Synthesis and functionalization of dendron‐polymer conjugate based hydrogels via sequential thiol‐ene “click” reactions

Fabrication and functionalization of hydrogels from well‐defined dendron‐polymer‐dendron conjugates is accomplished using sequential radical thiol‐ene “click” reactions. The dendron‐polymer conjugates were synthesized using an azide‐alkyne “click” reaction of alkene‐containing polyester dendrons bearing an alkyne group at their focal point with linear poly(ethylene glycol)‐bisazides. Thiol‐ene “click” reaction was used for crosslinking these alkene functionalized dendron‐polymer conjugates using a tetrathiol‐based crosslinker to provide clear and transparent hydrogels. Hydrogels with residual alkene groups at crosslinking sites were obtained by tuning the alkene‐thiol stoichiometry. The residual alkene groups allow efficient postfunctionalization of these hydrogel matrices with thiol‐containing molecules via a subsequent radical thiol‐ene reaction. The photochemical nature of radical thiol‐ene reaction was exploited to fabricate micropatterned hydrogels. Tunability of functionalization of these hydrogels, by varying dendron generation and polymer chain length was demonstrated by conjugation of a thiol‐containing fluorescent dye. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 926–934     

Thiol–ene polymerizations using imide‐based monomers

New diene and dithiol monomers, based on aromatic imides such as benzophenone‐3,3′,4,4′‐tetracarboxylic diimide were synthesized and used in thiol‐ene polymerizations which yield poly(imide‐co‐thioether)s. These linear polymers exhibit limited solubility in various organic solvents. The molecular weights of the polymers were found to decrease with increasing imide content. The glass transition temperature (T_g) of these polymers is dependent on imide content, with T_g values ranging from ?55 °C (with no imide) up to 13 °C (with 70% imide). These thermal property improvements are due to the H‐bonding and rigidity of the aromatic imide moieties. Thermal degradation, as studied by thermogravimetric analysis, was not significantly different to the nonimide containing thiol‐ene polymers made using trimethyloylpropane diallyl ether and 3,5‐dioxa‐1,8‐dithiooctane. It is expected that such monomers may lead to increased glass transition temperatures in other thiol‐ene polymer systems as these normally exhibit low glass transition temperatures. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4637–4642     

Photocatalyzed thiol–alkene coupling: Mechanistic study and polymer synthesis

Due to the “click” chemistry characteristics of the thiol–ene reaction, these transformations have been gaining an increasing amount of attention in current chemical research. The high efficiency and selectivity of these transformations have been useful for many areas of study, from small molecule organic synthesis, to polymer synthesis and functionalization, to bio‐conjugation reactions. In this work, a study of a novel method of photochemical thiol–ene reactions using alkyl halides and an tris[2‐phenylpyridinato‐C2,N]iridium(III) (Ir(ppy)₃) photocatalyst is investigated. This process is shown to progress rapidly and has the benefit of low catalyst and initiator concentrations relative to reagents as well as mild conditions associated with photochemical processes. To understand the mechanism of this process, catalyst and initiator concentrations and other reaction conditions are varied. To demonstrate the utility of this process, a step‐growth thiol–ene polymer is synthesized using dithiol and diene monomers and a crosslinked polymer network is synthesized as well. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 1931–1937     

ABC type miktoarm star copolymers through combination of controlled polymerization techniques with thiol‐ene and azide‐alkyne click reactions

ABC type miktoarm star copolymer with polystyrene (PS), poly(ε‐caprolactone) (PCL) and poly(ethylene glycol) (PEG) arms was synthesized using controlled polymerization techniques in combination with thiol‐ene and copper catalyzed azide‐alyne “click” reactions (CuAAC) and characterized. For this purpose, 1‐(allyloxy)‐3‐azidopropan‐2‐ol was synthesized as the core component in a one‐step reaction with high yields (96%). Independently, ω‐thiol functionalized polystyrene (PS‐SH) was synthesized in a two‐step protocol with a very narrow molecular weight distribution. The bromo end function of PS obtained by atom transfer radical polymerization was first converted to xanthate function and then reacted with 1, 2‐ethandithiol to yield desired thiol functional polymer (PS‐SH). The obtained polymer was grafted onto the core by thiol‐ene click chemistry. In the following stage, ε‐caprolactone monomer was polymerized from the core by ring opening polymerization (ROP) using tin octoate as catalyst through hydroxyl groups to form the second arm. Finally, PEG‐acetylene, which was simply synthesized by the esterification of Me‐PEG and 5‐pentynoic acid, was clicked onto the core through azide groups present in the structure. The intermediates at various stages and the final miktoarm star copolymer were characterized by ¹H NMR, FTIR, and GPC measurements. © 2011 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2011     

Visible light‐induced thiol‐ene reaction: A new strategy to prepare Α,ω‐dithiol and Α,ω‐divinyl telechelic polythiolether oligomers

A new strategy is developed to prepare both α,ω‐dithiol and α,ω‐divinyl linear telechelic polythiolether oligomers by visible light induced thiol‐ene chemistry in the presence of a fac‐Ir(ppy)₃ photoredox catalyst. Polythiolether oligomers of well‐defined end groups and controlled molecular weights have been successfully synthesized at varying monomer molar ratios of 1,4‐benzenedimethanethiol (BDMT) to diethylene glycol divinyl ether (DEGVE). ¹H NMR and MALDI‐TOF MS analyses demonstrate that as‐prepared polythiolethers possess high end‐group fidelity, which is further supported by the successful polyaddition of polythiolethers bearing α,ω‐dithiol and α,ω‐divinyl groups. For example, with the α,ω‐dithiol‐ (M_n = 1900 g mol^?1, PDI = 1.25) and α,ω‐divinyl‐terminated (M_n = 2000 g mol^?1, PDI = 1.29) polythiolethers as macromonomers, the molecular weight of resulting polythiolether is up to 7700 g mol^?1 with PDI as 1.67. The reactivity of the terminal thiol group is further confirmed by the addition reaction with N‐(1‐pyrenyl)maleimide. UV‐vis spectra and fluorescene measurements suggest that fac‐Ir(ppy)₃ undergo a redox quenching process reacted with BDMT to generate thiyl free radicals. With these results, the mechanism of the thiol‐ene reaction catalyzed by photoredox catalyst is proposed. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 740–749     

Thiol‐Ene Step‐Growth as a Versatile Route to Functional Polymers

A new use of the thiol‐ene reaction to generate functional, redox‐tunable polymers is described. To illustrate the versatility of this approach, tailored divinyl ether monomers were polymerized with triethylene glycol dithiol to yield polymers containing either a carbonate or zwitterionic phosphocholine within the polymer backbone. Similarly, dithioerythritol was polymerized with triethylene glycol divinyl ether to yield a polymer with pendant diols and show how functional groups can be designed into either the divinyl ether or dithiol monomer. Using the thioether functional group inherent to this polymerization, all three polymers were selectively and quantitatively oxidized to either sulfoxides or sulfones by treatment with dilute hydrogen peroxide or mCPBA, respectively. With these illustrative examples, it is shown that the thiol‐ene polymerization is a broad‐reaching method to access a class of new redox‐active polymers which contain varied and dense functional‐group compositions.     

Sequential thiol‐ene/thiol‐ene and thiol‐ene/thiol‐yne reactions as a route to well‐defined mono and bis end‐functionalized poly(N‐isopropylacrylamide)

Sequential thiol‐ene/thiol‐ene and thiol‐ene/thiol‐yne reactions have been used as a facile and quantitative method for modifying end‐groups on an N‐isopropylacrylamide (NIPAm) homopolymer. A well‐defined precursor of polyNIPAm (PNIPAm) was prepared via reversible addition‐fragmentation chain transfer (RAFT) polymerization in DMF at 70 °C using the 1‐cyano‐1‐methylethyl dithiobenzoate/2,2′‐azobis(2‐methylpropionitrile) chain transfer agent/initiator combination yielding a homopolymer with an absolute molecular weight of 5880 and polydispersity index of 1.18. The dithiobenzoate end‐groups were modified in a one‐pot process via primary amine cleavage followed by phosphine‐mediated nucleophilic thiol‐ene click reactions with either allyl methacrylate or propargyl acrylate yielding ene and yne terminal PNIPAm homopolymers quantitatively. The ene and yne groups were then modified, quantitatively as determined by ¹H NMR spectroscopy, via radical thiol‐ene and radical thiol‐yne reactions with three representative commercially available thiols yielding the mono and bis end functional NIPAm homopolymers. This is the first time such sequential thiol‐ene/thiol‐ene and thiol‐ene/thiol‐yne reactions have been used in polymer synthesis/end‐group modification. The lower critical solution temperatures (LCST) were then determined for all PNIPAm homopolymers using a combination of optical measurements and dynamic light scattering. It is shown that the LCST varies depending on the chemical nature of the end‐groups with measured values lying in the range 26–35 °C. © 2009 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 3544–3557, 2009     

Synthesis and characterization of crystalline graft polymer poly(ethylene oxide)‐g‐poly(ɛ‐caprolactone)2 with modulated grafting sites

The graft polymer poly(ethylene oxide)‐g‐poly(?‐caprolactone)₂ (PEO‐g‐PCL₂) with modulated grafting sites was synthesized by the combination of ring‐opening polymerization (ROP) mechanism, efficient Williamson reaction, with thiol–ene addition reaction. First, the precursor of PEO‐Allyl‐PEO with two terminal hydroxyl groups and one middle allyl group was prepared by ROP of EO monomers. Then, the macroinitiator [PEO‐(OH)₂‐PEO]_s was synthesized by sequential Williamson reaction between terminal hydroxyl groups and thiol–ene addition reaction on pendant allyl groups. Finally, the graft polymer PEO‐g‐PCL₂ was obtained by ROP of ?‐CL monomers using [PEO‐(OH)₂‐PEO]_s as macroinitiator. The target graft polymer and all intermediates were well characterized by the measurements of gel permeation chromatography, ¹H NMR, and thermal gravimetric analysis. The crystallization behavior was investigated by the measurements of differential scanning calorimetry, wide‐angle X‐ray diffraction and polarized optical microscope. The results showed that when the PCL content of side chains reached 59.2%, the crystalline structure had been dominated by PCL part and the crystalline structure formed by PEO part can be almost neglected. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 2239–2247     

Silicon‐based mercaptans: High‐performance monomers for thiol‐ene photopolymerization

Ester‐free silane and siloxane‐based thiol monomers were successfully synthesized and evaluated for application in thiol‐ene resins. Polymerization reaction rates, conversion, network properties as well as degradation experiments of those thiol monomers in combination with triallyl‐1,3,5‐triazine‐2,4,6(1H,3H,5H)‐trione (TATT) as ene component were performed and compared with formulations containing the commercially available mercaptopropionic ester‐based thiol pentaerythritol tetra‐3‐mercaptopropionate. Kinetic analysis revealed appropriate reaction rates and conversions reaching 90% and higher. Importantly, storage stability tests of those formulations clearly indicate the superiority of the synthesized mercaptans compared with pentaerythritol tetra‐3‐mercaptopropionate/TATT resins. Moreover, photocured samples containing silane‐based mercaptans provide higher glass transition temperatures and withstand water storage without a significant loss in their network properties. This behavior together with the observed excellent degradation resistance of photocured silane‐based thiol/TATT formulations make these multifunctional mercaptans interesting candidates for high‐performance applications, such as dental restoratives and automotive resins. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 418–424     

Photo‐initiated thiol–ene “click” hydrogels from RAFT‐synthesized poly(N‐isopropylacrylamide)

Despite the efficiency and robustness of the widely used copper‐catalyzed 1,3‐dipolar cycloaddition reaction, the use of copper as a catalyst is often not attractive, particularly for materials intended for biological systems. The use of photo‐initiated thiol‐ene as an alternative “click” reaction to synthesize “model networks” is investigated here. Poly(N‐isopropylacrylamide) precursors were synthesized by reversible addition fragmentation chain transfer (RAFT) polymerization and were designed to have trithiocarbonate moieties as end groups. This structure design provides opportunity for subsequent end‐group modifications in preparation for thiol‐ene “click.” Two reaction routes have been proposed and studied to yield thiol and ene moieties. The advantages and disadvantages of each reaction path were investigated to propose a simple but efficient route to prepare copper‐free “click” hydrogels. © 2013 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2013 , 51, 4626–4636     

Synthesis of networked polymers by crosslinking reactions of polybenzoxazine bearing allyl group in the side chain

A polybenzoxazine bearing allyl group in the side chain was synthesized by the ring‐opening polymerization of N‐allyl‐benzoxazine and was crosslinked by the two different processes, (1) thermally induced oligomerization of the allyl side chains and (2) radical addition of dithiol (thiol‐ene reaction) to the allyl side chains. The former process was promoted by adding 2,5‐dimethyl‐2,5‐di(tert‐butylperoxy)hexane as a radical source, leading to the improved yield of the networked polymer isolated as acetone‐insoluble fraction. The thiol‐ene reaction with using 1,6‐hexanedithiol was also an efficient method for crosslinking the polybenzoxazine. © 2013 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2013     

Orthogonal multifunctionalization of aliphatic polycarbonate via sequential Michael addition and radical‐thiol‐ene click reactions

Aliphatic polycarbonate (PC) copolymer is synthesized by ring opening copolymerization of acrylate‐ and allyl‐functional cyclic carbonate monomers. The post‐polymerization functionalization of the resulting copolymer is performed quantitatively using a variety of thiol compounds via sequential Michael addition and photo‐induced radical thiol‐ene click reactions within relatively short reaction time at ambient temperature. This metal‐free click chemistry methodology affords the synthesis of biocompatible PC copolymer with multifunctional groups. © 2014 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2014 , 52, 1581–1587     

Synthesis of polycarbosilanes having sugar‐derived structures as novel materials for cell cultivation

Polycarbosilanes with or without sugar‐derived structures in the polymer side chains were synthesized and their application to materials for cell cultivation was investigated. Polysilacyclobutanes having glucose‐derived moieties or N‐acetylglucosamine‐derived moieties (polyBMSB‐glucose and polyBMSB‐AGA) were synthesized by ene‐thiol reaction between precursor poly(1‐(3‐butenyl)?1‐methylsilacyclubane) (polyBMSB) and tetraacetylglucose or tetraacetylglucosamine having a thiol group at the anomeric position and the successive deprotection of the acetyl groups gave polycarbosilanes with sugar‐derived structures in the side chains. Poly(1‐(3‐hydroxybutyl)‐1‐methylsilacyclobutane) was synthesized by hydroboration/oxidation of the precursor polyBMSB. The cell cultivation efficiency using the polymers with or without sugar moieties was evaluated by cultivation of WRL cells on the polystyrene dishes coated with the polymers. © 2015 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2015 , 53, 2267–2272     

Dendrimers in thiol‐ene crosslinked networks and the effect of subsequent generations on thermoset properties

A series of well‐defined allyl‐ether functionalized polyester dendrimers has been synthesized via the divergent approach using traditional esterification reactions. Two commercially available trifunctional thiols, trimethylolpropane tri(3‐mercaptopropanoate) (TRIS) and ethoxylated trimethylolpropane tri(3‐mercaptopropanoate) (ETTMP), were incorporated with the dendrimers into the thiol‐ene polymer networks. The thiol‐ene reactions were conducted at room temperature and cured by UV light without the addition of photoinitiatior. Highly crosslinked films were obtained and characterized with respect to mechanical (DMA) and thermal (DSC and TGA) properties. © 2008 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 47: 589–601, 2009     

One‐pot enzymatic route to tetraallyl ether functional oligoesters: Synthesis,UV curing,and characterization

An enzymatic one‐pot route in bulk was used to synthesize tetraallyl ether (tAE) functional oligomers based on divinyl adipate, 1,4‐butanediol and trimethylolpropane diallyl ether. By using lipase B from Candida antarctica as catalyst and varying the stoichiometric ratio of monomers, it was possible to reach targeted molecular weights (from 1300 to 3300 g mol^?1) of allyl‐ether functional polyesters. The enzyme catalyzed reaction reached completion (>98% conversion based on all monomers) within 24 h at 60 °C, under reduced pressure (72 mbar) resulting in ～90% yield after filtration. The tAE‐functional oligoesters were photopolymerized, without any purification other than removal of the enzyme by filtration, with thiol functional monomers (dithiol, tetrathiol) in a 1:1 ratio thiol‐ene reaction. The photo‐initiator, 2,2‐dimethoxy‐2‐phenylacetophenone, was used to improve the rate of reaction under UV light. High conversions (96–99% within detection limits) were found for all thiol‐ene films as determined by FT‐Raman spectroscopy. The tAE‐functional oligoesters were characterized by NMR, MALDI, and SEC. The UV‐cured homopolymerized films and the thiol‐ene films properties were characterized utilizing DSC and DMTA. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2010     

A versatile synthetic path to thiol containing polysiloxanes

A synthetic strategy to polydimethylsiloxanes and polymethylsiloxanes containing thiol functions as end‐ or side‐groups, respectively, is presented. Such polymers are important starting materials for elastomeric networks and postpolymerization modifications. The synthesis starts either with vinyl end‐functionalized polydimethylsiloxanes or with polymethylvinylsiloxanes. The vinyl groups are reacted either with thioacetic acid or with a thioacetic acid/butanethiol mixture via a UV‐initiated thiol‐ene reaction to form the respective thioester quantitatively within few minutes. The thioesters are subsequently deprotected to the respective thiols by reduction with LiAlH₄. The resulting thiol containing polysiloxanes can be used for the formation of networks or another functionalization. © 2016 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2016 , 54, 2940–2948     

Synthesis and characterization of thiol–ene functionalized siloxanes and evaluation of their crosslinked network properties

Three types of linear thiol‐functionalized siloxane oligomers and three types of ene‐functionalized oligomers were synthesized and subsequently photopolymerized. Within each type of thiol‐functionalized oligomer, the ratio of mercaptan repeat units to nonreactive phenyl repeat units was varied to manipulate both the crosslink density and the degree of secondary interactions through π–π stacking. Similarly, the repeat units of the three ene‐functionalized oligomers are composed of allyl‐functional monomers, benzene‐functional monomers, and octyl‐functional monomers in varying ratios of benzene:octyl but with a constant fraction of allyl moieties. The structural composition of the siloxane oligomers plays a pivotal role in the observed material properties of networks formed through thiol–ene photopolymerization. Networks with a high concentration of thiol functionalities exhibit higher rubbery moduli, ultimate strengths, and Young's moduli than networks with lower thiol concentrations. Moreover, the concentration of functionalities capable of participating in secondary interactions via hydrogen bonding or π–π stacking directly impacts the network glass transition temperature and elasticity. The combination of low crosslink density and high secondary interactions produces networks with the greatest toughness. Finally, the fraction of octyl repeats correlates with the hydrophobic nature of the network. © 2012 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem, 2012     

The power of thiol‐ene chemistry

As a tribute to Professor Charlie Hoyle, we take the opportunity to review the impact of thiol‐ene chemistry on polymer and materials science over the past 5 years. During this time, a renaissance in thiol‐ene chemistry has occurred with recent progress demonstrating its unique advantages when compared with traditional coupling and functionalization strategies. Additionally, the robust nature of thiol‐ene chemistry allows for the preparation of well‐defined materials with few structural limitations and synthetic requirements. To illustrate these features, the utility of thiol‐ene reactions for network formation, polymer functionalization, dendrimer synthesis, and the decoration of three‐dimensional objects is discussed. Also, the development of the closely related thiol‐yne chemistry is described. © 2010 Wiley Periodicals, Inc. J Polym Sci Part A: Polym Chem 48: 743–750, 2010     

Synthesis and Spatiotemporal Modification of Biocompatible and Stimuli‐Responsive Carboxymethyl Cellulose Hydrogels Using Thiol‐Norbornene Chemistry

Carboxymethyl cellulose (CMC) is functionalized with norbornene groups to undergo thiol‐norbornene cross‐linking reactions. Hydrogels synthesized from a single norbornene‐modified carboxymethyl cellulose (NorCMC) via a light‐initiated thiol‐ene cross‐linking reaction with a variety of dithiol cross‐linkers yield hydrogels with a tunable compression modulus ranging from 1.7 to 103 kPa. Additionally, thermoresponsiveness is spatiotemporally imparted to NorCMC hydrogels by photopatterning a dithiol‐terminated poly(N‐isopropyl acrylamide) cross‐linker, enabling swelling and topological control of the hydrogels as a function of incubation temperature. NorCMC hydrogels are cytocompatible as the viability of encapsulated human mesenchymal stem cells (hMSCs) is greater than 85% after 21 d while using a variety of cross‐linkers. Moreover, hMSCs can remodel, adhere, and spread in the NorCMC matrix cross‐linked with a matrix metalloproteinase‐degradable peptide, further demonstrating the utility of these materials as a tunable biomaterial.