Preparation and characteristics of?a?BaO–Al2O3–B2O3–SiO2–La2O3 glass ceramic via spray pyrolysis

The characteristics of a BaO–Al₂O₃–B₂O₃–SiO₂–La₂O₃ glass ceramic prepared by spray pyrolysis were studied. Glass powders with spherical shape and amorphous phase were prepared by complete melting at a preparation temperature of 1 500°C. The mean size and geometric standard deviation of the powders prepared at the temperature of 1 500°C were 0.6 μm and 1.3. The glass powders had similar composition to that of the spray solution. The glass transition temperature (T _g) of the glass powders was 600.3°C. Two crystallization exothermic peaks were observed at 769.3 and 837.8°C. Densification of the specimen started at a sintering temperature of 600°C, in which Ba₄La₆O(SiO₄)₆ as main crystal structure was observed. Complete densification of the specimen occurred at a sintering temperature of 800°C. The specimens sintered at temperatures above 800°C had main crystal structure of BaAl₂Si₂O₈.     

Investigation of structural,physical and optical properties of CeO2–Bi2O3–B2O3 glasses

xCeO₂–30Bi₂O₃–(70−x) B₂O₃ glasses are synthesized by using the melt quench technique. A number of studies such as XRD, density, molar volume, optical band gap, refractive index and FTIR spectroscopy are employed to characterize the glasses. The band gap decreases from 2.15 to 1.61 eV, refractive index increases from 2.67 to 2.93 and density increases from 4.151 to 4.633 g/cm³. The decrease in band gap with CeO₂ doping approaches the semiconductor behavior. FTIR spectroscopy reveals that incorporation of CeO₂ into glass network helps to convert the structural units of [BO₃] into [BO₄] and results in Bi–O bond vibration of [BiO₆].     

Magnetic and structural properties of CaO–SiO2–P2O5–Na2O–Fe2O3 glass ceramics

Magnetic properties of glass ceramics derived from glasses with composition 41CaO·(52−x)SiO₂·4P₂O₅·xFe₂O₃·3Na₂O (2?x?10 mol% iron oxide (Fe₂O₃)) are reported. Structural investigation revealed the presence of nanocrystalline magnetite phase in the heat-treated samples containing x?2 mol% Fe₂O₃. Magnetic hysteresis cycles of the glass-ceramic samples were obtained with a maximum applied field of ±20 kOe as well as a low field of ±500 Oe, in order to evaluate the potential of these glass ceramics for hyperthermia treatment of cancer. Samples with x>2 mol% of iron oxide exhibited magnetic behavior similar to soft magnetic materials with low coercivity. The evolution of magnetic properties in these samples as a function of iron oxide molar concentration is correlated with the amount and crystallite size of magnetite phase present in them.     

Broadband near-IR emission and temperature dependence in Er/Tm co-doped Bi2O3–SiO2–Ga2O3 glasses

The broadband near-IR emission has been investigated in a series of Er/Tm co-doped Bi₂O₃–SiO₂–Ga₂O₃ (BSG) glasses with 800 nm laser diode as an excitation source. A broadband emission extending from 1350 to 1650 nm with a full width at half maximum (FWHM) around 165 nm is obtained in 0.2 wt% Er₂O₃ and 1.0 wt% Tm₂O₃ co-doped BSG glass. The fluorescence decay curves of glasses are measured and maximum energy transfer efficiency from Er³⁺ to Tm³⁺ reaches 71% when Tm³⁺ concentration is 1.0 wt%. The temperature dependence of the broadband emission spectra in Er³⁺–Tm³⁺ co-doped BSG glass is also recorded to further understand the energy-transfer processes between Er³⁺ and Tm³⁺. The present work suggests that Er/Tm co-doped BSG glasses can be a potential candidate for broadband integrated amplifier.     

Y2O3·Cr2O3复合氧化物热力学性质的研究

在1182—1386K温度范围内,用固体电解质氧浓差电池:Mo|Cr,Y₂O₃,Y₂O₃·Cr₂O₃|ZrO₂(+MgO)|Cr,Cr₂O₃|Mo测定了复合氧化物Y₂O₃·Cr₂O₃的热力学性质。对于反应Y_{2关键词：}     

FTIR structural investigation of gamma irradiated BaO–Na2O–B2O3–SiO2 glasses

Fourier transform infrared (FT-IR) spectra of xBaO–15Na₂O–(70−x)B₂O₃–15SiO₂ glass system with x=0, 5, 10, 15 and 20 (mol%) has been measured in the spectral range 400–4000 cm⁻¹ at room temperature in order to understand the characteristic frequencies of the chemical bonds and bonding mechanisms, which are susceptible to the structural and spectral changes. The effect of gamma irradiation in the dose range 0.1 kGy–60 kGy on the infrared absorption spectra of these glasses is also reported. The change in the glass structure due to the effect of composition is also discussed. It has been observed that irradiation of the glasses with the gamma rays increases the BO₃ groups and the non bridging oxygens which make the network loose.     

Ga2O3组分对Tm3+掺杂GeO2-Ga2O3-Li2O-BaO-La2O3玻璃的光谱性能影响

制备了Tm³⁺(8.0mol%)掺杂(77-x)GeO₂-xGa₂O₃-8Li₂O-10BaO-5La₂O₃(x=4,8,12,16)系列玻璃.系统地研究了Ga₂O₃从4mol%变化到16mol%时,玻璃的光谱性质与热学性质的变化规律.差热分析表明,随着Ga₂O₃含量的增加,锗酸盐玻璃的热稳定性增加.运用Judd-Ofelt(J_O)理论计算得到了Tm³⁺在不同Ga₂O₃含量的GeO₂-Ga₂O₃-Li₂O-BaO-La₂O₃玻璃中的J-O强度参数(Ω₂,Ω₄,Ω₆)及Tm³⁺各激发能级的自发跃迁概率、荧光分支比以及辐射寿命等光谱参量.在808nm激光二极管的激发下,测试并分析了Ga₂O₃对Tm³⁺荧光光谱特性的影响.随着Ga₂O₃从4mol%增加到16mol%,Tm³⁺在1.8μm处的荧光强度呈现先减弱后增强的特性.当Ga₂O₃含量大约在12mol%时,Tm³⁺在1.8μm处的荧光强度最弱,受激发射截面达到最小.还初步讨论了Ga₂O₃对玻璃结构与光谱参数的影响规律. 关键词： 3+掺杂锗酸盐玻璃')" href="#">Tm³⁺掺杂锗酸盐玻璃 光谱性能 Judd-Ofelt参数 热稳定性     

Al2O3增强的Co2-C98/Al2O3/Si异质结的光伏效应

随着能源危机的加剧,太阳能电池作为开发和利用太阳能的一种普遍形式, 日益受到世界各国的重视.随着太阳能电池向着高效率、薄膜化、无毒性和原材料丰富的方向发展, 单纯的硅系太阳能电池已经无法达到这样的要求,因此新的材料和工艺的开发利用迫在眉睫. 本文研究了碳材料在硅异质节上实现光伏效应的改善及其可能在太阳能电池上的应用. 采用脉冲激光沉积方法制备的Co₂-C₉₈/Al₂O₃/Si异质结构在标准日光照射 (AM1.5, 100 mW/cm²)条件下,可获得0.447 V的开路电压和18.75 mA/cm²的电流密度, 转换效率可达3.27%.通过电容电压特性和暗条件下的电输运性能测量, 证明了氧化铝层的引入不但对单晶硅的表面起到了物理钝化作用,减小了反向漏电流, 使异质结界面缺陷、界面能级和复合中心减少,还起到了场效应钝化作用, 增加了异质结界面的势垒高度,增加了开路电压,使异质结的光伏效应显著增强.     

La2O3对Yb:Y2O3透明陶瓷光谱性能的影响

研究了La₂O₃对Yb：Y₂O₃透明陶瓷光谱性能的影响，添加适量La₂O₃以后，Yb：Y₂O₃透明陶瓷的吸收峰和发射峰的位置不变，但由于La³⁺的离子半径大于Y³⁺的离子半径，在Y₂O₃中引入La³⁺离子后，导致Y₂O₃晶格常数变大，晶场强度变弱，同时降低了Y₂O₃晶体的有序度，致使发射峰强度有所下降，发射截面变小.过量的La₂O₃（x=0.16）造成Yb³⁺激活离子发射强度明显下降；其荧光寿命在添加La₂O₃后总体增大45%—60%. 关键词： 氧化镧 氧化钇 透明陶瓷 光谱性能     

Eu2O3在η-Al2O3和SiO2上固体-固体表面相互作用的研究

用穆斯堡尔谱和X射线衍射技术研究了Eu₂O₃在η-Al₂O₃和硅胶上的固体表面吸附。 关键词：     

Varistor and dielectric properties of Cr2O3 doped SnO2–Zn2SnO4 composite ceramics

Cr₂O₃ doped SnO₂–Zn₂SnO₄ composite ceramics were prepared by traditional ceramic processing and the varistor, dielectric properties were investigated. With increasing Cr₂O₃ content, the breakdown electrical field E_B increases from 11 to 92 V/mm and the relative dielectric constant ε_r measured at 1 kHz, 50 °C decreases from 11,028 to 3412, respectively. The barrier height ?_B about 0.8–0.84 eV and the decreasing of SnO₂ grain size suggest that the varistor behavior with high ε_r is originated from SnO₂–SnO₂ or SnO₂–Zn₂SnO₄ grain boundary. In the dielectric spectra lower than 1 kHz, a dielectric peak is presented and depressed with increasing bias voltage. Similarly, at high temperature, the dielectric constant also presents a dielectric peak in the temperature spectra and the peak becomes faint with increasing frequency. The exhibition of the dielectric peak is thought to be attributed to the conduction of grain boundary since it is accompanied by the sharp increase of dielectric loss. In addition, a dielectric relaxation with the activation energy about 0.4–0.5 eV was observed in the temperature range of 20–100 °C. Based on the results, the formation mechanism of Schottky barriers at grain boundaries and the varistor behavior with high dielectric constant are well understood.     

Nd3+掺杂B2O3-Nb2O5-BaO-La2O3玻璃光谱性质的研究

 用高温熔融法制备了Nd³⁺(物质的量分数2％）掺杂40B₂O₃-(15-χ)Nb₂O₅-45BaO-χLa₂O₃玻璃，测量了样品的吸收光谱、发射光谱和差热分析（DTA）曲线。根据Nd3+光学跃起矩阵的特点，应用Judd-Ofelt理论，从吸收光谱获得了Nd³⁺光学跃起的强度参数。并计算了Nd³⁺离子的自发辐射跃迁几率、总自发辐射几率、荧光分支比、辐射能级寿命和受激发射截面。结果表明：该体系玻璃中，随着Nb₂O₅ 含量的增加和La₂O₃₂增大，说明材料的对称性降低；而Ω₆减小，说明Nd-O键的共价性和键强增强；受激发射截面减小。DTA实验表明，随着Nb₂O₅含量的增加，材料的热稳定性提高。     

Al2O3衬底MgB2超薄膜的研究

我们利用混合物理化学气相沉积法(Hybrid physical-chemical vapor deposition简称为HPCVD)在(000l)Al2O3衬底上制备了系列干净的MgB2超薄膜,并通过R-T测量、SEM测量、M-T测量、XRD测量对它们进行了表征,探究了其超导电磁性能和薄膜的生长机制.其中的7.5nm厚的MgB2超薄膜为已报导的蓝宝石衬底上生长的性能最高的超薄膜.     

非晶态锂离子导体B2O3-0.7Li2O-0.7LiCl-xAl2O3

木文研究了Al₂O₃对B₂O₃-0.7Li₂O-0.7LiCl非晶态的形成和电学性能的影响,我们发现:加入适量的Al₂O₃后,无需借助液氮骤冷技术,直接将熔体倾倒在室温下的紫铜板上就很容易形成大块非晶锂离子导体B₂O₃-0.7Li₂O-0.7LiCl-xAl₂O₃。Al₂O₃的加入使B₂O₃-0.7Li₂O-0.7LiCl的电导率有所降低,但在高温下不太明显,电导激活能略微升高,实验发现:Al₂O₃含量x=0.03是较合适的剂量,较容易形成大块非晶态,对电导率的影响也不大。 关键词：     

Ce3+掺杂SiO2-Al2O3-Gd2O3玻璃的闪烁性能

通常, Ce离子掺杂的低密度玻璃有较高的发光效率, 而高密度的Ce离子掺杂玻璃其发光效率很低. 为了解释这一现象, 采用高温熔融法获得了SiO₂-Al₂O₃-Gd₂O₃三元系统的玻璃形成区, 并在还原气氛下制备了Ce³⁺掺杂SiO₂-Al₂O₃-Gd₂O₃以及SiO₂-Al₂O₃-Gd₂O₃-Ln₂O₃ (Ln=Y, La, Lu)闪烁玻璃, 研究了其光谱和闪烁性能. 测试结果显示: 随着Gd₂O₃含量增加, 玻璃紫外截止波长发生红移, 荧光强度降低, 衰减时间缩短; 加入Lu₂O₃, La₂O₃, Y₂O₃后, 紫外截止波长发生红移, 荧光强度降低, 衰减时间变短; 当Gd₂O₃超过10% mol时, X射线荧光积分光产额从相当于锗酸铋 晶体的61%降低到13%. 荧光强度降低、衰减时间缩短的原因是随着玻璃的紫外截止波长红移玻璃的能带宽度变窄, 使得Ce³⁺离子的d电子轨道开始接近玻璃的导带, Ce³⁺离子受辐射后跃迁到d电子轨道的电子会通过导带与玻璃中的空穴复合, 产生电荷迁移猝灭效应.     

γ-Fe2O3中的氢含量

利用热中子透射法测定γ-Fe₂O₃的氢含量。利用差热分析、磁分析以及穆斯堡尔效应研究γ-Fe₂O₃的相变,实验结果表明在γ-Fe₂O₃结构中确实含有一定量的氢,当γ-Fe₂O₃结构中的阳离子空位被H¹⁺,Co²⁺,Si⁴⁺,P⁵⁺等离子占据时,将 关键词：     

包钴型r-Fe2O3磁粉各向异性研究

包钴型γ-Fe₂O₃磁粉的矫顽力可比原γ-Fe₂O₃磁粉提高8000—32000A/m。木文研究探讨了两种包钴型γ-Fe₂O₃磁粉(包钴γ-Fe₂O₃和包钴包亚铁γ-Fe₂O₃)的单轴各向异性的起源和矫顽力增大的机制。包钴γ-Fe₂O₃磁粉矫顽力 关键词：     

Ti-Al2O3金属陶瓷的渗流模型

用渗流理论讨论了Ti-Al₂O₃金属陶瓷的显微结构同宏观电导率的关系,发现渗流模型结果与实验结果是一致的。该Ti-Al₂O₃金属陶瓷的渗流阈值为(Ti的临界百分含量)ω^*=0.16,其临界指数即为三维连续渗流的临界指数值。 关键词：     

Er3+掺杂的Bi2O3-B2O3-SiO2玻璃的光谱性质

测试了Bi₂O₃-B₂O₃-SiO₂玻璃中的Er³⁺离子的吸收光谱、发射光谱、⁴I_13/2的荧光寿命、拉曼光谱,及OH^-的傅里叶红外吸收光谱。应用Judd-Ofelt理论计算了该玻璃中的Er³⁺离子的J-O参数、振子强度、⁴I_13/2能级的寿命,从而利用测得的⁴I_13/2的荧光寿命得出了⁴I_13/2能级的量子效率(15%)。由于较低量子效率可能与OH^-有关,所以计算了玻璃中的OH^-浓度,发现其浓度较高(1.66×10¹⁹cm^-1,相当于Er³⁺浓度的3倍)。应用McCumber理论和四能级模型计算了Er³⁺离子的受激发射截面和荧光发射光谱的半峰全宽,结果与通过吸收光谱计算所得基本吻合。根据透射率和折射率的关系计算了折射率,发现和测量值相差很大,说明有较大的散射,通过拉曼光谱和显微镜测试,认为是玻璃中的微小气泡造成的。