Structural and magnetic properties of SmCo7−xMox alloys

Phase structure and magnetic properties of the as-cast and as-milled/annealed SmCo_7−xMo_x (x=0, 0.1, 0.2, 0.3, 0.4) alloys have been systematically studied. It is found that all the as-cast series alloys are composed of the CaCu₅-type and Th₂Zn₁₇-type phases. Saturation magnetization of the samples decreases with the Mo content increasing. Intrinsic coercivities (_iH_c) of no more than 0.06 T are observed in these as-cast samples, due to their rather coarse grain microstructures with an average grain size of 50 μm. The as-milled/annealed SmCo_7−xMo_x powders crystallize in the disordered TbCu₇-type (1:7) structure with very fine nanograins, and a minor Co₃Mo phase appears in the samples with x=0.1-0.4. High _iH_c (?0.95 T) are achieved in these samples, with a maximum of 1.26 T located at x=0.2, which can be primarily attributed to strong pinning of the domain wall motion at the nanograin boundaries. The temperature coefficient (β) of the _iH_c is about −0.22%/°C in the temperature range of 25-400 °C for the as-milled/annealed samples.     

Structure and magnetic properties of SmCoxTi0.4-1:7 ribbons

SmCo_xTi_0.4 (x=6.6, 7.1, 7.6, 8.1) ribbons have been prepared by melt spinning at a wheel speed of 42 m/s, followed by annealing at 750 °C for 2 h. Both as-spun and as-annealed ribbons possess the disordered TbCu7-type (1:7) phase even when the Sm/(Co,Ti) atomic ratio deviates from 1/7. The c/a ratio increases with increasing Co concentration x, but the unit cell volume decreases. The Curie temperatures show above 700 °C, increasing from 707 °C for x=6.6 to 782 °C for x=8.1. The saturation magnetizations increase almost linearly with increasing Co content. The observed magnetic hardening is believed to arise from the high magnetocrystalline anisotropy of the 1:7 phase and the fine nanograin structure. The intrinsic coercivity of 9797 Oe has been obtained in the melt-spun SmCo_7.1Ti_0.4 ribbons.     

Influence of partial rare-earth substitution for Sm in the giant intrinsic magnetic hardness compound SmCo2Ni3

The phenomenon of giant intrinsic magnetic hardness is investigated in compounds R_1−x Sm _x Co₂Ni₃ with R=Y, Pr, Gd, Tb, Er. Partial Er substitution for Sm actually increases magnetic hardness while all other substitutions decrease magnetic hardness. The strength of coercivity is thus dependent on both the sign and magnitude of the crystal field interaction. The temperature dependence of coercivity is complex in the case of Pr substitution as a result of competing effects from thermal activation and a decrease in anisotropy at low temperatures. This study has been supported by a grant from the National Science Foundation.     

Fabrication and magnetic properties of amorphous Co0.71Pt0.29 nanowire arrays

Highly ordered Co_0.71Pt_0.29 alloy nanowire arrays have been fabricated successfully by direct current electro-deposition into the pores of a porous anodic aluminum oxide (AAO) template. SEM and TEM images reveal that the nanowires of array are uniform, well isolated, and parallel to one another. The aspect ratio of nanowires is over 200. XRD and EDS pattern indicates that amorphous Co_0.71Pt_0.29 structure was formed during electro-deposition. In amorphous sample, magnetocrystal anisotropy is very small, therefore, shape anisotropy plays a dominant role which leads to strong perpendicular anisotropy. High coercivity (Hc=1.7 kOe) and squareness (Mr/Ms) around 0.7 were obtained in the samples when the field was applied parallel to the axis of the nanowires. However, when it changed to polycrystalline structure after annealing, due to the competition of magnetocrystal anisotropy and shape anisotropy, the sample did not display perpendicular anisotropy.     

Magnetic anisotropy-induced spin-reorientation in spinel FeCr2S4

In this paper, the low-field magnetic behavior of polycrystalline FeCr₂S₄ was investigated by thermal circling the sample from 5 to 200 K at a constant magnetic field. We show that, upon cooling the sample at 50 Oe to a temperature below the Curie temperature then warming back, the magnetization displays irreversibility between cooling and warming sequence. The irreversible behavior was suppressed gradually with increasing magnetic field. By considering spin-reorientation due to the increase of magnetic anisotropy upon cooling, the irreversible behavior has been explained qualitatively.     

Magnetic properties of Nd–Fe–B film magnets prepared by RF sputtering

Highly oriented films of ∼6 μm in thickness consisting of the Nd₂Fe₁₄B compound phase were obtained by a three-dimensional sputtering method at room temperature and the subsequent crystallization by annealing. The c-axis orientation and coercivity of film samples were sensitive to the sputtering parameters and annealing conditions. The optimum temperature and time for annealing were 650 °C and 30 min to show the highest coercivity without any deterioration for the orientation of Nd₂Fe₁₄B grains, and furthermore the degree of c-axis orientation was increased by decreasing the Ar gas pressure or input power for sputtering. The resultant film magnets with good magnetic properties of B_r=∼1.06 T, H_C=∼371 kA/m, and (BH)_max=∼160 kJ/m³ were obtained under the optimized parameters for sputtering.     

Hard magnetic properties of ErCo7−xCux [0.3⩽x⩽1] system

We report the observation of excellent hard magnetic properties on purely single phase ErCo_7−xCu_x compounds with x=0.3, 0.5, 0.8 and 1. Cu substitution leads to a decrease in the saturation magnetization, but enhances the uniaxial anisotropy in this system. The large anisotropy field (∼100 kOe) is attributed to the Er and the Co sublattices. Domain wall pinning effect seems to play a crucial role in determining the temperature and field dependences of magnetization in these compounds. The hard magnetic properties obtained at room temperature (RT) are comparable to the best results obtained in other RCo₇ based materials.     

Coercivity mechanism of Sm(Co, Cu)5

The mechanism of the high intrinsic coercivity of the Sm(Co_1−xCu_x)₅ (0≦x<1) system was studied by relating the coherency between the lattice constants of hexagonal Sm(Co, Cu)₅ and hcp Co to the coercive force. It was found analytically that the intrinsic coercive force reaches a maximum in the composition range from x=0.6 to 0.8, where the lattice mismatch approaches zero, so that there is a strong correlation between lattice matching and coercive force. When a Sm ion was located within a Sm(Co, Cu)₅ grain and in the outmost edge of the a and c planes of its grain surrounded or not surrounded by the coherent Co phase, the crystal field parameter at each Sm³⁺ site was calculated using a point charge model under the assumption that the Co and Cu atoms located in a grain and the hcp Co atoms situated at the interface uniformly have a charge of 3/5−. The results indicated that the Co phase precipitated coherently along the grain boundaries effectively enhances the magnetocrystalline anisotropy of Sm ions located in the outmost edges of the a and c planes of a Sm(Co, Cu)₅ grain.     

Effect of SiO2 nanopowders on magnetic properties and corrosion resistance of sintered Nd-Fe-B magnets

To improve the magnetic properties and corrosion resistance of magnet, SiO₂ nanopowders were added into Nd_28.25Dy_2.75Fe_balAl_0.15Ga_0.1Nb_0.1B_0.98-sintered magnets as grain boundary modifiers. It was found that the intrinsic coercivity (H_cj), remanence (B_r) and corrosion resistance were all improved with addition of certain amount of SiO₂ nanopowders. The optimum addition amount of SiO₂ nanopowders was found to be 0.01 wt%. Thermodynamic calculation in combination of energy dispersive X-ray spectroscopy (EDX) analyses indicated that SiO₂ nanopowders reacted with Nd of Nd-rich phase. As a result, the intergranular phase was modified, and the grain growth of main phase was restrained. It led to the optimization of microstructure.     

Electrodeposition and magnetic properties of Ni nanowire arrays on anodic aluminum oxide/Ti/Si substrate

Ni nanowire arrays with different diameters have now been extended to directly fabricate in porous anodic alumina oxide (AAO) templates on Ti/Si substrate by direct current (DC) electrodeposition. An aluminum film is firstly sputter-deposited on a silicon substrate coated with a 300 nm Ti film. AAO/Ti/Si substrate is synthesized by a two-step electrochemical anodization of the aluminum film on the Ti/Si substrate and then used as template to grow Ni nanowire arrays with different diameters. The coercivity and the squareness in parallel direction of Ni nanowires with about 10 nm diameters are 664 Oe and 0.90, respectively. The Ni nanowire arrays fabricated on AAO/Ti/Si substrates should lead to practical applications in ultrahigh-density magnetic storage devices because of the excellent properties.     

EPR and magnetic properties of MgO-CaO-SiO2-P2O5-CaF2-Fe2O3 glass-ceramics

Glass-ceramics have been derived from 4.5MgO(45−x)CaO34SiO₂16P₂O₅0.5CaF₂xFe₂O₃ (x=5, 10, 15, 20 wt%) glasses by heat treatment. Room temperature electron paramagnetic resonance (EPR) spectra and temperature-dependent magnetic susceptibility (χ) of the glass-ceramics have been obtained. The EPR absorption line centered at g≈4.3 disappeared at higher concentrations of iron oxide. The intensity and line width of the EPR absorption line centered at g≈2.1 increased as the iron oxide concentration was increased. Temperature-dependent magnetization of samples with low iron oxide content revealed ferrimagnetic as well as paramagnetic contributions. Information about the structural changes involving iron ions, their valence state and the type of magnetic interactions between the Fe ions as a function of composition was obtained using EPR and χ studies.     

Asymmetric Magnetization Reversal Probed by Recoil Loop Measurements inan Exchange Biased La0.67Sr0.33MnO3/La0.33Ca0.67MnO3 Bilayer Film

We exploit the recoil loop measurements to study La0.07 Sr0.33 Mn O3/La0.33 Ca0.67 Mn O3 bilayer film. the asymmetric magnetization reversal in an exchange-biased It is found that the recoil curve encloses a marked area only in the second quadrant of the hysteresis loop, and the recoil susceptibility in the descending branch of the major loop is evidently higher than that in the ascending branch. The study indicates that the exchange anisotropy of a unidirectional nature and an orientation deviated from the easy axis of the ferromagnetic layer plays a crucial role in creating the reversal asymmetry.     

Simple recipe to synthesize single-domain BaFe12O19 with high saturation magnetization

We report a new synthesis route for preparation of single-domain barium hexaferrite (BaFe₁₂O₁₉) particles with high saturation magnetization. Nitric acid, known as a good oxidizer, is used as a mixing medium during the synthesis. It is shown that formation of BaFe₁₂O₁₉ phase starts at 800 °C, which is considerably lower than the typical ceramic process and develops with increasing temperature. Both magnetization measurements and scanning electron microscope micrographs reveal that the particles are single domain up to 1000 °C at which the highest coercive field of 3.6 kOe was obtained. The best saturation magnetization of ≈60 emu/g at 1.5 T was achieved by sintering for 2 h at 1200 °C. Annealing at temperatures higher than 1000 °C increased the saturation magnetization, on the other hand, decreased the coercive field which was due to the formation of multi-domain particles with larger grain sizes. It is shown that the best sintering to obtain fine particles of BaFe₁₂O₁₉ occurs at temperatures 900-1000 °C. Finally, magnetic interactions between the hard BaFe₁₂O₁₉ phase and impurity phases were investigated using the Stoner-Wohlfarth model.     

Hydrogen-induced reduction of electric field gradient in La2Fe14BHx studied by NMR on La

The ¹³⁹La NMR spin-echo spectra of La₂Fe₁₄BH_x are reported. Since lanthanum has no 4f electrons, the observed quadrupole splittings are directly proportional to the lattice part of the electric field gradient, V_zz^lat. This quantity decreases as the content of interstitial hydrogen x grows. To describe the fall-off of V_zz^lat, a dimensionless function f₂(x) is introduced, normalised so that f₂(0)=1. Analysis of the new and earlier published data obtained by several experimental techniques demonstrates that the reduction of both the second-order crystal field parameter A₂₀ and the lattice electric field gradient V_zz^lat is described by the same function f₂(x) in all R₂Fe₁₄BH_x. The only distinction that needs to be made is between R being a light and a heavy rare earth.     

Structure and magnetic phase diagram of mixed rare-earth Nd1−xTbxFe10.5Mo1.5 compounds

The structural and magnetic properties of Nd_1−xTb_xFe_10.5Mo_1.5 (x=0$x=0$, 0.2, 0.4, 0.6, 0.8, 1.0) compounds have been investigated by means of X-ray diffraction and magnetic measurements. All the investigated compounds crystallize in the tetragonal ThMn₁₂-type structure with I4/mmm space group. The lattice parameters a, c and the unit-cell volume V decrease with increasing x. The Curie temperatures T_C are almost independent x. There exists a unique spin-reorientation transition for the end compositions of Nd_1−xTb_xFe_10.5Mo_1.5 compounds with x=0$x=0$ and x=1$x=1$, while two spin-reorientation transitions are observed for x=0.2–0.8$x=0.2–0.8$. The room-temperature magnetocrystalline anisotropy of Nd_1−xTb_xFe_10.5Mo_1.5 compounds changes from uniaxial to planar with increasing x content. Based on magnetic measurements, a magnetic phase diagram of Nd_1−xTb_xFe_10.5Mo_1.5 compounds is constructed. By minimizing the magnetocrystalline anisotropy energy, a theoretical magnetic phase diagram for the Nd_1−xTb_xFe_10.5Mo_1.5 system is derived, showing a reasonable agreement with the observations.     

Synthesis and magnetic properties of spinel CoFe2O4 nanowire arrays

Spinel CoFe₂O₄ nanowire arrays were synthesized in nanopores of anodic aluminum oxide (AAO) template using aqueous solution of cobalt and iron nitrates as precursor. The precursor was filled into the nanopores by vacuum impregnation. After heat treatment, it transformed to spinel CoFe₂O₄ nanowires. The structure, morphology and magnetic properties of the sample were studied by X-ray diffraction (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM) and vibrating sample magnetometer (VSM). The results indicate that the nanowire arrays are compact. And the individual nanowires have a high aspect ratio, which are about 80 nm in diameter and 10 μm in length. The nanowires are polycrystalline spinel phase. Magnetic measurements indicate that the nanowire arrays are nearly magnetic isotropic. The reason is briefly discussed. Moreover, the temperature dependence of the coercive force of the nanowire arrays was studied.     

Magnetic ordering in CeMnCuSi2

Temperature and field-dependent magnetization measurements on polycrystalline CeMnCuSi₂ reveal that the Mn moments in this compound exhibit ordering with a ferromagnetic (FM) component ordered instead of the previously reported purely antiferromagnetic (AFM) ordering. The FM ordering temperature, T_c, is about 120 K and almost unchanged with external fields up to 50 kOe. Furthermore, an AFM component (such as in a canted spin structure) is observed to be present in this phase, and its orientation is modified rapidly by the external magnetic field. The Ce L₃-edge X-ray absorption result shows that the Ce ions in this compound are nearly trivalent, very similar to that in the heavy fermion system CeCu₂Si₂. Large thermomagnetic irreversibility is observed between the zero-field-cooled (ZFC) and field-cooled (FC) M(T) curves below T_c indicating strong magnetocrystalline anisotropy in the ordered phase. At 5 K, a metamagnetic-type transition is observed to occur at a critical field of about 8 kOe, and this critical field decreases with increasing temperature. The FM ordering of the Mn moments in CeMnCuSi₂ is consistent with the value of the intralayer Mn–Mn distance R^a_Mn–Mn=2.890 Å, which is greater than the critical value 2.865 Å for FM ordering. Finally, a magnetic phase diagram is constructed for CeMnCuSi₂.     

Structural characterization and magnetization of Mg0.7Zn0.3SmxFe2−xO4 ferrites

Mg_0.7Zn_0.3Sm_xFe_2−xO₄ ferrites were prepared by the solid-state reaction method and were characterized by X-ray diffraction and magnetization measurements. A single spinel phase was obtained in the range 0.00?x?0.03$0.00?x?0.03$. The lattice parameter was found to increase at x=0.01$x=0.01$ and then decreases up to x=0.03$x=0.03$, which may indicate a distortion in the spinel lattice. The saturation magnetization was found to decrease with the increase in x up to 0.04, due to the replacement of the Fe³⁺ ions by the Sm³⁺ ions.     

Microstructure characterization and magnetic behavior of NiAlxFe2−xO4 and Ni1−yMnyAl0.2Fe1.8O4 ferrites

NiAl_xFe_2−xO₄ and Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites were prepared by the conventional ceramic method and were characterized by X-ray diffraction, scanning electron microscopy, and magnetic measurements. The single spinel phase was confirmed for all prepared samples. A proper explanation of data is possible if the Al³⁺ ions are assumed to replace Fe³⁺ ions in the A and B sites simultaneously for NiAl_xFe_2−xO₄ ferrites, and if the Mn²⁺ ions are assumed to replace Ni²⁺ ions in the B sites for Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites. Microstructural factors play an important role in the magnetic behavior of Ni_1−yMn_yAl_0.2Fe_1.8O₄ ferrites with large Mn²⁺ content.     

Room temperature ferromagnetism and magnetotransport properties of the layered manganite system La1.2Ba1.8Mn2−xRuxO7 (0≤x≤1.0)

The dc magnetization and ac susceptibility measurements on two dimensional layered manganite La_1.2Ba_1.8Mn₂O₇ samples reveal the occurrence of ferromagnetism above room temperature with ferromagnetic (FM) to paramagnetic (PM) transitions at 338 K. The bifurcation temperatures shown by the zero-field cooled (ZFC) and field cooled (FC) dc magnetization curves at high temperatures shift towards lower temperatures as the applied field is increased from 100 to 2500 Oe. The data are suggestive of a large magnetic anisotropy due to the strong competing ferromagnetic and antiferromagnetic interactions resulting in a spin-glass-like state. Ru doping is found to enhance the ferromagnetism and metallicity of the system in a remarkable way. The magnetoresistance (MR) values obtained are very high and about 40% even at 260 K for the undoped sample.