Superparamagnetic behavior of La0.67Sr0.33MnO3 nanoparticles prepared via sol-gel method

Magnetic nanoparticles of La_0.67Sr_0.33MnO₃ (LSMO) manganite were prepared by sol-gel method. Phase formation and crystal structure of the synthesized powder were examined by the X-ray diffraction (XRD) using the Rietveld analysis. The mean particle size was determined by the transmission electron microscopy (TEM). Infrared transmission spectroscopy revealed that stretching and bending modes are influenced by calcinations temperature. The temperature dependence of the ac magnetic susceptibility was measured at different frequencies and ac magnetic fields in the selected ranges of 40-1000 Hz and 80-800 A/m, respectively. The temperature dependence of ac susceptibility shows a characteristic maxima corresponding to the blocking temperature near room temperature. The frequency dependence of the blocking temperature is well described by the Vogel-Fulcher law. By fitting the experimental data with this law, the relaxation time τ₀=1.7×10⁻¹² s, characteristic temperature T₀=262±3 K, anisotropy energy E_a/k=684±15 K and effective magnetic anisotropy constant k_eff=2.25×10⁴ erg/cm³ have been obtained. dc Magnetization measurement versus magnetic field shows that some of LSMO nanoparticles are blocked at 293 K. The role of magnetic interparticle interactions on the magnetic behavior is also investigated.     

On-chip free-flow magnetophoresis: Separation and detection of mixtures of magnetic particles in continuous flow

The complete separation of mixtures of magnetic particles was achieved by on-chip free-flow magnetophoresis. In continuous flow, magnetic particles were deflected from the direction of laminar flow by a perpendicular magnetic field depending on their magnetic susceptibility and size and on the flow rate. 2.8 and 4.5 μm superparamagnetic particles with magnetic susceptibilities of 1.1×10⁻⁴ and 1.6×10⁻⁴ m³ kg⁻¹, respectively, could be completely separated from each other reproducibly. The separated particles were detected by video observation and also by on-chip laser light scattering. Potential applications of this separation method include sorting of magnetic micro- and nanoparticles as well as magnetically labelled cells.     

Temperature dependence of magnetic anisotropy constant in cobalt ferrite nanoparticles

The temperature dependence of the effective magnetic anisotropy constant K(T) of CoFe₂O₄ nanoparticles is obtained based on the SQUID magnetometry measurements and Mössbauer spectroscopy. The variation of the blocking temperature T_B as a function of particle radius r is first determined by associating the particle size distribution and the anisotropy energy barrier distribution deduced from the hysteresis curve and the magnetization decay curve, respectively. Finally, the magnetic anisotropy constant at each temperature is calculated from the relation between r and T_B. The resultant effective magnetic anisotropy constant K(T) decreases markedly with increasing temperature from 1.1×10⁷ J/m³ at 5 K to 0.6×10⁵ J/m³ at 280 K. The attempt time τ₀ is also determined to be 6.1×10⁻¹² s which together with the K(T) best explains the temperature dependence of superparamagnetic fraction in Mössbauer spectra.     

Temperature dependence of magnetic anisotropy in nanoparticles of CoxFe(3−x)O4

In this paper we present a study of the magnetic anisotropy constant of nanocrystalline magnetic particles of Co_xFe_(3−x)O₄, with x ranging from 0.05 to 1.6, synthesized by a combustion reaction. The magnetic anisotropy constants were obtained by fitting the high-field part of the major hysteresis loops with the law of approach equation down to temperatures of 4 K and up to fields of 60 kOe. The anisotropy constant depends strongly on both temperature and cobalt content x, exhibiting a nonmonotic dome-shaped dependence on x with a maximum at x=1.0. We found that fits at lower temperatures, i.e., 4 and 72 K, give values of K₁ that are approximately one order of magnitude higher than those at higher temperatures, i.e., 272 and 340 K. For example, K₁ for specimens with x=0.8 and 1.0 are 4.21×10⁷ and 4.22×10⁷ ergs/cm³ at 4 K, and 7.64×10⁶ and 7.51×10⁶ ergs/cm³ at 340 K, respectively. Thus, our determination of temperature-dependence of the anisotropy constant represents an improvement over existing works.     

Electrical characterization and carrier transportation in Hf-silicate dielectrics using ALD gate stacks for 90 nm node MOSFETs

Metal-oxide-semiconductor capacitors (MOSCs) and metal-oxide-semiconductor field-effect transistors (MOSFETs) incorporating hafnium silicate (Hf-silicate) dielectrics were fabricated by using atomic layer deposition (ALD). The electrical properties of these Hf-silicate thin films with various postnitridation annealing (PNA) temperatures were then examined to find the best nitridation condition. It is found that the best conditions to achieve the lowest gate leakage current and best equivalent oxide thickness (EOT) are when PNA is performed at 800 °C in NH₃ ambient for 60 s. To understand the obtained film, carrier transportation mechanisms, the temperature dependence of the leakage current was measured from 300 K to 500 K for both gate injection and substrate injection. The result reveals that the leakage mechanisms involve Schottky emission at high temperature and low electrical field and Poole-Frenkle emission at low temperature and high electrical field. The barrier heights of poly-Si/Hf-silicate and Hf-silicate/Si interfaces extracted from Schottky emission are 1.1 eV and 1.04 eV, respectively. The interface traps per unit area, the mean density of interface traps per area and energy and the mean capture cross-section are determined about 8.1 × 10¹⁰ cm⁻², 2.7 × 10¹¹ cm⁻² eV⁻¹ and 6.4 × 10⁻¹⁵ cm⁻² using charge pumping method.     

Thermally activated magnetization reversal process of self-assembled Fe55Co45 nanowire arrays

We have investigated the temperature dependence of the magnetic properties and the magnetic relaxation of the Fe₅₅Co₄₅ nanowire arrays electrodeposited into self-assembled porous alumina templates with the diameter about 10 nm. X-ray diffraction (XRD) pattern indicates that the nanowire arrays are BCC structure with [1 1 0] orientation along the nanowire axes. Owing to the strong shape anisotropy, the nanowire arrays exhibit uniaxial magnetic anisotropy with the easy magnetization direction along the nanowire axes. The coercivity at 5 K can be explained by the sphere chains of the symmetric fanning mechanism. The temperature dependence of coercivity can be interpreted by thermally activated reversal mechanism as being the localized nucleation reversal mechanism with the activation volume much smaller than the wire volume. Strong field and temperature-dependent magnetic viscosity effects were also observed.     

Spin-wave resonance and magnetic anisotropy in FePt thin films

Ferromagnetic Resonance (FMR) measurements at room temperature and X-band microwave frequency were performed on polycrystalline FePt thin films with face-centered cubic structure. With the external field perpendicular to the film plane, the absorption fields H_n of the odd and even spin-wave resonance modes n detected for the Fe_0.44Pt_0.56(45 nm)/Si(1 0 0) and Fe_0.51Pt_0.49(105 nm)/Pt(55 nm)/MgO(1 0 0) films, were found to obey the well-known H_n×n² ratio, giving for these films the exchange stiffness constant values of 3.9×10⁻⁸ and 4.4×10^–7 erg/cm, respectively. The study of the out-of-plane angular dependence of the absorption field of the uniform FMR mode allowed the measurement of the effective magnetic anisotropy constants of 5.3×10⁶ , 6.4×10⁶ , and 6.7×10⁶ erg/cm³, related, respectively, to the [1 1 1], [1 0 0], and [1 1 0] textures present in the films.     

Dependence of magnetic anisotropy of the La0.67Ca0.33MnO3 films on substrate and film thickness

Strain in the La_0.67Ca_0.33MnO₃ films has been tuned by varying substrate and film thickness, and its effects on magnetic anisotropy are studied based on the measurements of isothermal magnetization. Measuring the strain in the films by the out-of-plane lattice parameter (c), we found a strong dependence of the magnetic anisotropy constant (Ku) on strain. Ku decreases linearly from ∼−1.1×10⁶ erg/cm³ for c=0.763 nm to 1.2×10⁶ erg/cm³ for c=0.776 nm, corresponding to a change from tensile strain to compressive strain. Positive Ku signifies a uniaxial anisotropy with the easy axis perpendicular to the film plane, while negative Ku demonstrates an anisotropy of the easy plane character. Smaller or larger c leads a decrease or increase in Ku, which indicates the presence of other effects in addition to those associated with strain. Three distinctive processes for the magnetization are observed along the hard magnetic axis of the films on (001)SrTiO₃, suggesting a possibility of strain relaxation even in ultra-thin films.     

Spin-glass behavior and magnetocaloric effect in Tb-based bulk metallic glass

A noncollinear-ferromagnetic spin-glass-like state was observed in Tb₅₅Co₂₀Al₂₅ bulk metallic glass due to the strong random magnetic anisotropy. Associated with this behavior, we observed a comparatively large magnetic entropy change (ΔS_m is 9.75 J K⁻¹ kg⁻¹) in a field change of 7 T and a correspondingly high value of the magnetic refrigeration capacity (RC is 540 J kg⁻¹) with almost no hysteresis loss in the vicinity of the so-called Curie temperature. This opens the possibility of using this material for magnetic cooling purposes.     

High-temperature magnetic properties of noninteracting randomly oriented single-domain Fe3 − δO4 nanoparticles

Magnetic measurements have been performed on 40-nm sphere-like Fe_3 − δO₄ (δ=0.043) nanoparticles using a Quantum Design vibrating sample magnetometer. Coating Fe_3 − δO₄ nanoparticles with SiO₂ effectively eliminates magnetic interparticle interactions so that the coercive field HC in the high-temperature range between 300 K and the Curie temperature (855 K) can be well fitted by an expression for noninteracting randomly oriented single-domain particles. From the fitting parameters, the effective anisotropy constant K is found to be (1.38±0.11)×¹⁰⁵ erg/cm³, which is very close to the bulk magnetocrystalline anisotropy constant of 1.35×¹⁰⁵ erg/cm³. Moreover, the inferred mean particle diameter from the fitting parameters is in quantitative agreement with that determined from transmission electron microscope. Such a quantitative agreement between data and theory suggests that the ensemble of our SiO₂-coated sphere-like Fe_3 − δO₄ nanoparticles represents a good system of noninteracting randomly-oriented single-domain particles.     

Van der Pauw resistivity measurements on evaporated thin films of cadmium arsenide, Cd3As2

Cadmium arsenide is a II-V semiconductor, exhibiting n-type intrinsic conductivity with high mobility and narrow bandgap. It is deposited by thermal evaporation, and has shown the Schottky and Poole-Frenkel effects at high electric fields, but requires further electrical characterisation. This has now been extended to low-field van der Pauw lateral resistivity measurements on films of thickness up to 1.5 μm. Resistivity was observed to decrease with increasing film thickness up to 0.5 μm from about 3 × 10⁻³ Ω m to 10⁻⁵ Ω m, where the crystalline granular size increases with film thickness. This decrease in resistivity was attributed to a decrease in grain boundary scattering and increased mobility. Substrate temperature during deposition also influenced the resistivity, which decreased from around 10⁻⁴ Ω m to (10⁻⁵ to 10⁻⁶) Ω m for an increase in substrate deposition temperature from 300 K to 423 K. This behaviour appears to result from varying grain sizes and ratios of crystalline to amorphous material. Resistivity decreased with deposition rate, reaching a minimum value at about 1.5 nm s⁻¹, before slowly increasing again at higher rates. It was concluded that this resulted from a dependence of the film stoichiometry on deposition rate. The dependence of resistivity on temperature indicates that intercrystalline barriers dominate the conductivity at higher temperatures, with a hopping conduction process at low temperatures.     

Magnetic and magnetocaloric properties of the intermetallic compound TbNiAl

Magnetization measurements have been carried out on the intermetallic compound TbNiAl in applied fields up to 120 kOe. Temperature dependence of magnetization under zero-field-cooled and field-cooled conditions shows thermomagnetic irreversibility, which is attributed to magnetic frustration. With the increase of field, the irreversibility decreases and vanishes completely at high fields. Magnetocaloric effect has been calculated in terms of isothermal magnetic entropy change using magnetization isotherms obtained at various temperatures. The maximum entropy change is 13.8 J kg⁻¹ K⁻¹ near the ordering temperature for a field change of 50 kOe. The refrigerant capacity is found to be 494 J kg⁻¹ for the same field change and for a temperature difference of 52 K between the cold and the hot sinks.     

Propagation regimes of intense circularly polarized laser beam in magnetoactive plasma

This paper presents an analytical and numerical investigation of an intense circularly polarized wave propagating along the static magnetic field parallel to oscillating magnetic field in magnetoactive plasma. In the relativistic regime such a magnetic field is created by pulse itself. The authors have studied different regimes of propagation with relativistic electron mass effect for magnetized plasma. An appropriate expression for dielectric tensor in relativistic magnetoactive plasma has been evaluated under paraxial theory. Two modes of propagation as extraordinary and ordinary exist; because of the relativistic effect, ultra-strong magnetic fields are generated which significantly influence the propagation of laser beam in plasma. The nature of propagation is characterized through the critical-divider curves in the normalized beam width with power plane For given values of normalized density (ω_p/ω) and magnetic field (ω_c/ω) the regions are namely steady divergence (SD), oscillatory divergence (OD) and self-focusing (SF). Numerical computations are performed for typical parameters of relativistic laser-plasma interaction: magnetic field B = 10-100 MG; intensity I = 10¹⁶ to 10²⁰ W/cm²; laser frequency ω = 1.1 × 10¹⁵ s⁻¹; cyclotron frequency ω_c = 1.7 × 10¹³ s⁻¹; electron density n_e = 2.18 × 10²⁰ cm⁻³. From the calculations, we confirm that a circularly polarized wave can propagate in different regimes for both the modes, and explicitly indicating enhancement in wave propagation, beam focusing/self-guiding and penetration of E-mode in presence of magnetic field.     

Heat dissipation mechanism of magnetite nanoparticles in magnetic fluid hyperthermia

The relative contributions of Néel and Brownian relaxations on magnetic heat dissipation were studied by investigating the physical, magnetic and heating characteristics of magnetite nanoparticle suspensions with average diameters of 12.5 and 15.7 nm. Heating characteristics depended on the dispersion states of particles. The specific absorption rates (SAR) dropped by 27% for the 12.5 nm particles to 16.8×10⁻⁹ W g⁻¹ Oe⁻² Hz⁻¹ and by 67% for the 15.7 nm particles to 9.69×10⁻⁹ W g⁻¹ Oe⁻² Hz⁻¹, when the particle rotation was suppressed by dispersing magnetite nanoparticles in hydro-gel.     

The spectral sensitivity of long period gratings fabricated in elliptical core D-shaped optical fibre

Long period gratings (LPGs) were written into a D-shaped optical fibre that has an elliptical core with a W-shaped refractive index profile and the first detailed investigation of such LPGs is presented. The LPGs’ attenuation bands were found to be sensitive to the polarisation of the interrogating light with a spectral separation of about 15 nm between the two orthogonal polarisation states. A finite element method was successfully used to model many of the behavioural features of the LPGs. In addition, two spectrally overlapping attenuation bands corresponding to orthogonal polarisation states were observed; modelling successfully reproduced this spectral feature. The spectral sensitivity of both orthogonal states was experimentally measured with respect to temperature and bending. These LPG devices produced blue and red wavelength shifts depending upon the orientation of the bend with measured maximum sensitivities of −3.56 and +6.51 nm m, suggesting that this type of fibre LPG may be useful as a shape/bend orientation sensor with reduced errors associated with polarisation dependence. The use of neighbouring bands to discriminate between temperature and bending was also demonstrated, leading to an overall curvature error of ±0.14 m⁻¹ and an overall temperature error of ±0.3 °C with a maximum polarisation dependence error of ±8 × 10⁻² m⁻¹ for curvature and ±5 × 10⁻² °C for temperature.     

Order-disorder transformation in FePt nanoparticles studied by ferromagnetic resonance

We have investigated the ferromagnetic resonance (FMR) response of as-made and temperature annealed FePt magnetic nanoparticles. The as-made nanoparticles, which have been fabricated by a chemical route, crystallize in the low magnetic anisotropy fcc phase and have a diameter in the range of 2-4 nm. The annealing of the particles at high temperatures (T_A=550, 650 and C) in an inert Ar atmosphere produces a partial transformation to the high magnetocrystalline anisotropy L1₀ phase, with a significant increase in particle size and size distribution. FMR measurements at X-band (9.5 GHz) and Q-band (34 GHz) show a single relatively narrow line for the as-synthesized particles and a structure of two superimposed lines for the three annealed samples. The origin of this line shape has been attributed to the presence of the disordered fcc phase. Assuming that the system consists of a collection of identical particles with a random distribution of easy axes, we have been able to estimate a mean value for the magnetic anisotropy constant of the particles in the fcc phase, K∼2×10⁶ erg/cm³. The measured line shape in the annealed samples can be explained if we consider that the magnetic anisotropy of the particles has a gaussian distribution with a relatively broad width.     

Synthesis and magnetic properties of the size-controlled Mn-Zn ferrite nanoparticles by oxidation method

Size-controlled Mn_0.67Zn_0.33Fe₂O₄ nanoparticles in the wide range from 80 to 20 nm have been synthesized, for the first time, using the oxidation method. It has been demonstrated that the particle size can be tailor-made by varying the concentration of the oxidant. The magnetization of the 80 nm particles was 49 A m² kg⁻¹ compared to 34 A m² kg⁻¹ for the 20 nm particles. The Curie temperatures for all the samples are found to be within 630±5 K suggesting that there is no size-dependent cation distribution. The critical particle size for the superparamagnetic limit is found to be about 25 nm. The effective magnetic anisotropy constant is experimentally determined to be 7.78 kJ m⁻³ for the 25 nm particles, which is about an order of magnitude higher than that of the bulk ferrite.     

Ferromagnetism in amorphous Ge1−xMnx grown by low temperature vapor deposition

Magnetic properties of amorphous Ge_1−xMn_x thin films were investigated. The thin films were grown at 373 K on (100) Si wafers by using a thermal evaporator. Growth rate was ∼35 nm/min and average film thickness was around 500 nm. The electrical resistivities of Ge_1−xMn_x thin films are 5.0×10⁻⁴∼100 Ω cm at room temperature and decrease with increasing Mn concentration. Low temperature magnetization characteristics and magnetic hysteresis loops measured at various temperatures show that the amorphous Ge_1−xMn_x thin films are ferromagnetic but the ferromagnetic magnetizations are changing gradually into paramagnetic as increasing temperature. Curie temperature and saturation magnetization vary with Mn concentration. Curie temperature of the deposited films is 80-160 K, and saturation magnetization is 35-100 emu/cc at 5 K. Hall effect measurement at room temperature shows the amorphous Ge_1−xMn_x thin films have p-type carrier and hole densities are in the range from 7×10¹⁷ to 2×10²² cm⁻³.     

Nonlinear optical properties and photoinduced anisotropy of an azobenzene ionic liquid-crystalline polymer

The nonlinear optical properties and photoinduced anisotropy of an azobenzene ionic liquid-crystalline polymer were investigated. The single beam Z-scan measurement showed the polymer film possessed a value of nonlinear refractive index n₂ = −1.07 × 10⁻⁹ cm²/W under a picosecond 532 nm excitation. Photoinduced anisotropy in the polymer was studied through dichroism and photoinduced birefringence. A photoinduced birefringence value Δn ∼ 10⁻² was achieved in the polymer film. The mechanism for the nonlinear optical response and the physical process of photoinduced anisotropy in the polymer were discussed.     

Antiferromagnetic resonance study of sodalite loaded with sodium by multi-frequency ESR

We have carried out electron spin resonance (ESR) measurements on powder samples of sodalite loaded with Na at several frequencies between 9.7 and 35 GHz and at temperatures between 1.5 and 60 K. The ESR absorption spectrum below a Néel temperature T_N turns into an asymmetric spectrum with a long tail at low fields from a symmetric one above T_N. The line shape of the spectra below T_N is analyzed by a powder pattern simulation of the antiferromagnetic resonance spectra with easy-plane anisotropy. The calculated line shape reproduces the experimental one considerably well by assuming a Gaussian distribution of the zero-field energy gap. We have evaluated a small anisotropy field of about 2×10⁻⁴ T by using the exchange coupling constant calculated from the Weiss and the Néel temperatures. This result indicates that the sodalite loaded with Na is quite an ideal Heisenberg antiferromagnet as expected from the s-electron character of Na clusters and the cubic arrangement of nano-spaces in the sodalite.