The electrical, optical and magnetic properties of Si-doped ZnO films

In this paper, the influences of Si-doping on electrical, optical and magnetic properties of ZnO films have been systematically investigated. It is found that the resistivity of the films decreases from 3.0 × 10³ to 6.2 × 10^-2 Ωcm with Si-doping due to the increase of carrier concentration. The bandgap of ZnO films increases from 3.28 to 3.52 eV with increasing of Si concentration, which is found to be due to the collective effects of bandgap narrowing and Burstein-Moss effect induced by high carrier concentration. With increase of Si concentration, the near band edge (NBE) emission decreases due to the deterioration of crystal quality, while the yellow emission enhances due to the increase of extrinsic impurity or defects. The additional Si-doping has a profound influence on the enhancement of magnetic property and the maximum magnetic moment of 2.6 μ_B/Si is obtained. The ferromagnetic ordering is seen to be correlated with carrier concentration and structural defects.     

Analysis of Raman scattering of Ga1−xMnxAs dilute magnetic semiconductor

Ferromagnetic Ga_1−xMn_xAs layers (where x=1.4-3.0%) grown on (1 0 0) GaAs substrates by molecular beam epitaxy were characterized using Raman spectroscopy. As Mn is introduced into GaAs, a marked increase in disorder in the material occurs, as indicated by the growth of the disorder-allowed transverse-optical Raman line. Another important result is that as the Mn concentration in Ga_1−xMn_xAs increases further beyond ca. 2%, Raman-active coupled-plasmon-longitudinal-optical phonon modes arise, which signals the increasing presence of holes, and thus provides a useful tool for determining their concentration. Using the depletion-layer approach from the Raman spectroscopy data, we determined the carrier concentration for samples with x=2.2% and 3.0% was to be 7.2×10¹⁹ and 8.3×10²⁰ cm⁻³, respectively.     

Optical and magnetic properties of laser-deposited Co-doped ZnO thin films

We report the optical and magnetic properties of laser-deposited Zn_1−xCo_xO (x=0.06-0.3) thin films with no intentional electrical carrier doping. The analysis of the high-temperature magnetization data provides an unambiguous evidence that antiferromagnetic superexchange interaction is the dominant mechanism of the exchange coupling between Co ions in Zn_1−xCo_xO alloy, yielding the value of the effective exchange integral J₁/k_B to be about −27 K. The low-temperature magnetization data reveals a spin glass transition in Zn_1−xCo_xO alloy for the Co content x>0.15, giving the value of the spin freezing temperature T_f to be ∼8 and ∼12 K for x=0.2 and 0.25, respectively. Optical spectra analysis shows a linear increase of the band gap E_g with the increase of the Co content following E_g=3.231+1.144x eV.     

Magnetic behavior of MnAs precipitates in Ga1−xMnxAs diluted magnetic semiconductor

Ferromagnetic Ga_1−xMn_xAs layers (where x≈4.7–5.5%) were grown on (1 0 0) GaAs substrates by molecular beam epitaxy. These p-type (Ga,Mn)As films were revealed to have a ferromagnetic structure and ferromagnetism is observed up to a Curie temperature of 318 K, which is ascribed to the presence of MnAs secondary magnetic phases within the film. It is highly likely that the phase segregation occurs due to the high Mn cell temperature around 890–920 °C, as it is well established that GaMnAs is unstable at such a high temperature. The MnAs precipitate in the samples with x≈4.7–5.5% has a Curie temperature T_c≈318 K, which was characterized from field-cooled and zero-field-cooled magnetization curves.     

Band-edge exciton transitions in (Ga1−xMnx)N diluted magnetic semiconductor films with above room temperature ferromagnetic transition

(Ga_1−xMn_x)N thin films grown on GaN buffer layers by using molecular beam epitaxy were investigated with the goal of producing diluted magnetic semiconductors (DMSs) with band-edge exciton transitions for applications in optomagnetic devices. The magnetization curve as a function of the magnetic field at 5 K indicated that ferromagnetism existed in the (Ga_1−xMn_x)N thin films, and the magnetization curve as a function of the temperature showed that the ferromagnetic transition temperature of the (Ga_1−xMn_x)N thin film was above room temperature. Photoluminescence and photoluminescence excitation spectra showed that band-edge exciton transitions in (Ga_1−xMn_x)N thin films appeared. These results indicate that the (Ga_1−xMn_x)N DMSs with a magnetic single phase hold promise for potential applications in spin optoelectronic devices in the blue region of the spectrum.     

Magnetic and structural properties of Fe ion-implanted GaN

The magnetic and structural properties of Fe ion-implanted GaN was investigated by various measurements. XRD results did not show any peaks associated with second phase formation. The magnetization curve at 5 K showed ferromagnetic behavior for 900 °C-annealed sample. In zero-field-cooled (ZFC) and field-cooled (FC) magnetization measurements, the irreversibility and a cusp-like behavior of the ZFC curve were observed for 900 °C-annealed sample. These behaviors are typically observed in superparamagnetic or spin glass phase. While the temperature dependence magnetization of 800 °C-annealed sample showed non-Brillouin-like curve and it is not exhibited ferromagnetic hysteresis at 5 K. In XPS measurement, the coexistence of metallic Fe (Fe⁰) and Fe–N bond (Fe²⁺ and Fe³⁺) for Fe 2p core level spectra is observed in as-implanted sample. But 700–900 °C-annealed samples showed only Fe–N bond (Fe²⁺ and Fe³⁺) spectra. For Ga 3d core level spectra only Ga–N bonds showed for as implanted with 700–900 °C-annealed samples. From XPS results, it could be explained that magnetic property of our films originated from FeN structures.     

Structural and Magnetic Properties of Sm Implanted GaN

The structural and magnetic properties of Sm ion-implanted GaN with different Sm concentrations are investigated. XRD results do not show any peaks associated with second phase formation. Magnetic investigations performed by superconducting quantum interference device reveal ferromagnetic behavior with an ordering tem- perature above room temperature in all the implanted samples, while the effective magnetic moment per Sin obtained from saturation magnetization gives a much higher value than the atomic moment of Sm. These results could be explained by the phenomenological model proposed by Dhar et al. [Phys. Rev. Lett. 94（2005）037205, Phys. Rev. B 72（2005）245203] in terms of a long-range spin polarization of the GaN matrix by the Sm atoms.     

Effect of annealing on the electric and magnetic properties of GaMnAs and Be-codoped GaMnAs

GaMnAs and Be-codoped GaMnAs films grown via molecular beam epitaxy (MBE) were heat treated and the stability of Mn in the matrix was investigated. MnAs had a stable phase at the low growth temperature, but MnGa was stable at the annealing temperature. Be-codoping did not prevent the precipitation processes, but Be itself was stable during the annealing process to maintain the GaAs matrix at the high conductivity.     

Stabilization of ferromagnetism in Mn doped ZnO with C co-doping

We present a method for stabilizing ferromagnetism in Mn doped ZnO. We find that Mn doped ZnO show anti-ferromagnetic order in the absence of additional carriers. When Mn doped ZnO is co-doped with C atom at O sites ferromagnetic state gets stabilized. The C doping creates holes which leads to stabilization of ferromagnetic state via hole mediated double exchange mechanism.     

Structural, magnetic properties and photoemission study of Ni-doped ZnO

Nickel-doped ZnO (Zn_1−xNi_xO) have been produced using rf magnetron sputtering. X-ray diffraction measurements revealed that nickel atoms were successfully incorporated into ZnO host matrix without forming any detectable secondary phase. Ni 2p core-level photoemission spectroscopy confirmed this result and suggested Ni has a chemical valence of 2+. According to the magnetization measurements, no ferromagnetic but paramagnetic behavior was found for Zn_0.86Ni_0.14O. We studied the electronic structure of Zn_0.86Ni_0.14O by valence-band photoemission spectroscopy. The spectra demonstrate a structure at ∼2 eV below the Fermi energy E_F, which is of Ni 3d origin. No emission was found at E_F, suggesting the insulating nature of the film.     

Growth and characterization of rocksalt MnS/GaAs epilayers by hot-wall epitaxy

Epitaxial growth characteristics of α-MnS on GaAs(1 0 0) substrates have been investigated by X-ray diffraction and double crystal rocking curve measurements. Growth of stoichiometric α-MnS films has been performed by hot-wall epitaxy using Mn and ZnS as a source of sulfur. The films on GaAs(1 0 0) at low substrate temperature exhibit multiphase crystal structures of zincblende and rocksalt, and the main structure is changed to rocksalt with increasing substrate temperature. Photoluminescence spectrum of the α-MnS epilayer at 5 K exhibits broad emission bands, which are attributed to Mn²⁺ ions. The band gap energy of the α-MnS epilayer at room temperature was also estimated to be about 3.3 eV by reflection.     

Unidirectional variation of lattice constants of Al-N-codoped ZnO films by RF magnetron sputtering

Al-N-codoped ZnO films were fabricated by RF magnetron sputtering in the ambient of N₂ and O₂ on silicon (1 0 0) and homo-buffer layer, subsequently, annealed in O₂ at low pressure. X-ray diffraction (XRD) spectra show that as-grown and 600 °C annealed films grown by codoping method are prolonged along crystal c-axis. However, they are not prolonged in (0 0 1) plane vertical to c-axis. The films annealed at 800 °C are not prolonged in any directions. Codoping makes ZnO films unidirectional variation. X-ray photoelectron spectroscopy (XPS) shows that Al content hardly varies and N escapes with increasing annealing temperature from 600 °C to 800 °C.     

Structural, electronic and magnetic properties of Cr-doped (ZnTe)12 clusters

We have studied the energetics and magnetism in Cr-doped (ZnTe)₁₂ clusters by first principles density functional calculations. Total energy calculations suggest that it is energetically most favourable for Cr atoms to substitute at Zn sites. Both ferromagnetic and anti-ferromagnetic coupling between the Cr atoms exist depending on the Cr-Cr distance in the clusters. The magnetic exchange coupling between Cr atoms is short-ranged.     

Optical and magnetic properties of (Ga1−xMnx)N/GaN digital ferromagnetic heterostructures

(Ga_1−xMn_x)N/GaN digital ferromagnetic heterostructures (DFHs) and (Ga_1−xMn_x)N/GaN grown on GaN buffer layers by using molecular beam epitaxy have been investigated. The photoluminescence (PL) spectra showed band-edge exciton transitions. They also showed peaks corresponding to the neutral donor-bound exciton and the exciton transitions between the conduction band and the Mn acceptor, indicative of the Mn atoms acting as substitution. The magnetization curves as functions of the magnetic field at 5 K indicated that the saturation magnetic moment in the (Ga_1−xMn_x)N/GaN DFHs decreased with increasing Mn mole fraction and that the saturation magnetic moment and the coercive field in the (Ga_1−xMn_x)N/GaN DFHs were much larger than those in (Ga_1−xMn_x)N thin films. These results indicate that the (Ga_1−xMn_x)N/GaN DFHs hold promise for potential applications in spintronic devices.     

Synthesis and magnetic properties of Ni-doped zinc oxide powders

Polycrystalline Zn_1−xNi_xO diluted magnetic semiconductors have been successfully synthesized by an auto-combustion method. X-ray diffraction measurements indicated that the 5 at% Ni-doped ZnO had the pure wurtzite structure. Refinements of cell parameters from powder diffraction data revealed that the cell parameters of Zn_0.95Ni_0.05O were a little bit larger than ZnO. Transmission electron microscopy observation showed that the as-synthesized powders were of the size ∼60 nm. Magnetic investigations showed that the nanocystalline Zn_0.95Ni_0.05O possessed room temperature ferromagnetism with the saturation magnetic moment of 0.1 emu/g (0.29 μ_B/Ni²⁺).     

Magnetic and structural study of Cu-doped TiO2 thin films

Transparent pure and Cu-doped (2.5, 5 and 10 at.%) anatase TiO₂ thin films were grown by pulsed laser deposition technique on LaAlO₃ substrates. The samples were structurally characterized by X-ray absorption spectroscopy and X-ray diffraction. The magnetic properties were measured using a SQUID. All films have a FM-like behaviour. In the case of the Cu-doped samples, the magnetic cycles are almost independent of the Cu concentration. Cu atoms are forming CuO and/or substituting Ti in TiO₂. The thermal treatment in air promotes the CuO segregation. Since CuO is antiferromagnetic, the magnetic signals present in the films could be assigned to Cu substitutionally replacing cations in TiO₂.     

The role of the dopant in the magnetism of Fe-doped SnO2 films

Transparent pure and Fe-doped SnO₂ thin films were grown by pulsed laser deposition technique on LaAlO₃ substrates. X-ray diffraction shows that the films are polycrystalline and have the rutile structure. Surprisingly, the pure film presents magnetic-like behavior at room temperature with a saturated magnetization of almost one-third of the doped film (∼3.6 and 11.3 emu/g, respectively) and its magnetization could not be attributed to any impurity phase. Taking into account the magnetic moment measured in the pure film, the effective contribution of the impurity in the doped one can be inferred to be ∼2 μ_B per Fe atom. A large magnetic moment was also predicted by an ab initio calculation in the doped system, which increases if an oxygen vacancy is present near the Fe impurity.     

Influence of Mn-Doped Content on Ferromagnetism of Ga1-xMnxN Film Grown by LP-MOVPE

The diluted magnetic semiconductor Ga_1-xMn_xN was achieved by low-pressure metal organic vapour-phase epitaxy (LP-MOVPE). Proton-induced x-ray emission was employed non-destructively, quickly and accurately to determine the Mn-doped content. The magnetic property was measured by a superconducting-quantum-interference-device (SQID) magnetometer. Apparent ferromagnetic hysteresis loops measured at or above room temperature are presented. No ferromagnetic secondary phases were detected by high-resolution x-ray diffraction. The experimental results show that the ferromagnetic signal firstly decreases and then increases with the increasing Mn-doped content from 0.23% to 4.69% and it is the weakest when Mn content is 0.51%. The annealing treatment could make the ferromagnetic property stronger.     

Synthesis and magnetic properties of Mn doped ZnO nanowires

Mn doped ZnO nanowires have been synthesized using a simple autocombustion method. The as-synthesized Mn doped ZnO nanowires were characterized by X-ray diffraction and transmission electron microscopy. An increase in the hexagonal lattice parameters of ZnO is observed on increasing the Mn concentration. Optical absorption studies show an increment in the band gap with increasing Mn content, and also give evidence for the presence of Mn²⁺ ions in tetrahedral sites. All Zn_1−xMn_xO (0≤x≤0.25) samples are paramagnetic at room temperature. However, a large increase in the magnetization is observed below 50 K. This behavior, along with the negative value of the Weiss constant obtained from the linear fit to the susceptibility data below room temperature, indicate ferrimagnetic behavior. The origin of ferrimagnetism is likely to be either the intrinsic characteristics of the Mn doped samples, or due to some spinel-type impurity phases present in the samples that could not be detected.     

Electromodulation of the magnetoresistance in diluted magnetic semiconductors based heterostructures

We study the properties of heterostructures formed by two layers of a diluted magnetic semiconductor separated by a nonmagnetic semiconductor layer. We find that there is a RKKY-type exchange coupling between the magnetic layers that oscillates between ferromagnetic and antiferromagnetic as a function of the different parameters in the problem. The different transport properties of these phases make that this heterostructure presents strong magnetoresistive effects. The coupling can be also modified by an electric field. We propose that it is possible to alter dramatically the electrical resistance of the heterostructure by applying an electric field. Our results indicate that in a single gated sample the magnetoresistance could be modulated by an electrical bias voltage.