚物共混体系相容性是近年来研究的热点。本工作以光学显微镜、DSC、FT-IR为手段,研究了三嵌段高聚物苯乙烯-丁二烯-苯乙烯(SBS);SBS-48、SBS-30,SBS-28与聚乙烯基甲基醚共混体系的相容性。DSC结果表明,随SBS中PS含量的升高,体系相容性变好,PS段分子量增大,也有助于体系相容。FT-IR结果表明PVME中COCH_3在1100cm~(-1)附近呈现的双峰的相对强度对体系的相容性十分敏感,而由于苯环C—H振动产生的698cm~(-1)峰位却不象PS/PVME体系那样随相容性的改变而有显著的改变。总而言之,嵌段高聚物SBS/均聚物PVME共混体系中,体系的相容性依赖于嵌段高聚物在体系中的组份含量及嵌段高聚物中PS的重量百分含量,PS段分子量的大小对体系相容性也有影响。     

聚碳酸酯与苯乙烯-丙烯腈共聚物共混体系相容性及其对光学性能的影响

利用分子内链段排斥性相互作用理论研究了聚碳酸酯 (PC) 苯乙烯 丙烯腈共聚物 (SAN)共混体系中组份分子量及SAN共聚比例对体系相容性的影响规律 ,确定了获得均相的PC SAN共混体系的条件 ,考察了体系相容性与光学性能之间的关系 .通过实验获得了均相的PC SAN共混物 ;研究结果表明PC聚合度为 90、SAN聚合度为 3 0的PC SAN(S体积含量为 68%)体系共混比在 60∶40附近时体系的双折射能够实现补偿 ,紫外透光率达到 70 %.     

聚(ε-己内酯)(PCL)/苯乙烯-丙烯腈共聚物(SAN)共混物的研究

在0～30％PCL组成范围内的标题共混物,其DSC谱图上只出现单一的玻璃化转变,且位于两个纯组份之问。在红外光谱上,对于熔融状态的PCL/SAN共混物,观察到PCL的羧基峰随着SAN混入量的增加而移向低频。说明PCL分子与SAN分子之间存在着特殊的相     

Flory状态方程理论研究PS/PMMA/SAN相行为

将改进的Flory状态方程理论(EOS)引入含“分子内链段排斥性相互作用”的高分子共混物中,研究含无规共聚物的三元共混体系聚苯乙烯(PS)/聚甲基丙烯酸甲酯(PMMA)/聚苯乙烯-丙烯腈(SAN)无规共聚物的相行为,建立相应的适用于含无规共聚物三元共混体系Spinodal方程.用PS、PMMA、PAN的特征参数及其链段间相互作用参数分别计算相应共聚物的特征参数,由二元相互作用模型计算均聚物-共聚物间的相互作用能参数.在运用EOS理论研究三元均聚物共混体系相行为基础上,进一步预测PS/PMMA/SAN体系的相行为,计算并绘制不同温度下的Spinodal曲线并进行实验验证,理论计算与实验结果吻合.结果表明,EOS理论可以克服经典平均场理论的缺陷,成功描述含分子内排斥作用共混体系相行为与共聚物组成及温度之间的关系.     

改性酚氧树脂/聚(甲基丙烯酸丁酯-co-4-乙烯基吡啶)共混物的相容-络合行为和表面表征

合成了一系列不同4-乙烯基吡啶含量的聚(甲基丙烯酸丁酯-co-4-乙烯基吡啶)(BVPy)共聚物,并对酚氧树脂(Phenoxy)的仲羟基进行了不同乙酰化程度的改性.用粘度法和激光光散射(LLS)研究了BVPy/改性Phenoxy共混物在溶液中的络合行为对氢键相互作用基团密度的依赖性,并用DSC研究了共混体系在本体中的相容性.将粘度法及LLS的结果结合起来,得到了改性Phenoxy/BVPy共混体系的不相容-相容-络合转变相图.在此基础上,用XPS初步考察了共混物的相容性对其表面组成的影响.结果表明,大分子间的络合相互作用可抑制共混物的表面富集.     

Ternary blends of phenoxy/SAN/poly(-ε-caprolactone)

The compatibilizing effect of poly(ε-caprolactone) (PCL) on the blends of two immiscible polymers, poly(hydroxy ether of bisphenol A) (phenoxy) and poly(styrene-co-acrylonitrile) (SAN) has been investigated. The phase behavior of the ternary blends was affected by the AN content in the SAN copolymers and a maximum miscible region was observed at 19.5 wt % of AN. The effect of AN content on the phase behavior of the ternary blends was interpreted in terms of the relative magnitude of the segmental interaction energy densities, which were obtained by combining a melting point depression and an extended binary interaction model. When a small amount of PCL was added to the phenoxy/SAN blends, the phase morphology showed a finer phase dispersion, indicating that the interfacial tension between the phenoxy and SAN is considerably reduced. However, the improvement in tensile properties was limited despite the morphological change with the PCL content. From the results of the DSC measurements, SEM, and tensile testing, it was understood that the PCL acted as a compatibilizer for the immiscible phenoxy/SAN blends. © 1994 John Wiley & Sons, Inc.     

Miscibility of poly(ϵ-caprolactone) and of poly(styrene-co-acrylonitrile) with poly(styrene-co-acrylic acid)

The miscibility of poly (?-caprolactone) (PCL) with poly (styrene-co-acrylic acid) (SAA) and of poly (styrene-co-acrylonitrile) (SAN) with SAA was examined as a function of the comonomer composition in the copolymers. For PCL/SAA blends it was found that PCL is miscible with SAA within a specific range of copolymer compositions. Segmental interaction energy densities were evaluated by analysis of the equilibrium melting point depression and application of a binary interaction model. The results suggest that the intramolecular repulsion in SAA copolymer plays an important role in inducing the miscibility. Additionally, the critical AA content in SAA for the blend to be homogeneous was predicted by correlating the segmental interaction energy densities with the binary interaction model. For SAN/SAA blends, it was also found that SAA is miscible with SAN within a specific range of copolymer compositions. From the binary interaction model, segmental interaction energy denisties between different monomer units were estimated from the miscibility map and were found to be positive for all pairs, indicating that the miscibility of the blends is due to the strong repulsion in the SAA copolymers.     

聚己内酯和聚氧化乙烯共混体系中的两类片晶相间堆砌

对聚(ε-己内酯)(PCL)/聚氧化乙烯(PEO)共混物的相差显微镜、广角X-射线衍射(WAXD)、小角X-射线散射(SAXS)及示差扫描量热计(DSC)等的研究表明,只有当共混物中PCL(或PEO)的含量低于20％时,两组份是相容的.当PCL含量低于20％时,在共混物中形成了PEO片晶和PCL片晶相间堆砌的结晶形态,当PEO含量不超过20％时,PEO则完全以非晶形式混入PCL的非晶区,同时阻碍了PCL的结晶.可见在结晶过程中,相容的两组份对共混体系形态结构的影响却不尽相同.     

Evaluation of the interaction parameter for poly(ε‐caprolactone)/poly(styrene‐co‐acrylonitrile) blends

In this article, the miscibility of poly(ε‐caprolactone) (PCL) with poly(styrene‐co‐acrylonitrile) (SAN) containing 25 wt % of acrylonitrile is studied from both a qualitative and a quantitative point of view. The evidences coming from thermal analysis (differential scanning calorimetry) demonstrate that PCL and SAN are miscible in the whole range of composition. The Flory interaction parameter χ_1,2 was calculated by the Patterson approximation and the melting point depression of the crystalline phase in the blends; in both cases, negative values of χ_1,2 were found, confirming that the system is miscible. The interaction parameter evaluated within the framework of the mean field theory demonstrates that the miscibility of PCL/SAN blends is due to the repulsive interaction between the styrene and acrylonitrile segments in SAN. © 2010 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys, 2010     

聚环氧乙烷/聚乙基■唑啉共混体系结晶行为及相容性的研究

用偏光显微镜（ＰＬＭ）、ＤＳＣ、ＩＲ和ＷＡＸＤ等测试方法对聚环氧乙烷（ＰＥＯ）／聚乙基唑啉（ＰＥＯｘ）共混体系结晶行为及相容性进行了研究．结果表明，ＰＥＯ含量在３０％以上的共混体系中，几乎完全被球晶充满，非晶态ＰＥＯｘ作为微区分散在大球晶之间或之中；含量为２０％的共混体系照片上呈树枝状晶；含量低于１０％时则看不到结晶出现，体系形成单一的非晶相．对任何组成的共混物，均只出现单一的玻璃化转变温度（Ｔｇ），而且符合Ｆｏｘ方程揭示的规律；随ＰＥＯｘ组分含量的增加，共混体系的结晶度减小，熔点下降，并利用平衡熔点方程计算出ＰＥＯ与ＰＥＯｘ的相互作用能密度．非晶ＰＥＯ与ＰＥＯｘ热力学相容，其相容性是由于这两种分子间存在着特殊相互作用．ＰＥＯｘ的加入不会改变ＰＥＯ的晶胞参数．     

SiO2粒子对PMMA/SAN共混体系相分离行为的影响

采用小角激光光散射(SALLS)并结合动态流变学方法,考察了气相法二氧化硅(SiO2)粒子的加入对聚甲基丙烯酸甲酯/苯乙烯-丙烯腈无规共聚物(PMMA/SAN)共混体系相行为的影响,得到了添加SiO2粒子前后的相图,发现SiO2粒子对基体相行为的影响与基体的组成有关.对PMMA/SAN(60/40)体系,加入SiO2粒子后相分离温度上升,但并未改变相分离机理,仍为亚稳单相分解过程(spinodal decomposition,SD);而对于PMMA/SAN(30/70)体系,加入SiO2粒子后却降低了体系的相分离温度.该现象可能是SiO2粒子和基体组分界面间组成与PMMA/SAN共混物基体组成的差异造成的.     

THE COMPATIBILITY OF BLENDS OF POLY(VINYL CHLORIDE) OR CHLORINATED POLY(VINYL CHLORIDE) WITH POLY(METHYL METHACRYLATE)

IR spectral shifts of carbonyl vibrational absorption for ethyl acetate, which acts analogically as the structural unit of poly(methyl methacrylate), in cyclohexane, chloroform, chlorinated paraffins, poly(vinyl chloride) and chlorinated poly(vinyl chloride) were measured. The results suggest that there are specific interactions between the carbonyl groups and the chlorinated hydrocarbons which could be responsible for the apparent compatibility of poly(vinyl chloride)—poly(methyl methacrylate) and chlorinated poly(vinyl chloride)—poly(methyl methacrylate) blends. Additionally, the effects of the preparation mode of blend films on phase separation and observed compatibility are discussed.     

STUDIES ON MISCIBILITY OF POLY (ε-CAPROLACTONE) AND ALIPHATIC POLYCARBONATE BLENDS AND DETERMINATION OF THEIR INTERACTION PARAMETER*

In this paper the miscibility of poly (ε-caprolactone) (PCL) and aliphatic polycarbonate (APC) is studied by using DSC. The results show that PCL and APC are miscible in all ranges of composition. The interaction parameter between the polymers is calculated from the melting point depression data. Using optical microscope, the shapes of the PCL spherulites in the blends are observed.     

PTHF-b-PMMA/PVC共混体系的相容性和结晶行为

研究了具有焓效应的聚四氢呋喃-聚甲基丙烯酸甲酯两嵌段共聚物与聚氯乙烯PTHF-b-PMMA/PVC)共混体系的相容性和结晶行为. 结果表明, 其相容性比AB/A型嵌段共聚物共混体系的相容性要好得多; 与PTHF部分相容的PVC对PTHF微区的结晶行为可产生很大的影响. 应用有关理论和模型很好地解释了结晶行为的这种变化.