Bi2Fe4O9/g-C3N4/UiO-66三元复合材料的协同光催化作用

通过水热法合成具有协同机制的三元复合材料Bi₂Fe₄O₉/g-C₃N₄/UiO-66,研究表明三元复合光催化剂的催化活性要高于二元材料和纯材料。这主要是由于Bi₂Fe₄O₉更易于和g-C₃N₄结合形成稳定的Z-scheme异质结结构,使三元复合材料增强了可见光响应能力,提高了电子-空穴分离能力,增强了空穴和电子的氧化还原能力。     

Bi2Fe4O9纳米粉体:水热法制备及表征

Bi₂Fe₄O₉ nanoparticles were prepared at low temperature via a facile, one-step hydrothermal synthesis process using iron(Ⅲ) nitrate nonahydrate(Fe(NO₃)₃·9H₂O) and bismuth nitrate pentahydrate (Bi(NO₃)₃·5H₂O) as starting materials and sodium hydroxide (NaOH) as the precipitant and mineralizer. XRD results indicate that the as-prepared nanoparticles are pure Bi₂Fe₄O₉. SEM images reveal that the as-prepared Bi₂Fe₄O₉ nanoparticles have a sheet-like morphology. The Bi₂Fe₄O₉ nanoparticles thus obtained are paramagnetic at room temperature as shown by magnetic measurements.     

Bi2WO6/UiO-66复合材料的制备及其光催化性能

通过水热法制备了一种复合光催化剂Bi_2WO_6/UiO-66,探究了模板剂乙酸(CH_3COOH)对Ui O-66形貌的影响和2种中心元素Bi与Zr的不同物质的量之比对光催化性能的影响。通过XRD、SEM、N_2吸附-脱附、UV-Vis DRS、XPS等对催化剂的物相、形貌、比表面积、光吸收性能、元素组成等进行表征。实验结果表明,当n_(Bi)∶n_(Zr)=2∶1时,Bi_2WO_6/UiO-66对罗丹明B(RhB)的光催化活性最高,可见光照射50 min后,RhB的相对浓度降低98.5%。经过5次循环利用实验,催化剂的光催化活性没有明显下降,说明复合光催化剂的稳定性高。根据自由基捕获实验证明了空穴(h~+)为光催化中起决定性作用的活性物质,结合电化学测试以及UV-Vis DRS表征提出了可能的光催化降解机理。     

四角星形BiVO4/Bi2O3催化剂的制备及性能研究

采用水热法合成具有四角星形貌的钒酸铋,再将钒酸铋浸渍在碱溶液里二次水热,制备出BiVO₄/Bi₂O₃催化剂。采用X射线粉末衍射(XRD)、扫描电子显微镜(SEM),紫外-射(UV-Vis DRS)等方法征。可见光下,BiVO₄/Bi₂O₃复合物的光催化降解丹明B性能及光电优于纯BiVO₄。BiVO₄/Bi₂O₃复合材料形成了异质结构,有效抑制了光电子与空穴的复合效率。     

g-C3N4/CaTi2O5复合材料制备及其光催化性能

利用类石墨氮化碳（g-C₃N₄）和亚稳相钙钛氧化物（CaTi₂O₅）固相法制备C₃N₄/CaTi₂O₅复合材料。利用X射线衍射（XRD）、金相显微镜、扫描电子显微镜（SEM）及附带能谱分析仪（EDS）和N₂吸附-脱附对样品的显微结构和比表面积进行检测分析,并用紫外-可见吸收光度计（UV-Vis）测试了样品的光吸收性能,研究C₃N₄与CaTi₂O₅物质的量之比（n_C3N4/nCaTi₂O₅）对C₃N₄/CaTi₂O₅复合样品的物相结构和微观形貌的影响,同时考察C₃N₄/CaTi₂O₅复合样品在可见光照射下光催化降解罗丹明染料效果。实验结果表明：相比纯C₃N₄和CaTi₂O₅样品,C₃N₄/CaTi₂O₅复合样品在可见光下具有较高的光催化性能,随着n_C3N4/nCaTi₂O₅增加,样品的光催化降解率随之增加而后降低,当n_C3N4/nCaTi₂O₅=1：1时,样品的光催化降解率达到最大值99.5%,并且循环重复利用5次后,样品的光催化剂降解率仍几乎保持不变。复合样品光催化性能提高主要归因于复合能级结构有效地抑制了电子和空穴复合所致。     

不同晶型Bi2O3可见光光催化降解罗丹明B的研究

采用化学沉淀法制备了α、β、γ 3种晶体结构的Bi₂O₃光催化剂。利用XRD、TEM、氮气吸附、TG-DSC、紫外-可见漫反射光谱对样品的晶体结构、微观形貌、光学吸收特性进行了表征,并以罗丹明B(RhB)作为模型污染物,研究了不同的粉体光催化剂在可见光(λ>420 nm)照射下的光催化能力。结果表明：制备的α-Bi₂O₃为长3 μm、宽1 μm的板条状颗粒,带隙为2.84 eV;β-Bi₂O₃为粒径约150 nm的不规则颗粒,带隙为2.75 eV;γ-Bi₂O₃为直径6 nm、长度150~200 nm的纳米管,带隙为2.68 eV。在可见光照射下Bi₂O₃光催化降解RhB的活性如下：γ-Bi₂O₃>β-Bi₂O₃>α-Bi₂O₃,其中γ-Bi₂O₃在辐照60 min后对罗丹明B的脱色率可达97%以上。     

一维Bi2Fe4O9纳米棒阵列的无模板水热合成

以物质的量的比为1：1的Bi（NO₃）₃·5H₂O和Fe（NO₃）₃·9H₂O为反应原料,以NaOH为矿化剂,利用水热法在Ti基板上成功制备出一维Bi₂Fe₄O₉纳米棒阵列。对该纳米棒阵列分别进行XRD、FE-SEM、HR-TEM和UV-Vis测试,得到Bi₂Fe₄O₉纳米棒的直径为100nm,长度为3~4μm,并表现出良好的光吸收性能,禁带宽度约为1.9eV,对甲基紫溶液的光降解率达到86%,其活性明显高于市售P25（TiO₂）。该纳米棒阵列的生长方式完全遵循奥斯瓦尔德熟化（Ostwald ripening）单晶生长机理。     

一步法制备Bi2MoO6/CoMoO4绣花球结构及其光催化性能

以五水硝酸铋为铋源,采用简易的一步水热法合成出Bi_2MoO_6/CoMoO_4绣花球结构。通过X射线粉末衍射(XRD)、扫描电子显微镜(SEM)、透射电子显微镜(TEM)、傅里叶红外光谱(FT-IR)、紫外-可见漫反射光谱(UV-Vis DRS)、荧光光谱(PL)和电化学测试等表征对所制备催化剂的物相组成、微观形貌、光学性质以及光生电荷复合效率进行了分析。研究结果表明,引入Bi_2MoO_6之后,Bi_2MoO_6/CoMoO_4复合异质结的光吸收范围明显被拓宽,其光生电荷的分离率也得到了提升。以亚甲基蓝和头孢曲松钠为污染物来模拟废水,在可见光的条件下评估催化剂样品的光催化降解活性。在可见光下光照60 min后,Bi_2MoO_6负载量为30%(w/w)的复合物具有最佳的光催化性能,其降解速率常数约为纯CoMoO_4的2倍。基于实验的所有表征,进一步地研究了Bi_2MoO_6/CoMoO_4体系相应的光催化机理。     

球形Bi4Ti3O12制备及其可见光催化性能

采用水热法合成球形钛酸铋复合氧化物光催化剂,利用SEM、XRD和UV-Vis DRS等表征手段对复合氧化物的晶体结构、微观形貌和光学性能进行了分析,结果表明,制备的钛酸铋复合氧化物为10 nm的球形颗粒,具有良好的晶型结构,禁带宽度为2.7 nm,有较好的可见光吸收能力。以亚甲基蓝、甲基橙及酸性品红为目标污染物,研究了复合氧化物在可见光下的光催化降解有机污染物的性能,并对光催化降解机理进行了探讨。结果表明,在可见光照射下,该复合氧化物对酸性品红降解效果明显优于亚甲基蓝和甲基橙,光照150 min下,降解率可达91%。     

一锅法制备S型异质结光催化剂Fe2O3/Fe2TiO5及其高效降解有机污染物性能

首次采用简单的一锅法制备了Fe₂O₃/Fe₂TiO₅异质结纳米材料。构建S型异质结后,与纯的Fe₂O₃和Fe₂TiO₅相比,Fe₂O₃/Fe₂TiO₅复合材料表现出更高的光催化降解速率和效率。经过2.5 h的光照后,Fe₂O₃/Fe₂TiO₅可以降解接近100%的亚甲基蓝（MB）。在Fe₂O₃/Fe₂TiO₅复合材料中,Fe₂O₃和Fe₂TiO₅之间形成了内建电场,可以促进光生电子-空穴对的分离。因此,具有更高能量的Fe₂TiO₅导带中的电子和具有更高能量的Fe₂O₃价带中的空穴可以得到有效的保留,从而使它们更加有效地扩散到催化剂表面,并参加降解反应。此外,Fe₂O₃/Fe₂TiO₅复合材料具有很好的光催化稳定性。     

Densely packed single-crystal Bi2Fe4O9 nanowires fabricated from a template-induced sol-gel route

Densely packed single-crystal Bi₂Fe₄O₉ nanowires were successfully synthesized by a template-induced citrate-based sol-gel process. The structural properties of the nanowires were characterized using many techniques. The results of scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed that Bi₂Fe₄O₉ nanowires possessed a uniform length and diameter, which were controlled by the thickness and the pore diameter of the applied porous anodic aluminum oxide (AAO) template, respectively. The results of X-ray diffraction (XRD) and the selected area electron diffraction (SAED) indicated that Bi₂Fe₄O₉ nanowires had an orthorhombic single-crystal structure. Furthermore, the energy-dispersive X-ray (EDX) spectroscopy demonstrated that the stoichiometric Bi₂Fe₄O₉ was formed. The possible formation mechanism of nanowires was also discussed.     

A new 2212-type stair like structure: Bi14Sr21Fe12O61, m=5 member of the generic [Bi2Sr3Fe2O9]m[Bi4Sr6Fe2O16] family

A new oxide, Bi₁₄Sr₂₁Fe₁₂O_61, with a layered structure derived from the 2212 modulated type structure Bi₂Sr₃Fe₂O₉, was isolated. It crystallizes in the I2 space group, with the following parameters: a=16.58(3) Å, b=5.496(1) Å, c=35.27(2) Å and β=90.62°. The single crystal X-ray structure determination, coupled with electron microscopy, shows that this ferrite is the m=5 member of the [Bi₂Sr₃Fe₂O₉]_m[Bi₄Sr₆Fe₂O₁₆] collapsed family. This new collapsed structure can be described as slices of 2212 structure of five bismuth polyhedra thick along , shifted with respect to each other and interconnected by means of [Bi₄Sr₆Fe₂O₁₆] slices. The latter are the place of numerous defects like iron or strontium for bismuth substitution; they can be correlated to intergrowth defects with other members of the family.     

一维Bi_2Fe_4O_9纳米棒阵列的无模板水热合成

以物质的量的比为1∶1的Bi(NO3)3·5H2O和Fe(NO3)3·9H2O为反应原料,以NaOH为矿化剂,利用水热法在Ti基板上成功制备出一维Bi2Fe4O9纳米棒阵列。对该纳米棒阵列分别进行XRD、FE-SEM、HR-TEM和UV-Vis测试,得到Bi2Fe4O9纳米棒的直径为100 nm,长度为3~4μm,并表现出良好的光吸收性能,禁带宽度约为1.9 eV,对甲基紫溶液的光降解率达到86%,其活性明显高于市售P25(TiO2)。该纳米棒阵列的生长方式完全遵循奥斯瓦尔德熟化(Ostwald ripening)单晶生长机理。     

石墨相氮化碳/二氧化锡复合材料的制备及光催化性能

采用热聚合法和水热法相结合的方法制备了g-C_3N_4/SnO_2复合光催化剂。利用XRD、SEM、TEM、FT-IR和UV-Vis DRS等多种测试手段对所得样品的物相结构、微观形貌和吸光特性等进行了表征。结果表明,异质结构复合光催化剂的最大光吸收边位置相对纯相SnO_2发生了明显的红移,并且SnO_2颗粒均匀分布于g-C_3N_4表面,其中最优组分(50%-g-C_3N_4/SnO_2)光催化降解染料罗丹明B(RhB)的效率达到了纯相g-C_3N_4的3.78倍。     

Bi2WO6/g-C3N4复合型催化剂的制备及其可见光光催化性能

利用溶剂热法,把Bi2WO6纳米颗粒植入g-C3N4层间和表面成功地制备了Bi2WO6/g-C3N4复合型光催化剂。通过XRD、SEM、TEM、BET和UV-Vis分别对样品的结构、组成、形貌、比表面积、光学性能进行了表征。结果表明,g-C3N4层状结构被部分剥离成碎片且与Bi2WO6纳米颗粒形成了复合物。Bi2WO6/g-C3N4复合型光催化剂与单一Bi2WO6相比不仅扩展了可见光的响应范围、增大了比表面还加速了光生电子与空穴的分离。结果表明,Bi2WO6的最佳负载量为60wt%时,复合型光催化剂具有最高的可见光催化活性且性能稳定、易回收。     

Bi2WO6/g-C3N4复合型催化剂的制备及其可见光光催化性能

利用溶剂热法, 把Bi₂WO₆纳米颗粒植入g-C₃N₄层间和表面成功地制备了Bi₂WO₆/g-C₃N₄复合型光催化剂。通过XRD、SEM、TEM、BET和UV-Vis分别对样品的结构、组成、形貌、比表面积、光学性能进行了表征。结果表明, g-C₃N₄层状结构被部分剥离成碎片且与Bi₂WO₆纳米颗粒形成了复合物。Bi₂WO₆/g-C₃N₄复合型光催化剂与单一Bi₂WO₆相比不仅扩展了可见光的响应范围、增大了比表面还加速了光生电子与空穴的分离。结果表明, Bi₂WO₆的最佳负载量为60wt%时, 复合型光催化剂具有最高的可见光催化活性且性能稳定、易回收。